DE2630174B2 - SLIDER CLOSURES AND REPAIR COMPOUNDS FOR THESE MADE OF FIRE-RESISTANT BASIC MATERIAL - Google Patents
SLIDER CLOSURES AND REPAIR COMPOUNDS FOR THESE MADE OF FIRE-RESISTANT BASIC MATERIALInfo
- Publication number
- DE2630174B2 DE2630174B2 DE19762630174 DE2630174A DE2630174B2 DE 2630174 B2 DE2630174 B2 DE 2630174B2 DE 19762630174 DE19762630174 DE 19762630174 DE 2630174 A DE2630174 A DE 2630174A DE 2630174 B2 DE2630174 B2 DE 2630174B2
- Authority
- DE
- Germany
- Prior art keywords
- slide
- basic material
- magnesia
- mgo
- plates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
Die Erfindung betrifft Schieberverschlüsse und Reparaturmasse für diese aus feuerfestem, basischem Material für Metallschmelzen enthaltende Behälter.The invention relates to slide closures and repair compounds for these made of refractory, basic Material for containers containing molten metal.
Gießpfannen und andere Zwischenbehälter für die Aufnahme von geschmolzenen, flüssigen Metallen, wie insbesondere Stahl, weisen in ihrem Bodenteil zum Ausbringen der Metallschmelze eine Ausflußöffnung auf, die häufig durch einen Schieberverschluß abgeschlossen ist, der parallel zum Boden der Gießpfanne bzw. des Behälters bewegbar ist. Diese Schieberverschlüsse sind besonders stark durch Erosion und Verschlackung und ferner auch durch Temperaturwechsel beansprucht, und es sind daher schon zahlreiche feuerfeste Materialien für ihren Aufbau vorgeschlagen worden. Alle bisher bekannten Schieberverschlüsse waren jedoch aus gebrannten, feuerfesten Formkörpern aufgebaut, da angenommen wurde, daß nur hochwertige gebrannte, feuerfeste Materialien einer besonderen Zusammensetzung den hohen Anforderungen, die an Schieberverschlüsse zu stellen sind, gewachsen sein könnten.Ladles and other intermediate containers for holding molten, liquid metals such as in particular steel, have an outflow opening in their bottom part for discharging the molten metal on, which is often closed by a slide gate, which is parallel to the bottom of the ladle or the container is movable. These slide gate valves are particularly bad by erosion and Slagging and also stressed by temperature changes, and therefore there are already numerous refractory materials have been proposed for their construction. All known slide locks However, they were constructed from fired, refractory moldings, since it was assumed that only high quality Fired, refractory materials of a special composition meet the high requirements that Slide closures are to be provided, could have grown.
Die vorliegende Erfindung beruht nun auf der überraschenden Feststellung, daß Schieberverschlüsse aus bestimmten ungebrannten Materialien den bisher eingesetzten Schieberverschlüssen aus gebrannten, feuerfesten Stoffen in gewisser Hinsicht sogar überlegen sind. Demnach betrifft die Erfindung Schieberverschlüsse aus feuerfestem, basischem Material für Metallschmelzen enthaltende Behälter, welche dadurch gekennzeichnet sind, daß sie aus einem chemisch gebundenen, basischen Material auf der Grundlage von Magnesia oder Magnesitchrom mit MgO-Gehalten von 55 bis 98,5% aufgebaut sind. Vorzugsweise soll der MgO-Gehalt 756 bis 98,5% betragen. Bei einer besonders zweckmäßigen Ausführungsform enthalten die Schieberverschlüsse, wenn ihr MgO-Gehalt 75% und mehr ausmacht, als Bindemittel Phosphate, unter welcher Bezeichnung auch polymere Phosphate zuThe present invention is based on the surprising finding that slide closures made of certain unfired materials the previously used slide locks made of baked, refractories are even superior in some respects. Accordingly, the invention relates to slide locks Made of refractory, basic material for containers containing molten metal, which thereby are characterized in that they are made of a chemically bound, basic material on the basis of Magnesia or magnesite chromium are built up with MgO contents of 55 to 98.5%. Preferably the MgO content can be 756 to 98.5%. Contained in a particularly expedient embodiment the slide gate valves, if their MgO content is 75% and more, as a binder phosphate, under whatever name polymeric phosphates
verstehen sein sollen. Bei MgO-Gehalten von unter 75% sind Chromsäure oder Chromphosphate als Bindemittel vorzuziehen.should be understood. If the MgO content is below 75%, chromic acid or chromium phosphates are used as binders preferable.
Ferner wurde gefunden, daß sich für die Reparatur solcher Schieberverschlüsse ganz hervorragend basische, feuerfeste, chemisch gebundene Massen aus Magnesia oder Mischungen von Magnesia und Chromerz mit MgO-Gehalten von 55 bis 98,5%, insbesondere 65 bis 98,5%, und Chromaten und/oder Phosphaten als Bindemittel eigenen.Furthermore, it was found that for the repair of such slide closures very excellent basic, refractory, chemically bonded masses of magnesia or mixtures of magnesia and chrome ore with MgO contents of 55 to 98.5%, in particular 65 to 98.5%, and chromates and / or phosphates as Binders own.
Die Bezeichnung »Schieberverschlüsse« soll im vorliegenden Zusammenhang nicht nur Schieberverschlüsse als Ganzes, sondern auch Reparaturteile für solche umfassen.The term "slide locks" in the present context is not intended only to mean slide locks as a whole, but also include repair parts for such.
Die Erfindung wird an Hand der folgenden Beispiele näher erläutert. Der Ordnung halber ist festzuhalten, daß sich sämtliche Prozentangaben auf Gewichtsprozente beziehen. Die in den Beispielen erwähnten Figuren beziehen sich auf Halbmikro-Photographien, die bei photographischen Aufnahmen von Schieberplatten, die einem Verschleißversuch unterworfen wurden, erhalten wurden.The invention is explained in more detail with reference to the following examples. For the sake of order it should be noted that all percentages relate to percentages by weight. The ones mentioned in the examples Figures relate to semi-micro photographs taken from slide plates, which were subjected to a wear test were obtained.
65% Sintermagnesia I einer Korngröße von 0,3 bis 1 mm und 35% Sintermagnesia der gleichen Zusammensetzung in einer Körnung von 0 bis 0,2 mm wurden mit 3 kg/100 kg der Mischung Natriummetaphosphat und 2 kg/100 kg der Mischung Wasser zu Schieberverschlußplatten verpreßt und diese bei einer Temperatur von 180°C getrocknet. Die verwendete Sintermagnesia I hatte folgende Zusammensetzung:65% sintered magnesia I with a grain size of 0.3 to 1 mm and 35% sintered magnesia of the same composition In a grain size of 0 to 0.2 mm, 3 kg / 100 kg of the mixture were used to produce sodium metaphosphate and 2 kg / 100 kg of the mixture of water to form gate valve plates pressed and this dried at a temperature of 180 ° C. The sintered magnesia used I had the following composition:
Die auf diese Weise erhaltenen Schieberplatten wurden dem sogenanten Torch-Test (U. S. Steel's Research Laboratory), der speziell für die Prüfung von Pfannenverschlüssen entwickelt worden ist, unterworfen. Dieser Torch-Test wird im wesentlichen wie folgt durchgeführt:The valve plates obtained in this way were subjected to the so-called torch test (U.S. Steel's Research Laboratory), which has been specially developed for testing pan closures. This torch test is essentially carried out as follows:
Eine Fackel, die mit 142cmJ/sec Propan und 138cm3/sec Sauerstoff gespeist wird und in einer Entfernung von 6,4 mm von dem zu prüfenden feuerfesten Material bzw. Schieberverschluß angeordnet ist, wird mit einer Geschwindigkeit von 1,7 mm/sec über das zu prüfende Material bewegt. Gewünschtenfalls wird die Flamme mehrmals, aber jeweils über verschiedene Stellen des Materials, über dieses geführt. Bei dem gewählten Verhältnis von Propan zu Sauerstoff von etwa 1 :1 erfolgt eine unvollkommene Verbrennung, und die Flamme ist verhältnismäßig kühl. Durch die Einwirkung der Flamme auf die zu prüfenden Schieberplatten werden diese mehr oder weniger stark beansprucht und entsprechend dieser Beanspruchung z. B. nur oberflächlich erodiert oder tiefgreifend beschädigt.A torch, which is fed with 142 cm J / sec propane and 138 cm 3 / sec oxygen and is arranged at a distance of 6.4 mm from the refractory material or slide closure to be tested, is at a speed of 1.7 mm / sec moved over the material to be tested. If desired, the flame is passed over the material several times, but each time over different points. With the selected ratio of propane to oxygen of around 1: 1, the combustion is incomplete and the flame is relatively cool. By the action of the flame on the slide plates to be tested, these are more or less stressed and z. B. only superficially eroded or deeply damaged.
Beim Torch-Test wurden die erfindungsgemäß erhaltenen Schieberplatten durch die Beanspruchung durch die Flamme an ihrer Oberfsäche nur mäßig angerissen, wie aus Fig. 1 der beiliegenden Halbmikro-Photos zu ersehen ist, Zum Vergleich wurden auf genau die gleiche Art aufgebaute Schieberplatten, die jedoch bei 15000C gebrannt waren, ebenfalls dem Torch-TestIn the torch test, the slide plates obtained according to the invention were only moderately torn on their surface due to the stress of the flame, as can be seen from FIG. 1 of the enclosed semi-micro photos 1500 0 C were burned, also the torch test
unterworfen. In diesem Falle konnte nicht nur eine wesentlich stärkere Oberflächenerosior;, sondern auch ein vollständiges Springen der Platten beobachtet werden(Fig. 2).subject. In this case, not only could a much stronger surface erosion; but also complete cracking of the plates can be observed (Fig. 2).
Dieser Vergleichsversuch zeigt deutlich die Überlegenheit der erfindungsgemäßen Schieberplatten gegenüber gleich zusammengesetzten, jedoch gebrannten Schieberphtten.This comparison test clearly shows the superiority the slide plates according to the invention compared to identically composed, but fired Phthalates.
50% Sintermsgncsia I einer Körnung von 0,3 bis 1 mm, 20% Chromerz vom 0,3 bis 1 mm und 30% Sintermagnesia Il einer Korngröße von 0 bis 0,2 mm wurden mit 4 kg/100 kg der Mischung Natriummetanhosphat und 2 kg/100 kg der Mischung Wasser zu Schieberverschlußplatten verpreßt. Diese wurden bei I5O°C getrocknet und hierauf im Vakuum mit wasserfreiem Stahlwerksteer imprägniert.50% Sintermsgncsia I a grain size from 0.3 to 1 mm, 20% chrome ore from 0.3 to 1 mm and 30% sintered magnesia II with a grain size of 0 to 0.2 mm were added with 4 kg / 100 kg of the mixture sodium metanhosphate and 2 kg / 100 kg of the mixture water Compressed slide gate plates. These were dried at 150 ° C. and then in a vacuum Impregnated with anhydrous steel mill tar.
Als Chromerz wurde für die Herstellung eines Teiles der Schieberplatten Chromerz I, für die Herstellung des anderen Teiles der Platten Chromerz Il benutzt. Die Zusammensetzung der eingesetzten Sintermagnesia Il und der Chromerze I und Il waren wie folgt:Chrome ore I was used as chrome ore for the production of part of the valve plates, for the production of the other part of the plates chrome ore II used. The composition of the sintered magnesia used Il and the chrome ores I and II were as follows:
Die beiden Schieberplatten hatten folgende chemische Zusammensetzung:The two valve plates had the following chemical composition:
Das Schmelzprodukt hatte folgende Zusammensetzung- The melt product had the following composition-
SiO2 SiO 2
Fe2O,Fe 2 O,
AhO1 AhO 1
CnO1 CnO 1
CaOCaO
MgOMgO
1,64% 6,12% 2,36%1.64% 6.12% 2.36%
11,16% 2,85%11.16% 2.85%
75,51% 0.36%75.51% 0.36%
Oie Mischung wurde zu Schieberplatte!! verpreßt, die bei 170"C getrocknet wurden.The mixture turned into slide gate !! pressed that were dried at 170 "C.
Die auf diese Weise erhaltenen ungebrannten Schieberplatten zeigten beim Torch-Test eine nur unwesentliche und praktisch vernachlässigbare Oberflächenerosion (F i g. 5), wogegen auf genau die gleiche Art aufgebaute, jedoch gebrannte Schieberplatten beträchtliche Erosionsfurchen aufwiesen (F i g. 6).The unfired valve plates obtained in this way showed only one in the torch test insignificant and practically negligible surface erosion (Fig. 5), whereas in exactly the same way built up but burned slide plates had considerable erosion furrows (FIG. 6).
Bei Verwendung des gleichen Schmelzproduktes für die Herstellung von durch Schmelzguß erhaltenen Schieberplatten zeigte sich, daß diese Schieberplatten beim Torch-Test in kürzester Zeit in mehrere Stück zersprangen (F i g. 7).When using the same melt product for the production of obtained by melt casting Slide plates showed that these slide plates in the torch test in a very short time in several pieces shattered (Fig. 7).
65% Sintermagnesia III von 0,3 bis I mm und 35% Sintermagnesia III einer Korngröße von 0 bis 0,15 mm wurden mit 4 kg/100 kg der Mischung Natriummetaphosphat zu Schicberverschlußplatten verformt und diese bei einer Temperatur von 1500C getrocknet. Die eingesetzte Sintermagnesia III hatte folgende Analyse:65% sintered III of 0.3 to I mm and 35% sintered III a grain size of 0 to 0.15 mm were formed with 4 kg / 100 kg sodium metaphosphate to the mixture to Schicberverschlußplatten and it is dried at a temperature of 150 0 C. The sintered magnesia III used had the following analysis:
Auch in diesem Fall zeigten die erfir.dungsgemäß aufgebauten Schieberplattcn aus ungebranntem Material eine ganz wesentlich geringere Erosion (F i g. 3) als Schieberplatten von genau gleicher Zusammensetzung, die jedoch bei 10000C in einer reduzierenden oder neutralen Atmosphäre getempert worden waren (F ig. 4).In this case, too, the slide plates constructed according to the invention and made of unfired material showed significantly less erosion (Fig. 3) than slide plates of exactly the same composition, which, however, had been tempered at 1000 ° C in a reducing or neutral atmosphere (F Fig. 4).
65% eines Schmelzproduktes der unten angegebenen Analyse und einer Körnung von 0,3 bis 15 mm und 35% des gleichen Schmelzproduktes in einer Körnung von bis 0,2 mm wurden mit jeweils folgenden Mengen, bezogen auf 100 kg des Schmclzproduktes, Zusatzstoffenbzw. Bindemitteln vermischt: 65% of a melt product of the analysis given below and a grain size of 0.3 to 15 mm and 35% of the same melt product in a grain size of up to 0.2 mm were each in the following amounts, based on 100 kg of the melt product, additives or Mixed binders:
4 kg Natriummetaphosphat, 1 kg Trockensulfitabiauge,
1,7 kg Kreide und
1,9 kg Wasser.4 kg sodium metaphosphate, 1 kg dry sulphite waste,
1.7 kg of chalk and
1.9 kg of water.
Diese chemisch gebundenen Schieberplatten und bei 1580°C gebrannte Schieberplatten gleicher Zusammensetzung wurden einem Torch-Test unterworfen, wobei die ungebrannten Platten auf ihrer Oberflache nur mäßig, die gebrannten Platten hingegen sehr stark erodiert wurden.These chemically bonded valve plates and valve plates fired at 1580 ° C of the same composition were subjected to a torch test, leaving the unfired panels on their surface only moderate, but the burned panels were severely eroded.
Zwei Reparaturmassen für Schieberphitten wurden wie folgt aufgebaut:Two repair compounds for slide valve phits were made structured as follows:
a) 70% Sintermagnesia 1 0 — 0,3 mm 30% Chromerz ! 0-0,3 mm .3% Natriummetaphosphata) 70% sintered magnesia 1 0 - 0.3 mm 30% chrome ore! 0-0.3 mm .3% sodium metaphosphate
b) 94% Sintermagnesia 111 0 — 0,3 mmb) 94% sintered magnesia 111 0 - 0.3 mm
1,5% Sintermagnesia IU 0 — 0,12 nun 4,5% CrO!1.5% sintered magnesia IU 0 - 0.12 now 4.5% CrO!
Im Falle der Reparauirmassc a) können auch 1 bis 4% Phosphat, im Faiie der Reparalurinasse b) 3 bis 15% des Chromatbindemiltels, das aus CrO, und Sintermagnesia im Verhältnis 3 : I besteht, verwendet werden. Die Massen werden kurz vor ihrer Verwendung mit Wasser versetzt.In the case of the repair measure a) 1 to 4% Phosphate, in the case of reparalurinase b) 3 to 15% des Chromate binding agent made from CrO and sintered magnesia in a ratio of 3: I can be used. The masses are just before their use with water offset.
Aus den Beispielen ist zu ersehen, daß das überraschende und in keiner Weise vorhersehbare Verhalten ungebrannter Schieberverschlußplatten im Vergleich zu gebrannten Schieberplatten völlig gleicher Zusammensetzung darin besteht, daß die ungebranntenIt can be seen from the examples that this is surprising and in no way predictable Behavior of unfired valve gate plates is completely the same as that of fired valve plates Composition consists in that the unfired
Platten trotz ihrer wesentlich geringeren mechanischen Ausgangsfestigkeit eine erheblich bessere Widerstandsfähigkeit gegen den Temperaturschock und die Erosionswirkung, die beim Torch-Test durch die Flamme hervorgerufen werden, aufweisen.Plates have a considerably better resistance despite their significantly lower mechanical initial strength against the temperature shock and the erosion effect caused by the torch test Flame caused, have.
Hierzu 2 Blatt ZeichnungenFor this purpose 2 sheets of drawings
Claims (5)