DE2514810A1 - Flame sprayed powder coatings of copper alloys - contg. copper-phosphorus brazing powder to increase density and strength - Google Patents
Flame sprayed powder coatings of copper alloys - contg. copper-phosphorus brazing powder to increase density and strengthInfo
- Publication number
- DE2514810A1 DE2514810A1 DE19752514810 DE2514810A DE2514810A1 DE 2514810 A1 DE2514810 A1 DE 2514810A1 DE 19752514810 DE19752514810 DE 19752514810 DE 2514810 A DE2514810 A DE 2514810A DE 2514810 A1 DE2514810 A1 DE 2514810A1
- Authority
- DE
- Germany
- Prior art keywords
- copper
- contg
- alloys
- strength
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Verfahren zur Verbesserung der Eigenschaften von pulverförmigen Cu-Legierungen für das Pulverflammspritzverfahren Die Erfindung betrifft ein Verfahren zur Verbesserung der Eigenschaften von im Pllverflammspritzverfahren aufgetragenen, pulverförmigen Cu-Legierungen, wie Alu-Bronzen od. dgl. Process for improving the properties of powdery Cu alloys for the powder flame spraying process The invention relates to a method for improvement the properties of powdery products applied in the flame spraying process Cu alloys, such as aluminum bronzes or the like.
Die genannten Legierungen werden beispielsweise u.a. für Reparaturen benutzt, um verschlissene Werkstücke nicht durch neue ersetzen zu müssen.The alloys mentioned are used, for example, for repairs used to avoid having to replace worn workpieces with new ones.
Nach einer solchen Beschichtungsbehandlung sind gewisse nachteilige Eigenschaften an derart behandelten Werkstücken zu beobachten.After such a coating treatment, there are certain disadvantages Observe the properties of workpieces treated in this way.
So ist beispielsweise das Einstechen von Nuten od. dgl. nicht mehr ohne weiteres möglich, da die Bearbeitungskanten leicht ausbrechen. Handelt es sich um unter Druck stehende, flüssigder der keitsführende Behältnisse, so läßt häufig die Dichtheit/aufgesprühten Beschichtung zu wünschen übrig oder bei aufgesprühten Kontakten die elektrische Leitfähigkeit.For example, grooving or the like is no longer necessary possible without further ado, since the machining edges break out easily. Is it around pressurized, liquid the carrying containers, so often the tightness / sprayed coating leaves something to be desired or at contacts sprayed on the electrical conductivity.
Der Erfindung liegt die Aufgabe zugrunde, diese Nachteile zu beseitigen und ein Verfahren zur Verbesserung der Eigenschaften der genannten Legierungsbeschichtungen zu schaffen.The invention is based on the object of eliminating these disadvantages and a method of improving the properties of said alloy coatings to accomplish.
Diese Aufgabe ist mit einem Verfahren nach der Erfindung dadurch gelöst, daß die pulverförmige Cu-Legierung mit pulverförmigen Cu-P-Lot etwa im Verhältnis 50:50 gemischt und nach dem Auftragen auf ca. 7000C erwärmt wird.This object is achieved with a method according to the invention in that that the powdery Cu alloy with powdery Cu-P solder approximately in the ratio 50:50 mixed and heated to approx. 7000C after application.
Durch dieses Verfahren werden die Partikel der pulverförmigen Cu-Legierung vom Cu-P-Lot lrflossen bzw. umhüllt, wodurch sich beispielsweise ein dichteres, besser bearbeitbares und besser leitfähiges Gefüge der Auftragsschicht ergibt.By this process, the particles of the powdery Cu alloy by the Cu-P solder or enveloped, whereby, for example, a denser, results in a better workable and better conductive structure of the coating layer.
Wie sich gezeigt hat, können dabei ohne Schwierigkeiten und ohne Kantenbrüche beispielsweise ausgeschlagene Ringnuten an Kolben repariert und die Nuten durch entsprechende Bearbeitung (Einstechen) wieder auf das ursprüngliche Konstruktionsmaß für die einzusetzenden Kolbenringe gebracht werden.As has been shown, this can be done without difficulty and without edge breaks For example, worn out annular grooves on pistons were repaired and the grooves through corresponding processing (grooving) back to the original construction dimension for the piston rings to be used.
Außerdem zeigen solche Beschichtungen in anderen Anwendungsfällen der beispielsweise genannten Art verbesserte Dichtigkeits- und Leitfähigkeitseigenschaften.In addition, such coatings show in other applications the for example mentioned type improved sealing and conductivity properties.
Claims (1)