DE2457104B2 - Process for the production of textile fabrics with zone-wise reduced stiffness - Google Patents

Process for the production of textile fabrics with zone-wise reduced stiffness

Info

Publication number
DE2457104B2
DE2457104B2 DE2457104A DE2457104A DE2457104B2 DE 2457104 B2 DE2457104 B2 DE 2457104B2 DE 2457104 A DE2457104 A DE 2457104A DE 2457104 A DE2457104 A DE 2457104A DE 2457104 B2 DE2457104 B2 DE 2457104B2
Authority
DE
Germany
Prior art keywords
textile
rigidity
reduced
zones
stiffness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE2457104A
Other languages
German (de)
Other versions
DE2457104A1 (en
Inventor
Zdenek Regensdorf Koula (Schweiz)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Stotz und Co AG
Original Assignee
Stotz und Co AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Stotz und Co AG filed Critical Stotz und Co AG
Publication of DE2457104A1 publication Critical patent/DE2457104A1/en
Publication of DE2457104B2 publication Critical patent/DE2457104B2/en
Withdrawn legal-status Critical Current

Description

derung der mechanischen Festigkeit an Stellen verminderter Steifigkeit verhindert.Prevents mechanical strength from being reduced in places of reduced stiffness.

Das textile Flächengebilde kann eine homogene oder inhomogene Struktur aufweisen. Die gleichmäßige Steifigkeit kann mit verschiedenen bekannten Arbeitsweisen erzielt werden, beispielsweise durch Imprägnierung mit einer versteifend wirkenden Masse oder mit einem vernetzbaren Polymer und nachträgliche Vernetzung, durch durchgehende oder stellenweise Beschichtung, durch Verwendung von Fäden oder Fasern mit größerer Steifigkeit als die übrigen Bestandteile des Textflgebildes oder durch Verbinden, beispielsweise Verkleben, zweier textiler Flächenge bilde.The textile fabric can have a homogeneous or inhomogeneous structure. The uniform rigidity can be known with various Working methods can be achieved, for example by impregnation with a stiffening mass or with a crosslinkable polymer and subsequent crosslinking, through continuous or in places coating, through the use of threads or fibers with greater rigidity than the other components of the textile fabric or by connecting, for example gluing, two textile fabrics.

Bei dem Verfahren nach dem Anspruch 1, welches nicht mechanisch wirkt, kann gegebenenfalls ein chemischer Abbau des Fasermaterials oder einer aufgebrachten versteifend wirkenden Masse stattfinden. Je nach der Art des Materials des Flächengebildes ist die jeweils geeignetste Einwirkung auszuwählen, welche die Steifigkeit definiert vermindert und die mechanische Festigkeit möglichst unverändert läßt.In the method according to claim 1, which does not act mechanically, a chemical degradation of the fiber material or of an applied stiffening mass can optionally take place. Ever Depending on the type of material of the sheet-like structure, the most suitable effect must be selected in each case the rigidity is reduced in a defined manner and the mechanical strength is as unchanged as possible.

Bei dem Verfahren nach Anspruch 2 wird das textile Flächengebilde von der Oberfläche her teilweise abgetragen, wodurch das Flächengewicht und die Dicke des Flächengebildes in den Zonen verminderter Steifigkeit verringert werden. Hierzu eignet sich insbesondere ein Schleifen, Fräsen, Bürsten, Schaben oder Sandstrahlen. Beim Sandstrahlen kann der mit Textilteilchen verunreinigte Sand in bekannter Weise gereinigt und dem Verfahren wieder zugeführt werden. Eine solche mechanische Arbeitsweise ist insbesondere für zwei- oder mehrschichtige Textilgebilde geeignet, bei denen an den Stellen verminderter Steifigkeit eine oder bei Mehrschichtgebilden mehrere Schichten vollständig abgetragen werden. Dabei bleibt bevorzugt eine der Schichten, welche eine ausreichende mechanische Festigkeit aufweist, unverletzt erhalten. Das durch das Abtragen des Flächengebildes entstehende feinteilige Material kann abgesaugt oder weggeblasen werden.In the method according to claim 2, the surface of the textile fabric becomes partially removed, whereby the weight per unit area and the thickness of the fabric in the zones is reduced Stiffness can be reduced. Grinding, milling, brushing and scraping are particularly suitable for this purpose or sandblasting. During sandblasting, the sand contaminated with textile particles can be removed in a known manner cleaned and fed back into the process. Such a mechanical mode of operation is particularly useful for two-layer or multi-layer textile structures suitable, in which one or more in the case of multi-layer structures at the points of reduced rigidity Layers are completely removed. In this case, one of the layers which has sufficient mechanical strength preferably remains undamaged obtain. The finely divided material resulting from the removal of the surface structure can be suctioned off or be blown away.

Weiter kann das textile Flächengebilde mit einem Gas oder einer Flüssigkeit in Berührung gebracht werden, das bzw. die chemisch aktiv ist und einen chemischen Abbau der Ausrüstung oder der textlien Fasern bewirkt oder diese löst. Dabei kann die Flüssigkeit aufgesprüht werden, wird jedoch bevorzugt durch das textile Flächengebilde hindurchgesaugt, was auch mit Gasen durchgeführt werden kann. Es kommen auch Gemische derartiger Gase und/oder Flüssigkeiten in Frage. Das Arbeiten in einem stationären Medium mit einem bewegten textlien Flächengebilde ist ebenfalls möglich, wobei jedoch die Abbauprodukte nicht wie im ersten Fall weggeführt werden, sondern sich konzentrieren.Furthermore, the textile fabric can be brought into contact with a gas or a liquid that is or are chemically active and causes a chemical degradation of the equipment or the textile fibers or dissolves them. The liquid can be sprayed on, but is preferably through the textile fabric is sucked through, which can also be done with gases. There come mixtures of such gases and / or liquids are also possible. Working in a stationary medium with a moving textile fabric is also possible, but the degradation products are not carried away as in the first case, but concentrate.

Das textile Flächengebilde kann schon bei seiner Herstellung so ausgerüstet oder mit einer Masse versehen werden, daß eine besondere Arbeitsweise besonders begünstigt wird. So kann ein Flächengebilde, wie dies bereits oben erwähnt ist, vor der Behandlung mit einem mechanisch wirkenden Mittel mit einer Substanz versehen werden, welche eine weitere unerwünschte Zerfaserung des Textilmaterials nach der Bearbeitung verhindert. Weiter kann das textile Flächengebilde auch mit einem durch eine der genannten Strahlungsarten zersetzbaren oder eine solche Zersetzung initiierenden Material versehen werden.The textile fabric can already be finished or provided with a mass during its production in such a way that a particular mode of operation is particularly favored. So can a flat structure, as already mentioned above, before treatment with a mechanically acting agent with a Substance are provided, which further undesirable defibration of the textile material after Processing prevented. Furthermore, the textile fabric can also be equipped with one of the above Types of radiation decomposable or such a decomposition initiating material are provided.

Die fcrfindungsgemäß hergestellten textlien Flächengebilde eignen sich insbesondere zur Herstellung von Versteifungseinlagen für Kleidungskstückteile, insbesondere für Hemden- und Blusenkragen.The textile fabrics produced according to the invention are particularly suitable for production of stiffening inserts for parts of clothing, in particular for shirt and blouse collars.

Ein besonderer Vorteil der Erfindung ist es, daß die Verminderung der Steifigkeit sowohl beim KonA particular advantage of the invention is that the reduction in rigidity in both the Kon fektionär als auch in einem anderen Betrieb erfolgen kann. Bisher wurden textile Flächengebilde mit über ihre Fläche unterschiedlicher Steifigkeit im allgemeinen in einem Betrieb hergestellt, welcher das bahnf örmige Material vom Textilhersteller oder -ausrüsteras well as in another company can. Up to now, flat textile structures with different stiffnesses over their area have generally been produced in a company which supplies the web-like material from the textile manufacturer or supplier bezog und dann an den Konfektionär lieferte. Beim erfindungsgemäßen Verfahren kann zwar in der bisherigen Reihenfolge vorgegangen werden, der Konfektionär kann aber auch das bahnförmige Material von gleichmäßiger Steifigkeit direkt beziehen, zu-and then delivered to the clothing manufacturer. In the case of the method according to the invention, it is possible to proceed in the previous order, but the manufacturer can also use the web-like material of uniform stiffness directly refer to,

-'" schneiden und die zonenweise Verminderung der Steifigkeit erst vor dem Vernähen herbeiführen. Beispielsweise kann eine Schleif- oder Fräsvorrichtung unmittelbar der Nähmaschine oder dem Nähautomaten vorgeschaltet werden.- '"cut and the zone-wise reduction of the Only bring about rigidity before sewing. For example, a grinding or milling device be connected directly upstream of the sewing machine or the automatic sewing machine.

-> Das nachfolgende Beispiel dient zur Veracschaulichung bestimmter Ausführungsformen der Erfindung.-> The following example serves to illustrate certain embodiments of the invention.

Beispielexample Textile Flächengebilde:Textile fabrics:

J« - Permanente mit Kunstharz appretierte Grundeinlage aus gebleichtem bzw. gefärbtem Baumwollgewebe; Flächengewicht 125, 250 g/m2 (Etacol).J «- permanent base insert finished with synthetic resin made of bleached or dyed cotton fabric; Weight per unit area 125, 250 g / m 2 (Etacol).

- Grundeinlage aus gebleichtem bzw. gefärbtem J"» Baumwollgewebe mit Doppelappretur, wobei- Basic insert made of bleached or dyed J "» cotton fabric with double finish, whereby die zweite Appretur nicht vernetzt ist; Flächengewicht 125, 250 g/m2 (Etaset).the second finish is not crosslinked; Weight per unit area 125, 250 g / m 2 (Etaset).

- Wirrvlies.- Tangled fleece.

Die Verminderung der Steifigkeit erfolgte einmalThe decrease in rigidity was done once

■»ο mit einem Fräser, das andere Mal mit einer Steinschleifscheibe der Korngröße 120, Durchmesser 27 mm, Drehzahl 10000 bis 12000 U/min. Die Vorschubgeschwindigkeit des textlien Flächengebildes betrug 70 bis 112 m/h. Es wurden verschiedene Ver-■ »ο with a milling cutter, the other time with a stone grinding wheel with a grain size of 120, diameter 27 mm, speed 10,000 to 12,000 rpm. The feed rate of the textile fabric was 70 to 112 m / h. There were various

·»■> suche mit unterschiedlichem Auflagedruck der Bearbeitungswerkzeuge vorgenommen. Das anfallende feinteilige Material wurde mit einer gewöhnlichen Absaugvorrichtung entfernt.· »■> search carried out with different contact pressure of the processing tools. The accruing finely divided material was removed with an ordinary suction device.

Es wurden Zonen mit verminderter Steifigkeit amThere were zones with reduced stiffness on the

>o Stoffrand mit einer Breite bis zu 7 mm und in der Stoffbahn mit einer Breite von 1,5 bis 3 mm hergestellt. Dabei wurden von Flächengebilden der Dicke 0,25 bis 0,40 mm jeweils 0,03 bis 0,05 mm abgetragen. Es wurde beobachtet, daß ein Teil der abgetrage-> o Fabric edge with a width of up to 7 mm and made in the fabric with a width of 1.5 to 3 mm. The thickness of the flat structures 0.25 to 0.40 mm each 0.03 to 0.05 mm removed. It was observed that some of the removed nen feinen Fasern sich in die Faser- bzw. Fadenzwischenräume des textlien Flächengebildes einlagert. Die besten Resultate wurden beim Arbeiten mit Schleifscheibe erreicht, wobei sowohl in gerader Linie wie auch nach bestimmten Schablonen in gebogenenNEN fine fibers are embedded in the fiber or thread interstices of the textile fabric. The best results were obtained when working with the grinding wheel, both in a straight line as well as curved according to certain templates

bo Linien geschliffen wurde.bo lines was sanded.

Die textlien Flächengebilde wurden weder während des Schleifens noch während des Fräsens überhitzt, und die Fertigprodukte weisen sowohl eine genügende Reiß- wie auch Biegefestigkeit auf.The textile fabrics were neither overheated during grinding nor during milling, and the finished products have sufficient tear strength as well as sufficient flexural strength.

Claims (12)

Patentansprüche:Patent claims: 1. Verfahren zur Herstellung eines textlien Flächengebildes, insbesondere einer Versteifungseinlage für Kleidungsstücke bzw. Kragen, welches nach vorbestimmten! Muster, gegebenenfalls durch die Anwendung von Wärme, zonenweise verminderte Steifigkeit aufweist, aus einem Flächengebilde gleichmäßiger Steifigkeit mit homogener oder inhomogener Struktur, dadurch gekennzeichnet, daß die Steifigkeit des Flächengebildes durch die Anwendung von Ultraviolettoder Infrarotstrahlung, Mikrowellen, Laserstrahlen, Plasmastrahl, radioaktiver Strahlung, Elektroerosion oder Ultraschall vermindert wird.1. A method for producing a textile fabric, in particular a stiffening insert for items of clothing or collars, which according to predetermined! Patterns, if necessary through the application of heat, in zones has reduced stiffness, from a sheet of uniform stiffness with homogeneous or inhomogeneous structure, characterized in that the rigidity of the flat structure through the use of ultraviolet or infrared radiation, microwaves, laser beams, Plasma jet, radioactive radiation, electrical discharge machining or ultrasound is reduced. 2. Verfahren zur Herstellung eines textlien Flächengebildes, insbesondere einer Versteifungseinlage für Kleidungsstücke bzw. Kragen, welches nach vorbestimmtem Muster zonenweise verminderte Steifigkeit aufweist, aus einem Flächengebilde gleichmäßiger Steifigkeit mit homogener oder inhomogener Struktur, dadurch gekennzeichnet, daß man die Dicke des Flächengebildes durch teilweises Abtragen des das Flächengebilde ausmachenden Materials vermindert.2. A method for producing a textile fabric, in particular a stiffening insert for items of clothing or collars, which having reduced stiffness in zones according to a predetermined pattern, made of a flat structure uniform rigidity with a homogeneous or inhomogeneous structure, characterized in that that you can increase the thickness of the fabric by partially removing the fabric constituting material decreased. 3. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch Schleifen vermindert.3. The method according to claim 2, characterized in that the rigidity by Grinding decreased. 4. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch Fräsen vermindert.4. The method according to claim 2, characterized in that the rigidity by milling reduced. 5. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch Bürsten vermindert.5. The method according to claim 2, characterized in that the rigidity by brushing reduced. 6. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch Schaben vermindert.6. The method according to claim 2, characterized in that the rigidity by scraping reduced. 7. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch Sandstrahlen vermindert.7. The method according to claim 2, characterized in that the rigidity by sandblasting reduced. 8. Verfahren nach Anspruch 2, dadurch gekennzeichnet, daß man die Steifigkeit durch eine chemische Behandlung vermindert, indem ein chemisch aktives Gas, eine chemisch aktive Flüssigkeit oder ein Gemisch hieraus zur Anwendung gelangt.8. The method according to claim 2, characterized in that the rigidity by a Chemical treatment diminishes by using a chemically active gas, a chemically active liquid or a mixture thereof is used. 9. Verfahren nach Anspruch 8, dadurch gekennzeichnet, daß man das Gas, die Flüssigkeit oder deren Gemisch durch das textile Flächengebilde hindurchsaugt.9. The method according to claim 8, characterized in that the gas, the liquid or their mixture sucks through the textile fabric. 10. Verfahren nach einem der Ansprüche 1 bis10. The method according to any one of claims 1 to 9, dadurch gekennzeichnet, daß das textile Flächengebilde vor oder nach der Behandlung imprägniert wird.9, characterized in that the textile fabric is impregnated before or after the treatment will. 11. Verfahren nach einem der Ansprüche 1 bis11. The method according to any one of claims 1 to 10, dadurch gekennzeichnet, daß das textile Flächengebilde vor oder nach der Behandlung beschichtet wird.10, characterized in that the textile fabric is coated before or after the treatment will. 12. Verfahren nach einem der Ansprüche 1 bis12. The method according to any one of claims 1 to 11, dadurch gekennzeichnet, daß das textile Flächengebilde in den Zonen verminderter Steifigkeit mit einer Substanz behandelt wird, welche den Zusammenhalt der Fasern und Fäden der Zonen verbessert.11, characterized in that the textile fabric is treated in the areas of reduced stiffness with a substance which the Cohesion of the fibers and threads of the zones is improved. Die Erfindung betrifft ein Verfahren zur Herstellung eines textlien Flächengebildes nach dem Oberbegriff des Anspruchs 1 bzw. des Anspruchs 2.The invention relates to a method for producing a flat textile structure according to the preamble of claim 1 or claim 2. Textile Flächengebilde, die über ihre Fläche zonenweise unterschiedliche Steifigkeit aufweisen, sind bekannt und werden nach verschiedenen Verfahren hergestellt. Beispielsweise werden mehrere Rächengebilde miteinander verbunden, wobei an Stellen geringerer Steifigkeit die Anzahl der Schichten kleiner ist als an den Stellen mit höherer Steifigkeit. Abgesehen davon, daß dieses Verfahren sehr arbeits- und materialintensiv ist, sind die erhaltenen Flächengebilde voluminös und schwer.Textile fabrics which have different stiffness in zones over their surface are known and are manufactured by various processes. For example, several forms of revenge are connected to one another, with at points lower stiffness the number of layers is smaller than at the points with higher stiffness. Apart from that the fact that this process is very labor-intensive and material-intensive are the result of the planar structures voluminous and heavy. Nach einem anderen bekannten Verfahren wird eine textile Unterlage mit einer Beschichtung versehen, wobei die nicht zu beschichtenden Zonen, d. h. jene, die weniger steif werden sollen, mit einer Schablone abgedeckt werden. Dieses Verfahren ist auch sehr arbeitsintensiv, da die Beschichtung nur am zugeschnittenen Textil gut erfolgen kann, welches einzeln und von Hand in die Beschickungsvorrichtung eingelegt werden muß.According to another known method, a textile base is provided with a coating, the zones not to be coated, d. H. those that should be less stiff with a stencil to be covered. This process is also very labor intensive as the coating is only cut to size Textile can be done well, which is inserted individually and by hand into the loading device must become. Aus der DE-OS 2116 631 ist es bekannt, das textile Flächengebilde mit einer vernetzbaren Substanz zu versehen und letztere durch Wärmeeinwirkung zu vernetzen, wobei Stellen, die eine verminderte Steifigkeit aufweisen sollen, der Wärmebehandlung nicht unterworfen werden. Bei diesem Verfahren ist es schwierig, die genauen Bereiche der Vernetzung bzw. der Nicht-Vernetzung einzuhalten. Das nicht-vernetzte Harz muß aus dem Flächengebilde ausgewaschen werden, wonach letzteres noch getrocknet und gebügelt wird, d. h. nach dem Vernetzen sind noch drei zusätzliche Arbeitsgänge auszuführen. Außerdem sind die ausgerüsteten, jedoch noch nicht vernetzten Textilien nicht unbeschränkt lagerbar, da mit der Zeit Selbstvernetzung erfolgen kann.From DE-OS 2116 631 it is known that the textile To provide flat structures with a crosslinkable substance and the latter by the action of heat cross-link, with points that are supposed to have a reduced rigidity, the heat treatment not be subjected. With this method it is difficult to identify the exact areas of the mesh or of non-networking to be observed. The uncrosslinked resin must wash out of the sheet after which the latter is dried and ironed, d. H. after networking are still perform three additional operations. In addition, they are equipped, but not yet networked Textiles cannot be stored indefinitely as they can self-crosslink over time. Aus dem DE-GM 1971504 ist es bekannt, die Schwächung durch Wärmeeinwirkung dadurch herbeizuführen, daß das Flächengebilde mit einem beheizten Werkzeug beaufschlagt wird. Auch kann die Schwächung durch das Einschneiden oder Einstanzen von Schlitzen oder Löchern erfolgen, wie dies aus dem DE-GM 1 892201 und der DE-OS 2020451 bekannt ist. Hierbei entsteht aber keine gleichmäßige Schwächung des zu schwächenden Bereiches, sondern es entstehen lokal stark geschwächte Zonen neben lokal gar nicht geschwächten Zonen.From DE-GM 1971504 it is known that To bring about weakening by the action of heat that the flat structure with a heated Tool is applied. The weakening can also be achieved by cutting or punching of slots or holes, as known from DE-GM 1 892201 and DE-OS 2020451 is. However, this does not result in a uniform weakening of the area to be weakened, but rather it locally strongly weakened zones arise next to locally not weakened zones. Demgegenüber liegt der Erfindung die Aufgabe zugrunde, ein Verfahren der eingangs bezeichneten Gattung zu schaffen, mit dem eine im wesentlichen gleichmäßige Schwächung des zu schwächenden Bereiches auf herstellungstechnisch möglichst einfache und exakte Weise erreicht wird.In contrast, the invention is based on the object of providing a method of the type described at the outset To create a species with which a substantially uniform weakening of the area to be weakened is achieved in a manufacturing technology that is as simple and exact as possible. Die Lösung dieser Aufgabe erfolgt durch die kennzeichnenden Merkmale des Anspruchs 1 bzw. des Anspruchs 2.This problem is solved by the characterizing features of claim 1 or of Claim 2. Als textile Flächengebilde kommen dabei sowohl Gewebe, Gewirke und Vliese als auch mehrschichtige Gebilde, vorzugsweise solche mit zwei textlien Schichten, in Frage. Solche zwei- oder mehrschichtigen Gebilde werden insbesondere wegen ihrer guten Formstabilität bevorzugt. Sie können gefärbt und je nach Bedarf beispielsweise schmutz- oder wasserabstoßend, knitterarm oder feuerhemmend ausgerüstet sein. Von besonderer Bedeutung ist eine Ausrüstung, die ein zu starkes Ausfransen oder eine andere Art von Zerfall des Textilgebildes und damit eine Vermin-Woven fabrics, knitted fabrics and nonwovens as well as multilayered fabrics are used as textile fabrics Structures, preferably those with two textile layers, are in question. Such two-layer or multi-layer Structures are particularly preferred because of their good dimensional stability. They can be colored and depending For example, if required, it is dirt-repellent or water-repellent, crease-resistant or fire-retardant be. Of particular importance is equipment that has excessive fraying or some other type of of the disintegration of the textile structure and thus a reduction in
DE2457104A 1973-12-21 1974-12-03 Process for the production of textile fabrics with zone-wise reduced stiffness Withdrawn DE2457104B2 (en)