DE2453132A1 - METHOD FOR MANUFACTURING HOLLOW BODIES FROM VULCANIZED ELASTOMERS - Google Patents
METHOD FOR MANUFACTURING HOLLOW BODIES FROM VULCANIZED ELASTOMERSInfo
- Publication number
- DE2453132A1 DE2453132A1 DE19742453132 DE2453132A DE2453132A1 DE 2453132 A1 DE2453132 A1 DE 2453132A1 DE 19742453132 DE19742453132 DE 19742453132 DE 2453132 A DE2453132 A DE 2453132A DE 2453132 A1 DE2453132 A1 DE 2453132A1
- Authority
- DE
- Germany
- Prior art keywords
- mold
- temperature
- extruder
- heated
- blow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Dr. F. Zumsteln sen. - Dr. E. Assmann Dr. R. Koenlgsberger - Dipl.-Phys. R. Holzbauer « Dr. F. Zumsteln Jun.Dr. F. Zumsteln sen. - Dr. E. Assmann Dr. R. Koenlgsberger - Dipl.-Phys. R. Holzbauer «Dr. F. Zumsteln Jun.
PATENTANWÄLTEPATENT LAWYERS
TELEFON: SAMMEL-NR. 22 5341TELEPHONE: COLLECTIVE NO. 22 5341
TELEX 529979 . 8 MÜNCHEN 2.TELEX 529979. 8 MUNICH 2.
BRAUHAUSSTRASSE 4 TELEGRAMME: ZUMPATBRAUHAUSSTRASSE 4 TELEGRAMS: ZUMPAT
POSTSCHECKKONTO:
MÜNCHEN 91139-809, BLZ 70010O 80CHECK ACCOUNT:
MUNICH 91139-809, BLZ 70010O 80
BANKKONTO: BANKHAUS H. AUFHÄUSER
KTO.-NR. 397997. BLZ 70030600BANK ACCOUNT: BANKHAUS H. AUFHÄUSER
ACCOUNT NO. 397997. BLZ 70030600
SC 4339
U/hiiSC 4339
U / hii
RHONE-POULENC S.A.,. Paris / Frankreich' Verfahren zur Herstellung von Hohlkörpern aus vulkanisiertenRHONE-POULENC S.A.,. Paris, France' Process for the production of hollow bodies from vulcanized
Elastomeren.Elastomers.
Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung von Hohlkörpern aus vulkanisierten Siliconelastomeren und insbesondere von solchen, deren öffnung zu eng ist, um eine Formung durch Spritzung um einen Kern zu gestatten, beispielsweise von verschiedenen Flaschen und Fläschchen.The present invention relates to a method for the production of hollow bodies from vulcanized silicone elastomers and in particular of those whose opening is too narrow to allow a shaping by injection around a core, for example from various bottles and vials.
Die Herstellung von Gegenständen aus Siliconelastomeren wird im allgemeinen nach Techniken, wie Schleudergießen, Tiefziehen oder Spritzung vollzogen. Durch diese letztere Technik, die industriell die interessanteste ist, kann man jedoch nur Gegenstände einfacherer Form mit unbedeutendereren öffnungen in Form einer Hinterschneidung erhalten.The manufacture of articles from silicone elastomers is generally carried out by techniques such as centrifugal casting, deep drawing or injection completed. However, this latter technique, which is the most interesting industrially, can only be used for objects simpler shape with more insignificant openings in shape received an undercut.
Für verschiedene Anwendungen, insbesondere auf dem Gebiet der nicht herkömmlichen Verpackung und auf mit der Medizin verwandten Gebieten, besteht ein Bedarf art "den vorstehend definierten Hohlkörpern aus Siliconelastomeren, die durch die üblicher-For various uses, particularly in the field of non-conventional packaging and medicine-related Areas, there is a need type "the hollow bodies defined above made of silicone elastomers, which by the usual-
509821/0946509821/0946
weise verwendeten Techniken nicht erhalten werden können, beispielsweise an Taschen für die Aufbewahrung von Blut oder anderen biologischen Flüssigkeiten bei sehr niedriger Temperatur und an Behältern für Perfusionsflüssigkeiten.wisely used techniques cannot be obtained, for example on bags for the storage of blood or others biological fluids at very low temperature and on containers for perfusion fluids.
Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung von Hohlkörpern aus Elastomeren, ausgehend von in der Wärme vulkanisierbaren Zusammensetzungen, insbesondere. Siliconen, das dadurch gekennzeichnet ist, daß man unter Druck die kalte,nicht vulkanisierte Zusammensetzung"in einen Extruder einbringt, in der Kälte (vorzugsweise unterhalt) von 5O0O) einen im allgemeinen röhrenförmigen Vorformling (Blasrohling) extrudiert, der erhalten oder in eine auf eine die Vulkanisation gestattende Temperatur erwärmte Form transportiert wird, den Gegenstand in der erwärmten Form bis zu dem gewünschten Vulkanisationsgrad formt und dann den Hohlkörper entformt. Im allgemeinen ist die Form auf eine Temperatur zwischen 100 und 250° erwärmt, wobei die Verweilzeit von 1 bis 10 Minuten für TOQ0C bis zu 5 bis 30 Sekunden für 25Q°C variiert.The present invention relates to a process for the production of hollow bodies from elastomers, starting from compositions which can be vulcanized in the heat, in particular. Silicones, which is characterized in that the cold, unvulcanized composition "is introduced into an extruder under pressure, in which cold (preferably maintenance) of 50 0 O) a generally tubular preform (blow molding) is extruded, which is obtained or in a is transported to a heated mold that allows vulcanization, the object is shaped in the heated mold to the desired degree of vulcanization and then the hollow body is removed from the mold 10 minutes for TOQ 0 C up to 5 to 30 seconds for 25Q ° C.
Die Vorrichtung, die die Durchführung des erfindungsgemäßen Verfahrens gestattet, umfaßt im wesentlichen einen Extruder mit einer Vorrichtung für eine kontinuierliche Beschickung unter Druck, eine ringförmige Spritzdüse und eine für das Blasformen in der Wärme geeignete Form.The device that carries out the method according to the invention Permitted, essentially comprises an extruder with a device for continuous feeding underneath Pressure, an annular spray nozzle and a mold suitable for hot blow molding.
Es kann jeder für die Bearbeitung eines Elastomeren geeigneter Extruder verwendet werden. Jedoch besitzt dieser Extruder vorteilhafterweise eine Länge zwischen dem 10- und 25-fachen des Durchmessers der Schnecke,Any extruder suitable for processing an elastomer can be used. However, this extruder advantageously has a length between 10 and 25 times the diameter of the screw,
Dieser Extruder arbeitet bei Raumtemperatur ohne Zufuhr von Energie, gegebenenfalls mit einer Kühlvorrichtung, wobei die Temperatur des Materials 5O0C nicht überschreiten darf.This extruder is carried out at room temperature without addition of energy, optionally with a cooling device, wherein the temperature of the material may not exceed 5O 0 C.
Das Profil der Schnecke oder der Schnecken im Falle eines Extruders mit einer mehrgängigen Schnecke ist nicht kritisch. Es umfaßt im allgemeinen eine zylindrische Beschickungszone, eineThe profile of the screw or screws in the case of an extruder with a multi-flight screw is not critical. It generally comprises a cylindrical feed zone, one
509821/0946509821/0946
konische Kompressionszone und eine zylindrische Homogenisierungszone.Vorzugsweise ist die Schneckengangtiefe der Beschickungszone angesichts der Eingabe des Produktes, das im allgemeinen in Form eines Blockes oder Stranges vorliegt, relativ gering.conical compression zone and a cylindrical homogenization zone. Preferably, the screw flight depth of the feed zone, given the input of the product, is generally is in the form of a block or strand, relatively low.
Der Extruder wird durch Schneckenvorrichtungen, mit Hilfe eines Kolbens oder mit Hilfe eines dicht abschließenden Walzenförderers beschickt. Derartige Vorrichtungen sind insbesondere in der deutschen. Offenlegungsschrift 2 141 421 oder in der französischen Patentanmeldung 2 087 546 beschrieben.The extruder is driven by screw devices, with the aid of a piston or with the aid of a tightly sealed roller conveyor loaded. Such devices are particularly in the German. Offenlegungsschrift 2 141 421 or in French Patent application 2,087,546.
Ist der Extruder horizontal, so ist ein Winkelkopf erforderlich, damit der Vorformling vertikal extrudiert wird. Dieser Winkelkopf kann nach der Dornhalterung eine Zone für eine erneute Komprimierung enthalten, die es gestattet, die in dem Materialstrom durch die Befestigungsflügel der Dornhalterung hinterlassenen Spuren auszulöschen.If the extruder is horizontal, an angle head is required so that the parison is extruded vertically. This angle head may include a recompression zone after the mandrel support to allow those in the stream of material to wipe out traces left by the fastening wings of the mandrel holder.
Eine ringförmige Spritzdüse, deren Querschnitt von der Form und den Dimensionen des herzustellenden Gegenstandes abhängt, beendet den Winkelkopf.An annular spray nozzle, the cross-section of which depends on the shape and dimensions of the object to be manufactured, ends the angle head.
Der den Extruder verlassende Vorformling wird dann zwischen die beiden Backen einer metallischen Form genommen, die mit
Hilfe irgendeines geeigneten Mittels, wie eines Heizrnediums, mit Hilfe von in die Masse eingebetteten Widerständen oder
Heizstiften auf eine Temperatur," die von dem extrudierten Material abhängt, jed<
liegt, erwärmt ist.The preform leaving the extruder is then taken between the two jaws of a metal mold which, with the aid of any suitable means, such as a heating medium, with the aid of resistors or heating pins embedded in the mass, is brought to a temperature which depends on the material being extruded <
is heated.
terial abhängt, jedoch im allgemeinen zwischen 100 und 25O Cdepends on the material, but generally between 100 and 25O C
Die Extrusionsdauer eines Vorformlings ist im allgemeinen kürzer als die Vulkanisationsdauer und es ist im allgemeinen vorteilhaft, einen Satz Formen auf eine Vorrichtung mit wechselweiser oder rotierender Bewegung mit vertikaler oder horinzontaler Achse aufzubringen.The extrusion time of a preform is generally shorter than the vulcanization time and it is generally advantageous to have a set of molds on a device with alternating or rotating movement with a vertical or horizontal axis.
Gemäß einer Variante des Verfahrens,die es gestattet, Gegenstände großer Dimensionen und mehr oder minder komplexer FormenAccording to a variant of the method that allows objects large dimensions and more or less complex shapes
509821/0946509821/0946
zu erhalten, transportiert man mechanisch oder manuell jeden Vorformling in eine erwärmte, vom Betrieb des Extruders völlig unabhängige Form.to get, one transports each one mechanically or manually Preform into a heated mold that is completely independent of the operation of the extruder.
Die Formen besitzen vorteilhafterweise eine nicht glatte innere Oberfläche, die beispielsweise durch Sandstrahlen behandelt wurde, um Einschlüsse von Luft zu vermeiden und es dem Vorformling zu ermöglichen, sich an die ganze Oberfläche der Form anzuschließen.The molds advantageously have a non-smooth inner one Surface that has been treated, for example, by sandblasting, in order to avoid entrapping air and delivering it to the preform allow to join the whole surface of the form.
Eine Vorrichtung für das Blasformen, wie eine Blasdüse, ein Blasrohr oder ein Blasröhrchen, die ihrerseits auf eine Temperatur zwischen 100 und 200 C erwärmt sein können oder nicht, gestattet es, das Gas, das seinerseits vorerwärmt sein kann oder nicht, einzuführen.A device for blow molding, such as a blow nozzle, a blow pipe or a blowpipe, which in turn may or may not be heated to a temperature between 100 and 200 C it is necessary to introduce the gas, which in turn may or may not be preheated.
Der Druck dieses Gases liegt im allgemeinen zwischen 1 und 10 Bar. Die Geschwindigkeit des Blasens muß ausreichend langsam sein, um ein Zerreißen des Vorformlings zu vermeiden, dessen mechanische Eigenschaften sehr schwach sind.The pressure of this gas is generally between 1 and 10 bar. The rate of blowing must be slow enough to avoid tearing the parison, its mechanical Properties are very weak.
Man verwendet im allgemeinen komprimierte Luft als Gas für das Blasformen.Compressed air is generally used as a gas for blow molding.
Der Formgegenstand verbleibt in der Form während einer Zeitdauer, die gemäß der Temperatur der Form und gemäß der Dicke des hergestellten Gegenstandes variiert. Die für die Vulkanisation des Siliconelastomeren erforderliche Zeit variiert im allgemeinen zwischen 5 und 30 Sekunden bei 250 C (z.B. 15 Sekunden) und 1 bis 10 Minuten bei 1000C (z.B. 5 Minuten).The molded article remains in the mold for a period of time which varies according to the temperature of the mold and according to the thickness of the manufactured article. The time required for the vulcanization of the silicone elastomer generally varies between 5 and 30 seconds at 250 ° C. (for example 15 seconds) and 1 to 10 minutes at 100 ° C. (for example 5 minutes).
Die Form wird darauf geöffnet und der Hohlkörper durch geeignete automatische oder manuelle Mittel aus ihr entnommen.The mold is then opened and the hollow body is removed from it by suitable automatic or manual means.
Im Falle von Stücken mit großen Dimensionen und komplexer Form, bei denen man manuell arbeiten muß, kann es vorteilhaft sein, die Form zumindest teilweise vor der Entnahme des geformten Stückes abzukühlen. In the case of pieces with large dimensions and complex shapes that require manual work, it can be advantageous to use the To cool the mold at least partially before removing the shaped piece.
509821/0946509821/0946
In dem erfindungsgemäßen Verfahren kann man beispielsweise in der Wärme vulkanisierbare Siliconzusammensetzungen verwenden, die im allgemeinen auf das Gewicht bezogen je 100 Teile Diorganopolysiloxanharz mit einer Viskosität von mehr als 1000 Poise bei 25 C,bestehend im wesentlichen aus Diorganosiloxygruppierungen, die an jedem Kettenende durch eine Triorganosiloxy-, Hydroxy- oder Alkoxygruppe mit 1-4 Kohlenstoffatomen blockiert.sind,enthalten: 5 bis 100 Gewichtsteile anorganische Füllstoffe, die mit Organosiliciumverbindungen behandelt sein können oder nicht (z.B. gemäß der französischen Patentschrift 1 234 245), 0 bis 20 Teile eines die Strukturbildung verhindernden Mittels auf Organosiliciumbasis,In the process according to the invention, for example, in use heat vulcanizable silicone compositions generally based on weight per 100 parts of diorganopolysiloxane resin with a viscosity of more than 1000 poise at 25 C, consisting essentially of diorganosiloxy groupings, at each chain end by a triorganosiloxy, hydroxy or Alkoxy groups with 1-4 carbon atoms are blocked, contain: 5 to 100 parts by weight of inorganic fillers made with organosilicon compounds may or may not have been treated (e.g. according to French patent specification 1 234 245), 0 to 20 parts of a structure preventing agent based on organosilicon,
0 bis 20 Teile Pigmente und/oder Stabilisatoren und 0,2 bis 5 Teile Vulkanisationsmittel.0 to 20 parts of pigments and / or stabilizers and 0.2 to 5 parts of vulcanizing agents.
Die Diorganopolysiloxanharze enthalten im allgemeinen als organische an die Siliciumatome gebundene Reste, solche die ausgewählt sind aus der Gruppe, bestehend aus den fluorierten oder nicht-fluorierten Niedrigalkylresten, wie Methyl, Äthyl, Propyl, J5,3i3-Trifluorpropyl oder den Vinyl- oder Phenylresten.The diorganopolysiloxane resins generally contain as organic radicals bonded to the silicon atoms, those selected from the group consisting of the fluorinated or non-fluorinated lower alkyl radicals, such as methyl, ethyl, propyl, J5,3i3-trifluoropropyl or the vinyl or phenyl radicals.
Die Verfahren zur Herstellung dieser Harze sind gut bekannt. Man kann beispielsweise ein solches verwenden, das darin besteht, lineare und/oder cyclische Diorganopolysiloxane mit niedrigen. Molekulargewichten mit Hilfe von alkalischen oder sauren Katalysatoren und in Gegenwart einer geeigneten Menge Wasser, Alkoholen oder Organosiliciumverbindungen zur Einstellung des Molekulargewichtes durch Blockierung der Kettenenden zu polymerisieren (US-Patentschrift 2 954 357, französische PatentschriftenThe methods of making these resins are well known. For example, one can use one that consists in linear and / or cyclic diorganopolysiloxanes with low. Molecular weights using alkaline or acidic catalysts and in the presence of a suitable amount of water, alcohols or organosilicon compounds to adjust the molecular weight polymerize by blocking the chain ends (US Pat. No. 2,954,357, French patents
1 108 764, 1 134 005, 1 198 749, 1 226 745).1 108 764, 1 134 005, 1 198 749, 1 226 745).
Als Füllstoffe verwendet man im allgemeinen calciniertes oder gefälltes Siliciumdioxyd, Ruß, Diatomeenerde,Quarzmehl, Oxyde, des Eisens oder des Titans oder Calciumcarbonat.Calcined or precipitated fillers are generally used as fillers Silicon dioxide, soot, diatomaceous earth, quartz powder, oxides, des Iron or titanium or calcium carbonate.
Als die Strukturbildung verhinderndes Mittel (oder Plastifiziert mittel) verwendet man vorzugsweise Silane mit hydrolysierbarenAs a structure preventing agent (or plasticized medium) one preferably uses silanes with hydrolyzable
5098 21/09465098 21/0946
Gruppen oder hydroxylierte oder alkoxylierte Diorganopolysiloxanöle mit geringer Viskosität.Groups or hydroxylated or alkoxylated diorganopolysiloxane oils with low viscosity.
Gegebenenfalls kann die Zusammensetzung auch klassische Pigmente, wie die Oxyde des Chroms oder Phthalocyanine und/oder Stabilisatoren, wie die Octoate des Eisens, öers oder Mangans enthalten.If necessary, the composition can also contain classic pigments, such as the oxides of chromium or phthalocyanines and / or stabilizers, like the octoates of iron, orer or manganese.
Als Vulkanisationsmittel kann man die üblichen organischen Peroxyde, beispielsweise Cumylperoxyd, Benzoylperoxyd, Tert.-butylperbenzoat, Tert.-butylperoxyd und das >,4-Dichlorbenzoylperoxyd verwenden.The usual organic peroxides, for example cumyl peroxide, benzoyl peroxide, tert-butyl perbenzoate, Tert-butyl peroxide and the>, 4-dichlorobenzoyl peroxide use.
Das erfindungsgemäße Verfahren besitzt eine Anzahl an Vorteilen, unter denen man nennen kann:The method according to the invention has a number of advantages, among which one can mention:
Die Möglichkeit, mit einer geeigneten Vorrichtung erhöhte Produktionsleistungen zu erhalten,The possibility of increased production output with a suitable device to obtain,
die Möglichkeit, Hohlkörper großer Dimensionen und ohne Drehachse zu erhalten, die durch eine andere Technik nicht erhalten werden können.the possibility of obtaining hollow bodies of large dimensions and without an axis of rotation, which cannot be obtained by another technique can be.
Die folgenden Beispiele erläutern die Erfindung.The following examples illustrate the invention.
Herstellung einer Flasche (Gewicht 42 g, Volumen 550 cm , Durchmesser 60 mm, Höhe 220 mm).Production of a bottle (weight 42 g, volume 550 cm, diameter 60 mm, height 220 mm).
Man bereitet einen Extruder, der mit einem Winkelkopf und einer für die Beschickung mit Elastomeren geeigneten Vorrichtung versehen ist, vor.An extruder is prepared which is provided with an angle head and a device suitable for loading elastomers is before.
Die Schnecke besitzt einen Durchmesser von 4o mm und eine Länge von 800 mm. Ihr Gang beträgt 40 mm. Die Schnecke ist über >6 cm zylindrisch)entsprechend einer Beschickungszone, dann ist sie über 24 cm konisch, entsprechend einer Kompressionszone und schließlich ist sie über 20 cm erneut zylindrisch)entsprechendThe screw has a diameter of 40 mm and a length of 800 mm. Their gait is 40 mm. The snail is over > 6 cm cylindrical) corresponding to a loading zone, then is it is conical over 24 cm, corresponding to a compression zone and finally it is again cylindrical over 20 cm) accordingly
509 8 21/0946509 8 21/0946
einer Homogenisierungszone. Die SchneckengangtieFe beträgt am Eingang 6 mm. Die Schnecke dreht sich mit 20 Umdrehungen pro Minute« Der Kompressionsgrad beträgt um 2,4.a homogenization zone. The worm thread depth is am Entrance 6 mm. The screw rotates at 20 revolutions per minute. The degree of compression is around 2.4.
Der Winkelkopf enthält nach der Dornhalterung eine Zone für eine erneute Kompression, um die durch die Flügel des Kopfes hinterlassenen Spuren auszulöschen. Der Durchmesser des Dorns beträgt 20 mm. Eine ringförmige Spritzdüse mit einem äußeren Durchmesser von 24,2 mm beendet den Winkelkopf.After the mandrel mount, the angled head includes a recompression zone around that left by the wings of the head To wipe out traces. The diameter of the mandrel is 20 mm. An annular spray nozzle with an outer diameter of 24.2 mm ends the angle head.
Man bringt in den Extruder die in Form eines Stranges mit einem Durchmesser von ungefähr 7 cm vorliegende vulkanisierbare Zusammensetzung mittels eines Akkumulators, der es gestattet, das Material unter Druck zu halten, ein.The vulcanizable composition, which is in the form of a strand with a diameter of approximately 7 cm, is introduced into the extruder by means of an accumulator that allows the material to be kept under pressure.
Diese Vorrichtung ist ein zylindrisches Rohr mit einem Durchmesser von 7 cm und einer Höhe von 35 cm. Ein mit Druckluft betriebener Kolben gestattet es, das Material unter einem Druck von ungefähr 40 bis 50 Bar in die Schnecke zu drücken.This device is a cylindrical tube with a diameter of 7 cm and a height of 35 cm. One powered by compressed air Piston allows the material to be forced into the screw under a pressure of approximately 40 to 50 bar.
Ein Ventilationssystem verhindert, daß die Temperatur von» Extruder bis zur Spritzdüse über 5O0C ansteigt. Der kontinuierlich extrudierte Vorformling wird zwischen den beiden Teilen einer erwärmten und durch vier Heizstifte von 750 Watt, die in Bezug auf die Formhöhlung symmetrisch angeordnet sind, auf 18O°C regulierten Form festgehalten. Der Vorformling wird unmittelbar an der Spritzdüse durch Abreißen abgetrennt.A ventilation system prevents the temperature by "extruder rises up to the spray nozzle about 5O 0 C. The continuously extruded preform is held between the two parts of a heated mold that is regulated to 180 ° C. by four 750 watt heating pins that are symmetrically arranged with respect to the mold cavity. The preform is torn off directly at the spray nozzle.
Die Form gelangt dann in Kontakt mit dem Blasrohr, das zur Kalibrierung des Halses des Gegenstandes und zur Sicherstellung des Lufteintrittes in das Innere des Vorformlings dient und durch einen Heizstift von 500 Watt auf 18O°C erwärmt ist. Die Luft wird unter einem Druck von 6 Bar eingeführt.The mold then comes into contact with the blowpipe, which is used for calibration of the neck of the object and to ensure the entry of air into the interior of the preform and through a 500 watt heater is heated to 180 ° C. The air is introduced under a pressure of 6 bar.
Der Gegenstand verbleibt 20 Sekunden in der Form entsprechend der Zeit,während der die Vernetzung des Siliconelastomeren bewirkt wird. Der Gegenstand wird darauf durch einen Strahl komprimierterThe object remains in the shape according to the for 20 seconds Time during which the silicone elastomer is crosslinked. The object is then compressed by a jet
509821/0946509821/0946
Luft.aus der Form ausgestoßen.Air. Expelled from the mold.
Die vulkanisierbare Zusammensetzung umfaßt (bezogen auf das Gewicht):The vulcanizable composition comprises (by weight):
100 Teile eines Diorganopolysiloxanharzes mit einer Viskosität von 20 000 000 cP bei 250C, dargestellt durch eine Kette von 99*7 % Gruppierungen -(CH^)2SiO und 0,3 % Gruppierungen100 parts of a diorganopolysiloxane resin with a viscosity of 20,000,000 cP at 25 ° C., represented by a chain of 99 * 7 % groups - (CH ^) 2 SiO and 0.3 % groups
-CH=CH-SiO- , die an jedem Ende durch eine Gruppierung-CH = CH-SiO- represented by a grouping at each end
-(CH,),SiOn r- blockiert ist,
3 3 0,5 ' - (CH,), SiO n r- is blocked,
3 3 0.5 '
J>6 Teile eines calcinierten Siliciumdioxyds mit großer fischer Oberfläche (300 m /g), das durch Octamethylcyclotetrasiloxan behandelt ist, J> 6 parts of a calcined silica with a large fischer surface area (300 m / g), which is treated with octamethylcyclotetrasiloxane,
.1 Teil eines hydroxylierten Dimethylpolysiloxanöles mit einer Viskosität von 50 cP bei 250C mit 10 Gew.-% Hydroxylgruppen, die an Siliciumatome gebunden sind, und.1 part of a hydroxylated Dimethylpolysiloxanöles having a viscosity of 50 cP at 25 0 C with 10 wt -.% Hydroxyl groups bonded to silicon atoms, and
1,6 Teile einer Paste mit 50 Gew.-% 2,4-Dichlorbenzoylperoxyd in einem Dimethylpolysiloxanöl mit einer Viskosität von 1 000 cP bei 25 C, das an jedem Kettenende durch eine Gruppierung c- blockiert ist.1.6 parts of a paste containing 50 wt -.% Of 2,4-Dichlorbenzoylperoxyd in a dimethylpolysiloxane with a viscosity of 1000 cP at 25 C, which is c- blocked at each chain end by a grouping.
Die Gesamtdauer des Herstellungszyklusses einer Flasche beträgt weniger als 30 Sekunden.The total manufacturing cycle time for a bottle is less than 30 seconds.
Der Herstellungszyklus ist voll automatisch.The manufacturing cycle is fully automatic.
Man verwendet die gleiche Siliconzusammensetzung und den gleichen Extruder wie in dem vorangegangenen Beispiel, wobei man jedoch ein Rohr mit einem äußeren Durchmesser von 35 mm und einem inneren Durchmesser von 27 mm extrudiert. Man verwendet eine Form, deren Höhlung die Form eines U-Rohres mit einem Durchmesser von "Jh mm und einer entwickelten Länge von 5OO mm besitzt.The same silicone composition and extruder are used as in the previous example, except that a tube with an outer diameter of 35 mm and an inner diameter of 27 mm is extruded. Using a mold whose cavity has the shape of a U-tube having a diameter of "century mm and a developed length of 5OO mm.
509821/0946509821/0946
Man bringt manuell den Vorformling mit einer Länge von 520 mm in diese Form und verriegelt die Form, indem man die beiden Enden des Vorformlings klemmt. Man bläst Druckluft von 6 Bar durch ein nicht erwärmtes Blasrohr ein.The preform with a length of 520 mm is brought in manually into this shape and locked the shape by putting the two Stuck ends of the preform. Compressed air of 6 bar is blown in through an unheated blowpipe.
Man erwärmt es dann auf 150°C und beläßt 5 Minuten bei dieser Temperatur. Man beendet das Erwärmen und öffnet die Form. Man entnimmt eine Tasche mit einem Volumen von ungefähr 2 Liter, die als Behälter für eine Perfusionsflüssigkeit verwendbar ist.It is then heated to 150 ° C. and left there for 5 minutes Temperature. Stop heating and open the mold. Man takes a bag with a volume of about 2 liters, which can be used as a container for a perfusion liquid.
509821/0946509821/0946
Claims (1)