DE2450435C2 - Luminous material provided with a cladding layer and process for its manufacture - Google Patents
Luminous material provided with a cladding layer and process for its manufactureInfo
- Publication number
- DE2450435C2 DE2450435C2 DE19742450435 DE2450435A DE2450435C2 DE 2450435 C2 DE2450435 C2 DE 2450435C2 DE 19742450435 DE19742450435 DE 19742450435 DE 2450435 A DE2450435 A DE 2450435A DE 2450435 C2 DE2450435 C2 DE 2450435C2
- Authority
- DE
- Germany
- Prior art keywords
- phosphor
- oxide
- phosphors
- tungsten
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
zeichnet daß der Leuchtstoff mit pulverförmiger!! 20 lung von großen Mengen solcher ummantelter Leucht-Wolfram-Vl-Oxid gleichmäßig vermischt wird und stoffe ergeben sich gerade in dieser Hinsicht Schwierigdann diese Mischung bei Temperaturen zwischen ketten.draws that the phosphor with powdery !! 20 treatment of large quantities of such coated luminous tungsten VI oxide is mixed evenly and substances are difficult in this regard this mixture at temperatures between chains.
100° C und 1300° C über eine Zeit von 10 Minuten bis Der Erfindung liegt die Aufgabe zugrunde, einen neu-100 ° C and 1300 ° C over a period of 10 minutes to The invention is based on the object of a new
10 Stunden geglüht wird. artigen ummantelten Leuchtstoff sowie ein neuartiges,Is annealed for 10 hours. like coated fluorescent material as well as a new,
5. Verfahren nach Anspruch 4. dadurch gekenn- 25 einfaches Verfahren zur Herstellung solcher Leuchtzeichnet, daß die Mischung mit trockenen Kompo- stoffe anzugeben, das auch größere Leuchtstoffmengen5. The method according to claim 4. characterized marked 25 simple method for producing such luminous characters, that the mixture with dry composites indicate that also larger quantities of phosphor
gut reproduzierbar herzustellen gestattet, und das mit guter Genauigkeit die Stärke der Umm^nteiungsschicht zu beeinflussen gestattetPermitted to manufacture in a well reproducible manner, and that with good accuracy, the thickness of the coating layer allowed to influence
jo Gemäß der Erfindung wird vorgeschlagen, daß der Wolfram-Vl-Oxidanteil zur Einstellung des Anregungsschwellwertes des Leuchtstoffes 28 bis 38 Gewichtsprojo According to the invention it is proposed that the Tungsten VI oxide content for setting the excitation threshold value of the phosphor 28 to 38 percent by weight
nenten erfolgtnents takes place
6. Verfahren nach Anspruch 4, dadurch gekennzeichnet daß die Mischung in wäßrig-nassem Zustand erfolgt6. The method according to claim 4, characterized in that the mixture in the aqueous-wet state he follows
7. Verfahren nach einem der Ansprüche 4 bis 6, dadurch gekennzeichnet, daß das Glühen bei 8500C bis 1100° C, insbesondere bei etwa 10000C, erfolgt.7. The method according to any one of claims 4 to 6, characterized in that the annealing at 850 0 C to 1100 ° C, in particular at about 1000 0 C, takes place.
8. Verfahren nach einem der Ansprüche 4 bis 7,8. The method according to any one of claims 4 to 7,
zente ausmachtcenter
In einer Weiterbildung der Erfindung ist ein bevor-In a further development of the invention, a preferred
dadurch gekennzeichnet, daß das Glühen 1.5 bis 35 zugtes Verfahren zur Herstellung eines solchen umman-5 Stunden, insbesondere etwa 3 Stunden, lang er- telten Leuchtstoffes angegeben, folgt. Es hat sich gezeigt, daß die beschriebenen ummantelcharacterized in that the annealing 1.5 to 35 added process for the production of such an umman-5 Hours, in particular about 3 hours, given for the eluted phosphor, follows. It has been shown that the jacket described
ten Leuchtstoffe eine sehr gleichmäßige Struktur besit-th phosphors have a very uniform structure.
zen und sich der gewünschte Schwellwert auch bei derzen and the desired threshold value also with the
Herstellung größerer Mengen gut reproduzierbar einstellen läßt. Diese Einstellung erfolgt im wesentlichen durch Beeinflussung der Menge des der Mischung zugesetzten Wolfram-Vl-Oxids.Production of larger quantities can be adjusted in a reproducible manner. This setting is essentially done by influencing the amount of tungsten VI oxide added to the mixture.
Der für das Verfahren zur Herstellung eines solchenThe one for the process of making such
Die vorliegende Erfindung betrifft einen mit einer bei
Temperaturen zwischen 100° C und 1300°C aufgebrachten
Ummantelungsschicht aus Wolfram-VI-Oxid versc
henen Leuchtstoff für Kathodenstrahlrohren und ein 45 Leuchtstoffes notwendige Aufwand ist sehr gering, soThe present invention relates to one with one at
Temperatures between 100 ° C and 1300 ° C applied coating layer of tungsten VI oxide versc
Henen fluorescent material for cathode ray tubes and a 45 fluorescent material required is very low, so
Verfahren zu dessen Herstellung.Process for its manufacture.
Silicat-Leuchtstoffe werden für kommerzielle Kathodenstrahlröhren sehr häufig verwendet, da sie gegenüber Sulfidleuchtstoffen auf Zink oder Zinkcadmiumsulfidbasis hinsichtlich des f arbortes den gestellten Anforderungen am besten genügen.Silicate phosphors are used very often for commercial cathode ray tubes because of their opposition Sulphide phosphors based on zinc or zinc cadmium sulphide meet the requirements with regard to the color location best enough.
Zur Wiedergabe verschiedenfarbiger Zeichen sind bereits Elektronenstrahlröhren bekannt, deren Lcuchi schirme verschiedenfarbig emittierende Leuchtstoffe aufweisen. So ist es bekannt, zwei aufeinanderliegende Leuchtstoffschichten durch eine isolierende Schicht zu trennen, wobei diese Schicht so gewählt ist. daß Elektronen bei niedriger Spannung diese Schicht nicht zu durchdringen vermögen, bei höherer Spannung dage-Cathode ray tubes whose Lcuchi have screens emitting phosphors in different colors. So it is known to have two superimposed To separate phosphor layers by an insulating layer, this layer being selected. that electrons are unable to penetrate this layer at low voltage, but at higher voltage
daß sich dieses Vc- Uhren gut in einen Fertigungsablauf eingliedern läßt. Ein weiterer Vorteil besteht darin, daß der gewünschte erhöhte Schwellwert in einem großen Bereich gut reproduzierbar eingestellt werden kann.that this Vc watch fits well into a production process can be incorporated. Another advantage is that the desired increased threshold value can be set in a reproducible manner over a large range.
Von Vorteil ist ferner, daß der Farbort des Leuchtstoffes durch die Ummantelung mit der angegebenen Menge von Wolfram-VI-Oxid nicht störend beeinflußt wird. Anhand des nachfolgend beschriebenen Ausführungsbcispiels wird die Erfindung näher erläutert.Another advantage is that the color point of the phosphor is not adversely affected by the coating with the specified amount of tungsten VI oxide. The invention is explained in more detail using the exemplary embodiment described below.
Kin pulverförmiger Siiicat-Leuchtstoff wird abgewogen, mit vorzugsweise 28 bis 38 Gewichtsprozent pulverförmiger! Wolfram-VI-Oxid versetzt und gut homogenisiert, anschließend in einem Muffelofen bei einer Temperatur zwischen 100 bis 13003C, vorzugsweise et·A powdered Siiicate phosphor is weighed out, preferably with 28 to 38 percent by weight of powdery! Tungsten VI oxide added and well homogenized, then in a muffle furnace at a temperature between 100 to 1300 3 C, preferably et
gen diese Schicht durchdringen und auch den darunter- 6<) wa l000°C, über eine Zeit von 10 Minuten bis 10 Stunliegenden Leuchtstoff anregen. Die Herstellung solcher den, vorzugsweise etwa 3 Stunden, geglühtThey penetrate this layer and also the layer below it - 6 <) wa 1000 ° C, over a period of 10 minutes to 10 hours Stimulate fluorescent. The preparation of such den, preferably about 3 hours, annealed
' " ■ -" " Wenngleich sich das beschriebene Verfahren bevor'"■ -" "Although the procedure described is before
zugt zur Einstellung des Errsissionsschwcllwertcs vonadmitted to setting the Errsissionsschwcllwertcs of
Mehrschicht-Leuchtschirme ist verhältnismäßig kostspielig und schwierig.Multi-layer fluorescent screens are relatively expensive and difficult.
Zur mehrfarbigen Darstellung ist es weiter bckanni,For the multicolored representation it is further bckanni,
eine Leuchtsloffschicht aus einem Gemisch von .zwei 65 cat-Lcuchtstoffen (ZnSiO4: Mn) eignet, so kann es auch Leuchtstoffen herzustellen, deren Schwellwerte für die mil gutem Erfolg zur Ummantelung von Oxid·,If a fluorescent layer made of a mixture of two 65 cat fluorescent substances (ZnSiO 4 : Mn) is suitable, it can also produce fluorescent substances, the threshold values of which are good enough for the coating of oxide.
g gg g
Silicat-Lcuchtstoffcn, wie manganaktivierten Zinksili-Silicate fluorescent substances, such as manganese-activated zinc silicones
k hk h
Emissionsanregung unterschiedlich ist. Eine solche Leuchtstoffschicht kann dadurch hergestellt werden,Emission excitation is different. Such a phosphor layer can be produced by
g g gg g g
Phosphat-, Borat-, Vanadat-, Wolframat- oder Sulfat-Leuchtstoffen verwendet werden.Phosphate, borate, vanadate, tungstate or sulfate phosphors can be used.
Claims (4)