DE2364209C3 - Membrane for electro-acoustic transducers - Google Patents
Membrane for electro-acoustic transducersInfo
- Publication number
- DE2364209C3 DE2364209C3 DE19732364209 DE2364209A DE2364209C3 DE 2364209 C3 DE2364209 C3 DE 2364209C3 DE 19732364209 DE19732364209 DE 19732364209 DE 2364209 A DE2364209 A DE 2364209A DE 2364209 C3 DE2364209 C3 DE 2364209C3
- Authority
- DE
- Germany
- Prior art keywords
- membrane
- carbon
- carbon fibers
- fibers
- paper stock
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
3030th
Mit bisher bekannten Lautsprechern ist es schwierig, den allgemein wiederzugebenden breiten Frequenzbereich von tiefen Tönen mit 30 bin 50 Hertz bis zu hohen Tönen von 15 000 bis 20 (K)O Hertz einwandfrei wiederzugeben. Hierzu wurden bisher entweder mehrere Lautsprecher verwendet, die zur Wiedergabe tiefer Töne einen großen Durchmesse und zur Wiedergäbe hoher Töne einen kleinen Durchmesser besaßen, oder es wurden doppelkonische Lautsprecher verwendet, die eine kegelförmige Membran kleinen Durchmessers für hohe Töne mit einer kegelförmigen Membran großen Durchmessers für tiefe Töne vcreinigten. Derartige bekannte Lautsprecheranlagen hatten aber den Nachteil, daß entweder eine wechselseitige Interferenz auftrat oder, wenn eine Schaltung für eine Frequenztrennung verwendet wurde, keine zufriedenstellende Dämpfung der tiefen Töne erreicht wurde oder, wenn Verstärker für tiefe Töne und für hohe Töne verwendet wurden, die Kosten der Anlage sehr hoch sind.With previously known loudspeakers it is difficult to the broad frequency range that can generally be reproduced from low tones with 30 to 50 Hertz up to reproduce high notes from 15,000 to 20 (K) O Hertz correctly. So far either several loudspeakers are used, which have a large diameter for the reproduction of deep tones and for reproduction high tones had a small diameter, or biconical loudspeakers were used, a cone-shaped diaphragm with a small diameter for high notes with a cone-shaped one Large diameter diaphragm for low pitched tones. Such known loudspeaker systems but had the disadvantage that either mutual interference occurred or if a circuit was used for frequency separation, no satisfactory attenuation of the low tones was achieved or, if amplifiers were used for low notes and high notes, the cost of the system are very high.
Die DT-AS 10 93 414 beschreibt eine Membran für elektroakustische Wandler, die eine hohe mechanische Dämpfung und gleichmäßige Frequenztrennlinie besitzen soll und aus üblichen Papierrohstoffen und aktivem Ruß besteht, welcher letzterer durch Papierleimstoff an den Fasern des Papierrohstoffes festgehalten ist. Die Verwendung aktiven Rußes ist jedoch nicht geeignet, den genannten breiten Frequenzbereich einwandfrei wiederzugeben und eine zufriedenstellende innere Dämpfung zu erhallen.The DT-AS 10 93 414 describes a membrane for electroacoustic transducers that have a high mechanical Should have attenuation and a uniform frequency dividing line and be made from conventional paper raw materials and active carbon black, the latter being made up of paper size on the fibers of the paper stock is held. However, the use of active carbon black is not suitable for the broad frequency range mentioned reproduce flawlessly and achieve a satisfactory internal damping.
Die DL-PS 28 845 beschreibt Mchrschichtmembrane für Lautsprecher, die aus unterschiedlichen Faserstoffen bestehen sollen, doch ist weder von Papierstoffasern noch von Kohlenstoffasern die Rede, sondern als Werkstoffe sind lediglich Aluminium.The DL-PS 28 845 describes Mchrschichtmembrane for loudspeakers, which from different Should consist of fibers, but there is no mention of paper pulp fibers or carbon fibers, the only materials used are aluminum.
nimmer Glas- oder Asbesifasern genannt. Die ητ PS 6Π612 betrifft ebenfalls mehrschichtige Membrane für elektroakustische Wandler doch be-Xi diese Membranen aas einem in der Warme Artenden Grundstoff, wie Phenolkondensat oder Lack md "eilenden Zusätzen, wie Metal, oder Koh lenstöff Das Grundmaterial besteht in diesem Fall also nicht aus Papierstoff Schließlich ist m »Frealso nic.ru 1T s 166 bis ,68 von Membranennever called glass or asbesi fibers. The ητ PS 6Π612 also relates to multi-layer diaphragms for electroacoustic transducers, but these diaphragms are based on a warm type of base material, such as phenol condensate or varnish and rapid additives such as metal or carbon. In this case, the base material does not consist of paper stock Finally, m »Frealso nic.ru 1 T s 166 bis , 68 of membranes
SifRäe'derlL Grundstoff aus Cellulose, bestehen nnd Beimischungen enthalten kann. Als Beimischun-"en sind daher fedigJich Wolle oder bestimmte G.asfasern genannt. Alle diese völlig anders aufgebauten Membrane sind nicht geeignet, die der Erfindung zugrunde liegende Aufgabe zu losen.SifRäe'derlL basic material made of cellulose and may contain admixtures. As admixtures are therefore feathery wool or certain gas fibers called. All of these completely differently constructed membranes are not suitable for those of the invention underlying task to be solved.
Diese Aufgabe besteht dann, eine Membran Pur elektroakustische Wandler zu bekommen welche in der Lage ist mit einer einzigen Membran einen breiien Frequenzbereich von tiefen bis zu hohen Tönen wiederzugeben, «eiche eine ausgeze.L-hneie Tontrennung, geeignete innere Dampfung und emc möulichst iiroße Resonanzfrequenz hoher Tone ergibt und bei ihrer Herstellung keine inneren SpannungenThis task then consists of creating a pure membrane electroacoustic converters which in is able to cover a wide frequency range from low to high with a single membrane To reproduce tones, "mark an excellent L-hneie Sound separation, suitable internal damping and emc results in the highest possible resonance frequency of high tones and no internal stresses in their manufacture
aultreten läßt. ... , . .lets emerge. ...,. .
Die erfindungsücmäße Membran fur elektroakustische Wandler aus einem gleichmäßigen Gemisch von Papierstoff und Kohlenstoff ist dadurch gekennzeichnet daß ihr Papierstoff einen Mahlungsurad. Ü nach der TAPPl-Standardmethode T-227 m.58 von nicht mehr als 300 ecm besitzt und ihr Kohlenstoff aus zerhackten Kohlenstoffasern nu einem Young-Modul \on wenigstens 8000 kg .umbestellt. 1 . T I"The inventive membrane for electroacoustic transducers made of a uniform mixture of paper stock and carbon is characterized in that its paper stock has a grinding wheel. According to the TAPPI standard method T-227 m .58 of no more than 300 ecm and its carbon from chopped carbon fibers with a Young's modulus of at least 8000 kg. 1 . TI "
Die Resonanzfrequenz fh eines hohen Tones, dieThe resonance frequency fh of a high tone that
die Wiedergabegrenze dieses Tones ausdruckt, kann durch die folgende Gleichung wiedergegeben werden. wobei der vertikale Winkel des Kegels 2 w betrau,. der Radius des Kegels α ist. der Young-Modul des Kegels E ist. die Dichte des Kegels ,, ist. die Masse des Kegels mc ist und die Masse der Lautsprecherschwingspule mv ist.expressing the reproduction limit of this tone can be expressed by the following equation. where the vertical angle of the cone is 2 w. is the radius of the cone α . is the Young modulus of the cone E. the density of the cone ,, is. the mass of the cone is mc and the mass of the loudspeaker voice coil is mv.
cos (-) cos (-)
fh = ~ fh = ~
■' 2 .τ a ■ '2 .τ a
mc mvmc mv
Im Falle eines Kegels, bei dem die Masse des Kegels, der Radius des Kegels und die Masse der Schwingspule konstant gemacht werden, ist die Resonanzfrequenz fh eines_hohen Tones proportional l'E des Kegels. 1/ £ ?eigl die Ausbreitungsgeschwindigkeit eines Tones in der Membran und sollt; groß sein.In the case of a cone in which the mass of the cone, the radius of the cone and the mass of the voice coil are made constant, the resonance frequency fh of a high pitch is proportional to l ' E of the cone. 1 / £ ? Eig l is the speed of propagation of a sound in the membrane and should; be great.
Eine Methode zur Herstellung der Membran be steht gewöhnlich darin, daß man ein Gemisch de Fasern auf Wasser oder einem anderen geeignete! Medium schwimmen läßt, sie auf einer Form auf nimmt und so einen Bogen herstellt und diesel trocknet. ^__One method of making the membrane be is usually that a mixture de Fibers on water or another suitable! Medium floats them on a form takes and makes a bow and dries diesel. ^ __
Um eine Membran mit großem j, ^ zu bekommer muß die Haftung der Fasermatcrialien untcreinandc gut sein. Um die Haftung der Fasermalenalien untei einander gut zu machen, kann ein synthetisches ode natürliches Bindemittel, wie Kunstharz. Kunstkau tscbuk. Kunstfasern. Leim oder Kolophonium, züge setzt werden. Bevorzugt liegt der Young-Modul de Kohlenstoffasern bei wenigstens 15 000 kg/mnr. HiIn order to get a membrane with a capital j, ^ the adhesion of the fiber materials must be different be good. In order to make the adhesion of the fibrous materials good to one another, a synthetic or synthetic material can be used natural binder, such as synthetic resin. Kunstkau tscbuk. Synthetic fibers. Glue or rosin, pulls are set. The Young's modulus of the carbon fibers is preferably at least 15,000 kg / mnr. Hi
bevorzugter Durchmesser ist 1 bis 20 μ, und weiter ist es bevorzugt, eine fein aufgerauhte Oberfläche, die bei einer Oxidationsbehandlung der Faserober-Säche gebildet wird, zu haben, um die Haftung zu verbessern. Wenn die Länge der Kohlenstoffasern zu kurz ist, ist die Erhöhung von 1, - L'.ein. und anderer-preferred diameter is 1 to 20 μ, and further it is preferred to have a finely roughened surface, which is formed during an oxidation treatment of the fiber surface, in order to increase the adhesion improve. If the length of the carbon fibers is too short, the increase is 1, - L'.a. and other-
ieits sind die Mischbarkeil und Dispergierbarkeit bei der Papierherstellung schlecht, wenn die Län^e zu groß ist. Aus diesem Grund liegt die Länge der Kohlenstofffasern bevorzugt im Bereich von 0.5 bis 20 mm.ieits are miscibility and dispersibility in papermaking bad if the length is too great. Because of this, the length of the Carbon fibers preferably in the range from 0.5 to 20 mm.
Das Mahlen oder Schlagen des Papierstoffes erfolüt. um eine innere Fibnllierung der Papierfasern durch eine mechanische Behandlung zu bekommen (was eine Lockerung der feinen Faserstrukturen bedeutet, die dazu führt, daß die Fasern Wasser enthalten und quellen), um eine äußere Fibrillierung der Papierfasern zu bekommen (was ein Aufrauhen oder ein Verzweigen von Fibrillen bedeutet, welche auf der Faseroberfläche erscheinen), um die Bildung feiner Fasern zu bekommen und um Fasern zu kürzen (d. h Fasern in Längsrichtung zu schneiden).The pulp is milled or beaten. by an internal felling of the paper fibers to get a mechanical treatment (which means a loosening of the fine fiber structures, which leads to the fact that the fibers contain water and swell) to an external fibrillation of the paper fibers to get (which means roughening or branching of fibrils, which on the Fiber surface appear) in order to get the formation of fine fibers and to shorten fibers (i.e., cutting fibers lengthways).
In der Zeichnung bedeutet Fi g. 1 eine graphische Darstellung, die die Beziehung zwischen dem Malilungsgrad des Papierstoffes und der inneren Dämpfung (Tangens <>) der daraus hergestellten Membran zeigt.In the drawing, Fi means g. 1 a graphic Representation showing the relationship between the degree of malilation of the paper stock and the internal damping (Tangent <>) of the membrane produced therefrom shows.
F i g. 2 ist eine graphische Darstellung, die die Beziehung zwischen dem Mahlungsgrad des Pr pierstoffes und dem Young-Modul der daraus hergestellten Membran zeigt;F i g. Fig. 2 is a graph showing the relationship between the freeness of the pulp and shows the Young's modulus of the membrane made therefrom;
F i g. 3 ist eine graphische Darstellung, die die Beziehung zwischen dem Young-Modul einer Membran aus Papierstoff mit 30 Gewichtsprozent Kohlenstoffasern und dem Mahlungsgrad des Papierstoffes zeigt:F i g. 3 is a graph showing the relationship between Young's modulus of a membrane made of paper stock with 30 percent by weight carbon fibers and the degree of freeness of the paper stock indicates:
F1 g. 4 ist eine graphische Darstellung, die dieF1 g. Fig. 4 is a graph showing the
Beziehung zwischen I/ - einer Membran aus einemRelationship between I / - a membrane made of one
[ η[η 4C 4 C
Gemisch von Papierstoff mit einem hohen Mahlungsgrad und aus Kohlenstoffasern und dem Mischungsverhältnis zeigt;Mixture of paper stock with a high degree of freeness and of carbon fibers and the mixing ratio indicates;
Fig. 5 ist eine graphische Darstellung, die die Beziehung zwischen der inneren Dämpfung einer Membran aus einem Gemisch von Papierstoff mit hohem Mahlungsgrad und Kohlenstoffasern und dem Mischungsverhältnis zeigt;Fig. 5 is a graph showing the Relationship between the internal damping of a membrane made from a mixture of paper stock shows high freeness and carbon fibers and the mixing ratio;
F i g. 6 ist eine graphische Darstellung, die die Beziehung zwischen dem Mahlungsgrad eines Gemisches von Papierstoff mit hohem Mahlungsgrad und Kohlenstoffasern und dem Mischungsverhältnis zeigt:F i g. Fig. 6 is a graph showing the relationship between the degree of grinding of a mixture of paper stock with high freeness and carbon fibers and the mixing ratio indicates:
Fig. 7 ist eine graphische Darstellung, die das Verhältnis zwischen der Frequenz der Wiedergabe eines Lautsprechers unter Verwendung einer Membran nach der Erfindung und eines Lautsprechers unter Verwendung einer herkömmlichen Membran zeigtFig. 7 is a graph showing the Ratio between the frequency of reproduction of a loudspeaker using a diaphragm according to the invention and a loudspeaker using a conventional membrane indicates
Durch den Mahlungsgrad ist es möglich, die physikaiischen Eigenschaften der fertigen Membran zu verändern. Es gibt eine enge Beziehung /wischen dem Mahlungsgrad des Papierstoffes, dem Young-Modul. der Dichte und d'T inneren Dämpfung einer Membran. Wie in Fig. I gezeigt ist. nimmt die (,5 innere Dämpfung. Tangens Λ. ab. wenn der Mahlungsgrad des Papierstoffes erhöht wird.Due to the degree of grinding, it is possible to use the physical To change the properties of the finished membrane. There is a close relationship / wipe the degree of freeness of the paper stock, the Young's modulus. the density and d'T internal damping of a Membrane. As shown in FIG. takes the (, 5 internal damping. Tangent Λ. away. when the grind of the paper stock is increased.
Wie in Fig. 2 gezeigt ist. nehmen der Young-Modul E und die Dichte « der Membran zu. wenn der Mahlungsgrad des Papierstoffes ansteigt. Daher ist es bei der Herstellung einer Membran aus Naturpulpe bevorzugt, den Matilungsgrad der Pulpe so hoch wie möglich zu steigern, um I/ ■- zu erhöhen.As shown in FIG. the Young's modulus E and the density «of the membrane increase. when the freeness of the paper stock increases. Therefore, in making a membrane from natural pulp, it is preferable to increase the fraction of the pulp as high as possible in order to increase I / ■ -.
Andererseits wird die innere Dämpfung zu klein, wenn der Mahlungsgrad zu stark wird, was nicht bevorzugt ist. So gibt es zwei wechselseitige Begrenzungen. Demnach war es bisher normal, den Mahlungsgrad des Papierstoffes so einzustellen, daß man diese beiden Begrenzungen harmonisiert. Aus diesen Gründen wurde für den Mahlungsgrad von Papierstoff für eine Membran für elektroakustische Wandler bisher immer nur ein Mahlungsgrad \on etwa 350 bis 600 ecm verwendet.On the other hand, the internal damping becomes too small if the grind becomes too strong, which is not preferred. So there are two mutual limitations. Accordingly, it has hitherto been normal to adjust the degree of freeness of the paper stock in such a way that one of these two Limitations harmonized. For these reasons, the freeness of paper stock for a Membrane for electroacoustic transducers has so far only ever had a degree of grinding of around 350 to 600 ecm used.
Die Erfindung macht es möglich, eine Membran für elektroakustische Wandler mit einem großenThe invention makes it possible to provide a membrane for electroacoustic transducers with a large
Wert für / " und einer »eeiuneten inneren Dämp-Value for / "and a single internal damping
fung zu bekommen.to get fungus.
Wie oben erwähnt, hat Naturpapiersloff eine:, hohen Mahlungsgradcs Eigenschaften, wie innere Fibrillierung der Faser, äußere Fibrillierung der Faser und Bildung feiner Fasern. Ein solcher Papiersiofl arbeitet sehr wirksam als ein Bindemittel für Kohlenstoffasern mit einem hohen Young-Modul. Besonders im Falle \on Kohlenstoffasern. deren Oberfläche mit leinen Unebenheiten durch eine Oxidationsbehandlung \ersehen ist. ist der Effekt als Haftmittel sehr groß. Fi g. 3 zeigt die Beziehung /wischen dem Young-Modul einer Membran aus natürlichem Papierstoff mit einem Gehalt von 30 Gewichtsprozent Kohlenstoffasern und mit einem Young-Modul win 20 000 kg mm2 und dem Mahlungsgrad des natürlichen Papierstoffes. Sie zeigt, daß der Young-Modul der Membran steigt, wenn der Mahlungsgrad de* natürlichen Papierstoffes steigt, d. h. der Wert nach der TAPPl-Sianddidmethode T-227 m-5S abnimmt was zeigt, daß natürliche Pulpe eines hohen Yermahlungsgradcs wirksam als Bindemittel arbeitetAs mentioned above, natural paper pulp has high freeness properties such as internal fibrillation of the fiber, external fibrillation of the fiber, and fine fiber formation. Such a paper foil works very effectively as a binder for carbon fibers having a high Young's modulus. Especially in the case of carbon fibers. the surface of which is seen with linen bumps through an oxidation treatment. the effect as an adhesive is very great. Fi g. 3 shows the relationship between the Young's modulus of a membrane made of natural paper stock with a content of 30 percent by weight carbon fibers and with a Young's modulus of 20,000 kg mm 2 and the degree of freeness of the natural paper stock. It shows that the Young's modulus of the membrane increases when the degree of freeness of the natural paper stock increases, ie the value according to the TAPPI-Sianddid method T-227 m-5S decreases, which shows that natural pulp of a high degree of refinement works effectively as a binder
F i g. 4 zeigt die Beziehung zwischen ' einciF i g. 4 shows the relationship between 'einci
Membran aus einem Gemisch von natürlichen Papierstoff eines hohen Vermahlungsgrades vor 100 ecm und Kohlenstoffasern mit einem Young· Modul von 20000 kg nmr und dem Gehall dci Kohlensioffasern. Da der natürliche Papierstoff eine: hohen Vermahlungsgrades wirksam als ein Binde mittel arbeitet, steigt I/ " . wenr, der Gehalt deMembrane made from a mixture of natural paper stock with a high degree of milling 100 ecm and carbon fibers with a Young modulus of 20000 kg nmr and the Gehall dci Carbon fibers. Since the natural paper pulp has a: high degree of grind, it is effective as a bandage works medium, increases I / ". wenr, the salary de
Kohlenstoffasern
derart hohes I/Carbon fibers
such a high I /
=igt y ι. = igt y ι.
steigt.
T increases.
T
soso
wem,
daß diewhom,
that the
besitzt, wie esowns like it
Membran en herkömmlichiMembrane en conventionali
Membrane nicht haben können.Cannot have a membrane.
Wenn der Gehalt an Kohlenstoffasern 50 GewichtsWhen the carbon fiber content is 50 weight
prozent übersteigt, nimmt I/ ' ab. Dies beruhexceeds percent, I / 'decreases. This rest
wohl auf der Tatsache, daß die Menge an Papierstol eines hohen Mahlungsgrades gegenüber der Meng an Kohlenstoffasern eines hohen Young-Moduls uiii damit die llaftwirkung abnimmt.probably due to the fact that the amount of paper stol of a high degree of freeness compared to the amount on carbon fibers of high Young's modulus uiii so that the lifting effect decreases.
Fig. 5 zeigt ein Beispiel, bei dem die inner Dämpfung einer Membran deren Haupimateri;: natürlicher Papierstoff eines hohen Mahllingsgrade von etwa 100 ecm ist. durch Vermischen m: Kohlenstoffasern mit einem Young-Modul vo 20 000 kg nmr steigt. Beispielsweise ist ersichtliclFig. 5 shows an example in which the inner Damping of a membrane whose main material ;: natural paper stock of a high grind is about 100 ecm. by mixing m: carbon fibers with a Young's modulus vo 20,000 kg nmr increases. For example, it is evident
5 65 6
daß durch Vermischen von K) bis 30 Gewichtspro- Kantenkonslruktion aus weichem Leder. Baumwoll-that by mixing K) up to 30 percent by weight edge construction made of soft leather. cotton
zcnt Kohlenstoffasern mit einem solchen Papierstoff tuch oder Kunstgummi an einer Kante der kegel -zcnt carbon fibers with such a paper cloth or synthetic rubber on one edge of the cone -
die daraus hergestellte Membran eine innere Dämp- förmigen Membran ist es möglich, auch tiefe Tönethe diaphragm made from it, an inner muffler-shaped diaphragm, makes it possible to also produce deep tones
fung besitzt, die gleich oder besser als diejenige einer wiederzugeben.fung that is equal to or better than that of one to reproduce.
Membran aus natürlichem Papierstoff mit einem 5 In den obigen Ausführungen ist die Form derMembrane made of natural paper stock with a 5 In the above, the shape is the
niedrigen Mahlungsgrad von praktisch 400 bis Membran hauptsächlich als ein Kegel erläutert. Sielow freeness of practically 400 to membrane explained mainly as a cone. she
600 ecm ist. kann jedoch auch eine andere Form, wie die einer600 ecm is. however, it can also take another form, such as the one
Weiterhin eignet sich ein solches Gemisch gut für Kugel, haben,Furthermore, such a mixture is well suited for ball, have,
die Membranherstellung nach der Erfindung. Es ist also nach der Erfindung möglich, eine l-'re-the membrane production according to the invention. It is therefore possible according to the invention to produce a l-'re-
F i g. 6 zeigt ein Beispiel, bei dem durch Vcr- io quenz von liefen Tönen von 30 bis 50 Hertz bis /uF i g. 6 shows an example in which, through the frequency of running tones from 30 to 50 Hertz to / u
mischen von Kohlenstoffasern mit einem Young- hohen Tönen von 15 000 bis 20 000 Hertz einwand-mixing of carbon fibers with a Young high tones of 15,000 to 20,000 hertz
Modul von 20000 kg/mnr mit natürlichem Papier- frei wiederzugeben, was bisher mit einer einzigenModule of 20000 kg / mnr with natural paper-free to reproduce what was previously with a single
stoff eines hohen Mahlungsgrades die Trockenlegung Membran nicht möglich war. Da weiterhin einematerial of a high degree of grinding the draining membrane was not possible. There continues to be a
von Papier aus einem solchen Gemisch gut wird Membran nach der Erfindung eine geeignete innereOf paper made from such a mixture well, membrane according to the invention is a suitable inner one
und der Mahlungsgrad ansteigt. F i g. 6 zeigt, daß 15 Dämpfung hat. ist es auch möglich, eine schärfereand the degree of grinding increases. F i g. 6 shows that 15 has attenuation. it is also possible to have a sharper one
gemischte Fasern, erhalten durch Vermischen von Tontrennung frei von stoßhafter Wiedergabe zumixed fibers obtained by mixing sound separation free from intermittent reproduction
20 bis 30 Gewichtsprozent Kohlenstoffasern mit bekommen,Get 20 to 30 percent by weight of carbon fibers,
natürlichem Papierstoff eines hohen Mahlungsgrades Beispiel
von 80 bis 90 ecm, den gleichen guten Ablauf wienatural paper stock with a high degree of freeness, for example
from 80 to 90 ecm, the same good flow as
natürlicher Papierstoff eines ziemlich niedrigen Mali- 20 Zu 22 g Papierstoff wurde Wasser zugesetzt, umnatural pulp of a fairly low mali 20 To 22 g of paper stock water was added to
lungsgrades von 300 bis 450 ecm besitzen. das Gesamtgewicht des resultierenden Gemischeshave a degree of efficiency of 300 to 450 ecm. the total weight of the resulting mixture
Ein anderer Vorteil des Vermischens von Kohlen- auf 150 g zu bringen, und dieser Ganzstoff wurde mit stoffasern mit hohem Young-Modul mit natürlichem Hilfe eines Holländers gemahlen, bis der Mahlungs-Papierstoff eines hohen Mahlungsgrades ist der. daß grad. gemessen nach der TAPPI-Standardmethode in der Trockenstufe nach dem Formen einer Mem- 25 T-227 m-58, 100 ecm war. Der resultierende Ganzbran zu einem Kegel oder einer Kuppel in dem stoff wurde mit 6 g oberflächenbehandelter Kohlengetrockneten kegelförmigen oder kuppeiförmigen stoffasern eines Durchmessers von 8 μ und einer Formling keine Spannungen erzeugt werden, was bei Länge von 5 mm (Dichte 1,73. Young-Modul herkömmlichen Membranen gewöhnlich der Fall ist 20000 kg/mnr) versetzt, und beide wurden 1 bis und die anschließende Preßstufe erschwert Dieser 30 2 Minuten in einem Mischer vermischt. Das resul-Nachteil bekannter Membrane wächst mit steigen- tierende Gemisch wurde zu einem Papierkegel mit dem Mahlungsgrad des natürlichen Papierstoffes. einem Durchmesser von 20 cm und einem Trocken-Wenn jedoch erfindungsgemäß Kohlenstoffasern mit gewicht von etwa 2.1 g verarbeitet. Dieser Papierdem Papierstoff vermischt werden, ergeben sich keine kegel wurde leicht von 0.35 bis 0,40 g/ecm gepreßt. Spannungeninder Membran während des Trocknens. 35 Der erhaltene Papierkegcl wurde mit einer KanteAnother benefit of blending charcoal was bringing it up to 150 g, and this stock was made with Pulp fibers with a high Young's modulus are ground with the natural help of a Dutchman until the pulp is the same of a high degree of grinding is the. that grad. measured according to the TAPPI standard method was in the drying stage after forming a mem-25 T-227 m-58.100 ecm. The resulting whole brew A cone or dome in the fabric was dried with 6 g of surface treated charcoal conical or dome-shaped fabric fibers with a diameter of 8 μ and one Molding no stresses are generated, which is at a length of 5 mm (density 1.73. Young's modulus conventional membranes usually the case is 20000 kg / mnr) and both were 1 to and the subsequent pressing stage makes it difficult. This is mixed in a mixer for 2 minutes. The resul disadvantage known membrane grows with increasing mixture became a paper cone with the degree of grinding of the natural paper stock. a diameter of 20 cm and a dry-if However, according to the invention, carbon fibers with a weight of about 2.1 g are processed. This paper dem Paper pulp mixed, no cones were easily pressed from 0.35 to 0.40 g / ecm. Stresses in the membrane during drying. 35 The paper cone obtained was with one edge
Auf Grund der oben diskutierten Faktoren ist es aus Baumwolltuch verklebt, um eine Membran mitDue to the factors discussed above, it is made of cotton cloth glued to a membrane using
nach der Erfindung möglich, eine Membran mit freier Kante zu bekommen. Sodann wurde zu Ver-possible according to the invention to get a membrane with a free edge. Then became
n 11; . <-· l/~E~ a ■ r » i„„„i„, gleichszwecken nach der gleichen Methode eine kesiel-n 11; . <- · l / ~ E ~ a ■ r »i""" i ", for the same purposes using the same method a kesiel-
emem großen Wert Tür [/ ? und einer geeigneten förmige Membran mit einem Gewicht von etwa IA gemem great value door [/ ? and a suitable shaped membrane weighing about IA g
inneren Dämpfung zu erhalten, was nach hcrkömm- 40 aus natürlichem Papierstoff ohne KohlenstoffasernTo obtain internal cushioning, what comes after 40 from natural paper stock without carbon fibers
liehen Methoden unmöglich war. hergestellt.borrowed methods was impossible. manufactured.
Aus der obigen Gleichung ist ersichtlich, daß dann. Lautsprecher wurden unter Verwendung dieserFrom the above equation it can be seen that then. Speakers were using this
wenn der vertikale Winkel 2 (-) eines Membrankegels. beiden Membrane hergestellt, und die Frequenz-if the vertical angle 2 (-) of a membrane cone. made of both diaphragms, and the frequency
der Radius α des Kegels, die Masse mc des Kegels Charakteristiken derselben wurden gemessen. Die und die Masse mv der Schwingspule die gleichen 45 Ergebnisse sind in F ic. 7 gezeigt. Kurve . A inthe radius α of the cone, the mass mc of the cone, characteristics thereof were measured. The voice coil and the mass mv the same 45 results are in F ic. 7 shown. Curve . A in
s,„d. es m«,ch wM. ,„ ™ erhöhen, d. ffp. & l^t^tl^X^"™« s , "d. es m «, ch w M. , "™ increase, d. ffp. & l ^ t ^ tl ^ X ^ "™«
ist. Selbst wenn der Lautsprecher einen großen Durch- Lautsprecher mit der Membran aus Papierstoff ohn<is. Even if the loudspeaker does not have a large through loudspeaker with a paper pulp membrane
messer hat, ist es somit mögligh, hohe Töne von Kohlenstoffasergehalt erhalten. Aus den Kurven / 10000 bis 20 000 Hertz gleichmäßig wiederzugeben, 50 und ß ist ersichtlich, daß eine Membran nach de Thus, it is possible to obtain high tones of carbon fiber content. From the curves / 10,000 to 20,000 Hertz evenly reproduce, 50 and ß it can be seen that a membrane according to de
was mit herkömmlichen Lautsprechern bisher nicht Erfindung ausgezeichnet in der WiedergabekapazitäWhat with conventional loudspeakers so far not excellent in the playback capacity
möglich war. Mit Hilfe einer an sich bekannten freien hoher Töne istwas possible. With the help of a per se known free high tones is
Hierzu 4 Blatt Zeichnungen For this purpose 4 sheets of drawings
Claims (6)