DE2256110A1 - PACKING MATERIAL - Google Patents
PACKING MATERIALInfo
- Publication number
- DE2256110A1 DE2256110A1 DE19722256110 DE2256110A DE2256110A1 DE 2256110 A1 DE2256110 A1 DE 2256110A1 DE 19722256110 DE19722256110 DE 19722256110 DE 2256110 A DE2256110 A DE 2256110A DE 2256110 A1 DE2256110 A1 DE 2256110A1
- Authority
- DE
- Germany
- Prior art keywords
- polybutadiene
- packaging material
- film
- material according
- crystallinity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
PATENTANWÄLTE 9 9 R R 1 1 ΠPATENT LAWYERS 9 9 R R 1 1 Π
BERLINBERLIN
1 BERLIN 33 (GRUNEWALD), den 12.NOV.1972 HERBERTSTRASSE 22 1 BERLIN 33 (GRUNEWALD), NOV 12, 1972 HERBERTSTRASSE 22
' /Ha.'/ Ha.
47-112247-1122
JAPAN SYNTHETIC RUBBER COMPANY LIMITED,JAPAN SYNTHETIC RUBBER COMPANY LIMITED,
1, Kyobashi 1-chome, Chuo-ku, Tokyo, Japan·1, Kyobashi 1-chome, Chuo-ku, Tokyo, Japan
Verpackungsmaterialpacking material
Die Erfindung betrifft ein neuartiges Verpackungsmaterial. Insbesondere betrifft die Erfindung ein Verpackungsmaterial mit erwünschten Qualitätsmerkmalen, einschließlich sehr guter Transparenz, Permeabilität für Gase, Reißfestigkeit und Gleitfestigkeit. The invention relates to a novel packaging material. In particular The invention relates to a packaging material with desired quality features, including very good transparency, Permeability for gases, tear resistance and slip resistance.
Nach einer ausgedehnten Suche nach einem Plastikfilm oder -blatt mit ausgezeichneten Verpackungseigenschaften wurde nun gefunden, daß eine harzartige Masse, welche aus einem Polybutadien besteht, das hauptsächlich aus Einheiten in der 1,2-Konfiguration gebildet wird, bzw. aus einem solchen Polybutadien im Gemisch mit einem film- oder blattbildenden thermoplastischen Harz besteht, Filme oder Blätter liefert mit sehr erwünschten Qualitätsmerkmalen, Die vorliegende Erfindung geht auf diese Entdeckung zurück.After an extensive search for a plastic film or sheet with excellent packaging properties, now found that a resinous mass composed of a polybutadiene composed mainly of units in the 1,2-configuration is formed, or consists of such a polybutadiene mixed with a film or sheet-forming thermoplastic resin, Films or sheets provide highly desirable quality characteristics. The present invention is based on this discovery.
Hauptziel dieser Erfindung ist es daher, ein Verpackungsmaterial in Form eines Plastikfilms oder -blatts zu schaffen, was dadurch gekennzeichnet ist, daß solch ein Gegenstand in üblicher Weise aus einer harzartigen Masse hergestellt wird, welche aus 100 bis 5 Gew.-96 eines Polybutadiene mit einer Verbandstruktur aus nicht weniger als 70 % Einheiten der 1,2-Konfiguration und einer Kristallinität von nicht weniger als 10% und 0 bis 95 Gew.-%The main object of this invention is therefore to provide a packaging material in the form of a plastic film or sheet, which is characterized in that such an article is made in a conventional manner from a resinous mass composed of 100 to 5% by weight of a polybutadiene a bandage structure of not less than 70 % units of the 1,2-configuration and a crystallinity of not less than 10% and 0 to 95% by weight
303821/0317 - 2 -303821/0317 - 2 -
eines anderen thermoplastischen Harzes bestehty das zur Film- oder Blattbildung fähig ist.Another thermoplastic resin is y capable of film or sheet formation.
Die Menge der Einheiten in 1,2-Konfiguration in dem Polybuta-# dien mit einer Verbandstruktur hauptsächlich aus Einheiten der 1,2-Konfiguration ( hier der Einfachheit halber als 1,2-Polybutadien bezeichnet), welche bei Versuchen zur praktischen Durchführung der Erfindung verwendet wurden, wurde nach der Infrarotabsorptionsanalyse von Morero ( Horero et al.: Chim. e Ind.(Milano), 41, 758 (1959) bestimmt. Die Kristalllnität wurde durch die Verfahren zur Dichtemessung aus der FormelThe amount of units in 1,2 configuration in the polybuta- # serve with a bandage structure mainly of units of the 1,2-configuration (here for the sake of simplicity as 1,2-polybutadiene referred to), which were used in experiments to practice the invention, according to the infrared absorption analysis of Morero (Horero et al .: Chim. e Ind. (Milano), 41, 758 (1959). The crystallinity was established by the Method of density measurement from the formula
I _ X | 1 - X
d " dcr dam I _ X | 1 - X
d " d cr d am
berechnet, worin d : Dichte der bei 20°C gemessenen Probecalculated, where d: density of the sample measured at 20 ° C
dcr: Dichte der kristallinen Regiond cr : density of the crystalline region
dam: Dichte der amorphen Region X : Kristallinität in Prozentd am : density of the amorphous region X: crystallinity in percent
Der verwendete Wert von dcr war Jener des kristallinen 1,2-Polybutadiens, der von Natta aus Röntgenversuchen zu 0,963 berechnet wurde ( G.Natta: J. Polymer Sei., 20, 251 (1956) ). Der verwendete Wert von d war 0,894 oder die Dichte des 1,2-Polybutadiens, das nach dem in der US-Patentschrift 3 498 963 (entsprechend der britischen Patentschrift 1 158 296) vorgeschlagenen Syntheseverfahren erhalten wurde und sich nach Röntgenanalyse als vollständig amorph erwiesen hat.The value of d cr used was that of the crystalline 1,2-polybutadiene, which was calculated by Natta from X-ray experiments to be 0.963 (G. Natta: J. Polymer Sci., 20, 251 (1956)). The value of d used was 0.894 or the density of the 1,2-polybutadiene obtained by the synthetic method proposed in US Pat. No. 3,498,963 (corresponding to British Pat. No. 1,158,296) and which was found to be completely amorphous by X-ray analysis .
Brauchbares 1,2-Polybutadlen für die praktische Durchführung der Erfindung enthält nicht weniger als 70#, vorzugsweise nicht weniger als 85#, Einheiten der 1,2-Konfiguration in der Verbandstruktur und hat eine Kristallinität von nicht weniger als 10 %, vorzugsweise zwischen 10 und 5096. Es kann zum Beispiel nach den Lehren der US-Patentschrift 3 498 963 und 3 522 332 (entsprechend den britischen Patentschriften 1 158 296 bzw. 1 189 257) hergestellt werden. Es ist unmöglich, mit 1,2-Polybutadien, das Einheiten in der 1,2-Konfiguration und eine Kristallinität außerhalb der oben spezifizierten Bereiche aufweist, die vorteilhaften1,2-polybutadlene useful in practicing the invention contains no less than 70 #, preferably no less than 85 #, units of the 1,2-configuration in the dressing structure and has a crystallinity of no less than 10 %, preferably between 10% and 5096. It can be made, for example, according to the teachings of U.S. Patents 3,498,963 and 3,522,332 (corresponding to British Patents 1,158,296 and 1,189,257, respectively). It is impossible with 1,2-polybutadiene, which has units in the 1,2-configuration and a crystallinity outside the above-specified ranges, to achieve the advantageous
Wirkungen der vorliegenden Erfindung zu erhalten.To obtain effects of the present invention.
- 3 HO 9821/0317 - 3 HO 9821/0317
1 - 3 - 1 - 3 -
Thermoplastische Harze, welche im Gemisch mit 1,2-Polybutadien gemäß dieser Erfindung verwendet werden können, sind jedwedes Harz, das Plastikfilme oder -blätter bilden kann. Zu typischen Beispielen zählen Polyolefine, wie Polyäthylen ( Nieder-, Mittel·- und Hochdruck-Grade), Polypropylen und Polybuten-1, Polystyrol, Acrylnitril-Styrol-Butadien-Copolymerisatt-Harz (ABS-Harzj| und Äthylen-Vinylacetat-Copolymerisat. Die Vorteile der Erfindung sind besonders ausgeprägt, wenn 1,2-Polybutadien allein oder im Gemisch mit Polyolefinen verwendet wird. Die Gemische sollten nicht weniger als 5 Gew.-#, vorzugsweise nicht weniger als 10 Gew.- %t 1,2-Polybutadien enthalten.Thermoplastic resins which can be used in admixture with 1,2-polybutadiene in accordance with this invention are any resin that can form plastic films or sheets. Typical examples include polyolefins such as polyethylene (low, medium and high pressure grades), polypropylene and polybutene-1, polystyrene, acrylonitrile-styrene-butadiene copolymer resin (ABS resin and ethylene-vinyl acetate copolymer. The advantages of the invention are particularly pronounced when 1,2-polybutadiene is used alone or in a mixture with polyolefins. The mixtures should not be less than 5% by weight, preferably not less than 10 % by weight of 1,2-polybutadiene contain.
Ein solches thermoplastisches Harz kann mit 1,2-Polybutadien in der üblichen Weise gemischt werden; hinsichtlich des Mischverfahrens, das zu verwenden ist, bestehen keine Beschränkungen.Such a thermoplastic resin can be mixed with 1,2-polybutadiene be mixed in the usual way; there are no restrictions on the mixing method to be used.
Ein Film oder Blatt kann nach jeder der gewohnten Techniken gebildet werden, zum Beispiel mittels eines Blas-, T-Spritzform- oder Kalanderverfahrens.A film or sheet can be formed using any of the usual techniques, such as a blow molding, T-injection molding or calendering process.
Der Film oder das Blatt, welche aus dem 1,2-Polybutadien allein oder aus einer harzartigen Masse, die 5 Gew.-?6 oder mehr 1,2-Polybutadien enthält, erfindungsgemäß gebildet werden, sind ausgezeichnet hinsichtlich der mechanischen Eigenschaften, wie Zugfestigkeit, Schlagfestigkeit und Oberflächengleitfestigkeit. Daneben haben sie eine geringe Trübung und eine hohe Gesamtlichtdurchlässigkeit bzw. sind äußerst transparent. Neben anderen Merkmalen liegt eine große Permeabiltität für Sauerstoff und Kohlendioxid vor. Die hohe Gasperaeabilität ist günstig für die Nahrungsmittelindustrie«, da, wenn man Fleisch abpackt, der Film oder das Blatt eine Entfärbung des Inhalts verhindert, und wenn Gemüse oder Früchte eingepackt werden, er diese frisch hält. Die hohe Zugfestigkeit ist kombiniert mit einer hohen Zerreißfestigkeit und Festigkeit gegenüber Stichen und Stößen, so daß der Film oder das Blatt verwendbar zum Verpacken von Krustazeen, wie Krabben und Hummer, zu machen ist. Vorteil dieser Erfindung ist, daß der Film oder das Blatt mit hoher Transparenz und Flexibilität ohne Weichmacher erhalten werden kann. Außerdem ist der erfindungsgemäß geformte orientierte Film oder das Blatt bei verhältnismäßig niedrigen Temperaturen schrumpffähig und kann für Schrumpf-The film or sheet made up of the 1,2-polybutadiene alone or from a resinous mass containing 5 wt .- 6 or more 1,2-polybutadiene contains, are formed according to the invention, are excellent in terms of mechanical properties, such as tensile strength, Impact resistance and surface slip resistance. In addition, they have low haze and high overall light transmission or are extremely transparent. In addition to other features, there is a high permeability for oxygen and carbon dioxide before. The high gas permeability is beneficial for the food industry «, because when packing meat the film or leaf prevents discoloration of the contents, and when packing vegetables or fruits are packed, he keeps them fresh. The high tensile strength is combined with a high tear strength and resistance to stitches and bumps so that the film or sheet is useful for wrapping crustaceans such as crabs and lobster to make. Advantage of this invention is that the film or sheet has high transparency and flexibility can be obtained without plasticizers. In addition, the oriented film or sheet formed in accordance with the present invention is proportionate shrinkable at low temperatures and can be used for shrinkage
309821/0317. ""4V309821/0317. "" 4 V
verpackungen angewendet werden. Es 1st auch möglich, wenn man aus der Tendenz des 1,2-Polybutadlens, bei Belichtung einer Vernetzung zu unterliegen, Vorteil zieht, den Film oder das Blatt mit ultravioletter Strahlung zu bestrahlen, so daß er innerhalb einer kurzen Zeitspanne bis zu einem solchen Ausmaß gehärtet werden kann, daß ein kleinerer Schlag ihn leicht zu StUcken brechen kann. Folglich kann das Ausmaß der Photolyse gegebenenfalls durch Verwendung eines Ultravlolett-Absorbers eines geeigneten Typs in einer geeigneten Menge geregelt werden, und das Problem der Verschmutzung mit Kunststoffabfallen kann demgemäß gelöst werden.packaging can be applied. It is also possible if you from the tendency of 1,2-polybutadlene, upon exposure to a crosslink to succumb, prefers to irradiate the film or sheet with ultraviolet radiation so that it is within can be cured in a short period of time to such an extent that a minor blow can easily break it can break. Thus, the degree of photolysis can be increased by using an ultraviolet absorber of a suitable one if necessary Type can be regulated in an appropriate amount, and the problem of plastic waste pollution can accordingly be solved will.
Bei der praktischen Durchführung der Erfindung ist es natürlich möglich, einen Stabilisator, ein Verstärkungsmittel, Schmiermittel und andere herkömmliche Zusätze zu verwenden.It is natural in practicing the invention possible to use a stabilizer, a reinforcing agent, lubricant and other conventional additives.
Die vorliegend Erfindung wird durch die folgenden nichtbeschränkenden Beispiele erläutert.The present invention is defined by the following non-limiting ones Examples explained.
Ein Polybutadien, das 95% Einheiten der 1,2-Konfiguration enthält und eine Kristallinitat von 25 % und eine Grenzviskositätszahl (Jj^] ) von 1,43 (bestimmt bei 3O0C in Toluol) aufweist, wurde in eine Filmblasvorrichtung gegeben, und durch eine Spritzform bei 1350C wurde ein aufgeblasener Film (i. Orig.inflation film) gebildet. In der gleichen Weise wurde sowohl ein Gemisch aus dem Polybutadien und käuflichem Hochdruck-Polyäthylen in einem Mischungsverhältnis von 1:1 (Gewichtsverhältnis) und als Kontrolle Polyäthylen allein zu Filmen geblasen. Als Proben für die Tests zur Gesamtlichtdurchlässigkeit und Trübung wurden Folien von 0,185 cm Dicke aus den gleichen Materialien unter Verwendung einer Form- und Deckpresse bei 1100C hergestellt.A polybutadiene 95% of units of 1,2-configuration and having a crystallinity of 25% and an intrinsic viscosity (Jj ^]) of 1.43 (determined at 3O 0 C in toluene) which was placed in a Filmblasvorrichtung, and by an injection mold at 135 0 C, an inflated film (i. Orig.inflation film) was formed. In the same way, both a mixture of the polybutadiene and commercial high-pressure polyethylene in a mixing ratio of 1: 1 (weight ratio) and, as a control, polyethylene alone were blown into films. As samples for the tests for total light transmittance and haze films were made of 0.185 cm thick of the same materials using a forming and deck press at 110 0 C.
Es wurden verschiedene Eigenschaften dieser Filme und Blätter bestimmt. Die Ergebnisse sind in Tabelle 1 wiedergegeben.Various properties of these films and sheets were determined. The results are shown in Table 1.
309821/0317309821/0317
beispielComparison
example
dien1,2-polybuta
serve
polyäthylenHigh pressure
polyethylene
ErfindungExample of
invention
(Maschinenrichtung)Tensile strength Ä ^
(Machine direction)
dien/Hoch-
druckp olyathy-
len-Gemisch1,2-polybuta-
service / high
pressure p olyathy-
len mixture
(Maschinenrichtung)Strain * '
(Machine direction)
Iran +■ arC^ Elmendorf tear resistance
Iran + ■ arC ^
(kg/cm)iveii / ftc /
(kg / cm)
fizienten:
(x 1o°cc.cm/cm sek.cmGas permeability coefficient
efficient:
(x 1o ° cc.cm / cm sec.cm
(kg/cm)Impact resistance * 5 ^
(kg / cm)
keit *7) (^)Overall translucent
speed * 7) (^)
Anmerkungen: 3e1) Proben, die mit einem ψ$ Dumbbell-SchneiderNotes: 3e1) Samples made with a ψ $ dumbbell cutter
äß äaccording to
gemäß JIS Kö^cvl; .%eprä^t:Jj//,aren, wurden unter Spannung auf einem "Teötgerät des Instron-Typsaccording to JIS Kö ^ cvl; .% eprä ^ t : J j //, aren, were under tension on an "Instron-type device
tt'tt '
..,-.i-j.oj j '..:■ .., -. ij.oj j '..: ■
309821/0317309821/0317
nach JIS Z1702according to JIS Z1702
gemessen mit einem Gaspermeabilitätstester vom Typ Seikaken bei einer Meßtemperatur von 200C.measured using a Seikaken type Gaspermeabilitätstester at a measuring temperature of 20 0 C.
gemessen mit einem Toyo Seiki■TSS-Friktionsirinkeltester. measured with a Toyo Seiki ■ TSS friction iron tester.
nach ASTM-DI709.according to ASTM-DI709.
*'''unter Verwendung einer Form auf einer Deckpresse bei* '' 'using a form on a cover press
1100C wurden 0,185 cm dicke Folien als Testproben geformt. Gemessen mit Tokyo Denshoku's integrierendem Sphärenlichtdurchlässigkeitstester. 110 0 C were molded 0.185 cm thick films as test samples. Measured with Tokyo Denshoku's integrating spherical light transmission tester.
Ein Polybutadien, das 90 % Einheiten mit 1,2-KonfIguration enthielt und eine Kristallinitat von 25 % und [^] von 1,61 (bestimmt in Toluol bei 30°C) aufwies, und Polystyrol (nachfolgend PS genannt) wurden in einem Verhältnis von 1:1 gemischt und gleichmäßig· zusammengeschmolzen auf einer Walzmühle; mit einer Deckpresse wurde bei 1100C eine Folie geformt. In ähnlicher Weise wurden ein Äthylen-Vinylacetat-Copolymerisat (nachfolgend EVA genannt), ABS-Harz und Polypropylen (nachfolgend PP genannt) entsprechend mit dem Polybutadien gemischt und aus den Gemischen auf einer Deckpresse Folien hergestellt. Zum Vergleich wurden in|der gleichen Weise Folien aus PS, EVA, ABS-Harz und PP allein geformt. Die so erhaltenen Proben wurden den Eigenschaftstests unterzogen. Die Ergebnisa· sind in Tabelle 2 wiedergegeben.A polybutadiene containing 90 % units of 1,2 configuration and having a crystallinity of 25 % and 1.61 (determined in toluene at 30 ° C.) and polystyrene (hereinafter referred to as PS) were in a ratio mixed 1: 1 and evenly · melted together on a roller mill; with a cover press, a film was formed at 110 0 C. In a similar way, an ethylene-vinyl acetate copolymer (hereinafter referred to as EVA), ABS resin and polypropylene (hereinafter referred to as PP) were mixed with the polybutadiene and films were produced from the mixtures on a cover press. For comparison, sheets of PS, EVA, ABS resin and PP alone were molded in the same manner. The samples thus obtained were subjected to the property tests. The results are shown in Table 2 .
309821/0317 " ? "309821/0317 " ? "
k1)strain
k1)
winkel
k2)Friction
angle
k2)
(Gew.)
verhält
nisMixed
(Weight)
behaves
nis
keit x1)
kg/cm * j Tensile strength
speed x1)
kg / cm * j
butadien/EVA(Example) 1,2-poly
butadiene / EVA
butadien/PP(Example) 1,2-poly
butadiene / PP
butadien/PS(Example) 1,2-poly
butadiene / PS
ABS(Comparative example)
SECTION
butadien /ABS(Example) 1,2-poly
butadiene / ABS
ί74.2
ί
Anmerkungen: x1) Filme wurden mit einem ^ 2 Dumbbell-SchneiderNotes: x1) Films were made with a ^ 2 dumbbell cutter
gemäß JIS K6301 geprägt; die so erhaltenen Testproben wurden auf Spannung mit einem Tester vom Instron-Typ mit einer Zug|*sctiwindigkeit von 500 mm/min, getestet.embossed according to JIS K6301; the test specimens thus obtained were tested for tension with a tester from Instron type with a train speed of 500 mm / min, tested.
*2)* 2)
gemessen mit Toyo Seiki's TSS Friktionswinkel·· tester.measured with Toyo Seiki's TSS friction angle · · tester.
Tests wurden mit 1,2-Polybutadienen mit unterschiedlichen Kristallinitäten durchgeführt. Unter Verwendung von 1,2-Polybutadienen mit Kristallinitäten von Null (amorph, Vergleichsbeispiel), 14 96 und 30 % wurden auf einer Deckpresse Folien geformt und auf Zugfestigkeit, Rechtwinkel-Reißfestigkeit und Friktionswinkel getested. Die Ergebnisse sind in Tabelle 3 wiedergegeben. Tests were carried out with 1,2-polybutadienes with different crystallinities. Using 1,2-polybutadienes with crystallinities of zero (amorphous, comparative example), 14.96 and 30% , films were formed on a cover press and tested for tensile strength, right-angle tear strength and friction angle. The results are shown in Table 3.
309821/0317309821/0317
TestprobeTest sample
1,2-Bindung Kristall!- Zugfestig- Dehnung (^-Permeabilität*2^ 9o° *3^ Gleitfesti§1,2-bond crystal! - tensile strength- elongation (^ -permeability * 2 ^ 9o ° * 3 ^ slip resistance
Reiß- keit «4)Tear «4)
nität(5«) keit art) (kg/cm^)nity (5 «) keit type) (kg / cm ^)
keit
(kg/cm) speed
(kg / cm)
Amorphes 1,2-Polybutadien 86,οAmorphous 1,2-polybutadiene 86, ο
2oo2oo
152OO152OO
über 7o*over 7o *
U) O U5 OO U) O U5 OO
kristallines 1,2-Polybutadiencrystalline 1,2-polybutadiene
88,7 92to88.7 92 t o
3030th
9o9o
229229
75o 56 ο75o 56 ο
83 oo 62oo83 oo 62oo
37
9337
93
Anmerkungen: *1) gemegsen in der gleichen Weise wie in Beispiel 2 beschriebenNotes: * 1) measured in the same way as described in example 2
*2)* 2)
gemäß ASTM-D14-34according to ASTM-D14-34
Proben, die mit einem Schneider vom B-Typ gemäß JIS K63o1 geprägt waren, wurden getestet.Samples embossed with a B-type cutter according to JIS K63o1 were tested.
gemessen in der gleichen Weise wie in Beispiel 2measured in the same manner as in Example 2
to toto to
cncn
Es wurden zwei Arten von Polybutadien, die entsprechend 68 % (Vergleichsbeispiel) und 90 % Einheiten in 1,2-Konfiguration enthielten, in der gleichen Weise, wie in Beispiel 2 beschrieben, getestet; die in Tabelle 4 gezeigten Ergebnisse wurden erhalten. .Two kinds of polybutadiene containing 68 % (comparative example) and 90 % units in 1,2-configuration, respectively, were tested in the same manner as described in Example 2; the results shown in Table 4 were obtained. .
(kg/cmz)speed Hl)
(kg / cm z )
dienlybuta
serve
Anmerkungen: »1)Notes: »1)
gerneβsen in der gleichen Weise, wie in Beigladly in the same way as in Bei
spiel 2 beschrieben»game 2 described »
' gemessen in der gleichen Weise wie iß Beispiel 3f'measured in the same way as the example 3f
■3)■ 3)
gemessen in der gleichen Weise wie in Beispiel 2.measured in the same manner as in Example 2.
Gemische aus 1,2-Polybutadien, das 90 % Einheiten in 1,2-Konf iguration enthielt und eine Kristallinität von 25 % und von 1,30 (bestimmt in Toluol bei 300C) aufwies, und Hochdruckpolyäthylen in Mischungeverhältnissen von 20:80, 50:50 und 80:20 ( nach Gewicht) wurden in der gleichen Weise hergestellt, wie in Beispiel 2 beschrieben, und zu Folien mittels einer Deckpresse verarbeitet. Zu Vergleichszwecken wurde 1,2-Polybutadien durch hochanteiliges cis-1,4-Polybutadien (Japan Synthetic Rubber's JSR BROl) ersetzt und mit Folyäthylen in ^ ähnlichen Mischungsverhältnissen gemischt. Die aus den GemischenMixtures of 1,2-polybutadiene units, 90% in 1,2-conf iguration contained and a crystallinity of 25% and of 1.30 (determined in toluene at 30 0 C) exhibited, and high-pressure polyethylene in mixture Ever duty ratios of 20:80 , 50:50 and 80:20 (by weight) were produced in the same way as described in Example 2 and processed into films by means of a cover press. For comparison purposes, 1,2-polybutadiene was replaced by high-proportion cis-1,4-polybutadiene (Japan Synthetic Rubber's JSR BRO1) and mixed with polyethylene in similar proportions. The ones from the mixes
10-«10- «
309821/0317309821/0317
hergestellten Folien wurden ebenfalls getestet. Tabelle 5 zeigt die Ergebnisse.produced films were also tested. Table 5 shows the results.
festig
keit „
(kg/cm2)train
firm
ability "
(kg / cm 2 )
nung
(%) Deh
tion
(%)
meabi-
lität
*1)0 2 -per
meabi-
lity
*1)
Gesamt-
licht-
durch-
läBBig-
keit
(X) -ü2)
Total-
light-
by-
lazy-
speed
(X)
Trü
bung
{*) * 2)
Tru
exercise
{*)
Tempera
tur zum
Warmver
siegeln (0CT
«3)optimal
tempera
ture to
Warmver
seal ( 0 CT
«3)
(1,2-BR)tf, 2-polybutadiene
(1,2-BR)
(Cis-BR)Cis polybutadiene
(Cis-BR)
Anmerkungen: «1) gemeasen ln der gleichen Weise, wie in Beispiel 1Notes: «1) measured in the same way as in example 1
beschrieben; Einheit χ 10""10cc.cm/cm2sek.cmHg.described; Unit χ 10 "" 10 cc.cm/cm 2 sec.cmHg.
Meßtemtperatur: 25,5 C.Measuring temperature: 25.5 C.
gemessen in der gleichen Weise wie in Beispiel 1 beschrieben, mit der Ausnahme, daß die Folien 1 mm dick waren.measured in the same manner as described in Example 1, except that the films 1 mm thick.
zwei Streifen, jeder 1 cm breit, eines jeden Testfilms wurden aufeinander gelegt und gemeinsam durch einen Heißversiegelungstester der Nippon Rika Kogyo heiß versiegelt. Die optimalen Temperaturen wurden aus der Form jedes heiß versiegelten Produktes und aus der Bruchspannung der Heißversiegelung bestimmt· Die Heißversiege-two strips, each 1 cm wide, of each test film were placed on top of one another and shared heat sealed by a heat seal tester of the Nippon Rika Kogyo. The optimal Temperatures became from the shape of each heat-sealed product and from the stress at break the heat seal determines the heat seal
- 11 309821/0317 - 11 309821/0317
lungszeit betrug 2 Sekunden und der Druck 2 kg/cm ,recovery time was 2 seconds and the pressure 2 kg / cm,
Cis-BR allein konnte wegen Schwierigkeiten bei der Herstellung seiner Testproben nicht getestet werden· .Cis-BR alone failed because of difficulties not be tested in the manufacture of its test specimens ·.
Ein geblasener Film wurde aus dem gleichen 1,2-Polybutadien gebildet, das in Beispiel 2 verwendet wurde, und dann einem Bewitterungstest bei 400C mittels eines Bewitterungsgeräts ausgesetzt· Filme aus verschiedenen thermoplastischen Harzen des Handels wurden ebenfalls zus» Vergleichszwecken getestet. Die Ergebnisse sind in Tabelle 6 wiedergegeben. Es ist aus der Tabelle zu entnehmen, daß 1,2-Polybutadien Photovernetzungs eigenschaft besitzt. Der belichtete 1,2-Polybutadien-Film wurde leicht zujStUcken mittels geringer Schläge gebrochen.A blown film was formed from the same 1,2-polybutadiene that was used in Example 2 and then subjected to a weathering test at 40 ° C. using a weatherometer. Films made from various commercial thermoplastic resins were also tested for comparison purposes. The results are shown in Table 6. It can be seen from the table that 1,2-polybutadiene has photocrosslinking property. The exposed 1,2-polybutadiene film was easily broken into pieces by light impacts.
- 12 -- 12 -
309821/0317309821/0317
225Sl1O 225Sl 1O
ErfindungExample d
invention
butadien1,2 poly
butadiene
lenPolyethy
len
(mittels Bewitterungs
apparatur gemessen)Weathering tests:
(by means of weathering
apparatus measured)
lösliches (%Toluene un-
soluble (%
309821/0317309821/0317
Tabelle 6(Fortsetzung)Table 6 (continued)
chloridPolyvinyl
chloride
esterPoly-;
ester
carbonatPoly-
carbonate
styrolPoly
styrene
8 21/03178 21/0317
- 14 -- 14 -
-Ii---Ii--
Es wurde ein Film von 20 /u Dicke aus Polybutadien geformt, das 92 % 1,2-Additionseinheiten, eine Kristallinität von 23 % und Fo] von 1,30 (bestimmt in Toluol bei 300C ) aufwies. Mit dem Polybutadienfilm wurde Fleisch eingewickelt und in einem Kühlschrank bei O0C gelagert; es wurde keinerlei Änderung in der Farbe des Fleisches nach der Lagerung während einer Woche festgestellt.A film with a thickness of 20 μm was formed from polybutadiene which had 92 % 1,2-addition units, a crystallinity of 23 % and Fo] of 1.30 (determined in toluene at 30 ° C.). Meat was wrapped with the polybutadiene film and stored in a refrigerator at 0 ° C .; no change in the color of the meat was observed after one week of storage.
Zum Vergleich verfärbte sich Fleisch, das mit einem PoIyvinylidenchlorid-Film von 20 /u Dicke eingewickelt und im gleichen Kühlschrank gelagert wurde, innerhalb von 2 Tagen. Im Falle von nicht eingewickeltem fleisch trat merkliche Verfärbung innerhalb eines Tages ein.For comparison, meat stained with a polyvinylidene chloride film of 20 / u thickness was wrapped and stored in the same refrigerator within 2 days. in the In the case of meat that was not wrapped, discoloration occurred within a day.
Es wurde ein Film von 50 /u Dicke aus Polybutadien geformt, das 90 % 1,2-Additionseinheiten, eine Kristallinität von 25 % und Mj von 1,61 (bestimmt in Toluol bei 300C) aufwies. Drei Beutel von 25 cm χ 22 cm Größe wurden durch Falten der Polybutadienfilm e von 50 cm χ 22 cm Größe hergestellt. In Jedem Beutel wurden 600 g ABS-Harzpellets gepackt, die drei Krempen Jedes Beutels 2 Sekunden bei 800C und 2 kg/cm Drucfa^ieiß versiegelt. Zu einem Vergleich wurden drei Beutel, die ABS-Harzpellets enthielten, in der gleichen Weise wie oben erhalten, mit der Ausnahme, daß ein Polyäthylenfilm von 50 /u Dicke verwendet und der Film 2 Sekunden bei 1050C und 2 kg/cm Druck heiß versiegelt wurde. Diese Beutel wurden von einer Höhe von 2 m auf Beton bei 25°C fallen gelassen und das Aussehen der Beutel begutachtet. There was formed a film of 50 / u thick of polybutadiene containing 90% 1,2-addition units, a crystallinity of 25% and Mj of 1.61 (determined in toluene at 30 0 C) was obtained. Three bags of 25 cm × 22 cm in size were prepared by folding the polybutadiene films of 50 cm × 22 cm in size. In each bag was packed 600 g of ABS resin pellets, the three rims of each bag sealed two seconds at 80 0 C and 2 kg / cm ^ Drucfa IEISS. For a comparison, contained three bags, the ABS resin pellets obtained in the same manner as described above, hot except that a polyethylene film of 50 used / u thickness, and the film 2 seconds at 105 0 C and 2 kg / cm pressure was sealed. These bags were dropped from a height of 2 m onto concrete at 25 ° C. and the appearance of the bags was observed.
Keine Änderung war bei den drei Beuteln des PolybutadienfilmsThere was no change in the three bags of polybutadiene film
festzustellen, jedoch kam ein heiß versiegelter Teil bei einem Beutel aus Polyäthylenfilm heraus.noted, however, a heat-sealed part came on one Bag out of polyethylene film.
- tft -309821/0317- tft -309821/0317
Claims (7)