DE2161043C3 - Verfahren zum Verbinden von Geweben - Google Patents

Verfahren zum Verbinden von Geweben

Info

Publication number
DE2161043C3
DE2161043C3 DE2161043A DE2161043A DE2161043C3 DE 2161043 C3 DE2161043 C3 DE 2161043C3 DE 2161043 A DE2161043 A DE 2161043A DE 2161043 A DE2161043 A DE 2161043A DE 2161043 C3 DE2161043 C3 DE 2161043C3
Authority
DE
Germany
Prior art keywords
strength
fabric
film
pressing
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE2161043A
Other languages
English (en)
Other versions
DE2161043A1 (de
DE2161043B2 (de
Inventor
Joachim 4041 Zons Wank
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bayer AG
Original Assignee
Bayer AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bayer AG filed Critical Bayer AG
Priority to DE2161043A priority Critical patent/DE2161043C3/de
Priority to DE19722221337 priority patent/DE2221337A1/de
Priority to CA158,289A priority patent/CA981571A/en
Priority to AT1041772A priority patent/ATA1041772A/de
Priority to GB5649072A priority patent/GB1403410A/en
Priority to IT54542/72A priority patent/IT973943B/it
Priority to CH1785072A priority patent/CH554409A/de
Priority to JP12211972A priority patent/JPS563957B2/ja
Priority to NL7216737A priority patent/NL7216737A/xx
Priority to FR7243840A priority patent/FR2162624B1/fr
Priority to NO4541/72A priority patent/NO136200C/no
Priority to BE792480D priority patent/BE792480A/xx
Publication of DE2161043A1 publication Critical patent/DE2161043A1/de
Publication of DE2161043B2 publication Critical patent/DE2161043B2/de
Application granted granted Critical
Publication of DE2161043C3 publication Critical patent/DE2161043C3/de
Expired legal-status Critical Current

Description

Die Erfindung betrifft ein Verfahren zum Verbinden von Geweben, wobei die Verbindungsstelle hochtemperaturbeständig und nicht dicker als die doppelte Gewebedicke ist. 2>
Es ist bekannt, Gewebebahnen mittels Nähen zu verbinden. Diese Verbindungsart hat für zahlreiche Anwendungsfälle den Nachteil, daß die Verbindungsstelle ein Mehrfaches der Dicke des Gewebes aufweist. Hierdurch entstehen beim Aufwickeln der Gewebebahn «1 Wülste, die sich durch mehrere Lagen durchdrücken.
Zur Vermeidung dieser Wulstbildung werden nach einem anderen Verfahren Gewebeenden mittels einer Folie im Hochfrequenzverfahren verschweißt. Bei diesem Verfahren ist es erforderlich, daß die Folie einen r> möglichst hohen dielektrischen Verlustfaktor und einen möglichst niedrigen Erweichungspunkt besitzt, so daß sie beim Schweißen schmilzt. Der Nachteil dieser Methode besteht in der sehr aufwendigen Schweißapparatur und außerdem ist die Schweißnaht nicht genügend temperaturbeständig, so daß bei einer anschließenden Beschichtung mit Kunststoff die Gefahr besteht, daß infolge des niedrigen Erweichungspunktes der Folie die Verbindungsstelle reißt.
Überraschenderweise wurde nun gefunden, daß man 4 > diese Nachteile beheben kann, wenn man nach dem erfindungsgemäßen Verfahren arbeitet. Es betrifft ein Verfahren zum Verbinden von Gewebeteilen, das dadurch gekennzeichnet ist, daß man zwischen die zu verbindenden Gewebeenden eine hochtemperaturbe- ">o ständige Folie einbringt, nachdem man die Gewebeenden mit einem leicht flüchtigen Lösungsmittel für die Folie getränkt hat und die Gewebeenden durch Pressen verbindet.
Hochtemperaturbeständige Folien mit einer Dicke r> zwischen 20 und 100 μ eignen sich für das Verfahren. Besonders geeignet sind Polyhydantoinfolien, die man gemäß der Patentschrift 12 30 568 herstellt.
Als Lösungsmittel eignen sich leicht flüchtige Lösungsmittel, z. B. Methylenchlorid. wi
Der beim Pressen angewendete Druck liegt zwischen 5 — 55 kp/cm2. Üblicherweise wird das Pressen bei Zimmertemperatur durchgeführt. Die Preßtemperatur kann ;ibcr bis zum Siedepunkt des Lösungsmittels erhohl werden, wodurch die Verbindungsfestigkeit noch tu gesteigert und die Preßdauer, die /wischen I Sekunde um.I I Minute liegt /11 den kürzeren /eilen verschoben w ii'il.
Nach dem erfindungsgemäßen Verfahren können Gewebe natürlicher und synthetischer Herkunft innerhalb kurzer Zeit sehr fest und temperaturbeständig verbunden werden, wie zum Beispiel Baumwollgewebe, Gewebe aus Polyester, Polyamiden, Polyurethanen und Glas, ohne daß bei einer anschließenden Beschichtung mit Kunststoff eine Trennung der Gewebebahnen zu beobachten wäre.
Beispiel 1
Zwischen die mit Methylenchlorid benetzten, überlappend liegenden Bahnenden eines Baumwollgewebes wird ein Folienstreifen aus nichtorientierter amorpher Polyhydantcinfolie mit einer Dicke von ca. 40 μ eingelegt Durch Verpressen der Verbindungsstellen bei einer Preßtemperatur von ca. 40° C und einem spezifischen Preßdruck von ca. 20 kp/cm2 werden die Bahnenden ca. 10 see aufeinandergedrückt Die Festigkeit der Verbindungsstelle ist höher als die Festigkeit des Gewebes, sogar bei einem Vergleich der Festigkeiten bei höherer Temperatur. Ein Zahlenwert für die Festigkeit der Verbindungssteile kann somit nicht bestimmt werden. Die Klebestelle ist temperaturbeständig bis 260° C und ist beständig gegen kochende 10%ige Natronlauge, kochendes Wasserstoffperoxid und wird von einer Schmelze aus weichgemachtem PVC nicht geschädigt.
Beispiel 2
Zwischen die mit Methylenchlorid benetzten Bahnenden eines Glasseidengewebes wird ein Folienstreifen aus nichtorientierter amorpher Polyhydantoingießfolie gelegt. Durch Verpressen der Verbindungsstelle bei einer Preßtemperatur von ca. 40°C und einem spezifischen Preßdruck von 20 kp/cm2 werden die Bahnenden ca. 10 see aufeinandergedrückt Die Festigkeit der Verbindungsstelle ist höher als die Festigkeit des Gewebes. Ein Zahlenwert für die Festigkeit der Verbindungsstelle kann somit nicht bestimmt werden. Die Klebestelle ist temperaturbeständig bis 260° C.
Beispiel 3
Zwischen die mit Methylenchlorid benetzten, überlappend liegenden Bahnenden eines Polyestergewebes wird ein Folienstreifen aus nichtorientierter amorpher Polysulfonfolie, die aus einem Polysulfon bestehend aus der wiederkehrenden Einheit
hergestellt wurde, mit einer Dicke von ca. 40 μ eingelegt. Durch Verpressen der Verbindungsstellen bei einer Preßtemperatur von ca. 40° C und einem spezifischen Preßdruck von ca. 20 kp/cm2 werden die Bahnenden ca. 10 see aufeinandergedrückt. Die Festigkeit der Verbindungsslelle ist höher als die Festigkeit des Gewebes, sogar bei einem Vergleich der Festigkeiten bei höherer Temperatur. Ein Zahlenwert für die Festigkeit der Verbindungsstelle kann somit nicht bestimmt werden. Die Klebestelle isi temperaturbeständig bis 2000C und ist beständig gegen kochende l,0%ige Natronlauge, kochendes Wasserstoffperoxid und wird von einer Schmelze aus v. en hgeniachlem I1VC' mein geschädigt.
Beispiel 4
Zwischen die mit Methylenchlorid benetzten Bahnenden eines Polyamidgewebes wird ein Folienstreifen aus nichtorientierter amorpher Polyäthersulfonfolie, die aus einem Polymer, bestehend aus der wiederkehrenden Einheit
-SO,-
-0
hergestellt wurde, gelegt. Durch Verpressen der Verbindungsstelle bei einer Preßtemperatur von ca. 40° C und einem spezifischen Preßdruck von 20 kp/cm2 werden die Bahnenden ca. 10 see aufeinandergedrückt. Die Festigkeit der Verbindungsstelle ist höher als die Festigkeit des Gewebes. Ein Zahlenwert für die Festigkeit der Verbindungsstelle kann somit nicht bestimmt werden. Die Klebestelle ist temperaturbeständig bis 240°C.
Beispiel 5
Zwischen die mit Methylenchlorid benetzten, überlappend liegenden Bahnenden eines Baumwollgewebes wird ein Folienstreifen aus nichtorientierter amorpher Polycarbonatfolie auf Basis Isatinbisphenol mit einer Dicke von ca. 40 μ eingelegt Durch Verpressen der Verbindungsstellen bei einer Preßtemperatur von ca. 40° C und einem spezifischen Preßdruck von ca. 20 kp/cm2 werden die Bahnenden ca. 10 see aufeinandergeurückt. Die Festigkeit der Verbindungsstelle ist höher als die Festigkeit des Gewebes, sogar bei einem Vergleich der Festigkeiten bei höherer Temperatur. Ein Zahlenwert für die Festigkeit der Verbindungsstelle ι» kann somit nicht bestimmt werden. Die Klebestelle ist temperaturbeständig bis 26O0C und wird von einer Schmelze aus weichgemachtem PVC nicht geschädigt.
Beispiel 6
ι ΐ Zwischen die mit Methylenchlorid benetzten Bahnenden eines Leinengewebes wird ein Folienstreifen aus nichtorientierter amorpher Polybenzoxazindionfolie auf Basis Thiobissalicylsäure gelegt. Durch Verpressen der Verbindungsstelle bei einer Preßtemperatur von ca.
j(i 40° C und einem spezifischen Preßdruck von 20 kg/cm2 werden die Bahnenden ca. 10 see aufeinandergedrückt. Die Festigkeit der Verbindungsstelle ist höher als die Festigkeit des Gewebes. Ein Zahlenwert für die Festigkeit <jer Verbindungsstelle kann somit nicht
r. bestimmt werden. Die Klebestelle ist temperaturbeständig bis 300° C.

Claims (3)

Patentansprüche:
1. Verfahren zum Verbinden von Gewebeteilen, dadurch gekennzeichnet, daß man zwi- ϊ sehen die zu verbindenden Gewebeenden eine hochtemperaturbeständige Folie einbringt, nachdem man die Gewebeenden mit einem leicht flüchtigen Lösungsmittel für die Folie getränkt hat und die Gewebeenden durch Pressen verbindet κ
2. Verfahren gemäß Anspruch 1, dadurch gekennzeichnet, daß man als hochtemperaturbeständige Folie eine Polyhydantoinfolie verwendet
3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß man als Lösungsmittel Methylenchlo- rid verwendet.
DE2161043A 1971-12-09 1971-12-09 Verfahren zum Verbinden von Geweben Expired DE2161043C3 (de)