DE2123313B2 - PROCESS FOR MANUFACTURING HUETTENKOKS - Google Patents

PROCESS FOR MANUFACTURING HUETTENKOKS

Info

Publication number
DE2123313B2
DE2123313B2 DE19712123313 DE2123313A DE2123313B2 DE 2123313 B2 DE2123313 B2 DE 2123313B2 DE 19712123313 DE19712123313 DE 19712123313 DE 2123313 A DE2123313 A DE 2123313A DE 2123313 B2 DE2123313 B2 DE 2123313B2
Authority
DE
Germany
Prior art keywords
coke
coal
addition
added
coking
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19712123313
Other languages
German (de)
Other versions
DE2123313A1 (en
DE2123313C3 (en
Inventor
Yasuo Miura Mitsutoshi Yokohama Hayashi (Japan)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Engineering Corp
Original Assignee
Nippon Kokan Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Kokan Ltd filed Critical Nippon Kokan Ltd
Publication of DE2123313A1 publication Critical patent/DE2123313A1/en
Publication of DE2123313B2 publication Critical patent/DE2123313B2/en
Application granted granted Critical
Publication of DE2123313C3 publication Critical patent/DE2123313C3/en
Expired legal-status Critical Current

Description

Es ist auch schon der Einfluß metallischer Füllstoffe auf die Vorgänge beim Verkoken von Kohle untersucht worden, und zwar bei Zugabe in Pulverform. Die Teilchen hatten dabei einen Durchmesser von 5 bis 15 μ und machten 1 oder mehr Prozent des Volumens aus. Die Versuche zeigten, daß durch diese metallischen Füllstoffe wie Eisen, Kupfer, Silber und Kobalt die Porenbildung beeinflußt wird, aber die Versuchsergebnisse zeigten noch nicht, wie auf wirtschaftliche Weise die Trommelbeständigkeit des Kokses verbessert werden kann. Nach der Erfindung wird das erreicht, wenn folgende Bedingungen eingehalten werden:It is also the influence of metallic fillers on the processes involved in the coking of coal has been investigated when added in powder form. The particles had a diameter from 5 to 15 μ and made up 1 or more percent of the Volume. The tests showed that these metallic fillers such as iron, copper, silver and Cobalt affects pore formation, but the test results did not yet show how economical it was Way the drum resistance of the coke can be improved. According to the invention this is achieved if the following conditions are met:

a) Die metallischen Zusätze sollen Draht- oder Faserform haben bzw. die zugesetzte Kohle \ aserform;a) The metallic additives are intended to wire or fiber form or have the added coal \ aserform;

b) der Durchmesser bzw. die Breite des zugegebenen und zugemischten Materials soll im Bereich von 0,1 bis 0,8 mm und die Länge im Bereich von 2 mm bis 150 mm liegen;b) the diameter or the width of the added and mixed material should be in the range of 0.1 to 0.8 mm and the length in the range of 2 mm to 150 mm;

c) die zugegebene Menge soll 0,01 bis 0,05 Gewichtsprozent betragen.c) the amount added should be 0.01 to 0.05 percent by weight.

Durch die Zugabe der angegebenen Füllstoffe in dieser Form wird die Wärmeübertragung von der Wandung bis zum Zentrum des Ofens beschleunigt und vergleichmäßigt. Die Risse, die im Koks während der Verkokung auftreten, werden verbunden, und die Graphitbildung wird durch den Wärmeausgleich verbessert. By adding the specified fillers in this form, the heat transfer from the Wall accelerated and equalized up to the center of the furnace. The cracks made in the coke during the coking occur, are connected, and the graphite formation is improved by the heat balance.

Als Material kommen in erster Linie Stahl, rostfreier Stahl, Kupfer, Kohlenstoff-Fasern und kohlenstoffreiche, synthetische Harze in Frage. Es ist nicht immer erforderlich, daß der Querschnitt der drahtförmigen oder drahtartigen Materialien kreisförmig ist. Wenn die Dimensionen innerhalb des obenerwähnten Bereiches liegen, kann ein kleines Stück, das aus einem blattförmigen Material, wie aus einem Blech, geschnitten wird, ebenfalls verwendet werden. Es versteht sich, daß auch draht- oder schnitzeiförmiger Schrott geeignete Materialien darstellen.The main materials used are steel, stainless steel, copper, carbon fibers and high-carbon, synthetic resins in question. It is not always necessary that the cross-section of the wire-shaped or wire-like materials is circular. If the dimensions are within the aforementioned Area, a small piece made of a sheet-like material, such as sheet metal, cut can also be used. It goes without saying that wire-shaped or carved-shaped Suitable materials for scrap.

Der Grund, daß die Abmessungen der zugesetzten Materialien, wie oben angegeben, beschränkt sind, liegt darin, daß, wenn das Material zu klein ist, es dazu neigt, bei der erhöhten Temperatur, d. h. bei einer Temperatur von mehr als 13000C, zu schmelzen, wogegen, wenn das Material zu groß ist, sich eine schlechte Verträglichkeit mit den gemischten Kohlen ergibt.The reason that the dimensions of the added materials as indicated above, are limited, is that if the material is too small, it tends, at the elevated temperature, ie at a temperature of more than 1300 0 C to melt, whereas if the material is too large, there will be poor compatibility with the mixed coals.

Die Begrenzung hinsichtlich der Länge beruht auf ähnlichen Gründen. Wenn das Material zu kurz ist,The limitation on the length is based on similar reasons. If the material is too short,

neigt das Material dazu, zu schmelzen, und wenn es zu lang ist, wird es schwierig, die Korngröße des Kokses zu steuern. Wenn die Materialzugabe unterhalb 0,01 Gewichtsprozent liegt, werden das Zusammenhaften und die Wärmeübertragung verschlechtert. Wenn andererseits die Menge zu hoch liegt, ergeben sich im allgemeinen keine Schwierigkeiten. Jedoch sollte die zugefügte Menge aus wirtschaftlichen Überlegungen auf einen bestimmten Wert begrenzt werden. Wenn z. B. die monatlich hergestellte Koksmenge 250 000 t/Monat erreicht, wären bei einer Zugabemenge von 1 Gewichtsprozent 25001 des drahtartigen Materials pro Monat erforderlich. Selbst wenn das Material Stahldraht ist, der leicht erhältlich ist, ist es nicht leicht, eine derart große Menge von Eisendraht herzustellen. Dies ist ein Grund dafür, daß die zugesetzte Menge auf weniger als 0,5 Gewichtsprozent begrenzt wird.the material tends to melt and if it is too long it becomes difficult to determine the grain size of the Control coke. If the material addition is below 0.01 percent by weight, sticking together will occur and the heat transfer deteriorates. On the other hand, if the amount is too high, yield generally no difficulties. However, the amount added should be economical Considerations are limited to a certain value. If z. B. the monthly amount of coke produced Reached 250,000 t / month, an addition amount of 1 percent by weight would be 25001 of the wire-like Materials required per month. Even if the material is steel wire, it is easily available is, it is not easy to manufacture such a large amount of iron wire. This is one reason for that the amount added is limited to less than 0.5 percent by weight.

Die Eigenschaften des erfindungsgemäß hergestellten Kokses sind, wie sich aus den folgenden Beispielen ergibt, ausgezeichnet. Das heißt, Trommelfestigkeiten von etwa 1,0% (Festigkeit gemäß dem Trommel-Index) und Sturzfestigkeit 50 mm von etwa 6% (Sturz-Index) können mit Leichtigkeit erzielt werden.The properties of the coke prepared according to the invention are as can be seen from the following examples results, excellent. That is, drum strengths of around 1.0% (strength according to the drum index) and drop resistance 50 mm of about 6% (drop index) can be achieved with ease.

Verwendete Kohlearten:Types of coal used:

Beatrice, Tams:Beatrice, Tams:

Niedrigflüchtige Kohlen aus den USA. Davis, B., Eagle, S.:Low volatile coals from the USA. Davis, B., Eagle, S .:

Mittelflüchtige Kohlen aus den USA. Vicary:Medium volatile coals from the USA. Vicary:

Mittelflüchtige Kohlen aus Kanada. R. Moure, Itman:Medium volatile coals from Canada. R. Moure, Itman:

Mittelflüchtige Kohlen aus Australien, ölkoks: Inlandkohle.Medium volatility coals from Australia, oil coke: inland coal.

Zugesetzte drahtartige Materiahen:Added wire-like materials:

Durchmesser 0,6 mmDiameter 0.6 mm

Länge 60 mmLength 60 mm

Zugegebene Menge etwa 0,17 GewichtsprozentAmount added about 0.17 percent by weight

Mischverhältnis: Wie in den Tabellen I, II und III angegeben.Mixing ratio: As indicated in Tables I, II and III.

Verkokungstemperatur:Coking temperature:

Grundkohlen:Base coals:

übliche gemischte Kohlen ohne drahtartige Materialien.common mixed coals without wire-like materials.

Tabelle ITable I.

Kohlearl, %Carbon pearl,% Tl, %Tl,% Erfindungsgemäß
versetzte KohleAccording to the invention
staggered coal GrundkohleBase coal Differenzdifference Beat rice 7Beat rice 7 15 mm15 mm 90,190.1 89,289.2 + 0,9+ 0.9 Tams 7Tams 7 25 mm25 mm 82,782.7 82,482.4 + 0,3+ 0.3 Davis, B. 27Davis, B. 27 50 mm50 mm 15,915.9 15,515.5 + 0,4+ 0.4 Eagle, S. 10Eagle, p. 10 ST %ST% —- —- —- Vicary 7Vicary 7 75 mm75 mm 16,916.9 9,39.3 + 7,6+ 7.6 R. M ou re 14R. M ou re 14 50 mm50 mm 65,865.8 56,556.5 + 9,3+ 9.3 ölkoks 5oil coke 5 38 mm38 mm 82,482.4 78,478.4 + 4,0+ 4.0 lnlandkohle höherer Qualität 16Higher quality inland coal 16 25 mm25 mm 94,294.2 93,993.9 + 0,3+ 0.3 Inlandkohle niedrigerer Qualität 7Lower quality domestic coal 7 15 mm15 mm 97,297.2 96,996.9 +0,3+0.3

Tabelle HTable H.

TI, %TI,% Erfindungs-Inventive ErfindungsInvention OrUFlQ-
kohle OrUFlQ-
money Differenzdifference Differenzdifference Kohleart, %Type of coal,% gemäß veraccording to ver gemäß veraccording to ver setzte Kohleput coal setzte Kohleput coal (Fe)(Fe) (Cu)(Cu) 15 mm15 mm (Fe)(Fe) (Cu)(Cu) 89,089.0 +0,4+0.4 + 1,4+ 1.4 Bea t rice 7Bea t rice 7 25 mm25 mm 89,489.4 90,490.4 81,981.9 +0,7+0.7 + 2,4+ 2.4 Tams 7Tams 7 50 mm50 mm 82,682.6 84,384.3 15,315.3 + 3,9+ 3.9 + 0,7+ 0.7 Davis, B. 26Davis, B. 26 ST %ST% 19,119.1 16,016.0 —- —- —- Eagle, S. 8Eagle, p. 8 75 mm75 mm —- —- 15,715.7 -0,6-0.6 -2,4-2.4 Vicary 10Vicary 10 50 mm50 mm 15,115.1 13,313.3 60,760.7 + 1,6+ 1.6 + 0,3+ 0.3 R. M 0 u re 14R. M 0 u re 14 38 mm38 mm 62,362.3 61,061.0 82,882.8 -0,1-0.1 + 0,8+ 0.8 ölkoks 3oil coke 3 25 mm25 mm 82,782.7 83,683.6 94,194.1 +0,3+0.3 +0,1+0.1 Itman 7Itman 7 15 mm15 mm 94,494.4 94,294.2 96,096.0 +0,8+0.8 + 1,3+ 1.3 lnlandkohle höherer Qualität 18Higher quality inland coal 18 96,896.8 97,397.3

Tabelle mTable m

TUV.TUV. (1)(1) (2)(2) Mil 3%Mil 3% Mit 6%With 6% Grund-Reason-
lcohlelcohle (l)
Differenz(l)
difference (2)
Differenz(2)
difference J /O
Pech
Differenz Y / O
bad luck
difference 6%6% Kohleart, %Type of coal,% Frfgcm.
versetzte
Kohle Frfgcm.
displaced
money Erfgem.Successful
versetztedisplaced
Kohlemoney Pechbad luck
versetztedisplaced
Kohlemoney Pechbad luck
versetztedisplaced
Kohlemoney (Fe)(Fe) (Fe)(Fe) Pech
Differenzbad luck
difference 15mm15mm (Fe)(Fe) (Fe)(Fe) 88,388.3 + 1,5 + 1.5 +2,4+2.4 +2,3+2.3 Beatrice 7Beatrice 7 25 mm25 mm 89,889.8 90,790.7 90,690.6 91,391.3 80,480.4 + U+ U +2,2+2.2 + 1,0 + 1.0 + 2,0 + 2.0 Tarns 7 Tarns 7 50 mm50 mm 82,582.5 82,682.6 81,481.4 84,484.4 20,320.3 +4,9+4.9 + 2,2+ 2.2 -7,3-7.3 +4,0+4.0 Davis, B. 26Davis, B. 26 ST %ST% 25,225.2 22,522.5 13,013.0 15,415.4 —- —- —- —- -5,1-5.1 Eagle, S. 8Eagle, p. 8 75 mm75 mm —- —- —- —- 17,417.4 +9,2+9.2 —- -1,4-1.4 —- Vicary 10Vicary 10 50 mm50 mm 26,626.6 20,520.5 16,016.0 14,014.0 56,056.0 +4,8+4.8 —- + 3,2+ 3.2 -2,6-2.6 R. Moure 14R. Moure 14 38 mm38 mm 70,870.8 67,667.6 59,059.0 60,060.0 81,181.1 + 3,5 + 3.5 —- +0,7+0.7 +4,0+4.0 tflkoks 5tflc coke 5 84,684.6 85,285.2 81,881.8 83,583.5 + 2,4 + 2.4 InlandkohleInland coal höhererhigher 25 mm 25 mm 94,494.4 + 1,0 + 1.0 -- +0,1+0.1 Qualität 14 Quality 14 94,394.3 94,794.7 94,594.5 95,295.2 + 0,8+ 0.8 lnlandkohleinland coal 15 mm 15 mm 97,097.0 -0,2-0.2 —- +0,4+0.4 niedrigerer
Qualität 9lower
Quality 9 96,896.8 97,097.0 97,497.4 97,397.3 + 0,3+ 0.3

Anmerkungannotation

Die Spalte »TI« bezeichnet die Untersuchungen gemäß dem Trommel-Index, und die mit »ST« bezeichneten Werte sind die nach dem Sturz-Test erhaltenen.The column "TI" denotes the tests according to the drum index, and the values denoted by "ST" are those after the Received fall test.

Die mittleren Werte für die Trommelfestigkeit und für die Sturzfestigkeit sind in den folgenden Tabellen IV und V angegeben.The mean values for the drum strength and for the drop strength are in the following Tables IV and V indicated.

ArtArt 15 mm 15 mm 2525th mmmm Tabelle VTable V 50 mm50 mm 38 mm38 mm 1,91.9 oO Ά) mm Ά) mm Grundkohle ..Base coal .. 88 888 8 88th 66th Sturz-TestFall test 57,557.5 81.081.0 204204 Tabelle IVTable IV Versetzte Kohle .Staggered coal. 90 090 0 8? 68th? 6th 75 mm75 mm 65,565.5 82,982.9 20 620 6 Differenz difference + 1 J + 1 y 4-4- 13,313.3 + 8,0+ 8.0 ++ + 03+ 03 19,919.9 Trommel-TestDrum test + 6,3+ 6.3 ArtArt 15 mm15 mm Grundkohle ....Basic coal .... 25 mm25 mm 97,197.1 Versetzte KohleStaggered coal 942942 97,097.0 Differenz difference 94.494.4 -0,1-0.1 +0.,:+0.,: ιι

Anmerkungannotation

»Versetzte Kohlen« sind die gemischten Kohlen, die durch Zugabe der drahtartigen Materialien zu den Grundkohlen erhalten wurden. Die mittleren Teilchengrößen bei dem obenerwähnten Sturztest sind die folgenden:"Offset coals" are the mixed coals obtained by adding the wire-like materials to the base coals. The mean particle sizes in the above-mentioned drop test are as follows:

Grundkohlen 54,5%Base coals 54.5%

Versetzte Kohlen 57,9%Offset coals 57.9%

Differenz 3,4%Difference 3.4%

Die in den obigen Tabellen angegebenen Werte wurden mit Hilfe eines Test-Koksofens erhalten. Aus den Tabellen ergibt sich, daß die Ergebnisse der errindungsgemäß versetzten Kohle besser als die der Grundkohle sind. Insbesondere die Tatsache, daß die mittlere Korngröße der versetzten Kohle der der Grundkohle um etwa 3% überlegen ist, weist auf die verminderte Zerbrechlichkeit des Kokses hin. Es ist im allgemeinen gut bekannt, daß die mit einem Testofen erhaltenen Ergebnisse schlechter sind als die mit einem echten Koksofen. Dies beruht darauf, daß die Verkokungsgeschwindigkeit des Test-Koksofens größer ist als die in einem wirklichen Koksofen. Demzufolge sind die Wirkungen der Zugabe von drahlförmigen oder drahtartigen Materialien, die sich bei Anwendung eines echten Ofens ergeben, besser als die Ergebnisse, die man bei einem Testofen erreicht.The values given in the tables above were obtained with the aid of a test coke oven. the end the tables shows that the results of the inventions offset coal are better than that of the base coal. In particular, the fact that the mean grain size of the offset coal, which is superior to the base coal by about 3%, indicates the decreased fragility of the coke. It is generally well known that those with a test oven results obtained are worse than those obtained with a real coke oven. This is because the The coking rate of the test coke oven is greater than that of a real coke oven. As a result are the effects of the addition of wire-like or wire-like materials that change when applied results obtained with a real oven are better than the results obtained with a test oven.

Weiterhin konnte an dem Aussehen des Kokses kein nachteiliger Effekt auf Grund der Zugabe der drahtartigen Materialien festgestellt werden. Das heißt, die Neigung der Abtrennung wird nicht beobachtet, und die Bildung kleiner Löcher wird nicht verhindert. Die Oberflächenqualitäl des Kokses ist ebenfalls sehr gut. Somit ist das Aussehen des Kokses ebenso gut wie das von bekanntem Koks.Furthermore, no adverse effect due to the addition of the coke could be found on the appearance of the coke wire-like materials are detected. That is, the tendency of separation is not observed, and the formation of pinholes is not prevented. The surface quality of the coke is also very good. Thus, the appearance of the coke is as good as that of the known coke.

Claims (3)

Patentansprüche:Patent claims: 1. Verfahren zur Herstellung von Hüttenkoks durch Verkoken von Kohle in einem Koksofen unter Zugabe von metallischem Material oder von Kohlenstoff, gekennzeichnet durch folgende Merkmale:1. Process for the production of metallurgical coke by coking coal in a coke oven with the addition of metallic material or carbon, characterized by the following Characteristics: a) Die metallischen Zusätze sollen Draht- oder Faserform haben bzw, die zugesetzte Kohle Faserfonn;a) The metallic additives should have wire or fiber form or the added carbon Fiber form; b) der Durchmesser bzw. die Breite des zugegebenen und zugemischten Materials soll im Bereich von 0,1 bis 0,8 mm und die Länge im Bereich von 2 bis 150 mm liegen;b) the diameter or the width of the added and mixed material should be in Range from 0.1 to 0.8 mm and the length in the range from 2 to 150 mm; c) die zugegebene Menge soll 0,01 bis 0,5 Gewichtsprozent betragen.c) the amount added should be 0.01 to 0.5 percent by weight be. 2. Verfahren zur Herstellung von Hüttenkoks nach Anspruch 1, dadurch gekennzeichnet, daß das zugegebene und zugemischte Material Stahl, rostfreier Stahl oder Kupfer ist.2. A method for the production of metallurgical coke according to claim 1, characterized in that the added and mixed material is steel, stainless steel or copper. 3. Verfahren zur Herstellung von Hüttenkoks nach Anspruch 1, dadurch gekennzeichnet, daß für das zugegebene und zugemischte Material draht- oder schinitzelformigcr Schrott verwandt wird.3. A method for the production of metallurgical coke according to claim 1, characterized in that for the added and mixed material used wire- or schinitzel-shaped scrap will. 3°3 ° 3535 Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung von Hüttenkoks in einem Koksofen unter Zugabe von metallischem Material oder von Kohlenstoff.The present invention relates to a method for producing metallurgical coke in a coke oven with the addition of metallic material or carbon. Eine der wichtigen Eigenschaften von Koks, der als Hüttenkoks zur Herstellung von Eisen u. dgl. verwendet werden soll, ist seine Festigkeit. Das Brechen bzw. Zerbrechen des Kokses, das bei den Entnahme-, Lagerungs- und Beschickungsstufen eintreten kann, muß möglichst vermieden werden. Aus diesem Grunde wurden viele Verfahren, gemäß denen dieser Koks verbessert werden kann, vorgeschlagen und in die Praxis eingeführt. Es ist z. B. gut bekannt, daß man mittelhartes Pech, das etwa die chemische Qualität von Kokskohle aufweist, Anthrazit, ölkoks, der als Aggregat nützlich ist, oder Ferrokoks, der durch Vermischen von calciniertem Eisenerz mit einer Kokskohle hergestellt wird, zu der Kokskohle oder zu gemischter Kohle zugeben kann.One of the important properties of coke, which is used as metallurgical coke to make iron and the like is to be its strength. The breaking or breaking of the coke that occurs during the removal, Storage and loading stages can occur must be avoided as far as possible. For this reason many methods by which this coke can be improved have been proposed and included in US Pat Practice introduced. It is Z. B. It is well known that one has medium-hard pitch, which is about the chemical quality of coking coal, anthracite, oil coke, which is useful as an aggregate, or ferrocoke, which is made by mixing of calcined iron ore with a coking coal, to the coking coal or to mixed Can add coal. Es ist jedoch ebenfalls bekannt, daß die bisher bekannten Verfahren die im folgenden angegebenen ungünstigen Nachileile aufweisen:However, it is also known that the previously known methods are unfavorable as given below Have disadvantages: 1. Die Zugabe von Pech kann die Fluidität der Kohle steigern, wenn die Betriebsgeschwindigkeit des Ofens niedrig liegt und die Verkokungstemperatur unterhalb 12000C liegt. Wenn jedoch die Temperatur höher als 1200° C liegt, wird aus dem Pech Kohlenstoff an den Ofenwandungen abgeschieden, auf Grund dessen die Thermozersetzung im Ofen heftig wird, was das Ausströmen von Gasen und den Ausstoßbetrieb des Ofens beeinflussen kann. Diese Tatsache fördert die Bildung von Blasen in dem Koks, wodurch eine Verminderung der Festigkeit hervorgerufen wird. 2. Die Zugabe von inaktiven Materialien, wie Anthrazit, ähnlicher Kohle, Pulverkoks, ölkoks, mineralischen Materiahen od. dgl. als Kernmaterial ist nützlich zur Verbesserung der Festigkeit einer Kohle, die ein Verbackungsvermögen und eine Fluidität aufweist Wenn jedoch eine derartige Kohle, deren Fluidität gering ist, wie eine kanadische Kohle oder eine australische Kohle, mit anderen Kohlen vermischt wird, sollte die Zugabe der obenerwähnten inaktiven Materialien begrenzt werden, da diese Zugabe das Verbakkungsvermögen beeinträchtigt.1. The addition of pitch can increase the fluidity of the coal, when the operation speed of the furnace is low, and the coking temperature is below 1200 0 C. However, if the temperature is higher than 1200 ° C, carbon is deposited from the pitch on the furnace walls, due to which the thermal decomposition in the furnace becomes violent, which can affect the outflow of gases and the discharge operation of the furnace. This fact promotes the formation of bubbles in the coke, causing a decrease in strength. 2. The addition of inactive materials such as anthracite, like coal, powder coke, oil coke, mineral materials od. The like. As a core material is useful for improving the strength of a coal that has a caking ability and fluidity. However, if such a coal, its fluidity is small, such as a Canadian coal or an Australian coal, is mixed with other coals, the addition of the above-mentioned inactive materials should be limited because this addition impairs the caking ability.
DE2123313A 1970-05-11 1971-05-11 Process for the production of metallurgical coke Expired DE2123313C3 (en)