DE202019104379U1 - Heated glass fiber fleece - Google Patents

Heated glass fiber fleece Download PDF

Info

Publication number
DE202019104379U1
DE202019104379U1 DE202019104379.2U DE202019104379U DE202019104379U1 DE 202019104379 U1 DE202019104379 U1 DE 202019104379U1 DE 202019104379 U DE202019104379 U DE 202019104379U DE 202019104379 U1 DE202019104379 U1 DE 202019104379U1
Authority
DE
Germany
Prior art keywords
glass fiber
heatable
fiber fleece
binder
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
DE202019104379.2U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Future Carbon GmbH
Original Assignee
Future Carbon GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Future Carbon GmbH filed Critical Future Carbon GmbH
Priority to DE202019104379.2U priority Critical patent/DE202019104379U1/en
Publication of DE202019104379U1 publication Critical patent/DE202019104379U1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Beheizbares Glasfaservlies, umfassend eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, wobei das Flächengewicht des beheizbaren Glasfaservlieses mindestens 250 g/m2 beträgt.

Figure DE202019104379U1_0000
A heatable glass fiber nonwoven comprising a coating comprising at least one conductivity additive and at least one binder, wherein the basis weight of the heatable glass fiber nonwoven is at least 250 g / m 2 .
Figure DE202019104379U1_0000

Description

Gebiet der ErfindungField of the invention

Die vorliegende Erfindung betrifft ein beheizbares Glasfaservlies, welches insbesondere geeignet ist, direkt auf ein Substrat oder auf eine auf dem Substrat befindliche Grundierung und/oder Kleberschicht angebracht zu werden, ein Glasfaservliesbauteil, enthaltend das beheizbare Glasfaservlies, ein Kit zum Herstellen eines Glasfaservliesbauteils und einen Gegenstand, einen Boden, eine Wand und/oder eine Decke, enthaltend das erfindungsgemäße beheizbare Glasfaservlies, Glasfaservliesbauteil und/oder Kit. Ferner betrifft die vorliegende Erfindung die Verwendung dieser Gegenstände zum Beheizen eines Gegenstandes, eines Bodens und/oder eines Raumes oder zum Abschirmen eines Gegenstandes und/oder Raumes vor elektromagnetischer Strahlung und ein Verfahren zum Beheizen eines Gegenstandes, Bodens und/oder Raumes unter Verwendung des erfindungsgemäßen beheizbaren Glasfaservlieses, Glasfaservliesbauteils und/oder Kits.The present invention relates to a heatable glass fiber fleece, which is particularly suitable for being applied directly to a substrate or to a primer and / or adhesive layer located on the substrate, a glass fiber fleece component comprising the heatable glass fiber fleece, a kit for producing a glass fiber fleece component and an article , a floor, a wall and / or a ceiling, containing the inventive heatable glass fiber fleece, glass fiber fleece component and / or kit. Furthermore, the present invention relates to the use of these articles for heating an article, a floor and / or a room or for shielding an object and / or space from electromagnetic radiation and a method for heating an object, floor and / or room using the inventive heatable glass fiber fleece, glass fiber fleece component and / or kits.

Hintergrundbackground

Die Beheizung der Oberfläche eines Objektes oder Körpers ist in vielen Lebenslagen erforderlich, wobei bei der Beheizung von Räumen vielerorts elektrische Wandheizvorrichtungen, die beispielsweise mäanderförmige Heizdrähte aufweisen, oder wassergestützte Boden- und/oder Wandheizvorrichtungen, in denen erwärmtes Wasser zirkuliert, eingesetzt werden können. Gemein ist diesen Heizvorrichtungen, dass sie Wandoberflächen auf eine gewünschte Temperatur erwärmen, wobei, da diese erwärmten Wände mit den übrigen mobilen und immobilen Gegenständen des Raumes (wie Möbel, Luft, Decke, Fußboden und Wände, an denen keine Boden- und/oder Wandheizvorrichtung befestigt ist) im Temperaturaustausch stehen, diese übrigen mobilen und immobilen Gegenstände des Raumes schlussendlich die gleiche Temperatur wie die erwärmten Wände aufweisen.The heating of the surface of an object or body is required in many situations, wherein in the heating of rooms in many places electric wall heaters, which have, for example, meandering heating wires, or water-based floor and / or wall heaters in which heated water circulates, can be used. Common to these heaters is that they heat wall surfaces to a desired temperature, as these heated walls interact with the other mobile and immobile objects of the room (such as furniture, air, ceiling, floor and walls, where there is no floor and / or wall heater is fixed) in the temperature exchange stand, this remaining mobile and immobile objects of the room ultimately have the same temperature as the heated walls.

Auch ist die Verwendung einer leitfähigen Beschichtung, üblicherweise enthaltend ein oder mehrere leitfähige Zusatzstoffe, zur Anbringung auf der Baustelle (also „vor Ort“), grundsätzlich bekannt. Eine direkte Auftragung derartiger Beschichtungen auf einer Wand und/oder einer Decke „vor Ort“ kann grundsätzlich den Vorteil haben, dass eine individuelle Anpassung an die räumlichen Gegebenheiten möglich ist. Jedoch hat dies den Nachteil, dass mehrere Arbeitsschritte und Trocknungsschritte vor Ort notwendig sind und somit die Bauzeit verlängert wird. Unter Umständen ist zudem eine fachgerechte Anbringung vor Ort nicht immer gewährleistet, so dass die tatsächlich erreichte Heizleistung wesentlich geringer ausfällt als die bei fachgerechtem Anbringen erreichbare. Zudem ist in vielen Bereichen die Anbringung eines Glasfaservlieses wünschenswert, beispielsweise in einem Dachgeschoss, da Dachstühle aus Holz in Bewegung sind und andere Oberflächen (beispielsweise Raufasertapete) reißen könnten und Gipsfaserplatten Risse bekommen können. Die Anbringung eines Glasfaservlieses über einer beheizbaren Schicht könnte jedoch die Heizleistung dieser Schicht verringern und/oder zu einem Wärmestau führen. Zudem ist die fachgerechte Abbringung einer leitfähigen Beschichtung auf einem Glasfaservlies (oder darüber liegenden Schichten) „vor Ort“ nicht oder nur eingeschränkt möglich. Darüber hinaus wären ebenfalls mehrere Arbeitsschritte und Trocknungsschritte vor Ort notwendig was zu einer Verlängerung der Bauzeit führen würde.Also, the use of a conductive coating, usually containing one or more conductive additives, for attachment to the site (ie "on site"), basically known. A direct application of such coatings on a wall and / or a ceiling "on site" can in principle have the advantage that an individual adaptation to the spatial conditions is possible. However, this has the disadvantage that several steps and drying steps are necessary on site and thus the construction time is extended. Under certain circumstances, a professional installation on site is not always guaranteed, so that the actually achieved heating power is much lower than the achievable with professional installation. In addition, in many areas, the attachment of a fiberglass mat is desirable, for example, in an attic, because wood trusses are in motion and other surfaces (such as Raspasertapete) could break and gypsum fiber can crack. However, the attachment of a glass fiber fleece over a heatable layer could reduce the heat output of this layer and / or lead to a heat accumulation. In addition, the professional delivery of a conductive coating on a glass fiber fleece (or overlying layers) "on site" is not possible or only to a limited extent. In addition, several steps and drying steps would also be necessary on site, which would lead to an extension of the construction period.

Zudem kann es wünschenswert sein, Gegenstände, wie beispielsweise Rohre, Werkzeuge, etc. zu beheizen. Die Verwendung einer wassergestützten Heizung beansprucht jedoch eine Menge Platz. Zudem ist eine homogene Beheizung u.U. schwierig. Die Verwendung beheizbarer Beschichtungen ist hierfür prinzipiell denkbar. Jedoch werden derartige Beschichtungen u.U. durch thermische Expansion des beheizten Gegenstandes beschädigt, oder es müssen entsprechende Vorkehrungen getroffen werden, dass dies nicht passiert, was weiteren Platz beanspruchen kann.In addition, it may be desirable to heat objects such as pipes, tools, etc. However, using a water-based heater takes up a lot of space. In addition, a homogeneous heating u.U. difficult. The use of heatable coatings is conceivable in principle for this purpose. However, such coatings are u.U. damaged by thermal expansion of the heated object, or it must be taken precautions that this does not happen, which may take up more space.

Zusammenfassung der ErfindungSummary of the invention

Aufgabe der vorliegenden Erfindung ist es somit, ein Glasfaservlies bereitzustellen, welches einfach montiert werden kann und welches eine zuverlässige Beheizung ermöglicht. Zudem sollte dieses mit konventionellen Methoden verarbeitbar sein.Object of the present invention is therefore to provide a glass fiber fleece, which can be easily mounted and which allows reliable heating. In addition, this should be processable by conventional methods.

Diese Aufgabe wird erfindungsgemäß durch die in den Ansprüchen beschriebenen Gegenstände gelöst. Insbesondere haben die Erfinder der vorliegenden Erfindung überraschenderweise herausgefunden, dass die Beschichtung eines Glasfaservlieses mittels einer leitfähigen Beschichtung möglich ist und z.B. die Beheizung eines Raumes durch das beschichtete Glasfaservlies einfach möglich ist.This object is achieved by the objects described in the claims. In particular, the inventors of the present invention have surprisingly found that coating a glass fiber web by means of a conductive coating is possible, e.g. the heating of a room by the coated glass fiber fleece is easily possible.

Insbesondere betrifft die vorliegende Erfindung in einem ersten Aspekt ein beheizbares Glasfaservlies, umfassend eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, wobei das Flächengewicht des beheizbaren Glasfaservlieses mindestens 250 g/m2 beträgt.In particular, in a first aspect, the present invention relates to a heatable glass fiber fleece, comprising a coating which comprises at least one conductivity additive and at least one binder, wherein the basis weight of the heatable glass fiber fleece is at least 250 g / m 2 .

In einem zweiten Aspekt wird erfindungsgemäß ein Glasfaservliesbauteil bereitgestellt, umfassend das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung und mindestens zwei elektrisch leitfähige Kontaktelemente, die an das beheizbare Glasfaservlies derart angeordnet sind, dass das beheizbare Glasfaservlies mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar ist.In a second aspect, the invention provides a glass fiber fleece component, comprising the heatable glass fiber fleece according to the present invention and at least two electrically conductive contact elements, which are connected to the heatable Glass fiber fleece are arranged such that the heated glass fiber fleece can be acted upon by electrical voltage and / or electric current.

In einem dritten Aspekt wird erfindungsgemäß ein Kit zum Herstellen eines Glasfaservliesbauteils bereitgestellt, wobei das Kit (1) ein beheizbares Glasfaservlies gemäß der vorliegenden Erfindung, (2) mindestens zwei elektrisch leitfähige Kontaktelemente und (3) optional, Glasgewebekleber, umfasst.In a third aspect, according to the invention, there is provided a kit for producing a glass fiber nonwoven component, wherein the kit ( 1 ) comprises a heatable glass fiber fleece according to the present invention, (2) at least two electrically conductive contact elements and (3) optionally, glass fabric adhesive.

In einem vierten Aspekt wird erfindungsgemäß ein Gegenstand, ein Boden, eine Wand und/oder eine Decke, enthaltend ein beheizbares Glasfaservlies gemäß der vorliegenden Erfindung oder ein Glasfaservliesbauteil gemäß der vorliegenden Erfindung oder ein mittels des erfindungsgemäßen Kits hergestellten Glasfaservliesbauteils, bereitgestellt.In a fourth aspect there is provided according to the invention an article, a floor, a wall and / or a ceiling comprising a heatable glass fiber mat according to the present invention or a glass fiber mat member according to the present invention or a glass fiber mat member made by means of the kit according to the invention.

Ein einem fünften Aspekt wird erfindungsgemäß die Verwendung des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung oder des Glasfaservliesbauteils gemäß der vorliegenden Erfindung oder eines mittels des Kits gemäß der vorliegenden Erfindung hergestellten Glasfaservliesbauteils zum Beheizen eines Gegenstand, eines Bodens und/oder Raumes oder zum Abschirmen eines Raumes vor elektromagnetischer Strahlung bereitgestellt.A fifth aspect of the present invention provides the use of the heatable glass fiber nonwoven fabric according to the present invention or the nonwoven glass fiber member according to the present invention or a glass fiber nonwoven fabric article produced by the kit according to the present invention for heating an article, a floor and / or a room or for shielding a room provided electromagnetic radiation.

In einem sechsten Aspekt wird erfindungsgemäß ein Verfahren zum Beheizen eines Gegenstand, eines Bodens und/oder eines Raumes bereitgestellt, umfassend die Schritte (i) Anbringen eines oder mehrerer beheizbaren/beheizbarer Glasfaservliese(s) gemäß der vorliegenden Erfindung oder eines oder mehrerer Glasfaservliesbauteils/Glasfaservliesbauteile gemäß der vorliegenden Erfindung an dem Gegenstand, dem Boden, eine oder mehrere Wand/Wände und/oder Decke(n), und (ii) Beaufschlagen des/der beheizbaren Glasfaservliese(s) oder des/der Glasfaservliesbauteils/Glasfaservliesbauteile mit elektrischer Spannung und/oder elektrischem Strom.In a sixth aspect there is provided according to the invention a method of heating an article, floor and / or room, comprising the steps of (i) attaching one or more heatable / heatable glassfiber webs according to the present invention or one or more nonwoven glass fiber / nonwoven components according to the present invention, to the article, the floor, one or more walls / walls and / or ceiling (s), and (ii) subjecting the heated glass fiber web (s) or the glass fiber nonwoven component (s) to electrical voltage and / or or electric current.

Beheizbares GlasfaservliesHeated glass fiber fleece

Glasfaservliesfiberglass mat

Ein in dem erfindungsgemäßen, beheizbaren Glasfaservlies enthaltene Komponente ist das Glasfaservlies vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst. Prinzipiell ist für das erfindungsgemäße, beheizbare Glasfaservlies jegliches für den Baubereich geeignete Glasfaservlies einsetzbar, sofern die Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst möglich ist.A component contained in the heatable glass fiber fleece according to the invention is the glass fiber fleece before the application of the coating, which comprises at least one conductivity additive and at least one binder. In principle, any glass fiber fleece suitable for the construction sector can be used for the heatable glass fiber fleece according to the invention, provided that the application of the coating comprising at least one conductivity additive and at least one binder is possible.

Das Flächengewicht des Glasfaservlieses vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beträgt vorzugsweise nicht mehr als 240 g/m2, mehr bevorzugt nicht mehr als 220 g/m2, noch mehr bevorzugt nicht mehr als 210 g/m2. Üblicherweise beträgt das Flächengewicht des Glasfaservlieses vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, mindestens 140 g/m2.The weight per unit area of the glass fiber fleece before application of the coating comprising at least one conductivity additive and at least one binder is preferably not more than 240 g / m 2 , more preferably not more than 220 g / m 2 , even more preferably not more than 210 g / m 2 . The basis weight of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder, is usually at least 140 g / m 2 .

Das Glasfaservlies vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann eine oder mehrere Beschichtung(en) aufweisen, die keine Leitfähigkeitsadditive umfasst(umfassen). Derlei Beschichtungen sind im Stand der Technik bekannt. Das o.g. Flächengewicht des Glasfaservlieses vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, schließt (eine) derartige Beschichtung(en) ein.The fiberglass web prior to application of the coating, which comprises at least one conductivity additive and at least one binder, may comprise one or more coatings that do not include conductivity additives. Such coatings are known in the art. The o.g. Basis weight of the fiberglass mat prior to application of the coating comprising at least one conductivity additive and at least one binder includes such coating (s).

Beispielsweise kann das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung als Rollware ausgeführt sein, z.B. in üblichen Größen von bis zu 1000 m2, wie 1 m × 500 m.For example, the heatable fiberglass mat according to the present invention may be designed as rolled goods, for example in conventional sizes of up to 1000 m 2 , such as 1 m × 500 m.

Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst Eine weitere in dem erfindungsgemäßen, beheizbaren Glasfaservlies enthaltene Komponente ist die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst. Prinzipiell kann hier jede Beschichtung verwendet werden, die in der Lage ist, IR-Strahlung zu erzeugen, durch die ein Raum beheizt wird. Üblicherweise wird eine Beschichtung verwendet, die mindestens ein auf Kohlenstoff basierendes Leitfähigkeitsadditiv enthält, insbesondere eine Beschichtung, die mit einer Schutzkleinspannung betreibbar ist.Coating comprising at least one conductivity additive and at least one binder Another component contained in the heatable glass fiber nonwoven fabric according to the invention is the coating which comprises at least one conductivity additive and at least one binder. In principle, here any coating can be used which is able to generate IR radiation, through which a space is heated. Usually, a coating is used which contains at least one carbon-based conductivity additive, in particular a coating which can be operated with a safety extra-low voltage.

Die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann auf das Glasfaservlies in an sich bekannter Weise aufgebracht werden, beispielsweise mittels Foulardieren, Sprühen, Siebdruck (beispielsweise im Rotations- oder Flachbettverfahren), Rakeln mit Schlitzdüse und/oder Tauchbeschichtung.The coating, which is at least one Conductive additive and at least one binder, can be applied to the glass fiber fabric in a conventional manner, for example by means of padding, spraying, screen printing (for example, in the rotary or flat bed method), knife-edge slitting and / or dip coating.

Die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann auf beide Seiten des Glasfaservlieses oder nur auf einer Seite des beheizbaren Glasfaservlieses aufgebracht sein. Die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, dringt in das Glasfaservlies ein bzw. durchdringt dieses. Daher sind bei einer beidseitigen Beschichtung des Glasfaservlieses mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, die Beschichtungen auf beiden Seiten miteinander elektrisch leitend verbunden. Somit ist bei einer derartigen beidseitigen Beschichtung eine elektrische Kontaktierung (siehe unten) auf beliebigen Seiten des Glasfaservlieses möglich. Bei einer einseitigen Beschichtung des Glasfaservlieses mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, ist daher eine elektrische Kontaktierung (siehe unten) auch auf der der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, abgewandten Seite möglich. Üblicherweise ist die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, nur auf einer Seite des beheizbaren Glasfaservlieses aufgebracht.The coating, which comprises at least one conductivity additive and at least one binder, can be applied to both sides of the glass fiber fleece or only on one side of the heatable glass fiber fleece. The coating, which comprises at least one conductivity additive and at least one binder, penetrates or penetrates into the glass fiber fleece. Therefore, in the case of a coating of the glass fiber fleece on both sides with the coating, which comprises at least one conductivity additive and at least one binder, the coatings are electrically conductively connected to one another on both sides. Thus, with such a double-sided coating, electrical contacting (see below) is possible on any sides of the glass fiber fleece. In a one-sided coating of the glass fiber fleece with the coating, which comprises at least one conductivity additive and at least one binder, electrical contacting (see below) is therefore also possible on the side facing away from the coating, which comprises at least one conductivity additive and at least one binder. Usually, the coating, which comprises at least one conductivity additive and at least one binder, is applied only on one side of the heatable glass fiber fleece.

Auf dem beheizbaren Glasfaservlies umfassend eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, können eine oder mehrere weitere Schichten (wie eine Schutzschicht (z.B. ein Schutzlack, Sperrgrund, Haftgrund und/oder eine Farbschicht) aufgebracht sein. Die Schutzschicht kann in einer Ausführungsform die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, elektrisch isolieren. Vorteilhafterweise ist die Schutzschicht thermisch leitend, gegebenenfalls auch elektrisch isolierend. Die Schutzschicht kann in an sich bekannter Weise erzeugt werden. Beispiele für eine solche Schutzschicht ist ein Sperrgrund. Ein derartiger Sperrgrund kann zur chemischen Entkopplung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst und von der Deckbeschichtung, sofern vorhanden, führen. Weiterhin kann eine Farbschicht als oberste Schicht aufgetragen werden oder sein, die vorteilhafterweise thermisch leitend ist. In einer weiteren Ausführungsform kann eine Vliesschicht auf dem erfindungsgemäßen Glasfaservlies aufgebracht sein, wobei diese Vliesschicht, sofern vorhanden, normalerweise kein Leitfähigkeitsadditiv enthält. Eine derartige Vliesschicht, falls vorhanden, weist vorzugsweise ein Flächengewicht von nicht mehr als 100 g/m2, mehr bevorzugt nicht mehr als 60 g/m2 und noch mehr bevorzugt nicht mehr als 30 g/m2 auf. Diese Vliesschicht, falls vorhanden, kann ein Kunststoff- und/oder ein Glasfaservlies aufweisen bzw. daraus bestehen, beispielsweise ein Glasfaservlies aufweisen bzw. daraus bestehen. Falls derartige Schichten vorhanden sind, befinden sie sich üblicherweise nur auf einer Seite des Glasfaservlieses. Ansonsten ist die elektrische Kontaktierung unter Umständen schwierig.One or more further layers (such as a protective layer (eg a protective lacquer, barrier base, primer and / or a color layer) may be applied to the heatable glass fiber fleece comprising a coating comprising at least one conductivity additive and at least one binder The protective layer may be thermally conductive, and may also be electrically insulating Such a barrier may result in the chemical decoupling of the coating comprising at least one conductivity additive and at least one binder and from the topcoat, if present, Further, a colorant layer may be or may be applied as the topmost layer, ie e is advantageously thermally conductive. In a further embodiment, a nonwoven layer may be applied to the glass fiber fleece according to the invention, this nonwoven layer, if present, normally containing no conductivity additive. Such a nonwoven layer, if present, preferably has a basis weight of not more than 100 g / m 2 , more preferably not more than 60 g / m 2, and even more preferably not more than 30 g / m 2 . This nonwoven layer, if present, may comprise or consist of a plastic and / or a glass fiber fleece, for example comprising or consisting of a glass fiber fleece. If such layers are present, they are usually only on one side of the glass fiber fleece. Otherwise, the electrical contacting may be difficult.

Das Leitfähigkeitsadditiv, das in der vorstehend genannten Beschichtung enthalten ist, die zur Herstellung des erfindungsgemäßen Glasfaservlieses verwendet wird, ist vorzugsweise ein kohlenstoffbasiertes Leitfähigkeitsadditiv. In der vorliegenden Erfindung werden als kohlenstoffbasierte Leitfähigkeitsadditive Leitfähigkeitsadditive angesehen, die elementaren Kohlenstoff enthalten. Beispielsweise werden Carbid-haltige Verbindungen in der vorliegenden Erfindung nicht als kohlenstoffbasierte Leitfähigkeitsadditive angesehen.The conductivity additive contained in the above-mentioned coating used for producing the nonwoven fabric of the present invention is preferably a carbon-based conductivity additive. In the present invention, carbon-based conductivity additives are considered to be conductivity additives containing elemental carbon. For example, carbide-containing compounds in the present invention are not considered to be carbon-based conductivity additives.

Die erfindungsgemäß verwendete Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, umfasst vorzugsweise mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, und mindestens ein Bindemittel, umfassend ein elektrisch nicht leitfähiges Polymer und/oder ein anorganisches Bindemittel. Mehr bevorzugt umfasst die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, mindestens zwei Leitfähigkeitsadditive, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, und mindestens ein Bindemittel, umfassend ein elektrisch nicht leitfähiges Polymer und/oder ein anorganisches Bindemittel.The coating used according to the invention, which comprises at least one conductivity additive and at least one binder, preferably comprises at least one conductivity additive selected from conductivity additives comprising graphite, graphene and carbon black, and at least one binder comprising an electrically nonconductive polymer and / or an inorganic binder , More preferably, the coating comprising at least one conductivity additive and at least one binder comprises at least two conductivity additives selected from conductivity additives comprising graphite, graphene and carbon black, and at least one binder comprising an electrically nonconductive polymer and / or an inorganic binder.

In der bevorzugten Ausführungsform, in der die Beschichtung, die mindestens ein kohlenstoffbasiertes Leitfähigkeitsadditiv, vorzugsweise ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält, und mindestens ein Bindemittel umfasst, wobei das Bindemittel ein elektrisch nicht leitfähiges Polymer und/oder ein anorganisches Bindemittel umfasst, ist die Beschichtung, die mindestens ein auf Kohlenstoff basierendes Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufgrund des Vorhandenseins des einen oder der mehreren Leitfähigkeitsadditive niederohmig, was zu einer guten elektrischen Leitfähigkeit führt, da nur ein geringer elektrischer Widerstand vorhanden ist. Dadurch kann eine homogene Beheizbarkeit realisiert werden. Durch die Niederohmigkeit ist zudem gewährleistet, dass an die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, nur geringe Spannungen und/oder geringe Ströme angelegt werden müssen, um eine gute Beheizung zu erreichen.In the preferred embodiment, the coating comprising at least one carbon-based conductivity additive, preferably selected from conductivity additives comprising graphite, graphene and carbon black, and comprising at least one binder, wherein the binder is an electrically nonconductive polymer and / or an inorganic Binder, the coating comprising at least one carbon-based conductivity additive and at least one binder is low-resistance due to the presence of the one or more conductivity additives, resulting in good electrical conductivity since there is little electrical resistance. As a result, a homogeneous heatability can be realized. The low resistance also ensures that only low voltages and / or low currents have to be applied to the coating, which comprises at least one conductivity additive and at least one binder, in order to achieve good heating.

Leitfähigkeitsadditive, insbesondere kohlenstoffbasierte Leitfähigkeitsadditive, sind elektrisch leitende Materialien und sind dem Fachmann bekannt. Spezifische Beispiele für auf Kohlenstoff basierende Leitfähigkeitsadditive beinhalten Graphit, Ruß, Graphen, Kohlenstoff-Nanotubes (CNTs), Carbonfasern und Kohlenstoff-Nanofasern.Conductivity additives, especially carbon-based conductivity additives, are electrically conductive materials and are known to those skilled in the art. Specific examples of carbon-based conductivity additives include graphite, carbon black, graphene, carbon nanotubes (CNTs), carbon fibers and carbon nanofibers.

Die Eigenschaften der vorstehend genannten Leitfähigkeitsadditive werden im Folgenden genauer erläutert.The properties of the aforementioned conductivity additives are explained in more detail below.

Graphit ist ein sehr häufig vorkommendes Mineral und gehört zur Ordnung der Halbmetalle und Nichtmetalle. Er ist neben Diamant und Fullerenen die dritte unter irdischen Normalbedingungen stabile Form (Modifikation) des Kohlenstoffs und kristallisiert meist im hexagonalen, sehr selten auch im trigonalen Kristallsystem.Graphite is a very common mineral and belongs to the order of semi-metals and Non-metals. In addition to diamond and fullerenes, it is the third stable form (modification) of carbon under terrestrial normal conditions and crystallizes mostly in the hexagonal, very rarely also in the trigonal crystal system.

Graphit entwickelt undurchsichtige, graue bis schwarze Kristalle in sechseckiger, tafeliger, schuppiger oder stengeliger Form, die auf den Kristallflächen Metallglanz aufweisen.Graphite develops opaque, gray to black crystals in hexagonal, tabular, scaly, or stem-like shapes with metallic luster on the crystal surfaces.

Im kristallinen Graphit liegen parallel verlaufende ebene Schichten, die „Basalebenen“ oder „GraphenSchichten“, vor. Eine Schicht besteht aus kovalent verknüpften Sechsecken, deren Kohlenstoffatome sp2-hybridisiert sind. Innerhalb dieser Ebenen beträgt die Bindungsenergie zwischen den Kohlenstoffatomen 4,3 eV, zwischen ihnen dagegen lediglich 0,07 eV. Aus dieser extremen Richtungsabhängigkeit der Bindungskräfte resultiert eine deutliche Anisotropie der mechanischen, elektrischen und thermischen Eigenschaften des Graphits:

  • - leichte Spaltbarkeit des reinen Graphits entlang der Basalebenen, deutlich höhere Festigkeit entlang der Kristallschichten;
  • - thermische und elektrische Isolation orthogonal zu den Basalebenen gegenüber einer fast metallischen Leitfähigkeit entlang der Ebenen.
In crystalline graphite, there are parallel planar layers, the "basal planes" or "graphene layers". A layer consists of covalently linked hexagons whose carbon atoms are sp 2 -hybridized. Within these levels, the bond energy between the carbon atoms is 4.3 eV, but only 0.07 eV between them. This extreme directional dependence of the bond forces results in a clear anisotropy of the mechanical, electrical and thermal properties of the graphite:
  • - easy cleavage of pure graphite along the basal planes, significantly higher strength along the crystal layers;
  • - Thermal and electrical insulation orthogonal to the basal planes against a nearly metallic conductivity along the planes.

Die Leitfähigkeit innerhalb einer Ebene wird durch die Delokalisation der π-Elektronen ermöglicht. Weisen die Ebenen keine feste Korrelation zueinander auf, spricht man von turbostratischem Kohlenstoff. Graphit kann auch synthetischen Ursprungs sein, als Produkt der Verkokung von dafür geeigneten Kunststoffen, Pech, Erdöl, Kohle und dergleichen.The conductivity within a plane is made possible by the delocalization of the π electrons. If the planes do not have a fixed correlation with each other, this is called turbostatic carbon. Graphite may also be of synthetic origin, as a product of carbonization of suitable plastics, pitch, petroleum, coal and the like.

Graphen besteht, wie oben bereits erwähnt, aus einer einzelnen Schicht, bestehend aus kovalent verknüpften Sechsecken von Kohlenstoffatomen, wobei diese Kohlenstoffatome sp2-hybridisiert sind. Im Gegensatz zum Graphit liegt eine einzelne Schicht isoliert vor, besteht also nicht aus parallel verlaufenden Schichten. Graphen ist folglich eine Modifikation des Kohlenstoffs mit zweidimensionaler Struktur. Graphen ist in Schichtrichtung extrem steif, da die Bindung zwischen zwei benachbarten sp2-hybridisierten Kohlenstoffatomen von der Stärke her mit der Bindung zwischen zwei sp3-hybridisierten Kohlenstoffatomen innerhalb eines Diamantgitters vergleichbar ist. Graphen kann mittels einer Vielzahl von synthetischen Methoden hergestellt werden.Graphene consists, as mentioned above, of a single layer consisting of covalently linked hexagons of carbon atoms, these carbon atoms being sp 2 -hybridized. In contrast to graphite, a single layer is isolated, ie it does not consist of parallel layers. Graphene is thus a modification of carbon with a two-dimensional structure. Graphene is extremely stiff in the layer direction because the bond between two adjacent sp 2 -hybridized carbon atoms is comparable in strength to the bond between two sp 3 -hybridized carbon atoms within a diamond lattice. Graphene can be prepared by a variety of synthetic methods.

Ruß ist ein schwarzer, pulverförmiger Feststoff, der je nach Qualität und Verwendung zu 80% oder mehr aus Kohlenstoff besteht.Carbon black is a black, powdered solid that is 80% or more carbon, depending on its quality and use.

Je nach ihrem Anwendungsgebiet besitzen Ruße spezielle Eigenschaftsprofile, die durch die Art des Herstellverfahrens und durch Variation der Prozessparameter gezielt beeinflusst werden.Depending on their field of application, carbon blacks have special property profiles that are specifically influenced by the type of manufacturing process and by variation of the process parameters.

Ruße, ihre Eigenschaften, Herstellungsverfahren, Verwendungen und so weiter sind bereits weitreichend beschrieben, so dass an dieser Stelle auf die einschlägige Fachliteratur verwiesen wird.Carbon blacks, their properties, production processes, uses and so on are already extensively described, so that reference is made here to the relevant specialist literature.

Kohlenstoff-Nanotubes (CNTs) bestehen aus zum Zylinder aufgerollten, geschlossen Graphen-Schichten. Einzelne Röhren nennt man „single wall carbon nanotubes“ (SWCNT), Teilchen aus konzentrisch gestapelten Röhren aufsteigenden Durchmessers werden „multiwall carbon nanotubes“ (MWCNT) genannt.Carbon nanotubes (CNTs) consist of rolled-up, closed graphene layers. Single tubes are called "single wall carbon nanotubes" (SWCNT), particles of concentrically stacked tubes of increasing diameter are called "multiwall carbon nanotubes" (MWCNT).

CNTs kann man über verschiedene Methoden herstellen. Am bekanntesten sind der Lichtbogenprozess, das Laserablationsverfahren und die katalytisch unterstützte Gasphasenabscheidung (CCVD). Letzteres Verfahren eignet sich zur großtechnischen Produktion von CNTs. Hierbei entstehen die CNT aus gasförmigen Kohlenstofflieferanten (Kohlenwasserstoffe, Alkohole, CO, CO2) auf metallischen, katalytisch aktiven Substanzen.CNTs can be produced by different methods. The best known are the arc process, the laser ablation process and the catalytically assisted vapor deposition (CCVD). The latter method is suitable for the large-scale production of CNTs. The CNTs are produced from gaseous carbon sources (hydrocarbons, alcohols, CO, CO 2 ) on metallic, catalytically active substances.

Typischerweise weisen SWCNT einen Durchmesser von 0,5 - 4 nm, MWCNT einen Durchmesser zwischen 6 und 100 nm auf. Die Länge von CNTs kann bis zu einigen mm betragen.Typically, SWCNT have a diameter of 0.5-4 nm, MWCNT a diameter between 6 and 100 nm. The length of CNTs can be up to a few mm.

Die physikalischen Eigenschaften von CNTs entsprechen weitestgehend jenen des Graphits entlang der Basalebenen.The physical properties of CNTs largely correspond to those of graphite along basal planes.

CNTs werden heute als mechanische Verstärkung, elektrisch und thermisch leitfähiges Additiv in Polymeren, Keramiken und Metallen eingesetzt. Dazu werden die CNTs oft an ihrer Oberfläche chemisch modifiziert, um den Anforderungen einer guten Dispergierbarkeit und Anbindung an die Matrix zu genügen. In der Regel werden die CNTs dem Matrixmaterial zugegeben. Somit soll der Begriff „CNTs“ sowohl unmodifizierte als auch modifizierte (insbesondere seitenwandmodifizierte) CNTs umfassen. Aufgrund des hohen Aspektverhältnisses und der hohen spezifischen Oberfläche der CNTs sind nur Komposite mit verhältnismäßig niedrigem CNT-Gehalt darstellbar.CNTs are now used as a mechanical reinforcement, as an electrically and thermally conductive additive in polymers, ceramics and metals. For this purpose, the CNTs are often chemically modified on their surface in order to meet the requirements of good dispersibility and connection to the matrix. In general, the CNTs are added to the matrix material. Thus, the term "CNTs" is intended to include both unmodified and modified (especially sidewall-modified) CNTs. Due to the high aspect ratio and the high specific surface area of the CNTs, only composites with a relatively low CNT content can be produced.

Carbonfasern (auch Kohlenstofffasern genannt) sind industriell hergestellte Fasern. Man unterscheidet isotrope und anisotrope Typen, wobei isotrope Fasern nur geringe Festigkeiten aufweisen und sich anisotrope Fasern durch hohe Festigkeiten und Steifigkeiten bei gleichzeitig geringer Bruchdehnung in axialer Richtung auszeichnen. Der Durchmesser einer Carbonfaser beträgt etwa 5 bis 9 µm und ist somit größer als der von Kohlenstoff-Nanofasern oder CNTs.Carbon fibers (also called carbon fibers) are industrially produced fibers. A distinction is made between isotropic and anisotropic types, with isotropic fibers having only low strengths and anisotropic fibers being distinguished by high strengths and stiffness with simultaneously low elongation at break in the axial direction. The diameter of a carbon fiber is about 5 to 9 microns and is thus larger than that of carbon nanofibers or CNTs.

Kohlenstoff-Nanofasern (CNF) bestehen aus Graphenschichten, die entlang der Filamentachse aufeinander gestapelt sind. Der Winkel (die Orientierung) der Graphenebenen bezüglich der Filamentachse wird zur groben Unterscheidung herangezogen. Sogenannte ‚Herringbone‘ CNF besitzen demnach Graphenebenen die in einem Winkel ≠ 90° angeordnet sind. Diese CNF können massiv oder auch hohl sein. Ihre Durchmesser liegen im Bereich 50 nm - 1 µm und ihre Längen können bis zu mm betragen. Im Falle, dass die Graphenschichten in einen Winkel = 90° zur Filamentachse angeordnet sind spricht man von ‚Platelet‘ CNF. Ihre Durchmesser liegen im Bereich von 50 bis 500 nm und ihre Längen können bis zu 50 µm betragen. Carbon nanofibers (CNF) consist of graphene layers stacked along the filament axis. The angle (orientation) of the graphene planes with respect to the filament axis is taken as a rough distinction. So-called 'herringbone' CNF have graphene planes which are arranged at an angle ≠ 90 °. These CNFs can be massive or hollow. Their diameters are in the range 50 nm - 1 μm and their lengths can be up to mm. In the case that the graphene layers are arranged at an angle = 90 ° to the filament axis one speaks of, Platelet 'CNF. Their diameters are in the range of 50 to 500 nm and their lengths can be up to 50 microns.

Diese CNF werden in der Regel über CVD hergestellt. Ihre Anwendungen finden sich vornehmlich in der Katalyse als Katalysatorträger und als aktive Zusatzstoffe in Li-Ionen-Batterien oder bei der Gasspeicherung.These CNFs are usually manufactured via CVD. Their applications are found primarily in catalysis as catalyst supports and as active additives in Li-ion batteries or in gas storage.

Kohlenstoff-Nanotubes, Carbonfasern und Kohlenstoff-Nanofasern weisen aufgrund ihrer hohen Neigung zur Selbstaggregation die Nachteile auf, dass sie nur schwer und unter hohem technischem Aufwand in Dispersionen überführt werden können und dass die dispergierten Fasern stark dazu neigen, wieder zu aggregieren. Das führt dazu, dass einerseits die Herstellungskosten von Dispersionen faseriger Leitfähigkeitsadditive sehr hoch sind und anderseits solche Dispersionen eine geringe Lagerstabilität aufweisen. Um diese Nachteile zu vermeiden, ist die erfindungsgemäße Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, vorzugsweise frei von elektrisch leitfähigen Carbonfasern und Kohlenstoff-Nanotubes, insbesondere frei von elektrisch leitfähigen Carbonfasern, Kohlenstoff-Nanofasern und Kohlenstoff-Nanotubes.Carbon nanotubes, carbon fibers and carbon nanofibers, because of their high tendency to self-aggregate, have the disadvantages that they can be converted into dispersions only with difficulty and with great technical effort and that the dispersed fibers have a strong tendency to aggregate again. As a result, on the one hand, the production costs of dispersions of fibrous conductivity additives are very high and, on the other hand, such dispersions have a low storage stability. In order to avoid these disadvantages, the coating according to the invention comprising at least one conductivity additive and at least one binder is preferably free of electrically conductive carbon fibers and carbon nanotubes, in particular free of electrically conductive carbon fibers, carbon nanofibers and carbon nanotubes.

Der Gewichtsanteil des mindestens einen Leitfähigkeitsadditivs, bezogen auf das Gesamtgewicht der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beträgt vorzugsweise 10 bis 90 Gew.%, mehr bevorzugt 20 bis 80 Gew.% und noch mehr bevorzugt 30 bis 70 Gew.%.The weight fraction of the at least one conductivity additive, based on the total weight of the coating, which comprises at least one conductivity additive and at least one binder is preferably 10 to 90% by weight, more preferably 20 to 80% by weight and even more preferably 30 to 70% by weight. %.

In der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann vorzugsweise mindestens ein Bindemittel enthalten sein, welches ein elektrisch nicht leitfähiges Polymer umfasst. Unter „Bindemittel“ wird erfindungsgemäß eine Verbindung verstanden, durch die Partikel (z.B. Leitfähigkeitsadditive, wie beispielsweise Graphit, Graphen und/oder Ruß) auf einem Substrat, z.B. dem Glasfaservlies des erfindungsgemäßen beheizbaren Glasfaservlieses oder evtl. vorhandener Beschichtung(en), die keine Leitfähigkeitsadditive umfasst/umfassen, derart aufbringbar sind, dass die Partikel zusammen mit dem Bindemittel (und gegebenenfalls mit weiteren Substanzen) auf einem Substrat, z.B. dem Glasfaservlies des erfindungsgemäßen beheizbaren Glasfaservlieses oder evtl. vorhandener Beschichtung(en), die keine Leitfähigkeitsadditive umfasst/umfassen, haften. Das Bindemittel fördert also die Kohäsion der Partikel in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und die Adhäsion der beheizbaren Schicht an dem Substrat, z.B. dem Glasfaservlies des erfindungsgemäßen beheizbaren Glasfaservlieses oder evtl. vorhandener Beschichtung(en), die keine Leitfähigkeitsadditive umfasst/umfassen. Bindemittel können organisch oder anorganisch ausgebildet sein.The coating comprising at least one conductivity additive and at least one binder may preferably contain at least one binder which comprises an electrically nonconductive polymer. By "binder" is meant, according to the invention, a compound through which particles (e.g., conductivity additives such as graphite, graphene, and / or carbon black) on a substrate, e.g. the glass fiber fleece of the heatable glass fiber fleece according to the invention or any existing coating (s), which does not comprise conductivity additives, are applied so that the particles together with the binder (and optionally with other substances) on a substrate, e.g. adhere to the glass fiber fleece of the heatable glass fiber fleece according to the invention or any existing coating (s) which does not comprise any conductive additives. The binder thus promotes the cohesion of the particles in the coating comprising at least one conductivity additive and at least one binder, and the adhesion of the heatable layer to the substrate, e.g. the glass fiber fleece of the heatable glass fiber fleece according to the invention or any existing coating (s) which does not comprise any conductivity additives. Binders may be organic or inorganic.

In ähnlicher Weise kann die Dispersion, die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält und zur Erzeugung einer Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält, verwendbar ist, mindestens ein wie vorstehend definiertes Bindemittel enthalten.Similarly, the dispersion containing at least one conductivity additive selected from conductivity additives comprising graphite, graphene and carbon black, and for producing a coating comprising at least one conductivity additive and at least one binder, and the at least one conductivity additive selected from conductivity additives containing graphite, graphene and carbon black, is usable, containing at least one binder as defined above.

Das elektrisch nicht leitfähige Polymer ist nicht besonders begrenzt und beinhaltet verschiedene Arten von Polymeren, insbesondere thermoplastische Polymere (auch Thermoplaste genannt), Elastomere und Reaktivharze, gegebenenfalls im Gemisch mit einem oder mehreren Zusatzstoffen (wie Härtern und Beschleunigern). Unter Polymeren versteht man chemische Verbindungen, die aus einer oder wenigen Sorten von gleichartigen Einheiten (Monomeren) aufgebaut sind. Solche Moleküle sind meist kettenartig oder verzweigt aufgebaut und weisen kovalente Bindungen zwischen den Monomeren auf. Nachfolgend werden einige, jedoch nicht ausschließliche Beispiele für bevorzugte Polymere beschrieben, die jeweils einzeln, oder aber in jeder beliebigen Kombination zum Einsatz kommen können. Der Anteil des nicht elektrisch leitfähigen Polymers in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann 10 bis 90% (beispielsweise 20 bis 80%, 30 bis 70%) nach Gewicht betragen. Gleichfalls kann der Anteil des nicht elektrisch leitfähigen Polymers in der Dispersion, die zur Erzeugung einer Beschichtung, die mindestens ein Leitfähigkeitsadditiv ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, und mindestens ein Bindemittel umfasst, verwendbar ist, 10 bis 90% (beispielsweise 20 bis 80%, 30 bis 75% oder 40 bis 60%) nach Gewicht betragen.
Beispielhafte Gruppen von thermoplastischen Polymeren umfassen die folgenden:

  • - Polyolefine (wie Polypropylen, Polyethylen, Polybutylen, Polyisobutylen, etc.)
  • - Polyamide (wie z.B. Polyamid-66, Polyamid-12, Polyamid-11, Polyamid-6, etc.)
  • - Polyacryl-Polymere (wie Polymethylmethacrylat, Polyacrylnitril, Polyacrylsäure und Derivate, etc.)
  • - Fluorpolymere (wie Polytetraflourethylen, Polyvinylidenfluorid, etc.)
  • - aliphatische und aromatische Polyester (wie z.B. Polyglykole, Polyethylenterephthalat, etc.)
  • - Polyimide (wie z.B. Polyetherimid)
  • - Poly(aryl)etherketone (wie z.B. Polyetherketone, Polyetheretherketone, etc.)
  • - Polysulfide (wie z.B. Polyphenylensulfid, Polyphenylensulfon, Polysulfon, Polyethersulfon, etc.)
  • - Polyacetale
  • - Cellulose und Derivate davon (wie z.B. Cellulosenitrate, -acetate, -acetatbutyrate, etc.)
  • - Vinylpolymere (wie z.B. Polyvinylchlorid, Polyvinylacetat, Polyvinylalkohol, Polyvinylbutyral, Polyvinylpyrrolidon, etc.)
The electrically non-conductive polymer is not particularly limited and includes various types of polymers, especially thermoplastic polymers (also called thermoplastics), elastomers and reactive resins, optionally in admixture with one or more additives (such as hardeners and accelerators). Polymers are understood as meaning chemical compounds which are composed of one or a few types of similar units (monomers). Such molecules are usually chain-like or branched and have covalent bonds between the monomers. Some, but not exclusive, examples of preferred polymers will be described below, each of which may be used individually or in any combination. The proportion of the non-electrically conductive polymer in the coating comprising at least one conductivity additive and at least one binder may be 10 to 90% (for example 20 to 80%, 30 to 70%) by weight. Likewise, the proportion of the non-electrically conductive polymer in the dispersion useful for forming a coating comprising at least one conductivity additive selected from conductivity additives comprising graphite, graphene and carbon black and at least one binder may be from 10 to 90% (e.g. 20 to 80%, 30 to 75% or 40 to 60%) by weight.
Exemplary groups of thermoplastic polymers include the following:
  • - Polyolefins (such as polypropylene, polyethylene, polybutylene, polyisobutylene, etc.)
  • Polyamides (such as polyamide-66, polyamide-12, polyamide-11, polyamide-6, etc.)
  • Polyacrylic polymers (such as polymethylmethacrylate, polyacrylonitrile, polyacrylic acid and derivatives, etc.)
  • Fluoropolymers (such as polytetrafluoroethylene, polyvinylidene fluoride, etc.)
  • aliphatic and aromatic polyesters (such as polyglycols, polyethylene terephthalate, etc.)
  • Polyimides (such as polyetherimide)
  • Poly (aryl) ether ketones (such as polyether ketones, polyether ether ketones, etc.)
  • Polysulfides (such as polyphenylene sulfide, polyphenylene sulfone, polysulfone, polyethersulfone, etc.)
  • - polyacetals
  • Cellulose and derivatives thereof (such as cellulose nitrates, acetates, acetate butyrates, etc.)
  • Vinyl polymers (such as polyvinyl chloride, polyvinyl acetate, polyvinyl alcohol, polyvinyl butyral, polyvinyl pyrrolidone, etc.)

Beispielhafte Gruppen von Elastomeren umfassen die folgenden:

  • - Naturkautschuke, die Chlor-, Styrol-, Nitril-, Schwefel- oder Sauerstoffsubstituenten enthalten können
  • - Isoprenkautschuke, die Chlor-, Styrol-, Nitril-, Schwefel- oder Sauerstoffsubstituenten enthalten können
  • - Butadienkautschuke, die Chlor-, Styrol-, Nitril-, Schwefel- oder Sauerstoffsubstituenten enthalten können
  • - andere Kautschuke, die Chlor-, Styrol-, Nitril-, Schwefel- oder Sauerstoffsubstituenten enthalten können
  • - Silikonelastomere
  • - Polyurethane
Exemplary groups of elastomers include the following:
  • - Natural rubbers, which may contain chlorine, styrene, nitrile, sulfur or oxygen substituents
  • - Isoprene rubbers, which may contain chlorine, styrene, nitrile, sulfur or oxygen substituents
  • Butadiene rubbers which may contain chlorine, styrene, nitrile, sulfur or oxygen substituents
  • - Other rubbers which may contain chlorine, styrene, nitrile, sulfur or oxygen substituents
  • - silicone elastomers
  • - Polyurethanes

Ein Beispiel für Reaktivharze ist ein Epoxydharz, das epoxygruppenhaltige Monomere, Oligomere und/oder Polymere enthält. Epoxydharze können auf aromatischen Monomeren (z.B. auf Bisphenol-A, -F, Novolak und andere), aliphatischen Monomeren oder cycloaliphatischen Monomeren basieren. Beispiele für die letztere Gruppe beinhalten in nicht begrenzender Weise 3,4-Epoxycyclohexylmethyl-3,4-epoxycyclohexancarboxylat, Bis((3,4-epoxy-cyclohexyl)methyl)adipat und andere Derivate höheren oder auch niedrigeren Molekulargewichts. Die Epoxydharze können mono-, di-, tri-, tetra- und mehrfunktionell sein und umfassen alle Molekulargewichte.An example of reactive resins is an epoxy resin containing epoxy group-containing monomers, oligomers and / or polymers. Epoxy resins can be based on aromatic monomers (e.g., on bisphenol A, F, novolak, and others), aliphatic monomers, or cycloaliphatic monomers. Examples of the latter group include, but are not limited to, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, bis ((3,4-epoxycyclohexyl) methyl) adipate, and other higher or lower molecular weight derivatives. The epoxy resins can be mono-, di-, tri-, tetra- and polyfunctional and include all molecular weights.

Weitere Gruppen für Reaktivharze stellen Cyanatester und Isocyanate dar und einzelne Vertreter hiervon umfassen in nicht begrenzender Weise 2,4-Diisocyanato-1-methyl-benzol, 1-Isocyanato-4-[(4-isocyanatophenyl)methyl]benzol, 1, 1-Bis(4-cyanatophenyl)ethan, 2,2-Bis(4-cyanatophenyl)propan, Oligo(3-methylen-1,5-phenylencyanat) und andere Derivate höheren oder auch niedrigeren Molekulargewichts.Further groups for reactive resins are cyanate esters and isocyanates, and individual members thereof include, but are not limited to, 2,4-diisocyanato-1-methylbenzene, 1-isocyanato-4 - [(4-isocyanatophenyl) methyl] benzene, 1, 1- Bis (4-cyanatophenyl) ethane, 2,2-bis (4-cyanatophenyl) propane, oligo (3-methylene-1,5-phenylcyanoate) and other derivatives of higher or lower molecular weight.

Eine weitere Gruppe für Reaktivharze ist die Gruppe von linearen und verzweigten Diolen und mehrfunktionellen Alkoholen, wie Oligo- und Polyester-Polyole und Polyether-Polyole.Another group for reactive resins is the group of linear and branched diols and polyhydric alcohols, such as oligo- and polyester polyols and polyether polyols.

Eine weitere Gruppe für Reaktivharze ist die Gruppe von reaktiven Polyimidsystemen. Reaktive Polyimidsysteme können monofunktionelle Monomere (wie z.B. N-Phenylmaleimid, 2,6-Xylylmaleimid, N-Cyclohexylmaleimid, etc.) und/oder difunktionelle Monomere (wie z.B. 4,4'-Diphenylmethanbismaleimid, N,N'-(4-Methyl-m-phenylen)bismaleimid, N,N'-m-Phenylenbismaleimid, Bisphenol-A Diallylether, o,o'-Diallylbisphenol-A, Polyphenylmethanbismaleimid, Polybenzimidazol, etc.) enthalten.Another group for reactive resins is the group of reactive polyimide systems. Reactive polyimide systems may be monofunctional monomers (such as N-phenylmaleimide, 2,6-xylylmaleimide, N-cyclohexylmaleimide, etc.) and / or difunctional monomers (such as 4,4'-diphenylmethane bismaleimide, N, N '- (4-methyl) m-phenylene) bismaleimide, N, N'-m-phenylenebismaleimide, bisphenol A diallyl ether, o, o'-diallylbisphenol-A, polyphenylmethane bismaleimide, polybenzimidazole, etc.).

Eine weitere Gruppe für Reaktivharze ist die Gruppe von Phenolharzen. Beispiele umfassen in nicht begrenzender Weise diejenigen, die auf Novolak oder Resol basieren.Another group for reactive resins is the group of phenolic resins. Examples include, but are not limited to, those based on novolac or resol.

Weitere beispielhafte Gruppen für Reaktivharze umfassen die folgenden:

  • - ungesättigte Polyester- und Vinylesterharze
  • - Alkydharze
  • - Melaminharze
  • - Polysilane und Silikone
  • - Acrylate (einschließlich Methacrylate)
  • - Polychinoxaline
  • - Peche und Bitumen
Other exemplary reactive resin groups include the following:
  • unsaturated polyester and vinyl ester resins
  • - Alkyd resins
  • - Melamine resins
  • Polysilanes and silicones
  • - acrylates (including methacrylates)
  • - Polyquinoxalines
  • - pitches and bitumen

Weiterhin können Härter und/oder Beschleuniger, wie Amine, Amide, Amidoamine, Aminoalkohole, Aminosäuren, Anhydride, Imidazole, Cyanamide, Alkohole, Phenole, Polyole, Cyanate, Mercaptane, Carbonsäuren, Metallkomplexe etc., in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, (z.B. die Dispersion die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält, und die zur Erzeugung einer Beschichtung, die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, und mindestens ein Bindemittel umfasst, enthält, verwendbar ist) enthalten sein. Unter „Härter“ wird erfindungsgemäß eine Verbindung verstanden, durch die eine Vielzahl einzelner Grundbausteine (z.B. eines Bindemittels) zu einem dreidimensionalen Netzwerk verknüpft wird. Der Härter weist vorzugsweise mindestens zwei funktionelle Gruppen auf, die fähig sind, mit einem Bindemittel zu reagieren, und gleich oder verschieden sein können. Der Anteil des Härters/Beschleunigers in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, z.B. in der Dispersion) ist vorzugsweise stöchiometrisch mit Bezug auf das jeweilige Reaktivharz (d.h. der Härter/Beschleuniger liegt in einer solchen Menge vor, dass theoretisch nahezu jedes Härter/Beschleuniger-Molekül mit einem Reaktivharz-Molekül reagieren kann; vorzugsweise beträgt die Menge an Härter/Beschleuniger 80 bis 150% (wie 85 bis 130%, 90 bis 120%, 95 bis 110%, 97 bis 105%, 98 bis 102% oder 100%) bezogen auf die molare Menge des Reaktivharzes in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, (bzw. in der Dispersion).Furthermore, hardeners and / or accelerators, such as amines, amides, amidoamines, amino alcohols, amino acids, anhydrides, imidazoles, cyanamides, alcohols, phenols, polyols, cyanates, mercaptans, carboxylic acids, metal complexes, etc., in the coating, the at least one conductivity additive and comprises at least one binder, (eg, the dispersion, the at least one conductivity additive, selected from Conductive additives comprising graphite, graphene and carbon black, and which for forming a coating, the at least one conductivity additive, selected from conductivity additives, which include graphite, graphene and carbon black, and at least one binder comprises, contains, is usable). By "hardener" is meant according to the invention a compound by which a plurality of individual basic building blocks (eg a binder) is linked to a three-dimensional network. The hardener preferably has at least two functional groups capable of reacting with a binder and may be the same or different. The proportion of the curing agent / accelerator in the coating, which comprises at least one conductivity additive and at least one binder, eg in the dispersion) is preferably stoichiometric with respect to the particular reactive resin (ie, the curing agent / accelerator is present in an amount that is theoretically close to each hardener / accelerator molecule can react with a reactive resin molecule, preferably the amount of hardener / accelerator is 80 to 150% (such as 85 to 130%, 90 to 120%, 95 to 110%, 97 to 105%, 98 to 102% or 100%) based on the molar amount of the reactive resin in the coating, which comprises at least one conductivity additive and at least one binder, (or in the dispersion).

Es kann bevorzugt sein, dass die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, (z.B. die Dispersion die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält, und die zur Erzeugung einer Beschichtung, die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, und mindestens ein Bindemittel umfasst, enthält, verwendbar ist) keine organischen Bindemittel enthält. In diesem Fall kann die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, (bzw. die Dispersion) anstatt des elektrisch nicht leitfähigen Polymers ein oder mehrere anorganische Bindemittel umfassen. Der Begriff „anorganisches Bindemittel“ betrifft erfindungsgemäß einen mineralischen Stoff, der beim Mischen mit Wasser eine insbesondere verarbeitbare Paste ergibt, die anschließend erhärtet bzw. erhärtbar ist. Vorzugsweise ist das anorganische Bindemittel im festen und/oder erhärteten Zustand elektrisch nicht leitfähig. Die Erhärtung kann hydraulisch (d.h. mit und unter Wasser; Beispiel: Zement, Magnesiabinder), carbonatisch (Beispiel: Kalk), hydratisch (Beispiel: Gips) oder anderweitig (z.B. polymerisch; Beispiel: Wasserglas) oder gemischt erfolgen. Beispiele für anorganische Bindemittel beinhalten in nicht begrenzender Weise Zement (wie Portlandzement, Tonerdezement (Calciumaluminate), Portlandschnellzement (Calciumsilicate, Anhydrit (CaSO4)), Calciumsulfoaluminatzement (Ye'elimit, Belit, Anhydrit), Sulfathüttenzement (Hüttensand, Anhydrit, Calciumsilicate)), Kalk (wie Brandkalk (CaO) oder gelöschter Kalk (Ca(OH)2)), Gips (wie Anhydrit (CaSO4), Halbhydrat (CaSO4·0,5 H2O) oder Dihydrat (CaSO4·2 H2O)), Magnesiabinder (Magnesia, Magnesiumsalze), Wasserglas (Alkalisilicate, insbesondere Natron- und/oder Kalisilicate) und Geopolymere (z.B. Alumosilicate wie Tone). Bevorzugte Beispiele für anorganische Bindemittel sind gebrannter Kalk, gelöschter Kalk, Wasserglas, Gips, Ton und Zement. Der Anteil des anorganischen Bindemittels in der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, kann 10 bis 90% (beispielsweise 20 bis 80%, 30 bis 70%) nach Gewicht betragen. Gleichfalls kann der Anteil des anorganischen Bindemittels in der Dispersion die mindestens ein Leitfähigkeitsadditiv, ausgewählt aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen, enthält, und zur Erzeugung einer Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, verwendbar ist, 10 bis 90% (beispielsweise 20 bis 80%, 30 bis 75% oder 40 bis 60%) nach Gewicht betragen.It may be preferred that the coating comprises at least one conductivity additive and at least one binder (eg, the dispersion containing at least one conductivity additive selected from conductivity additives comprising graphite, graphene, and carbon black, and those for forming a coating at least one conductivity additive selected from conductivity additives comprising graphite, graphene, and carbon black, and comprising, containing, usable at least one binder) does not contain organic binders. In this case, the coating comprising at least one conductivity additive and at least one binder (or the dispersion) may comprise one or more inorganic binders instead of the electrically nonconductive polymer. According to the invention, the term "inorganic binder" refers to a mineral substance which, when mixed with water, gives a paste which can be processed in particular, which is subsequently hardened or hardenable. Preferably, the inorganic binder is electrically nonconductive in the solid and / or hardened state. The hardening can be carried out hydraulically (ie with and under water, example: cement, magnesium binder), carbonatic (example: lime), hydrate (example: gypsum) or otherwise (eg polymer, example: water glass) or mixed. Examples of inorganic binders include, but are not limited to, cement (such as Portland cement, alumina cement (calcium aluminates), Portland instant cement (calcium silicates, anhydrite (CaSO 4 )), calcium sulfoaluminate cement (yelimite, belite, anhydrite), sulfa lattice cement (granulated slag, anhydrite, calcium silicates)). , Lime (such as quicklime (CaO) or slaked lime (Ca (OH) 2 )), gypsum (such as anhydrite (CaSO 4 ), hemihydrate (CaSO 4 · 0.5 H 2 O) or dihydrate (CaSO 4 · 2 H 2 O)), magnesia binder (magnesia, magnesium salts), water glass (alkali silicates, in particular sodium and / or potassium silicates) and geopolymers (eg aluminosilicates such as clays). Preferred examples of inorganic binders are quicklime, slaked lime, waterglass, gypsum, clay and cement. The proportion of the inorganic binder in the coating comprising at least one conductivity additive and at least one binder may be from 10 to 90% (for example 20 to 80%, 30 to 70%) by weight. Likewise, the proportion of inorganic binder in the dispersion containing at least one conductivity additive selected from conductivity additives comprising graphite, graphene and carbon black, and usable to produce a coating comprising at least one conductivity additive and at least one binder may be used 90% (for example 20 to 80%, 30 to 75% or 40 to 60%) by weight.

Das Flächengewicht des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung beträgt mindestens 250 g/m2, vorzugsweise mindestens 275 g/m2, mehr bevorzugt mindestens 300 g/m2, noch mehr bevorzugt mindestens 325 g/m2. Üblicherweise beträgt das Flächengewicht des beheizbaren Glasfaservlieses 600 g/m2 oder weniger. Diese Flächengewichte beziehen sich auf die Summe aus dem Glasfaservlies vor Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und der auf diesem Glasfaservlies befindlichen Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst.The weight per unit area of the heatable fiberglass mat according to the present invention is at least 250 g / m 2 , preferably at least 275 g / m 2 , more preferably at least 300 g / m 2 , even more preferably at least 325 g / m 2 . Usually, the weight per unit area of the heatable glass fiber fleece is 600 g / m 2 or less. These basis weights refer to the sum of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder, and the coating on this glass fiber fleece, which comprises at least one conductivity additive and at least one binder.

Das Flächengewicht (auch „flächenbezogene Masse“ genannt) eines Glasfaservlieses wird in der vorliegenden Erfindung gemäß DIN EN 29073-1-1992 bestimmt.The weight per unit area (also called the "area-related mass") of a glass fiber fleece is determined in the present invention according to DIN EN 29073-1-1992.

Der Gewichtsanteil der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung beträgt vorzugsweise mindestens 30%, mehr bevorzugt mindestens 35%, noch mehr bevorzugt mindestens 40%, bezogen auf die Summe der Gewichte des Bereiches des Glasfaservlieses, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst. Üblicherweise beträgt der Gewichtsanteil der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung nicht mehr als 65%, bezogen auf die Summe der Gewichte des Bereiches des Glasfaservlieses, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst. Wie weiter unten detailliert ausgeführt, kann das beheizbare Glasfaservlies nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sein. Daher wurde der Gewichtsanteil der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, nur auf die beschichteten Bereiche bezogen.The proportion by weight of the coating which comprises at least one conductivity additive and at least one binder of the heatable glass fiber fleece according to the present invention is preferably at least 30%, more preferably at least 35%, even more preferably at least 40%, based on the Sum of the weights of the region of the glass fiber fleece which is coated with the coating comprising at least one conductivity additive and at least one binder, before application of the coating comprising at least one conductivity additive and at least one binder, and the coating containing at least one conductivity additive and comprises at least one binder. Usually, the proportion by weight of the coating, which comprises at least one conductivity additive and at least one binder, of the heatable glass fiber fleece according to the present invention is not more than 65%, based on the sum of the weights of the area of the glass fiber fleece, which with the coating, the at least one conductivity additive and at least one binder is coated, prior to application of the coating comprising at least one conductivity additive and at least one binder, and the coating comprising at least one conductivity additive and at least one binder. As explained in detail below, the heatable glass fiber fleece can only be partially coated with the coating comprising at least one conductivity additive and at least one binder. Therefore, the weight fraction of the coating comprising at least one conductivity additive and at least one binder was based only on the coated areas.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, kann das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung einen oder mehrere voneinander getrennte Bereiche, welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, aufweisen. Beispielsweise können die voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, in einer 2 x n-Anordnung oder in einer 1 x n-Anordnung auf das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung aufgetragen sein, wobei n eine positive ganze Zahl von bis zu 500, wie bis zu 250 oder bis zu 200 ist (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist, kann n eine positive ganze Zahl von bis zu 500, wie bis zu 250 oder bis zu 200 sein).If the heatable fiberglass mat according to the present invention is only partially coated with the coating comprising at least one conductivity additive and at least one binder, the heatable glass fiber mat according to the present invention may have one or more separate regions which are coated with the coating. which comprises at least one conductivity additive and at least one binder, is / are coated. For example, the separate regions, which are coated with the coating comprising at least one conductivity additive and at least one binder, can be applied in a 2 × n arrangement or in a 1 × n arrangement to the heatable fiberglass mat according to the present invention where n is a positive integer of up to 500, such as up to 250 or up to 200 (in particular, if the heatable fiberglass nonwoven fabric is a rolled article, n can be a positive integer of up to 500, such as up to 250 or up to 200).

Der Einfachheit halber werden in der vorliegenden Erfindung die Begriffe „Bereich“, „Bereiche“ oder „Bereich(e)“ für den einen oder die mehreren voneinander getrennte Bereich(e), welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, verwendet.For the sake of simplicity, in the present invention, the terms "region," "regions," or "region (s)" will be used for the one or more separate regions (s) containing the coating, the at least one conductivity additive, and at least one binder comprises coated is / are used.

Üblicherweise sind diese Bereiche ungefähr gleich groß, d.h. das Verhältnis der Fläche des größten Bereiches zu der Fläche des kleinsten Bereiches ist üblicherweise kleiner als 1,1, vorzugsweise kleiner als 1,05. In einer bevorzugten Ausführungsform sind alle Bereiche gleich groß.Usually, these areas are approximately the same size, i. the ratio of the area of the largest area to the area of the smallest area is usually smaller than 1.1, preferably smaller than 1.05. In a preferred embodiment, all areas are the same size.

Die Dicke des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung beträgt vorzugsweise zwischen 0,20 und 1,00 mm, mehr bevorzugt zwischen 0,25 und 0,90 mm, noch mehr bevorzugt zwischen 0,30 und 0,80 mm. In einer Ausführungsform beträgt die Dicke des beheizbaren Glasfaservlieses zwischen 0,30 und 0,50 mm. Diese Ausführungsform ist insbesondere zur Abbringungen an Gegenstände, Wände und/oder Decken geeignet.The thickness of the heatable nonwoven fabric according to the present invention is preferably from 0.20 to 1.00 mm, more preferably from 0.25 to 0.90 mm, still more preferably from 0.30 to 0.80 mm. In one embodiment, the thickness of the heatable fiberglass mat is between 0.30 and 0.50 mm. This embodiment is particularly suitable for the removal of objects, walls and / or ceilings.

Die Dicke des Glasfaservlieses eines Glasfaservlieses wird in der vorliegenden Erfindung gemäß DIN EN ISO 9073-2:1997 bestimmt.The thickness of the glass fiber fleece of a glass fiber fleece is determined in the present invention according to DIN EN ISO 9073-2: 1997.

Die Höchstzugkraft des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung in Längs- und/oder Querrichtung beträgt vorzugsweise mindestens 120 N/5 cm, mehr bevorzugt beträgt die Höchstzugkraft des beheizbaren Glasfaservlieses in Längs- und/oder Querrichtung mindestens 135 N/5 cm, noch mehr bevorzugt beträgt die Höchstzugkraft des beheizbaren Glasfaservlieses

  • - in Längsrichtung mindestens 160 N/5 cm und/oder
  • - in Querrichtung mindestens 135 N/5 cm, mehr bevorzugt beträgt die Höchstzugkraft des beheizbaren Glasfaservlieses
  • - in Längsrichtung mindestens 175 N/5 cm und/oder
  • - in Querrichtung mindestens 145 N/5 cm.
The maximum tensile force of the heatable fiberglass mat according to the present invention in the longitudinal and / or transverse direction is preferably at least 120 N / 5 cm, more preferably the maximum tensile force of the heatable fiberglass mat in the longitudinal and / or transverse direction is at least 135 N / 5 cm, more preferably is the maximum tensile force of the heated glass fiber fleece
  • - in the longitudinal direction at least 160 N / 5 cm and / or
  • - In the transverse direction at least 135 N / 5 cm, more preferably the maximum tensile force of the heated glass fiber fleece
  • - in the longitudinal direction at least 175 N / 5 cm and / or
  • - in the transverse direction at least 145 N / 5 cm.

Die Höchstzugkraft des Glasfaservlieses in Längs- und Querrichtung wird durch die Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, üblicherweise nicht bzw. nicht wesentlich beeinträchtigt, sondern kann sogar erhöht werden.The maximum tensile force of the glass fiber fleece in the longitudinal and transverse direction is usually not or not significantly affected by the application of the coating, which comprises at least one conductivity additive and at least one binder, but may even be increased.

Beispielsweise beträgt die die Höchstzugkraft des beheizbaren Glasfaservlieses

  • - in Längsrichtung mindestens 210 N/5 cm und/oder
  • - in Querrichtung mindestens 175 N/5 cm.
For example, this is the maximum tensile force of the heated glass fiber fleece
  • - in the longitudinal direction at least 210 N / 5 cm and / or
  • - in the transverse direction at least 175 N / 5 cm.

Die Höchstzugkraft des Glasfaservlieses vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, in Längs- und/oder Querrichtung beträgt vorzugsweise mindestens 120 N/5 cm, mehr bevorzugt beträgt die Höchstzugkraft des Glasfaservlieses vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, in Längs- und/oder Querrichtung mindestens 135 N/5 cm, noch mehr bevorzugt beträgt die Höchstzugkraft des Glasfaservlieses vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst,

  • - in Längsrichtung mindestens 160 N/5 cm und/oder
  • - in Querrichtung mindestens 135 N/5 cm, mehr bevorzugt beträgt die Höchstzugkraft des Glasfaservlieses vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst,
  • - in Längsrichtung mindestens 175 N/5 cm und/oder
  • - in Querrichtung mindestens 145 N/5 cm.
The maximum tensile force of the glass fiber fleece before application of the Coating comprising at least one conductivity additive and at least one binder in the longitudinal and / or transverse direction is preferably at least 120 N / 5 cm, more preferably the maximum tensile force of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder, in the longitudinal and / or transverse direction at least 135 N / 5 cm, more preferably the maximum tensile force of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder,
  • - in the longitudinal direction at least 160 N / 5 cm and / or
  • in the transverse direction at least 135 N / 5 cm, more preferably the maximum tensile force of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder,
  • - in the longitudinal direction at least 175 N / 5 cm and / or
  • - in the transverse direction at least 145 N / 5 cm.

Die Höchstzugkraft eines Glasfaservlieses in Längs- und Querrichtung wird in der vorliegenden Erfindung gemäß DIN EN ISO 29073-3:1992 bestimmt.The maximum tensile force of a glass fiber fleece in the longitudinal and transverse directions is in the present invention according to DIN EN ISO 29073-3: 1992 certainly.

Das erfindungsgemäße Glasfaservlies kann eine Perforation und/oder Lochung aufweisen. Hierdurch wird beispielsweise die blasenfreie Anbringung des erfindungsgemäßen Glasfaservlieses erleichtert. Zudem kann sich Feuchtigkeit, die sich unterhalb des erfindungsgemäßen Glasfaservlieses befindet, leichter verflüchtigen. Da lediglich ein Gasdurchtritt erleichtert wird, können die einzelnen Löcher der Perforation und/oder Lochung klein gehalten werden, um die Funktionsweise des erfindungsgemäßen Glasfaservlieses nicht oder nur unwesentlich zu beeinträchtigen. Eine Perforation oder Lochung kann unter Umständen jedoch zu einer Verringerung der Höchstzugkraft führen. Die zuvor genannten Werte für die Höchstzugkraft betreffen daher normalerweise nur ein Glasfaservlies vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst bzw. ein beheizbares Glasfaservlies gemäß der vorliegenden Erfindung, welches (noch) keine Perforation und/oder Lochung aufweist. Da eine Perforation und/oder Lochung üblicherweise nach Anbringung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, durchgeführt wird, kann die Höchstzugkraft des Glasfaservlieses vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, bzw. des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung während der Herstellung des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung und vor der Perforation und/oder Lochung bestimmt werden.The glass fiber fleece according to the invention may have a perforation and / or perforation. As a result, for example, the bubble-free attachment of the glass fiber fleece according to the invention is facilitated. In addition, moisture, which is located below the glass fiber mat according to the invention, more easily volatilize. Since only a gas passage is facilitated, the individual holes of the perforation and / or perforation can be kept small in order not to affect the functioning of the glass fiber fleece according to the invention or only insignificantly. However, perforation or perforation may result in a reduction in the maximum tensile force. The abovementioned values for the maximum tensile force therefore normally relate only to a glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder or a heatable glass fiber fleece according to the present invention which (still) has no perforation and / or perforation. Since a perforation and / or perforation is usually carried out after the application of the coating, which comprises at least one conductivity additive and at least one binder, the maximum tensile force of the glass fiber fleece before application of the coating, which comprises at least one conductivity additive and at least one binder, or the heatable Fiberglass mat according to the present invention during the production of the heatable fiberglass mat according to the present invention and before the perforation and / or perforation are determined.

Die Ausmaße und Form des Glasfaservlieses der vorliegenden Erfindung können herkömmlich sein und sind daher nicht besonders begrenzt. In Draufsicht (d.h. in Blickrichtung des Lotes auf die Fläche, die von der Länge und Breite des Glasfaservlieses aufgespannt wird) kann das Glasfaservlies jede beliebige zweidimensionale Form aufweisen, z.B. rechteckig, quadratisch, kreisförmig, ellipsoid, in Form einer Raute oder eines Parallelogramms, etc.The dimensions and shape of the glass fiber fabric of the present invention may be conventional and are therefore not particularly limited. In plan view (i.e., in the direction of the solder on the surface spanned by the length and width of the glass fiber mat), the glass fiber mat may have any two-dimensional shape, e.g. rectangular, square, circular, ellipsoidal, in the form of a rhombus or a parallelogram, etc.

Vorzugsweise weist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht eine Fläche von mindestens 50,0 cm2, mehr bevorzugt mindestens 64,0 cm2, noch mehr bevorzugt mindestens 225 cm2 und am meisten bevorzugt mindestens 400 cm2, auf. Das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung kann in Draufsicht eine Fläche von bis zu 500 m2 aufweisen (beispielsweise falls das beheizbare Glasfaservlies als Rollware ausgeführt ist). Vorzugsweise weist das beheizbare Glasfaservlies in Draufsicht eine Fläche von nicht mehr als 8,00 m2, mehr bevorzugt von nicht mehr als 6,00 m2 auf, beispielsweise beträgt die Fläche des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung in Draufsicht nicht mehr als 3,00 m2, nicht mehr als 2,00 m2 oder nicht mehr als 1,00 m2 oder ist (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) in Abschnitte dieser Größen teilbar, vorzugsweise ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, mehr bevorzugt ist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung parallel zu einer Kante des beheizbaren Glasfaservlieses in Abschnitte dieser Größen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen. Beispielsweise kann das beheizbare Glasfaservlies (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) abwechselnd Bereiche, die eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweisen, und Bereiche, die keine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweisen, aufweisen. Mehr bevorzugt weist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht eine Fläche von mindestens 50,0 cm2, vorzugsweise von mindestens 64,0 cm2, noch mehr bevorzugt von mindestens 225 cm2 und am meisten bevorzugt von mindestens 400 cm2, auf und das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung weist in Draufsicht eine Fläche von nicht mehr als 8,00 m2, vorzugsweise von nicht mehr als 6,00 m2 auf, beispielsweise beträgt die Fläche des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung in Draufsicht nicht mehr als 3,00 m2, nicht mehr als 2,00 m2 oder nicht mehr als 1,50 m2 oder ist (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) in Abschnitte dieser Größen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, vorzugsweise ist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung parallel zu einer Kante des beheizbaren Glasfaservlieses in Abschnitte dieser Größen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen. Preferably, the heatable fiberglass mat according to the present invention has in plan view an area of at least 50.0 cm 2 , more preferably at least 64.0 cm 2 , even more preferably at least 225 cm 2 and most preferably at least 400 cm 2 . The heatable glass fiber fleece according to the present invention can have an area of up to 500 m 2 in plan view (for example, if the heatable glass fiber fleece is designed as rolled goods). Preferably, the heatable glass fiber fleece in plan view has an area of not more than 8.00 m 2 , more preferably not more than 6.00 m 2 , for example, the area of the heatable glass fiber fleece according to the present invention in plan view is not more than 3, 00 m 2 , not more than 2.00 m 2 or not more than 1.00 m 2 or is (especially if the heatable glass fiber fleece designed as a roll) divisible into sections of these sizes, preferably without a portion of the heated glass fiber fleece, which a Coating comprising at least one conductivity additive and at least one binder has to be severed, more preferably the heatable fiberglass web according to the present invention is divisible into sections of these sizes parallel to an edge of the heatable fiberglass web without a region of the heatable fiberglass web having a coating containing at least one conductivity additive and at least ei n comprises binder, has to cut through. For example, the heatable glass fiber fleece (in particular if the heatable glass fiber fleece is designed as a rolled product) may alternately have areas which comprise a coating comprising at least one conductivity additive and at least one binder, and areas which do not have a coating, the at least one conductivity additive and at least one binder comprises, have, have. More preferably, the heatable fiberglass mat according to the present invention has in plan view an area of at least 50.0 cm 2 , preferably at least 64.0 cm 2 , more preferably at least 225 cm 2, and most preferably at least 400 cm 2 and the heatable glass fiber nonwoven according to the present invention has an area of not more than 8.00 m 2 , preferably not more than 6.00 m 2 in plan view, for example, the area of the heatable nonwoven fabric according to the present invention is not more in plan view as 3.00 m 2 , not more than 2.00 m 2 or not more than 1.50 m 2, or is divisible into sections of these sizes (in particular if the heatable glass fiber fleece is designed as rolled goods), without a region of the heatable glass fiber fleece, which has a coating which comprises at least one conductivity additive and at least one binder has to cut, preferably is the wärba The glass fiber nonwoven according to the present invention can be divided into sections of these sizes parallel to an edge of the heatable fiberglass mat without cutting through a region of the heatable fiberglass mat which has a coating comprising at least one conductivity additive and at least one binder.

Vorzugsweise weist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht die Form eines Quadrates, eines Rechtecks, einer Raute oder eines Parallelogramms auf und weist insbesondere eine Fläche wie im vorangegangen Absatz definiert auf. Insbesondere bevorzugt weist das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht die Form eines Quadrates oder eines Rechtecks auf.Preferably, the heatable fiberglass mat according to the present invention in plan view in the form of a square, a rectangle, a rhombus or a parallelogram and in particular has a surface as defined in the preceding paragraph. Particularly preferably, the heatable fiberglass mat according to the present invention in plan view in the form of a square or a rectangle.

Im mathematischen Sinn ist eine Raute ein Spezialfall eines Parallelogramms und ein Quadrat ist ein Spezialfall eines Rechtecks. In der vorliegenden Erfindung werden Rauten nicht als Parallelogramm und Quadrate nicht als Rechteck angesehen.In the mathematical sense, a diamond is a special case of a parallelogram and a square is a special case of a rectangle. In the present invention, diamonds are not considered a parallelogram and squares are not a rectangle.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht die Form einer Raute oder eines Parallelogramms aufweist, beträgt der spitze Winkel der Raute oder des Parallelogramms vorzugsweise nicht weniger als 30°, mehr bevorzugt nicht weniger als 45° und noch mehr bevorzugt nicht weniger als 60°.If the heatable nonwoven fabric according to the present invention has the form of a rhombus or a parallelogram in plan view, the acute angle of the rhombus or the parallelogram is preferably not less than 30 °, more preferably not less than 45 °, and still more preferably not less than 60 °.

Ein Quadrat, ein Rechteck, eine Raute und ein Parallelogramm weisen eine erste Kante und eine zweite Kante auf, die nicht parallel zueinander sind. Zu jeder dieser zwei Kanten existiert jeweils eine parallele und gleichlange Kante, weswegen der Einfachheit halber im Folgenden nur auf die erste und zweite Kante Bezug genommen wird.A square, a rectangle, a rhombus, and a parallelogram have a first edge and a second edge that are not parallel to each other. Each of these two edges has a parallel edge of equal length, which is why in the following only the first and second edges are referred to for the sake of simplicity.

Die erste und die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung können gleich lang sein, d.h. das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung weist in Draufsicht die Form eines Quadrates oder einer Raute auf, oder die erste und die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung können unterschiedlich lang sein, d.h. das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung weist in Draufsicht die Form eines Rechtecks oder Parallelogramms auf. Falls die erste und die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung unterschiedlich lang sind, wird die kürzere Kante als erste Kante und die längere Kante als zweite Kante angesehen.The first and second edges of the heated fiberglass mat according to the present invention may be the same length, i. the heatable glass fiber nonwoven according to the present invention has the shape of a square or a rhombus in plan view, or the first and second edges of the heatable nonwoven fabric according to the present invention may be of different lengths, i. The heatable glass fiber mat according to the present invention has the shape of a rectangle or parallelogram in plan view. If the first and the second edge of the heatable glass fiber fleece according to the present invention have different lengths, the shorter edge is considered as the first edge and the longer edge as the second edge.

Die erste Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung weist vorzugsweise eine Länge von 8,00 bis 100 cm, mehr bevorzugt von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf. Die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung kann eine Länge von bis zu 500 m aufweisen (beispielsweise falls das beheizbare Glasfaservlies als Rollware ausgeführt ist). Die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung weist vorzugsweise eine Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm auf oder die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) ist in Abschnitte einer Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm, beispielsweise 20,0 bis 250 cm, 20,0 bis 200 cm oder 20,0 bis 150 cm, teilbar, vorzugsweise ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, mehr bevorzugt ist die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) parallel zu einer anderen Kante des beheizbaren Glasfaservlieses, vorzugsweise parallel zu der ersten Kante, in Abschnitte dieser Längen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen. Insbesondere bevorzugt weist die erste Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung eine Länge von 8,00 bis 100 cm, vorzugsweise von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf, und die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung weist eine Länge von 8,00 bis 600 cm, vorzugsweise von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm auf oder die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) ist in Abschnitte einer Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm, beispielsweise 20,0 bis 250 cm, 20,0 bis 200 cm oder 20,0 bis 150 cm, teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, vorzugsweise ist die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) parallel zu einer anderen Kante, vorzugsweise parallel zu der ersten Kante, des beheizbaren Glasfaservlieses in Abschnitte dieser Längen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen.The first edge of the heated fiberglass mat according to the present invention preferably has a length of from 8.00 to 100 cm, more preferably from 15.0 to 100 cm, and most preferably from 20.0 cm to 100 cm. The second edge of the heatable fiberglass mat according to the present invention may have a length of up to 500 m (for example, if the heatable fiberglass mat is designed as rolled goods). The second edge of the heated fiberglass mat according to the present invention preferably has a length of from 8.00 to 600 cm, more preferably from 15.0 to 600 cm and most preferably from 20.0 cm to 600 cm or the second edge of the heatable Glass fiber mat according to the present invention (especially if the heatable glass fiber mat is designed as a rolled product) is in sections of a length from 8.00 to 600 cm, more preferably from 15.0 to 600 cm and most preferably from 20.0 cm to 600 cm , For example, 20.0 to 250 cm, 20.0 to 200 cm or 20.0 to 150 cm, divisible, preferably without a portion of the heatable glass fiber nonwoven, which has a coating comprising at least one conductivity additive and at least one binder more preferably, the second edge of the heatable fiberglass mat according to the present invention (in particular if the heatable glass fiber mat is designed as a rolled product) is paral to another edge of the heatable fiberglass mat, preferably parallel to the first edge, divisible into sections of these lengths without severing a portion of the heatable fiberglass mat which has a coating comprising at least one conductivity additive and at least one binder. Particularly preferably, the first edge of the heatable fiberglass mat according to the present invention has a length of 8.00 to 100 cm, preferably of 15.0 to 100 cm and most preferably of 20.0 cm to 100 cm, and the second edge of Heated fiberglass mat according to the present invention has a length of 8.00 to 600 cm, preferably of 15.0 to 600 cm and most preferably of 20.0 cm to 600 cm or the second edge of the heatable fiberglass mat according to the present invention ( in particular if the heatable glass fiber nonwoven fabric is designed as a rolled product) is in sections of a length of 8.00 to 600 cm, more preferably 15.0 to 600 cm, and most preferably 20.0 cm to 600 cm, for example 20.0 to 250 cm, 20.0 to 200 cm or 20.0 to 150 cm, divisible, without a region of the heatable glass fiber fleece, which has a coating comprising at least one conductivity additive and at least one binder Preferably, the second edge of the heatable fiberglass mat according to the present invention (in particular if the heatable fiberglass mat is made as a roll) is divisible into sections of these lengths parallel to another edge, preferably parallel to the first edge, of the heatable fiberglass mat without a region of the heatable glass fiber fleece, which has a coating comprising at least one conductivity additive and at least one binder, to cut.

In einer Ausführungsform weist die erste Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung eine Länge von 8,00 bis 100 cm, mehr bevorzugt von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf, und die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung weist eine Länge von 8,00 bis 300 cm, mehr bevorzugt von 15,0 bis 200 cm und am meisten bevorzugt von 20,0 cm bis 150 cm auf, oder die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) ist in Abschnitte dieser Längen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, vorzugsweise ist die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) parallel zu einer anderen Kante, vorzugsweise parallel zu der ersten Kante, des beheizbaren Glasfaservlieses in Abschnitte dieser Längen teilbar, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen.In one embodiment, the first edge of the heatable fiberglass mat according to the present invention has a length of from 8.00 to 100 cm, more preferably from 15.0 to 100 cm, and most preferably from 20.0 cm to 100 cm, and the second The edge of the heated fiberglass mat according to the present invention has a length of from 8.00 to 300 cm, more preferably from 15.0 to 200 cm, and most preferably from 20.0 cm to 150 cm, or the second edge of the heatable fiberglass mat according to FIG of the present invention (in particular if the heatable fiberglass nonwoven fabric is designed as rolled goods) can be divided into sections of these lengths without cutting through a region of the heatable fiberglass mat which has a coating comprising at least one conductivity additive and at least one binder, preferably second edge of the heatable glass fiber fleece according to the present invention (in particular if the heatable glass fiber non-woven is designed as a roll) parallel to another edge, preferably parallel to the first edge, the heatable fiberglass mat in sections of these lengths divisible, without a portion of the heated glass fiber mat, which comprises a coating comprising at least one conductivity additive and at least one binder to cut through.

In einer weiteren Ausführungsform

  • - weist das beheizbare Glasfaservlies die Form eines Rechtecks auf, wobei die Länge der ersten Kante 10,0 bis 100 cm, vorzugsweise 50,0 bis 100 cm beträgt, und die zweite Kante des beheizbaren Glasfaservlieses eine Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm, beispielsweise 20,0 bis 250 cm, 20,0 bis 200 cm oder 20,0 bis 150 cm aufweist oder die zweite Kante (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) eine Länge von bis zu 500 m aufweist, wobei die zweite Kante des beheizbaren Glasfaservlieses in Abschnitte einer Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm, beispielsweise 20,0 bis 250 cm, 20,0 bis 200 cm oder 20,0 bis 150 cm, teilbar ist, ohne einen Bereich des beheizbaren Glasfaservlieses, welcher eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, zu durchtrennen, vorzugsweise parallel zu der ersten Kante,
  • - weist das beheizbare Glasfaservlies (insbesondere falls das beheizbare Glasfaservlies als Rollware ausgeführt ist) zwei bis 250, beispielsweise 2 bis 500 voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, wobei diese Bereiche in Form eines Quadrats oder Rechtecks, vorzugsweise in Form eines Rechtecks, ausgeführt sind,
  • - erstreckt sich jeder dieser Bereiche von der zweiten Kante des beheizbaren Glasfaservlieses zu der Kante, die zu dieser zweiten Kante parallel ist, oder ist maximal 10,0 cm, bevorzugt maximal 8,00 cm, noch mehr bevorzugt maximal 6,0 cm (wie 0,1 cm) jeweils von der zweiten Kante des beheizbaren Glasfaservlieses und der Kante die zu dieser zweiten Kante parallel ist, entfernt und parallel zueinander angeordnet,
  • - weist jeder dieser Bereiche eine Fläche von 0,25 bis 2,00 m2 auf, und
  • - beträgt der Abstand zwischen zwei Bereichen, mindestens 10,0 cm, bevorzugt mindestens 30,0 cm und am meisten bevorzugt mindestens 50,0 cm.
In a further embodiment
  • the heated glass fiber fleece has the shape of a rectangle, the length of the first edge being 10.0 to 100 cm, preferably 50.0 to 100 cm, and the second edge of the heatable glass fiber fleece being 8.00 to 600 cm long, more preferably from 15.0 to 600 cm, and most preferably from 20.0 cm to 600 cm, for example 20.0 to 250 cm, 20.0 to 200 cm or 20.0 to 150 cm or the second edge (in particular if the heatable fiberglass mat is made as a roll) has a length of up to 500 m, the second edge of the heatable fiberglass mat being in lengths of 8.00 to 600 cm, more preferably 15.0 to 600 cm, and most preferably from 20.0 cm to 600 cm, for example 20.0 to 250 cm, 20.0 to 200 cm or 20.0 to 150 cm, is divisible, without a portion of the heated glass fiber fleece, which is a coating containing at least one conductivity additive and at least one binder comprises, has to race, preferably parallel to the first edge,
  • the heatable glass fiber fleece (in particular if the heatable fiberglass fleece is designed as rolled goods) has two to 250, for example 2 to 500, separate regions which are coated with the coating comprising at least one conductivity additive and at least one binder; In the form of a square or rectangle, preferably in the form of a rectangle,
  • each of these areas extends from the second edge of the heatable fiberglass mat to the edge parallel to this second edge, or is at most 10.0 cm, preferably at most 8.00 cm, more preferably at most 6.0 cm (as in FIG 0.1 cm) each of the second edge of the heated glass fiber fleece and the edge which is parallel to this second edge, removed and arranged parallel to each other,
  • each of these areas has an area of 0.25 to 2.00 m 2 , and
  • the distance between two regions is at least 10.0 cm, preferably at least 30.0 cm and most preferably at least 50.0 cm.

In einer weiteren Ausführungsform des Glasfaservlieses der vorliegenden Erfindung weist das Glasfaservlies die Form eines Rechtecks oder Parallelogramms, insbesondere die Form eines Rechtecks, auf, wobei die erste Kante zwischen 66,0 und 100 cm misst, und die zweite Kante zwischen 120 und 160 cm misst, vorzugsweise die erste Kante zwischen 76,0 und 96,0 cm misst, und die zweite Kante zwischen 130 und 150 cm misst.In a further embodiment of the glass fiber fleece of the present invention, the glass fiber fleece in the form of a rectangle or parallelogram, in particular the shape of a rectangle, with the first edge measures between 66.0 and 100 cm, and the second edge between 120 and 160 cm measures , preferably the first edge measures between 76.0 and 96.0 cm, and the second edge measures between 130 and 150 cm.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht die Form eines Quadrates oder einer Raute aufweist, sind die erste und die zweite Kante gleich lang, und beide Kanten weisen üblicherweise die Abmessungen der ersten Kante wie oben ausgeführt auf.If the heatable glass fiber nonwoven according to the present invention has the shape of a square or a rhombus in plan view, the first and the second edge are the same length, and both edges usually have the dimensions of the first edge as stated above.

In einer bevorzugten Ausführungsform (im Folgenden auch als „Ausführungsform (A)“ bezeichnet) des Glasfaservlieses der vorliegenden Erfindung beträgt das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks vorzugsweise zwischen 0,20 und < 1,00 oder das beheizbare Glasfaservlies weist die Form einer Raute oder eines Quadrates auf, mehr bevorzugt beträgt das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks zwischen 0,40 und 0,80, noch mehr bevorzugt zwischen 0,50 und 0,70.In a preferred embodiment (hereinafter also referred to as "embodiment (A)") of the glass fiber fabric of the present invention, the aspect ratio between the first edge of the parallelogram and the second edge of the parallelogram is preferably between 0.20 and < 1.00 or the heated fiberglass mat has the shape of a rhombus or a square, more preferably the aspect ratio between the first edge of the parallelogram or rectangle and the second edge of the parallelogram or rectangle is between 0.40 and 0.80 more preferably between 0.50 and 0.70.

Ausführungsform (A) ist beispielsweise geeignet, um herkömmliche Glasfaservliese, die zur Wand- und/oder Deckenmontage verwendet werden, zu ersetzen.Embodiment (A) is suitable, for example, to replace conventional glass fiber nonwoven fabrics used for wall and / or ceiling mounting.

In einer alternativen Ausführungsform (im Folgenden auch als „Ausführungsform (B)“ bezeichnet) kann das Glasfaservlies band- oder streifenförmig in ausgestaltet sein (z.B. als Bandware), beispielsweise in Form eines Rechtecks oder Parallelogramms. In dieser Ausführungsform (B) beträgt das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks üblicherweise weniger als 0,40, vorzugsweise weniger als 0,30, mehr bevorzugt weniger als 0,20, beispielsweise weniger als 0,10, weniger als 0,05 oder weniger als 0,025.In an alternative embodiment (hereinafter also referred to as "embodiment (B)"), the glass fiber fleece can be configured in strip or strip form (eg as a band product), for example in the form of a rectangle or parallelogram. In this embodiment (B), this is Aspect ratio between the first edge of the parallelogram or rectangle and the second edge of the parallelogram is typically less than 0.40, preferably less than 0.30, more preferably less than 0.20, for example less than 0.10, less than 0.05 or less than 0.025.

Ausführungsform (B) ist beispielsweise geeignet, um der Schimmelbildung an Wänden, Decken und Böden, insbesondere in Ecken oder an Stellen mit Kältebrücken vorzubeugen und/oder zu verhindern.Embodiment (B) is suitable, for example, for preventing and / or preventing the formation of mold on walls, ceilings and floors, in particular in corners or at locations with cold bridges.

Im Folgenden werden alle Ausführungsformen des erfindungsgemäßen beheizbaren Glasfaservlieses beschrieben, es sei denn, es wird ausdrücklich auf bestimmte Ausführungsformen verwiesen.In the following, all embodiments of the heatable fiberglass mat according to the invention are described, unless it is expressly made to certain embodiments.

Wie oben ausgeführt, kann das beheizbare Glasfaservlies nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sein. Falls beispielsweise ein bestimmter Bereich eines Gegenstandes, eines Bodens, einer Wand und/oder einer Decke ganzflächig mit Glasfaservlies versehen werden soll, jedoch nur Teile dieses bestimmten Bereiches beheizt werden sollen (beispielsweise können sich auf einem Boden, an einer Wand und/oder an einer Decke Bilder und/oder Möbel befinden bzw. ist deren Anbringung geplant), kann/können das/die teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtete(n) beheizbare(n) Glasfaservlies(e) so angebracht werden, dass nur der/die zu beheizende(n) Bereich(e) die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist/aufweisen. Hierdurch kann die Anzahl der Glasfaservliese, welche keine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, reduziert werden bzw. es kann vollständig auf diese verzichtet werden. Somit kann beispielsweise der Arbeitsaufwand, der notwendig ist, mehrere Glasfaservliese auf Stoß zu montieren, verringert werden.As stated above, the heatable glass fiber fleece may be only partially coated with the coating comprising at least one conductivity additive and at least one binder. For example, if a particular area of an article, a floor, a wall and / or a ceiling to be provided over the entire surface with glass fiber fleece, but only parts of this particular area to be heated (for example, can be on a floor, on a wall and / or on a Ceiling images and / or furniture are or is their attachment planned), / may / may be partially / with the coating comprising at least one conductivity additive and at least one binder coated (s) heatable (n) glass fiber fleece (s) so attached that only the area (s) to be heated has / have the coating comprising at least one conductivity additive and at least one binder. As a result, the number of glass fiber webs which does not comprise a coating which comprises at least one conductivity additive and at least one binder can be reduced or it can be completely dispensed with. Thus, for example, the labor required to mount multiple glass fiber webs on impact can be reduced.

Wie oben ausgeführt, kann die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf beiden Seiten des Glasfaservlieses oder nur auf einer Seite des beheizbaren Glasfaservlieses aufgebracht sein.As stated above, the coating, which comprises at least one conductivity additive and at least one binder, can be applied on both sides of the glass fiber fleece or only on one side of the heatable glass fiber fleece.

In einer Ausführungsform weisen in Draufsicht auf eine Fläche des beheizbaren Glasfaservlieses, vorzugsweise mindestens 25%, mehr bevorzugt mindestens 50% und am meisten bevorzugt mindestens 75% der betrachteten Fläche mindestens auf der dem Betrachter zugewandten oder abgewandten Seite des beheizbaren Glasfaservlieses eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.In one embodiment, in a plan view of a surface of the heatable fiberglass mat, preferably at least 25%, more preferably at least 50% and most preferably at least 75% of the area considered, at least on the side of the heated fiberglass mat facing or facing away from the viewer a coating which is at least a conductive additive and at least one binder comprises.

Dies soll anhand der folgenden Beispiele erläutert werden.

  • - Falls das beheizbare Glasfaservlies auf einer Seite vollflächig mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, weisen 100% der betrachteten Fläche eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.
  • - Falls das beheizbare Glasfaservlies jeweils auf beiden Seiten vollflächig mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, weisen ebenfalls 100% der betrachteten Fläche eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.
  • - Falls eine Hälfte des beheizbaren Glasfaservlieses auf einer Seite mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist und die andere Hälfte, also der Teil des Glasfaservlieses, der zunächst auf keiner Seite eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, auf der anderen Seite mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet wird, weisen ebenfalls 100% der betrachteten Fläche eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.
  • - Falls jedoch eine Hälfte des beheizbaren Glasfaservlieses auf beiden Seiten mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist und die andere Hälfte auf keiner Seite eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufweist, weisen 50% der betrachteten Fläche eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.
This will be explained by the following examples.
  • - If the heatable fiberglass fabric on one side over the entire surface with the coating, which comprises at least one conductivity additive and at least one binder coated 100% of the surface considered a coating comprising at least one conductivity additive and at least one binder on.
  • If the heatable glass fiber fleece is coated on both sides over its entire area with the coating which comprises at least one conductivity additive and at least one binder, likewise 100% of the surface considered has a coating comprising at least one conductivity additive and at least one binder.
  • - If one half of the heated glass fiber fleece coated on one side with the coating comprising at least one conductivity additive and at least one binder, and the other half, ie the part of the glass fiber fleece, the first on no side a coating, the at least one conductivity additive and At least one binder comprises, coated on the other side with the coating, which comprises at least one conductivity additive and at least one binder, also have 100% of the surface considered a coating comprising at least one conductivity additive and at least one binder on.
  • However, if one half of the heatable fiberglass mat is coated on both sides with the coating comprising at least one conductivity additive and at least one binder, and the other half on each side has a coating comprising at least one conductivity additive and at least one binder 50% of the surface considered a coating comprising at least one conductivity additive and at least one binder on.

In einer Ausführungsform weisen in Draufsicht auf eine Fläche des beheizbaren Glasfaservlieses, vorzugsweise mindestens 95,0%, mehr bevorzugt mindestens 97,5% und am meisten bevorzugt 100% der betrachteten Fläche mindestens auf der dem Betrachter zugewandten oder abgewandten Seite des beheizbaren Glasfaservlieses eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf.In one embodiment, in plan view of a surface of the heatable fiberglass mat, preferably at least 95.0%, more preferably at least 97.5%, and most preferably 100% of the area considered, at least on the side of the heated fiberglass mat facing or facing away from the viewer comprising at least one conductivity additive and at least one binder.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung einen oder mehrere voneinander getrennte Bereiche, welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, aufweist, so weist jeder Bereich der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, vorzugsweise mindestens eine Fläche von 64,0 cm2, mehr bevorzugt mindestens 225 cm2 und am meisten bevorzugt mindestens 400 cm2 auf. If the heatable glass fiber nonwoven according to the present invention has one or more separate regions coated with the coating comprising at least one conductivity additive and at least one binder, then each region of the coating comprising at least one Conductive additive and at least one binder comprises, preferably at least an area of 64.0 cm 2 , more preferably at least 225 cm 2 and most preferably at least 400 cm 2 .

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung einen oder mehrere voneinander getrennte Bereich(e), welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, aufweist, so weist jeder Bereich der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, vorzugsweise eine Fläche von nicht mehr als 5,00 m2, mehr bevorzugt von nicht mehr als 3,00 m2 und am meisten bevorzugt von nicht mehr als 1,00 m2 auf.If the heatable glass fiber fleece according to the present invention has one or more separate regions which are / is coated with the coating which comprises at least one conductivity additive and at least one binder, then each region of the coating, which comprises at least one conductivity additive and at least one binder, preferably an area of not more than 5.00 m 2 , more preferably not more than 3.00 m 2, and most preferably not more than 1.00 m 2 .

Wie oben ausgeführt werden der Einfachheit halber die Begriffe „Bereich“, „Bereiche“ oder „Bereich(e)“ für den einen oder die mehreren voneinander getrennte Bereich(e), welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, verwendet.As noted above, for simplicity, the terms "region," "regions," or "region (s)" will be for the one or more separate regions (s) containing the coating, the at least one conductivity additive, and at least a binder comprises coated is / are used.

Der Abstand zwischen zwei Bereichen, sofern mindestens zwei Bereiche auf dem beheizbaren Glasfaservlies angeordnet sind, beträgt vorzugsweise mindestens 10,0 cm, mehr bevorzugt mindestens 30,0 cm und am meisten bevorzugt mindestens 50,0 cm.The distance between two regions, if at least two regions are arranged on the heatable glass fiber fleece, is preferably at least 10.0 cm, more preferably at least 30.0 cm and most preferably at least 50.0 cm.

Vorzugsweise weist jeder Bereich der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, in Draufsicht die Form eines Quadrates, eines Rechtecks, einer Raute oder eines Parallelogramms auf, mehr bevorzugt die Form eines Quadrates oder eines Rechtecks.Preferably, each region of the coating comprising at least one conductivity additive and at least one binder has in plan view the shape of a square, a rectangle, a rhombus or a parallelogram, more preferably the shape of a square or a rectangle.

Falls ein oder mehrere Bereich(e) der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, in Draufsicht die Form einer Raute oder eines Parallelogramms aufweist/aufweisen, beträgt der spitze Winkel der Raute(n) oder des/der Parallelogramms/Parallelogramme vorzugsweise nicht weniger als 30°, mehr bevorzugt nicht weniger als 45° und noch mehr bevorzugt nicht weniger als 60°.If one or more regions of the coating, which comprises at least one conductivity additive and at least one binder, have the form of a rhombus or a parallelogram in plan view, the acute angle of the rhombus (s) or of the parallelogram (s) is / are parallelograms preferably not less than 30 °, more preferably not less than 45 ° and even more preferably not less than 60 °.

Wie oben ausgeführt, weisen ein Quadrat, ein Rechteck, eine Raute und ein Parallelogramm eine erste Kante und eine zweite Kante auf, die nicht parallel zueinander sind. Zu jeder dieser zwei Kanten existiert jeweils eine parallele und gleichlange Kante, weswegen der Einfachheit halber im Folgenden nur auf die erste und zweite Kante Bezug genommen wird.As stated above, a square, a rectangle, a rhombus, and a parallelogram have a first edge and a second edge that are not parallel to each other. Each of these two edges has a parallel edge of equal length, which is why in the following only the first and second edges are referred to for the sake of simplicity.

Im Folgenden wird die Ausführungsform, in der das beheizbare Glasfaservlies nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, weiter beschrieben.In the following, the embodiment in which the heatable glass fiber fleece is only partially coated with the coating which comprises at least one conductivity additive and at least one binder is described further.

Die erste und die zweite Kante eines Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, können gleich lang sein, d.h. der Bereich der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, weist in Draufsicht die Form eines Quadrates oder einer Raute auf, oder die erste und die zweite Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, können unterschiedlich lang sein, d.h. der Bereich der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, weist in Draufsicht die Form eines Rechtecks oder Parallelogramms auf. Falls die erste und die zweite Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, unterschiedlich lang sind, wird die kürzere Kante als erste Kante und die längere Kante als zweite Kante angesehen.The first and second edges of a portion of the coating comprising at least one conductivity additive and at least one binder may be the same length, i. the region of the coating comprising at least one conductivity additive and at least one binder has, in plan view, the shape of a square or rhombus, or the first and second edges of the region of the coating comprising at least one conductivity additive and at least one binder be different in length, ie the region of the coating which comprises at least one conductivity additive and at least one binder has in plan view the shape of a rectangle or a parallelogram. If the first and second edges of the area of the coating comprising at least one conductivity additive and at least one binder are of different lengths, the shorter edge is considered to be the first edge and the longer edge the second edge.

Die erste Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, weist vorzugsweise eine Länge von 8,00 bis 100 cm, mehr bevorzugt von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf und/oder die zweite Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, weist vorzugsweise eine Länge von 8,00 bis 500 cm, mehr bevorzugt von 15,0 bis 300 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf. Insbesondere bevorzugt weist die erste Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, eine Länge von 8,00 bis 100 cm, vorzugsweise von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf, und die zweite Kante des Bereiches der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, weist eine Länge von 8,00 bis 500 cm, vorzugsweise von 15,0 bis 300 cm und am meisten bevorzugt von 20,0 cm bis 100 cm auf.The first edge of the area of the coating comprising at least one conductivity additive and at least one binder preferably has a length of from 8.00 to 100 cm, more preferably from 15.0 to 100 cm, and most preferably from 20.0 cm to 100 1 cm to and / or the second edge of the area of the coating comprising at least one conductivity additive and at least one binder preferably has a length of from 8.00 to 500 cm, more preferably from 15.0 to 300 cm and most preferably from 20 , 0 cm to 100 cm on. More preferably, the first edge of the area of the coating comprising at least one conductivity additive and at least one binder has a length of from 8.00 to 100 cm, preferably from 15.0 to 100 cm, and most preferably from 20.0 cm to 100 2 cm and the second edge of the area of the coating comprising at least one conductivity additive and at least one binder has a length of from 8.00 to 500 cm, preferably from 15.0 to 300 cm and most preferably 20.0 cm up to 100 cm.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung in Draufsicht die Form eines Quadrates, eines Rechtecks, einer Raute oder eines Parallelogramms aufweist, wie oben ausgeführt, können der/die Bereich(e) der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, so ausgeführt sein, dass sie sich von der zweiten Kante des beheizbaren Glasfaservlieses zu der Kante die zu dieser zweiten Kante parallel ist, erstrecken oder maximal 10,0 cm, bevorzugt maximal 8,00 cm, noch mehr bevorzugt maximal 6,0 cm (wie 0,1 cm) jeweils von der zweiten Kante des beheizbaren Glasfaservlieses und der Kante die zu dieser zweiten Kante parallel ist entfernt angeordnet sind, üblicherweise parallel zueinander. Beispielsweise, erstrecken sich der/die beheizbare(n) Bereich(e), falls das beheizbare Glasfaservlies in Draufsicht die Form eines Rechtecks aufweist, über die gesamte Breite des beheizbaren Glasfaservlieses.If the heatable fiberglass mat according to the present invention in plan view in the form of a square, a rectangle, a rhombus or a parallelogram, as stated above, For example, the area (s) of the coating comprising at least one conductivity additive and at least one binder may be configured to extend from the second edge of the heatable fiberglass mat to the edge parallel to that second edge, or at most 10 , 0 cm, preferably not more than 8.00 cm, more preferably not more than 6.0 cm (such as 0.1 cm) each of the second edge of the heated glass fiber fleece and the edge which is parallel to this second edge are arranged away, usually in parallel to each other. For example, extend the / the heatable area (s), if the heated glass fiber fleece in plan view has the shape of a rectangle over the entire width of the heated glass fiber fleece.

In einer bevorzugten Ausführungsform sind bis zu vier Bereiche auf dem Glasfaservlies so angeordnet wie im vorangegangen Absatz definiert. Inbesondere bevorzugt weisen in dieser Ausführungsform das beheizbare Glasfaservlies die Form eines Rechtecks und die Bereiche die Form eines Rechtecks oder eines Quadrates auf. Hieraus resultiert eine „leiterartige“ Struktur, welche ermöglicht, passende Stücke des beheizbaren Glasfaservlieses zurechtzuschneiden.In a preferred embodiment, up to four regions are arranged on the glass fiber fleece as defined in the preceding paragraph. In particular, in this embodiment, the heatable glass fiber fleece in the form of a rectangle and the areas in the form of a rectangle or a square. This results in a "ladder-like" structure, which makes it possible to cut to size suitable pieces of heated glass fiber fleece.

GlasfaservliesbauteilFiberglass mat component

Die vorliegende Erfindung ist ferner auf ein Glasfaservliesbauteil gerichtet, umfassend das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung und mindestens zwei elektrisch leitfähige Kontaktelemente, die an das beheizbare Glasfaservlies derart angeordnet sind, dass das beheizbare Glasfaservlies mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar ist.The present invention is further directed to a glass fiber fleece component, comprising the heatable glass fiber fleece according to the present invention and at least two electrically conductive contact elements, which are arranged on the heatable glass fiber fleece such that the heatable glass fiber fleece can be acted upon by electrical voltage and / or electric current.

Bezüglich des beheizbaren Glasfaservlieses wird vollumfänglich auf den ersten erfindungsgemäßen Aspekt verwiesen.With regard to the heatable fiberglass mat, reference is made in full to the first aspect of the invention.

Die bevorzugten Abmessungen, inklusive Dicke, die Höchstzugkraft in Längs- und/oder Querrichtung etc. des beheizbaren Glasfaservlieses des ersten erfindungsgemäßen Aspektes ist/sind ebenfalls bevorzugte Abmessungen, inklusive Dicke, Höchstzugkraft in Längs- und/oder Querrichtung etc. des erfindungsgemäßen Glasfaservliesbauteils. Die Messung der Höchstzugkraft wird so durchgeführt, dass die mindestens zwei elektrisch leitfähigen Kontaktelemente die Messung nicht beeinflussen.The preferred dimensions, including thickness, the maximum tensile force in the longitudinal and / or transverse direction etc. of the heatable glass fiber fleece of the first aspect of the invention is / are also preferred dimensions, including thickness, maximum tensile force in the longitudinal and / or transverse direction etc. of the glass fiber fleece component according to the invention. The measurement of the maximum tensile force is performed so that the at least two electrically conductive contact elements do not affect the measurement.

Elektrische KontaktelementeElectrical contact elements

Die Kontaktelemente können insbesondere Kontaktstreifen oder Kontaktbänder darstellen.The contact elements may in particular represent contact strips or contact strips.

Die Kontaktelemente können in einer Ausführungsform als gerade Streifen ausgebildet sein. Allerdings ist die Form der Kontaktelemente auch für weitere Ausführungsformen nicht auf eine solche gerade Konfiguration beschränkt. Die Kontaktelemente können beispielsweise durch Streifen gebildet werden, die in der Hauptausdehnungsrichtung des beheizbaren Glasfaservlieses kurvenförmig verlaufen.The contact elements may be formed in one embodiment as a straight strip. However, the shape of the contact elements for other embodiments is not limited to such a straight configuration. The contact elements can be formed, for example, by strips which run in the main extension direction of the heatable glass fiber fleece curved.

Die Breite der Kontaktelemente ist nicht kritisch. Jedoch sollten die Kontaktelemente derart dimensioniert sein, dass sie eine Beaufschlagung des beheizbaren Glasfaservlieses mit elektrischer Spannung und/oder elektrischem Strom, vorzugsweise über die gesamte Länge und/oder Breite des beheizbaren Glasfaservlieses erlauben. Es ist insbesondere bevorzugt, dass zwei der mindestens zwei elektrisch leitfähigen Kontaktelemente an sich gegenüberliegenden Randbereichen des beheizbaren Glasfaservlieses angeordnet sind.The width of the contact elements is not critical. However, the contact elements should be dimensioned such that they allow exposure of the heatable glass fiber fleece with electrical voltage and / or electric current, preferably over the entire length and / or width of the heatable glass fiber fleece. It is particularly preferred that two of the at least two electrically conductive contact elements are arranged on opposite edge regions of the heatable glass fiber fleece.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, sind vorzugsweise jeweils zwei der mindestens zwei elektrisch leitfähigen Kontaktelemente an sich gegenüberliegenden Randbereichen des/der Bereiche, welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, derart angeordnet, dass jeder der Bereiche mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar ist. Beispielsweise können bei einer 2 x n-Anordnung der Bereiche wie oben ausgeführt, zwei Paare oder n Paare von elektrisch leitfähigen Kontaktelementen derart angeordnet sein, dass alle Bereiche mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar sind. Bei einer 2 x 4-Anordnung der Bereiche, können entsprechend zwei oder vier Paare von elektrisch leitfähigen Kontaktelementen derart angeordnet sein, dass alle acht Bereiche mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar sind. Bei einer 1 x n-Anordnung der Bereiche, wie oben ebenfalls beispielsweise angeführt, kann entsprechend ein Paar oder n Paare von elektrisch leitfähigen Kontaktelementen derart angeordnet sein, dass alle n Bereiche mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar sind. Vorzugsweise ist bei einer 1 x n-Anordnung der Bereiche ein Paar von elektrisch leitfähigen Kontaktelementen derart angeordnet, dass alle n Bereiche mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar sindIf the heatable glass fiber fleece according to the present invention is only partially coated with the coating which comprises at least one conductivity additive and at least one binder, preferably two of the at least two electrically conductive contact elements are on opposite edge regions of the region (s) which is / are coated with the coating, which comprises at least one conductivity additive and at least one binder, is arranged such that each of the areas with electric voltage and / or electric current can be acted upon. For example, in a 2 × n arrangement of the regions as stated above, two pairs or n pairs of electrically conductive contact elements can be arranged such that all regions can be subjected to electrical voltage and / or electrical current. In the case of a 2 × 4 arrangement of the regions, correspondingly two or four pairs of electrically conductive contact elements can be arranged such that all eight regions can be subjected to electrical voltage and / or electrical current. In the case of a 1 × n arrangement of the regions, as also stated above, for example, a pair or n pairs of electrically conductive contact elements can accordingly be arranged such that all n regions can be acted upon by electrical voltage and / or electric current. Preferably, in the case of a 1 × n arrangement of the regions, a pair of electrically conductive contact elements is arranged such that all n regions can be subjected to electrical voltage and / or electrical current

Wie oben ausgeführt, werden der Einfachheit halber die Begriffe „Bereich“, „Bereiche“ oder „Bereich(e)“ für den einen oder die mehreren voneinander getrennte Bereich(e), welche(r) mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist/sind, verwendet.As noted above, for simplicity, the terms "region," "regions," or "region (s)" will be used for the one or more separate region (s) containing the coating, the at least one conductivity additive, and at least one binder comprises coated is / are used.

Vorzugsweise umfasst jedes elektrisch leitfähige Kontaktelement einen elektrisch leitenden Metallstreifen, insbesondere aus Kupfer, wobei mehr bevorzugt jedes dieser elektrisch leitenden Kontaktelemente eine Klebeschicht aufweist, die sich auf der dem beheizbaren Glasfaservlies abgewandten Seite der elektrisch leitfähigen Kontaktelemente befindet, die Klebeschicht ist insbesondere mit einer Schutzfolie bedeckt. Preferably, each electrically conductive contact element comprises an electrically conductive metal strip, in particular made of copper, wherein more preferably each of these electrically conductive contact elements has an adhesive layer which is located on the side facing away from the heatable glass fiber fleece side of the electrically conductive contact elements, the adhesive layer is covered in particular with a protective film ,

Die Dicke jedes elektrisch leitfähigen Kontaktelements beträgt vorzugsweise maximal 120 µm, vorzugsweise maximal 110 µm, mehr bevorzugt maximal 90 µm.The thickness of each electrically conductive contact element is preferably at most 120 μm, preferably at most 110 μm, more preferably at most 90 μm.

Vorzugsweise steht jedes der elektrisch leitfähigen Kontaktelemente über eine Kante des beheizbaren Glasfaservlieses um mindestens 10 cm, mehr bevorzugt um mindestens 25 cm, noch mehr bevorzugt mindestens 40 cm über. Vorzugsweise stehen die elektrisch leitfähigen Kontaktelemente über dieselbe Kante des beheizbaren Glasfaservlieses über, insbesondere falls das beheizbare Glasfaservlies die Form eines Parallelogramms bzw. Rechtecks aufweist. In dieser Ausführungsform ist es beispielsweise möglich, die Anschlussklemme auf Höhe der Fußleisten anzubringen und diese somit in der Fußleiste versenken.Preferably, each of the electrically conductive contact elements projects beyond an edge of the heatable glass fiber fleece by at least 10 cm, more preferably by at least 25 cm, even more preferably by at least 40 cm. Preferably, the electrically conductive contact elements over the same edge of the heated glass fiber fleece over, in particular if the heatable glass fiber fleece has the shape of a parallelogram or rectangle. In this embodiment, it is possible, for example, to attach the terminal at the height of the baseboards and thus sink them in the baseboard.

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung nur teilweise mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, befinden sich die elektrischen Kontaktelemente vorzugsweise auch auf unbeschichteten Teilen des beheizbaren Glasfaservlieses, beispielsweise zwischen zwei der Bereiche und/oder zwischen dem Ende eines Bereiches und dem Ende des Glasfaservlieses, falls das Glasfaservlies nicht bis zu dem entsprechenden Ende mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist. Jedes der elektrisch leitfähigen Kontaktelemente kann ebenfalls über eine Kante des beheizbaren Glasfaservlieses wie im vorangegangenen Absatz definiert überstehen.If the heatable glass fiber fleece according to the present invention is only partially coated with the coating comprising at least one conductivity additive and at least one binder, the electrical contact elements are preferably also on uncoated parts of the heatable glass fiber fleece, for example between two of the regions and / or between the end of a region and the end of the glass fiber fleece, if the glass fiber fleece is not coated to the corresponding end with the coating comprising at least one conductivity additive and at least one binder. Each of the electrically conductive contact elements can likewise project beyond an edge of the heatable glass fiber fleece as defined in the preceding paragraph.

Jedes elektrisch leitfähige Kontaktelement weist vorzugsweise eine Breite von 1,4 bis 4,4 cm, mehr bevorzugt von 1,9 bis 3,9 cm, noch mehr bevorzugt von 2,4 bis 3,4 cm auf.Each electrically conductive contact element preferably has a width of 1.4 to 4.4 cm, more preferably 1.9 to 3.9 cm, even more preferably 2.4 to 3.4 cm.

Vorzugsweise sind die mindestens zwei elektrisch leitfähigen Kontaktelemente parallel angeordnet und der Abstand zwischen ihren Innenkanten beträgt mindestens 30 cm, vorzugsweise mindestens 40 cm, mehr bevorzugt mindestens 50 cm.Preferably, the at least two electrically conductive contact elements are arranged in parallel and the distance between their inner edges is at least 30 cm, preferably at least 40 cm, more preferably at least 50 cm.

Vorzugsweise sind die mindestens zwei elektrisch leitfähigen Kontaktelemente parallel angeordnet und der Abstand zwischen ihren Innenkanten beträgt nicht mehr als 3,00 m, vorzugsweise nicht mehr als 2,00 m und am meisten bevorzugt nicht mehr als 1,00 m.Preferably, the at least two electrically conductive contact elements are arranged in parallel and the distance between their inner edges is not more than 3.00 m, preferably not more than 2.00 m, and most preferably not more than 1.00 m.

Vorzugsweise ist jedes elektrisch leitfähige Kontaktelement 0,0 bis 10,0 cm (wie 0,1 bis 10,0 cm), mehr bevorzugt 0,0 bis 8,0 cm (wie 0,1 bis 8,0 cm), noch mehr bevorzugt 0,0 bis 6,0 cm (wie 0,1 bis 6,0 cm) von dem Rand des beheizbaren Glasfaservlieses entfernt angeordnet. In dieser Variante ist/sind die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, bzw. die Bereiche derart angeordnet, dass eine Beaufschlagung mit elektrischer Spannung und/oder elektrischem Strom möglich ist.Preferably, each electrically conductive contact element is 0.0 to 10.0 cm (such as 0.1 to 10.0 cm), more preferably 0.0 to 8.0 cm (such as 0.1 to 8.0 cm), even more preferably 0.0 to 6.0 cm (as 0.1 to 6.0 cm) away from the edge of the heated glass fiber fleece arranged. In this variant, the coating, which comprises at least one conductivity additive and at least one binder, or the regions is / are arranged in such a way that an application of electrical voltage and / or electrical current is possible.

Das erfindungsgemäße Glasfaservliesbauteil weist vorzugsweise eine spezifische Leistung von 20 bis 1000 W/m2 auf, vorzugsweise 50 bis 800 W/m2, mehr bevorzugt 100 bis 600 W/m2 und am meisten bevorzugt 200 bis 400 W/m2 auf. Die Leistung wird mit einem Leistungsmessgerät in Abhängigkeit der angelegten Spannung gemessen. Hierzu wird üblicherweise ein spannungsstabilisiertes Netzteil, welches 24 V Wechselspannung zur Verfügung stellt, verwendet.The glass fiber nonwoven component according to the invention preferably has a specific power of 20 to 1000 W / m 2 , preferably 50 to 800 W / m 2 , more preferably 100 to 600 W / m 2 and most preferably 200 to 400 W / m 2 . The power is measured with a power meter depending on the applied voltage. For this purpose, usually a voltage-stabilized power supply, which provides 24 V AC voltage is used.

Die Kontaktelemente können auf jegliche bekannte Weise auf das beheizbare Glasfaservlies angebracht werden, z.B. mittels Aufdrucken, Einlegen, Einlaminieren, Aufkleben, thermischen Spritzen (wie Lichtbogenspritzen) oder Plasmaspritzen. Für eine einfache Handhabung und Herstellung des Glasfaservliesbauteils ist jedoch ein Aufkleben der Kontaktelemente auf das beheizbare Glasfaservlies bevorzugt. Für diese Ausführungsform weisen die Kontaktelemente vorzugsweise eine Klebschicht auf.The contact elements may be attached to the heatable fiberglass mat in any known manner, e.g. by means of printing, insertion, lamination, gluing, thermal spraying (such as arc spraying) or plasma spraying. For easy handling and production of the glass fiber fleece component, however, adhesive bonding of the contact elements to the heatable glass fiber fleece is preferred. For this embodiment, the contact elements preferably have an adhesive layer.

Die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, dringt in das Glasfaservlies ein bzw. durchdringt dieses, wie bereits oben ausgeführt. Daher können sich die Kontaktelemente auf beliebigen Seiten des beheizbaren Glasfaservlieses befinden, unabhängig davon, ob die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf beiden Seiten des Glasfaservlieses oder nur auf einer Seite des beheizbaren Glasfaservlieses aufgebracht ist. Üblicherweise befinden sich alle Kontaktelemente auf einer Seite des beheizbaren Glasfaservlieses. Dadurch wird normalerweise die Ver- und Bearbeitung erleichtert.The coating, which comprises at least one conductivity additive and at least one binder, penetrates or penetrates into the glass fiber fleece, as already explained above. Therefore, the contact elements can be located on any sides of the heated glass fiber fleece, regardless of whether the coating comprising at least one conductivity additive and at least one binder is applied on both sides of the glass fiber fleece or only on one side of the heatable glass fiber fleece. Usually, all contact elements are located on one side of the heated glass fiber fleece. This usually facilitates editing and editing.

In einer Variante ist die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, nur auf einer Seite des beheizbaren Glasfaservlieses aufgebracht. In dieser Variante können sich die elektrischen Kontaktelemente auf derselben Seite wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht sein, oder auf der gegenüberliegenden Seite. Falls, in dieser Variante, die elektrischen Kontaktelemente auf der gegenüberliegenden Seite der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht sind, sind die oben angeführten weiteren Schichten üblicherweise auf der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, aufgebracht. Ferner wäre es möglich diese weiteren Schichten vor oder nach Anbringung der elektrischen Kontaktelemente aufzubringen. Falls in dieser Variante die elektrischen Kontaktelemente auf derselben Seite wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht sind, werden die oben angeführten weiteren Schichten üblicherweise nach Anbringung der der elektrischen Kontaktelemente aufgebracht. Andernfalls ist u.U. eine elektrisch leitende Verbindung zwischen den Kontaktelementen und der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, nicht oder nur eingeschränkt möglich. In einer bevorzugten Form dieser Variante sind die elektrischen Kontaktelemente auf derselben Seite wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht, und eine Vliesschicht ist auf derselben Seite wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht, wobei diese Vliesschicht normalerweise kein Leitfähigkeitsadditiv enthält. D.h. die elektrischen Kontaktelemente befinden sich zwischen dem erfindungsgemäßen beheizbaren Glasfaservlies und dieser Vliesschicht. Eine derartige Vliesschicht weist, wie oben ausgeführt, vorzugsweise ein Flächengewicht von nicht mehr als 100 g/m2, mehr bevorzugt nicht mehr als 60 g/m2 und noch mehr bevorzugt nicht mehr als 30 g/m2 auf. Diese Vliesschicht, falls vorhanden, kann ein Kunststoff- und/oder ein Glasfaservlies aufweisen bzw. daraus bestehen, beispielsweise ein Glasfaservlies aufweisen bzw. daraus bestehen. Bei dieser Variante wäre es möglich, dass die elektrischen Kontaktelemente durchgängig auf dieser Vliesschicht angebracht sind, jedoch das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung nur abschnittsweise, üblicherweise in regelmäßigen Abständen, darauf angebracht ist. In dieser Variante wäre es möglich, ein oder mehrere Stücke mit der benötigten Größe abzuschneiden.In one variant, the coating, which comprises at least one conductivity additive and at least one binder, is applied only on one side of the heatable glass fiber fleece. In this variant, the electrical contact elements on the same side as the coating, which comprises at least one conductivity additive and at least one binder may be attached, or on the opposite side. If, in this variant, the electrical contact elements on the opposite side of the coating, which comprises at least one conductivity additive and at least one binder, are attached, the above-mentioned further layers are usually on the coating, which comprises at least one conductivity additive and at least one binder, applied. Furthermore, it would be possible to apply these further layers before or after attachment of the electrical contact elements. If, in this variant, the electrical contact elements are arranged on the same side as the coating which comprises at least one conductivity additive and at least one binder, the above-mentioned further layers are usually applied after attachment of the electrical contact elements. Otherwise, an electrically conductive connection between the contact elements and the coating, which comprises at least one conductivity additive and at least one binder, may or may not be possible to a limited extent. In a preferred form of this variant, the electrical contact elements are disposed on the same side as the coating comprising at least one conductivity additive and at least one binder, and a nonwoven layer is on the same side as the coating comprising at least one conductivity additive and at least one binder. attached, this nonwoven layer usually does not contain a conductivity additive. That is to say the electrical contact elements are located between the heatable glass fiber nonwoven according to the invention and this nonwoven layer. Such a nonwoven layer, as stated above, preferably has a basis weight of not more than 100 g / m 2 , more preferably not more than 60 g / m 2, and even more preferably not more than 30 g / m 2 . This nonwoven layer, if present, may comprise or consist of a plastic and / or a glass fiber fleece, for example comprising or consisting of a glass fiber fleece. In this variant, it would be possible that the electrical contact elements are continuously mounted on this nonwoven layer, but the heatable fiberglass mat according to the present invention only partially, usually at regular intervals, is mounted on it. In this variant, it would be possible to cut one or more pieces of the required size.

In einer bevorzugten Ausführungsform

  • - weist das beheizbare Glasfaservlies (und somit das Glasfaservliesbauteil) die Form eines Rechtecks auf, wobei die erste Kante zwischen 66,0 und 100 cm misst und die zweite Kante zwischen 120 und 160 cm misst, vorzugsweise die erste Kante zwischen 76,0 und 96,0 cm misst und die zweite Kante zwischen 130 und 150 cm misst,
  • - weisen in Draufsicht auf eine Fläche des beheizbaren Glasfaservlieses, vorzugsweise mindestens 95,0%, mehr bevorzugt mindestens 97,5% und am meisten bevorzugt 100% der betrachteten Fläche mindestens auf der dem Betrachter zugewandten oder abgewandten Seite des beheizbaren Glasfaservlieses eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf,
  • - ist jedes elektrisch leitfähige Kontaktelement 0,0 bis 6,0 cm (wie 0,1 bis 6,0 cm) von dem Rand des beheizbaren Glasfaservlieses entfernt und parallel zu der zweiten Kante des beheizbaren Glasfaservlieses angeordnet, und
  • - steht jedes der elektrisch leitfähigen Kontaktelemente über dieselbe Kante des beheizbaren Glasfaservlieses um mindestens 10 cm, bevorzugt um mindestens 25 cm, mehr bevorzugt um mindestens 40 cm über.
In a preferred embodiment
  • the heated glass fiber fleece (and thus the glass fiber fleece component) has the shape of a rectangle, the first edge measuring between 66.0 and 100 cm and the second edge measuring between 120 and 160 cm, preferably the first edge between 76.0 and 96 Measures 0 cm and measures the second edge between 130 and 150 cm,
  • have in a plan view of a surface of the heatable glass fiber fleece, preferably at least 95.0%, more preferably at least 97.5% and most preferably 100% of the surface considered at least on the side facing the viewer or facing away from the heated glass fiber fleece a coating, the at least one conductivity additive and at least one binder comprises,
  • - Each electrically conductive contact element 0.0 to 6.0 cm (such as 0.1 to 6.0 cm) from the edge of the heated glass fiber fleece and arranged parallel to the second edge of the heated glass fiber fleece, and
  • each of the electrically conductive contact elements projects beyond the same edge of the heatable glass fiber fleece by at least 10 cm, preferably by at least 25 cm, more preferably by at least 40 cm.

In einer weiteren, bevorzugten Ausführungsform

  • - weist das beheizbare Glasfaservlies (und somit das Glasfaservliesbauteil) die Form eines Rechtecks auf, wobei die Länge der ersten Kante 50,0 bis 100 cm und die Länge der zweiten Kante 2,00 bis 6,00 m beträgt, vorzugsweise die Länge der ersten Kante 50,0 bis 100 cm und die Länge der zweiten Kante 3,00 bis 6,00 m beträgt,
  • - weist das beheizbare Glasfaservlies zwei bis acht, vorzugsweise zwei bis vier, voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, auf, wobei diese Bereiche in Form eines Quadrats oder Rechtecks, vorzugsweise in Form eines Rechtecks ausgeführt sind,
  • - erstreckt sich jeder dieser Bereiche von der zweiten Kante des beheizbaren Glasfaservlieses zu der Kante die zu dieser zweiten Kante parallel ist, oder ist maximal 10,0 cm, bevorzugt maximal 8,00 cm, noch mehr bevorzugt maximal 6,0 cm (wie 0,1 cm) jeweils von der zweiten Kante des beheizbaren Glasfaservlieses und der Kante die zu dieser zweiten Kante parallel ist, entfernt und parallel zueinander angeordnet,
  • - weist jeder dieser Bereiche eine Fläche von 0,25 bis 2,00 m2 auf,
  • - ist jedes elektrisch leitfähige Kontaktelement 0,0 bis 10,0 cm (wie 0,1 bis 10,0 cm), mehr bevorzugt 0,0 bis 8,0 cm (wie 0,1 bis 8,0 cm), noch mehr bevorzugt 0,0 bis 6,0 cm (wie 0,1 bis 6,0 cm) von dem Rand des beheizbaren Glasfaservlieses entfernt und parallel zu der zweiten Kante des beheizbaren Glasfaservlieses angeordnet,
  • - ist jedes der elektrisch leitfähigen Kontaktelemente auf derselben Seite des beheizbaren Glasfaservlieses wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, angebracht, und jedes der elektrisch leitfähigen Kontaktelemente steht über dieselbe Kante des beheizbaren Glasfaservlieses um mindestens 10 cm, bevorzugt um mindestens 25 cm, mehr bevorzugt mindestens 40 cm über,
  • - beträgt der Abstand zwischen zwei Bereichen, mindestens 10,0 cm, bevorzugt mindestens 30,0 cm und am meisten bevorzugt mindestens 50,0 cm, und
  • - weist das Glasfaservliesbauteil optional eine Vliesschicht auf, die auf derselben Seite wie die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und die elektrisch leitfähigen Kontaktelemente angebracht ist, wobei diese Vliesschicht normalerweise kein Leitfähigkeitsadditiv enthält und/oder ein Flächengewicht von nicht mehr als 100 g/m2, bevorzugt nicht mehr als 60 g/m2 und mehr bevorzugt nicht mehr als 30 g/m2 aufweist. Diese Vliesschicht, falls vorhanden, kann ein Kunststoff- und/oder ein Glasfaservlies aufweisen bzw. daraus bestehen, beispielsweise ein Glasfaservlies aufweisen bzw. daraus bestehen.
In a further preferred embodiment
  • the heatable glass fiber fleece (and thus the glass fiber fleece component) has the shape of a rectangle, the length of the first edge being 50.0 to 100 cm and the length of the second edge being 2.00 to 6.00 m, preferably the length of the first Edge is 50.0 to 100 cm and the length of the second edge is 3.00 to 6.00 m,
  • the heatable glass fiber fleece has two to eight, preferably two to four, mutually separate regions which are coated with the coating which comprises at least one conductivity additive and at least one binder, these regions being in the form of a square or rectangle, preferably in Shape of a rectangle are executed,
  • each of these areas extends from the second edge of the heatable fiberglass mat to the edge parallel to this second edge, or is at most 10.0 cm, preferably at most 8.00 cm, more preferably at most 6.0 cm (like 0 , 1 cm) each of the second edge of the heated glass fiber fleece and the edge which is parallel to this second edge, removed and arranged parallel to each other,
  • each of these areas has an area of 0.25 to 2.00 m 2 ,
  • Each electrically conductive contact element is 0.0 to 10.0 cm (such as 0.1 to 10.0 cm), more preferably 0.0 to 8.0 cm (such as 0.1 to 8.0 cm), even more preferably 0.0 to 6.0 cm (such as 0.1 to 6.0 cm) away from the edge of the heatable glass fiber fleece and arranged parallel to the second edge of the heatable glass fiber fleece,
  • - For example, each of the electrically conductive contact elements on the same side of the heated fiberglass mat as the coating comprising at least one conductivity additive and at least one binder is attached, and each of the electrically conductive contact elements is at least 10 cm, preferably at least 25, over the same edge of the heatable glass fiber mat cm, more preferably at least 40 cm above,
  • the distance between two regions is at least 10.0 cm, preferably at least 30.0 cm and most preferably at least 50.0 cm, and
  • the nonwoven glass fiber member optionally comprises a nonwoven layer attached on the same side as the coating comprising at least one conductivity additive and at least one binder and the electrically conductive contact elements, said nonwoven layer normally containing no conductivity additive and / or no more basis weight than 100 g / m 2 , preferably not more than 60 g / m 2 and more preferably not more than 30 g / m 2 . This nonwoven layer, if present, may comprise or consist of a plastic and / or a glass fiber fleece, for example comprising or consisting of a glass fiber fleece.

Im Folgenden werden alle Ausführungsformen des erfindungsgemäßen beheizbaren Glasfaservlieses und des erfindungsgemäßen Glasfaservliesbauteils beschrieben, es sei denn, es wird ausdrücklich auf etwas anderes verwiesen.In the following, all embodiments of the heatable glass fiber fleece according to the invention and of the glass fiber fleece component according to the invention are described, unless it is expressly referred to something else.

Das erfindungsgemäße beheizbare Glasfaservlies und das erfindungsgemäße Glasfaservliesbauteil sind vorzugsweise durch Beaufschlagung mit einer Schutzkleinspannung betreibbar. Üblicherweise wird hierzu die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, mit einer Schutzkleinspannung beaufschlagt. Geeignete Spannungsquellen und Steuerungselemente hierfür werden unten, unter anderem im dritten erfindungsgemäßen Aspekt (Kit zum Herstellen eines Glasfaservliesbauteils), beschrieben.The heatable glass fiber fleece according to the invention and the glass fiber fleece component according to the invention are preferably operable by application of a protective extra-low voltage. Usually, for this purpose, the coating, which comprises at least one conductivity additive and at least one binder, subjected to a protective extra-low voltage. Suitable voltage sources and control elements therefor are described below, inter alia in the third aspect of the invention (kit for producing a fiberglass nonwoven component).

Das beheizbare Glasfaservlies und das erfindungsgemäße Glasfaservliesbauteil können dazu verwendet werden, Temperaturen zu erzeugen, die üblicherweise im Inneren eines Hauses (wie eines Wohnhauses) vorgefunden werden, beispielweise eine Temperatur im Bereich von 15 bis 30°C. Dabei kann die maximale Oberflächentemperatur des beheizbaren Glasfaservlieses/Glasfaservliesbauteils bis zu 50°C betragen, insbesondere wenn sich das beheizbare Glasfaservlies/Glasfaservliesbauteil am Boden und/oder in einem Bereich einer Wand befindet, der für Personen erreichbar ist (typischerweise in einem Bereich der Wand, der einen Abstand vom Boden von weniger als 2,5 m aufweist). Wenn das beheizbare Glasfaservlies/Glasfaservliesbauteil sich in einem Bereich einer Wand befindet, der für Personen nicht erreichbar ist (typischerweise in einem Bereich der Wand, der mindestens einen Abstand von 2,5 m vom Boden aufweist und/oder an einer Decke, z.B. an einer entsprechenden Schräge eines Raumes), kann die maximale Oberflächentemperatur des beheizbaren Glasfaservlieses/Glasfaservliesbauteils bis zu 120°C (wie bis zu 110°C, bis zu 100°C, bis zu 90°C, bis zu 80°C oder bis zu 70°C) betragen. In einer Ausführungsform ist auch vorgesehen, das erfindungsgemäße beheizbare Glasfaservlies/Glasfaservliesbauteil dazu zu verwenden, höhere als übliche Raumtemperaturen zu erreichen, beispielsweise Temperaturen, die in einer Sauna vorgefunden werden (z.B. 80°C bis 120°C, wie 85°C bis 110°C).The heatable glass fiber nonwoven fabric and the nonwoven glass fiber member of the invention can be used to produce temperatures commonly found inside a home (such as a home), such as a temperature in the range of 15 to 30 ° C. The maximum surface temperature of the heatable glass fiber fleece / nonwoven component may be up to 50 ° C., in particular if the heatable glass fiber fleece / glass fiber fleece component is located on the floor and / or in a region of a wall accessible to persons (typically in a region of the wall, which has a distance from the ground of less than 2.5 m). When the heatable glass fiber nonwoven fabric member is in an area of a wall which is not accessible to persons (typically in a region of the wall at least 2.5m from the floor and / or on a ceiling, eg at a wall) corresponding slant of a room), the maximum surface temperature of the heatable glass fiber fleece / fiberglass nonwoven component up to 120 ° C (as up to 110 ° C, up to 100 ° C, up to 90 ° C, up to 80 ° C or up to 70 ° C) amount. In one embodiment, it is also envisaged to use the heatable glass fiber nonwoven / glass fiber nonwoven component according to the invention to achieve higher than usual room temperatures, for example temperatures that are found in a sauna (eg 80 ° C to 120 ° C, such as 85 ° C to 110 ° C).

Bei der Beheizung von Gegenständen ist die Oberflächentemperatur entsprechend zu wählen. Falls Oberflächen beheizt werden sollen, mit denen Personen in Kontakt kommen bzw. in Kontakt kommen können, wie beispielsweise Griffe von Werkzeugen, Rohre in einer Höhe von weniger als 2,5 m etc., sollte die Oberflächentemperatur des beheizbaren Glasfaservlieses/Glasfaservliesbauteils nicht mehr als 50°C, vorzugsweise nicht mehr als 42°C betragen. Falls ein Kontakt mit Personen normalerweise ausgeschlossen ist, kann die maximale Oberflächentemperatur des beheizbaren Glasfaservlieses/Glasfaservliesbauteils bis zu 120°C (wie bis zu 110°C, bis zu 100°C, bis zu 90°C, bis zu 80°C oder bis zu 70°C) betragen.When heating objects, the surface temperature should be selected accordingly. If surfaces are to be heated with which persons come into contact or come into contact, such as tool handles, pipes less than 2.5 m in height, etc., the surface temperature of the heatable glass fiber nonwoven component should not exceed 50 ° C, preferably not more than 42 ° C. If contact with people is normally excluded, the maximum surface temperature of the Heated Fiberglass Fleece / Fiberglass Nonwoven component may be up to 120 ° C (up to 110 ° C, up to 100 ° C, up to 90 ° C, up to 80 ° C or until to 70 ° C).

Das erfindungsgemäße beheizbare Glasfaservlies/Glasfaservliesbauteil ist insbesondere dazu geeignet, einen Raum zu beheizen, wobei es nicht darauf ankommt, wie der Raum ausgestattet ist oder wo er sich befindet. Z.B. kann der Raum ein Teil eines Hauses oder Gebäudes (d.h. immobil) sein; der Begriff „Raum“ schließt aber auch mobile Varianten (wie Container) ein. Der Begriff „Wand“ schließt erfindungsgemäß jegliche Begrenzung eines Raumes ein, wobei Fenster ausgeschlossen sind. Der Begriff „Wand“ umfasst insbesondere neben den vertikalen Wänden (tragend oder nicht tragend) auch eventuell vorhandene Trennwände, eventuell vorhandene Schrägen und Decken des Raumes (einschließlich Abhängdecke). Der Begriff „Boden“ schließt erfindungsgemäß jede begehbare Fläche, auch außerhalb von Räumen (beispielsweise Straßen, Geh- und Radwege, Parkplätze etc.), ein, wobei transparente Böden ausgeschlossen sind. Der Begriff „Boden“ umfasst insbesondere neben horizontalen Böden auch eventuell vorhandene Schrägen, wie beispielsweise Auffahrten, Rollstuhlrampen, etc. Der Begriff „Gegenstand“ schließt erfindungsgemäß jeden Gegenstand ein, der mittels des erfindungsgemäßen Glasfaservlieses beheizbar ist, beispielsweise Rohre, Werkzeuge, Sitzgelegenheiten, etc. Insbesondere schließt der Begriff „Gegenstand“ keinen „Raum“, „Wand“ oder „Decke“ ein, wie vorstehend definiert.The heatable glass fiber nonwoven / glass fiber nonwoven component according to the invention is particularly suitable for heating a room, it does not matter how the room is equipped or where it is located. For example, the room may be part of a house or building (ie immobile); The term "space" also includes mobile variants (such as containers). The term "wall" according to the invention includes any limitation of a room, with windows are excluded. The term "wall" includes, in addition to the vertical walls (load-bearing or non-load-bearing), any existing partition walls, any existing slants and ceilings of the room (including ceiling). The term "floor" includes according to the invention any walk-in area, also outside of rooms (for example, roads, pedestrian and cycle paths, parking lots, etc.), with transparent floors excluded. The term "floor" includes in addition to horizontal floors also any existing slopes, such as driveways, wheelchair ramps, etc. The term "object" includes according to the invention any object that is heatable by means of the glass fiber fleece according to the invention, for example pipes, Tools, seating, etc. In particular, the term "article" does not include a "room,""wall," or "ceiling," as defined above.

Das erfindungsgemäße beheizbare Glasfaservlies/Glasfaservliesbauteil weist den Vorteil auf, dass es zum Beheizen von Räumen verwendet werden kann, in denen die Raumluft möglichst wenig bewegt werden soll (z.B. Patientenzimmer oder Operationssäle von Krankenhäusern, Zimmer von Allergikern, etc.). Ein weiterer Vorteil besteht darin, dass das erfindungsgemäße beheizbare Glasfaservlies/Glasfaservliesbauteil direkt an einer Wand angebracht ist und bei Betrieb die Temperatur dieser Wand über der Raumtemperatur liegt. Folglich wird Wasser, das sich an (oder in) dieser Wand befindet, eher verdunsten (im Gegensatz zu herkömmlichen Systemen, bei denen Wasser eher an den Wänden kondensiert), was insgesamt einer Schimmelbildung vorbeugt. Zudem weist das erfindungsgemäße beheizbare Glasfaservlieses/Glasfaservliesbauteil eine höhere Flexibilität als viele andere Boden-, Wand- und/oder Deckenkonstruktionen auf (beispielsweise Baustoffplatten, Betonwände, gemauerte Wände etc.), in denen Haarrisse entstehen können. Derartige Haarrisse können die Heizleistung direkt darauf angebrachter Heizschichten verringern bzw. im schlimmsten Fall diese Schichten unbrauchbar machen, was bei dem erfindungsgemäßen beheizbaren Glasfaservlies/Glasfaservliesbauteil vermieden werden kann. Falls ein Gegenstand beheizt wird, beispielsweise ein Rohr, welches mit dem erfindungsgemäßen Glasfaservlies umwickelt ist, kann das erfindungsgemäße Glasfaservlies thermische Ausdehnungen aufgrund der bewirkten Heizung normalerweise ebenfalls besser kompensieren als beheizbare Beschichtungen. Ein weiterer Vorteil liegt darin, dass mittels des erfindungsgemäßen beheizbaren Glasfaservlieses/Glasfaservliesbauteils elektromagnetische Strahlung abschirmbar ist. Um diese Abschirmung zu erreichen, wird das beheizbare Glasfaservlies/Glasfaservliesbauteil nicht mit elektrischen Strom oder elektrischer Spannung beaufschlagt, sondern auf Erdung gelegt.The heatable glass fiber nonwoven fabric / fiberglass nonwoven component according to the invention has the advantage that it can be used for heating rooms in which the room air is to be moved as little as possible (for example, patient rooms or operating theaters of hospitals, rooms of allergy sufferers, etc.). Another advantage is that the inventive heated glass fiber fleece / glass fiber fleece component is mounted directly on a wall and in operation, the temperature of this wall is above the room temperature. As a result, water that is on (or in) this wall tends to evaporate (unlike conventional systems where water tends to condense on the walls), which generally prevents mold growth. In addition, the heatable glass fiber nonwoven fabric / fiberglass component according to the invention has a higher flexibility than many other floor, wall and / or ceiling constructions (for example building boards, concrete walls, masonry walls, etc.) in which hairline cracks can occur. Such hairline cracks can reduce the heat output of heating layers applied directly thereto or, in the worst case, make these layers unusable, which can be avoided in the case of the inventive heatable glass fiber fleece / glass fiber fleece component. If an object is heated, for example a tube which is wrapped with the glass fiber fleece according to the invention, the glass fiber fleece according to the invention can normally compensate thermal expansions better than heated coatings due to the heating effect. A further advantage resides in the fact that electromagnetic radiation can be shielded by means of the heatable glass fiber nonwoven / glass fiber nonwoven component according to the invention. In order to achieve this shielding, the heatable glass fiber fleece / fiberglass nonwoven component is not subjected to electrical current or electrical voltage, but is grounded.

Kit zum Herstellen eines GlasfaservliesbauteilsKit for producing a glass fiber fleece component

Bezüglich der Ausgestaltung der Komponenten des erfindungsgemäßen Kits wird vollinhaltlich auf die vorstehenden Ausführungen bezüglich des ersten (beheizbares Glasfaservlies) und zweiten (Glasfaservliesbauteil) erfindungsgemäßen Aspekt verwiesen.With regard to the configuration of the components of the kit according to the invention, reference is made in full to the above statements regarding the first (heatable glass fiber fleece) and second (glass fiber fleece component) aspect of the invention.

Der optional in dem Kit zum Herstellen eines Glasfaservliesbauteils gemäß des dritten erfindungsgemäßen Aspektes enthaltene Glasgewebekleber kann ein üblicher Glasgewebekleber sein. Vorzugsweise ist der Gewebekleber ein lösemittelfreier Dispersionskleber, beispielsweise eine Polyvinylacetatdispersion, gefüllt mit Calciumcarbonat.The glass cloth adhesive optionally contained in the kit for producing a glass fiber nonwoven member according to the third aspect of the present invention may be a common glass cloth adhesive. The tissue adhesive is preferably a solvent-free dispersion adhesive, for example a polyvinyl acetate dispersion filled with calcium carbonate.

Vorzugsweise umfasst das erfindungsgemäße Kit ferner

  • (4) ein Steuerungselement, das eine Spannungsquelle, vorzugsweise eine Spannungsquelle für Schutzkleinspannung, und eine Steuerungsvorrichtung zum Steuern eines beheizbaren Glasfaservlieses umfasst, und
  • (5) zwei elektrische Leitungen, wobei die erste elektrische Leitung mit einem der Pole der Spannungsquelle verbindbar oder verbunden ist und die zweite elektrische Leitung mit dem anderen Pol der Spannungsquelle verbindbar oder verbunden ist und die erste elektrische Leitung mit einem der mindestens zwei elektrisch leitfähigen Kontaktelementen elektrisch leitend verbindbar ist und die zweite elektrische Leitung mit einem der anderen der mindestens zwei elektrisch leitfähigen Kontaktelementen elektrisch leitend verbindbar ist.
Preferably, the kit of the invention further comprises
  • (4) a control element comprising a voltage source, preferably a voltage extra low voltage power supply, and a control device for controlling a heatable glass fiber nonwoven, and
  • (5) two electrical lines, wherein the first electrical line is connectable or connected to one of the poles of the voltage source and the second electrical line is connectable or connected to the other pole of the voltage source and the first electrical line to one of the at least two electrically conductive contact elements electrically conductively connected and the second electrical line with one of the other of the at least two electrically conductive contact elements is electrically conductively connected.

Steuerungselementcontrol element

Das Steuerungselement umfasst eine Spannungsquelle (zur Bereitstellung von elektrischer Spannung und/oder elektrischem Strom) und eine Steuerungsvorrichtung zum Steuern des beheizbaren Glasfaserv lieses/Glasfaservliesbauteils.The control element comprises a voltage source (for providing electrical voltage and / or electrical current) and a control device for controlling the heatable Glasfaserv read / glass fiber fleece component.

Der Begriff „Spannungsquelle“ soll erfindungsgemäß eine jegliche elektrische Energiequelle umfassen, die geeignet ist, eine elektrische Spannung und/oder einen elektrischen Strom bereitzustellen. In einer Ausführungsform ist die Spannungsquelle ein Netzteil, d.h. ein Gerät oder eine Baugruppe, das/die an das Hausstromnetz (typischerweise 230 V AC ± 10%, 50/60 Hz) angeschlossen werden kann und andere Geräte oder Baugruppen, die andere Spannungen und/oder Ströme benötigen, als vom Hausstromnetz bereitgestellt wird, mit Energie versorgt. Das Netzteil kann ein Schalt- oder Trafonetzteil sein. In einer Ausführungsform stellt die Spannungsquelle eine Wechselspannung (insbesondere im Schutzkleinspannungsbereich) bereit oder ist derart konfiguriert und ausgestaltet, eine Wechselspannung (insbesondere im Schutzkleinspannungsbereich) bereitzustellen. In einer alternativen Ausführungsform stellt die Spannungsquelle eine Gleichspannung (insbesondere im Schutzkleinspannungsbereich) bereit oder ist derart konfiguriert und ausgestaltet, eine Gleichspannung (insbesondere im Schutzkleinspannungsbereich) bereitzustellen.The term "voltage source" is intended according to the invention to include any electrical energy source which is suitable to provide an electrical voltage and / or an electric current. In one embodiment, the voltage source is a power supply, i. a device or assembly that can be connected to the household power supply (typically 230 V AC ± 10%, 50/60 Hz) and other devices or assemblies that require different voltages and / or currents than those supplied by the household power network, energized. The power supply can be a switching or transformer power supply. In one embodiment, the voltage source provides an AC voltage (in particular in the safety extra-low voltage range) or is configured and configured to provide an AC voltage (in particular in the protective extra-low voltage range). In an alternative embodiment, the voltage source provides a DC voltage (in particular in the protective extra-low voltage range) or is configured and configured to provide a DC voltage (in particular in the protective extra-low voltage range).

In einer Ausführungsform ist die Spannungsquelle derart ausgelegt und konfiguriert, mehr als eine (z.B. mindestens 2, mindestens 3 oder mindestens 4) beheizbare Glasfaservliese/Glasfaservliesbauteile, oder, falls das/die beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) mehrere voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, diese Bereiche, mit Spannung (und/oder elektrischem Strom) gleichzeitig versorgen zu können. Beispielsweise können alle vorhandenen beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder alle voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, mit derselben elektrischen Spannung (und/oder demselben elektrischem Strom) beaufschlagt werden. Alternativ können alle vorhandenen beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder alle voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, individuell mit elektrischer Spannung und/oder elektrischem Strom beaufschlagt werden, d.h. dass alle der beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder alle voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, mit jeweils unterschiedlicher elektrischer Spannung und/oder unterschiedlichem elektrischen Strom beaufschlagbar sind.In one embodiment, the voltage source is configured and configured to provide more than one (eg at least 2, at least 3 or at least 4) heatable fiberglass webs / Glass fiber fleece components, or, if the heatable nonwoven fabric (s) / fiberglass nonwoven component (s) a plurality of separate areas, which are coated with the coating comprising at least one conductivity additive and at least one binder, these areas, with voltage ( and / or electrical power) at the same time. For example, all existing heatable glass fiber nonwoven / glass fiber fleece components and / or all separate areas, which are coated with the coating comprising at least one conductivity additive and at least one binder, if present, with the same electrical voltage (and / or the same electric current) acted upon become. Alternatively, all existing heatable glass fiber nonwoven / glass fiber fleece components and / or all separate areas, which are coated with the coating comprising at least one conductivity additive and at least one binder, if present, individually supplied with electrical voltage and / or electrical current, ie that all of the heatable glass fiber nonwoven fabric / glass fiber nonwoven components and / or all separate areas, which are coated with the coating comprising at least one conductivity additive and at least one binder, if present, each with different electrical voltage and / or different electrical current can be acted upon.

Die Steuerungsvorrichtung ist vorzugsweise derart konfiguriert und ausgestaltet, das(die) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, zu steuern, d.h. zu steuern, mit welcher elektrischen Spannung und/oder welchem elektrischen Strom das/die beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennte Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, beaufschlagt wird(werden), um die gewünschte Temperatur zu erreichen.The control device is preferably configured and configured to coat the heatable glass fiber nonwoven fabric (s) / fiberglass nonwoven component (s) and / or the discrete regions coated with the coating comprising at least one conductivity additive and at least one binder are, if available, to control, ie to control with what electrical voltage and / or which electric current the heatable glass fiber nonwoven fabric (s) / glass fiber fleece component (s) and / or the separate regions, which with the coating, the at least one conductivity additive and at least one binder coated, if present, is applied to achieve the desired temperature.

In einer bevorzugten Variante dieser Ausführungsform ist die Steuerungsvorrichtung derart ausgelegt und konfiguriert, dass jedes der vorhandenen beheizbaren Glasfaservliese/Glasfaservliesbauteile, und/oder jeder der voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, individuell, d.h. mit einer unterschiedlichen Spannung (und/oder elektrischem Strom), beaufschlagbar sind. Hierdurch kann eine Feinabstimmung der Heizleistung der einzelnen beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder der einzelnen voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, erreicht werden und beispielsweise eine Heizung, die dem Benutzer „zu warm“ ist, heruntergedreht werden oder eine zu kalte Fläche etwas heraufgedreht werden. Insbesondere bevorzugt in dieser Variante ist, dass das Steuerungselement derart ausgelegt und konfiguriert ist, dass die Spannung (und/oder der elektrische Strom), die(der) an jedes einzelne der beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder an jeden der voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, angelegt wird, in dem Steuerungselement voreinstellbar ist, insbesondere bevorzugt ist, dass das Steuerungselement derart ausgelegt und konfiguriert ist, dass die Spannung (und/oder der elektrische Strom), die(der) an jedes einzelne der an jedes einzelne der beheizbaren Glasfaservliese/Glasfaservliesbauteile und/oder jeden der voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, angelegt wird, relativ zueinander in dem Steuerungselement voreinstellbar ist. Beispielsweise ließe sich bei zwei beheizbaren Glasfaservliesen/Glasfaservliesbauteilen A und B voreinstellen, dass das beheizbare Glasfaservlies/Glasfaservliesbauteil A mit 90% der Spannung (und/oder des elektrischen Stroms) des beheizbaren Glasfaservlieses/Glasfaservliesbauteils B betrieben wird oder, dass das beheizbare Glasfaservlies/Glasfaservliesbauteil A mit 2 V weniger als das beheizbare Glasfaservlies/Glasfaservliesbauteil B betrieben wird etc.In a preferred variant of this embodiment, the control device is designed and configured such that each of the existing heatable glass fiber nonwoven fabric components, and / or each of the separate regions, which are coated with the coating comprising at least one conductivity additive and at least one binder, if available, individually, ie with a different voltage (and / or electric current), can be acted upon. In this way, a fine-tuning of the heating power of the individual heatable glass fiber nonwoven / glass fiber nonwoven components and / or the individual separate areas, which are coated with the coating comprising at least one conductivity additive and at least one binder, coated, if present, can be achieved and, for example, a heater that the user is "too warm", turned down or turned up too cold a surface. Particularly preferred in this variant is that the control element is designed and configured in such a way that the voltage (and / or the electrical current) that is applied to each of the heatable glass fiber fleece / nonwoven components and / or to each of the separate regions, which is coated with the coating comprising at least one conductivity additive and at least one binder, if present, is presettable in the control element, in particular preferred is that the control element is designed and configured such that the voltage (and / or the electric current) which is coated on each one of each of the heatable glass fiber nonwoven fabric members and / or each of the discrete portions which is coated with the coating comprising at least one conductivity additive and at least one binder, if present , is applied, relative to each other in the Ste is predeterminable. For example, in the case of two heatable glass fiber nonwovens / glass fiber nonwoven components A and B, it may be presumed that the heatable glass fiber nonwoven component A is operated with 90% of the voltage (and / or electric current) of the heatable glass fiber nonwoven component B or that the heatable glass fiber nonwoven component / glass fiber nonwoven component A is operated with 2 V less than the heatable glass fiber nonwoven / glass fiber nonwoven component B etc.

Hierzu ist es zweckmäßig, dass in einer Ausführungsform das Steuerungselement einen Thermostat aufweist, der insbesondere derart konfiguriert und ausgestaltet ist, die Temperatur des Raumes, in dem sich das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) befindet(befinden), messen und gegebenenfalls überwachen zu können. Zweckmäßig ist der Thermostat derart konfiguriert und ausgestaltet, mit der Steuerungsvorrichtung kommunizieren zu können. Vorteilhafterweise ist der Thermostat in dem Raum, in dem sich das das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) befindet(befinden), angebracht, jedoch vorzugsweise nicht direkt neben einem erfindungsgemäßen beheizbaren Glasfaservlies/Glasfaservliesbauteil, sondern eher an auf einem Teil des Bodens und/oder einer Wand, auf dem/der kein erfindungsgemäßes beheizbares Glasfaservlies/Glasfaservliesbauteil aufgebracht ist (beispielsweise kann sich der Thermostat an einer Wand des Raumes befinden, die der Wand gegenüberliegt, an die das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) angebracht ist(sind)). In einer Ausführungsform ist der Thermostat derart konfiguriert und ausgestaltet, dass an ihm die gewünschte Raumtemperatur (Solltemperatur) einstellbar ist.For this purpose, it is expedient that in one embodiment the control element has a thermostat, which in particular is configured and configured in this way, the temperature of the space in which the heatable nonwoven fabric (s) / glass fiber nonwoven component (s) according to the invention e) are located, able to measure and, if necessary, to monitor. Suitably, the thermostat is configured and configured to communicate with the control device. Advantageously, the thermostat is mounted in the space in which the heatable nonwoven nonwoven fabric (s) according to the invention is located, but preferably not directly next to a heatable nonwoven fabric according to the invention. Fiberglass nonwoven component, but rather on a portion of the floor and / or a wall to which no inventive heated glass fiber fleece / fiberglass nonwoven component is applied (for example, the thermostat may be located on a wall of the space opposite the wall to which the (FIG. the heatable nonwoven fabric (s) according to the invention (s) / Fiberglass cloth component (s) is (are) attached). In one embodiment, the thermostat is configured and configured such that the desired room temperature (desired temperature) can be set on it.

In einer Ausführungsform misst die Steuerungsvorrichtung im Betrieb fortwährend den elektrischen Strom, der durch das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, fließt, und vergleicht diesen mit einem Normalwert/Referenzwert. Dadurch kann sichergestellt werden, dass Fehlfunktionen eines erfindungsgemäßen beheizbaren Glasfaservlieses/Glasfaservliesbauteils, (z.B. Funkenbildung) oder mechanische Änderungen an dem/der zu beheizenden Boden, Wand und/oder Decke nicht zu einer unsicheren Situation bzw. Gefährdung von Personen und/oder Tieren führen. Beispielsweise weist in einer Ausführungsform das Steuerungselement eine Abschaltautomatik der Spannungsquelle auf. Hierzu kann das Steuerungselement derart konfiguriert und ausgestaltetet sein, dass es die Entstehung von Funken auf dem erfindungsgemäßen beheizbaren Glasfaservlies/Glasfaservliesbauteil und/oder auf den voneinander getrennten Bereichen, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, erkennt und bei Auftreten derartiger Funken die Abschaltautomatik aktiviert, d.h. die Spannungsquelle abschaltet. Alternativ oder zusätzlich ist das Steuerungselement derart konfiguriert und ausgestaltetet, dass es überwacht, welche Strommenge durch das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, fließt, und bei einer Abweichung von mindestens 1% (wie mindestens 5% oder mindestens 10%) des durch das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, fließenden Stroms vom Normalwert/Referenzwert die Abschaltautomatik aktiviert, d.h. die Spannungsquelle abschaltet.In one embodiment, during operation, the control device continuously measures the electrical current flowing through the inventive heated glass fiber nonwoven fabric (s) / fiberglass nonwoven component (s) and / or the separate regions associated with the coating, comprises at least one conductivity additive and at least one binder, are coated, if any, flows, and compares this with a normal value / reference value. It can thus be ensured that malfunctions of a heatable glass fiber fleece / nonwoven glass fiber component according to the invention (for example sparking) or mechanical changes to the floor, wall and / or ceiling to be heated do not lead to an unsafe situation or endangering of persons and / or animals. For example, in one embodiment, the control element has an automatic shutdown of the voltage source. For this purpose, the control element can be configured and configured such that it is coated with the formation of sparks on the inventive heatable glass fiber fleece / glass fiber fleece component and / or on the separate regions which are coated with the coating comprising at least one conductivity additive and at least one binder. if present, recognizes and activates the automatic shutdown when such sparks occur, ie the power source shuts off. Alternatively or additionally, the control element is configured and configured such that it monitors the amount of current through the heatable nonwoven fabric (s) / glass fiber nonwoven component (s) according to the invention and / or the separate regions which are connected to the Coating comprising at least one conductivity additive and at least one binder are coated, if any, flowing, and with a deviation of at least 1% (as at least 5% or at least 10%) of the heatable (s) according to the invention (s) n) glass fiber fleece (s) / glass fiber fleece component (s) and / or the separate regions which are coated with the coating which comprises at least one conductivity additive and at least one binder, if present, flowing current of normal value / reference value activates the automatic switch-off device, ie the power source shuts off.

In einer Ausführungsform weist das Steuerungselement einen Temperatursensor, der auf dem erfindungsgemäßen beheizbaren Glasfaservlies/Glasfaservliesbauteil angebracht werden kann, auf. Der Temperatursensor ist vorteilhafterweise derart ausgestaltet und konfiguriert, die Temperatur unmittelbar auf oder über dem erfindungsgemäßen beheizbaren Glasfaservlies/Glasfaservliesbauteil und/oder auf oder über einem der voneinander getrennten Bereiche, welche mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, zu messen und die Messdaten an den Thermostat und/oder die Steuerungsvorrichtung weiterzuleiten. Dadurch ist eine Gefährdung durch eine übermäßig heißes beheizbares Glasfaservlies/Glasfaservliesbauteil und/oder einen übermäßig heißen voneinander getrennten Bereich, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, (z.B. mit einer Temperatur an der Oberfläche des beheizbaren Glasfaservlieses/Glasfaservliesbauteils und/oder voneinander getrennten Bereich, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, von über 50°C (insbesondere falls das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) am Boden und/oder an einem Bereich einer Wand angebracht ist(sind), der für Personen erreichbar ist)) oder mit einer Temperatur an der Oberfläche des beheizbaren Glasfaservlieses/Glasfaservliesbauteils und/oder voneinander getrennten Bereichs, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, von über 70°C oder über 120°C (insbesondere falls das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) und/oder die voneinander getrennten Bereiche, welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet sind, falls vorhanden, an einer Decke und/oder einem Bereich einer Wand angebracht ist(sind), der für Personen nicht erreichbar ist) verhinderbar. Bei einem Gegenstand ist der Thermostat und/oder der Temperatursensor, sofern vorhanden, entsprechend der Ausgestaltung des Gegenstandes anzubringen. Beispielsweise kann sich bei einem Rohr der Temperatursensor auch an der Innenseite des Rohres oder an einem Abschnitt des Rohres befinden, der, in Strömungsrichtung des Rohres gesehen, sich nach dem/den beheizbaren Glasfaservlies(en)/Glasfaservliesbauteil(en) befindet.In one embodiment, the control element has a temperature sensor, which can be mounted on the heatable glass fiber nonwoven / glass fiber nonwoven component according to the invention. The temperature sensor is advantageously designed and configured in such a way as to coat the temperature directly on or above the heatable glass fiber fleece / glass fiber fleece component according to the invention and / or on or above one of the separate regions which are coated with the coating comprising at least one conductivity additive and at least one binder if present, measure and pass the measurement data to the thermostat and / or the control device. As a result, there is a risk of an excessively hot, heatable glass fiber fleece / glass fiber fleece component and / or an excessively hot, separate area which is coated with the coating, which comprises at least one conductivity additive and at least one binder, if present (eg with a temperature at the Surface of the heatable glass fiber fleece / fiberglass nonwoven component and / or separate area, which are coated with the coating, which comprises at least one conductivity additive and at least one binder, if present, above 50 ° C (in particular if the (s) according to the invention (s) heatable glass fiber nonwoven fabric (s) / glass fiber nonwoven component (s) is attached to the floor and / or to a region of a wall accessible to persons)) or at a temperature at the surface of the heatable glass fiber nonwoven fabric and / or or separate area, which with the Coating, which comprises at least one conductivity additive and at least one binder, are coated, if present, above 70 ° C. or above 120 ° C. (in particular if the heatable nonwoven fabric (s) / nonwoven glass fiber component (s) according to the invention e) and / or the separate regions coated with the coating comprising at least one conductivity additive and at least one binder, if any, attached to a ceiling and / or portion of a wall suitable for persons is not achievable) preventable. For an article, the thermostat and / or the temperature sensor, if present, according to the design of the object to install. For example, in the case of a tube, the temperature sensor can also be located on the inside of the tube or on a section of the tube which, viewed in the flow direction of the tube, is located after the heatable glass fiber fleece / fiberglass component (s).

Das Steuerungselement kann in dem Raum, der das(die) erfindungsgemäße(n) beheizbare(n) Glasfaservlies(e)/Glasfaservliesbauteil(e) enthält, angebracht sein. In einer alternativen Ausführungsform kann sich das Steuerungselement an einem anderen Ort (z.B. in einem Nebenraum, in einem zentralen Schalt- oder Sicherungsraum, an den der zu beheizende Raum angeschlossen ist, oder in einem Keller) befinden. Bei Gegenständen ist die Anbringung entsprechend der Ausgestaltung des Gegenstandes durchzuführen. Insbesondere bei ortsfesten Gegenständen kann das Steuerungselement in der Nähe des Gegenstandes angebracht sein oder sich beispielsweise in einem Nebenraum, in einem zentralen Schalt- oder Sicherungsraum etc. befinden. Bei mobilen Gegenständen, z.B. Werkzeugen, ist das Steuerungselement üblicherweise Teil des Gegenstandes.The control member may be mounted in the space containing the heatable nonwoven fabric (s) / nonwoven fabric member (s) of the present invention. In an alternative embodiment, the control element may be located at another location (eg in an adjoining room, in a central control or safety room to which the room to be heated is connected, or in a basement). For objects, the attachment is carried out according to the design of the object. Especially with stationary objects, the control element be mounted in the vicinity of the object or, for example, in an adjoining room, in a central switching or fuse space, etc. are located. For mobile objects, eg tools, the control element is usually part of the article.

Der elektrische Anschluss an die Kontaktelemente kann beispielsweise als Anschlussklemme ausgeführt sein, die z.B. als Stecker für eine Steckverbindung ausgeführt sein können oder ein Loch aufweisen, durch das ein Kabel, beispielsweise mittels Schraube und Kabelschuh, befestigt werden kann. Beispielsweise kann zur Kontaktierung der Kontaktelemente ein flaches Metallstück an dem jeweiligen Kontaktelement angebracht werden, z.B. mittels Schrauben, die durch das jeweilige Kontaktelement geführt werden. Dieses flache Metallstück kann ferner dazu ausgelegt sein, eine elektrische Leitung anzuschließen, beispielsweise ausgelegt sein, dass eine Flachsteckhülse aufgesteckt werden kann. Alternativ könnte beispielsweise auch ein Kabelschuh an einer der ggf. vorhandenen Schrauben befestigt werden. Ggf. muss eine zusätzliche Zugentlastung angebracht werden. Derartige Zugentlastungen sind aus dem Stand der Technik bekannt.The electrical connection to the contact elements may, for example, be designed as a connection terminal, which may be e.g. can be designed as a plug for a plug connection or have a hole through which a cable, for example by means of screw and cable lug, can be attached. For example, for contacting the contact elements, a flat metal piece may be attached to the respective contact element, e.g. by means of screws, which are guided by the respective contact element. This flat piece of metal can also be designed to connect an electrical line, for example, be designed so that a blade receptacle can be plugged. Alternatively, for example, a cable lug could be attached to one of the screws, if present. Possibly. An additional strain relief must be installed. Such strain reliefs are known from the prior art.

Die Fläche des Metallstückes, die auf dem Kontaktelement aufliegt, beträgt üblicherweise zwischen 1,0 und 6,0 cm2, vorzugsweise 2,0 bis 4,0 cm2.The area of the metal piece resting on the contact element is usually between 1.0 and 6.0 cm 2 , preferably 2.0 to 4.0 cm 2 .

Gegenstand, Boden, Wand und/oder DeckeObject, floor, wall and / or ceiling

Die vorliegende Erfindung ist ferner gerichtet auf einen Gegenstand, einen Boden, eine Wand und/oder eine Decke, enthaltend ein beheizbares Glasfaservlies gemäß der vorliegenden Erfindung oder ein Glasfaservliesbauteil gemäß der vorliegenden Erfindung.The present invention is further directed to an article, a floor, a wall and / or a ceiling comprising a heatable glass fiber mat according to the present invention or a glass fiber mat fabric according to the present invention.

Bezüglich der Ausgestaltung der Komponenten des/der erfindungsgemäßen Gegenstandes, Bodens, Wand und/oder Decke wird vollumfänglich auf den ersten (beheizbares Glasfaservlies) und zweiten (Glasfaservliesbauteil) erfindungsgemäßen Aspekt verwiesen.With regard to the design of the components of / the object according to the invention, floor, wall and / or ceiling, reference is made in full to the first (heatable glass fiber fleece) and second (glass fiber fleece component) aspect of the invention.

Das erfindungsgemäße beheizbare Glasfaservlies und Glasfaservliesbauteil ermöglichen einen einfachen Gegenstand-, Wand- und/oder Deckenaufbau, insbesondere, wenn es mit einer Schutzkleinspannung betrieben wird, ohne dass zusätzliche Schichten benötigt werden.The heatable glass fiber fleece according to the invention and glass fiber fleece component allow a simple object, wall and / or ceiling construction, in particular, if it is operated with a safety extra-low voltage, without additional layers are needed.

Daher ist es bevorzugt, dass die Wand und/oder Decke vorzugsweise ein Substrat ausgewählt aus einer Spanplatte, Holzplatte, MDF-Platte, OSB-Platte, Hart-PVC-Platte, Polystyrolplatte, Fliesenlegerplatte, Bauplatte, z.B. Fliesenverlegeplatte, Thermoplatte, Thermopanel, Thermovlies, Innendämmplatte, Klimaplatte, Acrylglas, Gipskartonplatte, einer Gipsfaserplatte, mineralischem Putz, Kunststoffputz, Beton, einer Dispersions-Wandfarbe, vorzugsweise auf Acrylat- oder Polyvinylacetat-Basis, und einer Dispersions-Silikat-Wandfarbe, umfasst, und sich zwischen dem Substrat und dem beheizbaren Glasfaservlies gemäß der vorliegenden Erfindung bzw. dem Glasfaservliesbauteil gemäß der vorliegenden Erfindung nicht mehr als eine Grundierung und/oder eine Kleberschicht befindet. Insbesondere bevorzugt ist das Substrat ausgewählt aus einer Gipskartonplatte, einer Gipsfaserplatte, mineralischem Putz, Kunststoffputz, Beton, einer Dispersions-Wandfarbe, vorzugsweise auf Acrylat- oder Polyvinylacetat-Basis, und einer Dispersions-Silikat-Wandfarbe.Therefore, it is preferable that the wall and / or ceiling is preferably a substrate selected from a chipboard, wood board, MDF board, OSB board, hard PVC board, polystyrene board, tiler board, building board, e.g. Tile laying plate, thermal plate, thermopanel, thermal nonwoven, interior insulation board, climatic sheet, acrylic glass, plasterboard, a gypsum fiber board, mineral plaster, plastic plaster, concrete, a dispersion wall paint, preferably based on acrylate or polyvinyl acetate, and a dispersion silicate wall paint comprises and no more than a primer and / or an adhesive layer is located between the substrate and the heatable glass fiber nonwoven according to the present invention or the nonwoven glass fiber member according to the present invention. Most preferably, the substrate is selected from a gypsum board, a gypsum fiber board, mineral plaster, plastic plaster, concrete, a dispersion wall paint, preferably based on acrylate or polyvinyl acetate, and a dispersion silicate wall paint.

Vorzugsweise befindet sich auf der dem Substrat abgewandten Seite des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung bzw. des Glasfaservliesbauteils gemäß der vorliegenden Erfindung nicht mehr als eine Putz-/Trennfarbe, eine Wandfarbe und ggf. eine Vliesschicht, wobei diese Vliesschicht, sofern vorhanden, normalerweise kein Leitfähigkeitsadditiv enthält, mehr bevorzugt enthalten ferner die Putz-/Trennfarbe und die Wandfarbe, sofern vorhanden, kein Leitfähigkeitsadditiv. Eine derartige Vliesschicht, falls vorhanden, weist vorzugsweise ein Flächengewicht von nicht mehr als 100 g/m2, mehr bevorzugt nicht mehr als 60 g/m2 und noch mehr bevorzugt nicht mehr als 30 g/m2 auf.Preferably, on the side facing away from the substrate of the heatable glass fiber fleece according to the present invention or the glass fiber fleece component according to the present invention is no more than a Putz- / Trennfarbe, a wall paint and possibly a nonwoven layer, said nonwoven, if present, usually no Conductive additive also contains, more preferably, the cleaning / release paint and the wall paint, if present, no conductivity additive. Such a nonwoven layer, if present, preferably has a basis weight of not more than 100 g / m 2 , more preferably not more than 60 g / m 2, and even more preferably not more than 30 g / m 2 .

Falls das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung bzw. das Glasfaservliesbauteil gemäß der vorliegenden Erfindung in einem Boden enthalten ist, so befindet sich vorzugsweise das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung bzw. das Glasfaservliesbauteil gemäß der vorliegenden Erfindung direkt unterhalb des Nutzbelages des Bodens und

  1. (i) der Nutzbelag des Bodens und das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung bzw. das Glasfaservliesbauteil gemäß der vorliegenden Erfindung sind beide schwimmend verlegt;
  2. (ii) der Nutzbelag des Bodens und das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung bzw. das Glasfaservliesbauteil gemäß der vorliegenden Erfindung sind miteinander und mit dem darunterliegenden Teil des Bodens verklebt; oder
  3. (iii) das beheizbare Glasfaservlies gemäß der vorliegenden Erfindung bzw. das Glasfaservliesbauteil gemäß der vorliegenden Erfindung ist mit dem darunterliegenden Teil des Bodens verklebt und der Nutzbelag ist schwimmend verlegt.
If the heatable glass fiber nonwoven according to the present invention or the glass fiber nonwoven component according to the present invention is contained in a soil, then preferably the heatable glass fiber fabric according to the present invention or the glass fiber nonwoven component according to the present invention directly below the floor covering and
  1. (i) the floor covering and the glass fiber nonwoven fabric according to the present invention and the nonwoven glass fiber fabric according to the present invention are both laid in a floating manner;
  2. (ii) the floor covering and the heatable glass fiber fleece according to the present invention and / or the glass fiber fleece building according to the present invention are adhered to each other and to the underlying part of the floor; or
  3. (iii) the heatable glass fiber mat according to the present invention or the glass fiber mat component according to the present invention is glued to the underlying part of the floor and the utility mat is laid floating.

Verwendungen uses

Das erfindungsgemäße beheizbare Glasfaservlies oder das erfindungsgemäße Glasfaservliesbauteil oder das mittels des erfindungsgemäßen Kits hergestellten Glasfaservliesbauteil können zum Beheizen eines Gegenstandes, eines Bodens und/oder eines Raumes oder zum Abschirmen eines Gegenstandes und/oder Raumes vor elektromagnetischer Strahlung verwendet werden.The heatable glass fiber nonwoven fabric according to the invention or the glass fiber nonwoven component according to the invention or the glass fiber nonwoven component produced by means of the kit according to the invention can be used for heating an object, a floor and / or a room or for shielding an object and / or room from electromagnetic radiation.

Hinsichtlich der Ausgestaltung der erfindungsgemäßen Verwendung wird vollinhaltlich auf die vorstehenden Ausführungen bezüglich des ersten (beheizbares Glasfaservlies), zweiten (Glasfaservliesbauteil) und dritten (Kit zum Herstellen eines Glasfaservliesbauteils) erfindungsgemäßen Aspektes Bezug genommen.With regard to the configuration of the use according to the invention, reference is made in full to the above statements regarding the first (heatable glass fiber fleece), second (glass fiber fleece component) and third (kit for producing a glass fiber fleece component) aspect of the invention.

Verfahrenmethod

Das erfindungsgemäße beheizbare Glasfaservlies oder das erfindungsgemäße Glasfaservliesbauteil oder das mittels des erfindungsgemäßen Kits hergestellte Glasfaservliesbauteil können an eine(n) oder mehrere Gegentand/Gegenstände, Boden/Böden, Wand/Wände und/oder Decke(n) angebracht werden und durch Beaufschlagen des/der beheizbaren Glasfaservliese(s) oder des/der Glasfaservliesbauteils/Glasfaservliesbauteile mit elektrischer Spannung und/oder elektrischem Strom kann ein Gegenstand und/oder Raum beheizt werden.The heatable glass fiber mat according to the invention or the glass fiber fleece component or the glass fiber fleece component produced by means of the kit according to the invention can be applied to one or more surfaces / objects, floor / floors, wall / walls and / or ceiling (s) and by applying the / heatable glass fiber web (s) or the / the glass fiber fleece component / fiberglass nonwoven components with electrical voltage and / or electric current, an object and / or space can be heated.

Hinsichtlich der Ausgestaltung des erfindungsgemäßen Verfahrens wird vollinhaltlich auf die vorstehenden Ausführungen bezüglich des ersten (beheizbares Glasfaservlies), zweiten (Glasfaservliesbauteil) und dritten (Kit zum Herstellen eines Glasfaservliesbauteils) erfindungsgemäßen Aspektes Bezug genommen.With regard to the embodiment of the method according to the invention, reference is made in full to the above statements regarding the first (heatable glass fiber fleece), second (glass fiber fleece component) and third (kit for producing a glass fiber fleece component) aspect of the invention.

Die Beaufschlagung des/der beheizbaren/beheizbarer Glasfaservliese(s) oder des/der Glasfaservliesbauteils/Glasfaservliesbauteile erfolgt vorzugsweise durch ein Steuerungselement, elektrische Leitungen, Kontaktelemente und/oder Anschlussklemmen wie hierin im zweiten (Glasfaservliesbauteil) und dritten (Kit zum Herstellen eines Glasfaservliesbauteils) erfindungsgemäßen Aspekt beschrieben, auf die vollinhaltlich Bezug genommen wird.The heating / heating of the glass fiber nonwoven fabric (s) or of the nonwoven glass fiber component (s) preferably takes place by a control element, electrical lines, contact elements and / or terminals as described herein in the second (glass fiber nonwoven component) and third (kit for producing a glass fiber nonwoven component) Aspect, to which reference is made in full.

1 ist eine schematische, nicht maßstabsgetreue Vorderansicht eines bevorzugten Ausführungsbeispiels des Glasfaservliesbauteils (1) gemäß der vorliegenden Erfindung. Das Glasfaservliesbauteil (1) weist ein beheizbares Glasfaservlies (2) und zwei Kontaktelemente (3) auf. Die gestrichelten Linien in 1 zeigen die Anordnung der Kontaktelemente (3) hinter dem Glasfaservlies (2). Das gezeigte Glasfaservliesbauteil (1) kann dadurch hergestellt werden, dass die Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, auf ein Glasfaservlies aufgetragen wird und anschließend die Kontaktelemente daran angebracht werden, beispielsweise angeklebt werden. 1 is a schematic, not to scale front view of a preferred embodiment of the glass fiber nonwoven component ( 1 ) according to the present invention. The glass fiber fleece component (1) has a heatable glass fiber fleece ( 2 ) and two contact elements ( 3 ) on. The dashed lines in 1 show the arrangement of the contact elements ( 3 ) behind the glass fiber fleece ( 2 ). The glass fiber nonwoven component ( 1 ) may be prepared by applying the coating comprising at least one conductivity additive and at least one binder to a glass fiber mat and then attaching the contact elements thereto, for example by gluing.

BezugszeichenlisteLIST OF REFERENCE NUMBERS

1.1.
GlasfaservliesbauteilFiberglass mat component
2.Second
beheizbares Glasfaservliesheatable glass fiber fleece
3.Third
Kontaktelementcontact element

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • DIN EN ISO 29073-3:1992 [0068]DIN EN ISO 29073-3: 1992 [0068]

Claims (30)

Beheizbares Glasfaservlies, umfassend eine Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, wobei das Flächengewicht des beheizbaren Glasfaservlieses mindestens 250 g/m2 beträgt.A heatable glass fiber nonwoven comprising a coating comprising at least one conductivity additive and at least one binder, wherein the basis weight of the heatable glass fiber nonwoven is at least 250 g / m 2 . Beheizbares Glasfaservlies gemäß Anspruch 1, wobei das Flächengewicht des beheizbaren Glasfaservlieses mindestens 275 g/m2, vorzugsweise mindestens 300 g/m2, mehr bevorzugt mindestens 325 g/m2 beträgt.Heated fiberglass mat according to Claim 1 , wherein the basis weight of the heatable glass fiber fleece at least 275 g / m 2 , preferably at least 300 g / m 2 , more preferably at least 325 g / m 2 . Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei der Gewichtsanteil der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, mindestens 30%, vorzugsweise mindestens 35%, mehr bevorzugt mindestens 40%, bezogen auf die Summe der Gewichte des Bereiches des Glasfaservlieses welcher mit der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beschichtet ist, vor Auftragung der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, und der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beträgt.Heated fiberglass fabric according to one of the preceding claims, wherein the weight fraction of the coating comprising at least one conductivity additive and at least one binder, at least 30%, preferably at least 35%, more preferably at least 40%, based on the sum of the weights of the region of the glass fiber fleece coated with the coating comprising at least one conductivity additive and at least one binder, prior to application of the coating comprising at least one conductivity additive and at least one binder, and the coating comprising at least one conductivity additive and at least one binder. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei die Dicke des beheizbaren Glasfaservlieses zwischen 0,20 und 1,00 mm, vorzugsweise zwischen 0,25 und 0,90 mm, mehr bevorzugt zwischen 0,30 und 0,50 mm beträgt.Heated fiberglass fabric according to one of the preceding claims, wherein the thickness of the heatable fiberglass mat is between 0.20 and 1.00 mm, preferably between 0.25 and 0.90 mm, more preferably between 0.30 and 0.50 mm. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei die Höchstzugkraft des beheizbaren Glasfaservlieses in Längs- und/oder Querrichtung mindestens 120 N/5 cm beträgt, vorzugsweise die Höchstzugkraft des beheizbaren Glasfaservlieses in Längs- und/oder Querrichtung mindestens 135 N/5 cm beträgt, mehr bevorzugt die Höchstzugkraft des beheizbaren Glasfaservlieses - in Längsrichtung mindestens 160 N/5 cm und/oder - in Querrichtung mindestens 135 N/5 cm, beträgt, mehr bevorzugt die Höchstzugkraft des beheizbaren Glasfaservlieses - in Längsrichtung mindestens 175 N/5 cm und/oder - in Querrichtung mindestens 145 N/5 cm beträgt.Heated fiberglass fabric according to one of the preceding claims, wherein the maximum tensile force of the heatable glass fiber fleece in the longitudinal and / or transverse direction is at least 120 N / 5 cm, preferably the maximum tensile force of the heatable fiberglass fleece in the longitudinal and / or transverse direction is at least 135 N / 5 cm, more preferably the maximum tensile force of the heated glass fiber fleece - in the longitudinal direction at least 160 N / 5 cm and / or - in the transverse direction at least 135 N / 5 cm, is, more preferably the maximum tensile force of the heated glass fiber fleece - in the longitudinal direction at least 175 N / 5 cm and / or - in the transverse direction at least 145 N / 5 cm is. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, aufweisend eine Fläche von 50,0 cm2 bis 6,00 m2, vorzugsweise aufweisend eine Fläche von 225 cm2 bis 6,00 m2 und noch mehr bevorzugt aufweisend eine Fläche von 400 cm2 bis 6,00 m2, beispielsweise beträgt die Fläche des beheizbaren Glasfaservlieses in Draufsicht nicht mehr als 3,00 m2, nicht mehr als 2,00 m2 oder nicht mehr als 1,50 m2 oder das beheizbare Glasfaservlies weist eine Fläche von bis zu 500 m2 auf und ist in Abschnitte dieser Größen teilbar.A heated fiberglass mat according to any one of the preceding claims, having an area of 50.0 cm 2 to 6.00 m 2 , preferably having an area of 225 cm 2 to 6.00 m 2 and even more preferably having an area of 400 cm 2 to 6.00 m 2 , for example, the surface of the heated glass fiber fleece in plan view is not more than 3.00 m 2 , not more than 2.00 m 2 or not more than 1.50 m 2 or the heated glass fiber fleece has an area of up to 500 m 2 and is divisible into sections of these sizes. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche aufweisend die Form eines Quadrates, eines Rechtecks, einer Raute oder eines Parallelogramms, wobei die kürzere Kante des Rechtecks oder Parallelogramms als erste Kante und die längere Kante des Rechtecks oder Parallelogramms als zweite Kante angesehen wird.Heated fiberglass fabric according to one of the preceding claims having the shape of a square, a rectangle, a rhombus or a parallelogram, wherein the shorter edge of the rectangle or parallelogram is considered as a first edge and the longer edge of the rectangle or parallelogram as the second edge. Beheizbares Glasfaservlies gemäß Anspruch 7, (i) aufweisend die Form eines Rechtecks oder Parallelogramms, wobei die erste Kante des beheizbaren Glasfaservlieses eine Länge von 8,00 bis 100 cm, bevorzugt von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm aufweist und/oder die zweite Kante des beheizbaren Glasfaservlieses weist eine Länge von 8,00 bis 600 cm, bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm auf, oder die zweite Kante des beheizbaren Glasfaservlieses gemäß der vorliegenden Erfindung weist eine Länge von bis zu 500 m auf und ist in Abschnitte einer Länge von 8,00 bis 600 cm, mehr bevorzugt von 15,0 bis 600 cm und am meisten bevorzugt von 20,0 cm bis 600 cm, beispielsweise 20,0 bis 250 cm, 20,0 bis 200 cm oder 20,0 bis 150 cm, teilbar, oder (ii)als Quadrat und Raute ausgeführt, wobei alle Kanten eine Länge von 8,00 bis 100 cm, bevorzugt von 15,0 bis 100 cm und am meisten bevorzugt von 20,0 cm bis 100 cm aufweisen.Heated fiberglass mat according to Claim 7 , (i) having the shape of a rectangle or parallelogram, wherein the first edge of the heatable fiberglass mat has a length of 8.00 to 100 cm, preferably 15.0 to 100 cm, and most preferably 20.0 to 100 cm and / or the second edge of the heatable fiberglass mat has a length of 8.00 to 600 cm, preferably of 15.0 to 600 cm, and most preferably of 20.0 cm to 600 cm, or the second edge of the heatable fiberglass mat according to The present invention has a length of up to 500 m and is in sections of a length of 8.00 to 600 cm, more preferably from 15.0 to 600 cm, and most preferably from 20.0 cm to 600 cm, for example 20 , 0 to 250 cm, 20.0 to 200 cm or 20.0 to 150 cm, divisible, or (ii) executed as a square and rhombus, all edges having a length of 8.00 to 100 cm, preferably of 15.0 to 100 cm, and most preferably from 20.0 cm to 100 cm. Beheizbares Glasfaservlies gemäß Anspruch 7 aufweisend die Form eines Rechtecks oder Parallelogramms oder Anspruch 8(i), wobei das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks zwischen 0,20 und < 1,00 beträgt, bevorzugt beträgt das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks zwischen 0,40 und 0,80, noch mehr bevorzugt zwischen 0,50 und 0,70.Heated fiberglass mat according to Claim 7 having the shape of a rectangle or parallelogram or claim 8 (i), wherein the aspect ratio between the first edge of the parallelogram and the second edge of the parallelogram is between 0.20 and <1.00, preferably the aspect ratio between the first edge of the parallelogram and the second edge of the parallelogram between 0.40 and 0.80, more preferably between 0.50 and 0.70. Beheizbares Glasfaservlies gemäß gemäß Anspruch 7 aufweisend die Form eines Rechtecks oder Parallelogramms oder Anspruch 8(i), aufweisend die Form eines Rechtecks oder Parallelogramms, wobei das Seitenverhältnis zwischen der ersten Kante des Parallelogramms bzw. Rechtecks und der zweiten Kante des Parallelogramms bzw. Rechtecks weniger als 0,40, vorzugsweise weniger als 0,30, mehr bevorzugt weniger als 0,20, beispielsweise weniger als 0,10, weniger als 0,05 oder weniger als 0,025.Heated fiberglass mat according to Claim 7 having the shape of a rectangle or parallelogram or claim 8 (i) having the shape of a rectangle or parallelogram, wherein the aspect ratio between the first edge of the parallelogram and the second edge of the parallelogram is less than 0.40, preferably less than 0.30, more preferably less than 0.20, for example, less than 0.10, less than 0.05, or less than 0.025. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei das mindestens eine Leitfähigkeitsadditiv ausgewählt ist aus Leitfähigkeitsadditiven, die Graphit, Graphen und Ruß umfassen.Heated fiberglass fabric according to one of the preceding claims, wherein the at least one conductivity additive is selected from Conductivity additives comprising graphite, graphene and carbon black. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei das mindestens eine Bindemittel ein elektrisch nicht leitfähiges Polymer oder ein anorganisches Bindemittel umfasst.A heatable glass fiber nonwoven according to any one of the preceding claims, wherein the at least one binder comprises an electrically nonconductive polymer or an inorganic binder. Beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche, wobei der Gewichtsanteil des mindestens einen Leitfähigkeitsadditivs zwischen 10 bis 90 Gew.%, vorzugsweise zwischen 20 bis 80 Gew.%, mehr bevorzugt 30 bis 70 Gew.% bezogen auf das Gesamtgewicht der Beschichtung, die mindestens ein Leitfähigkeitsadditiv und mindestens ein Bindemittel umfasst, beträgt.The heated glass fiber fleece according to claim 1, wherein the weight fraction of the at least one conductivity additive is between 10 and 90% by weight, preferably between 20 to 80% by weight, more preferably 30 to 70% by weight, based on the total weight of the coating, which is at least one Conductive additive and at least one binder is. Glasfaservliesbauteil, umfassend das beheizbare Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 und mindestens zwei elektrisch leitfähige Kontaktelemente, die an das beheizbare Glasfaservlies derart angeordnet sind, dass das beheizbare Glasfaservlies mit elektrischer Spannung und/oder elektrischem Strom beaufschlagbar ist.A glass fiber nonwoven component comprising the heatable glass fiber nonwoven according to one of the preceding Claims 1 to 13 and at least two electrically conductive contact elements which are arranged on the heatable glass fiber fleece such that the heatable glass fiber fleece can be acted upon by electrical voltage and / or electric current. Glasfaservliesbauteil gemäß Anspruch 14, wobei zwei der mindestens zwei elektrisch leitfähigen Kontaktelemente an sich gegenüberliegenden Randbereichen des beheizbaren Glasfaservlieses angeordnet sind.Glass fiber fleece component according to Claim 14 wherein two of the at least two electrically conductive contact elements are arranged on opposite edge regions of the heatable glass fiber fleece. Glasfaservliesbauteil gemäß einem der Ansprüche 14 oder 15, wobei jedes elektrisch leitfähige Kontaktelement einen elektrisch leitenden Metallstreifen, insbesondere aus Kupfer, umfasst, wobei vorzugsweise jedes dieser elektrisch leitfähigen Kontaktelemente eine Klebeschicht aufweist, die sich auf der dem beheizbaren Glasfaservlies abgewandten Seite der elektrisch leitfähigen Kontaktelemente befindet, die Klebeschicht ist insbesondere mit einer Schutzfolie bedeckt.Glass fiber nonwoven component according to one of Claims 14 or 15 wherein each electrically conductive contact element comprises an electrically conductive metal strip, in particular of copper, wherein preferably each of these electrically conductive contact elements has an adhesive layer which is located on the side facing away from the heatable glass fiber fleece side of the electrically conductive contact elements, the adhesive layer is in particular with a protective film covered. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 16, wobei die Gesamtdicke jedes elektrisch leitfähigen Kontaktelements maximal 120 µm, vorzugsweise maximal 110 µm, mehr bevorzugt maximal 90 µm beträgt.Glass fiber nonwoven component according to one of the preceding Claims 14 to 16 , wherein the total thickness of each electrically conductive contact element is a maximum of 120 microns, preferably at most 110 microns, more preferably at most 90 microns. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 17, wobei die mindestens zwei elektrisch leitfähigen Kontaktelemente parallel angeordnet sind und der Abstand zwischen ihren Innenkanten mindestens 30 cm, vorzugsweise mindestens 40 cm, mehr bevorzugt mindestens 50 cm beträgt und/oder die mindestens zwei elektrisch leitfähigen Kontaktelemente sind parallel angeordnet und der Abstand zwischen ihren Innenkanten beträgt nicht mehr als 3,00 m, vorzugsweise nicht mehr als 2,00 m und am meisten bevorzugt nicht mehr als 1,00 m.Glass fiber nonwoven component according to one of the preceding Claims 14 to 17 wherein the at least two electrically conductive contact elements are arranged in parallel and the distance between their inner edges at least 30 cm, preferably at least 40 cm, more preferably at least 50 cm and / or the at least two electrically conductive contact elements are arranged in parallel and the distance between their inner edges is not more than 3.00 m, preferably not more than 2.00 m, and most preferably not more than 1.00 m. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 18, wobei jedes der elektrisch leitfähigen Kontaktelemente über eine Kante des beheizbaren Glasfaservlieses um mindestens 10 cm, vorzugsweise um mindestens 25 cm, mehr bevorzugt um mindestens 40 cm übersteht.Glass fiber nonwoven component according to one of the preceding Claims 14 to 18 wherein each of the electrically conductive contact elements projects beyond an edge of the heatable glass fiber fleece by at least 10 cm, preferably by at least 25 cm, more preferably by at least 40 cm. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 19, wobei jedes elektrisch leitfähige Kontaktelement eine Breite von 1,4 bis 4,4 cm, vorzugsweise von 1,9 bis 3,9 cm, mehr bevorzugt von 2,4 bis 3,4 cm aufweist.Glass fiber nonwoven component according to one of the preceding Claims 14 to 19 wherein each electrically conductive contact element has a width of 1.4 to 4.4 cm, preferably 1.9 to 3.9 cm, more preferably 2.4 to 3.4 cm. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 20, wobei jedes elektrisch leitfähige Kontaktelement 0,0 bis 10,0 cm, vorzugsweise 0,0 bis 8,0 cm, mehr bevorzugt 0,0 bis 6,0 cm von dem Rand des beheizbaren Glasfaservlieses entfernt angeordnet ist.Glass fiber nonwoven component according to one of the preceding Claims 14 to 20 wherein each electrically conductive contact element is 0.0 to 10.0 cm, preferably 0.0 to 8.0 cm, more preferably 0.0 to 6.0 cm away from the edge of the heated fiberglass mat. Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 21, welches durch Beaufschlagung mit einer Schutzkleinspannung betreibbar ist.Glass fiber nonwoven component according to one of the preceding Claims 14 to 21 , which is operable by applying a protective extra-low voltage. Kit zum Herstellen eines Glasfaservliesbauteils, wobei das Kit umfasst: (1) ein beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13, (2) mindestens zwei elektrisch leitfähige Kontaktelemente, und (3) optional, Glasgewebekleber.A kit for making a fiberglass nonwoven component, the kit comprising: (1) a heatable fiberglass mat according to any one of the preceding Claims 1 to 13 , (2) at least two electrically conductive contact elements, and (3) optionally, glass fabric adhesive. Kit gemäß Anspruch 23, ferner umfassend: (4) ein Steuerungselement, das eine Spannungsquelle, vorzugsweise eine Spannungsquelle für Schutzkleinspannung, und eine Steuerungsvorrichtung zum Steuern eines beheizbaren Glasfaservlieses umfasst, und (5) zwei elektrische Leitungen, wobei die erste elektrische Leitung mit einem der Pole der Spannungsquelle verbindbar oder verbunden ist und die zweite elektrische Leitung mit dem anderen Pol der Spannungsquelle verbindbar oder verbunden ist und die erste elektrische Leitung mit einem der mindestens zwei elektrisch leitfähigen Kontaktelementen elektrisch leitend verbindbar ist und die zweite elektrische Leitung mit einem der anderen der mindestens zwei elektrisch leitfähigen Kontaktelementen elektrisch leitend verbindbar ist.Kit according to Claim 23 further comprising: (4) a control element comprising a voltage source, preferably a safety extra-low voltage power supply, and a control device for controlling a heatable fiberglass mat, and (5) two electrical leads, the first electrical lead being connectable to one of the poles of the voltage source or is connected and the second electrical line with the other pole of the voltage source is connectable or connected and the first electrical line with one of the at least two electrically conductive contact elements is electrically conductively connected and the second electrical line with one of the other of the at least two electrically conductive contact elements electrically conductive is connectable. Kit gemäß Anspruch 24, wobei das Steuerungselement eine Abschaltautomatik der Spannungsquelle aufweist, wobei vorzugsweise bei (I) Entstehung von Funken in dem Glasfaservlies oder (II) einer Abweichung von mindestens 1% des durch das beheizbare Glasfaservlies fließenden Stroms vom Normalwert die Abschaltautomatik aktiviert, d.h. die Spannungsquelle abgeschaltet wird.Kit according to Claim 24 wherein the control element has an automatic shutdown of the voltage source, wherein preferably in (I) generation of sparks in the glass fiber fleece or (II) a deviation of at least 1% of the current flowing through the heated glass fiber fleece normal value activates the automatic shutdown, ie the voltage source is turned off , Kit gemäß einem der Ansprüche 24 oder 25, wobei das Steuerungselement ferner einen Thermostat aufweist. Kit according to one of Claims 24 or 25 wherein the control element further comprises a thermostat. Gegenstand, Boden, Wand und/oder Decke, enthaltend ein beheizbares Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 oder ein Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 oder eines mittels des Kits gemäß einem der Ansprüche 23 bis 26 hergestellten Glasfaservliesbauteils.An article, floor, wall and / or ceiling, comprising a heatable fiberglass mat according to one of the preceding Claims 1 to 13 or a glass fiber nonwoven component according to any one of the preceding Claims 14 to 22 or one by means of the kit according to one of the Claims 23 to 26 manufactured fiberglass nonwoven component. Wand und/oder Decke gemäß Anspruch 27, wobei die Wand und/oder Decke ein Substrat ausgewählt aus einer Spanplatte, Holzplatte, MDF-Platte, OSB-Platte, Hart-PVC-Platte, Polystyrolplatte, Fliesenlegerplatte, Bauplatte, z.B. Fliesenverlegeplatte, Thermoplatte, Thermopanel, Thermovlies, Innendämmplatte, Klimaplatte, Acrylglas, Gipskartonplatte, einer Gipsfaserplatte, mineralischem Putz, Kunststoffputz, Beton, einer Dispersions-Wandfarbe, vorzugsweise auf Acrylat- oder Polyvinylacetat-Basis, und einer Dispersions-Silikat-Wandfarbe, umfasst, und sich zwischen dem Substrat und dem beheizbaren Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. dem Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 nicht mehr als eine Grundierung und/oder eine Kleberschicht befindet.Wall and / or ceiling according to Claim 27 in which the wall and / or ceiling is a substrate selected from a chipboard, wood board, MDF board, OSB board, hard PVC board, polystyrene board, tile board, building board, eg tile laying board, thermoplate, thermo panel, thermal nonwoven, interior insulation board, climatic board, Acrylic glass, gypsum plaster board, a gypsum fiber board, mineral plaster, plastic plaster, concrete, a dispersion wall paint, preferably based on acrylate or polyvinyl acetate, and a dispersion silicate wall paint, and between the substrate and the heatable glass fiber fabric according to one of previous Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 no more than a primer and / or an adhesive layer is located. Wand und/oder Decke gemäß Anspruch 28, wobei sich auf der dem Substrat abgewandten Seite des beheizbaren Glasfaservlieses gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. des Glasfaservliesbauteils gemäß einem der vorangegangenen Ansprüche 14 bis 22 nicht mehr als eine Putz-/Trennfarbe, eine Wandfarbe und ggf. eine Vliesschicht befindet, wobei die Vliesschicht, sofern vorhanden, kein Leitfähigkeitsadditiv enthält.Wall and / or ceiling according to Claim 28 , wherein on the side facing away from the substrate of the heatable fiberglass mat according to one of the preceding Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 no more than a cleaning / release paint, a wall paint and optionally a nonwoven layer, wherein the nonwoven layer, if present, contains no conductivity additive. Boden gemäß Anspruch 27, wobei sich das beheizbaren Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. das Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 direkt unterhalb des Nutzbelages des Bodens befindet und (i) der Nutzbelag des Bodens und das beheizbaren Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. das Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 sind beide schwimmend verlegt; (ii) der Nutzbelag des Bodens und das beheizbaren Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. das Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 sind miteinander und mit dem darunterliegenden Teil des Bodens verklebt; oder (iii) das beheizbaren Glasfaservlies gemäß einem der vorangegangenen Ansprüche 1 bis 13 bzw. das Glasfaservliesbauteil gemäß einem der vorangegangenen Ansprüche 14 bis 22 ist mit dem darunterliegenden Teil des Bodens verklebt und der Nutzbelag ist schwimmend verlegt.Soil according to Claim 27 , wherein the heatable glass fiber fleece according to one of the preceding Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 located directly below the floor covering and (i) the floor covering and the heatable glass fiber fleece according to any one of the preceding Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 Both are floating; (Ii) the floor covering and the heatable glass fiber fleece according to one of the preceding Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 are glued together and to the underlying part of the floor; or (iii) the heatable fiberglass mat according to any one of the preceding Claims 1 to 13 or the glass fiber fleece component according to one of the preceding Claims 14 to 22 is glued to the underlying part of the floor and the floor covering is laid floating.
DE202019104379.2U 2019-08-08 2019-08-08 Heated glass fiber fleece Active DE202019104379U1 (en)