DE202019005552U1 - Dimensionally stable flooring - Google Patents
Dimensionally stable flooring Download PDFInfo
- Publication number
- DE202019005552U1 DE202019005552U1 DE202019005552.5U DE202019005552U DE202019005552U1 DE 202019005552 U1 DE202019005552 U1 DE 202019005552U1 DE 202019005552 U DE202019005552 U DE 202019005552U DE 202019005552 U1 DE202019005552 U1 DE 202019005552U1
- Authority
- DE
- Germany
- Prior art keywords
- functional layer
- plastic core
- reinforcement mat
- fibers
- mat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Bodenbelag (1) mit einem Kunststoffkern (10), die eine Oberseite (11) und eine Unterseite (12) aufweist, wobei an der Oberseite (11) eine Funktionsschicht (21) und Verstärkungsmatte (22) angeordnet ist, die Fasern (23) und dazwischen liegende Zwischenräume (27) aufweist, wobei die Verstärkungsmatte (22) zwischen der Oberseite (11) des Kunststoffkerns (10) und der Funktionsschicht (21) liegt, dadurch gekennzeichnet, dass die Verstärkungsmatte (22) und die Funktionsschicht (21) eine vorproduzierte Einheit (20) darstellt, bei der die Verstärkungsmatte (22) an der Funktionsschicht (21) befestigt ist, wobei der Kunststoffkern (10) mit der vorproduzierten Einheit (20) derart verbunden ist, dass der Kunststoffkern (10) mit den Fasern (23) der Verstärkungsmatte (22) und durch die Zwischenräume (27) der Verstärkungsmatte (22) hindurch mit der Funktionsschicht (21) verbunden ist. Floor covering (1) with a plastic core (10) which has an upper side (11) and an underside (12), with a functional layer (21) and reinforcing mat (22) being arranged on the upper side (11), the fibers (23) and having intermediate spaces (27), the reinforcement mat (22) lying between the top side (11) of the plastic core (10) and the functional layer (21), characterized in that the reinforcement mat (22) and the functional layer (21) have a represents a preproduced unit (20) in which the reinforcement mat (22) is attached to the functional layer (21), the plastic core (10) being connected to the preproduced unit (20) in such a way that the plastic core (10) with the fibers ( 23) of the reinforcement mat (22) and through the interspaces (27) of the reinforcement mat (22) is connected to the functional layer (21).
Description
Die Erfindung betrifft einen Bodenbelag mit einem Kunststoffkern, die eine Oberseite und eine Unterseite aufweist, wobei an der Oberseite eine Funktionsschicht und eine Verstärkungsmatte angeordnet ist, die Fasern und dazwischen liegende Zwischenräume aufweist.The invention relates to a floor covering with a plastic core, which has an upper side and an underside, with a functional layer and a reinforcing mat being arranged on the upper side, which has fibers and intermediate spaces.
Aus der
Aus der
Gleichwohl besteht ein Bedarf, weitere Bodenbeläge bereitzustellen, die eine gute Dimensionsstabilität bei möglichst einfachem Aufbau aufweisen und sich kostengünstig herstellen lassen. Der Erfindung liegt daher die Aufgabe zu Grunde, ein Bodenbelag bereitzustellen, den man bei schwankenden Umweltbedingungen problemlos einsetzen kann, einfach aufgebaut ist und sich einfach herstellen lässt.Nevertheless, there is a need to provide further floor coverings which have good dimensional stability with the simplest possible structure and which can be produced inexpensively. The invention is therefore based on the object of providing a floor covering which can be used without any problems in fluctuating environmental conditions, is of simple construction and can be produced easily.
Die der Erfindung zu Grunde liegende Aufgabe wird mit der Merkmalskombination gemäß Anspruch 1 gelöst. Ausführungsbeispiele der Erfindung können den Unteransprüchen zu Anspruch 1 entnommen werden.The object on which the invention is based is achieved with the combination of features according to
Erfindungsgemäß ist vorgesehen, dass die Verstärkungsmatte und die Funktionsschicht als vorproduzierte Einheit vorliegt, bei der die Verstärkungsmatte an der Funktionsschicht befestigt ist, wobei der Kunststoffkern mit der vorproduzierten Einheit derart verbunden ist, dass der Kunststoffkern mit den Fasern der Verstärkungsmatte und durch die Zwischenräume der Verstärkungsmatte hindurch zusätzlich mit der Funktionsschicht verbunden ist. Dadurch ergibt sich ein besonders stabiler Verbund zwischen der Funktionsschicht, der Verstärkungsmatte und dem Kunststoffkern, wodurch der Bodenbelag besonders dimensionsstabil ist. Die Verbindung zwischen dem Kunststoffkern und der Funktionsschicht erfolgt somit auf zwei voneinander unabhängigen Wegen. Zum einen besteht ein mittelbarer Weg, da der Kunststoffkern an der Verstärkungsmatte befestigt ist, die wiederum an der Funktionsschicht im befestigt ist. Zum anderen besteht eine unmittelbare Verbindung zwischen dem Kunststoffkern und der Funktionsschicht durch die Zwischenräume der Verstärkungsmatte hindurch.According to the invention, it is provided that the reinforcement mat and the functional layer are present as a pre-produced unit in which the reinforcement mat is attached to the functional layer, the plastic core being connected to the pre-produced unit in such a way that the plastic core is connected to the fibers of the reinforcing mat and through the gaps in the reinforcing mat through it is additionally connected to the functional layer. This results in a particularly stable bond between the functional layer, the reinforcement mat and the plastic core, which makes the floor covering particularly dimensionally stable. The connection between the plastic core and the functional layer thus takes place in two mutually independent ways. On the one hand, there is an indirect way, since the plastic core is attached to the reinforcement mat, which in turn is attached to the functional layer. On the other hand, there is a direct connection between the plastic core and the functional layer through the spaces in the reinforcement mat.
Die vorproduzierte Einheit kann als aufrollbare Endlosware produziert werden. Nach deren Herstellung kann die vorproduzierte Einheit zunächst gelagert und/oder zu einer anderen Fertigungsstätte transportiert werden, in der dann - zeitlich entkoppelt - die Verbindung mit dem Kunststoffkern erfolgt. Es ist auch möglich, dass die Herstellung der vorproduzierten Einheit und deren Verbindung mit dem Kunststoffkern in einem kontinuierlichen Verfahren mit nacheinander geschalteten Verfahrensschritten erfolgt. Dabei wird zunächst die Verstärkungsmatte an der Funktionsschicht befestigt und nach erfolgter Befestigung erfolgt dann direkt auf der gleichen Strecke die Verbindung mit dem Kunststoffkern.The pre-produced unit can be produced as rollable endless goods. After its production, the pre-produced unit can first be stored and / or transported to another production site, in which the connection with the plastic core then takes place - decoupled in time. It is also possible that the production of the pre-produced unit and its connection to the plastic core take place in a continuous process with successive process steps. In this case, the reinforcement mat is first attached to the functional layer and, once it has been attached, the connection to the plastic core takes place directly on the same route.
In einem Ausführungsbeispiel umfasst die Funktionsschicht eine Kunststofffolie. Die Kunststofffolie kann aus einem Polyestermaterial wie Polyethylenterephthalat (PET) sein. Polyethylen oder Polypropylen sind weitere Beispiele für das Material, aus dem die Kunststofffolie sein kann. Auf die Kunststofffolie kann ein Dekormuster aufgebracht sein. Es ist auch denkbar, dass die Funktionsschicht ein Dekorpapier umfasst, auf dem ein Dekormuster aufgedruckt ist.In one embodiment, the functional layer comprises a plastic film. The plastic film can be made of a polyester material such as polyethylene terephthalate (PET). Polyethylene or polypropylene are further examples of the material from which the plastic film can be. A decorative pattern can be applied to the plastic film. It is also conceivable that the functional layer comprises a decorative paper on which a decorative pattern is printed.
Die Funktionsschicht und insbesondere die Kunststofffolie kann eine Stärke von 8 bis 220 µm, vorzugsweise 20 bis 50 µm aufweisen. In einem konkreten Ausführungsbeispiel wird eine PET-Folie eingesetzt, die eine Stärke von 35 bis 40 µm aufweist.The functional layer and in particular the plastic film can have a thickness of 8 to 220 μm, preferably 20 to 50 μm. In a specific exemplary embodiment, a PET film is used that has a thickness of 35 to 40 μm.
Die Verstärkungsmatte kann eine Glasfasermatte sein. In diesem Fall handelt es sich bei den Fasern der Verstärkungsmatte um Glasfasern. Die Verstärkungsmatte kann alternativ oder zusätzlich Fasern aus Polyester, Polyamid oder Nylon aufweisen. Denkbar ist auch der Einsatz von Naturfasern. Die Fasern können eine praktisch unbegrenzte Länge wie Endlosfasern aufweisen. Sie können auch als Faserstücke mit nur geringer Länge (beispielsweise kleiner als 3 cm) ausgebildet sein.The reinforcement mat can be a glass fiber mat. In this case, the fibers of the reinforcement mat are glass fibers. The reinforcement mat can alternatively or additionally have fibers made of polyester, polyamide or nylon. The use of natural fibers is also conceivable. The fibers can have a practically unlimited length, such as continuous fibers. They can also be designed as pieces of fiber with only a small length (for example less than 3 cm).
Die Verstärkungsmatte kann ein Vlies, ein Gewebe, ein Gestricke oder ein Gelege umfassen. Unter einem Gewebe wird ein textiles Flächengebilde aus sich kreuzenden Kett- und Schußfäden verstanden, die miteinander verwebt sind. Bei einem Gelege liegen ein oder mehrere Fadensysteme verschiedener Orientierungsrichtungen übereinander, wobei die Kreuzungspunkte vorzugsweise fixiert sind. Vliese sind nicht gewebte Flächengebilde, deren Herstellung mit statistisch ungeordneten Fasern erfolgt. Ein Gestrick stellt ein textiles Flächengebilde dar, das aus einem oder mehreren Fadensystemen durch Maschenbildung erzeugt wird.The reinforcement mat can comprise a fleece, a woven fabric, a knitted fabric or a scrim. A fabric is understood to be a flat textile structure made of crossing warp and weft threads which are interwoven. In the case of a scrim, one or more thread systems of different orientation directions lie on top of one another, the crossing points preferably being fixed. Nonwovens are non-woven fabrics which are manufactured with randomly disordered fibers. A knitted fabric is a flat textile structure that is produced from one or more thread systems through loop formation.
Zur Fixierung der Fasern kann die Verstärkungsmatte ein Bindemittel aufweisen, wobei das Bindemittel vorzugsweise auch zur Befestigung der Verstärkungsmatte an die Funktionsschicht verwendet wird. Die Fasern können mit dem Bindemittel, das vorzugsweise ein polymeres Bindemittel ist, getränkt oder umhüllt sein, wobei insbesondere bei einem Gelege die Kreuzungspunkte mit diesem Bindemittel fixiert werden. Bei dem polymeren Bindemittel kann es sich um ein duroplastisches oder thermoplastisches Material handeln.To fix the fibers, the reinforcement mat can have a binding agent, the binding agent preferably also being used to attach the reinforcing mat to the functional layer. The fibers can be soaked or coated with the binding agent, which is preferably a polymeric binding agent, the crossing points being fixed with this binding agent, particularly in the case of a scrim. The polymeric binder can be a thermoset or thermoplastic material.
Vorzugsweise ist der Kunststoffkern aus Polyurethan. Durch den Kunststoffkern aus Polyurethan lässt sich ein Bodenbelag bereitstellen, der günstige Eigenschaften bezüglich Trittschalldämmung, Gehkomfort, Elastizität und Flexibilität aufweist. Polyurethan lässt sich zudem auf Basis von nachwachsenden Rohstoffen wie etwa Rizinusöl frei von jeglichen schädlichen Zusatzstoffen wie etwa Weichmacher, Formaldehyd, Schwermetallen oder dergleichen herstellen. Für den Kunststoffkern können auch andere Materialien wie PVC, Polyethylen oder Polypropylen eingesetzt werden.The plastic core is preferably made of polyurethane. The plastic core made of polyurethane makes it possible to provide a floor covering that has favorable properties in terms of impact sound insulation, walking comfort, elasticity and flexibility. Polyurethane can also be produced on the basis of renewable raw materials such as castor oil, free of any harmful additives such as plasticizers, formaldehyde, heavy metals or the like. Other materials such as PVC, polyethylene or polypropylene can also be used for the plastic core.
Der Kunststoffkern kann mit Füllstoffen, vorzugsweise mit mineralischen Füllstoffen wie Sand oder Kreide, gefüllt sein. Dadurch lässt sich die Dichte des Kunststoffkerns und die mechanischen und akustischen Eigenschaften des Kunststoffkerns einstellen. Die Dichte des Kunststoffkerns kann somit Werte annehmen, die deutlich über der Dichte des verwendeten Kunststoffs liegen. In einem Ausführungsbeispiel beträgt die Dichte des Kunststoffkerns mehr als 1,5 oder gar 1,8 g/cm3. Die Dichte des Kunststoffkerns kann auch Werte kleiner als 1,5 g/cm3 annehmen, beispielsweise von 0,9 bis 1,5 g/cm3. In einem Ausführungsbeispiel handelt es sich hier um einen Kunststoffkern mit geschäumten Kunststoff und mit Füllstoffen.The plastic core can be filled with fillers, preferably with mineral fillers such as sand or chalk. This allows the density of the plastic core and the mechanical and acoustic properties of the plastic core to be adjusted. The density of the plastic core can thus assume values that are significantly higher than the density of the plastic used. In one embodiment, the density of the plastic core is more than 1.5 or even 1.8 g / cm 3 . The density of the plastic core can also assume values less than 1.5 g / cm 3 , for example from 0.9 to 1.5 g / cm 3 . In one embodiment, this is a plastic core with foamed plastic and with fillers.
Die Dicke des Kunststoffkerns kann 0,5 bis 10 mm, vorzugsweise 0,9 bis 4 mm betragen. Die Gesamtdicke des Bodenbelags kann 1 bis 12 mm, vorzugsweise 1,5 bis 5 mm betragen.The thickness of the plastic core can be 0.5 to 10 mm, preferably 0.9 to 4 mm. The total thickness of the floor covering can be 1 to 12 mm, preferably 1.5 to 5 mm.
Auf einer dem Kunststoffkern abgewandten oder oberen Seite der Funktionsschicht kann wenigstens eine weitere Schicht vorgesehen sein. Bei dieser weiteren Schicht kann es sich beispielsweise um eine Klebstoffschicht handeln, die durch eine abziehbare Schutzfolie abgedeckt sein kann. So lässt sich der erfindungsgemäße Bodenbelag als selbstklebende Unterlegematte verwenden, auf die dann ein weiterer Bodenbelag verlegt werden kann.At least one further layer can be provided on a side of the functional layer facing away from the plastic core or on the upper side. This further layer can be, for example, an adhesive layer that can be covered by a removable protective film. Thus, the floor covering according to the invention can be used as a self-adhesive underlay mat, on which a further floor covering can then be laid.
Alternativ kann es sich bei dieser weiteren Schicht auch um eine transparente Verschleißschicht handeln, die die Funktionsschicht von oben vor äußeren Einwirkungen schützt. Beispielsweise kann in diesem Ausführungsbeispiel die Funktionsschicht ein Dekorpapier mit einem Dekormuster sein, das durch die transparente Verschleißschicht von oben sichtbar ist.Alternatively, this further layer can also be a transparent wear layer that protects the functional layer from external influences from above. For example, in this exemplary embodiment, the functional layer can be a decorative paper with a decorative pattern that is visible from above through the transparent wear layer.
An der Unterseite des Kunststoffkerns kann eine rückseitige Funktionsschicht angeordnet sein. Diese rückseitige Funktionsschicht kann die Funktion einer Gegenzugschicht aufweisen, durch die ein Verformen des Bodenbelags aus seiner Hauptebene heraus (Schüsseln) vermieden wird. Die rückseitige Funktionsschicht kann alternativ oder zusätzlich die Funktion einer Dämpfungsschicht aufweisen. Auch ist denkbar, dass die rückseitige Funktionsschicht ein Selbstklebefilm ist, um den erfindungsgemäßen Bodenbelag auf einen darunterliegenden Unterboden oder Estrich zu kleben. Die rückseitige Funktionsschicht kann somit ihrerseits auch mehrschichtig aufgebaut sein. Im Ausführungsbeispiel des Selbstklebefilms kann die Funktionsschicht eine Trägerfolie, eine auf die Trägerfolie aufgebracht Klebstoffschicht und eine abziehbare Schutzfolie umfassen.A rear functional layer can be arranged on the underside of the plastic core. This functional layer on the back can have the function of a backing layer, by means of which a deformation of the floor covering out of its main plane (bowls) is avoided. The functional layer on the rear side can alternatively or additionally have the function of a damping layer. It is also conceivable that the functional layer on the back is a self-adhesive film in order to glue the floor covering according to the invention to an underlying sub-floor or screed. The functional layer on the rear side can therefore also have a multilayer structure. In the exemplary embodiment of the self-adhesive film, the functional layer can include a carrier film, an adhesive layer applied to the carrier film and a removable protective film.
Der erfindungsgemäße Bodenbelag kann als aufrollbare und/oder faltbare Bahnware ausgeführt sein. Auch kann der erfindungsgemäße Bodenbelag in Form eines Fußbodenpaneels ausgebildet sein, das vorzugsweise an wenigstens zwei Kanten Verbindungsprofile zum Verbinden mit anliegenden Fußbodenpaneelen gleicher Bauform aufweist. Die Verbindungsprofile können Nut und Feder aufweisen. Sie können auch Verriegelungssysteme aufweisen, so dass verbundene Verbindungsprofile in horizontaler und vertikaler Richtung miteinander verriegelt sind. Vorzugsweise sind die Verbindungsprofile vollständig in den Kunststoffkern eingeformt, beispielsweise durch Fräsen. An den zwei Kanten können auch ein stufenförmiger Überstand bzw. komplementär dazu eine stufenfömige Auflage vorgesehen sein, so dass sich zwei benachbarte Fußbodenpaneele bei Ausbildung einer ebenen Fußbodenoberfläche stufenweise überlappen.The floor covering according to the invention can be designed as rollable and / or foldable web material. The floor covering according to the invention can also be designed in the form of a floor panel, which preferably has connecting profiles on at least two edges for connecting to adjacent floor panels of the same design. The connecting profiles can have tongue and groove. They can also have locking systems so that connected connecting profiles are locked to one another in the horizontal and vertical directions. The connecting profiles are preferably completely molded into the plastic core, for example by milling. A step-shaped overhang or, in addition, a step-shaped support can also be provided on the two edges, so that two adjacent floor panels overlap in steps when a flat floor surface is formed.
Mit Hilfe eines Verfahrens, welches im Folgenden beschrieben wird, lässt sich der erfindungsgemäße Bodenbelag herstellen.The floor covering according to the invention can be produced with the aid of a method which is described below.
Das Verfahren zum Herstellen des Bodenbelags mit dem Kunststoffkern mit seiner Oberseite und Unterseite, wobei an der Oberseite die Funktionsschicht und die Verstärkungsmatte angeordnet sind, welche die Fasern und dazwischen angeordnete Zwischenräume aufweist, umfasst die Bereitstellung der vorproduzierten Einheit, wobei die Verstärkungsmatte an die Funktionsschicht befestigt wird. Diesem Verfahrensschritt folgt das Verbinden der vorproduzierten Einheit mit dem Kunststoffkern, wobei die vorproduzierte Einheit so zur Oberseite des Kunststoffkerns ausgerichtet wird, dass die Verstärkungsmatte zwischen der Oberseite des Kunststoffkerns und der Funktionsschicht angeordnet ist. Der Kunststoffkern wird dann mit der vorproduzierten Einheit verbunden, wobei der Kunststoffkern sowohl mit der Verstärkungsmatte als auch unmittelbar mit der Funktionsschicht verbunden wird. Die unmittelbare Verbindung des Kunststoffkerns mit der Funktionsschicht wird ermöglicht durch die Zwischenräume der Verstärkungsmatte, wobei die für die Verbindung von Kunststoffkern und Funktionsschicht verwendeten Verbindungsmittel durch die Zwischenräume der Verstärkungsmatte hindurch greifen.The method for producing the floor covering with the plastic core with its upper side and lower side, with the functional layer and the reinforcement mat being arranged on the upper side, which has the fibers and intermediate spaces, comprises the provision of the pre-produced unit, the reinforcement mat being attached to the functional layer becomes. This process step is followed by connecting the pre-produced unit to the plastic core, the pre-produced unit being aligned with the top of the plastic core so that the reinforcement mat is arranged between the top of the plastic core and the functional layer. The plastic core is then connected to the pre-produced unit, the plastic core being connected both to the reinforcement mat and directly to the functional layer. The direct connection of the plastic core to the functional layer is made possible by the interspaces of the reinforcement mat, the connecting means used to connect the plastic core and the functional layer reaching through the interspaces of the reinforcement mat.
Zur Fixierung der Fasern der Verstärkungsmatte kann das bereits oben beschriebene Bindemittel eingesetzt werden, das auch dazu genutzt werden kann, die Verstärkungsmatte an der Funktionsschicht zu befestigen. Die Verstärkungsmatte kann mithilfe von Druck und/oder Wärmeeintrag mit der Funktionsschicht verbunden werden (beispielsweise durch Kalandrieren). In einem Ausführungsbeispiel, bei dem die Verstärkungsmatte ein Gelege umfasst, dessen Fasern und Kreuzungspunkte mit einem thermoplastischen Bindemittel fixiert sind, können Verstärkungsmatte und Funktionsschicht durch das Kalandrieren miteinander verbunden werden. Die Temperatur beim Kalandrieren sollte dann so eingestellt sein, dass das thermoplastische Bindemittel erweicht. Es kann dann als Klebemittel zwischen den Fasern der Verstärkungsmatte und der Funktionsschicht wirken. Danach wird das thermoplastische Bindemittel wieder hart, so dass die derart vorproduzierte Einheit nun mit dem Kunststoffkern verbunden werden kann.To fix the fibers of the reinforcement mat, the binder already described above can be used, which can also be used to attach the reinforcement mat to the functional layer. The reinforcement mat can be connected to the functional layer with the aid of pressure and / or heat input (for example by calendering). In one embodiment in which the reinforcement mat comprises a scrim, the fibers and crossing points of which are fixed with a thermoplastic binding agent, the reinforcement mat and the functional layer can be connected to one another by calendering. The temperature during calendering should then be adjusted so that the thermoplastic binder softens. It can then act as an adhesive between the fibers of the reinforcement mat and the functional layer. The thermoplastic binding agent then hardens again so that the unit produced in advance can now be connected to the plastic core.
Die Verstärkungsmatte kann zum Herstellen der vorproduzierten Einheit an die Funktionsschicht gelegt werden, wenn sich das Bindemittel in einem flüssigen oder pastösen Zustand befindet. Beispielsweise können die Fasern des Geleges mit einem noch nicht ausgehärteten duroplastischen Bindemittel wie Polyurethan benetzt werden. Das derart benetzte Gelege wird dann auf die Funktionsschicht gelegt. Das noch flüssige Bindemittel fixiert bei seinem Aushärten einerseits die Fasern des Geleges untereinander und sorgt aber auch für eine feste Verbindung der Fasern an der Funktionsschicht. The reinforcement mat can be placed on the functional layer to produce the pre-produced unit if the binding agent is in a liquid or pasty state. For example, the fibers of the scrim can be wetted with a not yet hardened thermosetting binder such as polyurethane. The scrim so wetted is then placed on the functional layer. The binder, which is still liquid, fixes the fibers of the scrim to one another as it hardens and also ensures that the fibers are firmly bonded to the functional layer.
Nach erfolgter Aushärtung des Bindemittels erfolgt dann nachgeschaltet die Verbindung mit dem Kunststoffkern. Die Herstellung des Geleges mit dem Fixieren des Bindemittels wird somit mit dem Schritt des Befestigens des Geleges an der Funktionsschicht zusammengelegt. Das Verbinden der Verstärkungsmatte mit der Funktionsschicht und das Verbinden von dem Kunststoffkern mit dem Verbund bestehend aus Funktionsschicht und Verstärkungsmatte sind erfindungsgemäß voneinander getrennt.After the binding agent has hardened, the connection with the plastic core takes place downstream. The production of the scrim with the fixing of the binding agent is thus combined with the step of attaching the scrim to the functional layer. The connection of the reinforcement mat to the functional layer and the connection of the plastic core to the composite consisting of the functional layer and reinforcement mat are separated from one another according to the invention.
Zur Herstellung des Kunststoffkerns kann ein Kunststoffmaterial verwendet werden, das auf die vorgefertigte Einheit von Funktionsschicht und Verstärkungsmatte in flüssiger Form aufgetragen wird. Das flüssige Kunststoffmaterial tritt dabei durch die Zwischenräume der Verstärkungsmatte und geht somit eine Verbindung mit der Funktionsschicht und den Fasern der Verstärkungsmatte ein. Das Kunststoffmaterial in flüssiger Form ist in einem bevorzugten Ausführungsbeispiel flüssiges Polyurethan bzw. eine flüssige Mischung aus den Komponenten (Polyole und Isocyanate), aus denen sich Polyurethan bildet.To produce the plastic core, a plastic material can be used that is applied in liquid form to the prefabricated unit of functional layer and reinforcement mat. The liquid plastic material passes through the spaces in the reinforcement mat and thus forms a connection with the functional layer and the fibers of the reinforcement mat. In a preferred exemplary embodiment, the plastic material in liquid form is liquid polyurethane or a liquid mixture of the components (polyols and isocyanates) from which polyurethane is formed.
Als besonders vorteilhaft hat sich herausgestellt, dass durch das erfindungsgemäße Verfahren und der dadurch erreichbaren guten Haftung zwischen der Funktionsschicht, der Verstärkungsmatte und dem Material des Kunststoffkerns auf den Einsatz von zusätzlichem Klebstoff, der üblicherweise unmittelbar vor dem Auftragen des flüssigen Polyurethan auf die Funktionsschicht und der darauf angeordneten Verstärkungsmatte ausgetragen wird, verzichtet werden kann. Dies reduziert nicht nur die Materialkosten, sondern vermeidet auch die mit dem Klebstoffauftrag verbundenen Probleme wie die Blasenbildung in dem Polyurethan-Material. Die Erfindung führt somit zu einem Bodenbelag mit besonders homogenen Kunststoffkern ohne unerwünschte Unregelmäßigkeiten.It has been found to be particularly advantageous that the method according to the invention and the good adhesion that can be achieved between the functional layer, the reinforcement mat and the material of the plastic core result in the use of additional adhesive, which is usually applied immediately before the liquid polyurethane is applied to the functional layer and the Reinforcing mat arranged thereon is discharged, can be dispensed with. This not only reduces material costs, but also avoids the problems associated with the application of the adhesive, such as the formation of bubbles in the polyurethane material. The invention thus leads to a floor covering with a particularly homogeneous plastic core without undesirable irregularities.
Anhand eines in der Zeichnung dargestellten Ausführungsbeispiels soll die Erfindung näher erläutert werden. Es zeigen:
-
1 schematisch einen mehrschichtigen Bodenbelag gemäß der Erfindung; und -
2 eine vorproduzierte Einheit als Teil desBodenbelags von 1 .
-
1 schematically a multilayer floor covering according to the invention; and -
2 a pre-fabricated unit as part of the flooring of1 .
An einer Unterseite
An einer dem Kunststoffkern
Zur Fixierung der Fasern
Die Anhaftung der Verstärkungsmatte
Zur Herstellung des Bodenbelags
Ein Verhältnis des Anteils der Fläche der Funktionsschicht (PET-Folie
Bei einem Gelege, bei dem der Abstand benachbarter Fasern groß sei kann, nimmt das Verhältnis vergleichsweise kleine Werte an, beispielsweise 2 bis 6 %. Bei einem Vlies können pro Flächeneinheit viele Fasern auf der PET-Folie
BezugszeichenlisteList of reference symbols
- 11
- Bodenbelag/Unterlegematte Floor covering / mat
- 1010
- KunststoffkernPlastic core
- 1111
- OberseiteTop
- 1212
- Unterseite bottom
- 2020th
- vorproduzierte/vorgefertigte Einheitpre-produced / prefabricated unit
- 2121st
- Funktionsschicht/PET-FolieFunctional layer / PET film
- 2222nd
- VerstärkungsmatteReinforcement mat
- 2323
- Faserfiber
- 2424
- LängsfaserLongitudinal fiber
- 2525th
- QuerfaserTransverse fiber
- 2626th
- KreuzungspunktCrossing point
- 2727
- Zwischenraum Space
- 4040
- rückseitige Funktionsschicht functional layer on the back
- 5050
- KlebeschichtAdhesive layer
- 5151
- SchutzfolieProtective film
ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDED IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant was generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.
Zitierte PatentliteraturPatent literature cited
- EP 3168388 A1 [0002]EP 3168388 A1 [0002]
- DE 102017100735 A1 [0003]DE 102017100735 A1 [0003]
Claims (8)