DE202006017700U1 - Paint in the form of a paste comprises an aqueous dispersion of a styrene/acrylate ester copolymer to which inorganic pigments and a solution of an acrylic resin in toluene or xylene have been added - Google Patents
Paint in the form of a paste comprises an aqueous dispersion of a styrene/acrylate ester copolymer to which inorganic pigments and a solution of an acrylic resin in toluene or xylene have been added Download PDFInfo
- Publication number
- DE202006017700U1 DE202006017700U1 DE202006017700U DE202006017700U DE202006017700U1 DE 202006017700 U1 DE202006017700 U1 DE 202006017700U1 DE 202006017700 U DE202006017700 U DE 202006017700U DE 202006017700 U DE202006017700 U DE 202006017700U DE 202006017700 U1 DE202006017700 U1 DE 202006017700U1
- Authority
- DE
- Germany
- Prior art keywords
- paints
- pasty
- xylene
- solvent
- solvents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
Pastöse Anstrichstoffe für innen und außen ist eine Farbe die aus wässriger Dispersion eines Styrol- Acrylsäuerester- Copolymerisates erfindungsgemäß mit einrühren durch höhere Geschwindigkeit und beimischen von Acrylhaltigem Lösemittel in gewissem Prozentsatz hergestellt wird. Das heißt, wässrige Dispersion wird im Grunde genommen zunächst durch einen physikalischen Vorgang verbunden mit Lösemittel und daraus resultierende Reaktion ist chemische Plastifizierung. Erfindungsgemäß ist das, dass einfachste Prinzip auf diese Art einen elastischen Kunstharz zu erstellen. Wenn jetzt Farbkonzentrat leicht eingerührt wird, dann ist das Ergebnis einer Farblasur in durchsichtiger Form. Farbe ist relativ dickflüssig und kann durch beimischen von Wasser so wie man sich wünscht eingestellt werden. Dieses System eignet sich insbesondere für Holzlasuren von Möbeln, Balken und allen Hölzer innen und außen, die nicht mehr nachlackiert werden brauchen.Pasty paints for inside and outside is a color of watery Dispersion of a styrene-acrylic acid ester Copolymerisin with stirring by higher Speed and mixing of acrylic solvent produced in a certain percentage. That is, aqueous dispersion is basically initially through a physical process associated with solvent and the resulting reaction is chemical plasticization. According to the invention, the simplest principle in this way is an elastic synthetic resin to create. If color concentrate is stirred in slightly, then the result is a color glaze in a transparent form. colour is relatively thick and can be adjusted by mixing water as desired become. This system is particularly suitable for wood stains of furniture, beams and all woods inside and outside, that do not need to be repainted.
Erfindungsgemäß wird für Wand und Fassadenfarben folgendes vorgeschlagen: Zunächst wird in den Grundstoff Titandioxid Spezialmischer dispergiert, dann wird anteilig Talkum und Schlämmkreide mit gleichem Rührwerk untergemischt und dann erst wird in die angerührte Masse mit hoher Geschwindigkeit und einfachem Rührwerk Acrylhaltiger Lösemittelanteil eingerührt. Sofort ist zu ersehen das jetzt durch chemische Reaktion wasserhaltige Dispersion sehr dick quasi zähflüssig, ja sogar ein Gelprodukt entstanden ist. Dieser Vorgang ist die Plastifizierung von Styrol- Acrylsäuerester- Copolymerisates.According to the invention for wall and Facade paints suggested the following: First, in the base material Titanium dioxide specialty mixer dispersed, then proportionally talc and whiting with same agitator mixed in and then only in the stirred mass at high speed and simple agitator Acrylic solvent content stirred. Immediately you can see that now by chemical reaction hydrous Dispersion very thick, almost viscous, yes even a gel product has been created. This process is the plasticization of Styrene acrylic acid ester Copolymer.
Dieses Produkt ist jetzt eine weiße Spezial Kunstharz Farbe, die in solchem Zustand fast uneingeschränkt lagerfähig ist. Das heißt, dass in diesem Zustand und bei geschlossenem Gefäß keine physikalischen und chemischen Ereignisse außer Kondensbildung mehr folgen. Erst nach der Anwendung folgen zwei physikalische Ereignisse und ein chemischer Vorgang, der bei einer Anwendungstemperatur unter 20°C zwischen 8 und 10 Tage dauert.This Product is now a white one Special synthetic resin color, which is almost completely storable in such condition. This means, that in this state and with closed vessel no physical and chemical events except Condensation follow more. Only after the application follow two physical Events and a chemical process taking place at an application temperature 20 ° C between 8 and 10 days lasts.
Zur Erklärung ist das erste physikalische Ereignis erst in freier Atmosphäre möglich, dabei ist verdunsten von Lösemittel und Bildung von Acrylvergitterung in Styrol eingreifend vollzogen. Das zweite Ereignis ist erst in freier Atmosphäre möglich und dabei ist verdunsten von vorhandenen Wasseranteilen weniger als 10% und Bildung von Styrolvergitterung Acryleingreifend vollzogen. Dritter Vorgang ist chemische Ausarbeitung, wobei Anstrich erst zwischen 8 und 10 Tagen vollständig aushärtet. So ist Plastifizierung erst in freier Atmosphäre und nach gewisser Zeit vollständig abgeschlossen, wobei jetzt erst dreifache Vergitterung zustande gekommen ist. Bei der ersten Plastifizierung wird größter Teil von Wasseranteilen für die Umwandlung, dass heißt für den chemischen Prozess verwendet. Verbleibende Wasseranteile betragen danach maximal 10% und ist bei dem Anstrich deutlich zu erkennen das Farbe eine Struktur, die bei Anstrich entsteht, auch nach dem austrocknen beibehält. Das heißt, dass fast kein Materialverlust entsteht. So sind auch hier Vorteile gegenüber Handelsüblichen Dispersionsfarben so zu verstehen, dass Handelsübliche Farben den Wasseranteil als Materialverlust bilden.to statement the first physical event is possible only in free atmosphere, thereby is evaporation of solvents and formation of acrylic grating in styrene completed. The second event is possible only in a free atmosphere and it evaporates of existing water contents less than 10% and formation of styrene grating acrylic intervening completed. Third operation is chemical work-up, with painting only fully hardened between 8 and 10 days. So is plasticization only in a free atmosphere and after a while completely completed, now only three times grating concluded has come. The first plasticization becomes the biggest part of water shares for the transformation, that is for the used chemical process. Remaining water content amount then a maximum of 10% and is clearly visible in the painting the paint a structure that arises when painting, even after the dehydrates. This means, that almost no material loss occurs. So here are benefits across from Use commercially available To understand emulsion paints so that commercial colors the water content as a loss of material.
Erfindungsgemäß kann eine Grundrezeptur ausreichen eine Farbe für Alles herzustellen. Jedoch ist es möglich mit Hilfsrezepturen Eigenschaften von der Grundrezeptur aufzuwerten.According to the invention, a Basic recipe sufficient to make a color for everything. However, that is it possible with auxiliary formulations to upgrade properties of the basic recipe.
Anstrich selbst ist bei Verarbeitungstemperatur von 15°C nach ca. 30 Minuten trocken. Das heißt, dass Anstrichfläche relativ schnell physikalisch trocken ist und durch Wasser zum Beispiel aufkommender Regen nicht mehr angegriffen werden kann. Nach Ausdünstung von Lösemittel ist das Produkt in keinem Fall gefährlich und toxisch. Reste von Farbe können auf einer Plastikmatte ausgekippt werden, dann trocknen lassen und endstehender Kunstharzklumpen kann in Restmüll entsorgt werden. In Grunde ist es so das nach chemischen Entprozess Farbpartikeln angeknabbert werden können und keine Gefahr am Leib und Leben verursachen. Es folgen auch keinerlei Ausdünstungen von irgendwelchen Stoffen.painting itself is dry at processing temperature of 15 ° C after about 30 minutes. It means that All surfaces Physically dry relatively quickly and by water for example emerging rain can no longer be attacked. After exhalation of solvent In no case is the product dangerous and toxic. Remains of Color can be dumped on a plastic mat, then let it dry and Residual synthetic resin lump can be disposed of as residual waste. Basically is it so nibbled after chemical Entprozess color particles can be and cause no danger to life and limb. There are no consequences exhalations of any substances.
Farbe selbst wird nach endgültiger chemischer Reaktion extrem fest, ja fast unzerstörbar. Erfindungsgemäße Eigenschaften sind insbesondere das Farbe atmungsaktiv ist, vergleichbar mit Latexhandschuh, dass Farbe CO2, Nikotin und UV fest ist, dass Farbe Wasserabweißend ist, dass Farbe mit dem Untergrund bei Temperatureinfluss elastisch wird und sich dehnt und bei Kälte wieder schrumpft ohne dabei Risse zu bilden. Bei Anstrich von Heizkörpern kann Heizkörper aufgewärmt werden und somit wird der chemische Prozess beschleunigt, wobei dann der Anstrich richtig eingebrannt wird. Jetzt wird auch erkennbar das bei Anstrich von Blechteilen wie Abwasserrohre, Dachrinnen, Blechdächern Anstrich erfolgen kann und auch wenn erst nach einiger Zeit Sonne die Blechteile aufwärmt wird die Einbrennung durchgeführt.colour itself becomes final chemical reaction extremely strong, almost indestructible. Inventive properties In particular, the color is breathable, comparable to latex glove, that color is CO2, nicotine and UV solid, that color is water-repellent, that the color becomes elastic with the surface under the influence of temperature and stretches and in cold weather again it shrinks without forming cracks. When painting of radiators can radiator warmed up and thus the chemical process is accelerated, in which case the painting is properly baked. Now it becomes recognizable when painting sheet metal parts such as sewer pipes, gutters, tin roofs Painting can take place and even if only after some time sun the sheet metal parts warm up the burn-in is carried out.
Weitere Vorteile sind in der Vorreinigung einer Fassade. Reinigung ist nur dann notwendig wenn Moos oder Grünspann auf der Wand ist. Staub und geringfügiges Fett von Abgasen können ohne Vorreinigung gestrichen werden, da Staub und geringe Fettpartikeln in die Farbmasse eingebunden werden. Sicherheitsrelevant insbesondere für Anstriche in hellen Farben von Tunneln, da dann Übergang von und zum Tageslicht für das Auge von Vorteil ist.Further Advantages are in the pre-cleaning of a facade. Cleaning is only then necessary if moss or Grünspann is on the wall. Dust and minor fat of exhaust gases can without Pre-cleaning should be deleted as dust and low fat particles be integrated into the paint mass. Security relevant in particular for paintings in bright colors of tunnels, since then transition from and to the daylight for the Eye is beneficial.
Von besserer Sicht ganz abzusehen ist auch die Unfallgefahr wesentlich verringert.From better vision completely foreseeable, the risk of accidents is essential reduced.
So sind nur einige Beispiele aufgeführt um die erfindungsgemäßen Vorschläge zu verstehen. Es ist ein Produkt das eigentlich rund um das Haus angewendet werden kann. Hervorragende Haftung bildet die Farbe auf Fassade, Gipswand, allerlei Putze, Beton, Holz, Glas, Tapete, Betonboden, grundierte Metalle u.s.w. Anstrichflächen werden gleichzeitig tiefgrundiert. Da Produkt quasi unzerstörbar ist, ist die Haltbarkeit bis zu 50 Jahre möglich und gerade bei Hausfassade ist es wichtig, dass die Haussubstanz durch Witterungseinflüsse nicht angegriffen wird.So only a few examples are listed to understand the proposals of the invention. It is a product that is actually used around the house can. Outstanding adhesion is the color on facade, gypsum wall, all kinds of plaster, concrete, wood, glass, wallpaper, concrete floor, primed metals etc. paint surfaces are simultaneously deep-primed. Because product is virtually indestructible, Shelf life is possible up to 50 years and just at the house facade It is important that the house substance is not affected by the weather is attacked.
Ein weiterer Vorteil ist, dass auf eine Walze aufgenommene Farbe nicht tropft.One Another advantage is that recorded on a roller paint is not drips.
Erfindungsgemäß erstelltes Produkt hat auch geringfügige Nacheile. Bearbeitungswerkzeuge können nach geringfügiger Antrocknung nicht mehr gereinigt werden.Created according to the invention Product also has minor Hot pursuit. Machining tools can after slight drying no longer be cleaned.
Grundrezeptur für 10 Liter Gebinde in weiß
- 6,4 Liter wässrige Dispersion eines Styrol- Acrylsäuerester- Copolymerisates
- 2 Liter Titandioxid
- 200 Gramm Talkum
- 200 Gramm Schlämmkreide
- 1,2 Liter Akrylhaltiges Lösemittel
- 6.4 liters of aqueous dispersion of a styrene-Acrylsäuerester- copolymer
- 2 liters of titanium dioxide
- 200 grams of talc
- 200 grams of whiting
- 1.2 liters of acrylic-containing solvent
Claims (4)