DE2005549C - Process for the production of black powder flour - Google Patents
Process for the production of black powder flourInfo
- Publication number
- DE2005549C DE2005549C DE19702005549 DE2005549A DE2005549C DE 2005549 C DE2005549 C DE 2005549C DE 19702005549 DE19702005549 DE 19702005549 DE 2005549 A DE2005549 A DE 2005549A DE 2005549 C DE2005549 C DE 2005549C
- Authority
- DE
- Germany
- Prior art keywords
- black powder
- mill
- jet mill
- powder
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Bei der Herstellung von Schwarzpulver besteht der Während dieser Maßnahme hat die Reibung zwischen zeitraubendste Teil des Verfahrens in der Pulverisie- den einzelnen Körnern zur Folge, daß die Ränder des rung der drei Rohmaterialien Kaliumnitrat, Schwefel Schwarzpulvers abgeschliffen werden, so daß die und Aktivkohle sowie in dem Vermischen und Ver- Körner runder und glatter werden. Dies nennt man mahlen dieser Rohmaterialien. Dieser letzte Teil des 5 Glätten. Die Dauer des Glättens hängt von dem geVerfahrens wurde als Einmengung bezeichnet. Das wünschten Abriebgrad des fertigen Schwarzpulvers ab. nach der Einmengung erhaltene Produkt wird Schwarz- An das Glätten schließt sicfi im allgemeinen ein mehlpulver genannt. Die zwei Verfahrensstufen der Fertigpolieren an. Dies erfordert 1 bis 2 Stunden und Pulverisierung und Einmengung sind jedoch nicht wird in der gleichen Trommel durchgeführt, und zwar nur zeitraubend, sondern erfordern auch Raum und io anschließend an sowie in der gleichen Weise wie das sind teuer. Infoige der Explosionsgefahr wurde die Glätten. Der einzige Unterschied besteht darin, daß 0,1 Pulverisierung der Rohmaterialien getrennt durchge- bis 1,0% feinpulverisierter Graphit zugesetzt werden, führt, beispielsweise wurden Kaliumnitrat sowie Während dieses Teiles des Polierens setzt sich derDuring the production of black powder there is friction between Most time consuming part of the process in pulverizing the individual grains results in the edges of the tion of the three raw materials potassium nitrate, sulfur black powder are abraded so that the and activated carbon, as well as in the mixing and graining of grains become rounder and smoother. This is called grind these raw materials. This last part of the 5 smoothing. The duration of smoothing depends on the process was referred to as constriction. The desired degree of abrasion of the finished black powder. product obtained after incorporation turns black. Smoothing generally includes called flour powder. The two process stages of finish polishing. This takes 1 to 2 hours and However, pulverization and blending are not carried out in the same drum, namely just time consuming but also require space and io following on as well as in the same way as that are expensive. Infoige of the risk of explosion was the smoothing. The only difference is that 0.1 Pulverization of the raw materials separately by adding up to 1.0% of finely pulverized graphite, leads, for example, were potassium nitrate as well as during this part of the polishing the
Schwefel und Aktivkohle getrennt pulverisiert Ferner Graphit als dünner Film auf der Außenseite der kann man Kaliumnitrat mit etwas Aktivkohle getrennt 15 Schwarzpulverkörner ab und macht sie glänzend, g!att sowie Schwefel und den Rest der Aktivkohle getrennt und elektrisch etwas leitender sowie gegen Feuchtigpulverisieren. keit etwas unempfindlicher. Während des PolierensSulfur and activated carbon are powdered separately. Furthermore, graphite as a thin film on the outside of the you can separate 15 black powder grains from potassium nitrate with a little activated charcoal and make them shiny, g! att as well as sulfur and the rest of the activated carbon separated and electrically somewhat more conductive as well as against moisture pulverization. something less sensitive. While polishing
Die Pulverisierung wurde beispielsweise in Kugel- steigt die Temperatur in der Schwarzpulvermasse mühlen, Nadelmühlen oder Hammermühlen durchge- infolge der Reibung, der die Körner unterzogen werführt. D.\s Vermählen unter Verwendung von Kugel- 20 den,an.EswurdenTemperaturenbiszu70°Cgemessen. mühlen erfordert 6 bis 12 Stunden und dauert in einigeji Der Nachteil des Polierens besteht darin, daß es eine Fällen noch länger. Infolge der Explosionsgefahr sehr lange Zeit erfordert, so daß daher eine relativ wurde das Einmengen in kleinen Chargen durch- große Menge an Schwarzpulver in jeder Poliertrommel geführt, und zwar in Chargen bis zu ungefähr 100 kg, vorliegen muß. Beispielsweise hat eine Anlage für wobei man sich langsam laufender Spezialvorrichtun- 25 300 kg pro Stunde zur Voraussetzung, daß eine Menge gen bediente, von deneii Kugelmühlen, Gitteipoch- von bis zr 2700 kg Schwarzpulver in dem Poliergebäude vcrke oder Walzenmühlen erwähnt seien. Im ailge- zusammenkommt. Aus Sicherheitsgründen ist jedoch meinen dauerte die Einmengung 7 Stunden oder mehr eine derartige Menge äußerst unerwünscht. Andererpro Charge. Explosionsunfälle während der Ein- seits führt eine Erhöhung der Abriebgescnwindigkeit mengung v/aren nicht selten. 30 der Körner in notwendiger Weise zu einem gesteigertenThe pulverization was for example in ball- the temperature in the black powder mass rises mills, needle mills or hammer mills due to the friction that the grains subjected to. D. Milling using spherical 20 deniers, temperatures up to 70 ° C were measured. Milling takes 6 to 12 hours and takes a few times. The disadvantage of polishing is that it is a Cases even longer. As a result of the risk of explosion requires a very long time, so that therefore a relatively was blending in small batches through- large amount of black powder in each polishing drum performed, in batches of up to approximately 100 kg. For example, an attachment for with slow running special devices 25 300 kg per hour assuming that a lot gen served, from deneii ball mills, Gitteipoch- of up to 2700 kg black powder in the polishing building vcrke or roller mills may be mentioned. Come together on a long-term basis. However, for security reasons mine took 7 hours or more to mix, such an amount extremely undesirable. Other pro Batch. Explosion accidents during the one hand leads to an increase in the abrasion speed Mixing v / aren not uncommon. 30 of the grains necessarily increased to one
Der Begriff »Ei.imengung« wird nachstehend noch Erhitzen des Schwarzpulvers. Die Entzündungstemperanäiier
ei läutert, bisher war nicht recht klar, welche tür von Schwarzpulver beträgt ungefähr 3000C. Es
Vorgänge dieser Begrii. i-mfaßt. Es konnte jedoch liegt auf der Hand, daß man unterhalb dieser Grenze
durch Experimente gezeigt werden, daß darunter eine arbeiten muß, um den Sicherheitsbestimmungen zu
weitere Unterteilung der Rohmaterialien, insbesondere 35 entsprechen. Daher s;nd Einrichtungen zum Abkühlen
Aktivkohle, und natürlich auch ein Vermischen der während des Polierens erforderlich.
Rohmaterialien zu verstehen ist. Die Reaktivität der Ziel der Erfindung iii die Beseitigung der vorstehendThe term "egg mixture" will be used in the following to refer to the heating of black powder. The Entzündungstemperanäiier purifies egg, yet was not quite clear which door is of black powder about 300 0 C. It processes these Begrii. i-mfasst. However, it was obvious that below this limit it was shown by experiments that one of these had to work in order to comply with the safety regulations for further subdivision of the raw materials, in particular 35. Hence s ; nd facilities for cooling activated carbon, and of course mixing of the required during polishing.
Raw materials is to be understood. The reactivity of the object of the invention iii eliminating the above
Aktivkohle ist für die Wirkung eines Schwarzpulvers erwähnten Nachteile. Erfindungsgemäß werden die
von grundlegender Bedeutung. Bei einer hohen Reakti- Pulverisierung und Ehmengung durch eine einzige
vität wird ein stark und gleichmäßig wirkendes Schwarz- 40 Behandlung in einer schnell laufenden und kontinuierpulver
erhalten. Die Reaktivität der Aktivkohle hängt lieh arbeitenden Vorrichtung ersetzt,
von ihrem Gehalt an freien Radikalen ab. Dieser Ge- Das erSndungsgemäße Verfahren zur HerstellungActivated charcoal is one of the disadvantages mentioned for the effect of black powder. According to the invention, these are of fundamental importance. With a high reactivity and mixing through a single vity, a strong and evenly acting black treatment is obtained in a fast running and continuous powder. The reactivity of the activated carbon depends on the working device replaced,
on their free radical content. This production method according to the invention
halt steigt mit einer zunehmenden Unterteilung an. eines Schwarzpulvermehls aus den Rohmaterialien Dies konnte durch Messungen der Elektronenspin- Kaliumnitrat, Schwefel und Aktivkohle durch Verresonanz in Aktivkohle sowie in einem fertigen 45 mischen der Rohmaterialien in den entsprechenden Schwarzpulver gezeigt werden. Mengenverhältnissen, Entladung der Mischung unterhalt increases with an increasing subdivision. of a black powder meal from the raw materials This could be done by measuring the electron spin- potassium nitrate, sulfur and activated charcoal through resonance in activated carbon as well as in a finished 45 mix the raw materials in the appropriate Gunpowder will be shown. Proportions, discharge of the mixture under
Die weitere Verarbeitung des Schwarzpulvermehls Beschickung eines Aufgabetrichters ist dadurch gebesteht gewöhnlich aus den folgenden Stufen: kennzeichnet, daß über eine geeignete Zumessungsein-This enables the further processing of the black powder meal to be fed into a feed hopper usually made up of the following levels: indicates that a suitable assessment unit
richtung kontinuierlich eine konstante Menge Roh-direction continuously a constant amount of raw
Kompaktierung (Verpressen), ^0 malerialienmischung in eine bekannte, aus einer ring-Compaction (pressing), ^ 0 mixture of paints in a well-known, from a ring-
Zerkleinern förmigen Kammer mit tangentialen Einlassen fürCrushing shaped chamber with tangential inlets for
„.., ' Druckluft bestehenden Strahlmühle eingeführt, dort"..," compressed air introduced into existing jet mills there
•3IC^CI1· durch auf Überschallgeschwindigkeit gebrachte Luft• 3IC ^ CI1 · by air brought to supersonic speed
Polieren. vermählen und pulverisiert und anschließend in einemPolishing. ground and pulverized and then in one
55 Zyklon oder ähnlichen Einrichtung für eine mögliche55 cyclone or similar device for a possible
Das Polieren von Schwarzpulver wird gewöhnlich in weitere Verarbeitung gesammelt wird,
zwei Stufen eingeteilt, und zwar. Als Kohle wird zwar Aktivkohle eingesetzt, esThe polishing of black powder is usually collected in further processing,
divided into two stages, namely. Activated charcoal is used as charcoal, it
können aber auch andere Typen eines aktivierendenbut can also have other types of activating
1. Glätten und Kohlenstoffs verwendet werden.1. Smoothing and carbon are used.
2. Fertigbearbeiten. 60 Die Erfindung schafft ferner die Möglichkeit, das2. Finishing. 60 The invention also creates the possibility that
Polieren des Schwarzpulvers in einer kontinuierlichPolishing the black powder in a continuous way
Bisher wurde das Polieren in der folgenden Weise arbeitenden Vorrichtung durchzuführen, die dem TypHeretofore, polishing has been carried out in the following operating apparatus, of the type
durchgefüh-t: Eine bestimmte Menge Schwarzpulver ähnlich ist, welcher für die Pulverisierung eingesetztcarried out: A certain amount of black powder is similar to that used for pulverization
aus der Zerkleinerungsvorricntung wird in eine Rota- wird.the shredding device is turned into a rotary.
tionstrommel eingefüllt. Die Menge schwankt je nach 65 Zunächst sei der erste Teil des Verfahrens beschrie-tion drum filled. The amount fluctuates depending on the 65 First, the first part of the procedure is described.
der Produktionskapazität, sie liegt jedoch gewöhnlich ben.the production capacity, but it is usually ben.
zwischen 250 und 1500 kg pro Trommel. Diese Menge Ein Teil der Wirkung der Eirmengung besteht inbetween 250 and 1500 kg per drum. This amount. Part of the effect of the consolidation consists in
wird 3 bis 7 Stunden lang mit 12 bis 20 UpM rotiert. einer Einbettung von Schwefel und/oder Kaliumnitratis rotated at 12 to 20 rpm for 3 to 7 hours. an embedding of sulfur and / or potassium nitrate
3 43 4
in die Poren der Aktivkohle. Zur Erzielung dieser Wir- Stücken zerbrochen werden. Auf diese Weise werdeninto the pores of the activated carbon. To achieve these we- pieces are broken. Be that way
kung müssen alle drei Rohmaterialien in der einge- sie zu Teilchen mit Großen vermählen, die unterhalbIn order to achieve this, all three raw materials must be ground together into particles of the size below
setzten Mühle verarbeitet werden. 1 μ liegen können.put mill to be processed. 1 μ can be.
Natürlich versucht man auch, die anschließenden Die hohe Luftgeschwindigkeit wird in bekannterOf course, one also tries the subsequent The high air speed is known in
Stufen in der gleichen Weise durchzuführen, um die 5 Weise erzeugt, und zwar durch Durchleiten von unterCarry out stages in the same way to create the 5 ways, namely by passing through under
Wirtschaftlichkeit und Sicherheit zu erzielen, die bei Druck stehender Luft durch besonders geformte Düsen,To achieve economic efficiency and safety, the compressed air through specially shaped nozzles,
der Durchführung des ersten Teils des Verfahrens, d. h. worauf der Luft Gelegenheit gegeben wird, sich zuperforming the first part of the procedure, d. H. whereupon the air is given the opportunity to grow
beim Vermischen, Pulverisieren und Einmengen, mög- expandieren.when mixing, pulverizing and blending in, may expand.
lieh ist, und zwar in kontinuierlicher Weise sowie durch Derartige Strahlmühlen sind zur Pulverisierung vonis borrowed, in a continuous manner and by Such jet mills are for pulverizing
Fernbedienung. Dies bietet keine besonderen Schwie- io verschiedenen Substanzen bekannt, sie wurden jedochRemote control. This does not offer any particular difference in the number of substances known, but they have been known
rigkeiten bezüglich der Kontaktierung, der Zerkleine- bisher noch niemals zur Herstellung von Schwar/pul-skills regarding the contacting, the chopping - so far never for the production of black / pulp
rimg sowie des Siebens, jedoch, wie vorstehend er- ver verwendet,rimg as well as sieving, however, as used above,
wähnt, ist die Lage t-eim Polieren anders. Zunächst schien es so, als sei es sehr riskant, die dreithinks the situation is different when polishing. At first it seemed like the three of them were very risky
Es wurde versucht, zu Durchführung des Polierens Komponenten gleichzeitig zu vermischen und /u pulve-An attempt was made to mix and / u powder components at the same time to carry out the polishing
ebenfalls die Strahlmühle ei· verwenden, die bereits zur 15 risieren.also use the jet mill which is already being used.
Herstellung des Sch ν ,ir'p.ulvermehis verwendet wird. Die Pulverisierung von Schwefel allein stellt bereits Zunächst hätte nun <m,-..jnmen können, daß die Mühle hinsichtlich einer Entzündung ein großes Risiko dar, zu kräftig arbc 1 und damit die Körner zu einem und zwar wahrscheinlich infolge der großen Ansamm-Staub pub-riaiert anstatt ihre Kanten abzuschleifen. lung von statischer Elektrizität Werden jedoch alle Zunächst it .τ diese Erscheinung auch ein. Es konnte 20 drei Ausgangsmaterialien gleichzeitig zugesetzt, so jedoch dann herausgefunden werden, daß ein zufrieden- daß das Oxyd? jnsmittel (KNO3) mit den Redukstellendes Polieren des Sehwarzpulvers unter spezifi- tionsmitteln (S und C) zusammenstößt, wobei diese sehen Bedingungen, auf die nachstehend noch näher Zusammenstöße wahrscheinlich zu lokalen Temperaeingegangen werden wird, staltfinden kann. turanstiegen führen, dann stellt rr an fest, daß cii.e Un-Production of the Sch ν, ir'p.ulvermehis is used. The pulverization of sulfur alone already shows at first that the mill poses a great risk of ignition, that it would work too vigorously and that the grains would become a pub, probably as a result of the large accumulation of dust -rated instead of sanding its edges. The development of static electricity, however, will all begin with this phenomenon as well. It was possible to add three starting materials at the same time, but then it was found that one satisfied- that the oxide? The solvent (KNO 3 ) collides with the reducing polishing of the black powder under specifying agents (S and C), whereby these conditions can arise, which will probably be discussed in more detail below on collisions at local temperatures. rise, then rr an determines that cii.e Un-
In den Rahmen der Erfindung fällt ferner ein Ver- 25 terieilung und Vermischung ohne Anzeichen einer Entfahren zur weiteren Verarbeitung des Schwarzpulver- zündung des Pulvers stattfindet. r)iese Erscheinung mehls durch Kontaktieren, wonach das Schwarz- läßt sich nicht vollständig erklären. Man nimmt an, pulver zerkleinert, gesiebt und poliert wird. Dieses daß einer der Gründe in dem Expandieren der Luft zu Verfahren zeichnet steh dadurch aus. daß das Schwarz- sehen ist, so daß sine Kühlung in der Vorrichtung stattpulver in einer gleichen Strahlmühle, wie sie auch für 30 findet.The scope of the invention also includes distribution and mixing taking place without any signs of escape for further processing of the black powder ignition of the powder. r) hese phenomenon is not fully explain flour by contacting, after which the black leaves. It is assumed that powder is crushed, sifted and polished. This is one of the reasons for expanding the air to process. that the black is seen, so that its cooling in the device instead of powder in the same jet mill as is also found for 30.
das Vermählen der Mischung dient, poliert wird, wobei Es hat sich als unnötig erwiesen, ein Inertgas, wieThe grinding of the mixture is used to polish, whereby it has been found unnecessary to use an inert gas, such as
die Strahlmühle mit wenigstens 10- bis 20mal soviel beispielsweise Stickstoff, in der Vorrichtung /u ver-the jet mill with at least 10 to 20 times as much nitrogen, for example, in the device / u
Schwarzpulver wie während der Pulverisierung be- wenden. Die Verwendung eines derartigen InertgasesUse black powder as you would during pulverization. The use of such an inert gas
laden und der Druck der in die Mühle eingeführten würde zu erheblichen Extrakosten führen, da nan dannloading and the pressure of the imported into the mill would lead to considerable extra costs, since nan then
Luft auf sehr geringe Werte reduziert wird, 'ind daß 35 in einem geschlossenen System arbeiten müßteAir is reduced to very low levels, 'ind that 35 would have to work in a closed system
in die Mühle an einer Stelle nach dem tangentialen Die Einmengungswirkung, die aus einer Linbeifinginto the mill at a point after the tangential The entangling effect resulting from a Linbeifing
Einlaß für die Arbeitsluft ein feiner Strahl aus pulveri- von Schwefel und/oder Kaliumnitrat in den Poren derInlet for the working air a fine jet of powdery sulfur and / or potassium nitrate in the pores of the
siertem Graphit eingeblasen und die Schv irzpulver- Aktivkohle besteht, entfalte«, sich voll bei den kräftigenThe strong graphite is blown in and the charcoal is made of hot-melt powder
körner mit Grpahit überzogen werden. Zusammenstößen zwischen den verschiedenen Roh-grains are coated with grpahit. Collisions between the various raw
Das erfindungsgemäße Verfahren zur Herstellung 40 materialien.The inventive method for producing 40 materials.
von Schwarzpulvermehl wird nachstehend näh be- Das fertige Schwarzpulvermehl wird aus der MühleBlack powder meal is sewn below. The finished black powder meal is taken from the mill
schrieben. mitteis des Luftstrom«, abgezogen und in einem Zv klonwrote. mitteis des Luftstrom «, withdrawn and cloned in a room
Die Rohr ^tenaiien Kaliumnitrat, Aktivkohle und od. dgl. abgetren.it. Größere Teilchen werden erneutThe Rohr ^ tenaiien potassium nitrate, activated charcoal and od. The like. Separated. Larger particles will reappear
Schwefel werden in den entsprechenden Mengen ver- der ersten Zone zugeführt.Sulfur is fed to the first zone in the corresponding quantities.
hältnissen in bekannter Weise vermischt, und zwar 45 Auf diese Weise erfolgt die Unterteilung und Einentweder durch rein mechanisches Mischen, durch mengung gleichzeitig sowie nur mittels eines Luftsirahls Vermischen in einer Trommel, d'Tch Luftmischen oder in einer Vorrichtung ohne mechanisch bewegbare nach irgendeiner anderen üe tnnten Methode. Die Teile. Dies ist von großer Bedeutung im Hinblick auf Teilchengröße des Kaliumnitrat^ und des Schwefels be- die Sicherheit während der Herstellung des Schwarzträgt vorzugsweise 1 mm, während die Teilchengröße 50 pulvers. Ferner kann die Herstellung automatisch ohne der Aktivkohle zwischen 1 μ und 1 mm schwankt. Oies Steuerung erfolgen. Dies bedeutet, daß sich keine bedeutet, daß die Aktivkohle gegebenenfalls im voraus Menschen in einer möglichen Gefahrenzone aufhaltenratios mixed in a known manner, namely 45 In this way, the subdivision and unity takes place by purely mechanical mixing, by mixing at the same time and only using an air sirahl Mixing in a drum, d'Tch air mixing or in a device without mechanically movable any other appropriate method. The parts. This is of great importance in terms of Particle size of potassium nitrate and sulfur contributes to the safety during the manufacture of the black preferably 1 mm, while the particle size 50 powder. Furthermore, the production can be done automatically without the activated carbon fluctuates between 1 μ and 1 mm. These controls take place. This means that there are no means that the activated carbon may hold people in a possible danger zone in advance
Ist die Teilchengröße des Kaliumnitrats und des tung ist sehr kurz, so dajj die Menge an SchwarzpulverIf the particle size of the potassium nitrate and the tung is very short, then the amount of black powder
Schwefels relativ groß, d. h- ungefähr 1 mm, dann ist 55 in der Mahlvorrichtung selbst nur in der Größenord-Sulfur relatively large, d. h- about 1 mm, then 55 in the grinding device itself is only in the order of magnitude
die Mischung harmlos, nicht explosiv und nur in dem nung von 200 g liegt. Dies ist im Hinblick auf die S<cher-the mixture is harmless, non-explosive and only contains 200 g. This is with regard to the security
MaßeverbrennbarwieandereverbrennbareSubstar-zen. heit ebenfalls von großer Bedeutung. Ferner kunn dasDimensions combustible as other combustible substars. is also of great importance. Furthermore, you can
Die vermischte Mischung wird kontinuierlich in Schwarzpulver auf billige Weise here stellt «■■ . ιThe blended mixture is continuously put in black powder in a cheap way «■■. ι
einen Luftstrahl in einer bekannten Vorrichtung einge- wobei der Ausschuß niedrig ist.a jet of air in a known device, the reject rate being low.
führt, die als Strahlmühle oder Dampf- oder Luftstrahl- 60 Das auf diese Weis*, hergestellte Schw;tr/pul\erm -ιleads that as a jet mill or steam or air jet 60 The in this way *, produced Schw; tr / pul \ erm -ι
pulverisierungsvorrichtung bekannt ist. In dieser Vor- ist völlig gleichmäßig vermischt. F.s ist -,ehr laJ't /pulverizing device is known. In this pre is mixed completely evenly. F. it is -, honestly
richtung wird die Mischung weiter vermählen, und sammendrückbar und kann daher .»hne Sihwiencl·direction the mixture is ground further, and squeezable and can therefore. »hne Sihwiencl ·
zwar in der Weite, daß sie durch einen jetrennten Luft- zu jedem Schwarzpulvertyp weiter.erarbeitet v* r:!t ·to the extent that it can be further processed by a separate air to each type of black powder. v * r:! t ·
strom in eine Zone geführt wird, in welcher die Luft Verschiedene Typen von Schwar/puK wir<)ct 1 ifStrom is led into a zone in which the air Different types of black / puK we <) ct 1 if
eine Überschallgeschwindigkeit besitzt In dieser Zone 65 diese Weise hergestellt. Sie /eigen n.w.nale I leeu-has a supersonic speed In this zone 65 produced in this way. You / own n.w.nale I leeu-
erfolgt *;ae Anzahl schwerer Kollisionen zwischen den schäften bei einer Verwendung in Gewehren rx-> ηoccurs * ; ae number of serious collisions between the stocks when used in rifles rx-> η
Teilchen infolge der hohen Luftgeschwindigkeit. Diese Verbrennen in Schmelz- und Zündrohren sowie KParticles as a result of the high air speed. These burn in melting and ignition tubes as well as K
Kollisionen sind derart kräftig, daß die Teilchen zu züglich der Elektronenspinkonzentration.Collisions are so powerful that the particles increase the electron spin concentration.
Das Schwarzpulvermehl kann vollständig trocken hergestellt werden. Gegebenenfalls kann Wasser dem Schwarzpulvermchl in dem Zyklon zugesetzt werden. Bisher war es üblich, das Schwarzpulvermehl mit 3 bis 5% Wasser zu befeuchten, um den Staub in einem gewissen Ausmaße zu binden, die Kompressibilität zu erhöhen und die Sicherheit zu steigern. Nach dem erfindungsgemäßen Verfahren hergestelltes Schwarzpulvcrmch! staubt in überraschender Weise nur in geringfügigem Ausmaß und ist sehr leicht infolge der kleinen Teilchengröße, insbesondere von Schwefel und Kaliumnitrat, kompressibcl. Die Zugabe von Wasser ist daher nicht erforderlich. Is kann jedoch ion Vorteil sein. Wasser beispielsweise aus Sicherheitsgründen /u/uscl/cn.The black powder meal can be made completely dry. Optionally, water can be added to the black powder mix in the cyclone. Up until now it was common practice to moisten black powder meal with 3 to 5% water in order to bind the dust to a certain extent, to increase the compressibility and to increase the safety. Black powder powder produced by the process of the invention! Surprisingly, it only produces a small amount of dust and is very easily compressible due to the small particle size, especially of sulfur and potassium nitrate. It is therefore not necessary to add water. However, it can be an advantage. Water, for example, for safety reasons / u / uscl / cn.
Die Vorrichtung /um Vermählen und Linmcngen. welche crfindungsgcmäß verwendet wild, arbeitet kontinuierlich um) kann auf alle Kapazitäten ausgc-Icgl «erden, und /war von einigen Heklogramm bis /u einigen Tonnen pro StundeThe device / for grinding and grinding. which is used wildly, works continuously around) can be used for all capacities «Earth, and / was from a few heclograms to / u several tons per hour
/um Polieren Λ» Schwar/pulvcrs wird die Mühle mit wenigstens 10- bis 2öma! soviel Schwarzpulver wie bei der Pulvcmierurg beladen, während der Druck der durih die ungcnliaicn f mläßc der Sirahlmühle zugeführten Luft »on einem relativ hohen Druck, beispielsweise 7 bis 8 kg/cm*, auf einer sehr ricdcren Druck, beispielsweise 0.1 bis 0.5 kg,'cm1, reduziert/ um polishing Λ »The mill will be black powder with at least 10 to 2 ma! as much black powder is loaded as in the powder burner, while the pressure of the air fed through the unreliable pressure of the sir grinding mill is at a relatively high pressure, for example 7 to 8 kg / cm *, at a very low pressure, for example 0.1 to 0.5 kg, ' cm 1 , reduced
;>cr Graphitübcrzug wird auf dem Schwarzpulver in der «!eichen Operation sowie in der gleichen Mühle aufgebracht, und /war durch hinblascn eines feinen Strahl* aus pulverisiertem Giaphif in die Mühle an einer Steile nach dem tangentialcn finlaß für die Arbsril«luff.;> cr graphite coating is on the black powder in the same operation and in the same mill applied, and / was started by blowing a fine stream * of pulverized Giaphif into the mill one steeply after the tangential end for the Arbsril «luff.
Wird ois Mühte auf diese Weise eingestellt, dann ei folgt ein zufriedenstellendes Polieren mit einer hohen Geschwindigkeit sowie ohne merkliches Erhitzen des Schwarzpulver*. Die Anreicherung von Schwarzpulver während des Polierens hängt natürlich von der Größe des Restes der Anlage ab. Bei einer Anlage mit einer Kapazität von beispielsweise 300 kg pro Stunde überslcig! /. B. die Menge nicht 4 kg. und /war im Gegensat/ /u bis /xx 2700 kg bei der Durchführung der bisher bekannten Verfahren. Ois is struggling adjusted in this manner, then ei follows a satisfactory polishing at a high speed and without significant heating of the black powder *. The build-up of black powder during polishing depends of course on the size of the rest of the plant. In the case of a system with a capacity of, for example, 300 kg per hour, this is clear! /. B. the amount is not 4 kg. and / was on the contrary / / u to / xx 2700 kg when carrying out the previously known methods.
Nachstehend wird ein Beispiel für eine Aiisführungsform der I Windung gegeben.The following is an example of an embodiment given the I turn.
Die Erii-«j-'ig läßt sich am besten durch Bezugnahme auf d;*- Fließbild erläutern. In diesem Fließbild bedeutetThe Erii- «j-'ig can be best understood by reference on d; * - explain the flow diagram. In this flow sheet means
A unter Drucfc stehende : uft, A under pressure: uft,
B Wasser. B water.
C Schwarzpulvcnnehl. C Gunpowder flour.
D Hitler Druck stehende Luft zum Reinigen, D Hitler pressurized air for cleaning,
/. LufiausiaS./. LufiausiaS.
/ Sfaubabführung./ Sfaubabführung.
Die Sirahlmühlc 7 wird durch den Aufgabetrichter 5 bcühfcki Der Aufgabetrichtcr kann 200 kg der Rohrnaicnafmischiing (Kaliumnitrat. Kohlenstoff und Schwefel) aufnehmen. Line geeignete Zumcssungsein- nchttmeo. wie beispielsweise eine Vibrationsrinnc oder «»κ· Best hickungsschncckc. entfernt kontinuierlich eine lim ante Menge von 300 kg pro Stunde aiii, dem Aufgabclrichtcr S. Nachdem noch ungefähr 90 fcg in dem Aufgabetrichtcr vorhanden sind, startet ein Höhenanzeiger die Vibrationsrinne unterhalb des Aufgabetrichters für Kaliumnitrat. Diese Rinne fördert 75 kgThe Sirahlmühlc 7 is fed through the feed funnel 5. The feed funnel can hold 200 kg of the Rohrnaicnafmischiing (potassium nitrate, carbon and sulfur). Line suitable allocation un- tmeo. such as a vibrating trough or «» κ · Best hickungsschncckc. continuously removes a limited amount of 300 kg per hour aiii, the feed funnel S. After about 90 fcg are left in the feed funnel, a height indicator starts the vibrating chute below the feed funnel for potassium nitrate. This channel transports 75 kg
Kaliumnitrat auf die Waage 2. Die Waage stoppt die Zufuhr, wenn 75 kg erreicht worden sind. Bann wird die Vibrationsrinne unter dem Aufgabctrichter fur Schwefel 3 gestartet- Sie fuhrt 10 kg zu, worauf die Vibrationsrinnc für Aktivkohle 4 gestaltet wird SiePotassium nitrate on the scale 2. The scale stops feeding when it reaches 75 kg. The vibrating chute under the feed hopper for sulfur 3 is then started - it feeds 10 kg, whereupon the vibrating chute for activated carbon 4 is designed
ία führt 15 kg /u Die Waage 2 ist nach dem Spannungsan/cigcprm/ip gebaut und wirkt ebenfalls als Vermischungscinrichtung mit einem doppelten Boden, der mit unter Druck stehender Luft vcr* undcit ist. Die unter Druck stehende Luft vird automatisch umgelenkt. ία leads to 15 kg / u. The balance 2 is built according to the voltage con / cigcprm / ip and also acts as a mixing device with a double bottom, which is vcr * undcit with pressurized air. The pressurized air is automatically diverted.
wenn das Wiegen beendet ist. Das Vermischen dauert währc.id einer bestimmten Zeitspanne, bfispielsweisc 3 Minuten, an Dann beginnt dzt Bodenventil der Waage die Mischung auf das Förderband /·ι entladen, das kontinuierlich läuft und die Mischung dem Auf-when the weighing is finished. The mixing takes währc.id a certain period, bfispielsweisc 3 minutes to then dzt bottom valve of the balance will start the mixture onto the conveyor belt / · ι discharged, the continuously running and the mix up the
vt gabctrichter 5 zuführt. Nachdem die Waage geleert ist, steht die ganze Anlage zum Wiegen und Vermischen so lange «till, bis der Höhenanzeiger in dem Aufgabetrichtcr Seinen neue. Zyklus startet. Bei einer Gesamtkapa/ilät von 300 kg pro Stunde erfolgen auf diese vt feed funnel 5 feeds. After the scales have been emptied, the whole weighing and mixing system is in place until the height indicator in the feed hopper is new. Cycle starts. With a total capacity of 300 kg per hour, this takes place
*5 Weise 3 Wägungen pro Stum1-. Die Strahlmühle 7 läuft kontinuierlich und lief : ein fer';ges Schwarzpulvermehl in das Zyklon 8. Der Überschuß an Luft wird an der Obcn»eiic durch das Filter? abgeblasen Das Filter spült sich selbst mittels eines automatischen.* 5 way 3 weighings per mute 1 -. The jet mill 7 runs continuously and ran: a ferrous black powder meal into the cyclone 8. The excess air is on the surface through the filter? blown off The filter rinses itself by means of an automatic.
pulsierenden umgekehrten Luftstroms durrh das Filter. Im unteren Teil des Zyklons is* ein System aus feinen Wasserdüsen eingebaut, das 91 Wasser pro Stunde liefert, so daß dem Pulver ein Feuchtigkeitsgehalt von 3°/0 verliehen wird. Das Schwarzpulvermehl wird kontinuierlich aus dem Zyklon durch das Drehventil in dem Boden abgezogen. Das Förderband transportiert es zu einer möglichen weiteren Verarbeitung. pulsating reverse airflow through the filter. Installed in the lower part of the cyclone is * a system of fine water jets, the water provides 91 per hour so that the powder has a moisture content of 3 ° / imparted 0th The black powder meal is continuously withdrawn from the cyclone through the rotary valve in the bottom. The conveyor belt transports it for possible further processing.
Claims (5)