DE2002843A1 - Process for the production of laminated panels - Google Patents

Process for the production of laminated panels

Info

Publication number
DE2002843A1
DE2002843A1 DE19702002843 DE2002843A DE2002843A1 DE 2002843 A1 DE2002843 A1 DE 2002843A1 DE 19702002843 DE19702002843 DE 19702002843 DE 2002843 A DE2002843 A DE 2002843A DE 2002843 A1 DE2002843 A1 DE 2002843A1
Authority
DE
Germany
Prior art keywords
synthetic resin
powder
resin
layer
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
DE19702002843
Other languages
German (de)
Inventor
Milian Dipl-Ing Hans
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Isovolta AG
Original Assignee
Isovolta AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Isovolta AG filed Critical Isovolta AG
Publication of DE2002843A1 publication Critical patent/DE2002843A1/en
Pending legal-status Critical Current

Description

PAVGNT AN WX LTiS 'PAVGNT AN WX LTiS '

PROF. DR. DR. J. REITSTOTTER 9 Ω Π 9 ß ^ QPROF. DR. DR. J. REITSTOTTER 9 Ω Π 9 ß ^ Q

DR.-ING. WOLFRAM BUNTE * U U Z Q I»DR.-ING. WOLFRAM BUNTE * U U Z Q I »

DR. KARL GEORG LÖSCHDR. KARL GEORG LÖSCH

D - 8O0O MÜNCHEN 13. BAUERSTRASSE 22. FERNRUF ΪΟΘΙΙ) 37 08 S3D - 8O0O MUNICH 13. BAUERSTRASSE 22. FERNRUF ΪΟΘΙΙ) 37 08 S3

ISOVOLTAISOVOLTA

Österreichisches
Isolierstoffwerk KG
H. Turnauer & Co.Austrian
Isolierstoffwerk KG
H. Turnauer & Co.

München, den 22. Januar 1970 M/11011Munich, January 22, 1970 M / 11011

Verfahren zur Herstellung von SchichtstoffplattenProcess for the production of laminated panels

Schichtstoffpiatten werden üblicherweise aus Papier, Holz, Textilien oder dgl. hergestellt. Die Materialbahnen werden zu diesem Zweck meistens mit Kunstharz; getränkt, zugeschnitten und unter Druck und erhöhter Temperatur miteinander verpresst.Laminate panels are usually made of paper, wood, textiles or the like. Made. For this purpose, the material webs are usually made of synthetic resin ; soaked, cut to size and pressed together under pressure and elevated temperature.

Als Oberflächenschicht wurde je nach dem Verwendungszweck eine veredelte Schicht, wie z.B. Dekorpapier, Schliffholz usw. oder eine unveredelte Schicht verwendet. Oberflächenmaterial, wie'Dekorpapier, Holzfurnier usw. ist Im Handel erhältlich. As a surface layer, depending on the purpose a refined layer, such as decorative paper, ground wood, etc. or an unfinished layer is used. Surface material such as decorative paper, wood veneer, etc. is commercially available.

Gegenstand der Erfindung ist ein Verfahren zur Herstellung von Schichtstoffpiatten. Erfindungsgemäß geht man dabei so vor, daß man eine Mischung aus Kunstharz und Metallpulver auf eine gegebenenfalls mit Kunstharz vorimprägnierte Schicht, aufbringt und diese hernachThe invention relates to a method for production of laminated panels. According to the invention, the procedure is such that a mixture of synthetic resin is used and metal powder, optionally with synthetic resin pre-impregnated layer, applies and this afterwards

0 09836720670 0983672067

vortrocknet sowie diese Auftragsschicht beim Aushärten einer Schichtstoffplatte als Oberflächenschicht einsetzt. Diese Oberflächenschicht kann gegebenenfalls noch mit einer dünnen Deckschicht, beispielsweise Papier oder Kunststoff, überzogen werden.pre-dries as well as this coating layer during hardening a laminate board is used as the surface layer. This surface layer can optionally also be covered with a thin cover layer, for example paper or plastic, be coated.

Pur das erfindungsgemäße Verfahren können Pulver von fast allen Metallen verwendet werden. Ausgenommen sind eigentlich nur diejenigen, welche sehr große Reaktivität zeigen, wie z.B. die Alkali- oder Erdalkalimetalle.Purely the process according to the invention can powder of almost all metals can be used. The only exceptions are actually those that show very high reactivity, such as the alkali or alkaline earth metals.

Als besonders vorteilhaft erweisen sich Kupfer, Aluminium, Eisen, Blei sowie diverse Legierungen, wie Bronze, Messing oder dgl..Copper, aluminum, iron, lead and various alloys such as bronze and brass have proven to be particularly advantageous or the like ..

Als Trägermaterial sind verschiedenste Produkte einsetzbar, wie z.B. Papier, Textilien, Glasfasermatten, Holz usw.. Bei Verwendung von Papier erweist es sich als vorteilhaft, daß durch die Deckkraft der Kunststoff-Metallpulverschicht auch Papiere eingesetzt werden können, deren Eigenfärbung durch eine unpigmentierte Kunststoffschicht durchscheinen würde. Es ist also nach dem erfindungsgemäßen Verfahren durchaus möglich, ein sogenanntes Kernpapier (Papier für das Innere einer Schichtstoffplatte) auch als "Trägerpapier für die äußere Haut aus Kunststoff und Metallpulver zu verwenden. Diese Tatsache ist ein Vorteil für die Herstellung von Dekorplatten.A wide variety of products can be used as carrier material, such as paper, textiles, fiberglass mats, wood, etc. When using paper, it has been found to be advantageous that, due to the opacity of the plastic-metal powder layer It is also possible to use papers whose intrinsic color shines through through an unpigmented plastic layer would. According to the method according to the invention, it is quite possible to use a so-called core paper (paper for the inside of a laminate board) also called "backing paper to use for the outer skin made of plastic and metal powder. This fact is an advantage for manufacturing of decorative panels.

Hinzu kommt noch, daß die eingearbeiteten Metallpulver der Platte ausgezeichnete optische Eigenschaften vermitteln, welche je nach Konzentration des Metalls im Kunststoff sowie gegebenenfalls durch verschiedene Vorbehandlung des Metallpulvers beliebig variiert werden können. Da die Metallpartikel vom Kunststoff fest umhüllt sind, ergibt sich eine große Stabilität und Korrosionsfestigkeit.In addition, the incorporated metal powder of the plate gives excellent optical properties, which depending on the concentration of the metal in the plastic as well optionally can be varied as desired by various pretreatments of the metal powder. As the metal particles are tightly encased by plastic, there is great stability and corrosion resistance.

009836/2067009836/2067

Die nach dem erfindungsgemäßen Verfahren hergestellten Schichtstoffplatten sind für verschiedenste Zwecke verwendbar. Neben den guten optischen Eigenschaften ergeben sich je nach dem eingesetzten Metallpulver sowie nach dessen Konzentration auch verschiedene technisch verwertbare Effekte. So lassen sich z.B. Oberflächen mit einer gewünschten elektrischen oder thermischen Leitfähigkeit herstellen. Bei Verwendung von Blei oder ähnliehen Metallen ergibt sich eine hohe Absorptionsfähigkeit von Kernstrahlen, so daß eine derartige Platte als Strahlenschutzplatte Verwendung finden kann.Those produced by the process of the invention Laminate panels can be used for a wide variety of purposes. In addition to the good optical properties Depending on the metal powder used and its concentration, there are also various technically usable ones Effects. For example, surfaces with a desired electrical or thermal conductivity can be created produce. When using lead or similar metals This results in a high absorption capacity of nuclear rays, so that such a plate can be used as a radiation protection plate Can be found.

Als Kunstharze kommen praktisch alle solchen in Frage, welche der gestellten Aufgabe genügen, das heißt, sie sollen auftragbar sein und sollen bei der Plattenproduktion aushärten. Als sehr günstig haben sich Polyester, Phenolharze, Aminoplaste und insbesondere Melaminharze erwiesen.Practically all synthetic resins can be used which are sufficient for the task at hand, that is, they should be applicable and should be used in panel production Harden. Polyesters, phenolic resins, Aminoplasts and especially melamine resins proved.

Die Herstellung der Platten kann durch Verpressen oder Verkleben erfolgen. Beim Verpressen können noch zusätzliche Muster in die Oberfläche eingepreßt werden.The panels can be produced by pressing or gluing take place. When pressing, additional patterns can be pressed into the surface.

Das erfindungsgemäße Verfahren wird durch nachstehendes Beispiel erläutert:The method of the present invention is accomplished by the following Example explained:

Beispielexample

2000 Gewichtsteile eines ßj #igen Melaminharzes (MF 19 SBD) werden mit 570 Gewichtsteilen eines feingemahlenen Bronzepulvers unter Rühren gemischt. Die Menge des Bronzepulvers wird so berechnet, daß sie 30: .-Gewichtsprozent des Feststoffanteiles ausmacht. 2000 parts by weight of a ßj #igen melamine resin (MF 19 SBD) are mixed with 570 parts by weight of a finely ground bronze powder with stirring. The amount of bronze powder is calculated so that it makes up 30 percent by weight of the solids content.

Nach gleichmäßiger Verteilung werden 10 Gewichtsteile Netzmittel bzw. Quellmittel zugegeben. >After uniform distribution, there are 10 parts by weight Wetting agent or swelling agent added. >

009836/2067009836/2067

Um vollkommen knotenfreie Mischung zu erhalten, wird die Paste 24 Stunden ruhen gelassen.In order to obtain a completely knot-free mixture, the paste is left to rest for 24 hours.

Nach dieser Zeit wird nochmals gut durchgerührt und sobald keine Phasentrennung mehr festzustellen ist, wird mit der Imprägnierung begonnen.After this time, the mixture is again thoroughly stirred and as soon as no more phase separation can be determined, the Impregnation started.

Als Trägermaterial wird ein Sulfitzellstoff mit einem Füllstoff gehalt von 17 % verwendet.A sulfite pulp with a filler content of 17 % is used as the carrier material.

Papierwerte:Paper values: 100 g/m2 100 g / m 2 Grammatur:Grammage: 0,15 mm0.15 mm Dicke:Thickness: I1 « 22 mm 10I 1 «22 mm 10 Saughöhe Klemm:Suction height clamp: 15"15 " Saugfähigkeit TappisTappis absorbency 6,56.5 pH-Wert:PH value: 0,5 kg0.5 kg Naßreißfestigkeit:Wet tensile strength: 17 % 17 % Asche:Ash:

45 ram45 ram

Das Rohpapier wird zunächst mit einem Melaminharz vorimprägniert und zwar ergeben sich Harzaufträge von 70 bis 80 fr. Der Berechnung wird das Rohpapier mit 100 % zu Grunde gelegt. Der volatile Gehalt beträgt 7 bis 8 %. The base paper is first pre-impregnated with a melamine resin, which results in a resin application of 70 to 80 fr. The calculation is based on the raw paper with 100 % . The volatile content is 7 to 8 %.

Werte des Melaminharzes: Values of the melamine resin :

Festkörper; 55 % Solid body; 55 %

pH-Wert: 8,4pH value: 8.4

Viskosität: 53"Viscosity: 53 "

Das vorimprägnierte Material wird nun mit der oben angeführten Bronze-Harzmischung einseitig beschichtet. DerThe pre-impregnated material is now coated on one side with the bronze-resin mixture listed above. Of the

ο ρο ρ

Bestrich enthält 20 g/m Bronze und 50 g/m Harz. Der volatile Gehalt des Materials beträgt 5 bis 6 %. Floor screed contains 20 g / m bronze and 50 g / m resin. The volatile content of the material is 5 to 6 %.

009836/2067009836/2067

Imprägnierdaten:Impregnation data:

Temperatur der Paste: 25° bis JO0 C Temperatur in.der■Kanalzone: 155° bis 'l45°C Imprägniergeschwindigkeit·: ca. 12 m/MinuteTemperature of the paste: 25 ° to JO 0 C Temperature in the ■ channel zone: 155 ° to 145 ° C Impregnation speed: approx. 12 m / minute

Das Halbfabrikat wird anschließend zur Herstellung einer Schichtstoffplatte eingesetzt. Die erhaltene Schichtstoff platte ist einer Bronze-kaschierten Platte gleichzusetzen und hat den Vorteil, oxydationsunempfindlich zu sein.The semi-finished product is then used to manufacture a laminate board. The obtained laminate plate is equivalent to a bronze-clad plate and has the advantage of being insensitive to oxidation.

. ■ .-' -:■ -.,' -- .'-..■ Stellt man so eine Platte nach dem Prägeverfahren her, dann erhält man Produkte, die einer getriebenen Bronze-Platte täuschend ähnlich sind.. ■ .- '-: ■ -.,' - - .'- .. ■ If you manufacture such a plate using the embossing process, you get products that are deceptively similar to a stamped bronze plate.

0 09838720670 0983872067

Claims (14)

PatentansprücheClaims Θ Verfahren zur Herstellung von Schichtstoffplatten, dadurch gekennzeichnet , daß man eine Mischung aus Kunstharz und Metallpulver auf eine gegebenenfalls mit Kunstharz vorimprägnierte Schicht aufbringt und, diese hernach vortrocknet sowie diese ■ Auftragsschicht beim Aushärten einer Schichtstoffplatte als Oberflächenschicht einsetzt. Θ Process for the production of laminated panels, characterized in that a mixture of synthetic resin and metal powder is optionally applied applies a layer pre-impregnated with synthetic resin and then pre-dries this as well as this ■ Application layer is used as a surface layer when a laminate board cures. 2. Verfahren nach Anspruch 1, dadurch g e k e η η zeichnet, daß man die Oberflächenschicht noch mit einer dünnen Deckschicht, beispielsweise Papier oder Kunststoff, überzieht.2. The method according to claim 1, characterized in that g e k e η η, that the surface layer can be covered with a thin top layer, for example Paper or plastic, coated. J>. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet , daß man als Kunstharz ein Polyesterharz einsetzt. J>. Process according to Claim 1 or 2, characterized in that the synthetic resin used is a polyester resin. 4. Verfahren nach Anspruch 1 oder 2, dadurch g e kennzeichnet , daß man als Kunstharz ein Phenolharz einsetzt.4. The method according to claim 1 or 2, characterized in g e that a phenolic resin is used as the synthetic resin. 5. Verfahren nach Anspruch 1 oder 2, dadurch g e kennzeichnet, daß man als Kunstharz einen Aminoplasten einsetzt.5. The method according to claim 1 or 2, characterized in g e that an aminoplast is used as the synthetic resin. 6. Verfahren nach Anspruch 1 oder 2, dadurch g e kennzeichnet , daß man als Kunstharz ein Melaminharz einsetzt.6. The method according to claim 1 or 2, characterized in that one is used as a synthetic resin a melamine resin is used. 7. Verfahren nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet , daß man als Träger ein Papier einsetzt.7. The method according to any one of claims 1 to 6, characterized in that there is used as a carrier insert a paper. 009836/2067009836/2067 8. Verfahren nach einem der Ansprüche 1 bis 6/ dadurch g-e Kennzeich.net , daß man als Träger Textilmaterial einsetzt.8. The method according to any one of claims 1 to 6 / characterized g-e Kennzeich.net that you as a carrier Uses textile material. 9. Verfahren nach einem der Ansprüche 1 bis 6,.dadurch g-e k e η η ζ ei c h η et , daß man als Träger eine Glasfasermatte einsetzt.9. The method according to any one of claims 1 to 6 ,. thereby ge ke η η ζ ei ch η et that a glass fiber mat is used as a carrier. 10. Verfahren nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet ,daß man Eisenpulver einsetzt. ' ■10. The method according to any one of claims 1 to 9, characterized characterized by iron powder begins. '■ 11, Verfahren nach einem der Ansprüche 1 bis 9, dadurch g e k en
einsetzt.11, the method according to any one of claims 1 to 9, characterized in that
begins. g e ken η ζ e i c h η et , daß man Kupferpulver ~g e ken η ζ e i c h η et that one is copper powder ~ 12. Verfahren nach einem der Ansprüche 1 bis9, dadurch ge kr e η η ζ e i c h η et , daß man Bleipulver einsetzt.12. The method according to any one of claims 1 to 9, characterized ge kr e η η ζ e i c h η et that you get lead powder begins. IJ. Verfahren nach einem der Ansprüche 1 bis 9, dadurch g e k e η η ζ e lehnet ■ , daß man Aluminiumpulver einsetzt. v ■ . - ■■ IJ. Process according to one of Claims 1 to 9, characterized in that aluminum powder is used. v ■. - ■■ 14., Verfahren nach einem der Ansprüche 1 bis 9, dadurch g e k e η η ζ e 1 c h η e t , daß man Messing- oder Bronzepulver einsetzt.14., The method according to any one of claims 1 to 9, characterized g e k e η η ζ e 1 c h η e t that one brass or Bronze powder is used. 0 098 36/20 6 70 098 36/20 6 7
DE19702002843 1969-02-03 1970-01-22 Process for the production of laminated panels Pending DE2002843A1 (en)