DE19547598C1 - Coating disc honeycomb catalyst substrate with dispersion - Google Patents

Abstract

In the new method, a dispersed coating is applied to flow channel walls in monolithic disc-shaped catalyst substrates. The substrates are of generally cylindrical section, penetrated by flow channels, and are coated by a dispersion of fine particulate inorganic materials and/or their precursors. The improvement is coating by injection or spraying on the end faces of the substrate. The finely-divided material is a catalytic composition, a catalyst precursor; or an ab- or ad-sorbent material. Preferably, the substrate is partially covered during spraying. Coatings of differing composition are sprayed from both end faces, at least one being a catalyst. Multilayers are applied, each layer of the same or of differing composition, at least one being a catalyst. The device so formed is used for exhaust (or waste) gas cleaning.

Description

Gegenstand der vorliegenden Erfindung ist ein Verfahren zum Aufbringen einer Dispersionsbeschichtung auf wabenförmige Katalysator-Tragkörper gemäß dem Oberbegriff des Patentanspruchs 1.The present invention relates to a method for Application of a dispersion coating on honeycomb Catalyst carrier body according to the preamble of patent claim 1.

Moderne Verfahren zur Abgasreinigung insbesondere von Verbrennungsmotoren verwenden monolithische Katalysatoren, welche auf wabenförmigen Katalysator-Tragkörpern eine katalytisch aktive Beschichtung enthalten. Die waben­ förmigen Katalysator-Tragkörper haben zumeist eine zylindrische Form beliebigen Querschnitts und sind von der Gaseintritts-Stirnfläche zur Gasaustritts-Stirnfläche von parallelen Strömungskanälen für die Abgase durchzogen. Die Dichte der Kanäle über den Querschnitt der Tragkörper, auch als Zelldichte bezeichnet, liegt üblicherweise zwischen 10 und 200 pro Quadratzentimeter. Die Wandungen dieser Strömungskanäle sind zur Konversion der Schadstoffe im Abgas mit einer Dispersionsbeschichtung beschichtet, welche katalytisch aktive Komponenten enthält. Die Tragkörper selbst sind üblicherweise aus einem keramischen oder einem metallischen Material.Modern processes for exhaust gas purification, in particular from Internal combustion engines use monolithic catalysts, which on honeycomb-shaped catalyst carriers contain catalytically active coating. The honeycomb shaped catalyst carrier usually have one cylindrical shape of any cross section and are of the Gas inlet end face to the gas outlet end face from parallel flow channels for the exhaust gases. The Density of the channels across the cross section of the supporting body, too referred to as cell density is usually between 10 and 200 per square centimeter. The walls of this Flow channels are used to convert the pollutants in the Exhaust gas coated with a dispersion coating, which contains catalytically active components. The supporting body themselves are usually made of a ceramic or a metallic material.

Die üblichen Tragkörper weisen eine Länge auf, die im allgemeinen größer als ihre größte Querschnittsabmessung ist. Dies gilt sowohl für Tragkörper mit kreisförmigem als auch ovalem oder anders geformtem Querschnitt.The usual support body have a length that in generally larger than their largest cross-sectional dimension is. This applies to both supporting bodies with circular as also oval or other shaped cross-section.

Zum Aufbringen der katalytisch aktiven Beschichtung auf die Kanalwandungen der Tragkörper sind verschiedene Verfahren bekannt. So können die Tragkörper in Dispersionen des Beschichtungsmaterials getaucht werden oder damit übergossen werden. To apply the catalytically active coating on the Channel walls of the support body are different processes known. So the support body in dispersions of the Coating material are immersed or with it be poured over.  

Die DE 40 40 150 C2 beschreibt ein Verfahren zur gleichmäßigen Beladung eines Wabenkörpers aus Keramik oder Metall mit einer Dispersionsbeschichtung, bei dem der Wabenkörper in eine formgleiche Tauchkammer eingebracht und die Beschichtungsdispersion von unten in den Wabenkörper gepumpt wird. Nach Auspumpen des Wabenkörpers und Entnahme aus der Tauchkammer wird er durch Ausblasen oder Absaugen von überschüssiger Dispersion befreit. DE 40 40 150 C2 describes a method for uniform loading of a honeycomb body made of ceramic or Metal with a dispersion coating, in which the The honeycomb body is introduced into a plunge chamber of the same shape and the coating dispersion from below into the honeycomb body is pumped. After pumping out the honeycomb body and removing it it is blown or suctioned out of the dipping chamber freed from excess dispersion.  

Danach wird die Beschichtung gewöhnlich an Luft getrocknet und anschließend bei erhöhten Temperaturen calciniert.After that, the coating is usually dried in air and then calcined at elevated temperatures.

Neuere Entwicklungen führen vermehrt zur Verwendung von kurzen, scheibenförmigen Katalysatoren. Ihre Längsdimensionen sind deutlich kleiner als ihre Querschnittsabmessungen. Solche kurzen Katalysatoren werden zum Beispiel zur Verbesserung der Abgasdurchmischung eingesetzt. Hierbei werden mehrere solcher Katalysatoren mit einem Abstand hintereinander angeordnet. Auch die Entwicklung von heizbaren Katalysatoren hat aus Gründen der Minimierung der elektrischen Leistungsaufnahme zur Verwendung von scheibenförmigen Katalysatoren beziehungsweise Tragkörpern geführt. Üblich sind Tragkörperdurchmesser von etwa 90 mm und Längen kleiner als 25 mm. Diese Katalysatoren bestehen aus Metallfolien und werden durch Stromdurchleitung elektrisch beheizt. Sie weisen aufgrund ihrer speziellen Konstruktion eine vergleichsweise labile Struktur auf.Recent developments increasingly lead to the use of short, disc-shaped catalysts. Your Longitudinal dimensions are significantly smaller than theirs Cross-sectional dimensions. Such short catalysts will be for example to improve exhaust gas mixing used. This involves several such catalysts spaced one behind the other. Also the Development of heatable catalysts has for the sake of Minimization of electrical power consumption Use of disk-shaped catalysts or supported bodies. Are common Support body diameter of about 90 mm and lengths less than 25 mm. These catalysts consist of metal foils and are electrically heated by electricity. she have a due to their special construction comparatively unstable structure.

Die bisher üblichen Beschichtungsverfahren sind für kurze Katalysator-Tragkörper mit sehr kleinem Durchmesser/Längen­ verhältnis wenig praktikabel. Die Handhabung dieser kurzen, scheibenförmigen Katalysator-Tragkörper mit der bisher üblichen Anlagenausstattung für lange Tragkörper bereitet Probleme. Darüber hinaus sind gerade bei beheizbaren Katalysatoren wegen der notwendigen elektrischen Isolation Hinterschneidungen und Sicken vorhanden, in die die Dispersion beim herkömmlichen Beschichtungsverfahren eindringt und von dort kaum oder nur unter speziellen Bedingungen entfernt werden kann. Darüber hinaus tragen die herkömmlichen Beschichtungsverfahren zu wenig der mechanischen Labilität mancher Tragkörper- Konstruktionen Rechnung.The coating methods used up to now are for short Catalyst support body with very small diameter / lengths not very practical. The handling of this short, disc-shaped catalyst carrier with the previously prepares the usual system equipment for long supports Problems. In addition, they are especially heated Catalysts because of the necessary electrical insulation There are undercuts and beads in which the Dispersion in the conventional coating process penetrates and from there hardly or only under special Conditions can be removed. In addition, the conventional coating processes too little  the mechanical instability of some Constructions bill.

Aufgabe der vorliegenden Erfindung ist es daher, ein Beschichtungsverfahren zur Verfügung zu stellen, welches es gestattet, scheibenförmige Katalysator-Tragkörper in einfacher Weise zu beschichten.The object of the present invention is therefore a To provide coating processes which it allowed in disc-shaped catalyst carrier easy way to coat.

Diese Aufgabe wird durch ein Verfahren zum Aufbringen einer Dispersionsbeschichtung auf die Kanalwandungen von Strömungskanälen monolithischer, scheibenförmiger Katalysator-Tragkörper von allgemein zylindrischem Querschnitt, welche von der Eintrittsstirnfläche zur Austrittsstirnfläche von den Strömungskanälen durchzogen werden, unter Verwendung einer Beschichtungsdispersion aus feinteiligen anorganischen Stoffen und/oder deren Vorläufer, gelöst, welches dadurch gekennzeichnet ist, daß die Beschichtung der Kanalwandungen durch Spritzen oder Sprühen auf die Stirnflächen der Tragkörper erfolgt und die feinteiligen Stoffe aus einer Katalysatorzusammensetzung, einer Katalysatorvorstufe oder einem ab- oder adsorbierenden Material bestehen.This task is accomplished by a method of applying a Dispersion coating on the channel walls of Flow channels monolithic, disc-shaped Catalyst support body of generally cylindrical Cross-section, which from the entrance face to Exit face traversed by the flow channels are made using a coating dispersion finely divided inorganic substances and / or their Precursor, solved, which is characterized in that the coating of the channel walls by spraying or Spraying takes place on the end faces of the support body and the finely divided substances from a catalyst composition, a catalyst precursor or an off or adsorbent material exist.

Das Verfahren ist besonders für kurze scheibenförmige Wabenkörper geeignet. Die Beschichtungsdispersion wird durch Spritzen oder Sprühen von einer oder von beiden Stirnflächen des Tragkörpers auf die Kanalwandungen aufgebracht. Bevorzugt werden im Verfahren wäßrige Beschichtungsdispersionen verwendet. Zur Erzielung besonderer Schichteigenschaften oder bei Verwendung bestimmter Feststoffe sind aber auch in gleicher Weise andere Trägerflüssigkeiten, zum Beispiel organische Flüssigkeiten, wie Alkohol sowie deren Mischungen mit Wasser, verwendbar. The procedure is especially for short disc-shaped ones Honeycomb body suitable. The coating dispersion will by spraying or spraying one or both End faces of the support body on the channel walls upset. Aqueous are preferred in the process Coating dispersions used. To achieve special layer properties or when used certain solids are also in the same way other carrier liquids, for example organic Liquids such as alcohol and mixtures thereof Water, usable.  

Die mit dem Verfahren bevorzugt zu beschichtenden monolithischen Tragkörper weisen üblicherweise Längen bis zu 50 mm, vorzugsweise bis zu 25 mm auf. Die maximal beschichtbare Länge mittels Spritzverfahren hängt von verschiedenen Bedingungen, zum Beispiel vom freien Quer­ schnitt der Zellen (beziehungsweise von der Zelldichte), vom Material, zum Beispiel dessen Saugverhalten, der Spritztechnik, der Viskosität der Dispersion und Tröpfchen­ größe des Sprühnebels ab. Bei wenig porösen Tragkörper- Materialien ist eine Beschichtung längerer Tragkörper möglich als bei hochporösem Material. Bevorzugt wird die Spritzbeschichtung der Tragkörper von beiden Seiten ausgeführt, weil dann die Eindringtiefe in die Zellen sich verdoppelt und auf den jeweiligen Stirnflächen der Monolithe eine die Zellwand umhüllende Beschichtung entsteht, die ein Ablösen des Beschichtungsmaterials im Gasstrom erschwert.Those to be coated preferably with the method monolithic support bodies usually have lengths up to to 50 mm, preferably up to 25 mm. The maximum coatable length by spraying depends on different conditions, for example from the free cross cut the cells (or the cell density),  of the material, for example its suction behavior, the Spray technology, the viscosity of the dispersion and droplets size of the spray. With less porous supporting body Materials is a coating of longer supporting bodies possible than with highly porous material. The is preferred Spray coating of the support body from both sides executed because then the depth of penetration into the cells itself doubled and on the respective end faces of the Monoliths a coating enveloping the cell wall arises that detach the coating material in the Gas flow difficult.

Gegebenenfalls kann es notwendig werden, nach dem Spritzen die Beschichtung in den Strömungskanälen der monolithischen Tragkörper gleichmäßig zu verteilen und eventuell einzelne, durch flüssige Dispersion verschlossene Kanäle zu öffnen. Dies kann zum Beispiel durch Schüttelbewegungen, günstiger aber mittels Durchblasen oder Durchsaugen eines Gasstromes geschehen.It may be necessary after spraying the coating in the flow channels of the monolithic Distribute the support body evenly and possibly individual, open channels closed by liquid dispersion. This can be cheaper, for example, by shaking but by blowing or sucking through a gas stream happen.

Neben der Beschichtung vergleichsweise dünner Tragkörper­ scheiben kann das erfindungsgemäße Verfahren auch zur Herstellung partieller, sich nicht über die gesamte Länge oder den gesamten Querschnitt üblicher monolithischer Tragkörper erstreckender katalytisch aktiver Überzüge mit Erfolg eingesetzt werden.In addition to the coating of comparatively thin supporting bodies The method according to the invention can also be disks to make partial, not covering the whole Length or the entire cross section of common monolithic Supporting body extending catalytically active coatings with Success.

Die monolithischen Tragkörper können schon vor der Spritz­ beschichtung eine auf beliebige Weise aufgebrachte katalytische Beschichtung beziehungsweise Trägerschicht aufweisen.The monolithic support body can be sprayed coating an applied in any way catalytic coating or carrier layer exhibit.

Die aufzubringende katalytische Beschichtung enthält beliebige anorganische Komponenten, gegebenenfalls versetzt mit organischen Zusätzen, zur Verbesserung der Beschichtungseigenschaften oder Beschichtungsgüte. The catalytic coating to be applied contains any inorganic components, optionally mixed with organic additives, to improve the Coating properties or coating quality.  

Entsprechende anorganische Komponenten stellen beispiels­ weise feinteilige und hochoberflächige Oxide wie Aluminiumoxid, Siliziumdioxid, Seltenerdoxide, Titandioxid, Zeolithe, Nickeloxid, Eisenoxid, Erdalkalimetalloxid, Molybdänoxid und Wolframoxid, Silizide wie, Molybdän­ silizid, Metalle wie Platin, Palladium, Rhodium und/oder deren Verbindungen dar. Diese Stoffe können ganz oder teilweise als Oxide und/oder als beliebige lösliche und/oder unlösliche Verbindungen, zum Beispiel als Nitrate, Acetate, Oxalate, Tartrate, Formiate, Carbonate oder Hydroxide in der Dispersion vorliegen. In letzterem Fall erfolgt dann üblicherweise die Überführung in katalytisch aktive, als Promotor wirkende und/oder feinteilige, als Trägermaterial dienende Stoffe der Beschichtung meist durch thermische Zersetzung. Bevorzugt finden Katalysator­ formulierungen Verwendung mit gegebenenfalls stabilisiertem Aluminiumoxid und Ceroxid, Zirkonoxid, Seltenerdoxiden, Erdalkalimetalloxiden, Platinmetallen und/oder deren Vorläufer.Corresponding inorganic components, for example wise fine-particle and high-surface oxides such as Aluminum oxide, silicon dioxide, rare earth oxides, titanium dioxide, Zeolites, nickel oxide, iron oxide, alkaline earth metal oxide, Molybdenum oxide and tungsten oxide, silicides such as, molybdenum silicide, metals such as platinum, palladium, rhodium and / or their compounds. These substances can be whole or partly as oxides and / or as any soluble and / or insoluble compounds, for example as nitrates, Acetates, oxalates, tartrates, formates, carbonates or Hydroxides are present in the dispersion. In the latter case the conversion to catalytic then usually takes place active, acting as a promoter and / or finely divided, as Most of the time, the coating material serves as the carrier material thermal decomposition. Catalysts are preferred formulations Use with stabilized if necessary Aluminum oxide and cerium oxide, zirconium oxide, rare earth oxides, Alkaline earth metal oxides, platinum metals and / or their Precursor.

Monolithische Tragkörper, auf die die Katalysatorschicht oder Trägermaterialschicht aufgespritzt wird, können aus einem beliebigen Metall oder Metallegierung bestehen und zum Beispiel durch Extrusion oder Aufwickeln oder Stapeln oder Falten von Metallfolien hergestellt sein. Bekannt für den Bereich der Abgasreinigung sind temperaturbeständige Legierungen mit den Hauptbestandteilen Eisen, Chrom und Aluminium. Bevorzugt für die Beschichtung sind entsprechende, frei durchströmbare Tragkörper mit oder ohne innere Anströmkanten zur Abgasverwirbelung. Jedoch lassen sich auch Tragkörper mit Schlitzen, Lochungen, Perforationen und Prägungen in der Metallfolie mit zumindest befriedigendem Erfolg beschichten.Monolithic support body on which the catalyst layer or carrier material layer is sprayed on, can any metal or metal alloy and for example by extrusion or winding or stacking or folding of metal foils. Known for the area of exhaust gas cleaning are temperature-resistant Alloys with the main components iron, chrome and Aluminum. Are preferred for the coating corresponding, freely flowable support body with or without inner leading edges for swirling exhaust gas. However, let there are also support bodies with slots, perforations, Perforations and embossing in the metal foil with coat at least satisfactory success.

In gleicher Weise können monolithische Tragkörper aus keramischem Material Verwendung finden. In den meisten Fällen wird es sich bei dem keramischen Material um ein inertes, niedrigoberflächiges Material wie Cordierit, Mullit, α-Aluminiumoxid und Siliciumcarbid handeln. Jedoch kann der verwendete keramische Monolith auch aus hochoberflächigem Trägermaterial wie γ-Aluminiumoxid bestehen. Schließlich besteht auch die Möglichkeit, einen bereits auf beliebige Weise ganz oder teilweise mit einer katalytischen Beschichtung oder dessen Vorläufer versehenen keramischen oder metallischen Tragkörper mindestens eine weitere Beschichtung aufzusprühen beziehungsweise aufzuspritzen. Zur Erzielung besonderer katalytischer Effekte, zum Beispiel zur Erzielung eines Teilumsatzes einer bestimmten Schadstoffkomponente bei Abgaskatalysatoren, ist es dabei oft angebracht, daß die nachträglich aufgespritzte Beschichtung nicht über die gesamte Länge des Tragkörpers verteilt ist.In the same way, monolithic support bodies can be made ceramic material are used. In most  Cases, the ceramic material will be a inert, low-surface material such as cordierite, Act mullite, α-alumina and silicon carbide. However the ceramic monolith can also be used high-surface carrier material such as γ-aluminum oxide consist. Finally, there is also the option of one already in any way wholly or partly with one catalytic coating or its precursor provided ceramic or metallic support body at least one spray on further coating respectively spray on. To achieve special catalytic Effects, for example to achieve partial sales a certain pollutant component Exhaust gas catalysts, it is often appropriate that the subsequently sprayed coating not over the entire length of the support body is distributed.

Bevorzugt erfolgt das Aufbringen der vollständigen Katalysatorformulierung durch Spritzen in einem einzigen Schritt. Jedoch können auch zunächst nur Teile davon, zum Beispiel das meist oxidische Trägermaterial allein mit gegebenenfalls einem Teil der katalytischen Komponenten und/oder Promotoren, aufgespritzt werden. Anschließend können durch Imprägnieren nach beliebigen Verfahren, zum Beispiel durch Tauchen, Spritzen und Übergießen die restlichen katalytischen und/oder als Promotoren wirkenden Komponenten aufgebracht werden.The complete application is preferably carried out Catalyst formulation by spraying in one Step. However, at first only parts of it can be used Example with the mostly oxidic carrier material alone optionally part of the catalytic components and / or promoters. Subsequently can be impregnated by any method to Example by diving, spraying and pouring over the remaining catalytic and / or acting as promoters Components are applied.

Ebenso kann auf die durch Spritzen erzeugte erste Schicht aus anorganischen Stoffen mindestens eine weitere Schicht, vorzugsweise durch Spritzen, aufgebracht werden. Auf diese Weise lassen sich schichtartige Strukturen mit gleicher oder bevorzugt unterschiedlicher Zusammensetzung erzeugen. In der Regel wird mindestens eine dieser Beschichtungen eine Katalysatorformulierung sein. Likewise, the first layer produced by spraying at least one further layer made of inorganic substances, preferably by spraying. To this Layer-like structures can be created with the same or preferably produce different compositions. As a rule, at least one of these coatings be a catalyst formulation.  

Mittels der Spritzbeschichtung lassen sich auf dem Tragkörper durch entsprechende Abdeckung beim Spritzvorgang, zum Beispiel am Randbereich, auf einfache Weise beschichtungsfreie Zonen schaffen. Solche Zonen werden zum Beispiel dann vorgeschlagen, wenn Teile des Katalysators später beim Einbau in ein Gehäuse durch Halterungen abgedeckt werden. Durch Verzicht auf eine vollständige Beschichtung lassen sich nämlich Kosten für Beschichtungsmaterial sparen, was besonders bei vergleichs­ weise teuren edelmetallhaltigen Katalysatorformulierungen von Bedeutung ist. Ebenso können Reinigungsarbeiten über­ flüssig werden, zum Beispiel dann, wenn fügetechnische Verbindungen am metallischen Formkörper nachfolgend angebracht werden.The spray coating can be used on the Support body by appropriate cover at Spraying process, for example at the edge area, on simple How to create coating-free zones. Such zones are proposed, for example, if parts of the Catalyst later when installed in a housing Brackets are covered. By waiving one full coating can namely cost for Save coating material, which is particularly the case with comparative wise expensive precious metal-containing catalyst formulations is important. Likewise, cleaning work can be done via become fluid, for example when joining technology Connections to the metallic molded body below be attached.

Schließlich läßt sich durch das Spritzverfahren auch leicht eine ungleichmäßige Beschichtung über den Tragkörper- Querschnitt, zum Beispiel eine Beschichtungsverdickung in der Trägermitte zur Verbesserung der Strömungsverteilung des katalytisch zu behandelnden Gases, realisieren. Ebenso lassen sich auch Beschichtungsgradienten über die Länge des Katalysatorkörpers einstellen, indem eine Stirnfläche des Monolithen länger und/oder stärker besprüht wird als die andere.Finally, it can also be easily sprayed an uneven coating over the supporting body Cross section, for example a coating thickening in the center of the beam to improve flow distribution of the gas to be catalytically treated. As well can also coating gradients over the length of the Adjust the catalyst body by one end face of the Monolith is sprayed longer and / or more than that other.

Eine weitere Ausgestaltung der Erfindung besteht darin, bei Bespritzen beider Stirnflächen eines Tragkörpers jede Stirnfläche mit einer unterschiedlichen Beschichtungs­ zusammensetzung zu versehen, wobei zumeist eine davon eine katalytisch aktive Zusammensetzung aufweist, um so ein Katalysatorsystem mit Doppelfunktion zu erhalten. Beispielsweise können auf diese Weise Abgaskatalysatoren erhalten werden, die die NO_x-Reduktion auf der einen und die CO-Oxidation bevorzugt auf der anderen Seite des Katalysators durchführen. Another embodiment of the invention is to provide each end face with a different coating composition when spraying both end faces of a support body, one of which mostly has a catalytically active composition, so as to obtain a catalyst system with a double function. For example, exhaust gas catalysts can be obtained in this way, which carry out the NO _x reduction on one side and the CO oxidation preferably on the other side of the catalyst.

Gleichermaßen ist es möglich, durch Aufspritzen von der späteren Eintrittsseite her eine Schutzbeschichtung auf eine vorhandene Katalysatorbeschichtung, zum Beispiel gegen Einflüsse von Katalysatorgiften wie Blei, Zinn und Phosphor aufzubringen. Diese Schutzbeschichtungen haben zumeist die Aufgabe, durch ihre hochoberflächige Struktur die Katalysatorgifte ganz oder teilweise abzufangen, zu adsorbieren und nicht zur katalytisch aktiven Schicht vordringen zu lassen. Eine bevorzugte Ausführung ist daher die vollständige Überdeckung des darunter befindlichen Katalysators durch erfindungsgemäßes Aufspritzen.Similarly, it is possible by spraying on the a protective coating on the later entry side an existing catalyst coating, for example against Influences of catalyst poisons such as lead, tin and phosphorus to apply. These protective coatings mostly have the Task, due to its high surface structure To trap catalyst poisons in whole or in part, too adsorb and not to the catalytically active layer to advance. A preferred embodiment is therefore the complete coverage of the underlying Catalyst by spraying according to the invention.

In gleicher Weise wie Schutzbeschichtungen lassen sich auch zur Adsorption oder Absorption zumeist gasförmiger Komponenten wie Kohlenwasserstoffe, Stickoxide und Kohlen­ monoxid befähigter Materialien, wie dotierte und undotierte Zeolithe verschiedenster Zusammensetzung und Struktur, aufbringen.In the same way as protective coatings can also be for adsorption or absorption mostly gaseous Components such as hydrocarbons, nitrogen oxides and coal monoxide-enabled materials, such as doped and undoped Zeolites of various compositions and structures, apply.

Katalysatoren, die durch das Spritzverfahren mit feinteiligem Trägermaterial beschichtet worden sind, eignen sich zur Durchführung verschiedener Stoffumwandlungen. Insbesondere lassen sich erfindungsgemäß beschichtete Katalysatoren zur Abgasreinigung einsetzen. Bevorzugt ist die Anwendung für die Schadstoffkonversion von Verbrennungsmotoren.Catalysts by spraying with finely divided carrier material have been coated to carry out various substance conversions. Especially can be coated according to the invention Use catalytic converters for exhaust gas cleaning. The application for pollutant conversion is preferred of internal combustion engines.

Claims (5)

1. Verfahren zum Aufbringen einer Dispersionsbeschichtung auf die Kanalwandungen von Strömungskanälen monolithischer, scheibenförmiger Katalysator-Tragkörper von allgemein zylindrischem Querschnitt, welche von der Eintrittsstirnfläche zur Austrittsstirnfläche von den Strömungskanälen durchzogen werden, unter Verwendung einer Beschichtungsdispersion aus feinteiligen anorganischen Stoffen und/oder deren Vorläufer, dadurch gekennzeichnet, daß die Beschichtung der Kanalwandungen durch Spritzen oder Sprühen auf die Stirnflächen der Tragkörper erfolgt und die feinteiligen Stoffe aus einer Katalysatorzusammensetzung, einer Katalysatorvorstufe oder einem ab- oder adsorbierenden Material bestehen.1. A method for applying a dispersion coating to the channel walls of flow channels of monolithic, disk-shaped catalyst carrier bodies of generally cylindrical cross section, which are traversed by the flow channels from the inlet end surface to the outlet end surface, using a coating dispersion of finely divided inorganic substances and / or their precursors, thereby characterized in that the coating of the channel walls is carried out by spraying or spraying on the end faces of the support body and the finely divided substances consist of a catalyst composition, a catalyst precursor or an absorbing or adsorbing material. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß der monolithische Tragkörper beim Aufspritzen der Dispersion partiell abgedeckt wird.2. The method according to claim 1, characterized, that the monolithic support body when spraying the Dispersion is partially covered. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß von beiden Stirnflächen Beschichtungen unterschiedlicher Zusammensetzung aufgespritzt werden, wovon mindestens eine Beschichtung eine Katalysatorbeschichtung ist.3. The method according to claim 1, characterized, that coatings from both faces different compositions are injected, of which at least one coating is one Catalyst coating is. 4. Verfahren nach den Ansprüchen 1 bis 3, dadurch gekennzeichnet, daß die Beschichtung mehrlagig aufgebracht wird, wobei die einzelnen Lagen die gleiche oder eine unterschiedliche Zusammensetzung aufweisen und mindestens eine Lage eine Katalysatorbeschichtung darstellt.4. The method according to claims 1 to 3, characterized, that the coating is applied in multiple layers, wherein the individual layers the same or one  have different compositions and at least one layer of a catalyst coating represents. 5. Verwendung eines nach den Patentansprüchen 1 bis 4 beschichteten monolithischen Katalysators zur Abgasreinigung.5. Use of a coated according to claims 1 to 4 monolithic catalyst for exhaust gas cleaning.