DE1926943A1 - Method of gluing - Google Patents
Method of gluingInfo
- Publication number
- DE1926943A1 DE1926943A1 DE19691926943 DE1926943A DE1926943A1 DE 1926943 A1 DE1926943 A1 DE 1926943A1 DE 19691926943 DE19691926943 DE 19691926943 DE 1926943 A DE1926943 A DE 1926943A DE 1926943 A1 DE1926943 A1 DE 1926943A1
- Authority
- DE
- Germany
- Prior art keywords
- adhesive
- particles
- adhesive mixture
- carbon particles
- microns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
CB-Kp. 2575V6S *i.R. Grace & Co*CB-Kp. 2575V6S * i.R. Grace & Co *
Weif York» N.Y.A.St,A. Hamburg, 19. Mai 1969Weif York »N.Y.A.St, A. Hamburg, May 19, 1969
Verfahren zum VerklebenMethod of gluing
Die vorliegende Erfindung betrifft ein Verfahren zum Verkleben von Gegenständen und bezieht sieh insbesondere auf die Verwendung thermisch aktivierter Klebstoffmischungen bei der Verbindung zweier Werkstücke.The present invention relates to a method for Bonding of objects and relates in particular to the use of thermally activated adhesive mixtures when connecting two workpieces.
Gent&ss Erfindung wird ein Verfahren zum Verkleben zweier Gegenstunde vorgeschlagen, welches dadurch gekennzeichnet ist« daß man zwischen die beiden Oberflächen der zu verklebenden Gegenstände eine thermisch aktivier* bare KLebstoffmlschuns bringt, -welche Kohlenstoffteilchen enthält und daS man das zusammengesetzte Gebilde der Einwirkung eines magnetischen Hoohfrequenzweehselfeldeg unterwirft, bis die Klebstoffmlschung ausreichend erwärmt und aktiviert i3t.Gent & ss invention is a method of gluing two counter-lesson proposed, which is characterized by the fact that there is one between the two surfaces of the objects to be glued a thermally activated * Bare adhesive brings us what carbon particles and that one contains the compound structure the action of a magnetic high frequency alternating field submits until the adhesive deletion is sufficient warms and activates i3t.
Die Klebstoffmischung kann ein thermoplastisches» heißschraelsendes oder wSrmehSrtbares synthetisches Harz oder dessen Ausgangsprodukt, beispielsweise ein polymerisierbares Monomeres oder ein niedriges Polymeres enthalten· Die thermoplastische Mischung oder die heiße Schmelze kann gegebenenfalls einen Weichmacher enthalten. Beispiele für thermoplastische Stoffe sind Polyolefine, Insbesondere Polyäthylen, Polypropylen, Mischpolymerisate aus Äthylen und Propylen sowie Polystyrol und Polyvlnylver-The adhesive mixture can be thermoplastic or heat-treatable synthetic resin or its starting product, for example a polymerizable one Contain monomer or a lower polymer The thermoplastic mixture or the hot melt can optionally contain a plasticizer. Examples for thermoplastics are polyolefins, in particular Polyethylene, polypropylene, copolymers of ethylene and propylene as well as polystyrene and polyvinyl
0 9 8 4 9/1330 BAB omm*L 0 9 8 4 9/1330 BAB omm * L
bindungen, vie beispielsweise waiehgestelltes Polyvinylchlorid, Polyvinylacetat und Polyvinyl ao at ale, wie Butyral· Beispiele für helßoehm'elsende Mischungen sind unter anderem hochmolekulare lineare Polyamide. Wannehärtbare HargsBischungen enthalten unter anderes vsrnetzbare Polyester und ferner Phenol/Foruialdehydharsa, Harnstoff/Formaldehydharze -und Melaisin/Formaldehydharze» Die Mischungen können gegebenenfalls zwei oder sshrera Komponenten enthalten, wie beispielsweise ein Melamin/ oder Phenol/Pormaldehydharz und ein Polyvinyl ac et al.bonds, such as polyvinyl chloride Polyvinyl acetate and polyvinyl ao at ale, such as Butyral · Examples of helßoehm'elsende mixtures are including high molecular weight linear polyamides. Tub-curable Hargs mixtures contain, among other things, wettable polyesters and also phenol / formaldehyde harsa, Urea / formaldehyde resins and melaisin / formaldehyde resins » The mixtures can optionally be two or more Contain components such as a melamine / or phenol / formaldehyde resin and a polyvinyl ac et al.
Die Kohlenstoffteilchen können Graphit oder amorpher Kohlenstoff sein, wie beispielsweise Ru.3* Dar Graphit kann in Form von nahezu kugelförmigen Teilchen oder in Form von dünnen Plättchen verschiedener GröSe vorliegen. Die kugelförmigen Teilchen haben gewöhnlich einen Durchmesser von 100 Mikron oder weniger und können ]50 Kikz»on und kleiner sein. Amorpher Kohlenstoff steht in dar verschiedensten Teilchengröße zur Verfügung, wobei hler wiederum die Teilchen etwa kugelförmig sein können.The carbon particles can be graphite or amorphous carbon, such as Ru.3 * Dar graphite can be in the form of almost spherical particles or in the form of thin platelets of various sizes. The spherical particles usually have a diameter of 100 microns or less and can] 50 kikzon and be smaller. Amorphous carbon is available in a wide variety of particle sizes again the particles can be roughly spherical.
Diese Teilchen brauchen nicht vollständig aus Kohl engt&?f zu bestehen· Beispielsweise kann der Kohlenstoff als Überzug auf einem inerten, elektrisch nicht leitenden TrSger vorhanden sein, beispielsweise auf sehr kleinen GlaskUgelohen. Derartige Stoffe werden erhalten, indem man die Trägerteilchen, die gewöhnlich kugelförmig sind, mit einer kolloidalen Graphitsuspension in Wasser oder in einer anderen Flüssigkeit behandelt, wobei diese Flüssigkeit vorteilhafterweise noch ein nicht leitendes harz artiges Bindemittel enthalten kann· Die Trägeri;eliehen können einen Durchmesser von 20 bis 850 Mikron haben. Auch diese zusammengesetzten oder beschichteten Teilchen im folgenden als Kohlenstoff teilchen bezeichnet»These particles do not need to be completely narrowed from cabbage &? F to insist · For example, the carbon can be used as a coating on an inert, electrically non-conductive TrSger be present, for example on very small ones GlaskUgelohen. Such substances are obtained by the carrier particles, which are usually spherical, treated with a colloidal graphite suspension in water or in another liquid, this liquid being treated advantageously a non-conductive resin-like one May contain binders · The carriers can be 20 to 850 microns in diameter. Also these composite or coated particles hereinafter referred to as carbon particles »
9098A9/ 1 3309098A9 / 1 330
ΒΑ© ORIGIMALΒΑ © ORIGIMAL
Obgleich die Größe der sl&aeXnsn KohlesistofitsiXohön nicht wesentlich ist und duraa anöer* Faktoren vis mechanidohe Festigkeit der endgültigen El öl-3Gh iaht und deren geforderte Dicke afchfiagt, liegt der durohschftittliche Durchmesser etwa bei 1 mia und racist oei etwa 400 bis 500 Mikron. Wenn die Veilchen in der Klebmisohung einigermaßen voneinander entfernt sind, so b^Ktioimt sieh die untere Grenze dadurch, daß die Teilchengröße mindestens das Doppelte der wirksamen Tiefe der StremdurcfeflrlYisung entsprechen muß. Wenn jedoch die Konzentration und Verteilung der Kohlenstoff eilehcsi so bemessen ist, daß mehrere Teilchen zusammen ein elektrisch leitendes Netz bilden, können kleinere Teilchen verwendet werden. Die Tief· der StroMurohdringung wird durch verschiedene Faktoren einschließlich dor Frequenz und der Stärke des magnetischen Weohaelfeldes bestimmt, so daß keine für alle PHlIe geltende untere Grenze für die Teilchengröße angegeben werden kann· Im allgemeinen soll die Teilchengröße nicht kleiner ale 30 Mikron und vorzugsweise Ir. eimern Bereich von 50 bia 200 Mikron und insbesondere In einem Bereich von 75 bis 150 Mikron liegen, sofern nicht ein elektrisch leitendes Nets der Teilchen gebildet wird* Selbst wenn ein derartiges leitendes Netz gebildet wird, sind auch die oben angegebenen OröSenbereiche am besten geeignet. Unter gleichen Bedingungen erreicht der Klebstoff seine Aktivierüngstsmii«.»af,ur umso schnei] ev, je größer die Teilchen sind.Although the size of the sl & aeXnsn KohlesistofitsiXohön is not essential and duraa anöer * factors vis mechanical strength of the final El oil 3Gh iaht and whose required thickness is less, the average diameter is about 1 mia and racist oei about 400 to 500 microns. When the violets in the glue mix are somewhat distant from one another, so b ^ Ktioimt see the lower limit in that the particle size is at least twice the effective depth of the stress relief must correspond. However, if the concentration and distribution of carbon eilehcsi is such that several particles together form an electrically conductive network smaller particles can be used. the The depth of the current penetration is determined by various factors including the frequency and the strength of the Magnetic Weohaelfeldes determined, so that no lower limit for the particle size valid for all PHlIe · In general, the particle size should not be smaller than 30 microns and preferably Ir. buckets range from 50 to 200 microns and especially In be in the range of 75 to 150 microns, unless an electrically conductive network of particles is formed * Even if such a conductive network is formed, the range of exposure above is also best suitable. Under the same conditions, the adhesive reaches its activation smii «.» Af, ur all the faster, the larger the particles are.
Das GewichtBverhältnis der Kohlenstoffteilchen zu den* Klebstoff kanu in einem breiten Bereich von beispielsweise 5*95 bis 80:20 sclraanlren und wird entsprechend dan Eins&tzbedingunsen aucgexShlt. -Je boiler dieses Verhältnis ist, desto schneller kann die fföschung durch ein Feld bei gegebeiu-r Frequenz unä Stärk© erhitzt werden,«The weightB ratio of the carbon particles to the * Adhesive can be sclraanlren in a wide range of, for example, 5 * 95 to 80:20 and is danced accordingly Conditions of use also excluded. -The boiler this ratio is, the faster it can be cleared through a field be heated at a given frequency and strength, «
909849/1330909849/1330
seite wird duuch einsn £.tjoßsn Aiiijföil en teilchen die Stsifheit der fertigen Klebstoffschient erhöht, was nicht immer ertnlngoht isEt. Farner kanr. dadurch die Benetzbarkeit des Klebstoffes an den zu vor« bindenden Oberflächen leiden, so daß auch die EaftfShiskeit der Klebstoff schicht, insbesondere iia oberen Bereich der Mengenverhältnisse verringert wird· Der EInfluß dieser Wirkungen schwankt ,1© nach Art der iluBganseklebstoffmi3chung. Mischungen, wäsche stark kristalline Polymere enthalten, wie Polyäthylen hoher Dichte, sind besonders empfindlich, da die Teilchen sich in dem amorphen Teil der polymeren Sohlcht Ir.onsentrierai, so daß sehr hohe lokale Konzentrationen entstehen, selbst wenn die Gesamtbeladung verhältnlemUssig niedrig ist.On the side, you will not only see a small amount of j oßsn Aiiijföil en particles, but the stiffness of the finished adhesive rail is increased, which is not always the case. Farner Kanr. as a result, the wettability of the adhesive on the surfaces to be pre-bonded deteriorates, so that the effectiveness of the adhesive layer, especially in the upper range of the quantitative proportions, is reduced. The influence of these effects varies depending on the type of joint adhesive mixture. Mixtures containing highly crystalline polymers, such as high density polyethylene, are particularly sensitive because the particles are concentrated in the amorphous part of the polymeric base, so that very high local concentrations arise, even if the total loading is relatively low.
Wenn kleinere Teilchen mit beispielsweise einem Durchmesser unter j50 Mikron verwendet werden, so muß man sich darauf verlassen, daß ein elektrisch leitendes Netz gebildet wird, v.obei die Konzentration der Teilchen ausreichen soll, um einen geeigneten Schttttvolumen-Widerstand im allgemeinen zwischen 10 und 5 χ 10 Ohm/cm sur Erzielung der besten Ergebnisse zu erreichen.If smaller particles, for example less than 50 microns in diameter, are used, one must rely on the formation of an electrically conductive network, especially the concentration of the particles being sufficient to provide a suitable bulk volume resistance, generally between 10 and 5 χ 10 ohms / cm sur to achieve the best results.
Mit dem erfindungsgeeässen Verfahren kann man Gegenstände verkleben, deren Oberflächen aus verschiedenen Polymeren bestehen, beispielsweise aus verstärkten oder nichtverstSrkten thermoplastischen oder tiSrm^hKrfbaren Harzen oder Gummi oder Kombinationen .dieser Werkstoffe. Bei der Auswahl der geeigneten Klebstoffe für eine bestimmte Kombination von Werkstoff «si kann xan sich an das den KLebstoffachmann bekannte Wissen halten. 3s können beliebig viel Oberflächen gleichzeitig; miteinander verbunden werden, vorausgesetzt, daß ein entsprechend großes Magnetfeld geschaffen wird, welches in jeder Klebstoff-The method according to the invention can be used to glue objects whose surfaces consist of different polymers, for example of reinforced or non-reinforced thermoplastic or thermoplastic resins or rubber or combinations of these materials. When selecting the suitable adhesives for a certain combination of materials, you can apply the knowledge known to the adhesive specialist. 3s can be any number of surfaces at the same time; are connected to each other, provided that a correspondingly large magnetic field is created, which in each adhesive
909849/1330 HBOlMlNAL 909849/1330 HBOlMlNAL
schiene Hifcse erzeugt. In i.^lch«a Pttl.ler?. k'Jnnen auch Laminate aus Mehrere» vterkstüiTen heegestelXb wsvdm. Schiene Hifcse generated. In i. ^ Lch «a Pttl.ler ?. Laminates can also be made from several »vterkstüiTen heegestelXb wsvdm.
Das erfindungsgeinfisse Verfahren ist besonders baiia Va?- binden der Deckel au.? KunststoffbsliMltera und Insfoesondere HunetBtoffflaseaen gssig&et· Da» übliche V$r~ föbren jjuin V^rschlieSea von FXaschen aalt; «sineni korken ist bei Kunststoffjtl&soh&a luißseigiAöl; iinö insbesondere bei Flaschen i-v.a PplyviDylchlorld^ da dl« üaelsten Plnsahoa durch den sum VerschliöSssi es'fo.^ürliohfs Druck zarstört werden, durch das erf lndimgsgeraäss® Vorfahren kann «an ohne Verformung eines* Xunststoffflassolis diese mit oinera ßcckel bsi hoher Arbeitsgesch^rinölgkolt verschließen, die bei schriallaufaaäcsn Fl&sohenverschlufi» maschinen erforderlich ist. Da die Hitze in erster Linie in dem Klebstoff selbst erzeugt wird, kann der Klebstoff ohne weiter© UUrmezufuhren zu dem VerschlußstUck oder der Flasche aktiviert werden, so daß eine Verformung des Verschlußes vermieden wird» der gewöhnlich aus Kunststoff, belspieleweiae aus Polyvinylchlorid hergestellt wird. Auoh eine Verformung dar Flaschen wird verhindert.The method according to the invention is particularly baiia Va? - tie the lid off. KunststoffbsliMltera and Insfoes special HunetBtoffflaseaen gssig & et · The usual V $ r ~ föbren jjuin V ^ rschlieSea von FXaschen aalt; «Sineni cork is at Kunststoffjtl & soh & a luißseigiAöl; iinö especially with bottles i-v.a PplyviDylchlorld ^ da dl « üaelsten Plnsahoa through the sum VerschliöSssi es'fo. ^ ürliohfs Pressure can be disturbed by the inventor's ancestors without deforming a plastic lassola these with oinera ßcckel to high Arbeitsgesch ^ rinölgkolt close that at schriallaufaaäcsn Fl & sohenverschlufi » machinery is required. Because the heat in the first place in the adhesive itself is generated, the adhesive can without further feeding to the closure piece or of the bottle are activated, so that a deformation of the Closure is avoided »which is usually made of plastic, belspieleweiae is made from polyvinyl chloride. Deformation of the bottles is also prevented.
Die Frequenz des magnetischen Wechselfeldes zvtr Erwärmung liegt in einem Bereich von 0,5 bis 100 MHz oder mehr und gewöhnlich in einem Bereich von 15 bis 30MHi, im allgemeinen werden Vorrichtungen mit einer Leistung von etwa O1I bis 20 kW verwandet« wobei Jedoch eine Leistung von 2 bis 5 kW im allgemeinen ausreicht« Vorzugsweise wird die Frequenz xmd die Feldstärke entsprechend der GrSfle und de? ?orm der Werkstoffe und der Zusammensetzung der Klebstoffe ausgewählt^ so daß eine wirksame Erhitzung' in S Hinuten oder weniger? gewöhnlich in einigen Sekunden erfolgt«The frequency of the alternating magnetic field zvtr heating is in a range of 0.5 to 100 MHz or more, and usually in a range of 15 to 30MHi, in general devices are verwandet with a power of about O 1 I up to 20 kW "except that a Power from 2 to 5 kW is generally sufficient «Preferably the frequency xmd is the field strength according to the size and de? ? form of the materials and the composition of the adhesives selected ^ so that an effective heating 'in S Hinuten or less? usually takes a few seconds "
909849/1330909849/1330
DIo zur Durchführung d^sDIo to carry out d ^ s
verwendete Vorrichtung 1st Ia der bslllsgeaden nSher erläutert. Sie besteht aus sines Generator X9 dor an eine elektrische Leitung 2 abgeschlossen 1st« Ferner ist eine elektrisch betriebene Zelteinsfcollvsrrrteht'jEsg 3 vorgesehen, die den Gsnsrato? betreibt, so daß das Wechselfeld eine vorbestiasato Zelt au einer Arbeifcsspule 4 fuhrt. Ein typischer Generator arbeitet mS.t oiner leistung von. 5 kW und 27,12 Megahertz ^e Sekunde» Me ilrbeitsspule und deren unmittelbare tfcngebua^ lat mit '.sinaip Kühlvorrichtung verbunden, va>*s~<sgsttdise einem thermostatisch gesteuerten abgeschlossenen L^J.tungasystem 5 mit destillier« tem .Wasser als Kühlmedium« Weniger reinso Hasser ergibt größere Energievspluöte im Klihlsysteia und itsnn selbst so weit erhitzt weiden* daß die Wirksamkeit verringert wird· Verschiedene Vorriohtungen, die 3chGm&tlsöh mit-6 bezeichnet sind» können verwendet «erden» um die zu verbindenden Werkstücke dar Arbeltsspule in der gewischten Stellung zuzuführen· Die Ausbildung der Arbeitsspalt wird so ausgewählt, daS sie der Fora und der Größe der zu verbindenden Werkstücke entspricht» Bei einer anderen Arbeitsweise kann die Arbeltsspule gegenüber den au verbindenden Werkstücken bewegbar sein*The device used is explained in the bslllsgeaden nSher. It consists of a generator X 9 dor connected to an electrical line 2 1st «Furthermore, an electrically operated tent installation 3 is provided, which the Gsnsrato? operates so that the alternating field leads a vorbestiasato tent on a work coil 4. A typical generator works with a power of. 5 kW and 27.12 megahertz ^ e second "measuring coil and its direct tfcngebua ^ lat connected to a sinaip cooling device, especially a thermostatically controlled closed L ^ junga system 5 with distilled water as Cooling medium «Less pure so hater results in greater energy surges in the Klihlsysteia and itsnn itself heated so far * that the effectiveness is reduced · Various devices, which are designated 3chGm & tlsöh with -6» can be used to «ground» the workpieces to be connected to the work coil in the wiped Position · The design of the working gap is selected in such a way that it corresponds to the shape and size of the workpieces to be connected.
Im folgenden soll die Erfindung anhand von Beispielen näher erlSutert werden, wobei alle Mengenangaben, sich auf das Gewicht beziehen·In the following, the invention is intended to be based on examples will be explained in more detail, with all quantities, themselves refer to weight
57 Teile plättchenföraiger Graphit wurden ralb 45 Teilen Polypropylen auf eine» Brabender-Plastographsn Die erhaltene Mischung wurde bsi 200°C zu einea 0*5 dicken Bogen verformt· Bin Abschnitt dieses Bogens wurde swiechen zwei 12,7 on breite Polypropylenstreifen von57 parts of graphite were plättchenföraiger ralb 45 parts of polypropylene to a "Brabender Plastographsn The obtained mixture was bsi 200 ° C to Onea 0 * 5 thick sheet deformed · Bin portion of this sheet was 12.7 swiechen two on wide strip of polypropylene
9/13309/1330
6,3 oan DlokG gelegt, wr-bei cine Überlappung van 32^7 cmi entstand. Diese Sehlohten wurden dean suaaniinengepreot und in eine Spule mit vier VJIndungo^ ü&hrsxsht, die mit einem Induktionsgenerator von 1,2 kW und i>7#12 Megahertz verbunden wer. Die Arbeitsspule wurde 2C Sekunden mit einem Anodenstrom von 0,2 Anp^re betrastoer., wobei da« graphithaltige Polypropylen und die damit in VerbluduEß stehende Poly propylenoberf lache genügend bis zur Schmelze erhitzt wurde. Die verklebten Werkstück« wurden eine Minute vor Entfernung aus der Arbej-taspule ebjtekühli;' und dann in einen Hounsfiold-iensoaiefcei· :jur Bfciitimnmru; der Klebfeatigkeit bei eJnrr TrenngGechwlndigkeli: der Greifbacken von 2,5 ora Je Minute untersucht.. Die Sciiorfestigkeit betrug 7 kg/ena .6.3 oan DlokG, wr- at an overlap of 32 ^ 7 cm. These tubes were dean suaaniinengepreot and put into a coil with four VJIndungo ^ ü & hrsxsht, which were connected to an induction generator of 1.2 kW and i> 7 # 12 megahertz. The working coil was energized for 2C seconds with an anode current of 0.2 Anode, the polypropylene containing graphite and the polypropylene surface, which was thus blurry, being heated sufficiently until it melted. The glued workpiece "were ebjtekühli one minute before removal from the work coil;" and then in a Hounsf i old-iensoaiefcei ·: jur Bfciitimnmru; the stickiness at eJnrr TrenngGechwlndigkeli: the gripping jaws of 2.5 ora per minute examined. The sciior strength was 7 kg / year.
30 Teile des in Beispiel 1 verwendeten Graphits wurden mit 70 Teilen eines hoehscnlagfesten Polystyrols vermischt und zu einer Dichtungsscheibe verpreßt. Diese Qichtungssoheibe wurde zwischen dem Körper und dem Deckel eines PolystyrolbatteriebehSlters gelGgt, Der Batteriebehälter wurde dann in eine rechtwinklige einspulige Arbeitsepule gelegt, so daß die Klebraischung dicht cn der Spule lag. Die Arbeitsspule wurde mit einem 5 IW Induktionsgenerator mit 27,12 Megahertz 30 Sekunden mit einem Anodenstrom von 0,3 Ampere betrieben. Danach hatte sich zwischen dem BatteriebehSlter in dem Deckel eine feste Verbindung gebildet.30 parts of the graphite used in Example 1 were mixed with 70 parts of a high-impact polystyrene and pressed to form a sealing washer. This sealing washer was placed between the body and the lid of a polystyrene battery container. The battery container was then placed in a rectangular single-coil work coil so that the adhesive mixture was tight against the coil. The work coil was operated with a 5 IW induction generator at 27.12 megahertz for 30 seconds with an anode current of 0.3 amperes. Thereafter, had formed between the BatteriebehSlter in the cap a firm connection.
Es wurden verschiedene Hlschungen hergestellt, welche 10, bzw. 20, bzw. 40, bzw. 57 % amorphe Kohlenstoff teilchen In dem Polypropylen gemSss Beispiel 1 enthielten.Various Hlschungen were prepared containing 10, or 20, or 40, or 57% amorphous carbon particles in the polypropylene gemSss Example 1 contained.
9098Λ9/Τ330 BAB OR.0.NAL9098Λ9 / Τ330 BAB OR.0.NAL
Aus diesen Massen wurden S&heisea mit einem. von 31,7 und einer Wandstärke vor. 2,0 rom geformt. Dies* Scheiben wurden dann in eine ZAifcispiilige Spule gegeben und wurden von einem Halter aus Pol.ytetivafliioi'li'fchylec. gehalt«!. Die Spule vrurde- 60 S'Gicundon mit e-inam Anodenstrora von 0,3 impure mit einem Generator gemüse Beispiel 1 erhitzt. Die Temperatur dieser öcUci.bs wurde unmittelbar nach Afcsohaltcri de» Generators durch ein Thermoelement geraessen, das an de*1 SchsibenoberfltichG auflag. Γη verfolgenden Tabelle i«t dor ?empc?aturansticg der Sobsibe gegenüber der Raumtemperatur zus&ramGn rait dew Voluraenwiderstand der entsprecheaiden Mischung gemKas British Standard Nr. 278*, Verfahren 202B, mit Metallfolienelektroden angegeben»These masses became S & heisea with one. of 31 , 7 and a wall thickness . 2.0 rome shaped. These * disks were then placed in a double-sided spool and were removed from a holder made of Pol.ytetivafliioi'li'fchylec. salary"!. The coil was heated to 60 S'Gicundon with e-inam anode current of 0.3 impure with a generator vegetable example 1. The temperature of this öcUci.bs was screened eat immediately after Afcsohaltcri de »generator by a thermocouple which rested on de * 1 SchsibenoberfltichG. Γη following table i «t dor? Empc? Aturansticg the sobsibe compared to the room temperature together & ramGn rait the volume resistance of the corresponding mixture according to Kas British Standard No. 278 *, method 202B, indicated with metal foil electrodes»
Kohlenstoff Temperatur- Widerstand (1Carbon temperature resistance (1
in Gew. JE? ans ti es Chm.om)in weight JE? ans ti es Chm.om)
10 4 gröEsr als 710 4 larger than 7
20 18 4.0 - 4.320 18 4.0 - 4.3
40 49 2.3 - 3.140 49 2.3 - 3.1
57 75 2,1 - 2.557 75 2.1 - 2.5
57 Teile Graphit in Form von kleinen KVgelcfcen wurden mit 43 Teilen des in Beispiel 1 verwendeten Polypropylene vermischt und zu einem 1,3 mm dicken Bogen verpreßt. Eir?e Probe dieses Bogen wurde in eine sweispulige Spule ge geben, die tait einem Generator getaäsa Beispiel 2 verbunden 57 parts of graphite in the form of small KVgelcfcen were mixed with 43 parts of the polypropylene used in Example 1 and pressed into a sheet 1.3 mm thick. A sample of this bow was placed in a two-coil spool , which was connected to a generator with Example 2
909849/1330909849/1330
war. Es wurde nit einem Anotfenstrora van 0,i> Ampere gearbeitet. Die Mischung schmolz nach 100 SSakunden.was. An anotfenstrora of 0.1> amperes was used. The mixture melted after 100 seconds.
Obgleich in den Beispielen 1 und 2 eine Klebstoffmischung auf Basis eines therinöplasviseiisn Polymeren entsprechend der Art der au verbindenden Oberflächen verwenden wurde, kann man mit deai erfiiid'tmgsg-sraüssen Verfahren auch Werkstoffe mit Klebstoff eil verbinden., -die in ":Lhi? er Art verschied€?n sind. Selbstverständlich soll ein Klebstoff ausgewählt werden, der für den betreffenden Fall die geeignete Affinität für die zu verbindenden Werkstoffoberflächen hat.Although in Examples 1 and 2 an adhesive mixture based on a thermo-plastic viseiisn polymer was used in accordance with the nature of the surfaces to be connected, it is also possible to connect materials with adhesive using this process Naturally, an adhesive should be selected that has the appropriate affinity for the material surfaces to be joined for the case in question.
Beispiel 5 zeigt den Zusammenhang zwischen dem Widerstand des Kohlenstoff enthaltenden Klebstoffes und der Geschwindigkeit,, mit der die Mischung bei konstanter Eingangsleistung des Generatora erhitzt wird, während Beispiel 4 zeigt, daß man anstsllo von Graphit, wie in Beispiel I9 auch amorphen Kohlenstoff verwenden kann·Example 5 shows the relationship between the resistance of the carbon-containing adhesive and the speed ,, to which the mixture is heated at a constant input power of the Generatora, while Example 4 shows that anstsllo of graphite, using as in Example I 9 and amorphous carbon can ·
Die Verwendung von Kohlenstoffteilchen hat erhebliche Vorteile gegenüber der Verwendung ferromagnetiacher Teilchen, da eratere eine sehr viel kleinere Neigung haben» sich beim Schmelzen der Klebst of fmlsehurig abzutrennen und somit gleiehmUssiger verteilt bleiben und sich vfeniger an der Oberfläohe der Klebstoffschicht ansammeln. Aus den gleichen Gründen lassen sich diese Klebst off mass en weniger schwierig in flüssige Klebstoffmischungen einarbeiten. Darüberhinaus zeigt Kohlenstoff eine geringere Zersetzungseinwirkung der Klebstoffe, die bei einigen ferromagnetischen Metallen auftreten. Darüberhinaus unterliegen, die Teilchen keiner Korrosion. Schließlich ergeben die Kohlenstoff teilchen einen geringeren Verschleiß der Mischvorrichtungen und anderen Vorrichtungen, die zur Herstellung der Klebstoffmassen verwendet werden.The use of carbon particles has been significant Advantages over the use of ferromagnetic particles, since they have a much smaller tendency have »to detach the glue often painfully when it melts and thus remain more evenly distributed and more likely to accumulate on the surface of the adhesive layer. For the same reasons, these adhesives are less difficult to mass-form into liquid adhesive mixtures incorporate. In addition, carbon shows a lower decomposition effect of the adhesives some ferromagnetic metals occur. Furthermore the particles are not subject to corrosion. Finally, the carbon particles result in less wear the mixing devices and other devices used to make the adhesive masses.
90984 9/1.330 BAB omQ1NAL 90984 9 / 1.330 BAB omQ1NAL
Claims (2)