DE1596749A1 - Glass compositions - Google Patents

Glass compositions

Info

Publication number
DE1596749A1
DE1596749A1 DE19661596749 DE1596749A DE1596749A1 DE 1596749 A1 DE1596749 A1 DE 1596749A1 DE 19661596749 DE19661596749 DE 19661596749 DE 1596749 A DE1596749 A DE 1596749A DE 1596749 A1 DE1596749 A1 DE 1596749A1
Authority
DE
Germany
Prior art keywords
composition
glass
oxides
component
mgo
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
DE19661596749
Other languages
German (de)
Other versions
DE1596749B2 (en
DE1596749C3 (en
Inventor
Edmond Groene
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Compagnie de Saint Gobain SA
Original Assignee
Compagnie de Saint Gobain SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Compagnie de Saint Gobain SA filed Critical Compagnie de Saint Gobain SA
Publication of DE1596749A1 publication Critical patent/DE1596749A1/en
Publication of DE1596749B2 publication Critical patent/DE1596749B2/en
Application granted granted Critical
Publication of DE1596749C3 publication Critical patent/DE1596749C3/de
Granted legal-status Critical Current

Description

Dr.-Ing. Heinrich SchellerDr.-Ing. Heinrich Scheller Patentanwalt Aachen, den 10. Februar 1966Patent attorney Aachen, February 10, 1966 A A C H E N, Zollernstr. t .. . _ . , _ ΛΛ ,__AACHEN, Zollernstr. t ... _. , _ ΛΛ , __

zy.n *a 25!82 Mein Zeichen P 11 657 zy.n * a 25! 82 My reference P 11 657

Dr. Expl.Dr. Expl.

Gompagnie de Saint-Gobain, Neuilly-sur-Sein·Gompagnie de Saint-Gobain, Neuilly-sur-Sein

(Jrankreicli)(Jrankreicli)

Priorität aus der französischen Patentanmeldung Nr. 5318 vom 12. Februar 1965Priority from French patent application No. 5318 of February 12, 1965

Glaikompo»itionenGlass compositions

Sie Erfindung betrifft Glaskompositionen ohne Kalk mit besonders vorteilhaften Sigenschaften·The invention relates to glass compositions without lime with particularly advantageous properties

Die Glaskompositionen gemäß der Erfindung weisen die folgenden Bestandteile auf:The glass compositions according to the invention have the following components:

BAD ORIGINAL,BATH ORIGINAL,

109809/0355109809/0355

lieeelsäure 45 bie 65 %% vorzugsweise 50 bis 55 % Aluminiumoxyd 20 " 30 % " 23 » 2? % Magnesia 5 * 20 % . " 10 " 16 %Lieeelsäure 45 to 65 %% preferably 50 to 55% aluminum oxide 20 "30 % " 23 »2? % Magnesia 5 * 20 % . "10" 16%

und ein« oder mehrere der Oxyde von: Cerium, Selen,and one or more of the oxides of: cerium, selenium,

r Germanium, Zirkonium, Thorium, Mangan, Titan, Antimon, r germanium, zirconium, thorium, manganese, titanium, antimony,

s ' - < ■s' - <■ Blei, Strontium, Barium» Kupfer, Nickel, Lanthan,Lead, strontium, barium »copper, nickel, lanthanum, Thallium, Eisen, Arsen, Xndiaja, Wismut, Kobalt, Vanadin, Miob, Tantal, mit einem Anteil von 1 bis 18 %, vorzugsweise 4 bis 10 %, wobeiχ Thallium, iron, arsenic, Xndiaja, bismuth, cobalt, vanadium, miobium, tantalum, with a proportion of 1 to 18%, preferably 4 to 10%, where χ

s sl02 y s sl0 2 y

1,8 ^. S- ^ 31.8 ^. S- ^ 3

- AlO —- AlO -

o,2 </ -ÜBßo, 2 </ -ÜBß

Al2O3 Al 2 O 3

Die Gegenwart des oder der Oxyde, die den vierten Bestandteil bzw. die vierte Komponente bilden, verleiht den Gläsern eine Spinntemperatur, die im allgemeinen unterhalb 14000C liegt. Biese Gläser können mit Vorteil verwendet werden für die Fabrikation von Elementarfäden sowie von fäcten, Lunten, Spinnfäden, Bändern oder Bahnen, die aus fasern kleinen Durchmessers »jisaiimengeeetatThe presence of or the oxides constituting the fourth component or the fourth component, gives the glasses, a spinning temperature, which is generally less than 1400 0 C. These glasses can be used with advantage for the manufacture of elementary threads as well as of fäcten, runners, spun threads, ribbons or webs made of fibers of small diameter »jisaiimengeeetat

f γ * -f γ * -

sind, welch·» in der Größenordnung vek 10 Mikren liegt, wobei die Fabrikation insbesondere durch Ausziehen ausare, which · »is of the order of vek 10 microns, the fabrication in particular by undressing

1QIT09/03SS1QIT09 / 03SS

den öffnungen einer Spinndüse gefolgt von eine» im allgemeinen mechanischen Ziehverfahren erfolgt. Außerdem haben die erhaltenen Glasfaden gute Eigenschaften in mechanischer Hinsicht und insbesondere hinsichtlich dea Widerstandes gegen Zug. the openings of a spinneret followed by a »in general mechanical drawing process takes place. In addition, the glass threads obtained have good mechanical properties Respect and in particular with regard to resistance to train.

Es kann vorteilhaft sein, gemäß der Erfindung zur Bildung der vierten Komponente ein im Handel unter dem Namen "CEHOX" bekanntes Erzeugnis zu benutzen, das hier mit A bezeichnet sei und das enthält: It may be advantageous, according to the invention to form the fourth component, a commercially available under the name "CEHOX" known product, which is here designated with A and which contains:

CeO2 / OT (Totalmenge der Oxyde) 46 bis 47 % Sa2O + CaO 1 % CeO 2 / OT (total amount of oxides) 46 to 47 % Sa 2 O + CaO 1 %

La2O /OT 23 bi· 25 %La 2 O / OT 23 to 25%

Hd2O /OT 17 bis 18 % Hd 2 O / OT 17 to 18 %

Ein Beispiel der Komposition, das von besonderem Interesse ist und das das Erzeugnis A enthält, ist folgendes:An example of the composition that is of particular interest and that contains product A is the following:

SlO2 Al2O, MgO AR E T Liquidus-Temperatur 54 25 16 5 480 8400 1340 1320SlO 2 Al 2 O, MgO AR ET Liquidus temperature 54 25 16 5 480 8400 1340 1320

Andere Beispiele der erfindungsgemäßen Glaskampoaitionen sind folgendetOther examples of the glass compositions of the present invention are the following

BAD ORIG'NAL 109809/Π355 BAD ORIG'NAL 109809 / Π355

ft IT ft IT

Tabelle ITable I.

SiOSiO

Komponentecomponent

6060 2525th 66th CeO2 CeO 2 99 430430 71007100 14801480 5454 2323 1515th f1f1 66th 460460 77007700 13701370 5454 2525th 99 HH 1212th 425425 73007300 13701370 5454 2525th 1616 titi 55 455455 76007600 13701370 5454 2020th 2020th MM. 66th 440440 76007600 13401340 5050 2525th 1919th IlIl 66th 430430 75007500 13701370 5454 2525th 1515th ▲▲ 66th 470470 86008600 13701370 5454 2525th 1212th HH 99 430430 79007900 13701370 5454 2727 1717th NN 44th 475475 83008300 13701370 5454 2525th 1313th IlIl 88th 460460 81008100 13501350 5454 2727 1414th MM. 55 470470 83008300 13601360 5454 2323 1818th HH 55 475475 82008200 13401340 5252 2525th 1616 NN 77th 475475 82008200 13301330 5656 2525th 1414th NN 55 475475 82008200 13301330 6060 2828 1010 SeO2 SeO 2 22 505505 88008800 14501450 5454 2525th 1515th GeO2 GeO 2 66th 475475 85008500 14001400 5454 2525th 1515th ZrO2 ZrO 2 66th 445445 79007900 14001400 5454 2525th 1515th ThO2 ThO 2 66th 450450 78007800 13801380 5454 2525th 1515th MnO2 MnO 2 66th 450450 83008300 13501350 5*5 * 2525th 1515th TiO2 TiO 2 66th 450450 83008300 13101310 5454 2525th 1515th SbOSbO 66th 455455 81008100 13801380 5454 2525th 1515th PbOPbO 66th 450450 77007700 13601360 5454 2525th 1515th SrOSrO 66th 450450 77007700 14001400 5454 2525th 1515th BaOBaO 66th 445445 77007700 13801380

109809/0355109809/0355

ORIGINALORIGINAL

SiO2 SiO 2 Al2O5 Al 2 O 5 MgOMgO 4. Komponente4th component 66th RR. EE. TT 5454 2525th 1515th CuOCuO 66th 465465 82008200 13401340 5454 2525th 1515th NiONOK 66th 465465 82008200 13701370 5454 2525th 1515th La2O5 La 2 O 5 66th 435435 80008000 13601360 5454 2525th 1515th Tl2O5 Tl 2 O 5 66th 445445 81008100 13751375 5454 2525th 1515th Fe2O5 Fe 2 O 5 66th 455455 77007700 13501350 5454 2525th 1515th As2O3 As 2 O 3 66th 450450 79007900 13801380 5454 2525th 1515th In2O3 In 2 O 3 66th 470470 83008300 13501350 5454 2525th 1515th Bi2O5 Bi 2 O 5 66th 475475 82008200 13601360 5454 2525th 1515th Co3O4 Co 3 O 4 66th 455455 76007600 13801380 5454 ^^ 1515th V2O5 V 2 O 5 66th 430430 80008000 13701370 5454 2525th 1515th Nb2O5 Nb 2 O 5 66th 465465 85008500 13501350 5454 2525th 1515th Ta2O5 Ta 2 O 5 99 470470 84008400 13501350 5454 2525th 1212th ππ 480480 86008600 13601360

Die folgenden Beispiele beziehen sich auf den Fall, wo die Kompositionen als vierteJ Element bzw. als vierte Komponente zwei oder mehrere Oxyde enthalten·The following examples relate to the case where the compositions contain two or more oxides as a fourth element or as a fourth component.

8AD ORIGINAL8AD ORIGINAL

109809/0355109809/0355

Tabelle IITable II

Al2O5 Al 2 O 5 MgOMgO CeO2 CeO 2 ZrO2 ZrO 2 MnO2 MnO 2 AA. Ta2O5 Ta 2 O 5 SeO2 SeO 2 GeO2 GeO 2 Bi2OBi 2 O '3 R '3 R EE. TT SiO2 SiO 2 2323 1212th 77th 66th 435435 80008000 13401340 5252 2323 1212th 66th 99 470470 88008800 13601360 5050 2525th 1515th 66th 66th 490490 86008600 13451345 4848 2525th 1212th 99 66th 475475 81008100 13301330 4848 2525th 1212th 22 44th 55 470470 78007800 13301330 5252

Bei allen vorhergehenden Beispielen bedeuten die gegebenen Bezeichnungen folgendes!In all of the preceding examples, the designations given mean the following!

B ί Mechanischer Widerstand gegen Zug auf den jungfräulichen Elementarfaden in HektobarB ί Mechanical resistance to pull on the virgin Elementary thread in hectobars

£ t Modul nach Xoung bei Zug In Hektobar£ t module to Xoung at Zug In Hectobar

T ι Spinnteeperatur in 0C T ι spin tea temperature in 0 C

i Oi O

Dabei ist 1 Hektobar » 1 kp/me . ferner aind sämtlich· oben angegebenen Prozente Gewicht»proeente.1 hectobar is »1 kp / me. also all of the above Percentage weight »proeente.

} I } I.

Die Bedingungen, unter denen die Messungen τοη B, B und ϊ macht word·» sia4, siad di· iolfendeniThe conditions under which the measurements τοη B, B and ϊ are made word · » sia4, siad di · iolfendeni

BAD ORIGINAL .BATH ORIGINAL.

Messung des mechanischen Wideretandes bei Beanspruchung des jungfäullchen Elementarfadensι Man schallet die Komposition in eines Platin-Rhodium-Tiegel, der durch Joule'sehe Wärme auf eine Temperatur geheist «orden ist,Measurement of the mechanical resistance under stress des jungfäullchen Elementarfadensι One echoes the composition in a platinum-rhodium crucible, which through Joule's heat is said to be at a temperature die in der Größenordnung von 16CX)0C liegt. Mach demwhich is of the order of 16CX) 0 C. Do that

(Läutern) Schmelzen und Raffinieren/sieht man das Glas durch eine(Purify) Melting and refining / you can see the glass through a Öffnung im Boden des Tiegela mittels einer Spulmaschine aus.. Man entnimmt den Teil des Elementarfadens, dir iwi- -sehen dem Tiegel und der Spulmaschine liegt, mittels eines Rahmens· Man verfertigt Proben, indem man diesen Teil des Elementarfadens, der einen Durchmesser von ungefähr 10 Mikron hat, auf einen Streifen perforierten Kartons klebt. Jede Probe mißt J cm Länge. 8ie wird geprüft mittels eines Dynamometers nach ISSTBOK. Für jedes untersuchte Glas werden mindestens 25 Proben geprüft. Sie gemessenen Widerstände sind außerordentlich gleichmäßig, 95 % der Messungen liegen im Intervall von 2 bis 3 % um den mittleren angezeigten Wert herum·Opening in the bottom of the crucible by means of a winding machine .. Take the part of the filament that lies in the crucible and the winder, by means of a frame 10 microns, stuck to a strip of perforated cardboard. Each sample measures J cm in length. It is checked by means of a dynamometer according to ISSTBOK. At least 25 samples are tested for each glass examined. The measured resistances are extremely even, 95 % of the measurements lie in the interval of 2 to 3 % around the middle displayed value

Messung des Moduls nach Xoungt Der Modul nach Toung wird bestimmt aus dsr grafischen Darstellung der Terlängerung (Dehnung) abhängig von der Last, die mit dem Dynamometer nach IHSTROH bewirkt wird. Die eventuelle Verlängerung des Trägers aus Karton für die Probe wird nicht abgerechnetι der angezeigte Wert für den Modul ist also ein Minimalwert.Measurement of the module according to Xoungt The module according to Toung is determined from the graphic representation of the elongation (elongation) depending on the load caused by the IHSTROH dynamometer. The eventual extension of the beam Cardboard for the sample is not billed. The displayed value for the module is therefore a minimum value.

BAD ORIGINALBATH ORIGINAL

109809/0355109809/0355

- Messung der Spinntemperatur: Diese Messung wird durchgeführt mittels eines optischen Glühfadenpyrometers (pyromStre optique a disparition de filament), das auf die Verzugszwiebel gerichtet wird. Der Tiegel wird dabei auf einer Temperatur gehalten, die um etwa 500C höher ist als die angegebene Temperatur·- measurement of the spinning temperature: This measurement is carried out by means of an optical Glühfadenpyrometers (pyromStre optique de disparition a filament), which is directed to the default onion. The crucible is kept at a temperature which is about 50 ° C. higher than the specified temperature

Die erfindungsgemäßen Gläser zeigen eine mechanische Widerstandsfähigkeit, die von besonderem Interesse ist, insbesondere bei hohen Temperaturen. Sie sind verwendbar für die Verstärkung von wärmehärtbaren und thermoplastischen Materialien und von Elastomeren.The glasses according to the invention show a mechanical resistance which is of particular interest, especially at high temperatures. They are suitable for the reinforcement of thermoset and thermoplastic materials and elastomers.

Alle Merkmale, die in der vorstehenden Beschreibung erwähnt sind, sollen, sofern der bekannte Stand der Technik dies zuläßt, für sich allein oder auch in beliebigen Kombinationen All features that are mentioned in the above description are intended, insofar as the known state of the art permits, on their own or in any combination

als erfindungswesentUch oder Teilkombinationen /angesehen werden, auch wenn sie in den Ansprüchen nicht enthalten sind.are regarded as essential to the invention or partial combinations, even if they are in the claims are not included.

BAD ORIGINAL 109809/0355 BATH ORIGINAL 109809/0355

Claims (1)

Drying. Heinrich Schauer Aachen, den 10. Februar 1966Drying. Heinrich Schauer Aachen, February 10, 1966 Patentanwalt „ . _ . , _ . . ___Patent attorney ". _. , _. . ___ α κ r -4 c μ 7 ! ι Mein Zeichen P 11 657α κ r -4 c μ 7! ι My reference P 11 657 A A C Λ 5 N, Zoilsrü r. I 'AAC Λ 5 N, Zoilsru r. I ' 1Vo;. : ;2]?2 und 2 5: ιί2 1 Vo ;. :; 2]? 2 and 2 5: ιί2 .Dr. Expl.Dr. Expl Pat entansprüche Pat entansprüche 1) Glaskomposition, deren Bestandteile die folgenden sind1) Glass composition, the components of which are as follows Kieselsäure 4-5 bis 65 %Λ vorzugsweise 50 bis 55 % Aluminiumoxyd 20 M 30 % " 23 " 27 % Magnesia 5 M 20 % " 10 M 16 %Silicic acid 4-5 to 65 % Λ preferably 50 to 55 % aluminum oxide 20 M 30 % "23" 27% Magnesia 5 M 20% "10 M 16% und eins oder mehrere der Oxyde von: Cerium, Selen, Germanium, Zirkonium, Thorium, Mangan, Titan, Antimon, Blei, Strontium, Barium, Kupfer, Nickel, Lanthan, Thallium, Eisen, Arsen, Indijäm, Wismut, Kobalt, Vanadin, Niob, Tantal, mit einem Anteil von 1 bis 18 %, vorzugsweise 4 bis 10 %, wobei:and one or more of the oxides of: cerium, selenium, germanium, zirconium, thorium, manganese, titanium, antimony, lead, strontium, barium, copper, nickel, lanthanum, thallium, iron, arsenic, indijäm, bismuth, cobalt, vanadium, Niobium, tantalum, in a proportion of 1 to 18 %, preferably 4 to 10%, where: S SiO
1,8 < S SiO
1.8 < - Al2O3 ^- Al 2 O 3 ^ MgO
0,2 <MgO
0.2 < 2) Komposition nach Anspruch 1, bei welcher das vierte . Element bzw. der vierte Bestandteil bzw. die vierte Komponente gebildet ist durch das im Handel unter dem Namen CEROX bekannte Erzeugnis, das hier mit A bezeichnet ist und das die folgende Zusammensetzung hat 2) Composition according to claim 1, wherein the fourth. Element or the fourth component or the fourth component is formed has the well-known commercially under the name CEROX product which is referred to herein as A and which has the following composition BAD ORIGINAL 109809/0355 BATH ORIGINAL 109809/0355 JOJO CeO2 / OT (Totalmenge der Oxyde) 46 bis 47 % Na2O + CaO 1 ja CeO 2 / OT (total amount of oxides) 46 to 47 % Na 2 O + CaO 1 yes La2O /OT .23 bis 25 % La 2 O / OT. 2 3 to 25 % Nd2O / OT 17 bis 18 % Nd 2 O / OT 17 to 18 % Glas nach Anspruch 2, dessen auf 100 % bezogene Komposition folgende isttGlass according to Claim 2, the composition of which is as follows on a 100% basis SiO2 54 %
D* 25 % SiO 2 54%
D * 25 % MgO 16 %
A 5 % MgO 16 %
A 5 % 4) Anwendung der erfindungsgemäßen Glaskompositionen bei der fabrication von Elementarfäden kleinen Durchmessers, der insbesondere in der Größenordnung von 10 Mikron liegt.4) application of the glass compositions according to the invention in the fabrication of filaments of small diameter, which is in particular of the order of 10 microns. mt#*;#ti·mt # *; # ti ßAD ORIGINALßAD ORIGINAL
DE19661596749 1965-02-12 1966-02-11 AT TEMPERATURES BELOW 1400 DEGREES C, EXTENDABLE ALUMINUM SILICATE GLASSES Granted DE1596749B2 (en)