DE1469806A1 - Process for converting aqueous emulsions of elastomeric substances into solid products or solutions - Google Patents
Process for converting aqueous emulsions of elastomeric substances into solid products or solutionsInfo
- Publication number
- DE1469806A1 DE1469806A1 DE19611469806 DE1469806A DE1469806A1 DE 1469806 A1 DE1469806 A1 DE 1469806A1 DE 19611469806 DE19611469806 DE 19611469806 DE 1469806 A DE1469806 A DE 1469806A DE 1469806 A1 DE1469806 A1 DE 1469806A1
- Authority
- DE
- Germany
- Prior art keywords
- water
- emulsion
- weight
- parts
- fillers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Köln, den I8.I0.I96I Dt/AgCologne, the I8.I0.I96I Dt / Ag
Verfahren eur Umwandlung von wässrigen Emulsionen von elastomeren Stoffen in feste Produkte oder Lösungen.Process eur Conversion of aqueous emulsions of elastomeric substances into solid products or solutions.
Organische Stoffe vom Typ der Asphalte, Wachse, Fette, Kunststoffe, Gummi und dergleichen fallen häufig in Form von Emulsionen an, beziehungsweise gelangen in Form von Emulsionen, das heisst in waeserdispergierter Form zur Anwendung. Natürliche Emulsionen sind beispielsweise ein Naturgummilatex, künstlich hergestellte Emulsionen sind beispielsweise Gummiregeneratdispersionen· Man erhält Dispersionen auch bei Polymerisationsverfahren, bei denen die Monomeren zunächst im Wasser dispergiert und erst dann polymerisiert werden (Emulsionspolymerisat)· Bei einer solchen Emulsionspolymerisation erhält man als Endprodukt Polymerdispersionen (beispielsweise Dispersionen von synthetischen Gummierten).Organic substances of the type of asphalts, waxes, fats, plastics, rubber and the like often fall in the form of Emulsions or are used in the form of emulsions, that is, in a water-dispersed form. Natural emulsions are, for example, a natural rubber latex, Artificially produced emulsions are, for example, regenerated rubber dispersions. Dispersions are also obtained in polymerization processes in which the monomers are initially immersed in water dispersed and only then polymerized (emulsion polymer) · With such an emulsion polymerization, one obtains as the end product polymer dispersions (for example dispersions of synthetic rubberized coatings).
Die Eigenschaften von Dispersionen sind partiell von denon dor darin vorliegenden Grundstoffe völlig verschieden* Dispersionen sind im allgemeinen flüssig und niedrig- oder hochviskos* Der Unterschied in den Eigenschaften zwisohen dem Grundstoff der Dispersion und der Dispersion als solcher 1st häufig auch dazu noch zu erkennen, wenn nur noch wenige Prozent Wasser in der Dispersion vorliegen. Für den Übergang der Eigenschaften des Grundstoffes ist die Stabilität der Dispersion entscheidend. Wird diese Stabilität aufgehoben, dann erfolgt bekanntlich eine Koagulation der Dispersion, das holest, dass die bisher fein verteilten Teilchen des Grundstoffes Im Emulsionswasser sich miteinander vereinigen und grosse Klumpen bilden.The properties of dispersions are partially different The basic substances contained therein are completely different * Dispersions are generally liquid and have a low or high viscosity * The Difference in properties between the basic material of the Dispersion and the dispersion as such can often also be recognized when there is only a few percent water in the dispersion are present. The stability of the dispersion is decisive for the transition of the properties of the base material. If this stability is abolished, then it is known that the dispersion coagulates, which means that it has been fine up to now Particles of the base material dispersed in the emulsion water Combine with each other and form large lumps.
-2--2-
909844/1714909844/1714
Bei Abscheidung des Wassers werden die Eigenschaften des Grundstoffes wieder gewonnen.When the water is separated out, the properties of the raw material are regained.
Die Stabilitätseigenschaften der verschiedenen Emulsionen sind sehr unterschiedlich. Gewisse Emulsionen zeigen eine Stabilitätsverschleohterung bereits bei geringen Abweichungen der stabilitätebestimmenden Paktoren, wie beispielsweise den p^-Wert, der Temperatur, den Gehalt der Emulsion an Trockenstoff, an Stabilisierungsmittel und dergleichen. Beispiele solcher Emulsionen sind in erster Linie Natur- und verschiedene Kunatgumraidispersionen. Andere Emulsionen sind dagegen αehr leicht zu stabilisieren und behalten ihren Stabilitätszustand auch bei starker Variierung der vorstehend angeführten Paktoren. Eine solche Emulsion ist zum Beispiel eine isobutylendispersion. Die Präge der Stabilität der Emulsionen ist dann von Bedeutung, wenn die Eigenschaften des Grundstoffes der Emulsionen durch Destabilisierung wieder hergestellt werden sollen. Stark stabilisierte Emulsionen benötigen dabei wesentlich wirksamere Destabilieierungsma ssnahmen,The stability properties of the various emulsions are very different. Certain emulsions show a deterioration in stability even with minor deviations from the stability-determining Factors such as the p ^ value, the Temperature, the content of dry matter, stabilizer and the like in the emulsion. Examples of such emulsions are primarily natural and various Kunatgumra dispersions. Other emulsions, on the other hand, are very easy to stabilize and maintain their state of stability even when the above-mentioned factors are varied widely. Such An example of an emulsion is an isobutylene dispersion. The embossing The stability of the emulsions is important when the properties of the base material of the emulsions are damaged by destabilization should be restored. Strongly stabilized emulsions require significantly more effective destabilization measures ssamen,
Die Aufhebung dee stabilen Zustandes wurde bisher durch folgende Massnahmen erreicht:The abolition of the stable state has hitherto been carried out by the following Measures achieved:
1·) physikalische Behandlung, wo aas Fasser abgeschieden wird, beispielsweise durch Abdunsten, gegebenenfalls unter Anwendung von Wärme oder durch Adsorption vom Untergrund,1) physical treatment where the barrel is deposited, for example by evaporation, if necessary with the application of heat or by adsorption from the substrate,
2.) chemische Behandlung unter Zerstörung der stabilisierenden Emulgiermittel und anschliessendem Wasserentzug.2.) chemical treatment with destruction of the stabilizing Emulsifier and subsequent dehydration.
Das erste Verfahren hat sein gegebenee Anwendungsgebiet in allen Fällen, in denen die Emulsion in dünnen Schichten angewandt wird. Praktische Beispiele für solche Anwendungszwecke sind Emulsionsfarben, Beläge auf Papier, Gewebe und dergleichen, Imprägnierungen und ähnliche Anwendungszwecke. Dieses erste Verfahren kann jedoch nicht unbegrenzt angewendet werden, es findet seine Grenzen in der gewünschten Schicht des Endproduktes. Beim Ab-The first method has its given field of application in all of them Cases where the emulsion is applied in thin layers. Practical examples of such applications are emulsion paints, coverings on paper, fabric and the like, and impregnations and similar uses. This first procedure can However, it cannot be used indefinitely; it finds its limits in the desired layer of the end product. When leaving
909844/1714909844/1714
U69806U69806
dunsten äea Wassers entsteht nämlich auf der Oberfläche der Emulsionsschicht ein Film mit den Eigenschaften des Grundstoffea der Emulsion,und dieser Film verhindert dann mehr oder weniger stark das Verdunsten des unter dem Film vorliegenden Wassers aufgrund seiner diffusionsverhindernden Eigenschaften. Hier gilt daher die allcemoine Regel, dass die Abdunstungszeit des Wassere in einer Emulsion in ständigem Masse mit Zunahme der Schichtdicke der Emulsion verlängert wird. Praktisch haben die neiotsn Dispersionen bei einer Schichtdicke von 2 - 3 mm bereitsThat is to say, in the presence of steam of water, a film with the properties of the base material of the emulsion is formed on the surface of the emulsion layer, and this film then more or less strongly prevents the evaporation of the water present under the film due to its diffusion-preventing properties. The general rule here is that the evaporation time of the water in an emulsion is constantly lengthened as the layer thickness of the emulsion increases. In practice, the neiotsn dispersions already have a layer thickness of 2 - 3 mm
/so
eine lange Trockenzeit, dass das erste, vorstehend angeführte Verfahren in der Praxis nur in ςζηζ seltenen Fällen angewendet
werden kann./so
a long drying time that the first, above-mentioned method can be applied in practice only in rare cases ςζηζ.
Es ist bekannt, dass man die Trockenzeit auch unter Umständen durch Zusätze zu der Dispersion beeinflussen kann, beispielsweise durch Zusatz von Füllstoffen. Durch solche Zusätze werden die DiffuBionseigenschaften des Grundstoffes der Emulsion beeinflusst. Allgemein kann gesagt werden, dass eine Dispersion mit einem hohen Gehalt an Füllstoffen im allgemeinen bessere Trocknungseigenschaften aufweist.It is known that the drying time can also, under certain circumstances, be influenced by additives to the dispersion, for example by adding fillers. Such additives influence the diffusion properties of the base material of the emulsion. In general it can be said that a dispersion with a high content of fillers generally has better drying properties having.
Durch das vorstehend unter 2.) angeführte Verfahren kann eine wesentlich schnellere Aufhebung des diapergierten Zustandes erreicht werden. Als Zusatzstoff zur chemischen Zerstörung der Stabilisationsmittel eignen sich die verschiedensten Stoffe, beispielsweise Metallsalze oder Säuren. Bei Zusatz solcher Mittel erfolgt die Ausfällung der Emuleion sehr schnell und es bildet sich ein Konglomerat aus Wasser und Emulsionsgrundstoff. Zur Abscheidung des Wassers aus dem Konglomerat ist es erforderlich, die Masse, insbesondere wenn es sich um dickere Schichten handelt, mechanisch zu bearbeiten. Dies kann beispielsweise durch Pressen oder Walzen geschehen. Ein typisches Beispiel für eine solche Behandlung ist die bekonnte Überführung von Naturgummilatexis Kreppgummi· Das gleiche Verfahren wird aber auch in sehr grossem Ausmasse bei der Herstellung von kunststoffbelegten Geweben und bei der Imprägnierung von Schaumstoffen angewendet. Dadurch, dass das Wasser im Konglomerat ungebundenUsing the procedure listed under 2.) above, a much faster abolition of the diapered state can be achieved. As an additive to the chemical destruction of the A wide variety of substances, for example metal salts or acids, are suitable as stabilizers. With the addition of such funds the emuleion precipitates very quickly and it forms a conglomerate of water and emulsion base material. To separate the water from the conglomerate, it is necessary to mechanically process the mass, especially when it comes to thicker layers. This can be, for example done by pressing or rolling. A typical example of such a treatment is the well-known transfer of Natural rubber latex crepe rubber · The same process is used though also to a very large extent in the production of plastic-covered Woven fabrics and used in the impregnation of foams. Because the water in the conglomerate is unbound
-4-9098U/17U-4-9098U / 17U
vorliegt, i3t die Abscheidung wesentlich einfacher als bei dem ersten angeführten Verfahren, allerdings unter der Voraussetzung, das« dos Wasser nicht in drn Poren des Grundstoffes eingeschlossen 13t, Auch bei diesem Verfahren, bei dem eine chemische Ausfällung erfolgt, treten aber die gleichen Schwierigkeiten inbezug auf die Schichtdicke auf, wie sie vorstehend für das erste Verfahren angegeben wurden, das heisst, eine Erhöhung der Schichtdicke der Emulsion bringt eine wesentliche Verschlechterung der Abdunstungsverhältnisse mit sich.is present, the deposition is much easier than with the first procedure cited, but on the condition that the «dos water is not in the pores of the raw material included 13t, also in this procedure, in which one chemical precipitation occurs, but the same difficulties arise with regard to the layer thickness as described above for the first procedure indicated, that is, an increase the layer thickness of the emulsion leads to a significant deterioration the evaporation conditions with itself.
Bei allen bekannten Verfahren zur Entfernung von Wasser aus Emulsionen unter Anwendung von chemischen oder physikalischen Massnahmen orfolgt durch die Abscheidung des Wassers eine Volumenschrumpfung, das heisst, das Volumen des Endproduktes ist geringer als das Volumen der Emulsion· Diese Volumenschrumpfung ist besonders bei dicken Schicken so erheblich, dass die Anwendung von Emulsionen zum Ausfüllen von Hohlräumen völlig ausgeschlossen ist.In all known methods for removing water from emulsions using chemical or physical Measures are taken by separating the water Volume shrinkage, i.e. the volume of the end product is less than the volume of the emulsion. This volume shrinkage is so significant, especially in the case of thick mail, that emulsions are used to fill cavities is completely excluded.
Gegenstand der Erfindung ist ein Verfahren zur Überwindung der vorstehend angeführten Schwierigkeiten, bei dem das Emulsionswasser vorzugsweise durch chemische Reaktion gebunden wird und nicht verdunstet und bei dem auch keine Schrumpfung des Volumens erfolgt. Gemäss der Erfindung werden wässrige Emulsionen von filmbildcnden oder zusammenhängenden elastomeren Stoffen, die für sich oder auf Gegenständen vorliegen, in feste Produkte mit den wesentlichen elastomeren Eigenschaften der Eraulsionsgrundstoffe umgewandelt oder direkt in Lösungen überführt, die zur Y/ei teigverarbeitung auf solche festen Produkte geeignet sind, indem man die wässrigen Emulsionen mit hydratisierenden Füllstoffen in Anteilen unter der zur /stöoheometrischen Bindung des Emulsionswasseas erforderlichen Menge versetzt· Bei der Hydratisierung gehen die Zusatzstoffe unter Aufnahme von Wasser in wasserunlösliche Verbindungen über und wirken wie übliche Füllstoffe.The invention is a method for overcoming the difficulties mentioned above, in which the emulsion water is preferentially bound by chemical reaction and does not evaporate and in which there is also no shrinkage of the volume. According to the invention, aqueous emulsions are used of film-forming or cohesive elastomeric substances that are present on their own or on objects in Solid products with the essential elastomeric properties of the raw emulsion materials or converted directly into solutions transferred to the Y / egg dough processing on such solid products are suitable by using the aqueous emulsions with hydrating Fillers in proportions below the / stoheometric Binding of the emulsion water as required amount added When hydrated, the additives are absorbed from water to water-insoluble compounds and act like normal fillers.
-5--5-
9098U/17U9098U / 17U
" 5 " U69806" 5 " U69806
Bei der Verwendung von Produkten geiaäss der Erfindung werden vorzugsweise 2 Komponenten, die lager- und verkaufsfähig sein können, mehr oder weniger kurze Zoit vor der Anwendung als Produkt gemäss der Erfindung miteinander vermischt» Um die chemischen Reaktionen, die bei dem Verfahren gemäss der Erfindung ablaufen, klarzustellen, werden die vorteilhaftesten Zusatzstoffe bei der Reaktion nachstehend beschrieben. Die an-In the use of products geiaäss the invention preferably 2 components which can be stored and can be salable, more or less short Z o it be prior to use as P r oduct according to the invention mixed with one another "For the chemical reactions that in the method proceeding according to the invention, to clarify, the most advantageous additives in the reaction are described below. The other
/die geführte Reaktion bezieht sich jedoch nur auf wasserbindende Funktion des erfindungsgociässen hydratisierenden Füllstoffes./ The reaction carried out relates only to the water-binding function of the hydrating filler according to the invention.
1. CaSO. + 2 H2O * CaSO. χ 2 HgO.1. CaSO. + 2 H 2 O * CaSO. χ 2 HgO.
Die für eine vollständige Wasserabbindung stöcheometrisch erforderliche Menge Calciumsulfat beträgt 3,8 Gewichtsteile Claciurasulfat auf 1 Gewichtsteil V/asser.The stoecheometric method for complete water binding The required amount of calcium sulphate is 3.8 parts by weight of Claciurasulphate per part by weight of water per volume.
2. CaO + H2O a Ca(OH)2.2. CaO + H 2 O a Ca (OH) 2 .
Zur vollständigen Wasserabbindung sind bei dieser Reaktion 3,1 Gewichtsteile Calciumoxyd je Gewichtsteil Wasser erforderlich. Dabei ist zu berücksichtigen, dass die Kohlensäure dor Luft die Reaktionskomponente Ca(OH)2 in CqCO- unter Bildung von Wasser überführt Ca(OH)2 + CO2 = CaCO3 + HgO. Das bei dieser Reaktion frei werdende Wasser hat jedoch die Möglichkeit, im gleichen Masse, wie die Kohlensäure zum Caloiumhydroxyd zutritt, abzudunsten, ' '3.1 parts by weight of calcium oxide per part by weight of water are required for this reaction to completely bind water. It must be taken into account that the carbonic acid in the air converts the reaction component Ca (OH) 2 into CqCO- with the formation of water Ca (OH) 2 + CO 2 = CaCO 3 + HgO. However, the water released during this reaction has the possibility of evaporating to the same extent as the carbonic acid is added to the calcium hydroxide, ''
3. 3 CaO χ SiO2 + 2 HgO » CaO χ SiOg + 2 Ca(OH)2.3. 3 CaO χ SiO 2 + 2 HgO »CaO χ SiOg + 2 Ca (OH) 2 .
Für die Hydratisierung von Zement ist vorstehend die Reaktion zwischen Tricalciumsilikat und Wasser angeführt. Auch bei anderen Zementkomponenten, wie Aluminrten oder Ferriten, verläuft eine gleichartige Reaktion, Bei allen diesen Umsetzungen sind etwa 3,6 Gewichtsteile Zement je Gewichtsteil Wasser erforderlich, um eine vollständige Bindung des Wassers zu erreichen.For the hydration of cement, the reaction between tricalcium silicate and water is mentioned above. Even with other cement components such as Aluminrten or ferrites, runs a similar reaction, in all these reactions, about 3.6 parts by weight Z e are ment per part by weight of water required to achieve complete binding of water.
-6--6-
909844/1714909844/1714
Bei dem erfindungsgemässen Verfahren können notUrlich auch andere hydratisierende Bindemittel eingesetzt werden. Vorteilhafterweise arbeitet man mit möglichst geringen Mengen des hydratisierendon Füllstoffes, wobei sich diese Menge im allgemeinen in Abhängigkeit von der Schichtdicke des Endproduktes verringert* Bei einem zu grossen Zusatz an hydratisierendöu Füllstoff gehen die charokteristischen Eigenschaften, insbesondere natürlicher oder synthetischer Geinniiarten, verloren, offensichtlich, weil oberhalb der kritischen Grenze des erfindungsgemässen Verfahrens die Kristalle dee Bindemittels ineinander übergehen und dadurch eine Erstarrung des elastomoren Produktes bewirken« Wesentlich für da3 angemeldete Verfahren ist, dass das stabile Endprodukt die ulastomeren Eigenschaften dos Grundstoffes der Emulsion aufweist» Der Fachmann wird dabei schnell feststellen, ob innerhalb der kritischen Grenzen dee angemeldeten Verfahrenegrössere oder kleinere Mengen an hydratisierenden Füllstoff zugesetzt werden können· Beispielswelse können Polyisobutylene cdie mehrfache Menge an Füllstoffen pufnehnen, ohne dass die Grundeigenschaften des Polyisobutylene verändert werden· Bei synthetischen Guramiarten haben häufig der Polymerisationsgrad, der Typ des Polymerisates, der Gehalt an Weichmacher, die Teilchengrösse der erfindungsgemäsB erforderlichen Menge an hydratisierendemIn the case of the method according to the invention, of course other hydrating binders can be used. Advantageously one works with the smallest possible amounts of the hydrating filler, this amount in general depending on the layer thickness of the end product reduced * If too much hydrating oil is added The characteristic properties of filler go, in particular natural or synthetic species, lost, obviously, because above the critical limit of the inventive Process the crystals of the binder into one another pass over and thereby a solidification of the elastomoren Product effect «Essential for the registered procedure is that the stable end product is the ulastomeric properties dos basic substance of the emulsion has »The expert will quickly determine whether the notified processes are larger or smaller within the critical limits of hydrating filler can be added · Example catfish Polyisobutylenes can expand multiple amounts of fillers without affecting the basic properties of the Polyisobutylenes are changed · In synthetic gourami species often have the degree of polymerization, the type of polymer, the content of plasticizer, the particle size of the invention required amount of hydrating
. Füllstoff zur Bindung des Emuloionswassers einen Einfluss auf. Filler for binding the emulsion water has an influence
/de 8
die Mindestmenge nydratisierenden Füllstoffes*
Sie untere Grenze des erfindungsgemässen FüllstoffZusatzes
wird in noch höherem Grad von den Eigenschaften des Grundstoffes der Emulsion bestimmt* Stoffe mit gummiartigen Eigenschaften
sollen besonders bei sehr hohen Stabilisierungegraden möglichst wenig Wasser aufweisen, um die gewünschten elastischen Eigenschaften
aufzuweisen· Der Grund dafür dürfte darin zu sehen sein, dass das Wasser bei Stoffen nit eistischen Eigenschaften
die Ausbildung dieser elastischen Eigenschaften durch Kopplung der Einzelteilchen verhindert. Im einzelnen spielt dabei natürlich
die Stabilität der Emulsion und die Neigung der darin/ de 8
The minimum amount of hydrating filler * The lower limit of the filler addition according to the invention is determined to an even greater degree by the properties of the base material of the emulsion * Substances with rubber-like properties should have as little water as possible, especially with very high degrees of stabilization, in order to have the desired elastic properties The reason for this It can be seen in the fact that the water prevents the formation of these elastic properties in substances with icistic properties by coupling the individual particles. In detail, of course, the stability of the emulsion and the inclination of the emulsion play a role
-7--7-
909844/1714909844/1714
vorliegenden Teilchen zur Agglomeration eine wesentliche Rolle»present particles for agglomeration an essential Role"
Ausser den erfindungsgemäss zugesetzten hydratisierenden Füllstoffen können in die erfindungsgemässen Emulsionen noch andere Zusatzstoffe eingetragen werden, die für elastomere Produkte üblicherweise angewendet werden· Dabei handelt es sich in wesentlichen umExcept for the hydrating agents added according to the invention Fillers can also be added to the emulsions according to the invention other additives are entered which are usually used for elastomeric products · These are in essence
a) Emulgiernittel, schaumvorhindernde Mittel, Mittel zur Beeinflussung der Konsistenz und andere Mittel, die die Anwendung der Emulsion erleichtern,a) Emulsifiers, foam-preventing agents, agents for Influencing the consistency and other means that facilitate the application of the emulsion,
b) Vulkanisationsmittel, Vulkanisationsbeschleuniger und andere Mittel, die die Reaktion bei der Anwendung beeinflussen, b) vulcanizing agents, vulcanization accelerators and other agents that influence the reaction during use,
c) Antioxydationsmittel, Ultraviolettabsorptionsmittel, Weichmacher, sonstige Füllstoffe, Pigmente und andere Stoffe, die die Eigenschaften des fertigen Produktes beeinflussen ·c) antioxidants, ultraviolet absorbers, plasticizers, other fillers, pigments and other substances that influence the properties of the final P r · oduktes
Wie vorstehend bereits ausgeführt, wird das Produkt gemäss der Erfindung zweckmässig aus 2 Komponenten hergestellt, die vor der praktischen Anwendung des erfindungsgemässen Produktes miteinander vermischt werden. Die Zeitdifferenz zwischen Mischung und Anwendung des Mischproduktes hängt in örhoblichon Ausmasse von der Reaktionsgeschwindigkeit bei der Hydratisierung ab, die jedoch durch Zusatzstoffe dem gewünschten Zweck entsprechend geregelt werden kann. Die beiden Komponenten des crfindungsgemäsBen Produktes haben folgende Zusammensetzung: Teil A: Emulsion eines Elastomeren und Wasser mit gegebenenfalls Zusatzstoffen,As already stated above, the product according to the invention is expediently made from 2 components, the before the practical application of the product according to the invention are mixed together. The time difference between mixing and application of the mixed product depends on örhoblichon The extent depends on the rate of reaction during hydration, which, however, is achieved through additives in accordance with the desired purpose can be regulated. The two components of the invention Product have the following composition: Part A: Emulsion of an elastomer and water with optionally Additives,
Teil B: Hydratisierender Füllstoff mit gegebenenfalls Zusatzstoffen. Part B: Hydrating filler with optional additives.
Durch Zugabe der Komponente A zur Komponente B erhält man als Schlussprodukt den elastomeren Grundstoff mit einem Gehalt anBy adding component A to component B, the final product is the elastomeric base material with a content of
-8--8th-
809844/1714809844/1714
- 8 hydratisieren Füllstoffen und gegebenenfalls Zusatzstoffen«- 8 hydrate fillers and possibly additives «
Bei der Mischung der Komponenten des erfindungsgemässen End» Produktes muss rinn häufig darauf achten, dass das Mischungsprodukt eine Konsistenz hat? dio für die verschiedensten gewünschten Anwendungszwecke geeignet ist. Bekanntlich ist die Konsistenz solcher Produkte von dem Aufnahmevermögen der Emulsion für Füllstoffe und von der Teilchengrösse dieser Füllstoffe abhängig. Genäss der Erfindung ist eine möglichst geringe Teilchongrösso wünschenswert, um eine schnellere Eeaktion, das heisst, ein schnelleres Abbinden des Wassers und Ausbildung eines möglichst homogenen Schlußsproduktes zu erreichen.When mixing the components of the inventive end » Product must rinn often make sure that the mixed product has a consistency? dio for the most diverse desired Applications is suitable. It is well known that the consistency of such products depends on the absorption capacity of the Emulsion for fillers and on the particle size of these fillers addicted. According to the invention, the smallest possible particle size is desirable in order to achieve a faster reaction, that means a faster setting of the water and training to achieve a final product that is as homogeneous as possible.
Um Konsistenzschwierigkeiten bei hohem hohem Gehalt von hydratisierendcn Zusatzstoffen im Endprodukt der Mischung zu vermeiden und um die Verwendung von Füllstoffen kleiner Teilchongrösse zu ermöglichen, kann folgende Vorbehandlung durchgeführt werden:To avoid consistency problems with high levels of hydrating To avoid additives in the end product of the mixture and to use fillers of small particle size the following pretreatment can be carried out:
Die fuinen Teilchen des Füllstoffes werden mit Hilfe eines Bindemittels zu grösseren Einheiten von 1o - 1oo Einzelteilohen gebunden. Das dabei verwendete Bindemittel soll wasserlöslich sein. Nach dem Einrühren des so vorbehandelten Pulvers in die andere Komponente gemäss der Erfindung erfolgt nach einiger Zeit eine Auflösung des Bindemittels, die jedoch so lange verzögert werden soll, bis die Anwendung der erfindungsgemässen Masse erfolgt ist. Nach der Auflösung des Bindemittels beginnt die Abbindereaktion mit normaler Geschwindigkeit und die Masse erhärtet schnell. Ein Beispiel für ein zur Vorbehandlung geeignetes Bindesmittel ist Schellack.The fuinen particles of the filler are with the help of a Binding agent into larger units of 1o - 1oo individual parts bound. The binder used should be water-soluble. After stirring in the powder that has been pretreated in this way After some time, the binder dissolves in the other component according to the invention, but this takes so long should be delayed until the application of the invention Mass is done. After the binder has dissolved, the setting reaction begins at normal speed and the mass begins hardens quickly. An example of a binding agent suitable for pretreatment is shellac.
Wenn man bisher Emulsionen mit Gips, Zement oder anderen hydratisierenden Stoffen versetzt hat, dann sollte eine besondere Wirkung auf die Ausgangsstoffe nach der Umsetzung erreicht werden. So werden zum Beispiel Polyvinylacetat-EmulsionenIf you have previously used emulsions with plaster of paris, cement or other hydrating Has added substances, then a special effect should be achieved on the starting substances after the implementation will. For example, polyvinyl acetate emulsions are used
-9--9-
909844/17U909844 / 17U
Mischungen von Zement, Wasser und Sand zugesetzt, um einen "elastischeren" oder dichteren Beton zu erreichen. Alle diese Zusätze haben aoeh gemeinsam, dass die Reaktion zwischen den hydratisierenden Stoffen und deu Wasser dorainierend ist und ■ die Schlusseigenschaften bestimmen sollen· Diese Eigenschaften werden durch den Zusatz von Emulsionen in der Weise modifiziert, dass beispielsweise der gehärtete Beton wasserfester, säurefester oder in einer anderen Weise modifiziert wird. Im Gegensatz hierzu werden erfindungsgeoäss bei der Reaktion von hydratisierenden Substanzen mit Wasser die Eigenschaften der Ausgangsstoffe in der Emulsion nicht verändert·Mixtures of cement, water, and sand are added to one to achieve "more elastic" or denser concrete. All these Aoeh additives have in common that the reaction between the hydrating substances and deu water is dorainierend and ■ the final properties should determine these properties are modified by the addition of emulsions in such a way that that, for example, the hardened concrete is waterproof, acid-resistant or modified in another way. in the In contrast to this, according to the invention, the properties become when hydrating substances react with water of the starting materials in the emulsion not changed
Das erfindungsgemässe Verfahren hat viele praktische Anwendungsmöglichkeiten in allen den Fällen, in denen das in einer Emulsion, Dispersion oder Suspension vorliegende Wasser ohne Schrumpfung des Volumens gebunden werden soll« Die Erfindung wird nachstehend in Beispielen erläutert·The method according to the invention has many practical applications in all cases in which the water present in an emulsion, dispersion or suspension is without Shrinkage of the volume to be bound «The invention is explained below in examples
Baispiel 1Example 1
Pastenförmige AusfUllmassen, die nach der Umsetzung Xn Stoffe übergehen, die im wesentlichen die gleichen Eigenschaften aufweisen wie der Emulsionsgrundstoff·Paste-like filling compounds which, after the reaction, pass over Xn substances which have essentially the same properties as the emulsion base
a) Fugenina s sea) Fugenina s se
Teil A 3-8 Gewichtsteile Asphaltemulsion mit einemPart A 3-8 parts by weight of asphalt emulsion with a
Gehalt von 6o $> PeststoffSalary of $ 60> Peststoff
3-8 GewichtBteile Gummiregeneratemulsion mit einem Feststoffgehalt von 5o # und3-8 parts by weight of regenerated rubber emulsion with a solids content of 5o # and
1-3 Gewichtsteile Mineralölemulsion mit einem Gehalt von 5o f> Feststoff1-3 parts by weight of mineral oil emulsion with a content of 5o f> solid
(Solche Fugenmassen enthalten die Asphaltemulsionen häufig als verbilligenden Füllstoff).(The asphalt emulsions often contain such grout as a cheaper filler).
Teil B 8-14 Gewichtsteile Zement oder GipsPart B 8-14 parts by weight of cement or plaster of paris
b) Elastische Fugenmasseb) Elastic grout
Teil A 4-6 Gewichtsteile Gummiregeneratdispersion mitPart A 4-6 parts by weight of regenerated rubber dispersion with
einem Gehalt von 6o $> Feststoffa salary of $ 60> solids
4-6 Gewichtsteile Polyisobutylendispersion rait einem Gehalt von 55 # Feststoff4-6 parts by weight of polyisobutylene dispersion containing 55 # solids
909844Λ1714-' -9-909844Λ1714- '-9-
H69806H69806
Teil B 8-12 Gewichtsteile Zement oder Gips c) Fugenmasse mit guter ölbeständigkeitPart B 8-12 parts by weight of cement or plaster of paris c) Grout with good oil resistance
Teil A 1-5 Gewiohtsteile Butylgumniregenerat-Part A 1-5 parts by weight butyl rubber regenerated
Emuloion mit einem Gehalt von 60 i» FeststoffEmuloion with a content of 60 i "solid
- 1o Gewichtsteile Butadien-Akrylnitril-Llischpolymerisatdispersion mit einem Gehalt von 5o $> Peststoff- 10 parts by weight of butadiene-acrylonitrile-polymer dispersion with a content of 50 $> pesticide
Teil B 8-15 Gewichtsteile Zement oder GipsPart B 8-15 parts by weight of cement or plaster of paris
0,04-0,06 Gewichtsteile eines kalt härtenden Vulkanisationsmittels.0.04-0.06 parts by weight of a cold setting vulcanizing agent.
Elastische VersiegelungsmassenElastic sealing compounds
a) PUr Dilatationsfugena) PUr expansion joints
Teil A 8-12 Gewichtsteile Polyisobutylen-EmulsionPart A 8-12 parts by weight of polyisobutylene emulsion
mit einem Geholt von 5o 5* Peststoffwith a fetch of 5o 5 * plague
1-3 Gewichtsteile einer alkalibeständigen Harzemulsion mit einem Gehalt von 7o # Peststoff (Füllstoff) und1-3 parts by weight of an alkali-resistant resin emulsion containing 7o # Peststoff (filler) and
1-4 Gewichtsteile Asbestfaser oder Gumnipulver als weiteren Füllstoff1-4 parts by weight of asbestos fiber or rubber powder as an additional filler
Teil B 1o - 15 Gewichtsteile ZementPart B 1o - 15 parts by weight of cement
b) Lösungsinittelbeständige elastische Pugenmasseb) Solvent-resistant elastic pugen mass
Teil A 9-17 Gewichtsteile Chlorbutadien-^EmulsionPart A 9-17 parts by weight of chlorobutadiene emulsion
mit einem Gehalt von 5o # Peststoffcontaining 5o # pesticide
1-5 Gewichtsteile Ton
Teil B 12-18 Gewichtsteile Zement und/oder Gips 1-5 parts by weight of clay
Part B 12-18 parts by weight of cement and / or plaster of paris
ot1-o,2 Gewichtsteile übliche Vulkanisationsmittel o t 1-0.2 parts by weight of customary vulcanizing agents
0) Billige elastische Pugenmasse0) Cheap elastic pugen material
Teil A 8-12 Gcv/ichtstcile Butylregenerat-EmulsionPart A 8-12 Gcv / ichtstcile butyl regenerate emulsion
mit einem Gehalt von 60 % Peststoffwith a content of 60 % pesticide
1-6 Gewichtsteile Gurimi- und/oder Korkpulver als Füllstoff1-6 parts by weight of Gurimi and / or cork powder as a filler
Teil B 1o - 15 Gewichtsteile Zement, Gips und/oderPart B 1o - 15 parts by weight of cement, plaster and / or
Calciumoxyd.Calcium oxide.
-I0-909844/1714-I0-909844 / 1714
U69806 «4-U69806 «4-
Ausfüllmassen für verschiedene AnwendungenFillings for various applications
a) Elastische Ilassea) Elastic Ilasse
.Teil A 8-12 Gewichtsteile natürlicher oder synthetischer Guraniidispersion mit einen Gehalt von 5o JS PeststoffPart A 8-12 parts by weight natural or synthetic Guraniidispersion with a content of 5o JS Peststoff
1-5 Gewichtsteile Gumnipulver als Füllstoff1-5 parts by weight rubber powder as filler
1-4 Gewichtsteile Sandkreide oder dergleichen als weiteren Füllstoff1-4 parts by weight of sand chalk or the like as a further filler
Teil B 1o - 15 Gewichtsteile Zement, Gips oder Clacium-Part B 1o - 15 parts by weight of cement, plaster or calcium
oxydoxide
b) Elaotische Ausfüllnasseb) Elaotic filling wet
Teil A 8-12 Gewichteteile GummiregeneratdispersionPart A 8-12 parts by weight of regenerated rubber dispersion
rnit einem Gehalt von 6o $ Feststoffwith a solids content of $ 60
1-5 Gewichtsteile der Dispersion eines von der Firma Heroules Powder handelsmässig unter der Bezeichnung 11VInsol" vertriebenen modifizierton Kolophoniumharzes (unlöslicher Anteil)1-5 parts by weight of the dispersion of a modified rosin resin (insoluble portion) marketed by Heroules Powder under the name 11 VInsol "
Gewichtsteile FüllstoffParts by weight of filler
Gewichtsteile Zement, Gips oder Claoiumoxyd. Parts by weight of cement, plaster of paris or Claoium oxide.
Direkte Umwandlung einer Emulsion in eine LösungDirect conversion of an emulsion into a solution
a) Herstellung einer Gummilösung ausa) Making a rubber solution from
- 15 Gewichtsteilen einer 5o #igen Gummi-Emulsion, die- 15 parts by weight of a 50 # gum emulsion, the
- 5o Gewichtsteile Lösungsmittel für den elastomeren Grundstoff enthält und- Contains 5o parts by weight of solvent for the elastomeric base material and
- 5o Gewichtsteilen Zement oder Gips- 50 parts by weight of cement or plaster of paris
b) Herstellung von Bodenplatten und anderen Belagmaterialien aue Lösungen von elastomeren Stoffen, die man ausb) Manufacture of floor slabs and other covering materials aue solutions of elastomeric substances that can be made from
6-12 Gewichtsteilen einer 5o #igen Emulsion von synthetischen oder natürlichen elastomeren Grundstoffen, - 5o Gewichteteilen Lösungsmittel für diese Grundstoffe6-12 parts by weight of a 50 # emulsion of synthetic or natural elastomer base materials, - 50 parts by weight of solvents for these Raw materials
-11-909844/1714 -11- 909844/1714
U69806U69806
- Χ- Χ
1ο - 15 Gewichtsteilen inerten Fülletoffen und - 18 Gewichtsteilen Zement oder Gips erhält· 1ο - 15 parts by weight of inert Fülletoffen and - 18 parts by weight of cement or plaster gets ·
c) Herstellung von Packungen
Man verwendetc) Manufacture of packs
One uses
- 15 Gewichtsteile einer Emulsion mit einem- 15 parts by weight of an emulsion with a
Gehalt von 4o - 7o $> an Peststoffen, die vorzugsweise wie in den vorhergehenden Beispielen aus Polyisobrtylen, Chlorbutadien-Kautschuk oder Akrylnitrilbutadien-Mischpolymerisaten bestehen, undContent of 40 - 70 $> of pesticides, which preferably consist of polyisobrtylene, chlorobutadiene rubber or acrylonitrile butadiene copolymers as in the previous examples, and
15-30 Gewichtsteile Zement oder Gips.15-30 parts by weight of cement or plaster of paris.
909844/1714909844/1714
Claims (9)