DE102016214651A1 - Lightning protection system and method of manufacture - Google Patents

Lightning protection system and method of manufacture Download PDF

Info

Publication number
DE102016214651A1
DE102016214651A1 DE102016214651.3A DE102016214651A DE102016214651A1 DE 102016214651 A1 DE102016214651 A1 DE 102016214651A1 DE 102016214651 A DE102016214651 A DE 102016214651A DE 102016214651 A1 DE102016214651 A1 DE 102016214651A1
Authority
DE
Germany
Prior art keywords
lightning protection
protection system
metal particles
coating
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102016214651.3A
Other languages
German (de)
Inventor
Bastian Plochmann
Jürgen Huber
Steffen Lang
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Original Assignee
Siemens AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens AG filed Critical Siemens AG
Priority to PCT/EP2017/062752 priority Critical patent/WO2018001653A1/en
Publication of DE102016214651A1 publication Critical patent/DE102016214651A1/en
Withdrawn legal-status Critical Current

Abstract

Die Erfindung betrifft eine Blitzschutzanlage für beispielsweise eine nicht-statische Industrieanlage, wie ein Windkraftrad, sowie ein Verfahren zur Herstellung einer Blitzschutzanlage. Durch die Erfindung wird erstmals ein hocheffektiver, leicht applizierbarer Verbundwerkstoff, der in dünnsten Schichten wie ein Lack aufbringbar ist, vorgestellt, der als effektive Blitzschutzanlage bei nicht-statischen Anlagen einsetzbar ist. Der Lack ist beliebig ausbesserbar und nachrüstbar und somit beliebig flexibel anwendbar.The invention relates to a lightning protection system for example, a non-static industrial plant, such as a wind turbine, and a method for producing a lightning protection system. The invention introduces for the first time a highly effective, easily applied composite material which can be applied in the thinnest layers, such as a lacquer, which can be used as an effective lightning protection system in non-static systems. The paint can be repaired and retrofitted as desired and thus flexibly applicable.

Description

Die Erfindung betrifft eine Blitzschutzanlage für beispielsweise eine nicht-statische Industrieanlage wie ein Windkraftrad sowie ein Verfahren zur Herstellung einer Blitzschutzanlage. The invention relates to a lightning protection system for example, a non-static industrial plant such as a wind turbine and a method for producing a lightning protection system.

Eine Blitzschutzanlage vermeidet in erster Linie, dass ein Blitz in das geschützte Objekt einschlägt. Der Einschlag findet stattdessen in der Blitzschutzanlage statt. Im Falle eines Einschlags bietet die Blitzschutzanlage dem Blitzstrom einen definierten, niederohmigen Strompfad, womit Beschädigungen am geschützten Objekt vermieden werden. A lightning protection system primarily prevents a lightning strike in the protected object. The impact instead takes place in the lightning protection system. In the event of an impact, the lightning system provides the lightning current with a defined, low-impedance current path, thus avoiding damage to the protected object.

Bei einer nichtstatischen Industrieanlage, wie z.B. einem Windrad ist Blitzschlag ein großes Problem, da Windkraftanlagen meist an exponierten Lagen errichtet werden, welche häufig den höchsten Punkt in einem größeren Umfeld darstellen. In a non-static industrial plant, such as Lightning is a big problem for a windmill because wind turbines are usually built in exposed locations, which are often the highest point in a larger environment.

Nachdem der höchste Punkt eines vertikalen Windrades zu jeder Zeit die Spitze eines Rotorblattes ist, wird der Eintrittsbereich des Blitzes auf einem der Rotorblätter liegen. Die sehr hohe Stromdichte in einem Blitz muss über den Rotorflügel durch den Rotor nach unten abgeleitet werden. Since the highest point of a vertical wind turbine is the tip of a rotor blade at all times, the entrance area of the flash will be on one of the rotor blades. The very high current density in a flash must be dissipated down the rotor blade through the rotor.

Somit kommt es bei einem Blitzeinschlag im Rotorblatt, bedingt durch den inneren Widerstand der verwendeten Materialien, zu typischen Blitzschäden wie Brände und Überhitzung der einzelnen Komponenten sowie zu temperaturbedingten mechanischen Verformungen. Thus, a lightning strike in the rotor blade, caused by the internal resistance of the materials used, typical flash damage such as fires and overheating of the individual components as well as temperature-induced mechanical deformations.

In bestehenden Windkraftanlagen sind deshalb als Blitzschutzanlage konventionelle metallische Leiterbahnen zur Ableitung der hohen Stromdichte vorgesehen. Diese verlaufen entweder komplett an der Außenhaut des Rotorblattes oder sind im Inneren des Rotorblattes verlegt, sodass nur das Ende der Leiterbahnen an der Spitze des Rotorblattes aus diesem Austritt. Eine weitere Form des Blitzschutzes ist die Einbringung eines metallischen Netzes in eine deckende Lackschicht auf der Oberfläche des Rotorblattes. Hierdurch entsteht lokal eine metallische Struktur, welche entstehende Ströme und Spannungen durch eine Verbindung zum Stativ der Windkraftanlage erdet. In existing wind turbines, therefore, conventional metallic conductor tracks are provided as a lightning protection system for deriving the high current density. These either run completely on the outer skin of the rotor blade or are laid inside the rotor blade, so that only the end of the conductor tracks at the tip of the rotor blade from this outlet. Another form of lightning protection is the introduction of a metallic mesh in a covering lacquer layer on the surface of the rotor blade. This creates locally a metallic structure, which grounds resulting currents and voltages through a connection to the tripod of the wind turbine.

Nachteilig an den herkömmlich angewendeten Blitzschutzanlagen von nicht-statischen Industrieanlagen wie Windkrafträdern ist, dass sie nur kostenintensiv herstellbar und/oder applizierbar sind, korrosionsanfällig und nicht für die Nachrüstung bestehender Anlagen tauglich sind. A disadvantage of the conventionally used lightning protection systems of non-static industrial plants such as wind turbines that they are expensive to produce and / or can be applied, are prone to corrosion and not suitable for retrofitting existing facilities.

Aus der WO 2014/206676 ist eine fundamentale Neuerung zur Blitzableitung bei nichtstatischen Anlagen in Form einer Oberflächenbeschichtung zur Potentialabführung bekannt. Dabei wird ein Lack mit einem Füllstoff aus plättchenförmigen keramischen, leitfähig beschichteten Partikeln eingesetzt. Nachteilig an dieser Oberflächenbeschichtung ist jedoch die vergleichsweise niedrige Leitfähigkeit der keramischen Partikel zusammen mit den hohen Füllgraden, die erforderlich sind für eine effektive Blitzableitung. From the WO 2014/206676 is a fundamental innovation for lightning dissipation in non-static systems in the form of a surface coating for potential dissipation known. In this case, a paint with a filler of platelet-shaped ceramic, conductive coated particles is used. A disadvantage of this surface coating, however, is the comparatively low conductivity of the ceramic particles together with the high fill levels that are required for effective lightning discharge.

Aufgabe der vorliegenden Erfindung ist es, eine leicht applizierbare, wartungsfreundliche, gegebenenfalls nachrüstbare massenfertigungstaugliche, witterungsbeständige und vor allem hocheffektive Blitzschutzanlage zur Verfügung zu stellen, die insbesondere an nicht-statischen Industrieanlagen, wie beispielsweise an Windkrafträdern, einsetzbar ist. The object of the present invention is to provide an easy-to-apply, easy-to-maintain, optionally retrofit mass-producible, weather-resistant and, above all, highly effective lightning protection system that can be used, in particular, on non-static industrial installations, such as wind turbines.

Diese Aufgabe wird durch die vorliegende Erfindung, wie sie in der Beschreibung, den Figuren und den Ansprüchen offenbart wird, gelöst. This object is achieved by the present invention as disclosed in the specification, figures and claims.

Dementsprechend ist Gegenstand der vorliegenden Erfindung eine Blitzschutzanlage in Form einer hochleitfähigen Verbundwerkstoffschicht, die auf der Oberfläche einer nicht-statischen Industrieanlage aufgebracht wird, wobei die Verbundwerkstoffschicht eine polymere Matrix, die mit hochleitfähigen Metallpartikeln gefüllt ist, umfasst. Accordingly, the subject of the present invention is a lightning protection system in the form of a highly conductive composite material layer, which is applied to the surface of a non-static industrial plant, wherein the composite material layer comprises a polymeric matrix filled with highly conductive metal particles.

Durch eine Verbundwerkstoffschicht oder Verbundwerkstoffbeschichtung nicht-statischer – beispielsweise – rotierender Flächen aus temperaturbeständigem Verbundwerkstoff, gefüllt mit hochleitfähigen Metallpartikeln, kann die Potentialdifferenz, die durch den Blitzeinschlag im Körper aufgebaut wird, über die große Oberfläche der Anlage abgebaut werden, ohne dass es durch lokale, sehr große Stromdichte zu Überhitzungsschäden an der nicht-statischen Industrieanlage kommt. By a composite layer or composite coating non-static - for example - rotating surfaces made of temperature-resistant composite material, filled with highly conductive metal particles, the potential difference, which is built up by the lightning strike in the body, can be reduced over the large surface of the system without being affected by local, very high current density leads to overheating damage to the non-static industrial plant.

Nach einer bevorzugten Ausführungsform der Erfindung wird die eine polymere Matrix, gefüllt mit beschichteten Metallpartikeln, als Blitzschutz auf die Oberfläche von beispielsweise Wind-Rotorblättern aufgebracht. According to a preferred embodiment of the invention, the one polymeric matrix filled with coated metal particles is applied as lightning protection on the surface of, for example, wind rotor blades.

Bevorzugt werden leitfähige Metallpartikel aus elementarem Metall und/oder Metalllegierung eingesetzt, bevorzugt aus einem hochleitfähigen edlen Metall wie beispielsweise Kupfer. Der Füllstoff in Form von „Metallpartikeln“ im Sinne der vorliegenden Erfindung kann eine Mischung verschiedener metallischer Partikelfraktionen umfassen oder in einer einzigen Partikelfraktion vorliegen. Die Unterschiede zwischen den einzelnen Partikelfraktionen können dabei sowohl im Metallpartikelmaterial, im Aufbau des einzelnen Metallpartikels, also beispielsweise beschichtet oder unbeschichtet, in der Form, also beispielsweise plättchen-, kugel-, faser- oder stabförmig, sowie in der mittleren Größe der Metallpartikel liegen. Preferably, conductive metal particles of elemental metal and / or metal alloy are used, preferably of a highly conductive noble metal such as copper. The filler in the form of "metal particles" in the sense of the present invention may comprise a mixture of different metallic particle fractions or be present in a single particle fraction. The differences between the individual particle fractions can be both in the metal particle material, in the structure of the individual metal particle, so for example coated or uncoated, in the form, so for example platelet, spherical, fibrous or rod-shaped, as well as in the average size of the metal particles.

Bevorzugt wird ein Füllstoff, der mehrere Fraktionen umfasst, eingesetzt. Preferably, a filler comprising a plurality of fractions is used.

Bevorzugt liegt die mittlere Größe der Partikel im Bereich von 5µm bis 500µm, insbesondere im Bereich von 20 µm bis 100µm und ganz bevorzugt im Bereich von 35 bis 80 µm. Bevorzugte Ausführungsformen der Erfindung umfassen Mischungen verschiedener Partikelformen, wobei Plättchen und Kugeln besonders bevorzugt sind. The average size of the particles is preferably in the range from 5 μm to 500 μm, in particular in the range from 20 μm to 100 μm and very preferably in the range from 35 to 80 μm. Preferred embodiments of the invention include mixtures of different particle shapes, with platelets and spheres being particularly preferred.

Durch Variation der mittleren Partikelgröße in einer bi- oder multimodalen Füllstoffmischung lassen sich insbesondere Kosten sparen, die Verarbeitbarkeit verbessern und außerdem besonders leichte Verbundwerkstoffschichten im Sinne von Leichtbau herstellen, weil Leitfähigkeitspfade mit geringem Gehalt an Füllstoff realisierbar sind. By varying the average particle size in a bimodal or multimodal filler mixture, it is possible in particular to save costs, improve processability and, moreover, to produce particularly lightweight composite layers in the sense of lightweight construction, because conductive paths having a low content of filler can be realized.

Nach einer besonders vorteilhaften Ausführungsform sind die Metallpartikel beschichtet, insbesondere mit einem Metall und/oder einem Metalloxid. Beispielsweise werden mit Metall beschichtete Metallpartikel, wie silberbeschichtete Kupferpartikel, eingesetzt, bei denen im Betrieb durch Korrosion die zunächst rein metallische Beschichtung langsam durch Oxidation zum Metalloxid korrodiert, bis letztendlich, nach komplett erfolgter Korrosion oder Oxidation anstelle der metallischen Beschichtung des Metallpartikels nur noch eine metalloxidische Beschichtung des Metallpartikels nachweisbar ist. Dazwischen sind alle Stufen der teilweise oxidierten Beschichtung des Metallpartikels nachweisbar. According to a particularly advantageous embodiment, the metal particles are coated, in particular with a metal and / or a metal oxide. For example, with metal-coated metal particles, such as silver-coated copper particles, used in which corrosion by corrosion, the initially purely metallic coating slowly oxidized by oxidation to the metal oxide, until ultimately, after complete corrosion or oxidation instead of the metallic coating of the metal particle only a metal oxide Coating of the metal particle is detectable. In between, all stages of the partially oxidized coating of the metal particle can be detected.

Dabei haben sich für die Beschichtung der Metallpartikel insbesondere die Metalle und/oder Legierungen als günstig erwiesen, bei denen die metallische Beschichtung des Metallpartikels korrosionsbeständig ist, insofern als die korrodierte Beschichtung, also das Metalloxid selbst leitfähig bleibt, sodass die Korrosion der Metallpartikel-Beschichtung keinen oder nur einen geringen negativen Einfluss auf die Leitfähigkeit des Partikels hat. In this case, in particular the metals and / or alloys have proved to be favorable for the coating of the metal particles, in which the metallic coating of the metal particle is corrosion resistant, inasmuch as the corroded coating, so the metal oxide itself remains conductive, so that the corrosion of the metal particle coating no or has only a slight negative influence on the conductivity of the particle.

Beispielsweise besteht die Beschichtung der Metallpartikel aus einem reinen Metall, dessen oberflächliche Oxidschicht ebenfalls elektrisch leitfähig ist, vorzugsweise aus Silber. For example, the coating of the metal particles consists of a pure metal whose superficial oxide layer is also electrically conductive, preferably of silver.

Für eine Beschichtung der Rotorblätter ist eine flexible Applikation des Verbundwerkstoffes vorteilhaft. Die hier vorgeschlagene Herstellung der Verbundwerkstoffbeschichtung umfasst die Schritte

  • – Herstellung einer verarbeitbaren Mischung aus Lösungsmittel, unvernetztem Polymer und Füllstoff
  • – Versprühen, Rakeln, Tauchen und/oder Pinseln der verarbeitbaren Mischung auf die nicht-statische Industrieanlage
  • – Aushärten und Vernetzung des Polymers und Entfernen des Lösungsmittels.
For a coating of the rotor blades, a flexible application of the composite material is advantageous. The production of the composite coating proposed here comprises the steps
  • - Preparation of a workable mixture of solvent, uncrosslinked polymer and filler
  • - Spraying, doctoring, dipping and / or brushing the processable mixture on the non-static industrial plant
  • - curing and crosslinking of the polymer and removal of the solvent.

Es wurden in Versuchen bereits mehrere polymere Matrizen in Applikationstestreihen durch Sprühen, Rakeln, Tauchen und/oder Pinseln als Verbundwerkstoffschichten appliziert, sodass gezeigt werden konnte, dass die erfindungsgemäßen Blitzschutzanlagen durch eine funktionelle Beschichtung auch auf einer gekrümmten Oberfläche anwendbar sind. Beispielsweise können auf diese Weise komplette Rotorflügel z.B. über Sprüh- und/oder Pinselapplikation beschichtet werden. Several polymer matrices in application test series have already been applied in experiments by spraying, knife coating, dipping and / or brushing as composite material layers, so that it could be shown that the lightning protection systems according to the invention can also be applied to a curved surface by means of a functional coating. For example, complete rotor blades, e.g. be coated by spraying and / or brush application.

Nach einer vorteilhaften Ausführungsform ist die Beschichtung ein Verbundwerkstoff, dessen metallischer Füllstoff ein plättchenförmiges, hochleitfähiges Metallsubstrat, wie beispielsweise Kupfer, das eine elektrisch leitfähige metallische Beschichtung, wie beispielsweise Silber, umfasst. Die oberflächliche Metallbeschichtung wird durch die Wechselwirkung mit dem Luftsauerstoff sowie der Luftfeuchtigkeit oxidiert, wobei – zumindest bei einer Beschichtung aus Silber – ein ebenfalls elektrisch leitfähiges Metalloxid gebildet wird, was den darunterliegenden Metallkern passiviert und die Partikelkontaktwiderstände großteils eliminiert. According to an advantageous embodiment, the coating is a composite whose metallic filler comprises a platelet-shaped, highly conductive metal substrate, such as copper, which comprises an electrically conductive metallic coating, such as silver. The superficial metal coating is oxidized by the interaction with the atmospheric oxygen and the air moisture, wherein - at least in a coating of silver - also an electrically conductive metal oxide is formed, which passivates the underlying metal core and largely eliminates the particle contact resistances.

In Bezug auf die geeigneten polymeren Matrizen wird hiermit vollinhaltlich auf die WO 2014/206676 verwiesen, deren Inhalt hiermit zum Inhalt der vorliegenden Anmeldung gemacht wird. With respect to the appropriate polymeric matrices is hereby incorporated in full WO 2014/206676 Reference is made to the content of the present application.

Insbesondere eignen sich als polymere Matrix beispielsweise Duroplasten wie z.B. Epoxide oder Polyurethane, Thermoplasten wie z.B. PEEK, PAI oder PEI und schließlich Polysiloxane wie z.B. Silikonelastomere oder Silikonharze, sowie beliebige Mischungen, Blends oder Copolymere der vorgenannten Verbindungen in Betracht. Bevorzugt werden polymere Matrixmaterialien, die bei Raumtemperatur härten, damit die Applikation vereinfacht ist. In particular, thermosets such as e.g. Epoxies or polyurethanes, thermoplastics such as e.g. PEEK, PAI or PEI and finally polysiloxanes such as e.g. Silicone elastomers or silicone resins, as well as any mixtures, blends or copolymers of the aforementioned compounds into consideration. Preference is given to polymeric matrix materials which cure at room temperature, so that the application is simplified.

1 zeigt ein Ausführungsbeispiel der vorliegenden Erfindung und dabei den Pfad der elektrischen Leitfähigkeit in der polymeren Matrix, der sich durch die Füllstoffpartikel bildet. 1 shows an embodiment of the present invention, and thereby the path of electrical conductivity in the polymeric matrix, which is formed by the filler particles.

1 zeigt die hochleitfähige Beschichtung der hochleitfähigen Partikel, beispielsweise die Silber(oxid)-Schicht 1 an der Oberfläche der Kupfer-Partikel 2, die den hochleitfähigen Kupferkern 3 passiviert und damit die Kontaktwiderstände 4 zwischen den Partikeln Silber, Silberoxid und/oder Kupfer eliminiert. 1 shows the highly conductive coating of highly conductive particles, such as the silver (oxide) layer 1 on the surface of the copper particles 2 containing the highly conductive copper core 3 passivated and thus the contact resistance 4 between the particles silver, silver oxide and / or copper eliminated.

Gezeigt wird in 1 eine hochleitfähige Beschichtung, die innerhalb der Perkolation, also bei 25 Gew% und darüber Füllstoffanteil an plättchenförmigem und/oder kugelförmigen Füllstoff, einen sehr niedrigen Widerstand aufweist. Shown in 1 a highly conductive coating, which has a very low resistance within the percolation, ie at 25% by weight and above the filler content of platelet-shaped and / or spherical filler.

In Tests wurde beispielsweise eine Beschichtung mit einem Quadratwiderstand von 0,2 Ohm bei 60 µm Schichtdicke hergestellt, was in der Größenordnung des Widerstands von Metallgittern oder Kohlefasergittern liegt, die unter anderem auch für Blitzschutzanwendungen zum Einsatz kommen. In tests, for example, a coating having a square resistance of 0.2 ohms at a layer thickness of 60 μm was produced, which is of the order of magnitude of the resistance of metal meshes or carbon fiber meshes which are also used, inter alia, for lightning protection applications.

In 2 ist die Perkolationskurve plättchenförmiger und kugelförmiger Metallpartikel in einem Lack, das ungehärtete Polymer und ein Lösungsmittel umfassend, eines – beispielsweise bei Raumtemperatur härtenden – Polymers dargestellt. Zu erkennen ist, dass bei einem Anteil in Gew% von über 30 Gew%, insbesondere aber bei ungefähr 60Gew% ein mit metallischen Leitern vergleichbarer Widerstand resultiert. In 2 Figure 3 shows the percolation curve of platelet and spherical metal particles in a varnish comprising uncured polymer and a solvent comprising a polymer curing at room temperature, for example. It can be seen that with a proportion in Gew% of over 30% by weight, but especially at about 60% by weight, a resistance comparable to metallic conductors results.

3 zeigt den Vorteil der Versilberung. In der Graphik werden Edelstahlpigmente, Kupferpigmente und versilberte Kupferpigmente hinsichtlich ihres Widerstandes bei 45 PMK in PEI verglichen. Auf der x-Achse sind dazu in dieser Reihenfolge jeweils Messungen von Säulen 1a, 1b Stahlpigment 100, 1a, 2b, Stahlpigment 200, 3a, 3b, versilbertes Kupfer 100, 4a, 4b, versilbertes Kupfer 200, 5 dendritisches Kupfer 100 und 6 plättchenförmiges Kupfer 100 aufgetragen. Die Zahlenwerte bezeichnen die Rakelspaltdicke. Zu den ersten 4 Füllstoffpigmenten gibt es jeweils zwei Messungen 1a, 1b, 2a, 2b, 3a, 3b, 4a, 4b, einmal bei Raumtemperatur und einmal bei 110°C. Bei 110°C ist der Widerstand in allen Fällen geringer als bei Raumtemperatur. 3 shows the advantage of silvering. In the graph, stainless steel pigments, copper pigments and silver-plated copper pigments are compared in terms of their resistance at 45 PMK in PEI. On the x-axis are in this order each measurements of columns 1a . 1b steel pigment 100 . 1a . 2 B , Steel pigment 200 . 3a . 3b , silvered copper 100 . 4a . 4b , silvered copper 200 . 5 dendritic copper 100 and 6 platelet-shaped copper 100 applied. The numbers indicate the squeegee gap thickness. To the first 4 There are two measurements each of filler pigments 1a . 1b . 2a . 2 B . 3a . 3b . 4a . 4b once at room temperature and once at 110 ° C. At 110 ° C the resistance is lower in all cases than at room temperature.

Die reinen Kupferpigmente sind per se hochohmiger als die versilberten Kupferpigmente, was auf die hochohmige Kupferoxidschicht zurückzuführen ist. Die Edelstahlpigmente sind ebenfalls hochohmiger, allerdings aufgrund der höheren intrinsischen Widerstände. Nach einer Temperaturauslagerung bei 110°C sind die reinen Kupferpigmente nach erfolgter Oxidation, also nachempfundener Korrosion, nicht mehr messbar, die Edelstahl und versilberten Kupferpigmente sind stabil, da das durch Korrosion aus der Silberbeschichtung entstandene Silberoxid den innenliegenden metallischen Kern passiviert und selbst sehr leitfähig ist. The pure copper pigments are per se higher-impedance than the silver-plated copper pigments, which is due to the high-resistance copper oxide layer. The stainless steel pigments are also high-impedance, but due to the higher intrinsic resistances. After a temperature aging at 110 ° C, the pure copper pigments are no longer measurable after oxidation, imitation corrosion, the stainless steel and silver-plated copper pigments are stable, since the silver oxide formed by corrosion from the silver coating passivated the internal metallic core and is itself very conductive ,

Plättchenförmige Metallpartikel mit oberflächiger Oxidschicht haben an dieser Stelle mehrere Vorteile gegenüber rein kugelförmigen Partikeln: Sie zeigen eine frühe Perkolationsschwelle, beispielsweise zum Teil bei unter 50 Gew.-%. Dabei spielt der Formfaktor eine Rolle. Das wäre bei der Dichte von Kupfer ein Volumenfüllgrad von unter 10 Vol% Füllgrad in der polymeren Matrix. Platelet-shaped metal particles with a surface oxide layer have several advantages at this point compared to purely spherical particles: they show an early percolation threshold, for example, in some cases less than 50% by weight. The form factor plays a role here. In the case of the density of copper, this would be a volume filling degree of less than 10% by volume of degree of filling in the polymeric matrix.

Durch die geringe Einwaage kommt es zu einer geringen Verbundwerkstoffdichte, was dem Leichtbauprinzip entspricht, also einem deutlichen Vorteil des hier erstmals vorgestellten hochleitfähigen Verbundwerkstoffes, insbesondere gegenüber der rein metallischen Variante einer Blitzschutzanlage, die herkömmlich bei – beispielsweise – Windkrafträdern eingesetzt wird. Due to the low weighing results in a low composite density, which corresponds to the lightweight principle, ie a significant advantage of the here presented for the first time highly conductive composite material, especially compared to the purely metallic variant of a lightning system, which is conventionally used in - for example - wind turbines.

Die mit Silber beschichteten Metallpartikel sind korrosionsbeständig, da sie an der Oberfläche durch Ausbildung des Metalloxids passiviert werden. The silver-coated metal particles are corrosion-resistant because they are passivated on the surface by formation of the metal oxide.

Die Metallpartikel führen im Vergleich zur herkömmlichen Blitzschutzanordnung über metallische Netze bevorzugt zu einer hohen Verarbeitungsstabilität der Applikationsrezeptur, weil es sich um einen Lack handelt und Lösemittel im Lack bei Applikation verwendet wird. The metal particles lead in comparison to the conventional lightning protection arrangement via metallic networks preferably to a high processing stability of the application formulation, because it is a paint and solvent in the paint is used in application.

Die vorliegenden Metallpartikel mit leitfähiger, passivierender Oxidschicht sind hinsichtlich ihres elektrischen Widerstandes den alternativen Füllstoffen und Füllstoffsystemen, wie beispielsweise mit keramischen Füllstoffen für die Eignung in einer Blitzschutzanlage weit überlegen. Beispielsweise wird der Quadratwiderstand in Ohm des Kupfer-Silber-Hybrids im Bereich von 10–1 Ohm bis 102 Ohm angegeben, wohingegen der Quadratwiderstand von Glimmer bei über 1012 liegt. The present metal particles with conductive, passivating oxide layer are far superior in their electrical resistance to the alternative fillers and filler systems, such as with ceramic fillers for suitability in a lightning protection system. For example, the square resistance in ohms of the copper-silver hybrid is reported in the range of 10 -1 ohms to 10 2 ohms, whereas the squareness of mica is more than 10 12 .

Durch Nutzung eines leicht applizierbaren Lackes, der mit elektrisch hochleitfähigen Metallpartikeln gefüllt und gut sprühbar ist, können vorgefertigte Bauteile, wie z.B. Rotorblätter von Windkraftanlagen leicht beschichtet und kontaktiert werden. Zudem können mit dieser Technologie auch polymere Bauteile im Luftfahrtbereich beschichtet werden, die somit als potentialabführend wirksam werden können, beispielsweise als Ersatz für Metallgitter oder Kohlefasergitter. By using an easily applied lacquer which is filled with electrically highly conductive metal particles and can be sprayed well, prefabricated components, such as e.g. Rotor blades of wind turbines are easily coated and contacted. In addition, this technology can also be used to coat polymer components in the aerospace industry, which can thus be effective as a potential dissipator, for example as a replacement for metal mesh or carbon fiber mesh.

Gemäß der Erfindung wird durch die sehr hohe Leitfähigkeit der Metallpartikel sowie der ebenfalls leitfähigen Metalloxidschicht an deren Oberfläche ein sehr gut leitfähiger und Langzeit temperaturstabiler Lack erzeugt, der eine gute elektrische Ableitung gewährleistet, da er einen in etwa gleichen Widerstand wie Metall- und/oder Kohlefasernetze/gitter hat. Durch die Möglichkeit einer flächendeckenden Beschichtung des gesamten Bauteils wird eine sehr große Querschnittsfläche für die Ableitung hoher elektrischer Ströme und Spannungen zu Verfügung gestellt. Somit entstehen im Falle eines Blitzeinschlages in der Beschichtung keine gefährlichen Temperaturerhöhungen durch lokale Ströme und es kommt zu keiner Degeneration der darunterliegenden Polymerschichten und/oder zu Überhitzung der elektrischen Komponenten. According to the invention, the very high conductivity of the metal particles as well as the likewise conductive metal oxide layer on the surface of a very good conductive and long-term temperature stable paint produced which ensures a good electrical dissipation, as it has a roughly equal resistance as metal and / or carbon fiber nets / grid has. The possibility of a comprehensive coating of the entire component a very large cross-sectional area for the dissipation of high electrical currents and voltages is provided. Thus, in the case of a lightning strike in the coating no dangerous Temperature increases due to local currents and there is no degeneration of the underlying polymer layers and / or overheating of the electrical components.

Nach einer bevorzugten Ausführungsform werden verschiedene Partikelformen eingesetzt. Insbesondere bewährt hat sich dabei die Mischung plättchenförmig / rund. Durch die Nutzung und Mischung verschiedener Partikelformen und/oder Partikelgrößen kann die Leitfähigkeit der Blitzschutzanlage weiter verbessert werden. According to a preferred embodiment, different particle shapes are used. In particular, the mixture has proven to be platelet-shaped / round. By using and mixing different particle shapes and / or particle sizes, the conductivity of the lightning protection system can be further improved.

In Messungen konnte nachgewiesen werden, dass Mischungen aus Kugeln und Plättchen desselben Füllstoff-Materials um 1 Dekade besser leitfähig sind, als die reinen Füllstoffe mit Partikel aus plättchenförmigen oder globularen Partikelformen. Measurements have shown that mixtures of spheres and platelets of the same filler material are more conductive for 1 decade than the pure fillers with particles of platelet or globular particle shapes.

Deshalb wird hier beispielsweise ein stöchiometrisches Verhältnis von kugel- zu plättchenförmigen Partikeln bis hin zu Mischungen von ein Drittel zu zwei Drittel plättchenförmig zu kugelig, vorgeschlagen. Therefore, for example, a stoichiometric ratio of spherical to platelet-shaped particles up to mixtures of one-third to two-thirds is proposed as platelike to spherical.

Es können verschiedenste Matrizen für die Blitzschutzbeschichtung verwendet werden. Hierfür wären denkbar:

  • – Duroplasten wie z.B. Epoxide oder Polyurethane,
  • – Thermoplasten wie z.B. PEEK, PAI oder PEI,
  • – Polysiloxane wie z.B. Silikonelastomere oder Silikonharze.
Various matrices can be used for the lightning protection coating. For this purpose, it would be conceivable:
  • Thermosets such as epoxies or polyurethanes,
  • Thermoplastics such as PEEK, PAI or PEI,
  • - Polysiloxanes such as silicone elastomers or silicone resins.

Es können verschiedenste Applikationsmethoden verwendet werden. Zur Herstellung einer Blitzschutzanlage gemäß der vorliegenden Erfindung eignen sich folgende Methoden:

  • – Pinselbeschichtung,
  • – Sprühbeschichtung,
  • – Tauchbeschichtung und/oder Pulverbeschichtung.
Various application methods can be used. For producing a lightning protection system according to the present invention, the following methods are suitable:
  • - brush coating,
  • Spray coating,
  • - dip coating and / or powder coating.

Durch die Erfindung wird erstmals ein hocheffektiver, leicht applizierbarer Verbundwerkstoff, der in dünnsten Schichten wie ein Lack aufbringbar ist, vorgestellt, der als effektive Blitzschutzanlage bei nicht-statischen Anlagen einsetzbar ist. Der Lack ist beliebig ausbesserbar und nachrüstbar und somit beliebig flexibel anwendbar. The invention introduces for the first time a highly effective, easily applied composite material which can be applied in the thinnest layers, such as a lacquer, which can be used as an effective lightning protection system in non-static systems. The paint can be repaired and retrofitted as desired and thus flexibly applicable.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • WO 2014/206676 [0008, 0024] WO 2014/206676 [0008, 0024]

Claims (11)

Blitzschutzanlage in Form einer hochleitfähigen Verbundwerkstoffschicht, die auf der Oberfläche einer nichtstatischen Industrieanlage aufgebracht wird, wobei die Verbundwerkstoffschicht eine polymere Matrix, die mit Metallpartikeln gefüllt ist, umfasst.  Lightning protection system in the form of a highly conductive composite layer, which is applied to the surface of a non-static industrial plant, wherein the composite layer comprises a polymeric matrix filled with metal particles. Blitzschutzanlage nach Anspruch 1, wobei die Dicke der Verbundwerkstoffschicht im Bereich von 5µm bis 2 mm, insbesondere von 5µm bis 300µm liegt. Lightning protection system according to claim 1, wherein the thickness of the composite material layer in the range of 5 .mu.m to 2 mm, in particular from 5 .mu.m to 300 .mu.m. Blitzschutzanlage nach einem der Ansprüche 1 oder 2, wobei die mittlere Größe der Metallpartikel im Bereich von 5µm bis 500 µm liegt. Lightning protection system according to one of claims 1 or 2, wherein the average size of the metal particles in the range of 5 .mu.m to 500 .mu.m. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei die Metallpartikel plättchen- und/oder kugelförmig vorliegen. Lightning protection system according to one of the preceding claims, wherein the metal particles are platelet and / or spherical. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei plättchen- und kugelförmige Metallpartikel im stöchiometrischen Verhältnis von ungefähr 1 zu 1 vorliegen. Lightning protection system according to one of the preceding claims, wherein platelet and spherical metal particles in the stoichiometric ratio of about 1 to 1 are present. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei die Metallpartikel überwiegend Kupferpartikel sind. Lightning protection system according to one of the preceding claims, wherein the metal particles are predominantly copper particles. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei die Metallpartikel beschichtet sind. Lightning protection system according to one of the preceding claims, wherein the metal particles are coated. Blitzschutzanlage nach einem der vorhergehenden Ansprüche wobei die Beschichtung der Metallpartikel aus Silber und/oder Silberoxid ist. Lightning protection system according to one of the preceding claims, wherein the coating of the metal particles of silver and / or silver oxide. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei die polymere Matrix bei Raumtemperatur härtet. Lightning protection system according to one of the preceding claims, wherein the polymeric matrix cures at room temperature. Blitzschutzanlage nach einem der vorhergehenden Ansprüche, wobei die polymere Matrix ausgewählt ist aus der Gruppe folgender Verbindungen: Duroplasten wie Epoxide und/oder Polyurethane; Thermoplasten wie PEEK, PAI und/oder PEI und/oder Polysiloxane wie Silikonelastomere und/oder Silikonharze, sowie beliebige Mischungen, Blends oder Copolymere der vorgenannten Verbindungen.  Lightning protection system according to one of the preceding claims, wherein the polymeric matrix is selected from the group consisting of the following compounds: thermosets such as epoxies and / or polyurethanes; Thermoplastics such as PEEK, PAI and / or PEI and / or polysiloxanes such as silicone elastomers and / or silicone resins, as well as any mixtures, blends or copolymers of the abovementioned compounds. Verfahren zur Herstellung einer Blitzschutzanlage nach einem der vorstehenden Ansprüche, folgende Schritte umfassend: – Herstellung einer verarbeitbaren Mischung aus Lösungsmittel, unvernetztem Polymer und Füllstoff – Versprühen, Rakeln, Tauchen und/oder Pinseln der verarbeitbaren Mischung auf die nichtstatische Industrieanlage und – Aushärten und Vernetzung des Polymers und Entfernen des Lösungsmittels. Method for producing a lightning protection system according to one of the preceding claims, comprising the following steps: - Preparation of a workable mixture of solvent, uncrosslinked polymer and filler Spraying, doctoring, dipping and / or brushing the processable mixture on the non-static industrial plant and - curing and crosslinking of the polymer and removal of the solvent.
DE102016214651.3A 2016-06-30 2016-08-08 Lightning protection system and method of manufacture Withdrawn DE102016214651A1 (en)