DE102016119887A1 - FCC catalysts as NH3 binder - Google Patents

FCC catalysts as NH3 binder Download PDF

Info

Publication number
DE102016119887A1
DE102016119887A1 DE102016119887.0A DE102016119887A DE102016119887A1 DE 102016119887 A1 DE102016119887 A1 DE 102016119887A1 DE 102016119887 A DE102016119887 A DE 102016119887A DE 102016119887 A1 DE102016119887 A1 DE 102016119887A1
Authority
DE
Germany
Prior art keywords
ammonia
binding
aluminum silicate
catalyst material
zeolite powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102016119887.0A
Other languages
German (de)
Inventor
Frank Schmidtgen
Hans-Peter Noack
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PROMETIMPEX GmbH
Original Assignee
PROMETIMPEX GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PROMETIMPEX GmbH filed Critical PROMETIMPEX GmbH
Priority to DE102016119887.0A priority Critical patent/DE102016119887A1/en
Priority to EP17800392.7A priority patent/EP3529208A1/en
Priority to PCT/EP2017/076676 priority patent/WO2018073332A1/en
Publication of DE102016119887A1 publication Critical patent/DE102016119887A1/en
Withdrawn legal-status Critical Current

Abstract

Die Erfindung betrifft ein Verfahren zur Bindung von Ammoniak (NH) unter Verwendung eines Bindemittels. Es ist Aufgabe der Erfindung, ein Verfahren bereit zu stellen, dessen Einsatz Ammoniak insoweit zu binden vermag, dass eine Geruchsbelästigung und auch eine Gefährdung für die Gesundheit deutlich verringert wird. Diese Aufgabe löst die Erfindung dadurch, dass das Bindemittel ein verbrauchtes Aluminiumsilikat-Katalysatormaterial (FCC-Katalysator) enthält.The invention relates to a process for the binding of ammonia (NH) using a binder. It is an object of the invention to provide a method, the use of which ammonia is able to bind to the extent that an odor nuisance and also a risk to health is significantly reduced. This object is achieved by the invention in that the binder contains a spent aluminum silicate catalyst material (FCC catalyst).

Description

Die Erfindung betrifft ein Verfahren zur Bindung von Ammoniak (NH3), wobei das Bindemittel ein aufbereitetes Aluminiumsilikat-Katalysatormaterial ist.The invention relates to a method for binding ammonia (NH 3 ), wherein the binder is a treated aluminum silicate catalyst material.

Ammoniak (NH3) ist der Grundstoff für die Synthese nahezu aller weiteren Stickstoffverbindungen und wird im großindustriellen Maßstab synthetisiert.Ammonia (NH 3 ) is the basic material for the synthesis of almost all other nitrogen compounds and is synthesized on a large scale.

Ammoniak entsteht beim Schmelzen von Aluminium an der Luft, wenn zumindest ein Teil des Aluminiums mit den Luft-Stickstoff zunächst zu Aluminiumnitrit und anschließend mit Wasser weiter zu Aluminiumhydroxid und Ammoniak reagiert: 2Al + N2 → 2AlN AlN + 3H2O → Al(OH)3 + NH3 Ammonia is formed when aluminum melts in the air when at least part of the aluminum reacts with the air-nitrogen first to aluminum nitrite and then further to aluminum hydroxide and ammonia with water: 2Al + N 2 → 2AlN AlN + 3H 2 O → Al (OH) 3 + NH 3

Diese zweite Reaktion spielt eine wichtige Rolle bei der Aufbereitung von Aluminium-Salzschlacke, die in einem nicht unerheblichen Maß von bis zu 70 % beim Recycling von Aluminium-Schrott entsteht.This second reaction plays an important role in the treatment of aluminum salt slag, which is produced to a considerable extent by up to 70% in the recycling of aluminum scrap.

In einem vorbekannten Verfahren wird Aluminium-Salzschlacke stufenweise aufbereitet. Nach einer mechanischen Zerkleinerung wird zunächst das Aluminium-Metall durch Siebung abgetrennt. Anschließend werden die in der restlichen Schlacke verbliebenen Salzkomponenten mit Wasser ausgewaschen, wobei das Aluminium mit Wasser zu Aluminium-Hydroxid und Wasserstoff reagiert: 2Al + 6H2O → 2Al(OH)3 + 3H2 In a previously known method, aluminum salt slag is processed stepwise. After mechanical comminution, the aluminum metal is first separated by sieving. Subsequently, the salt components remaining in the remaining slag are washed out with water, the aluminum reacting with water to give aluminum hydroxide and hydrogen: 2Al + 6H 2 O → 2Al (OH) 3 + 3H 2

Ferner kommt es zu der zuvor beschriebenen Reaktion, bei der Aluminiumnitrit mit Wasser zu Aluminiumhydroxid und Ammoniak reagiert: AlN + 3H2O → Al(OH)3 + NH3 Furthermore, there is the reaction described above, in which aluminum nitrite reacts with water to aluminum hydroxide and ammonia: AlN + 3H 2 O → Al (OH) 3 + NH 3

Der Ammoniak wird dabei in einer Gasreinigung aufgefangen und zu Düngemittel (Ammoniumsulfat) weiterverarbeitet. Jedoch verbleibt ein Teil des Ammoniaks gelöst im Wasser der aufbereiteten Salzschlacke. Die so aufbereitete Schlacke wird als synthetischer Aluminium-Rohstoff unter dem Namen SEROX in industriellem Umfang hergestellt und vertrieben.The ammonia is collected in a gas purification and processed into fertilizer (ammonium sulfate). However, part of the ammonia remains dissolved in the water of the treated salt slag. The slag processed in this way is manufactured and sold on an industrial scale as a synthetic aluminum raw material under the name SEROX.

SEROX weist zum Ende der Aufbereitung eine Feuchte von bis zu 35 % auf und hat eine schlammige Konsistenz. Durch Trocknung kann die Restfeuchte auf unter 25 % reduziert werden, wodurch das nun lagerfeuchte SEROX eine rieselfähige Konsistenz erreicht. Bei der Trocknung wird Ammoniak freigesetzt, der auch beim lagerfeuchten Produkt wahrnehmbar ist und erst nach vollständiger Trocknung verschwindet.At the end of the treatment, SEROX has a moisture content of up to 35% and has a muddy consistency. By drying, the residual moisture can be reduced to below 25%, so that the now moisture-saturated SEROX reaches a free-flowing consistency. When drying, ammonia is released, which is also noticeable in the product that is in storage and disappears only after complete drying.

Auch von künstlichen und natürlichen Düngemitteln ist bekannt, dass der darin gebundene Ammoniak gasförmig freigesetzt wird.It is also known from artificial and natural fertilizers that the ammonia bound in it is released in gaseous form.

Ammoniak entsteht auch bei der Zersetzung von tierischen Exkrementen durch Mikroorganismen in der (Massen-) Tierhaltung und Stallhaltung. Dies kann zu einem Problem werden, denn neben dem unangenehmen Geruch können größere Mengen Ammoniak gesundheitsschädlich vor allem auf die Lungen der Tiere und Menschen wirken. Ammoniak ist in der Folge zudem eine der Hauptursachen für die Bildung von Feinstaubpartikeln.Ammonia is also produced by the decomposition of animal excrements by microorganisms in (mass) animal husbandry and housing. This can be a problem, because in addition to the unpleasant odor, larger amounts of ammonia can be detrimental to health, especially on the lungs of animals and humans. Ammonia is also one of the main causes of particulate matter formation.

In all diesen Fällen ist die Freisetzung von Ammoniak aus gesundheitlichen wie auch aus Gründen der Geruchsbelästigung ungewünscht.In all these cases, the release of ammonia for health reasons as well as for reasons of odor nuisance is undesirable.

Es ist daher eine Aufgabe der Erfindung, ein Verfahren bereit zu stellen, dessen Einsatz Ammoniak insoweit zu binden vermag, dass eine Geruchsbelästigung und auch eine Gefährdung für die Gesundheit deutlich verringert wird.It is therefore an object of the invention to provide a method whose use ammonia is able to bind to the extent that an odor nuisance and also a risk to health is significantly reduced.

Eine weitere Aufgabe der Erfindung ist es, ein Verfahren zur Bindung von Ammoniak bereitzustellen, das in möglichst vielen verschiedenen Bereichen eingesetzt werden kann.Another object of the invention is to provide a process for binding ammonia which can be used in as many different areas as possible.

Nicht zuletzt ist es eine Aufgabe der Erfindung, ein Verfahren zur Bindung von Ammoniak bereitzustellen, dessen Verfahrensstoffe problemlos entweder recycelbar sind oder direkt einer weiteren Verwertung zugeführt werden können.Not least of all, it is an object of the invention to provide a process for binding ammonia, the process materials of which are either readily recyclable or can be fed directly to further utilization.

Gelöst wird diese Aufgabe durch ein Verfahren mit den Merkmalen des Anspruchs 1. Vorteilhafte Ausgestaltungen sind jeweils Gegenstand der abhängigen Ansprüche. Es ist darauf hinzuweisen, dass die in den Ansprüchen einzeln aufgeführten Merkmale auch in beliebiger und technologisch sinnvoller Weise miteinander kombiniert werden können und somit weitere Ausgestaltungen der Erfindung aufzeigen.This object is achieved by a method having the features of claim 1. Advantageous embodiments are the subject matter of the dependent claims. It should be noted that the features listed individually in the claims can also be combined with one another in any desired and technologically sensible manner and thus show further embodiments of the invention.

Ein im Sinne der Erfindung geeignetes pulverförmiges Aluminiumsilikat-Katalysatormaterial mit hohem Al2O3-Gehalt fällt in großen Mengen als Abfallstoff in der chemischen Industrie an. Es handelt sich hierbei vor allem um verbrauchte Cracking-Katalysatoren, die bei der Herstellung von Benzin aus Rohöl eingesetzt werden. Die Aluminiumsilikat-Katalysatoren können, gegebenenfalls nach einer vorherigen Aufbereitung, zu geringen Kosten bereitgestellt werden. Es werden also große Mengen von Abfallstoffen, die üblicherweise als Sondermüll zu entsorgen sind, einer sinnvollen Verwendung zugeführt.A suitable in the context of the invention powdered aluminum silicate catalyst material with high Al 2 O 3 content is obtained in large quantities as waste in the chemical industry. These are mainly used cracking catalysts used in the production of gasoline from crude oil. The aluminosilicate catalysts can be provided at low cost, optionally after a previous treatment. So it will be large amounts of Waste materials that are usually to be disposed of as hazardous waste, fed to a meaningful use.

Typische Aluminiumsilikat-Katalysatoren, die in der Petrochemie zum Cracken von Kohlenwasserstoff verwendet werden, bestehen zu etwa gleichen Teilen aus Siliziumoxid und Aluminiumoxid. Meist enthalten sie wenigstens 40 Gew.-% Aluminiumoxid und ebenfalls wenigstens 40 Gew.-% Siliziumoxid. Die übrigen Bestandteile, die in solchen Materialien üblicherweise enthalten sind, stören bei der Bindung von NH3 nicht.Typical aluminosilicate catalysts used in hydrocarbon cracking petrochemicals consist of approximately equal proportions of silica and alumina. Most of them contain at least 40% by weight of aluminum oxide and also at least 40% by weight of silicon oxide. The remaining ingredients commonly included in such materials do not interfere with the binding of NH 3 .

In der Regel handelt es sich bei dem gemäß der Erfindung verwendeten Aluminiumsilikat-Katalysatormaterial um ein synthetisches Zeolithpulver. Bei den üblichen Cracking-Katalysatoren handelt es sich nämlich um synthetische Zeolithe mit einem vergleichsweise hohen Al2O3-Gehalt und einer sehr regelmäßigen porösen Kristallstruktur. Die Zeolithpulver sind stark hygroskopisch und liegen üblicherweise in hydratisierter Form vor, was die Aufnahme von NH3 sehr begünstigt.As a rule, the aluminum silicate catalyst material used according to the invention is a synthetic zeolite powder. Namely, the conventional cracking catalysts are synthetic zeolites having a comparatively high Al 2 O 3 content and a very regular porous crystal structure. The zeolite powders are highly hygroscopic and are usually present in hydrated form, which favors the uptake of NH 3 very.

Zweckmäßigerweise wird das Zeolithpulver vor dem erfindungsgemäßen Einsatz einer Vorbehandlung durch Kalzinierung unterzogen. Insbesondere wenn das Zeolithpulver als Abfall aus der Chemieindustrie stammt, ist eine derartige Vorbehandlung empfehlenswert, um die in dem Material verbliebenen Kohlenwasserstoffreste zu entfernen.The zeolite powder is expediently subjected to a pretreatment by calcination prior to the use according to the invention. In particular, if the zeolite powder originates as waste from the chemical industry, such a pretreatment is recommended to remove the hydrocarbon residues remaining in the material.

Die so vorbehandelten Zeolithe verfügen über nahezu kein Ammonium mehr in ihrer Käfigstruktur, da dieses im Laufe der Anwendung in der Raffinerie und der nachfolgenden Aufbereitung vor allem gegen Lanthan, Wasserstoff oder Natrium ausgetauscht wurde. Die Zeolithe sind im Anschluss erneut in der Lage, Ammoniak als Kation in ihre Käfigstruktur einzutauschen. Dies gelingt vor allem bei einem ausreichend großen Konzentrationsgefälle zum Ammoniak.The zeolites pretreated in this way have virtually no ammonium in their cage structure, since this has been exchanged for lanthanum, hydrogen or sodium in the refinery during subsequent use and subsequent processing. The zeolites are then again able to exchange ammonia as a cation in their cage structure. This succeeds above all with a sufficiently large concentration gradient to the ammonia.

Bezüglich der Partikelgröße gibt es praktisch keine Einschränkungen, es können die üblicherweise in der chemischen Industrie anfallenden Körnungen der dort verwendeten FCC-Katalysatoren eingesetzt werden. Vorteilhafterweise kann die Partikel- beziehungsweise Granulatgröße bei dem gemäß der Erfindung eingesetzten Zeolithpulver jedoch problemlos in einem Bereich von 10 µm bis 1000 µm eingestellt werden, sofern eine spezielle Anwendung dies erfordern sollte. Entsprechend lässt sich das Material besonders leicht auch in der Größe herstellen, die für eine bestmögliche Vermischung mit den übrigen Ausgangsstoffen und somit für eine optimale NH3-Bindung benötigt wird. Beispielsweise kann das Zeolithpulver mit einem Bindemittel und Wasser gebunden werden. Hierbei sind beliebige Größen und Formen realisierbar, die den einzelnen Verwendungszwecken problemlos angepasst werden können. Als Bindemittel kommen übliche Zementsorten in Frage, beispielsweise schnellbindender Portlandzement, aber auch Asche aus der Verbrennung von Deinking-Rückständen der Altpapieraufbereitung, die einen hohen Mineralstoffgehalt haben.With regard to the particle size, there are practically no restrictions; it is possible to use the grain sizes of the FCC catalysts customarily used in the chemical industry. Advantageously, however, the particle or granule size in the zeolite powder used according to the invention can be easily adjusted in a range of 10 .mu.m to 1000 .mu.m, if a particular application so requires. Accordingly, the material is particularly easy to produce in the size that is needed for the best possible mixing with the other starting materials and thus for optimal NH 3 binding. For example, the zeolite powder may be bound with a binder and water. Here, any sizes and shapes can be realized, which can be easily adapted to the individual uses. Suitable binders are conventional cement types, for example fast-binding Portland cement, but also ashes from the combustion of deinking residues of waste paper processing, which have a high mineral content.

Wenn es sich bei dem Zeolithpulver um Zeolith A, X, Y oder ZSM handelt, ist ein besonders hoher Anteil von Aluminiumoxid sichergestellt. Vorzugsweise werden die genannten Zeolithe, bei denen das Silizium-zu-Aluminium-Verhältnis zwischen 1 und 5 liegt, großtechnisch in der chemischen Industrie eingesetzt.When the zeolite powder is zeolite A, X, Y or ZSM, a particularly high proportion of alumina is ensured. Preferably, said zeolites, in which the silicon to aluminum ratio is between 1 and 5, are used industrially in the chemical industry.

Als Ausführungsbeispiel der Erfindung ist in der folgenden Tabelle die Zusammensetzung eines Aluminiumsilikat-Katalysatormaterials angegeben, bei dem es sich um einen Cracking-Katalysator handelt, wie er üblicherweise in der chemischen Industrie zum Einsatz kommt: Tabelle 1 Gew.-% Al2O3 45,2 SiO2 46,4 TiO2 1,7 MgO 0,01 CaO 0,01 K2O 0,03 CeO2 0,01 La2O3 1,60 Nd2O3 0,03 Pr6O 11 0,14 As an embodiment of the invention, the following table shows the composition of an aluminosilicate catalyst material which is a cracking catalyst commonly used in the chemical industry: TABLE 1 Wt .-% Al 2 O 3 45.2 SiO 2 46.4 TiO 2 1.7 MgO 0.01 CaO 0.01 K 2 O 0.03 CeO 2 0.01 La 2 O 3 1.60 Nd 2 O 3 0.03 Pr 6 O 11 0.14

Vorteilhaft an dem erfindungsgemäßen Verfahren ist, dass das Katalysatormaterial nach Kalzinierung wie beschrieben einfach weiterverarbeitet und der jeweiligen Verwendung zugeführt werden kann. Dabei kommt es neben der reinen NH3-Bindung zu weiteren Vorteilen.An advantage of the method according to the invention is that the catalyst material after calcination as described can be easily further processed and fed to the respective use. It comes next to the pure NH 3 -Bindung to other benefits.

SEROX wird wie beschrieben durch die Aufbereitung von Salzschlacken aus der sekundären Aluminium-Gewinnung erhalten. Dabei dient SEROX unter anderem als Aluminium-Rohstofflieferant für die Produktion von Glasfasern (Mineralwolle) und versuchsweise auch für Glas.SEROX is obtained as described by the treatment of salt slags from the secondary aluminum recovery. Among other things, SEROX serves as an aluminum raw material supplier for the production of glass fibers (mineral wool) and on a trial basis also for glass.

Die Zeolithe werden dem SEROX zur Bindung von Ammoniak mit einem Anteil von 10 % bis 50 %, bevorzugt mit einem Anteil von 20 % bis 40 % und insbesondere mit einem Anteil von 30 % beigemengt.The zeolites are added to the SEROX for the binding of ammonia in a proportion of 10% to 50%, preferably in a proportion of 20% to 40% and in particular in a proportion of 30%.

Zudem kann durch die Beimengung des erfindungsgemäßen Zeolith-Pulvers neben der Verringerung des Ammoniak-Geruchs weiterhin eine Erhöhung des recht niedrigen SiO2-Gehaltes von SEROX (nur etwa 10%) erreicht werden (siehe Tabelle 1). Dies kann die Attraktivität eines solchen Gemisches für weitere Verwendungen erhöhen als auch einen anteilsmäßig höheren Einsatz in bekannten Verwendungen ermöglichen.In addition, by adding the zeolite powder according to the invention, in addition to the reduction of the ammonia odor, an increase in the relatively low SiO 2 content of SEROX (only about 10%) can furthermore be achieved (see Table 1). This may increase the attractiveness of such a mixture for other uses as well as enable a proportionately higher use in known uses.

Zeolithe sind als poröse Mineralien seit langem als Zuschlagsstoffe für Böden in der Landwirtschaft oder auch im Garten bekannt. Das Zusetzen des erfindungsgemäßen Zeolith-Pulvers zu Düngemitteln führt neben der Verringerung des Ammoniak-Geruchs zusätzlich zu den bekannten Vorteilen für die so gedüngten Böden, wie beispielsweise eine hohe Wasserspeicherkapazität. Weitere Stoffe können einem so hergestellten Dünger problemlos beigemischt werden, die Zeolithe sorgen für seine Speicherung.Zeolites have long been known as porous minerals as aggregates for soils in agriculture or in the garden. The addition of the zeolite powder according to the invention to fertilizers results in addition to the reduction of the ammonia odor in addition to the known advantages for the thus fertilized soils, such as a high water storage capacity. Other substances can be easily added to a fertilizer produced in this way, the zeolites provide for its storage.

Bei der Verwendung des erfindungsgemäßen Zeolith-Pulvers zur Verringerung des Ammoniak-Geruchs als Einstreu in der Tierhaltung, beispielweise im Stall oder im Heimtierbereich, oder als Filtermaterial, beispielsweise in Luftfiltern, kann das verbrauchte Material gegebenenfalls auch ohne weitere Aufbereitung als natürlicher, geruchsarmer Stickstoffdünger verwendet werden.When using the zeolite powder according to the invention for reducing the ammonia odor as bedding in animal husbandry, for example in the stable or in the pet animal area, or as a filter material, for example in air filters, the spent material may also be used as natural, low-odor nitrogen fertilizer without further treatment become.

Die genannten Verwendungsmöglichkeiten sind selbstverständlich nur bevorzugte Beispiele. Grundsätzlich ist das erfindungsgemäße Verfahren und seine Verwendung nicht hierauf beschränkt.The aforementioned uses are of course only preferred examples. In principle, the method according to the invention and its use are not limited thereto.

Claims (17)

Verfahren zur Bindung von Ammoniak (NH3) unter Verwendung eines Bindemittels, dadurch gekennzeichnet, dass das Bindemittel ein verbrauchtes Aluminiumsilikat-Katalysatormaterial (FCC-Katalysator) enthält.Process for the binding of ammonia (NH 3 ) using a binder, characterized in that the binder contains a spent aluminum silicate catalyst material (FCC catalyst). Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass das Aluminiumsilikat-Katalysatormaterial wenigstens 35 Gew.-% Aluminiumoxid und wenigstens 35 Gew.-% Siliziumoxid enthält.Method according to Claim 1 , characterized in that the aluminosilicate catalyst material contains at least 35% by weight of alumina and at least 35% by weight of silica. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass das Aluminiumsilikat-Katalysatormaterial bis zu 5 Gew.-% Magnesiumoxid enthält.Method according to Claim 1 , characterized in that the aluminum silicate catalyst material contains up to 5 wt .-% magnesium oxide. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass das Aluminiumsilikat-Katalysatormaterial bis zu 1 Gew.-% Titanoxid enthält.Method according to Claim 1 , characterized in that the aluminum silicate catalyst material contains up to 1 wt .-% titanium oxide. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass das Aluminiumsilikat-Katalysatormaterial bis zu 5 Gew.-% Natrium- und/oder Kaliumoxid enthält.Method according to Claim 1 , characterized in that the aluminum silicate catalyst material contains up to 5 wt .-% sodium and / or potassium oxide. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass das Aluminiumsilikat-Katalysatormaterial bis zu 5 Gew.-% Selten-Erd-Oxide, insbesondere Lanthanoxid enthält.Method according to Claim 1 , characterized in that the aluminum silicate catalyst material contains up to 5 wt .-% rare earth oxides, in particular lanthanum oxide. Verfahren nach Anspruch 1, dadurch gekennzeichnet, dass es sich bei dem Aluminiumsilikat-Katalysatormaterial um ein synthetisches Zeolithpulver handelt.Method according to Claim 1 , characterized in that the aluminum silicate catalyst material is a synthetic zeolite powder. Verfahren nach Anspruch 7, dadurch gekennzeichnet, dass das Zeolithpulver vor Verwendung einer Vorbehandlung durch Kalzinierung unterzogen wird.Method according to Claim 7 , characterized in that the zeolite powder is subjected before use by pretreatment by calcination. Verfahren nach Anspruch 7, dadurch gekennzeichnet, dass das Zeolithpulver Zeolith A, X, Y oder ZSM enthält.Method according to Claim 7 , characterized in that the zeolite powder contains zeolite A, X, Y or ZSM. Verfahren nach einem der vorherigen Ansprüche, dadurch gekennzeichnet, dass das Zeolithpulver eine Partikelgröße zwischen 1 µm und 1000 µm aufweist.Method according to one of the preceding claims, characterized in that the zeolite powder has a particle size between 1 micron and 1000 microns. Verfahren nach Anspruch 10, dadurch gekennzeichnet, dass die Partikel zu Granulaten, Pellets oder sonstigen Körpern verarbeitet werden.Method according to Claim 10 , characterized in that the particles are processed into granules, pellets or other bodies. Verwendung von pulverförmigem oder granuliertem Cracking-Katalysator mit einem Aluminiumoxid-Gehalt von wenigstens 35 Gew.-% für die Bindung von Ammoniak (NH3) gemäß einem der Ansprüche 1 bis 11.Use of powdered or granulated cracking catalyst having an alumina content of at least 35 wt .-% for the binding of ammonia (NH 3 ) according to one of Claims 1 to 11 , Verwendung nach Anspruch 12, wobei der Cracking-Katalysator mit SEROX vermengt wird, um die Freisetzung von Ammoniak aus SEROX zu reduzieren.Use after Claim 12 wherein the cracking catalyst is blended with SEROX to reduce the release of ammonia from SEROX. Verwendung nach Anspruch 13, wobei der Cracking-Katalysator dem SEROX mit einem Anteil von 10 % bis 50 %, bevorzugt mit einem Anteil von 20 % bis 40 % und insbesondere mit einem Anteil von 30 % beigemengt wird.Use after Claim 13 , wherein the cracking catalyst is added to the SEROX in a proportion of 10% to 50%, preferably in a proportion of 20% to 40% and in particular in a proportion of 30%. Verwendung nach Anspruch 12 für die Bindung von Ammoniak in Luftfiltern.Use after Claim 12 for the binding of ammonia in air filters. Verwendung nach Anspruch 12 für die Bindung von Ammoniak in Dünger, wobei der Cracking-Katalysator mit dem Dünger vermengt wird.Use after Claim 12 for the binding of ammonia to fertilizer, wherein the cracking catalyst is mixed with the fertilizer. Verwendung von pulverförmigem Cracking-Katalysator mit einem Aluminiumoxid-Gehalt von wenigstens 35 Gew.-% als Einstreu in der Tierhaltung zur Bindung von Ammoniak (NH3) gemäß einem der Ansprüche 1 bis 11.Use of powdery cracking catalyst with an alumina content of at least 35 wt .-% as litter in animal husbandry for the binding of ammonia (NH 3 ) according to one of Claims 1 to 11 ,
DE102016119887.0A 2016-10-19 2016-10-19 FCC catalysts as NH3 binder Withdrawn DE102016119887A1 (en)