DE102014225156A1 - Functional polyurethane foam - Google Patents

Functional polyurethane foam Download PDF

Info

Publication number
DE102014225156A1
DE102014225156A1 DE102014225156.7A DE102014225156A DE102014225156A1 DE 102014225156 A1 DE102014225156 A1 DE 102014225156A1 DE 102014225156 A DE102014225156 A DE 102014225156A DE 102014225156 A1 DE102014225156 A1 DE 102014225156A1
Authority
DE
Germany
Prior art keywords
weight
parts
polyol
polyurethane foam
koh
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE102014225156.7A
Other languages
German (de)
Inventor
Jeong-Seok Oh
Gun Kang
Sung-Hyun Lee
Hye-Min Lee
Soon Joon Jung
Mi Jung Yun
Kwon-Yong Choi
Gi-Man Kim
Byeong-Guk LIM
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hyundai Motor Co
Kia Corp
Original Assignee
Hyundai Motor Co
Kia Motors Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hyundai Motor Co, Kia Motors Corp filed Critical Hyundai Motor Co
Priority to DE102014225156.7A priority Critical patent/DE102014225156A1/en
Publication of DE102014225156A1 publication Critical patent/DE102014225156A1/en
Ceased legal-status Critical Current

Abstract

Die vorliegende Erfindung betrifft funktionale Polyurethanschäume und insbesondere funktionale Polyurethanschäume, die ein Reaktionsprodukt einer Harzvormischung und einer Isocyanatkomponente einschließen, worin die Harzvormischung eine Polyolkomponente und ein Schäummittel einschließt und die Isocyanatkomponente monomeres Methylendiphenyldiisocyanat (MMDI) zu 4 bis 70 Gew.%, Carbodiimidmethylendiphenyldiisocyanat (CMDI) zu 5 bis 70 Gew.% und polymeres Methylendiphenyldiisocyanat (PMDI) zu 10 bis 80 Gew.% in Bezug auf das Gesamtgewicht der Isocyanatkomponente einschließt. Die funktionalen Polyurethanschäume der vorliegenden Erfindung sind in der Lage, für Fahrzeugsitze eingesetzt zu werden und die Vibrationsdurchlässigkeit zu minimieren, indem sie einen beträchtlichen Anteil der Vibrationen, die während der Fahrt auftreten, absorbieren.The present invention relates to functional polyurethane foams, and more particularly to functional polyurethane foams which include a reaction product of a resin premix and an isocyanate component wherein the resin premix includes a polyol component and a foaming agent and the isocyanate component is methylene diphenyl diisocyanate (MMDI) 4 to 70 wt%, carbodiimide methylene diphenyl diisocyanate (CMDI). from 5 to 70% by weight and polymeric methylene diphenyl diisocyanate (PMDI) at 10 to 80% by weight relative to the total weight of the isocyanate component. The functional polyurethane foams of the present invention are capable of being used on vehicle seats and minimizing vibration permeability by absorbing a significant portion of the vibrations that occur during travel.

Description

TECHNISCHES GEBIETTECHNICAL AREA

Die vorliegende Erfindung betrifft Polyurethanschäume, und insbesondere funktionale Polyurethanschäume, die geeignet sind, für Fahrzeugsitze eingesetzt zu werden und die Durchlässigkeit für Vibration zu minimieren, indem sie einen beträchtlichen Anteil der Vibrationen, die während der Fahrt auftreten, absorbieren. Die vorliegende Erfindung betrifft weiterhin einen Fahrzeugsitz, der einen solchen Polyurethanschaum einschließt.The present invention relates to polyurethane foams, and more particularly to functional polyurethane foams which are suitable for use in vehicle seats and to minimize the transmission of vibration by absorbing a significant portion of the vibrations that occur during travel. The present invention further relates to a vehicle seat including such a polyurethane foam.

TECHNISCHER HINTERGRUNDTECHNICAL BACKGROUND

Mit der Entwicklung der Automobilindustrie nimmt die im Inneren von Fahrzeugen verbrachte Zeitdauer zu, und gegenwärtig ist die Wichtigkeit des Fahrkomforts in Fahrzeugen bedeutsam geworden. Folglich wurde das Niveau der Kundenanforderungen für Komfort im Automobil sehr hoch.With the development of the automobile industry, the amount of time spent inside vehicles is increasing, and currently the importance of ride comfort in vehicles has become significant. As a result, the level of customer demands for comfort in the automobile has become very high.

Polyurethanschaum wird im allgemeinen durch die Reaktion einer Harzvormischung (premix) und Isocyanat hergestellt. Die Harzvormischung ist eine Rohflüssigkeit, in der Polyol, ein Vernetzungsmittel, ein Katalysator, ein Schäummittel und weitere Additive gemischt sind, und das Isocyanat ist ein Hauptmaterial in einer Polyurethanreaktion und reagiert mit der Harzvormischung, um eine Urethanbindung zu bilden.Polyurethane foam is generally made by the reaction of a premix and isocyanate. The resin premix is a raw liquid in which polyol, a crosslinking agent, a catalyst, a foaming agent and other additives are mixed, and the isocyanate is a main material in a polyurethane reaction and reacts with the resin premix to form a urethane bond.

Ein solcher Polyurethanschaum ist in verschiedenen Zusammensetzungen bekannt, und beispielsweise offenbart das koreanische Patent Nr. 10-0883514 eine Polyurethanschaumzusammensetzung, die überlegene Dauerhaftigkeit und Hydrolyseresistenz aufweist. Allerdings weist der bestehende Polyurethanschaum im allgemeinen keine wesentlich bessere Vibrationsabsorption auf. Wenn dieser Polyurethanschaum daher für Fahrzeugsitze eingesetzt wird und ein Fahrer für eine lange Zeitdauer fährt, so bestand das Problem, dass Fahrzeugvibrationen kontinuierlich übertragen werden, was Unannehmlichkeit verursacht, selbst wenn der Einfluss bei kurzzeitigem Fahren unbedeutsam ist.Such a polyurethane foam is known in various compositions, and discloses, for example Korean Patent No. 10-0883514 a polyurethane foam composition that has superior durability and resistance to hydrolysis. However, the existing polyurethane foam generally does not have much better vibration absorption. Therefore, when this polyurethane foam is used for vehicle seats and a driver is driving for a long period of time, there has been a problem that vehicle vibrations are continuously transmitted, causing inconvenience even if the influence in short-term driving is insignificant.

OFFENBARUNGEPIPHANY

TECHNISCHE AUFGABETECHNICAL TASK

Ein Ziel der vorliegenden Erfindung in Anbetracht des oben gesagten ist die Bereitstellung eines funktionalen Polyurethanschaums mit verbesserter Vibrationsabsorption. Ein weiteres Ziel ist die Bereitstellung eines Fahrzeugsitzes, der einen solchen funktionalen Polyurethanschaum einschließt.An object of the present invention in view of the above is to provide a functional polyurethane foam having improved vibration absorption. Another object is to provide a vehicle seat incorporating such a functional polyurethane foam.

TECHNISCHE LÖSUNGTECHNICAL SOLUTION

Die vorliegende Erfindung stellt einen funktionalen Polyurethanschaum bereit, der ein Reaktionsprodukt einer Harzvormischung und einer Isocyanatkomponente einschließt oder daraus besteht, worin die Harzvormischung eine Polyolkomponente und ein Schäummittel einschließt, und die Isocyanatkomponente monomeres Methylendiphenyldiisocyanat (MMDI) zu 4 bis 70 Gew.%, Carbodiimidmethylendiphenyldiisocyanat (CMDI) zu 5 bis 70 Gew.% und polymeres Methylendiphenyldiisocyanat (PMDI) zu 10 bis 80 Gew.% in Bezug auf das Gesamtgewicht der Isocyanatkomponente einschließt.The present invention provides a functional polyurethane foam which includes or consists of a reaction product of a resin premix and an isocyanate component wherein the resin premix includes a polyol component and a foaming agent and the isocyanate component is methylene diphenyl diisocyanate (MMDI) 4 to 70% by weight, carbodiimide methylene diphenyl diisocyanate ( CMDI) to 5 to 70% by weight and polymeric methylene diphenyl diisocyanate (PMDI) to 10 to 80% by weight relative to the total weight of the isocyanate component.

Hierbei weist die Polyolkomponente vorzugsweise einen Hydroxylwert (OH-Wert) von 10 bis 60 mg KOH/g auf und ist vorzugsweise eine oder mehrere Polyolkomponente(n) mit einem OH-Wert ausgewählt aus der Gruppe bestehend aus 20 bis 40 mg KOH/g, 20 bis 50 mg KOH/g, 20 bis 60 mg KOH/g und 10 bis 30 mg KOH/g, und die Polyolkomponente kann ein Polyol mit einem OH-Wert von 20 bis 40 mg KOH/g zu 40 bis 75 Gew.%; ein Polyol mit einem OH-Wert von 20 bis 50 mg KOH/g zu 10 bis 40 Gew.%; und ein Polyol mit einem OH-Wert von 10 bis 30 mg KOH/g zu 3 bis 40 Gew.% in Bezug auf das Gesamtgewicht der Polyolkomponente einschließen.Here, the polyol component preferably has a hydroxyl value (OH value) of 10 to 60 mg KOH / g and is preferably one or more polyol component (s) having an OH value selected from the group consisting of 20 to 40 mg KOH / g, 20 to 50 mg KOH / g, 20 to 60 mg KOH / g and 10 to 30 mg KOH / g, and the polyol component can be a polyol having an OH value of 20 to 40 mg KOH / g to 40 to 75 wt.% ; a polyol having an OH value of 20 to 50 mg KOH / g at 10 to 40% by weight; and a polyol having an OH value of 10 to 30 mg KOH / g at 3 to 40% by weight with respect to the total weight of the polyol component.

Außerdem kann die Harzvormischung weiterhin einen Härtungskatalysator, einen Schäumkatalysator, ein Vernetzungsmittel, ein Kettenerweiterungsmittel und ein Tensid einschließen.In addition, the resin premix may further include a curing catalyst, a foaming catalyst, a crosslinking agent, a chain extender, and a surfactant.

Hierbei ist in Bezug auf 100 Gew.-Teile der Polyolkomponente die Isocyanatkomponente vorzugsweise zu 40 bis 70 Gew.-Teilen, der Härtungskatalysator zu 0,1 bis 3 Gew.-Teilen, der Schäumkatalysator zu 0,1 bis 2 Gew.-Teilen, das Schäummittel zu 1 bis 5 Gew.-Teilen und das Vernetzungsmittel zu 0,1 bis 5 Gew.-Teilen enthalten, und das Kettenerweiterungsmittel ist vorzugsweise mit einem Kettenerweiterungsmittel mit einem OH-Wert von 1.500 bis 2.500 mg KOH/g zu 1 bis 10 Gew.-Teilen und einem Kettenerweiterungsmittel mit einem OH-Wert von 500 bis 1.500 mg KOH/g zu 0,1 bis 1 Gew.-Teilen enthalten, und das Tensid ist vorzugsweise zu 0,1 bis 3 Gew.-Teilen enthalten.Here, with respect to 100 parts by weight of the polyol component, the isocyanate component is preferably 40 to 70 parts by weight, the curing catalyst is 0.1 to 3 parts by weight, the foaming catalyst is 0.1 to 2 parts by weight, the foaming agent to 1 to 5 parts by weight and the crosslinking agent to 0.1 to 5 parts by weight and the chain extender is preferably added to a chain extender having an OH value of 1,500 to 2,500 mg KOH / g to 1 to 10 parts by weight and a chain extender having an OH value of 500 to 1,500 mg KOH / g to 0, 1 to 1 parts by weight, and the surfactant is preferably contained at 0.1 to 3 parts by weight.

Fahrzeugsitze können durch allgemein bekannte Verfahren unter Einsatz des funktionalen Polyurethanschaums, der solche Zusammensetzungen erfüllt, hergestellt werden.Vehicle seats can be made by well-known methods using the functional polyurethane foam that satisfies such compositions.

VORTEILHAFTE WIRKUNGENBENEFICIAL EFFECTS

Ein erfindungsgemäßer funktionaler Polyurethanschaum, der die oben beschriebenen Zusammensetzungen aufweist, hat den Vorteil, dass er im Vergleich zu bestehenden Polyurethanschäumen eine überragende Vibrationsabsorption aufweist.A functional polyurethane foam of the present invention having the above-described compositions has the advantage that it has superior vibration absorption as compared with existing polyurethane foams.

Des weiteren kann, wenn Fahrzeugsitze unter Einsatz des funktionalen Polyurethanschaums hergestellt werden, der Komfort verbessert werden, indem ein beträchtlicher Anteil von Vibrationen, die auf der Straße auftreten, absorbiert wird.Further, when manufacturing vehicle seats using the functional polyurethane foam, comfort can be improved by absorbing a significant amount of vibration occurring on the road.

Weiterhin wird dadurch, dass Toluoldiisocyanat (TDI), das in bestehenden Polyurethanschäumen eingesetzt wird, nicht enthalten ist und nur Methylendiphenyldiisocyanate (MDIs) als Isocyanatkomponente eingesetzt werden, die Spannungsreduktion des Schaumsitzes minimiert, und die Haltekraft zum Stützen des Körpers des Fahrers kann für eine lange Zeitdauer verbessert werden.Further, by not using toluene diisocyanate (TDI) used in existing polyurethane foams and using only methylene diphenyl diisocyanates (MDIs) as the isocyanate component, the stress reduction of the foam seat is minimized, and the holding force for supporting the driver's body can be long Time duration to be improved.

KURZE BESCHREIBUNG DER ZEICHNUNGENBRIEF DESCRIPTION OF THE DRAWINGS

1 ist ein Zeit-Spannungs-Graph eines Sitz-Schaums, der unter Einsatz von TDI hergestellt wurde, und eines Sitz-Schaums, der erfindungsgemäß unter Einsatz von MDI hergestellt wurde.
100: Sitzschaum, hergestellt unter Verwendung von TDI
200: Sitzschaum, hergestellt unter Verwendung von MDI 1 is a time-stress graph of a seat foam made using TDI and a seat foam made in accordance with the invention using MDI.
100: Seat foam made using TDI
200: Seat foam made using MDI

BESTER MODUS DER ERFINDUNGBEST MODE OF THE INVENTION

Im folgenden wird die vorliegende Erfindung im Detail unter Bezugnahme auf die beigefügte Zeichnung beschrieben.In the following, the present invention will be described in detail with reference to the accompanying drawings.

Ein Aspekt der vorliegenden Erfindung betrifft einen funktionalen Polyurethanschaum, dessen Vibrationsabsorption signifikant verbessert ist.One aspect of the present invention relates to a functional polyurethane foam whose vibration absorption is significantly improved.

Polyurethanschaum, der im allgemeinen für Fahrzeugsitze und ähnliches eingesetzt wird, ist ein Weichschaum, der durch Umsetzung einer Urethanschaumzusammensetzung, die ein Polyol, Isocyanat, einen Katalysator, ein Vernetzungsmittel, ein Tensid und ein Schäummittel enthält, erhalten wird. Das Polyol hat eine Hydroxy-funktionelle Gruppe(-OH) und das Isocyanat hat eine Isocyanat-funktionelle Gruppe(-NCO) im Molekül.Polyurethane foam, which is generally used for vehicle seats and the like, is a flexible foam obtained by reacting a urethane foam composition containing a polyol, isocyanate, a catalyst, a crosslinking agent, a surfactant and a foaming agent. The polyol has a hydroxy-functional group (-OH) and the isocyanate has an isocyanate-functional group (-NCO) in the molecule.

Das Polyol wird als Monol, Diol, Triol und ähnliches eingeteilt, in Abhängigkeit von der Anzahl der funktionellen Gruppen im Molekül, und das Isocyanat wird als Monoisocyanat, Diisocyanat und ähnliches in Abhängigkeit von der Anzahl funktioneller Gruppen im Molekül eingeteilt.The polyol is classified as monol, diol, triol and the like depending on the number of functional groups in the molecule, and the isocyanate is classified as monoisocyanate, diisocyanate and the like depending on the number of functional groups in the molecule.

Eine Urethanbindung wird typischerweise durch Verbinden von Alkohol, der eine aktive Hydroxylgruppe aufweist und Isocyanat, das eine Isocyanatgruppe aufweist, gebildet, wie in der folgenden chemischen Formel 1 gezeigt.A urethane bond is typically formed by combining alcohol having an active hydroxyl group and isocyanate having an isocyanate group, as shown in the following Chemical Formula 1.

Chemische Formel 1Chemical formula 1

  • R-NCO + R'-OH → R-NH-COO-R' R-NCO + R'-OH → R-NH-COO-R '

Ein Polymer, das eine solche Urethanbindung in großer Menge aufweist, wird als Polyurethan bezeichnet, und ein solcher Polyurethanschaum wird weit verbreitet für Fahrzeugkomponenten und Materialien eingesetzt, aufgrund von überlegenen Eigenschaften wie niedriger Dichte, hoher mechanischer Festigkeit, hoher Wärmebeständigkeit und ähnliches, und wird insbesondere weit verbreitet aufgrund der niedrigen Dichte und überlegenen Dauerhaftigkeit für Fahrzeugsitze eingesetzt.A polymer having such a urethane bond in a large amount is referred to as a polyurethane, and such a polyurethane foam is widely used for vehicle components and materials because of superior properties such as low density, high mechanical strength, high heat resistance and the like, and particularly Widely used for vehicle seats due to the low density and superior durability.

Die vorliegende Erfindung betrifft einen Polyurethanschaum, der ein Reaktionsprodukt einer Harzvormischung und einer Isocyanatkomponente enthält, worin die Harzvormischung eine Polyolkomponente und ein Schäummittel einschließt und die Isocyanatkomponente monomeres Methylendiphenyldiisocyanat (MMDI) zu 4 bis 70 Gew.%; Carbodiimidmethylendiphenyldiisocyanat (CMDI) zu 5 bis 70 Gew.%; und polymeres Methylendiphenyldiisocyanat (CMDI) zu 10 bis 80 Gew.% in Bezug auf das Gesamtgewicht der Isocyanatkomponente einschließt. Die Isocyanatkomponente kann zu 40 bis 70 Gew.-Teilen in Bezug auf 100 Gew.-Teilen der Polyolkomponente zugemischt und eingesetzt werden. The present invention relates to a polyurethane foam containing a reaction product of a resin premix and an isocyanate component, wherein the resin premix includes a polyol component and a foaming agent and the isocyanate component comprises methylene diphenyl diisocyanate (MMDI) at 4 to 70% by weight; Carbodiimide methylene diphenyl diisocyanate (CMDI) at 5-70% by weight; and polymeric methylene diphenyl diisocyanate (CMDI) at 10 to 80 wt.% relative to the total weight of the isocyanate component. The isocyanate component may be blended and used at 40 to 70 parts by weight with respect to 100 parts by weight of the polyol component.

Im folgenden wird der erfindungsgemäße Polyurethanschaum im Detail unter Bezugnahme auf die folgende Tabelle 1 untersucht. Tabelle 1 Bestandteil Zusammensetzung Anmerkung Erstes Polyol 40,0 bis 75,0 Gew.% Glycerin, OH-Wert = 20 bis 40 mg KOH/g Zweites Polyol 10,0 bis 40,0 Gew.% Glycerin, OH-Wert = 20 bis 50 mg KOH/g Drittes Polyol 5,0 bis 30,0 Gew.% Glycerin, OH-Wert = 20 bis 60 mg KOH/g Viertes Polyol 3,0 bis 40,0 Gew.% Glycerin, OH-Wert = 10 bis 30 mg KOH/g Feststoff 30 bis 50% Erstes Kettenerweiterungsmittel 1,0 bis 10,0 Gew.-Teile Diethanolamin, OH-Wert = 1.500 bis 2.500 mg KOH/g Zweites Kettenerweiterungsmittel 0,1 bis 1,0 Gew.-Teile 1,4-Butandiol, OH-Wert = 500 bis 1.500 mg KOH/g Vernetzungsmittel 0,1 bis 5,0 Gew.-Teile Triethanolamin, OH-Wert = 1.500 bis 2.500 mg KOH/g Wasser (Schäummittel) 1,0 bis 5,0 Gew.-Teile OH-Wert = 6.000 bis 7.000 mg KOH/g Härtungskatalysator (Dabco 33LV) (Air Products, US) 0,1 bis 3,0 Gew.-Teile 33% Triethylendiamin 67% Dipropylenglycol Schäumkatalysator (Dabco BL-11) (Air Products, US) 0,1 bis 2,0 Gew.-Teile 70% Bis(2-dimethylaminoethyl)ether 30% Dipropylenglycol Tensid (Niax L-3002) (Momentive, US) 0,1 bis 3,0 Gew.-Teile Polyether-modifiziertes Polysiloxan Gesamt Die Gew.-Teile basieren jeweils auf 100 Gew.-Teilen der Polyolkomponente In the following, the polyurethane foam of the present invention will be examined in detail with reference to the following Table 1. Table 1 component composition annotation First polyol 40.0 to 75.0% by weight Glycerol, OH value = 20 to 40 mg KOH / g Second polyol 10.0 to 40.0% by weight Glycerol, OH value = 20 to 50 mg KOH / g Third polyol 5.0 to 30.0% by weight Glycerol, OH value = 20 to 60 mg KOH / g Fourth polyol 3.0 to 40.0% by weight Glycerine, OH value = 10 to 30 mg KOH / g solid 30 to 50% First chain extender 1.0 to 10.0 parts by weight Diethanolamine, OH value = 1,500 to 2,500 mg KOH / g Second chain extender 0.1 to 1.0 parts by weight 1,4-butanediol, OH value = 500 to 1,500 mg KOH / g crosslinking agent 0.1 to 5.0 parts by weight Triethanolamine, OH value = 1,500 to 2,500 mg KOH / g Water (foaming agent) 1.0 to 5.0 parts by weight OH value = 6,000 to 7,000 mg KOH / g Curing catalyst (Dabco 33LV) (Air Products, US) 0.1 to 3.0 parts by weight 33% triethylenediamine 67% dipropylene glycol Foaming catalyst (Dabco BL-11) (Air Products, US) 0.1 to 2.0 parts by weight 70% bis (2-dimethylaminoethyl) ether 30% dipropylene glycol Surfactant (Niax L-3002) (Momentive, US) 0.1 to 3.0 parts by weight Polyether-modified polysiloxane total The parts by weight are each based on 100 parts by weight of the polyol component

(1) Polyolkomponente(1) polyol component

Zur Herstellung eines Polyurethanschaums wird die Polyolkomponente vorzugsweise zu mindestens 60 Gew.% eingesetzt, und anstelle der Verwendung eines einzelnen Polyols werden verschiedene Arten von Polyol eingesetzt, in Abhängigkeit von den Eigenschaften der Produkte und der Herstellungsbedingungen. Die Polyole können durch chemisches Verbinden eines Initiators, Propylenoxid (PO) und Ethylenoxid (EO) hergestellt werden.To prepare a polyurethane foam, the polyol component is preferably used at least 60% by weight, and instead of using a single polyol, various types of polyol are used, depending on the properties of the products and the conditions of preparation. The polyols can be prepared by chemically combining an initiator, propylene oxide (PO) and ethylene oxide (EO).

Ein Triol mit 3 Hydroxylgruppen wird hergestellt, wenn ein Initiator, wie Glycerol oder Glycerin, Trimethylolpropan, Triethanolamin, 1,2,6-Hexantriol, Phosphorsäure oder Triisopropanolamin eingesetzt wird. Hierbei wird der Hydroxylwert (OH-Wert) in Abhängigkeit vom Überkappungs-Grad von PO/EO bestimmt, und steht in Beziehung zum Molekulargewicht von chemisch gebundenem Polyol. Die erfindungsgemäße Polyolkomponente weist vorzugsweise einen OH-Wert von 10 bis 60 mg KOH/g auf.A triol with 3 hydroxyl groups is prepared when an initiator such as glycerol or glycerol, trimethylolpropane, triethanolamine, 1,2,6-hexanetriol, phosphoric acid or triisopropanolamine is used. Here, the hydroxyl value (OH value) is determined depending on the capping degree of PO / EO, and is related to the molecular weight of chemically bonded polyol. The polyol component according to the invention preferably has an OH value of 10 to 60 mg KOH / g.

Vorzugsweise schließt die erfindungsgemäße Polyolkomponente ein oder mehrere Polyolkomponenten mit OH-Werten ausgewählt aus der Gruppe bestehend aus 20 bis 40 mg KOH/g, 20 bis 50 mg KOH/g, 20 bis 60 mg KOH/g und 10 bis 30 mg KOH/g ein. Preferably, the polyol component of the invention includes one or more polyol components having OH values selected from the group consisting of 20 to 40 mg KOH / g, 20 to 50 mg KOH / g, 20 to 60 mg KOH / g and 10 to 30 mg KOH / g one.

In Bezug auf die Zusammensetzung ist ein Polyol mit einem OH-Wert von 20 bis 40 mg KOH/g (erstes Polyol) vorzugsweise zu 40 bis 75 Gew.% in Bezug auf das Gesamtgewicht der Polyolkomponente enthalten. Wenn das erste Polyol zu weniger als 40 Gew.% enthalten ist, verringert sich der Rückprall-Widerstand deutlich, und wenn das erste Polyol zu mehr als 75 Gew.% enthalten ist, tritt eine Abnahme der Härte auf.With respect to the composition, a polyol having an OH value of 20 to 40 mg KOH / g (first polyol) is preferably contained at 40 to 75% by weight with respect to the total weight of the polyol component. When the first polyol is contained less than 40% by weight, the rebound resistance significantly decreases, and when the first polyol is more than 75% by weight, a decrease in hardness occurs.

Weiterhin ist ein Polyol mit einem OH-Wert von 20 bis 50 mg KOH/g (zweites Polyol) vorzugsweise zu 10 bis 40 Gew.% in Bezug auf das Gesamtgewicht der Polyolkomponente enthalten. Wenn das zweite Polyol zu weniger als 10 Gew.% enthalten ist, steigt die Vibrationsdurchlässigkeit, und wenn das zweite Polyol zu mehr als 40 Gew.% enthalten ist, nimmt die permanente Kompressionsverformung ab.Further, a polyol having an OH value of 20 to 50 mg KOH / g (second polyol) is preferably contained at 10 to 40% by weight with respect to the total weight of the polyol component. When the second polyol is contained less than 10% by weight, the vibration permeability increases, and when the second polyol is contained more than 40% by weight, the permanent compression strain decreases.

Weiterhin ist ein Polyol mit einem OH-Wert von 20 bis 60 mg KOH/g (drittes Polyol) vorzugsweise zu 5 bis 30 Gew.% in Bezug auf das Gesamtgewicht der Polyolkomponente enthalten. Wenn das dritte Polyol zu weniger als 5 Gew.% enthalten ist, steigt die Vibrationsdurchlässigkeit, und wenn das dritte Polyol zu mehr als 30 Gew.% enthalten ist, nimmt die Elastizität und permanente Kompressionsverformung ab.Further, a polyol having an OH value of 20 to 60 mg KOH / g (third polyol) is preferably contained at 5 to 30% by weight with respect to the total weight of the polyol component. When the third polyol is contained less than 5% by weight, the vibration permeability increases, and when the third polyol is contained more than 30% by weight, the elasticity and permanent compression strain decrease.

Weiterhin ist ein Polyol mit einem OH-Wert von 10 bis 30 mg KOH/g (viertes Polyol) vorzugsweise zu 3 bis 40 Gew.% enthalten. Wenn das vierte Polyol zu weniger als 3 Gew.% enthalten ist, so ist die Härte zu niedrig, und wenn das vierte Polyol zu mehr als 40 Gew.% enthalten ist, so ist die Härte hoch und das Komfort-Niveau nimmt ab.Further, a polyol having an OH value of 10 to 30 mg KOH / g (fourth polyol) is preferably contained 3 to 40% by weight. When the fourth polyol is contained less than 3% by weight, the hardness is too low, and when the fourth polyol is more than 40% by weight, the hardness is high and the comfort level decreases.

Vorzugsweise hat die Polyolkomponente ein Molekulargewicht von ungefähr 3.000 bis 7.000.Preferably, the polyol component has a molecular weight of about 3,000 to 7,000.

(2) Isocyanatkomponente(2) isocyanate component

Isocyanate, die allgemein in der Herstellung von Polyurethanschaum verwendet werden, schließen Methylendiphenyldiisocyanat (MDI), Toluoldiisocyanat (TDI) oder eine Kombination davon ein. Die vorliegende Erfindung setzt modifizierte Methylendiphenyldiisocyanate (MDI) ein, um die Vibrationsabsorption zu verbessern. Die erfindungsgemäße Isocyanatkomponente schließt vorzugsweise, ohne Toluoldiisocyanat einzusetzen, monomeres Methylendiphenyldiisocyanat (MMDI) zu 4 bis 70 Gew.%; Carbodiimidmethylendiphenyldiisocyanat (CMDI) zu 5 bis 70 Gew.% und polymeres Methylendiphenyldiisocyanat (PMDI) zu 10 bis 80 Gew.% in Bezug auf das Gesamtgewicht der Isocyanatkomponente ein.Isocyanates commonly used in the production of polyurethane foam include methylene diphenyl diisocyanate (MDI), toluene diisocyanate (TDI), or a combination thereof. The present invention employs modified methylenediphenyl diisocyanates (MDI) to improve vibration absorption. The isocyanate component according to the invention preferably, without using toluene diisocyanate, monomeric methylene diphenyl diisocyanate (MMDI) to 4 to 70 wt.%; Carbodiimide methylene diphenyl diisocyanate (CMDI) at 5 to 70 weight percent; and polymeric methylene diphenyl diisocyanate (PMDI) at 10 to 80 weight percent based on the total weight of the isocyanate component.

Speziell sind das monomere Methylendiphenyldiisocyanat und das Carbodiimidmethylendiphenyldiisocyanat vorzugweise zu 4 bis 70 Gew.% bzw. 5 bis 70 Gew.% enthalten. Wenn die Menge weniger als die empfohlene Menge ist, so werden in übermäßigem Ausmaß geschlossene Zellen gebildet, was zu einer Verringerung der Produktivität führt, und wenn die Menge größer ist als die empfohlene Menge, so werden in übermäßigem Ausmaß offene Zellen gebildet und es wird kein Schaum produziert, was zu einem Anstieg der Defektrate führt.Specifically, the monomeric methylene diphenyl diisocyanate and the carbodiimide methylene diphenyl diisocyanate are preferably contained at 4 to 70% by weight and 5 to 70% by weight, respectively. If the amount is less than the recommended amount, excessively closed cells are formed, resulting in a decrease in productivity, and if the amount is larger than the recommended amount, excessively open cells are formed and there is no Foam produced, which leads to an increase in the defect rate.

Das polymere Methylendiphenyldiisocyanat (PMDI) ist vorzugsweise zu 10 bis 80 Gew.% enthalten. Wenn es zu weniger als 10 Gew.% enthalten ist, nimmt die Zugfestigkeit und Reißfestigkeit rapide ab, und es wenn es zu mehr als 80 Gew.% enthalten ist, nimmt die Härte rapide zu.The polymeric methylene diphenyl diisocyanate (PMDI) is preferably contained at 10 to 80% by weight. If it is less than 10% by weight, the tensile strength and tear resistance decrease rapidly, and if it is more than 80% by weight, the hardness increases rapidly.

Mit anderen Worten nimmt die Kraft, die den Körper des Fahrers stützt, dadurch zu, dass kein TDI, das im allgemeinen für Sitzschaum verwendet wird, enthalten ist. Dies ist durch die Tatsache begründet, dass MDI eine im Verhältnis größere Molekularstruktur als TDI aufweist und die Haltekraft des Schaums erhöht, wodurch die Deflektion des Schaums vom langen Fahren verhindert wird.In other words, the force supporting the driver's body is increased by not including TDI, which is generally used for seat foam. This is due to the fact that MDI has a larger molecular structure than TDI and increases the holding power of the foam, thereby preventing the deflection of the foam from long running.

Weiterhin schließt die erfindungsgemäße Harzvormischung vorzugsweise einen Härtungskatalysator, einen Schäumkatalysator, ein Vernetzungsmittel, ein Kettenerweiterungsmittel und ein Tensid ein.Further, the resin premix of the present invention preferably includes a curing catalyst, a foaming catalyst, a crosslinking agent, a chain extender, and a surfactant.

(3) Kettenerweiterungsmittel und Vernetzungsmittel(3) chain extenders and crosslinkers

Das Kettenerweiterungsmittel und das Vernetzungsmittel sind reaktive Einzelmoleküle, die für die Festigung der intermolekularen Bindung verwendet werden. Das Kettenerweiterungsmittel spielt die Rolle der Erweiterung der Hauptkette, und setzt normalerweise difunktionale Alkohole und/oder Amine ein, und das Vernetzungsmittel spielt die Rolle, die Kette zu einer Netzstruktur oder verzweigten Struktur zu formen, und setzt normalerweise Alkohole und/oder Amine mit drei oder mehr Funktionen ein.The chain extender and crosslinking agent are single reactive molecules used to strengthen intermolecular bonding. The chain extender plays the role of extension of the backbone, and usually employs difunctional alcohols and / or amines, and that Crosslinking agent plays the role of forming the chain into a network or branched structure, and normally employs alcohols and / or amines having three or more functions.

Das Kettenerweiterungsmittel und das Vernetzungsmittel erhöht die intramolekulare Vernetzungskraft und spielt daher eine wichtige Rolle beim Verbessern der allgemeinen physikalischen Eigenschaften, wie Zug- und Reißeigenschaft, und kann gleichzeitig die Produkteigenschaften unter Bedingungen hoher Temperatur und hoher Feuchtigkeit aufrechterhalten, indem die Hydrolyseresistenz erhöht wird.The chain extender and crosslinking agent enhances the intramolecular crosslinking force and therefore plays an important role in improving the general physical properties such as tensile and tear property, and at the same time, can maintain the product properties under high temperature and high humidity conditions by increasing the resistance to hydrolysis.

Allerdings nimmt die Produktivität eher ab, wenn die Eigenschaften nur des Endprodukts erfüllt werden, aufgrund von Problemen wie geschlossenen Zellen und Flusseigenschaft.However, productivity tends to decrease if only end-product performance is achieved due to problems such as closed cells and flow characteristics.

Dementsprechend ist in Bezug auf 100 Gew.-Teile der Polyolkomponente das Kettenerweiterungsmittel mit einem OH-Wert von 1.500 bis 2.500 mg KOH/g (erstes Kettenerweiterungsmittel) vorzugsweise zu 1 bis 10 Gew.-Teilen, und das Kettenerweiterungsmittel mit einem OH-Wert von 500 bis 1.500 mg KOH/g (zweites Kettenerweiterungsmittel) zu 0,1 bis 1 Gew.-Teilen enthalten.Accordingly, with respect to 100 parts by weight of the polyol component, the chain extender having an OH value of 1,500 to 2,500 mg KOH / g (first chain extender) is preferably 1 to 10 parts by weight, and the chain extender having an OH value of 500 to 1500 mg KOH / g (second chain extender) to 0.1 to 1 parts by weight.

Wenn das erste Kettenerweiterungsmittel zu weniger als 1 Gew.-Teil enthalten ist, verschlechtern die Zug- und Reißeigenschaften, und wenn es zu mehr als 10 Gew.-Teilen enthalten ist, werden übermäßig geschlossene Zellen gebildet, was zu einem schnellen Abfall der Produktivität führt. Wenn das zweite Kettenerweiterungsmittel zu weniger als 0,1 Gew.-Teilen enthalten ist, sind die Auswirkungen der Zugabe unbedeutend, und wenn es zu mehr als 1 Gew.-Teil enthalten ist, nimmt die Fließeigenschaft ab.When the first chain extender is contained less than 1 part by weight, the tensile and tear properties deteriorate, and when it is more than 10 parts by weight, excessively closed cells are formed, resulting in a rapid decline in productivity , When the second chain extender is contained to less than 0.1 part by weight, the effects of the addition are insignificant, and when it is more than 1 part by weight, the flow property decreases.

Weiterhin ist das Vernetzungsmittel vorzugsweise zu 0,1 bis 5 Gew.-Teilen enthalten. Wenn das Vernetzungsmittel zu weniger als 0,1 Gew.-Teilen enthalten ist, so sind die Auswirkungen der Zugabe unbedeutend, und wenn es zu mehr als 5 Gew.-Teilen enthalten ist, nimmt die Fließeigenschaft ab, was zu einem Anstieg der Defektraten führt.Further, the crosslinking agent is preferably contained at 0.1 to 5 parts by weight. When the crosslinking agent is contained less than 0.1 part by weight, the effects of the addition are insignificant, and when it is more than 5 parts by weight, the flow property decreases, resulting in an increase in the defect rates ,

Beispiele für Kettenerweiterungsmittel schließen Diethanolamin und/oder 1,4-Butandiol ein.Examples of chain extenders include diethanolamine and / or 1,4-butanediol.

Ein Beispiel für ein Vernetzungsmittel ist Triethanolamin.An example of a crosslinking agent is triethanolamine.

(4) Härtungskatalysator und Schäumkatalysator(4) Curing catalyst and foaming catalyst

Der Härtungskatalysator und der Schäumkatalysator spielen eine Rolle bei der Verringerung der Aktivierungsenergie für die Reaktion zwischen dem Isocyanat und dem Polyol. Die Produktion von stabilem Polyurethanschaumerzeugnissen kann in Abhängigkeit vom Grad des Einsatzes dieser beiden Katalysatoren durchgeführt werden.The curing catalyst and the foaming catalyst play a role in reducing the activation energy for the reaction between the isocyanate and the polyol. The production of stable polyurethane foam products can be carried out depending on the degree of use of these two catalysts.

Ohne darauf beschränkt zu sein, können repräsentative Beispiele des Härtungskatalysators Triethylendiamin, Dimethylpiperidin und ähnliches einschließen, und repräsentative Beispiele des Schäumkatalysators können Triethylamin, N,N'-Dimethylcyclohexylamin und ähnliches einschließen. Bei den meisten Herstellungsbedingungen ist die Zeit für das Entfernen aus der Form vorhanden, und um die Herstellung von Erzeugnissen innerhalb einer solchen beschränkten Zeitspanne fertigzustellen, wird der Härtungskatalysator vorzugsweise zu maximal 3 Gew.-Teilen und der Schäumkatalysator zu maximal 2 Gew.-Teilen eingesetzt.Although not limited thereto, representative examples of the curing catalyst may include triethylenediamine, dimethylpiperidine, and the like, and representative examples of the foaming catalyst may include triethylamine, N, N'-dimethylcyclohexylamine, and the like. In most production conditions, the time for removal from the mold is present, and to complete the production of products within such a limited period of time, the curing catalyst is preferably used at most 3 parts by weight and the foaming catalyst at a maximum of 2 parts by weight ,

In Bezug auf die Zusammensetzung ist der Härtungskatalysator vorzugsweise zu 0,1 bis 3 Gew.-Teilen enthalten, und der Schäumkatalysator zu 0,1 bis 2 Gew.-Teilen enthalten, in Bezug auf 100 Gew.-Teile der Polyolkomponente. Wenn die Menge geringer ist als die empfohlene Menge, nimmt die Produktivität aufgrund der Reduktion der Härtbarkeit ab, und wenn die Menge größer als die empfohlene Menge ist, können aufgrund der Abnahme der Fließeigenschaften Porendefekte auftreten.With respect to the composition, the curing catalyst is preferably contained at 0.1 to 3 parts by weight and the foaming catalyst at 0.1 to 2 parts by weight with respect to 100 parts by weight of the polyol component. If the amount is less than the recommended amount, the productivity decreases due to the reduction in the hardenability, and if the amount is larger than the recommended amount, pore defects may occur due to the decrease in the flow properties.

Der Härtungskatalysator kann beispielsweise Triethylendiamin und/oder Dipropylenglycol sein.The curing catalyst may be, for example, triethylenediamine and / or dipropylene glycol.

Bis(2-dimethylaminoethyl)ether und/oder Dipropylenglycol können beispielsweise als Schäumkatalysator eingesetzt werden.Bis (2-dimethylaminoethyl) ether and / or dipropylene glycol can be used, for example, as a foaming catalyst.

(5) Schäummittel(5) foaming agent

Das Schäummittel wird grob in physikalische Schäummittel und chemische Schäummittel eingeteilt, und im Fall der vorliegenden Erfindung ist der Einsatz eines chemischen Schäummittels bevorzugt. Die Reaktionsrate, Härtbarkeit und freie Anstiegsdichte werden in Abhängigkeit von der Menge des eingesetzten Schäummittels bestimmt. Daher wird die einzusetzende Menge in Abhängigkeit von den Herstellungsbedingungen bestimmt, innerhalb des Bereichs von maximal 5 Gew.-Teilen. Insbesondere wird Wasser bevorzugt als chemisches Schäummittel für Fahrzeugsitze eingesetzt.The foaming agent is roughly classified into physical foaming agents and chemical foaming agents, and in the case of the present invention, the use of a chemical foaming agent is preferred. The Reaction rate, hardenability and free growth density are determined depending on the amount of the foaming agent used. Therefore, the amount to be used is determined depending on the production conditions, within the range of at most 5 parts by weight. In particular, water is preferably used as a chemical foaming agent for vehicle seats.

Bezogen auf die Zusammensetzung ist das Schäummittel vorzugsweise zu 1 bis 5 Gew.-Teilen in Bezug auf 100 Gew.-Teilen der Polyolkomponente enthalten. Wenn das Schäummittel zu weniger als 1 Gew.-Teil enthalten ist, so ist es aufgrund des niedrigen Schäumverhältnisses schwierig, die für Sitze erforderliche Dichte zu erhalten, und wenn es zu mehr als 5 Gew.-Teilen enthalten ist, verschlechtern sich die physikalischen Eigenschaften aufgrund des übermäßigen Schäumens.Based on the composition, the foaming agent is preferably contained at 1 to 5 parts by weight with respect to 100 parts by weight of the polyol component. If the foaming agent is contained to less than 1 part by weight, it is difficult to obtain the density required for seats due to the low foaming ratio, and if it is more than 5 parts by weight, the physical properties deteriorate due to excessive foaming.

(6) Tensid(6) surfactant

Im allgemeinen werden Tenside aus der Siliciumreihe, wie Polyether-modifizierte Polysiloxane, vorzugsweise als das Tensid eingesetzt. Das Tensid nimmt an der Emulsionswirkung teil, die bei der Umsetzung von MDI und Polyol hilft, bildet Mikroblasen durch Verringerung der Oberflächenspannung und spielt auch eine Rolle beim Stabilisieren dieser Mikroblasen.In general, silicon-series surfactants such as polyether-modified polysiloxanes are preferably used as the surfactant. The surfactant participates in the emulsion action which aids in the reaction of MDI and polyol, forms microbubbles by reducing the surface tension, and also plays a role in stabilizing these microbubbles.

In Bezug auf die Zusammensetzung ist das Tensid vorzugsweise zu 0,1 bis 3 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten. Wenn das Tensid zu weniger als 0,1 Gew.-Teile enthalten ist, wird der Polyurethanschaum nicht gebildet, und wenn es zu mehr als 3 Gew.-Teilen enthalten ist, nimmt die Produktivität aufgrund der übermäßigen Bildung von geschlossenen Zellen ab.With respect to the composition, the surfactant is preferably contained at 0.1 to 3 parts by weight with respect to 100 parts by weight of the polyol component. When the surfactant is contained less than 0.1 part by weight, the polyurethane foam is not formed, and when it is more than 3 parts by weight, the productivity decreases due to the excessive formation of closed cells.

Funktionale Polyurethanschäume mit einer Zusammensetzung wie oben beschrieben können für Fahrzeugsitze und ähnliches unter Verwendung allgemeiner im Stand der Technik bekannter Verfahren eingesetzt werden, und es können Fahrzeugsitze hergestellt werden, die die Vibrationsdurchlässigkeit minimieren und den Komfort verbessern.Functional polyurethane foams having a composition as described above can be used for vehicle seats and the like using general methods known in the art, and vehicle seats can be manufactured which minimize vibration permeability and improve comfort.

Im folgenden wird die Erfindung in weiteren Details unter Verwendung von Beispielen beschrieben. Allerdings dienen diese Beispiele nur illustrativen Zwecken, und es ist für den Fachmann ersichtlich, dass der Bereich der vorliegenden Erfindung nicht als durch diese Beispiele beschränkt interpretiert werden soll. Tabelle 2 Vergleichsbeispiele Beispiele 1 2 3 4 1 2 erstes Polyol 80 Gew.% 60 Gew.% 60 Gew.% 60 Gew.% 60 Gew.% 60 Gew.% zweites Polyol - - 20 Gew.% 20 Gew.% 20 Gew.% 20 Gew.% drittes Polyol - 20 Gew.% - - - - viertes Polyol 20 Gew.% 20 Gew.% 20 Gew.% 20 Gew.% 20 Gew.% 20 Gew.% MMDI 70 Gew.% 70 Gew.% 80 Gew.% 15 Gew.% 20 Gew.% 30 Gew.% CMDI - - 15 Gew.% 80 Gew.% 40 Gew.% 30 Gew.% PMDI - - 5 Gew.% 5 Gew.% 40 Gew.% 40 Gew.% TDI-Derivate 30 Gew.% 30 Gew.% - - - - In the following the invention will be described in further details using examples. However, these examples are for illustrative purposes only and it will be apparent to those skilled in the art that the scope of the present invention should not be construed as limited by these examples. Table 2 Comparative Examples Examples 1 2 3 4 1 2 first polyol 80% by weight 60% by weight 60% by weight 60% by weight 60% by weight 60% by weight second polyol - - 20% by weight 20% by weight 20% by weight 20% by weight third polyol - 20% by weight - - - - fourth polyol 20% by weight 20% by weight 20% by weight 20% by weight 20% by weight 20% by weight MMDI 70% by weight 70% by weight 80% by weight 15% by weight 20% by weight 30% by weight CMDI - - 15% by weight 80% by weight 40% by weight 30% by weight PMDI - - 5% by weight 5% by weight 40% by weight 40% by weight TDI derivatives 30% by weight 30% by weight - - - -

In Tabelle 2 sind die Mengen vom ersten Polyol bis zum vierten Polyol auf Basis des Gesamtgewicht der Polyolkomponente in Gew.% dargestellt, und die Mengen des MMDI, des CMDI, des PMDI und des TDI-Derivats sind in Gew.% auf Basis des Gesamtgesichts der Isocyanatkomponente dargestellt. Die Isocyanatkomponente wurde zu 60 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente gemischt. Tabelle 3 Vergleichsbeispiele Beispiele 1 2 3 4 1 2 Härte (kgf/m3) 27 30 31 29 27 30 Hystereseverlust (%) 29 34 26 23 19 21 Zugfestigkeit (kgf/cm2) 2,1 1,85 2,3 1,9 1,94 2,1 Dehnung (%) 120 122 90 105 116 120 Rißfestigkeit (kgf/cm2) 0,94 0,72 0,85 0,65 0,72 0,79 permanente Kompressionsverformung (%) 3,2 12,5 5,7 8,5 7,7 9,5 Vibrationsdurchlässigkeit 6,5 5,7 5,5 4,5 3,2 3,9 Spannungsrelaxation (%) 25 23 22 22 21 20 In Table 2, the amounts of the first polyol to the fourth polyol based on the total weight of the polyol component are shown in weight percent, and the amounts of the MMDI, the CMDI, the PMDI and the TDI derivative are in% by weight based on the total face the isocyanate component. The isocyanate component was mixed to 60 parts by weight with respect to 100 parts by weight of the polyol component. Table 3 Comparative Examples Examples 1 2 3 4 1 2 Hardness (kgf / m 3 ) 27 30 31 29 27 30 Hysteresis loss (%) 29 34 26 23 19 21 Tensile strength (kgf / cm 2 ) 2.1 1.85 2.3 1.9 1.94 2.1 Strain (%) 120 122 90 105 116 120 Crack resistance (kgf / cm 2 ) 0.94 0.72 0.85 0.65 0.72 0.79 permanent compression deformation (%) 3.2 12.5 5.7 8.5 7.7 9.5 Vibration transmissibility 6.5 5.7 5.5 4.5 3.2 3.9 Stress relaxation (%) 25 23 22 22 21 20

Tabelle 3 ist eine Tabelle, in der die mechanischen Eigenschaften der Polyurethanschäume, die in der Zusammensetzung gemäß Tabelle 2 hergestellt sind, gemessen werden.Table 3 is a table in which the mechanical properties of the polyurethane foams prepared in the composition according to Table 2 are measured.

Die Vibrationsdurchlässigkeit ist ein Wert aller Vibrationen, die während des Fahrens auf die Sitze übertragen werden, dividiert durch die vom Fahrer wahrgenommene Vibration, und wenn der Wert abnimmt, verbessert sich der dynamische Komfort, da der Sitz viel Vibration absorbiert. Für die Vibrationsdurchlässigkeit wurden die Vibrationen, die auf der Straße beim Fahren des Fahrzeugs erzeugt werden, künstlich durch einen Vibrationsgenerator erzeugt und auf den Urethanschaum übertragen, und die Vibrationsabsorption des Urethanschaums wurde gemessen.Vibration transmittance is a value of all vibrations transmitted to the seats during travel divided by driver perceived vibration, and as the value decreases, dynamic comfort improves as the seat absorbs much vibration. For the vibration permeability, the vibrations generated on the road while driving the vehicle were artificially generated by a vibration generator and transmitted to the urethane foam, and the vibration absorption of the urethane foam was measured.

Spannungsrelaxation ist ein Phänomen, in dem Spannung innerhalb eines Objekts mit der Zeit reduziert wird, wenn eine instantan bewirkte Verformung konstant aufrechterhalten wird, und wenn der Spannungsrelaxationswert kleiner wird, kann die Haltkraft des Sitzschaums zum Stützen des Körpers des Fahrers aufrechterhalten werden, selbst wenn der Fahrer für eine lange Zeitspanne fährt.Stress relaxation is a phenomenon in which stress within an object is reduced with time when an instantaneous deformation is constantly maintained, and when the stress relaxation value becomes smaller, the holding force of the seat foam for supporting the body of the driver can be maintained even if Driver for a long period of time drives.

Wie in der Tabelle gezeigt, war die Vibrationsdurchlässigkeit niedrig, wenn nur MDI eingesetzt wurde, im Vergleich zum Einsatz eines bestehenden TDI-Derivats, und insbesondere wenn die Zusammensetzung die erfindungsgemäße Zusammensetzung erfüllte, zeigte die Vibrationsdurchlässigkeit den niedrigsten Wert von 3,2 bis 3,9, und die Hystereseverlustwerte waren auch allgemein niedrig.As shown in the table, the vibration transmittance was low when only MDI was used compared to the use of an existing TDI derivative, and especially when the composition satisfied the composition of the present invention, the vibration transmittance showed the lowest value of 3.2 to 3, 9, and the hysteresis loss values were also generally low.

1 zeigt einen Zeit-Spannungs-Graphen eines Sitzschaums, der unter Verwendung von TDI hergestellt wurde, und eines Sitzschaums, der erfindungsgemäß unter Verwendung von MDI hergestellt wurde, und wie durch das Diagramm gezeigt, ist ersichtlich, dass der unter Verwendung von MDI hergestellte Sitzschaum (200) eine höhere Haltekraft zum Stützen des Körpers des Fahrers als der unter Verwendung von TDI hergestellte Sitzschaum (100) aufweist, da der unter Verwendung von MDI hergestellte Sitzschaum eine relativ geringere Spannungsreduktion aufweist, selbst wenn der Fahrer für eine lange Zeitspanne fährt. Dies ist durch die Tatsache begründet, dass MDI eine im Verhältnis höhere Molekularstruktur als TDI aufweist. 1 1 shows a time-stress graph of a seat foam made using TDI and a seat foam made in accordance with the invention using MDI and as shown by the diagram, it can be seen that the seat foam (FIG. 200) has a higher holding force for supporting the driver's body than the seat foam (100) made using TDI, since the seat foam made using MDI has a relatively lower stress reduction even when the driver is driving for a long period of time. This is due to the fact that MDI has a relatively higher molecular structure than TDI.

Vorausgehend wurde die vorliegende Erfindung in Bezug auf spezielle erfindungsgemäße Ausführungsformen beschrieben, allerdings dient dies nur illustrativen Zwecken, und die vorliegende Erfindung ist nicht darauf beschränkt. Der Fachmann, an den sich die vorliegende Erfindung richtet, kann die beschriebenen Ausführungsformen modifizieren oder ändern, ohne vom Bereich der vorliegenden Erfindung abzuweichen, und verschiedene Überarbeitungen und Modifikationen können innerhalb der technologischen Ideen und des gleichen Bereichs der Ansprüche der vorliegenden Erfindung, die unten beschrieben sind, gemacht werden.Previously, the present invention has been described in terms of particular embodiments of the invention, however, this is for illustrative purposes only, and the present invention is not limited thereto. Those skilled in the art to which the present invention pertains may modify or modify the described embodiments without departing from the scope of the present invention, and various revisions and modifications may be made within the technological ideas and the same scope of the claims of the present invention described below are to be made.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • KR 10-0883514 [0004] KR 10-0883514 [0004]

Claims (13)

Funktionaler Polyurethanschaum, der ein Umsetzungsprodukt einer Harzvormischung und einer Isocyanatkomponente umfasst, worin die Harzvormischung eine Polyolkomponente und ein Schäummittel einschließt; und worin die Isocyanatkomponente monomeres Methylendiphenyldiisocyanat (MMDI) zu 4 bis 70 Gew.%, Carbodiimidmethylendiphenyldiisocyanat (CMDI) zu 5 bis 70 Gew.% und polymeres Methylendiphenyldiisocyanat (PMDI) zu 10 bis 80 Gew.% in Bezug auf das Gesamtgewicht der Isocyanatkomponente einschließt.Functional polyurethane foam comprising a reaction product of a resin premix and an isocyanate component, wherein the resin premix includes a polyol component and a foaming agent; and wherein the isocyanate component includes 4 to 70 weight percent methylene diphenyl diisocyanate (MMDI), 5 to 70 weight percent carbodiimide methylene diphenyl diisocyanate (CMDI) and 10 to 80 weight percent polymeric methylene diphenyl diisocyanate (PMDI) relative to the total weight of the isocyanate component. Funktionaler Polyurethanschaum gemäß Anspruch 1, worin die Polyolkomponente einen Hydroxylwert (OH-Wert) von 10 bis 60 mg KOH/g aufweist.A functional polyurethane foam according to claim 1, wherein the polyol component has a hydroxyl value (OH value) of 10 to 60 mg KOH / g. Funktionaler Polyurethanschaum gemäß Anspruch 2, worin die Polyolkomponente ein oder mehrere Polyolkomponenten ist, mit einem OH-Wert ausgewählt aus der Gruppe bestehend aus 20 bis 40 mg KOH/g, 20 bis 50 mg KOH/g, 20 bis 60 mg KOH/g und 10 bis 30 mg KOH/g.A functional polyurethane foam according to claim 2, wherein the polyol component is one or more polyol components having an OH value selected from the group consisting of 20 to 40 mg KOH / g, 20 to 50 mg KOH / g, 20 to 60 mg KOH / g and 10 to 30 mg KOH / g. Funktionaler Polyurethanschaum gemäß Anspruch 3, worin die Polyolkomponente ein Polyol mit einem OH-Wert von 20 bis 40 mg KOH/g zu 40 bis 75 Gew.%; ein Polyol mit einem OH-Wert von 20 bis 50 mg KOH/g zu 10 bis 40 Gew.%; und ein Polyol mit einem OH-Wert von 10 bis 30 mg KOH/g zu 3 bis 40 Gew.% in Bezug auf das Gesamtgewicht der Polyolkomponente einschließt.A functional polyurethane foam according to claim 3, wherein the polyol component is a polyol having an OH value of from 20 to 40 mg KOH / g at 40 to 75% by weight; a polyol having an OH value of 20 to 50 mg KOH / g at 10 to 40% by weight; and a polyol having an OH value of 10 to 30 mg KOH / g at 3 to 40 wt% with respect to the total weight of the polyol component. Funktionaler Polyurethanschaum gemäß irgendeinem der Ansprüche 1 bis 4, worin die Harzvormischung weiterhin einen Härtungskatalysator, einen Schäumkatalysator, ein Vernetzungsmittel, ein Kettenerweiterungsmittel und ein Tensid einschließt.A functional polyurethane foam according to any one of claims 1 to 4, wherein the resin premix further includes a curing catalyst, a foaming catalyst, a crosslinking agent, a chain extender and a surfactant. Funktionaler Polyurethanschaum gemäß irgendeinem der Ansprüche 1 bis 5, worin die Isocyanatkomponente zu 40 bis 70 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to any one of claims 1 to 5, wherein the isocyanate component is contained at 40 to 70 parts by weight with respect to 100 parts by weight of the polyol component. Funktionaler Polyurethanschaum gemäß Anspruch 5, worin der Härtungskatalysator zu 0,1 bis 3 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to claim 5, wherein the curing catalyst is contained at 0.1 to 3 parts by weight with respect to 100 parts by weight of the polyol component. Funktionaler Polyurethanschaum gemäß Anspruch 5, worin der Schäumkatalysator zu 0,1 bis 2 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to claim 5, wherein the foaming catalyst is contained at 0.1 to 2 parts by weight with respect to 100 parts by weight of the polyol component. Funktionaler Polyurethanschaum gemäß irgendeinem der Ansprüche 1 bis 8, worin das Schäummittel zu 1 bis 5 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to any one of claims 1 to 8, wherein the foaming agent is contained at 1 to 5 parts by weight with respect to 100 parts by weight of the polyol component. Funktionaler Polyurethanschaum gemäß Anspruch 5, worin das Vernetzungsmittel zu 0,1 bis 5 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to claim 5, wherein the crosslinking agent is contained at 0.1 to 5 parts by weight with respect to 100 parts by weight of the polyol component. Funktionaler Polyurethanschaum gemäß Anspruch 5, worin das Kettenerweiterungsmittel mit einem Kettenerweiterungsmittel mit einem OH-Wert von 1.500 bis 2.500 mg KOH/g zu 1 bis 10 Gew.-Teilen und einem Kettenerweiterungsmittel mit einem OH-Wert von 500 bis 1.500 mg KOH/g zu 0,1 bis 1 Gew.-Teile in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to claim 5, wherein the chain extender is added with a chain extender having an OH value of 1,500 to 2,500 mg KOH / g to 1 to 10 parts by weight and a chain extender having an OH value of 500 to 1,500 mg KOH / g 0.1 to 1 part by weight with respect to 100 parts by weight of the polyol component is contained. Funktionaler Polyurethanschaum gemäß Anspruch 5, worin das Tensid zu 0,1 bis 3 Gew.-Teilen in Bezug auf 100 Gew.-Teile der Polyolkomponente enthalten ist.A functional polyurethane foam according to claim 5, wherein the surfactant is contained at 0.1 to 3 parts by weight with respect to 100 parts by weight of the polyol component. Fahrzeugsitz, der den funktionalen Polyurethanschaum gemäß irgendeinem der Ansprüche 1 bis 12 einschließt.A vehicle seat including the functional polyurethane foam according to any one of claims 1 to 12.
DE102014225156.7A 2014-12-08 2014-12-08 Functional polyurethane foam Ceased DE102014225156A1 (en)