DE102014107312A1 - duct tape - Google Patents

duct tape Download PDF

Info

Publication number
DE102014107312A1
DE102014107312A1 DE102014107312.6A DE102014107312A DE102014107312A1 DE 102014107312 A1 DE102014107312 A1 DE 102014107312A1 DE 102014107312 A DE102014107312 A DE 102014107312A DE 102014107312 A1 DE102014107312 A1 DE 102014107312A1
Authority
DE
Germany
Prior art keywords
threads
adhesive tape
tape according
dtex
warp
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102014107312.6A
Other languages
German (de)
Inventor
Christoph Lodde
Gülay Wittig
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Coroplast Fritz Mueller GmbH and Co KG
Original Assignee
Coroplast Fritz Mueller GmbH and Co KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Coroplast Fritz Mueller GmbH and Co KG filed Critical Coroplast Fritz Mueller GmbH and Co KG
Priority to DE102014107312.6A priority Critical patent/DE102014107312A1/en
Publication of DE102014107312A1 publication Critical patent/DE102014107312A1/en
Withdrawn legal-status Critical Current

Abstract

Die vorliegende Erfindung betrifft ein Klebeband, insbesondere Kabelwickelband, umfassend einen bandförmigen Träger (1) aus einem textilen Gewebe aus Kettfäden (2) und Schussfäden (3). Die Kettfäden (2) sind aus einem Kunststoffmaterial hergestellt und als Filamentgarn ausgebildet. Auf den Träger (1) ist eine Klebebeschichtung (4) aufgebracht. Die Schussfäden (3) sind jeweils aus einem Stapelfasergarn aus Kunststoffmaterial gebildet.The present invention relates to an adhesive tape, in particular cable winding tape, comprising a band-shaped carrier (1) made of a textile fabric of warp threads (2) and weft threads (3). The warp threads (2) are made of a plastic material and formed as filament yarn. On the support (1) an adhesive coating (4) is applied. The weft threads (3) are each formed from a staple fiber yarn of plastic material.

Description

Die vorliegende Erfindung betrifft ein Klebeband, insbesondere ein Kabelwickelband, umfassend einen bandförmigen Träger aus einem textilen Gewebe aus Kettfäden und Schussfäden, wobei die Kettfäden aus einem PET-Kunststoffmaterial hergestellt und als Filamentgarn ausgebildet sind, sowie eine auf dem Träger aufgebrachte Klebebeschichtung.The present invention relates to an adhesive tape, in particular a cable winding tape, comprising a band-shaped carrier made of a textile fabric of warp threads and weft threads, wherein the warp threads are made of a PET plastic material and formed as filament yarn, and an adhesive coating applied to the carrier.

Ein derartiges Klebeband ist beispielsweise aus der EP 199 03 93 A1 bekannt. Hierbei ist ein auf die Breite bezogener Titer der Kettfäden kleiner als ein auf die Länge bezogener Titer der Schussfäden.Such an adhesive tape is for example from the EP 199 03 93 A1 known. In this case, a width-related titer of the warp threads is smaller than a length-related titer of the weft threads.

Weiterhin sind Kabelwickelbänder bekannt, wobei das Gewebe aus aus Zellwolle bestehenden Fäden gebildet wird. Derartige Klebebänder besitzen eine beschränkte Temperaturbeständigkeit, unterliegen einem starken Schrumpf, sind verrottbar und neigen zu einer starken Feuchtigkeitsaufnahme. Zudem sind auf Grund des verwendeten Materials die Herstellungskosten relativ hoch.Furthermore, cable winding tapes are known, wherein the fabric is formed of fibers consisting of staple fiber. Such adhesive tapes have a limited temperature resistance, are subject to a strong shrinkage, are rotting and tend to a strong moisture absorption. In addition, the production costs are relatively high due to the material used.

Klebebänder, die aus Kett- und Schussfäden bestehen, die ausschließlich aus PET-Kunststoffmaterial bestehen, besitzen eine unerwünschte Steifigkeit und sind je nach Konstruktion nicht quer einreißbar.Adhesive tapes, which consist of warp and weft threads, which consist exclusively of PET plastic material, have an undesirable stiffness and are not transversely tear-able depending on the construction.

Weiterhin ist aus der EP 107 45 95 A1 ein Klebeband bekannt, bei dem der aus einem Gewebe gebildete Träger, wobei die Kett- und Schussfäden aus einem PET-Kunststoff bestehen, derart aufgebaut ist, dass dünne Kettfäden und dicke Schussfäden verwendet werden. Hierbei besitzen die Kettfäden einen auf die auf die Breite bezogenen Titer von maximal 2.500 dtex pro cm, und die Schussfäden besitzen einen auf die Breite bezogenen Titer von 3.000 bis 4.500 dtex pro cm. Die Dicke der Kettfäden beträgt insbesondere 40 bis 60 dtex und die Dicke der Schussfäden 150 bis 250 dtex.Furthermore, from the EP 107 45 95 A1 an adhesive tape is known in which the carrier formed from a fabric, wherein the warp and weft threads are made of a PET plastic, is constructed such that thin warp threads and thick weft threads are used. In this case, the warp threads have a maximum titre of 2,500 dtex per cm, referred to the width, and the weft threads have a width-related titre of 3,000 to 4,500 dtex per cm. The thickness of the warp threads is in particular 40 to 60 dtex and the thickness of the weft threads 150 to 250 dtex.

Der vorliegenden Erfindung liegt die Aufgabe zu Grunde, ein Klebeband zu schaffen, das hinsichtlich seiner Haptik einem Klebeband mit einem Zellwolle-Träger, insbesondere hinsichtlich der Weichheit und der Schmiegsamkeit entspricht und auch eine Quereinreißbarkeit von Hand besitzt. Gleichzeitig soll es aber in Bezug auf die Temperaturstabilität, die Flexibilität und die übrigen Eigenschaften demjenigen Klebeband angepasst sein, das einen Kunststoff-Gewebeträger, z. B. PET-Gewebeträger besitzt.The present invention is based on the object to provide an adhesive tape which corresponds in terms of its feel an adhesive tape with a cellulose wool carrier, in particular with regard to softness and flexibility and also has a Quererissißbarkeit by hand. At the same time, however, it should be adjusted with respect to the temperature stability, the flexibility and the other properties of that adhesive tape, a plastic fabric carrier, for. B. PET tissue carrier has.

Erfindungsgemäß wird dies dadurch erreicht, dass ausgehend von dem eingangs beschriebenen Klebeband die Schussfäden des textilen Gewebes, das den bandförmigen Träger bildet, jeweils aus einem Stapelfasergarn aus Kunststoffmaterial gebildet sind. Bei dem Kunststoffmaterial für die Schuss- und Kettfäden kann es sich um Polyester, insbesondere PET (Polyethylenterephthalat), Polyamid und/oder Polypropylen handeln.According to the invention this is achieved in that, starting from the adhesive tape described above, the weft threads of the textile fabric, which forms the band-shaped carrier, each formed from a staple fiber yarn of plastic material. The plastic material for the weft and warp threads may be polyester, in particular PET (polyethylene terephthalate), polyamide and / or polypropylene.

Somit wird erfindungsgemäß ein Gewebe mit gemischten Garnen, und zwar Filamentgarn für die Kettfäden und Stapelfasergarn für die Schussfäden verwendet.Thus, according to the invention, a fabric with mixed yarns, namely filament yarn for the warp yarns and staple fiber yarn for the weft yarns, is used.

Stapelfasergarne zeichnen sich dadurch aus, dass die einzelnen Fasern eine endliche Länge besitzen. Durch Verdrehen der Fasern beim Spinnen entsteht ein Garn beliebiger Länge. Je nach eingesetzter Faserlänge der einzelnen Fasern unterscheidet man zwischen Kurz- und Langstapelfasergarn. Die Länge derartiger Fasern, die in einem Stapelfasergarn Verwendung finden, ist üblicherweise von 20 bis 150 mm.Staple fiber yarns are characterized by the fact that the individual fibers have a finite length. By twisting the fibers during spinning creates a yarn of any length. Depending on the fiber length of the individual fibers used, a distinction is made between short staple and long staple fiber yarn. The length of such fibers used in a staple fiber yarn is usually from 20 to 150 mm.

Unter einem Filamentgarn wird ein Garn verstanden, das theoretisch aus unendlich langen Fasern, den sogenannten Filamenten, besteht. Filamentgarne sind in der Regel nicht verdreht, da sie auch ohne eine Verdrehung der Fasern zueinander zusammenhalten. Monofilamentgarne bestehen nur aus einem einzigen Filament, und Multifilamentgarne bestehen aus mindestens zwei Einzelfasern, wobei man von Minifilamentgarnen spricht, wenn insbesondere zwei bis fünf Einzelfasern vorhanden sind, und von Multifilamentgarnen wird gesprochen, wenn diese aus mehr als fünf Einzelfasern bestehen.A filament yarn is understood to mean a yarn which theoretically consists of infinitely long fibers, the so-called filaments. Filament yarns are usually not twisted because they hold together without twisting the fibers to each other. Monofilament yarns consist of only a single filament, and multifilament yarns consist of at least two individual fibers, which is referred to as mini filament yarns, especially when two to five individual fibers are present, and multifilament yarns are considered to consist of more than five individual fibers.

Erfindungsgemäß können die Schussfäden jeweils unterschiedliche Schussfadenstärken besitzen, wobei vorteilhafterweise bei ein und demselben Träger stets dieselben Schussfadenstärken Verwendung finden. Hierbei betragen die Schussfädenstärken 30 dtex bis 200 dtex, wobei die Stapelfaserlängen größer/gleich 20 mm und kleiner/gleich 150 mm sein können, und vorzugsweise 20 mm bis 50 mm betragen können. Hierbei liegt bei dem jeweiligen Stapelfasergarn eine insbesondere konstante Faserlänge vor.According to the invention, the weft threads can each have different weft thread thicknesses, advantageously always using the same weft thread thicknesses in one and the same carrier. Here, the weft yarn thicknesses are from 30 dtex to 200 dtex, wherein the staple fiber lengths may be greater than or equal to 20 mm and less than or equal to 150 mm, and may preferably be 20 mm to 50 mm. In this case, a particular constant fiber length is present in the respective staple fiber yarn.

Das erfindungsgemäße Band zeichnet sich auf Grund des verwendeten Trägermaterials durch eine Weichheit und Schmiegsamkeit aus, wie diese beispielsweise bei einem Zellwoll-Gewebeband vorhanden sind. Darüber hinaus wird durch die Wahl der Fadenstärken von Kett- und Schussfäden eine Quereinreißbarkeit von Hand bewirkt. Das erfindungsgemäß verwendete Kunststoffmaterial garantiert eine Temperaturstabilität von 85°C bis 150°C. Zudem ist das erfindungsgemäße Klebeband flexibel, verrottungsfest und weist einen geringen Schrumpf auf.Due to the carrier material used, the band according to the invention is characterized by a softness and flexibility, as are present, for example, in a cellulosic woven fabric tape. In addition, by the choice of the yarn strengths of warp and weft yarns a Quererißißbarkeit done by hand. The plastic material used in the invention guarantees a temperature stability of 85 ° C to 150 ° C. In addition, the adhesive tape according to the invention is flexible, rotting resistant and has a low shrinkage.

Vorteilhafte Ausführungen der Erfindung sind in den Unteransprüchen enthalten und werden an Hand der in den beiliegenden Zeichnungen dargestellten Ausführungsbeispiele näher erläutert. Es zeigen:Advantageous embodiments of the invention are contained in the subclaims and will be explained in more detail with reference to the embodiments illustrated in the accompanying drawings. Show it:

1 eine Aufsicht auf eine Oberseite eines erfindungsgemäßen Klebebandes, 1 a top view of an upper side of an adhesive tape according to the invention,

2 einen Schnitt durch ein erfindungsgemäßes Klebeband gemäß 1, und zwar in Richtung der Längsfäden entlang der Schnittlinie II-II in 1 und 2 a section through an inventive adhesive tape according to 1 , in the direction of the longitudinal threads along the section line II-II in 1 and

3 einen Schnitt durch eine weitere Ausführung eines erfindungsgemäßen Klebebandes. 3 a section through a further embodiment of an adhesive tape of the invention.

In den verschiedenen Figuren der Zeichnung sind gleiche Teile stets mit denselben Bezugszeichen versehen.In the various figures of the drawing, like parts are always provided with the same reference numerals.

Zu der anschließenden Beschreibung wird beansprucht, dass die Erfindung nicht auf die Ausführungsbeispiele und dabei nicht auf alle oder mehrere Merkmale von beschriebenen Merkmalskombinationen beschränkt ist, vielmehr ist jedes einzelne Teilmerkmal des/jedes Ausführungsbeispiels auch losgelöst von allen anderen im Zusammenhang damit beschriebenen Teilmerkmalen für sich und auch in Kombination mit beliebigen Merkmalen eines anderen Ausführungsbeispiels von Bedeutung für den Gegenstand der Erfindung.For the ensuing description, it is claimed that the invention is not limited to the embodiments and not to all or several features of described combinations of features, but rather, each individual feature of the / each embodiment is also detached from all other features described in connection therewith also in combination with any features of another embodiment of importance for the subject invention.

Ein erfindungsgemäßes Klebeband besteht aus einem bandförmigen Träger 1 aus einem textilen Gewebe aus Kettfäden 2 und Schussfäden 3. Als Material für die Kettfäden 2 und Schussfäden 3 wird vorzugsweise ein PET-Kunststoffmaterial, insbesondere Polyester verwendet. Die Kettfäden 2 werden aus einem Filamentgarn gebildet, das als Monofilamentgarn oder als Multifilamentgarn gebildet ist, d. h. bei Verwendung eines Multifilamentgarns bestehen die Kettfäden 2 aus mehreren, unverdrehten Endlosfasern, d. h. Endlosfilamenten.An inventive adhesive tape consists of a band-shaped carrier 1 from a textile fabric of warp threads 2 and weft threads 3 , As material for the warp threads 2 and weft threads 3 For example, a PET plastic material, in particular polyester, is preferably used. The warp threads 2 are formed from a filament yarn formed as a monofilament yarn or a multifilament yarn, that is, when a multifilament yarn is used, the warp yarns are composed 2 from several, untwisted endless fibers, ie continuous filaments.

Erfindungsgemäß sind die Schussfäden 3 als Stapelfasergarne ausgebildet, wobei es sich um aus Endlosfilamenten geschnittene Stapelfasern handelt, deren Stapelfaserlänge gleich groß ist, vorzugsweise beträgt die Stapelfaserlänge 20 mm bis 150 mm, vorzugsweise 20 mm bis 50 mm. Vorteilhafterweise ist das Flächengewicht des Gewebeträgers größer/gleich 50 g/qm und kleiner/gleich 250 g/qm. Insbesondere ist es zweckmäßig, wenn das Flächengewicht des Trägers 1 70 bis 120 g/qm beträgt.According to the invention, the weft threads 3 formed as staple fiber yarns, which are cut from continuous filament staple fibers whose staple fiber length is the same size, preferably, the staple fiber length is 20 mm to 150 mm, preferably 20 mm to 50 mm. Advantageously, the weight per unit area of the fabric carrier is greater than or equal to 50 g / m 2 and less than or equal to 250 g / m 2. In particular, it is expedient if the basis weight of the carrier 1 70 to 120 gsm.

Die Fadenstärke der Kettfäden 2 beträgt 20 dtex bis 90 dtex, insbesondere 50 dtex bis 76 dtex, und die Kettfadenanzahl der Kettfäden 2 pro cm Trägerbreite beträgt 30 bis 70 Fäden, vorzugsweise 40 bis 50 Fäden. Weiterhin beträgt die Fadenstärke der Schussfäden 3 100 dtex bis 300 dtex, vorzugsweise 160 dtex bis 220 dtex. Die Anzahl der Schussfäden 3 pro cm Trägerlänge beträgt 20 bis 60 Fäden, insbesondere 25 bis 35 Fäden. Ein erfindungsgemäß verwendeter Träger 1 besitzt insbesondere ein Flächengewicht von 70 g/qm bis 120 g/qm. Die Dicke eines erfindungsgemäßen Trägers 1 liegt vorzugsweise in einem Bereich von 0,12 bis 0,24 mm, und die Dicke des fertigen Klebebandes beträgt vorzugsweise 0,14 mm bis 0,30 mm. Die Dicke ist dabei über die Fläche des Trägers 1 gleich groß, d. h. konstant. Die erfindungsgemäß auf mindestens einer Seite des Trägers 1 aufgebrachte Klebebeschichtung 4 besteht vorzugsweise aus einem Acrylatklebstoff oder aus einem Synthesekautschuk. Weiterhin kann es erfindungsgemäß zweckmäßig sein, wenn die Kettfäden 2 untereinander intermingelt und/oder texturiert und/oder glatt sind. Weiterhin kann es von Vorteil sein, wenn die Kettfäden 2 und die Schussfäden 3 spinndüsengefärbt und/oder stückgefärbt sind. Hierbei wird unter Spinndüsenfärben eine Einfärbung des Fadenmaterials während des Extrusionsprozesses der die Fäden bildenden Fasern verstanden. Stückfärben ist eine nachträgliche Färbung der extrudierten Fasern. In der nachfolgenden Tabelle 1 ist eine Übersicht der mechanischen Eigenschaften des bei einem erfindungsgemäßen Klebeband verwendeten Gewebeträgers im Vergleich mit einem Gewebeträger aus Zellwolle gezeigt. Hieraus ergibt sich, dass die erfindungsgemäßen Gewebe bei einer geringeren Dicke eine verbesserte Reißdehnung und eine gleichwertige Bruchkraft besitzen. Zudem ist die Luftdurchlässigkeit wesentlich reduziert. Dadurch, dass die Luftdurchlässigkeit deutlich reduziert wird, lassen sich die Materialien einfacher mit weniger Kleberauftrag beschichten. Die erfindungsgemäßen Gewebeträger (Konstruktion 1 und 2) zeichnen sich durch eine Weiterreißfestigkeit gemäß Elmendorf-Test von 5.000 bis 8.000 mN aus. Des Weiteren bedingen die Stapelfaserfilamentgarne eine dem Zellwollgewebe entsprechende Haptik, siehe hierzu Tabelle 1. Dieses lässt sich unter anderem auch durch die Biegesteifigkeit nachweisen. Die erfindungsgemäßen Gewebeträger haben eine Biegesteifigkeit von 1 bis 2 mNcm2.The thread thickness of the warp threads 2 is 20 dtex to 90 dtex, in particular 50 dtex to 76 dtex, and the warp thread count of the warp threads 2 per cm carrier width is 30 to 70 threads, preferably 40 to 50 threads. Furthermore, the thread thickness of the weft threads 3 100 dtex to 300 dtex, preferably 160 dtex to 220 dtex. The number of weft threads 3 per cm carrier length is 20 to 60 threads, in particular 25 to 35 threads. A carrier used according to the invention 1 in particular has a basis weight of 70 g / sqm to 120 g / sqm. The thickness of a carrier according to the invention 1 is preferably in a range of 0.12 to 0.24 mm, and the thickness of the finished adhesive tape is preferably 0.14 mm to 0.30 mm. The thickness is over the surface of the carrier 1 the same size, ie constant. The invention according to at least one side of the carrier 1 applied adhesive coating 4 preferably consists of an acrylate adhesive or of a synthetic rubber. Furthermore, it may be appropriate according to the invention if the warp threads 2 interlaced and / or textured and / or smooth. Furthermore, it may be advantageous if the warp threads 2 and the weft threads 3 Spinneret dyed and / or piece dyed. Here, spinneret dyeing is understood to mean a coloring of the thread material during the extrusion process of the fibers forming the filaments. Piece dyeing is a subsequent dyeing of the extruded fibers. Table 1 below shows an overview of the mechanical properties of the fabric carrier used in an adhesive tape according to the invention in comparison with a fabric carrier made of cell wool. It follows that the fabrics of the present invention have improved elongation at break and equivalent breaking force at a smaller thickness. In addition, the air permeability is significantly reduced. The fact that the air permeability is significantly reduced, the materials can be coated with less adhesive application easier. The fabric supports according to the invention (construction 1 and 2) are characterized by a tear strength according to the Elmendorf test of 5,000 to 8,000 mN. Furthermore, the staple fiber filament yarns cause a haptic corresponding to the cellulosic fabric, see Table 1. This can be demonstrated, inter alia, by the flexural rigidity. The fabric supports according to the invention have a bending stiffness of 1 to 2 mNcm 2 .

Tabelle 1: Table 1:

Alle Angaben beziehen sich auf das Trägermaterial ohne Beschichtung. Prüfung Einheit/Prüfart Stapel/Filament PET-Gewebe Konstruktion 1 Stapel/Filament PET-Gewebe Konstruktion 2 ZW-Gewebe Trägermaterial - Polyester Polyester Viskose Flächengewicht g/m2 90–100 105–110 105–110 Kettfadenanzahl Fd/cm 45 45 26,5 Fadenstärke der Kettfäden dtex 56 56 200 Schussfadenanzahl Fd/cm 34 30 26.5 Fadenstärke der Schussfäden dtex 200 281 200 Stapelfaserlänge mm 32 21 18 Dicke mm 0,12 0,14 0,18–0,19 Reißdehnung % 24–27 25–28 8–15 Bruchkraft N/cm 78–85 82–84 80–90 Flächengewicht g/m2 92–94 108–110 105–110 Luftdurchlässigkeit l/m2s 60–89 80–100 350–550 Weiterreißfestigkeit mN 5.000–7.000 6.000–8.000 8.500–12.000 Biegesteifigkeit mNcm2 1–2 1–2 1–2 Haptik sensorische Prüfung weich wie Zellwollgewebe weich wie Zellwollgewebe weich Handeinreißbarkeit LV 312 quereinreißbar quereinreißbar quereinreißbar All information refers to the carrier material without coating. exam Unit / test type Stack / filament PET fabric construction 1 Stack / filament PET fabric construction 2 ZW-tissue support material - polyester polyester viscose grammage g / m 2 90-100 105-110 105-110 Kettfadenanzahl Fd / cm 45 45 26.5 Thread thickness of the warp threads dtex 56 56 200 Weft number Fd / cm 34 30 26.5 Thread thickness of the weft threads dtex 200 281 200 Staple fiber length mm 32 21 18 thickness mm 0.12 0.14 0.18 to 0.19 elongation at break % 24-27 25-28 8-15 breaking force N / cm 78-85 82-84 80-90 grammage g / m 2 92-94 108-110 105-110 Air permeability l / m 2 s 60-89 80-100 350-550 Tear strength mN 5000-7000 6000 to 8000 8500-12000 bending stiffness mcm 2 1-2 1-2 1-2 haptics sensory examination soft as cellulosic tissue soft as cellulosic tissue soft hand tearability LV 312 transverse tearability transverse tearability transverse tearability

In der Tabelle 2 sind technische Daten eines erfindungsgemäßen Klebebandes gemäß 1 wiedergegeben.Table 2 shows technical data of an adhesive tape according to the invention 1 played.

Tabelle 2:Table 2:

Die Tabelle betrifft den Träger mit einseitiger Klebebeschichtung. Prüfung Einheit Ergebnisse Konstruktionen 1 und 2 Dicke mm 0,14–0,30 Reißdehnung % 33–39 Reißfestigkeit N/cm 78–82 Klebkraft Stahl N/cm 5,0–7,5 Klebkraft Bandrücken N/cm 4,0–6,0 Unwind N 2–9 Flagging (30 min.) mm 0–10 Flagging (24 Std.) mm 0–10 Abrieb mit 5 mm Dorn Hübe 80–95 (Klasse A) Handeinreißbarkeit - quereinreißbar The table concerns the backing with one-sided adhesive coating. exam unit Results constructions 1 and 2 thickness mm 0.14 to 0.30 elongation at break % 33-39 tear strength N / cm 78-82 Bond strength steel N / cm 5.0-7.5 Adhesive power band back N / cm 4.0-6.0 Unwind N 2-9 Flagging (30 min.) mm 0-10 Flagging (24 hours) mm 0-10 Abrasion with 5 mm mandrel strokes 80-95 (Class A) hand tearability - transverse tearability

Die in den beiden Tabellen 1 und 2 enthaltenen Basisdaten wurden nach den Normen der nachfolgenden Tabelle 3 bestimmt: Tabelle 3: DIN Normen Neue Bezeichnung Datum der aktuell gültigen Version EN ISO 2286-2 1998-07 Flächengewicht DIN 53830-3 1981-05 Bestimmung der Feinheit von Garnen DIN EN 1049-2 1994-02 Bestimmung der Anzahl der Fäden je Längeneinheit DIN EN 1942 2008-06 Dicke DIN EN 14410 2003-06 Bruchkraft/Dehnung DIN EN 1939 2003-12 Klebkraft DIN EN 1944 1996-04 Abrollkraft DIN EN 21974 DIN EN ISO 1974:2012-09 2012-09 Weiterreißfestigkeit DIN EN ISO 9237 1995-12 Luftdurchlässigkeit DIN 53 362 2003-10 Biegesteifigkeit flagging nach LV 312 LV 312 LV 312-1 2009 Okt. 2010 Schutzsysteme für Leitungssätze in Kraftfahrzeugen Klebebänder, Prüfrichtlinie LV 312 LV 312 2009 Okt. 2010 Handeinreißbarkeit The basic data contained in both Tables 1 and 2 were determined according to the standards of Table 3 below: Table 3: DIN standards New name Date of the currently valid version EN ISO 2286-2 1998-07 grammage DIN 53830-3 1981-05 Determining the fineness of yarns DIN EN 1049-2 1994-02 Determination of the number of threads per unit length DIN EN 1942 2008-06 thickness DIN EN 14410 2003-06 Tensile strength / elongation DIN EN 1939 2003-12 adhesive power DIN EN 1944 1996-04 unwind DIN EN 21974 DIN EN ISO 1974: 2012-09 2012-09 Tear strength DIN EN ISO 9237 1995-12 Air permeability DIN 53 362 2003-10 bending stiffness flagging to LV 312 LV 312 LV 312-1 2009 Oct. 2010 Protection systems for wiring harnesses in motor vehicles Adhesive tapes, test guideline LV 312 LV 312 2009 Oct. 2010 hand tearability

Die in Tabelle 2 angegebenen Parameter dokumentieren dabei die vorteilhaft erfindungsgemäß erreichbaren Eigenschaften. Der Abriebtest erfolgte dabei mit einem Abriebtester nach der gemeinsamen Prüfrichtlinie der Firma AUDI, BMW, Daimler und VW ”Klebebänder für Kabelsätze in Kraftfahrzeugen” LV 312 an einem 5-mm-Dorn. Nach jeweils zehn Hüben erfolgte eine Kontrolle. Der Endwert war erreicht, sobald die Rückseitenbeschichtung, d. h. die Klebeschicht 4 vom Gewebe des Trägers 1 abgerieben wurde.The parameters given in Table 2 document the properties that can advantageously be achieved according to the invention. The abrasion test was carried out using an abrasion tester according to the joint test guidelines of AUDI, BMW, Daimler and VW "Adhesive tapes for cable harnesses in motor vehicles" LV 312 on a 5mm mandrel. After every ten strokes, a check was made. The final value was reached as soon as the backside coating, ie the adhesive layer 4 from the fabric of the wearer 1 was rubbed off.

Das erfindungsgemäße Klebeband eignet sich einerseits als Kabelwickelband zum Umwickeln von einzelnen elektrischen Kabeln und Kabelsträngen. Es ist aber ebenso in der Medizin als medizinisches Klebeband oder als Reparatur-Klebeband im Do-it-yourself Bereich verwendbar. Weiterhin ist es erfindungsgemäß von Vorteil, das Klebeband auf seiner der Klebebeschichtung gegenüberliegenden Seite mit einer Oberflächenbeschichtung 5 aus Kunststoff, z. B. Acrylat, Polurethan, PVC oder Silikon zu versehen, siehe 3. Die Klebebeschichtung 4 und/oder die Oberflächenbeschichtung 5 kann auch in die Gewebestruktur des Trägers 1 eindringen.The adhesive tape according to the invention is suitable, on the one hand, as a cable winding tape for wrapping individual electrical cables and cable strands. However, it can also be used in medicine as a medical adhesive tape or as a repair adhesive tape in the do-it-yourself sector. Furthermore, it is advantageous according to the invention, the adhesive tape on its adhesive coating opposite side with a surface coating 5 made of plastic, z. As acrylate, polyurethane, PVC or silicone, see 3 , The adhesive coating 4 and / or the surface coating 5 may also be in the fabric structure of the wearer 1 penetration.

Die Erfindung beschränkt sich nicht auf die beschriebenen Ausführungsbeispiele, sondern umfasst auch alle im Sinne der Erfindung gleichwirkenden Ausführungen. Ferner ist die Erfindung nicht auf die im Anspruch 1 und den Unteransprüchen definierten Merkmalskombinationen beschränkt, sondern kann auch durch jede beliebige andere Kombination von bestimmten Merkmalen der insgesamt offenbarten Einzelmerkmale definiert sein.The invention is not limited to the described embodiments, but also includes all the same in the context of the invention embodiments. Furthermore, the invention is not limited to the feature combinations defined in claim 1 and the dependent claims, but may also be defined by any other combination of certain features of the overall disclosed individual features.

BezugszeichenlisteLIST OF REFERENCE NUMBERS

11
Trägercarrier
22
Kettfädenwarp
33
Schussfädenwefts
44
Klebebeschichtungadhesive coating
55
Oberflächenbeschichtungsurface coating

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • EP 1990393 A1 [0002] EP 1990393 A1 [0002]
  • EP 1074595 A1 [0005] EP 1074595 A1 [0005]

Zitierte Nicht-PatentliteraturCited non-patent literature

  • LV 312 [0022] LV 312 [0022]
  • EN ISO 2286-2 [0025] EN ISO 2286-2 [0025]
  • DIN 53830-3 [0025] DIN 53830-3 [0025]
  • DIN EN 1049-2 [0025] DIN EN 1049-2 [0025]
  • DIN EN 1942 [0025] DIN EN 1942 [0025]
  • DIN EN 14410 [0025] DIN EN 14410 [0025]
  • DIN EN 1939 [0025] DIN EN 1939 [0025]
  • DIN EN 1944 [0025] DIN EN 1944 [0025]
  • DIN EN 21974 [0025] DIN EN 21974 [0025]
  • DIN EN ISO 1974:2012-09 [0025] DIN EN ISO 1974: 2012-09 [0025]
  • DIN EN ISO 9237 [0025] DIN EN ISO 9237 [0025]
  • DIN 53 362 [0025] DIN 53 362 [0025]
  • LV 312 [0025] LV 312 [0025]
  • LV 312 [0025] LV 312 [0025]
  • LV 312-1 [0025] LV 312-1 [0025]
  • LV 312 [0025] LV 312 [0025]
  • LV 312 [0025] LV 312 [0025]
  • LV 312 [0026] LV 312 [0026]

Claims (14)

Klebeband, insbesondere Kabelwickelband, umfassend einen bandförmigen Träger (1) aus einem textilen Gewebe aus Kettfäden (2) und Schussfäden (3), wobei die Kettfäden (2) aus einem Kunststoffmaterial hergestellt und als Filamentgarn ausgebildet sind, und eine auf den Träger (1) aufgebrachte Klebebeschichtung (4), dadurch gekennzeichnet, dass die Schussfäden (3) jeweils aus einem Stapelfasergarn aus Kunststoffmaterial gebildet sind.Adhesive tape, in particular cable winding tape, comprising a tape-shaped carrier ( 1 ) of a textile fabric of warp threads ( 2 ) and weft threads ( 3 ), the warp threads ( 2 ) are made of a plastic material and are formed as filament yarn, and one on the support ( 1 ) applied adhesive coating ( 4 ), characterized in that the weft threads ( 3 ) are each formed from a Stapelfasergarn of plastic material. Klebeband nach Anspruch 1, dadurch gekennzeichnet, die Faserlänge der Stapelfasern des Stapelfasergarns 20 mm bis 150 mm, vorzugsweise 20 mm bis 50 mm beträgt.Adhesive tape according to claim 1, characterized in that the fiber length of the staple fibers of the staple fiber yarn is 20 mm to 150 mm, preferably 20 mm to 50 mm. Klebeband nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass das Flächengewicht des Trägers (1) größer/gleich 50 g/qm und kleiner/gleich 250 g/qm ist, vorzugsweise 70 g/qm bis 120 g/qm.Adhesive tape according to claim 1 or 2, characterized in that the basis weight of the carrier ( 1 ) greater than or equal to 50 gsm and less than or equal to 250 gsm, preferably 70 gsm to 120 gsm. Klebeband nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die Fadenstärke der Kettfäden (2) des Trägers (1) 20 dtex bis 90 dtex, vorzugsweise 50 dtex bis 76 dtex beträgt.Adhesive tape according to one of claims 1 to 3, characterized in that the thread thickness of the warp threads ( 2 ) of the carrier ( 1 ) Is 20 dtex to 90 dtex, preferably 50 dtex to 76 dtex. Klebeband nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Kettfadenanzahl, d. h. Anzahl der Kettfäden (2) pro cm Trägerbreite 30 bis 70 Fäden, vorzugsweise 40 bis 50 Fäden beträgt.Adhesive tape according to one of Claims 1 to 4, characterized in that the number of warp threads, ie the number of warp threads ( 2 ) per cm carrier width 30 to 70 threads, preferably 40 to 50 threads. Klebeband nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass die Fadenstärke der Schussfäden (3) 100 dtex bis 300 dtex, vorzugsweise 160 dtex bis 285 dtex beträgt.Adhesive tape according to one of claims 1 to 5, characterized in that the thread thickness of the weft threads ( 3 ) Is 100 dtex to 300 dtex, preferably 160 dtex to 285 dtex. Klebeband nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Schussfadenanzahl, d. h. die Anzahl der Schussfäden (3) pro cm Trägerlänge 20 bis 60 Fäden, vorzugsweise 25 bis 35 Fäden beträgt.Adhesive tape according to one of claims 1 to 6, characterized in that the weft number, ie the number of weft threads ( 3 ) per cm carrier length 20 to 60 threads, preferably 25 to 35 threads. Klebeband nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass die Dicke des Trägers (1) größer/gleich 0,12 und kleiner/gleich 0,24 mm ist und insbesondere die Dicke des Klebebandes größer/gleich 0,14 und kleiner/gleich 0,30 mm ist.Adhesive tape according to one of Claims 1 to 7, characterized in that the thickness of the backing ( 1 ) is greater than or equal to 0.12 and less than or equal to 0.24 mm and, in particular, the thickness of the adhesive tape is greater than or equal to 0.14 and less than or equal to 0.30 mm. Klebeband nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die Kettfäden (2) intermingelt und/oder texturiert und/oder glatt sind.Adhesive tape according to one of Claims 1 to 8, characterized in that the warp threads ( 2 ) are intermingled and / or textured and / or smooth. Klebeband nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass die Kettfäden (2) und die Schussfäden (3) spinndüsengefärbt und/oder stückgefärbt sind.Adhesive tape according to one of Claims 1 to 9, characterized in that the warp threads ( 2 ) and the weft threads ( 3 ) are spinneret dyed and / or piece dyed. Klebeband nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass die Kett- und Schussfäden aus Polyester, Polyamid und/oder Polypropylen gebildet sind.Adhesive tape according to one of claims 1 to 10, characterized in that the warp and weft threads of polyester, polyamide and / or polypropylene are formed. Klebeband nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass die Fadenstärke, die Anzahl der Kettfäden (2) und der Schussfäden (3) derart aufeinander abgestimmt sind, dass eine Biegesteifigkeit kleiner/gleich 5 mNcm2 gegeben ist.Adhesive tape according to one of claims 1 to 11, characterized in that the thread thickness, the number of warp threads ( 2 ) and the weft threads ( 3 ) are matched to one another such that a bending stiffness of less than or equal to 5 mNcm 2 is given. Klebeband nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass die Stapelfaserlänge der Schussfäden (3), die Anzahl der Kett- und Schussfäden (2, 3) und die Fadenstärke der Kett- und Schussfäden (3) derart gewählt sind, dass die Luftdurchlässigkeit des Trägers (1) kleiner/gleich 300 l/m2 s beträgt.Adhesive tape according to one of Claims 1 to 12, characterized in that the staple fiber length of the weft threads ( 3 ), the number of warp and weft threads ( 2 . 3 ) and the thread thickness of the warp and weft threads ( 3 ) are selected such that the air permeability of the carrier ( 1 ) is less than or equal to 300 l / m 2 s. Klebeband nach einem der Ansprüche 1 bis 13, dadurch gekennzeichnet, dass auf dem Träger (1) auf seiner der Klebebeschichtung (4) gegenüberliegenden Seite eine Oberflächenbeschichtung (5) aus Kunststoff aufgebracht ist.Adhesive tape according to one of claims 1 to 13, characterized in that on the support ( 1 ) on its adhesive coating ( 4 ) opposite side a surface coating ( 5 ) is applied from plastic.
DE102014107312.6A 2013-07-05 2014-05-23 duct tape Withdrawn DE102014107312A1 (en)