DE102012109808A1 - Preparing composite material used in e.g. door of oven, comprises applying of sol gel layer prepared by mixing pigment particle and oxide particle on glass or glass ceramic substrate, and applying polymer layer on sol gel layer - Google Patents

Preparing composite material used in e.g. door of oven, comprises applying of sol gel layer prepared by mixing pigment particle and oxide particle on glass or glass ceramic substrate, and applying polymer layer on sol gel layer Download PDF

Info

Publication number
DE102012109808A1
DE102012109808A1 DE201210109808 DE102012109808A DE102012109808A1 DE 102012109808 A1 DE102012109808 A1 DE 102012109808A1 DE 201210109808 DE201210109808 DE 201210109808 DE 102012109808 A DE102012109808 A DE 102012109808A DE 102012109808 A1 DE102012109808 A1 DE 102012109808A1
Authority
DE
Germany
Prior art keywords
layer
composite material
sol
gel layer
decorative coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
DE201210109808
Other languages
German (de)
Inventor
Matthias Bockmeyer
Andrea Anton
Claudia Kottenstedte
Lutz Klippe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott AG filed Critical Schott AG
Priority to DE201210109808 priority Critical patent/DE102012109808A1/en
Priority to JP2015506260A priority patent/JP6333237B2/en
Priority to EP13717776.2A priority patent/EP2838860B1/en
Priority to CN201380032644.2A priority patent/CN104395259A/en
Priority to CN201380032640.4A priority patent/CN104395258B/en
Priority to JP2015506259A priority patent/JP6257586B2/en
Priority to PCT/EP2013/058224 priority patent/WO2013156622A1/en
Priority to PCT/EP2013/058218 priority patent/WO2013156617A1/en
Priority to EP13719061.7A priority patent/EP2838861B1/en
Publication of DE102012109808A1 publication Critical patent/DE102012109808A1/en
Priority to US14/518,471 priority patent/US10590036B2/en
Priority to US14/518,456 priority patent/US10308548B2/en
Priority to US16/388,126 priority patent/US11713277B2/en
Ceased legal-status Critical Current

Abstract

The method comprises: applying of a sol gel layer (2) prepared by mixing a pigment particle (3) and an oxide particle (5) on a glass or a glass ceramic substrate; and applying a polymer layer on the sol gel layer, where the sol gel layer is infiltrated with a material of the polymer layer. The sol-gel layer has an average pore diameter of less than 10 nm, preferably less than 5 nm. The polymer layer is applied using a screen printing process before the penetration of the sol-gel layer. The polymer layer and the sol-gel layer are thermally cured at 200[deg] C. An independent claim is included for a composite material having a decorative coating.

Description

Gebiet der Erfindung Field of the invention

Die Erfindung betrifft ein Verfahren zur Herstellung eines Verbundmaterials mit dekorativer Beschichtung sowie ein entsprechendes dekoratives Verbundmaterial. Insbesondere bezieht sich die Erfindung auf ein Glaskeramiksubstrat, wie es beispielsweise für Kochflächen verwendet wird, mit einer dekorativen Unterseitenbeschichtung. The invention relates to a method for producing a composite material with decorative coating and a corresponding decorative composite material. In particular, the invention relates to a glass-ceramic substrate, such as used for cooking surfaces, with a decorative bottom coating.

Hintergrund der Erfindung Background of the invention

Mit einer dekorativen Beschichtung versehene Glas- oder Glaskeramiksubstrate sind bekannt. Insbesondere werden zumindest teiltransparente Glaskeramiksubstrate, wie sie für Kochflächen verwendet werden, mit einer Unterseitenbeschichtung versehen. Glass or glass ceramic substrates provided with a decorative coating are known. In particular, at least partially transparent glass-ceramic substrates, such as those used for cooking surfaces, are provided with a bottom-side coating.

Die dekorative Beschichtung kann aus funktionellen Gründen aufgebracht sein, beispielsweise zur Markierung von Kochfeldern. Weiter kann eine dekorative Beschichtung auch nur dazu dienen, einen besonderen optischen Eindruck zu erzeugen, beispielsweise um ein Kochfeld in einer bestimmten Farbe bereitzustellen. The decorative coating may be applied for functional reasons, for example for cooking hobs. Further, a decorative coating can only serve to create a special visual impression, for example to provide a hob in a particular color.

Zum Aufbringen von dekorativen Beschichtungen sind aus der Praxis eine Vielzahl von Möglichkeiten bekannt. For applying decorative coatings a variety of possibilities are known from practice.

Beispielsweise gibt es mittels eines Sputter-Verfahrens aufgebrachte dekorative Beschichtungen. Derartige Sputter-Verfahren sind aufwendig. Weiter ist die Auswahl hinsichtlich der optischen Anmutung begrenzt. Im Falle einer Teilbeschichtung, beispielsweise zur Markierung von Kochflächen, müssen aufwendige Maskierungsschritte vorgenommen werden und gesputterte Schichten haben häufig eine unerwünscht hohe Leitfähigkeit, so dass diese oft nicht hinter kapazitiven Schaltern angeordnet werden können. For example, there are decorative coatings applied by means of a sputtering process. Such sputtering methods are expensive. Furthermore, the choice is limited in terms of visual appearance. In the case of a partial coating, for example for marking cooking surfaces, complex masking steps must be performed and sputtered layers often have an undesirably high conductivity, so that they often can not be arranged behind capacitive switches.

Weiter sind Silikonbeschichtungen bekannt. Diese haben den Vorteil, dass sie sich leicht über eine Silikonfarbe, beispielsweise mittels Siebdruck, aufbringen lassen, haben aber meist eine nicht optimale mechanische Beständigkeit und können sich bei hoher Temperaturbelastung verfärben. Furthermore, silicone coatings are known. These have the advantage that they can easily be applied over a silicone ink, for example by means of screen printing, but usually have a non-optimal mechanical resistance and can discolor at high temperature load.

Weiter bekannt sind Glasfluss-basierte Schichten, sogenannte Emailleschichten. Derartige pigmentierte Glasfluss-basierte Schichten haben den Nachteil, dass sie das Glaskeramiksubstrat unter Zugspannung setzen und so dessen Festigkeit verringern. Dieser Nachteil kann durch das Aufbringen poröser Schichten reduziert werden, was allerdings mit einer matten Anmutung des so hergestellten Verbundmaterials einhergeht. Also known are glass flow-based layers, so-called enamel layers. Such pigmented glass flux-based layers have the disadvantage that they put the glass-ceramic substrate under tension and thus reduce its strength. This disadvantage can be reduced by the application of porous layers, but this is accompanied by a dull appearance of the composite material produced in this way.

Weiter bekannt sind pigmentierte Methylgruppenfunktionalsierte Sol-Gel-Schichten, welche allerdings zu Rissbildungen neigen, die sich als lokale Aufhellungen bemerkbar machen. Die Gefahr von Rissbildungen kann wiederum durch das Aufbringen von porösen Sol-Gel-Schichten reduziert werden, was wiederum mit einem matten Farbeindruck einhergeht. Insbesondere lassen sich keine tief schwarzen glänzenden Schichten bereitstellen. Also known are pigmented methyl group-functionalized sol-gel layers, which, however, tend to form cracks, which are noticeable as local whitening. The risk of cracking can in turn be reduced by the application of porous sol-gel layers, which in turn is accompanied by a dull color impression. In particular, no deep black glossy layers can be provided.

Schließlich ist noch das Aufbringen von Lüsterfarben bekannt. Auch bei Lüsterfarben ist die Farbwahl eingeschränkt und für die Herstellung von tief schwarzen Farben muss auf teure Edelmetall-basierende Farben zurückgegriffen werden. Finally, the application of chandelier paints is known. Even with chandelier colors, the color choice is limited and for the production of deep black colors must be resorted to expensive precious metal-based colors.

Aufgabe der Erfindung Object of the invention

Der Erfindung liegt demgegenüber die Aufgabe zugrunde, ein einfaches Verfahren zum Aufbringen einer Hochtemperaturbeständigen dekorativen Schicht mit guter optischer Anmutung bereitzustellen. The invention is the object of the invention to provide a simple method for applying a high temperature resistant decorative layer with good visual appearance.

Zusammenfassung der Erfindung Summary of the invention

Die Aufgabe der Erfindung wird bereits durch ein Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung sowie durch ein Verbundmaterial mit dekorativer Beschichtung nach einem der unabhängigen Ansprüche gelöst. The object of the invention is already achieved by a method for producing a composite material with decorative coating and by a composite material with decorative coating according to one of the independent claims.

Bevorzugte Ausführungsformen und Weiterbildungen der Erfindung sind Gegenstand der Unteransprüche. Preferred embodiments and further developments of the invention are subject of the dependent claims.

Die Erfindung betrifft ein Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung, wobei unter einer dekorativen Beschichtung auch eine Beschichtung verstanden wird, welche zumindest teilweise aus funktionellen Gründen aufgebracht ist, wie beispielsweise eine Markierung von Kochflächen, eine aufgebrachte Beschriftung etc. The invention relates to a method for producing a composite material with a decorative coating, wherein a decorative coating is also understood to mean a coating which is at least partially applied for functional reasons, such as, for example, a marking of cooking surfaces, an applied lettering, etc.

Die Beschichtung wird auf ein hitzebeständiges Glas oder Glaskeramiksubstrat aufgebracht. Für Kochflächen werden in der Regel hitzebeständige Glaskeramiksubstrate verwendet. Für andere Einsatzorte mit hoher Temperaturbelastung, also insbesondere mit einer Temperaturbelastung von mehr als 200°C, können aber auch manche hitzebeständigen Spezialgläser verwendet werden. The coating is applied to a heat-resistant glass or glass-ceramic substrate. For cooking surfaces usually heat-resistant glass ceramic substrates are used. For other sites with high temperature load, so in particular with a temperature load of more than 200 ° C, but also some special heat-resistant glasses can be used.

Das Glas oder Glaskeramiksubstrat ist vorzugsweise eben und im sichtbaren Bereich zumindest teilweise transparent ausgebildet. The glass or glass ceramic substrate is preferably planar and at least partially transparent in the visible region.

Auf das Glaskeramiksubstrat wird zunächst eine Sol-Gel-Schicht aufgebracht, welche zumindest Pigmentpartikel enthält. Insbesondere wird für die Sol-Gel-Schicht ein Hybridpolymer verwendet, so dass nach Trocknung eine teilweise anorganisch, teilweise organisch ausgebildete Schicht entsteht. First, a sol-gel layer containing at least pigment particles is applied to the glass-ceramic substrate. In particular, a hybrid polymer is used for the sol-gel layer, so that after drying, a partially inorganic, partially organic layer formed.

Zum Erreichen einer hohen Porosität im nanoskaligen Bereich werden dem Sol-Gel Partikel zugesetzt werden. To achieve a high porosity in the nanoscale particle will be added to the sol-gel.

Als Partikel können, wie es bei einer bevorzugten Ausführungsform der Erfindung vorgesehen ist, auch weitere Füllstoffe, insbesondere anorganisches, Skelett bildendes Material, zugesetzt werden. Vorzugsweise werden Metall- oder Halbmetalloxydpartikel verwendet. As particles, as provided in a preferred embodiment of the invention, other fillers, in particular inorganic, skeleton-forming material may be added. Preferably, metal or Halbmetalloxydpartikel be used.

Die Partikel haben vorzugsweise eine Größe von 0,5 bis 200 nm, besonders bevorzugt von 4 bis 150 nm. Weiter ist auch denkbar, Partikel mit einer mittleren Partikelgröße von 10 bis 50 nm zuzusetzen. Diese können insbesondere auch über die Sol-Gel-Vorstufe erzeugt werden. The particles preferably have a size of from 0.5 to 200 nm, particularly preferably from 4 to 150 nm. It is also conceivable to add particles having an average particle size of from 10 to 50 nm. These can also be generated in particular via the sol-gel precursor.

Gemäß einer bevorzugten Ausführungsform der Erfindung umfasst das Beschichtungsmaterial Partikel mit einer ketten- und/oder faserförmigen Morphologie. According to a preferred embodiment of the invention, the coating material comprises particles having a chain and / or fibrous morphology.

Unter einer ketten- oder faserförmigen Morphologie werden Partikel verstanden, deren Größe entlang ihrer Haupterstreckungsrichtung mindestens doppelt, vorzugsweise dreimal, so groß ist wie die Größe entlang der geringsten Ausdehung des Partikels, was wiederum im Durchschnitt für die verwendeten Partikel gilt. A chain or fibrous morphology refers to particles whose size along their main extension direction is at least twice, preferably three times, the size along the smallest dimension of the particle, which in turn applies on average to the particles used.

Im Fall von Partikel mit einer kettenförmigen Morphologie handelt es sich um Sekundärpartikel, welche aus einer Mehrzahl aneinander gereihter kleinerer Primärpartikel bestehen. Es versteht sich, dass die Partikel zumindest teilweise verzweigt sein können. In the case of particles with a chain-like morphology, they are secondary particles which consist of a multiplicity of smaller primary particles arranged next to each other. It is understood that the particles may be at least partially branched.

Insbesondere können Nanopartikel mit einer durchschnittlichen Länge von 50 bis 150 nm und einer durchschnittlichen Größe von 5 bis 25 nm verwendet. Die Größe kann mittels rasterelektronischer Aufnahmen bestimmt werden, wie im Folgenden noch detailliert beschrieben wird. In particular, nanoparticles having an average length of 50 to 150 nm and an average size of 5 to 25 nm may be used. The size can be determined by means of scanning electronical recordings, as will be described in detail below.

Wird die Partikelgröße von bevorzugt verwendeten kettenförmigen Nanopartiklen in einer 0,05 mass-% Dispersion mit der Methode der dynamischen Lichtstreuung (DLS) bestimmt (Gerät: Deltanano HC; Auswertung nach der Methode von Conten) so liegt die Partikelgröße bei ca. 91 nm mit einer sehr breiten Verteilung und einer Standardabweichung von ca. 70 nm. Der Durchmesser der Primärpartikel liegt bei den im REM (Rasterelektronenmikroskop) den vermessen Kettenförmigen Partikeln bei ca. 15 nm. If the particle size of preferably used chain-shaped nanoparticles in a 0.05% by mass dispersion is determined by the dynamic light scattering method (apparatus: Deltanano HC, evaluation according to the method of Conten), the particle size is about 91 nm a very broad distribution and a standard deviation of about 70 nm. The diameter of the primary particles is in the SEM (scanning electron microscope) the measured chain-shaped particles at about 15 nm.

DLS – Messungen an Dispersionen mit keinen Kettenförmigen Sekundär-Partiklen, bestehend nur aus entsprechend Kugelförmigen Primärpartikeln (Durchmesser von ca. 15 nm im REM) zeigen dagegen einen Durchmesser von 38 nm bei einer Standardabweichung von ca. 14 nm. DLS measurements on dispersions with no chain-shaped secondary particles, consisting only of correspondingly spherical primary particles (diameter of about 15 nm in the SEM) show a diameter of 38 nm with a standard deviation of about 14 nm.

Bei einer Ausführungsform sind die Füllpartikel aus nicht Farb-gebendem Material, wie beispielsweise Siliziumoxid, Zirkonoxid oder Aluminiumoxid. In one embodiment, the filler particles are of non-colorant material, such as silica, zirconia or alumina.

Weiter ist auch denkbar, Polysiloxan-Nanopartikel und Farbgebende nanoskalige Pigmente zuzusetzen. It is also conceivable to add polysiloxane nanoparticles and coloring nanoscale pigments.

Im Falle der Verwendung von Farb-gebenden Pigmentpartikeln und nicht Farb-gebenden Gerüst-bildenden Bestandteilen beträgt das Massenverhältnis von Farb-bildenden Bestandteilen zu nicht Farb-gebenden Bestandteilen 0,02 bis 5, bevorzugt 0,3 bis 2, besonders bevorzugt 0,6 bis 1,2. Das Volumenverhältnis von Farb-gebenden Gerüst-bildenden Bestandteilen zu nicht Farb-gebenden Gerüst-bildenden Bestandteilen liegt bei einer Ausführungsform der Erfindung bei 0,01 bis 3,5, bevorzugt bei 0,2 bis 1,5 und besonders bevorzugt bei 0,4 bis 1,0. In the case of using color-providing pigment particles and non-color-providing framework-forming constituents, the mass ratio of color-forming constituents to non-color-providing constituents is 0.02 to 5, preferably 0.3 to 2, particularly preferably 0.6 to 1.2. The volume ratio of color-providing framework-forming constituents to non-color-providing framework-forming constituents in one embodiment of the invention is from 0.01 to 3.5, preferably from 0.2 to 1.5 and particularly preferably 0.4 to 1.0.

Die Dichte des Gerüst-bildenden Materials, insbesondere des aus nanoskaligen Partikeln aufgebauten Gerüst-bildenden Materials, liegt bei einer bevorzugten Ausführungsform der Erfindung zwischen 2,0 und 6 g/cm3, bevorzugt bei 3 bis 4 g/ cm3. Die Skelettdichte kann über He-Pyknometrie bestimmt werden. The density of the scaffold-forming material, in particular of the scaffold-forming material composed of nanoscale particles, in a preferred embodiment of the invention is between 2.0 and 6 g / cm 3 , preferably between 3 and 4 g / cm 3 . Skeletal density can be determined by He-pycnometry.

Das Skelett-bildende Material, also das Material über das die Porosität bereitgestellt wird, besteht in einer Ausführungsform zumindest teilweise aus Oxiden, welche als Zersetzungsprodukte aus molekulardispersen Sol-Gel-Vorstufen entstanden sind. In one embodiment, the skeleton-forming material, that is to say the material via which the porosity is provided, consists at least partially of oxides which have been formed as decomposition products of molecular-disperse sol-gel precursors.

Dies können beispielsweise Zersetzungsprodukte von Alkoxysilanen oder Alkoxyzirkonaten sein (GPTES: Glycidyloxypropyltriethoxysilan, TEOS: Tetraethoxysilan, MTEOS: Methyltriethoxysilan, PhTEOS: Phenyltrithoxysilan, MPTES: Methacryloxypropyltriethoxysilan, MPTMS: Methacryloxypropyltrimethoxysilan, VTES: Venyltriethoxysilan, ATES: Allytriethoxysilan, Zirkontetrapropylat, Titantetraethylat, Aluminiumsecundärbutylat). This can, for example, decomposition products of alkoxysilanes or Alkoxyzirkonaten be (GPTES: glycidyloxypropyltriethoxysilane, TEOS: tetraethoxysilane, MTEOS: methyltriethoxysilane, PhTEOS: Phenyltrithoxysilan, MPTES: methacryloxypropyltriethoxysilane, MPTMS: methacryloxypropyltrimethoxysilane, VTES: Venyltriethoxysilan, ATES: Allytriethoxysilan, zirconium tetrapropylate, titanium tetraethylate, Aluminiumsecundärbutylat).

Bevorzugt werden als Skelett-bildendes Matrixmaterial kristalline und/oder glasige anorganische Materialien verwendet. The skeleton-forming matrix material used is preferably crystalline and / or glassy inorganic materials.

Die Sol-Gel-Schicht wird vorzugsweise mittels Siebdruck aufgebracht. The sol-gel layer is preferably applied by screen printing.

Auf die Sol-Gel-Schicht, welche zunächst getrocknet bzw. eingebrannt wird, um ein Skelett auszubilden, wird eine Polymerschicht aufgebracht, wobei die Sol-Gel-Schicht durch das Material der Polymerschicht infiltriert wird. A polymer layer is applied to the sol-gel layer, which is first baked to form a skeleton, whereby the sol-gel layer is infiltrated by the material of the polymer layer.

Überraschenderweise hat sich gezeigt, das auch eine Sol-Gel-Schicht mit einem mittleren Porendurchmesser von unter 100 nm, welche insbesondere bei Porositätsmessungen durch Stickstoffadsorption als dichte Schicht scheint, durch ein Polymermaterial durchsetzt wird, dass eine dichte Kompositschicht entsteht. It has surprisingly been found that a sol-gel layer with an average pore diameter of less than 100 nm, which appears as a dense layer in particular in the case of measurements of porosity by nitrogen adsorption, is penetrated by a polymer material, so that a dense composite layer is formed.

Die Polymerschicht hat vorzugsweise eine Hitzebeständigkeit bei 1 Stunde Belastungsdauer von über 200 °C, bevorzugt über 300 °C, ganz besonders bevorzugt über 400 °C. Insbesondere werden Polysiloxane, insbesondere Silkonfarben wie beispielsweise Methyl- oder Phenylsilikon-Harze verwendet. Denkbar ist aber auch, für die Polymerschicht ein anderes Sol-Gel-Material zu verwenden. The polymer layer preferably has a heat resistance at 1 hour loading time of over 200 ° C, preferably above 300 ° C, most preferably above 400 ° C. In particular, polysiloxanes, especially silicone inks such as methyl or phenyl silicone resins are used. It is also conceivable to use a different sol-gel material for the polymer layer.

Die Erfinder haben herausgefunden, dass sich über eine Kombination einer teilweise anorganisch ausgebildeten Schicht, welche mit einem Polymermaterial verfüllt wird, ein homogener dichter Schichtverbund bereitstellen lässt, der hochglänzend ausgebildet sein kann und weit weniger als bekannte Sol-Gel-Schichten zu Rissbildungen bei Temperaturbeanspruchung neigt. The inventors have found that a combination of a partially inorganically formed layer which is filled with a polymer material can provide a homogeneous dense layer composite which can be of high gloss and far less prone to cracking under temperature stress than known sol-gel layers ,

Vielmehr ist der Farbort vor und nach thermischer Belastung hochglänzend, insbesondere mit einem Glanzgrad von G1 nach EN ISO 2813 . Rather, the color is before and after thermal stress high gloss, especially with a gloss of G1 after EN ISO 2813 ,

Aufgrund der Dichte neigt der Schichtverbund auch beim Kontakt mit Schmutzstoffen oder deren Zersetzungsprodukten nicht zu lokalen Verfärbungen. Due to the density of the layer composite does not tend to local discoloration even when in contact with contaminants or their decomposition products.

Besonders gut lassen sich schwarze Schichten bereitstellen, insbesondere mit einem Wert L im Lab-Farbraum von weniger als 28,0, bevorzugt von weniger als 27,5 und besonders bevorzugt von weniger als 27,0. Black layers can be provided particularly well, in particular with a value L in the Lab color space of less than 28.0, preferably less than 27.5 and particularly preferably less than 27.0.

Die Skelettdichte der pigmentierten Polymerschicht im erfindungsgemäß hergestellten homogenen Kompositmaterial beträgt bei einer bevorzugten Ausführungsform 1,3 bis 5g/cm3, bevorzugt 1,5 bis 4,0 g/cm3 und besonders bevorzugt 1,8 bis 3,0 g/cm3. The skeletal density of the pigmented polymer layer in accordance with the invention homogeneous composite material is in a preferred embodiment from 1.3 to 5 g / cm 3, preferably 1.5 to 4.0 g / cm 3 and particularly preferably 1.8 to 3.0 g / cm 3 ,

Das Material der Polymerschicht durchdringt das Skelettbildende Material der Sol-Gel-Schicht nahezu homogen und auf nanoskaliger Dimension. The material of the polymer layer penetrates the skeletal forming material of the sol-gel layer almost homogeneously and on a nanoscale dimension.

Die Skelettdichte des durchdringenden polymeren Materials liegt Kompositmaterial bei einer bevorzugten Ausführungsform bei 1,0 bis 2,5 g/cm3, bevorzugt bei 1,3 bis 2,2 g/cm3 und besonders bevorzugt bei 1,5 bis 1,9 g/cm3. The skeletal density of the penetrating polymeric material in one preferred embodiment is 1.0 to 2.5 g / cm 3 , preferably 1.3 to 2.2 g / cm 3, and more preferably 1.5 to 1.9 g / cm 3 .

Als Polymermaterial werden insbesondere auch fluorierte Polymere und/oder Polysiloxane oder Sol-Gel-abgeleitete Hybridpolymere verwendet. Insbesondere können Methyl- oder Phenyl-substituierte Sol-Gel-Materialien oder Polysiloxane verwendet werden. In einer besonderen Ausführungsform wird ein Hochtemperatur-beständiges Methylphenylpolysiloxanharz und ein Siliziumoxid-haltiges Methylsiloxanharz verwendet. Denkbar sind aber auch Epoxid und/oder Polyester und/oder Methacrylat und/oder Phenyl-substituierte Siloxane. Fluorinated polymers and / or polysiloxanes or sol-gel-derived hybrid polymers are also used in particular as polymer material. In particular, methyl- or phenyl-substituted sol-gel materials or polysiloxanes can be used. In a particular embodiment, a high temperature resistant methylphenyl polysiloxane resin and a silica containing methyl siloxane resin are used. However, epoxide and / or polyester and / or methacrylate and / or phenyl-substituted siloxanes are also conceivable.

Das Volumenverhältnis des Materials der ersten Schicht zum Material der Polymerschicht beträgt dem hergestellten Verbundmaterial bei einer bevorzugten Ausführungsform der Erfindung 10 bis 0,5, bevorzugt 4 bis 1, besonders bevorzugt 3 bis 1,5. The volume ratio of the material of the first layer to the material of the polymer layer in a preferred embodiment of the invention is 10 to 0.5, preferably 4 to 1, particularly preferably 3 to 1.5, of the composite material produced.

Bei einer weiteren Ausführungsform der Erfindung wird auch das Material der Polymerschicht mit Füllstoffen und/oder Pigmenten versetzt. Vorzugsweise haben Füllstoffe und/oder Pigmente eine mittlere Partikelgröße von 100 nm bis 2 µm. Reine Füllstoffe können Partikelgrößen zwischen 1 nm und 300 µm annehmen. In a further embodiment of the invention, the material of the polymer layer is also mixed with fillers and / or pigments. Preferably, fillers and / or pigments have an average particle size of 100 nm to 2 microns. Pure fillers can assume particle sizes between 1 nm and 300 μm.

Als Füllstoffe können insbesondere Silica-Partikel, Alumina-Partikel, pyrogene Kieselsäuren, Kalk-Natron-, Alkali-Alumosilicat- und/oder Borosilicatglaskugeln und/oder Glashohlkugeln verwendet werden. Silica particles, alumina particles, fumed silicas, soda lime, alkali aluminosilicate and / or borosilicate glass spheres and / or glass hollow spheres can be used in particular as fillers.

Als Pigmente können insbesondere verwendet werden: plättchen- oder stäbchenförmige Pigmente, beschichtete Effektpigmente und Absorptionspigmente (Cobalt-Oxide/-Spinelle, Cobalt-Aluminium-Spinelle, Cobalt-Titan-Spinelle, Cobalt-Chorm-Spinelle, Cobalt-Nickel-Mangan-Eisen-Chrom-Oxide / -Spinelle, Cobalt-Nickel-Zink-Titan-Aluminium-Oxide/ -Spinelle, Eisen-Oxide, Eisen-Chrom-Oxide, Eisen-Chrom-Zink-Titan-Oxid, Kupfer-Chrom-Spinelle, Nickel-Chrom-Antimon-Titan-Oxide, Titan-Oxide, Zirkon-Silizium-Eisen-Oxide / -Spinelle etc.). Pigments which can be used in particular are: platelet- or rod-shaped pigments, coated effect pigments and absorption pigments (cobalt oxides / spinels, cobalt-aluminum spinels, cobalt-titanium spinels, cobalt-chorm spinels, cobalt-nickel-manganese-iron Chromium oxide / spinel, cobalt-nickel-zinc-titanium-aluminum oxide / spinel, iron oxide, iron-chromium oxide, iron-chromium-zinc-titanium oxide, copper-chromium spinel, nickel Chromium-antimony-titanium oxides, titanium oxides, zirconium-silicon-iron oxides / spinels, etc.).

Insbesondere die Verwendung von plättchenförmigen Pigmenten im Material der Polymerschicht kann dazu führen, dass Partikel und Füllstoffe des Materials der porösen Schicht zumindest teilweise abgedeckt werden. In particular, the use of platelet-shaped pigments in the material of the polymer layer can lead to particles and fillers of the material of the porous layer being at least partially covered.

Die poröse Schicht nach einer thermischen Behandlung von 400 °C hat bei einer bevorzugten Ausführungsform der Erfindung eine offene Porosität von über 10 %, vorzugsweise von über 20 %, besonders bevorzugt von über 25 %. Das Schichtgefüge der nicht infiltrierten Schicht weist nach thermischer Behandlung bei 400 °C sowohl Mikro als auch Mesoporen auf mit einem mittleren Porendurchmesser von 1–6 nm auf. The porous layer after a thermal treatment of 400 ° C has an open porosity in a preferred embodiment of the invention greater than 10%, preferably greater than 20%, most preferably greater than 25%. The layer structure of the non-infiltrated layer after thermal treatment at 400 ° C has both micro and mesopores with an average pore diameter of 1-6 nm.

Der mittlere Porendurchmesser wird dabei aus den Adsorptionskurven nach der BJH-methode aus der N2-Sorption ermittelt. The mean pore diameter is determined from the adsorption curves according to the BJH method from the N2 sorption.

Die offene Porosität wird dabei an abgekratzten Schichten welche nicht infiltriert worden sind aber mit identischen Parametern prozessiert worden sind, mittels der Methode der N2-Sorption und der He-Pyknometrie bestimmt. Aus dem Porenvolumen (N2-Sorption) und der Skelettdichte (He-Pyknometrie) wird anschließend die offene Porosität errechnet. The open porosity is determined on scraped layers which have not been infiltrated but processed with identical parameters by means of the N2 sorption and He pycnometry methods. From the pore volume (N2 sorption) and the skeletal density (He pycnometry), the open porosity is then calculated.

Das erfindungsgemäß hergestellte Verbundmaterial, welches eine Kompositschicht umfasst, die ein überwiegend anorganisches Gerüst mit Pigmentpartikeln umfasst, das seinerseits nanoskalige Poren umfasst, die mit einem Polymer aufgefüllt sind, hat vorzugsweise eine geschlossene Porosität von weniger als 20 Vol-%, besonders bevorzugt von weniger als 5 Vol- %. The composite material produced according to the invention comprising a composite layer comprising a predominantly inorganic framework with pigment particles, which in turn comprises nanoscale pores filled with a polymer, preferably has a closed porosity of less than 20% by volume, more preferably less than 5% by volume.

Die offene Porosität wird dabei an abgekratzten Komposit-Schichten mittels der Methode der N2-Sorption und der He-Pyknometrie bestimmt. Aus dem Porenvolumen und der Skelettdichte wird anschließend die offene Porosität errechnet. Als offene Porosität wird die Porosität bezeichnet, welche man aus den Porenvolumen errechnet, die über N2-Sorption messbar sind. The open porosity is determined on scratched composite layers using the method of N 2 sorption and He-pycnometry. From the pore volume and skeletal density, the open porosity is then calculated. Open porosity refers to the porosity, which is calculated from the pore volumes, which can be measured by N 2 sorption.

In einer weiteren Ausführungsform der Erfindung wird die hergestellte Kompositschicht von weiteren Schichten überdeckt. Insbesondere können pigmentierte Sol-Gel-Schichten oder Polysiloxanschichten verwendet werden. In a further embodiment of the invention, the composite layer produced is covered by further layers. In particular, pigmented sol-gel layers or polysiloxane layers can be used.

Neben der bevorzugten Verwendung als Unterseitenbeschichtung für eine Glaskeramikkochfläche eignet sich die Erfindung auch zur Glasscheibenbedruckung, beispielsweise für Backofenscheiben und Kaminsichtscheiben. In addition to the preferred use as a bottom coating for a glass ceramic cooking surface, the invention is also suitable for Glasscheibenbedruckung, for example, for oven panes and fireplace viewing windows.

Beschreibung der Zeichnungen Description of the drawings

Die Erfindung soll im Folgenden Bezug nehmend auf die Zeichnungen 1 bis 6 anhand schematisch dargestellter Ausführungsbeispiele näher erläutert werden. The invention will be described below with reference to the drawings 1 to 6 be explained in more detail with reference to schematically illustrated embodiments.

1 zeigt ein zur Illustration schematisch dargestelltes Verbundmaterial 1 mit einer erfindungsgemäß aufgebrachten Kompositschicht. Auf ein Glaskeramiksubstrat 2 ist eine Kompositschicht aufgebracht, die aus einer porösen Schicht besteht, welche mit einer Polymerschicht aufgefüllt wurde. 1 shows a schematically illustrated for illustration composite material 1 with a composite layer applied according to the invention. On a glass ceramic substrate 2 is applied a composite layer consisting of a porous layer which has been filled with a polymer layer.

Die Kompositschicht umfasst färbenden Pigmentpartikel 3. Die Pigmentpartikel 3 dienen gleichzeitig der Ausbildung eines porösen Skeletts. Beispielsweise kann ein Mangan-Ferrit-Spinell mit einer mittleren Partikelgröße von weniger als 100 nm verwendet werden. The composite layer comprises coloring pigment particles 3 , The pigment particles 3 simultaneously serve to form a porous skeleton. For example, a manganese ferrite spinel having an average particle size of less than 100 nm can be used.

Weiter umfasst das Material der zunächst als Sol-Gel-Schicht aufgebrachten ersten Schicht nicht färbende Füllstoffpartikel, in diesem Ausführungsbeispiel Füllpartikel 4 mit einem mittleren Durchmesser zwischen 15 und 150 nm. Weitere Partikel 5 sind ebenfalls nicht färbende Skelettpartikel aus einer molekularen Sol-Gel-Vorstufe, beispielsweise Siliziumoxid mit granularer Struktur mit einer mittleren Partikelgröße von unter 5 nm aus pyrolisierten und vorher hydrolisierten Hybridpolymeren (beispielsweise GPTES, TEOS). Furthermore, the material of the first layer applied initially as a sol-gel layer comprises non-coloring filler particles, in this embodiment filler particles 4 with a mean diameter between 15 and 150 nm. Other particles 5 are also non-staining skeletal particles of a sol-gel molecular precursor, for example, silica of granular structure having an average particle size of less than 5 nm from pyrolyzed and previously hydrolyzed hybrid polymers (e.g., GPTES, TEOS).

Die Partikel 3, 4, 5 der zuerst aufgebrachten Schicht sind mit einem Polymermaterial 6, in diesem Ausführungsbeispiel mit einem Hochtemperatur-beständigen Polysiloxan aufgefüllt, so dass ein dichtes Kompositmaterial 8 entstanden ist. The particles 3 . 4 . 5 the first applied layer are with a polymeric material 6 , filled in this embodiment with a high-temperature-resistant polysiloxane, so that a dense composite material 8th originated.

In dem hier dargestellten Ausführungsbeispiel wurde das Polymermaterial 6 in einer derart großen Menge aufgebracht, dass über dem Kompositmaterial 8 eine Versiegelungsschicht 9 entstanden ist, die keine Füllstoff-Partikel 4, 5 und Pigementpartikel 3 des Materials der ersten porösen Schicht enthält. In the embodiment shown here, the polymer material 6 applied in such a large amount that over the composite material 8th a sealing layer 9 has emerged that no filler particles 4 . 5 and pigment particles 3 of the material of the first porous layer.

Vielmehr wurde das Polymermaterial 6 mit größeren plättchenförmigen Pigmenten versetzt, welche sich als zusätzliche Schicht über die Partikel der ersten Schicht legen. Es ist mithin eine Versiegelungsschicht 9 entstanden. Rather, the polymer material became 6 added with larger platelet-shaped pigments, which lay as an additional layer over the particles of the first layer. It is therefore a sealing layer 9 emerged.

2a und 2b zeigen anhand eines Flussbildes die wesentlichen Verfahrensschritte eines Ausführungsbeispiels der Erfindung. 2a and 2 B show on the basis of a flow chart, the essential steps of an embodiment of the invention.

Zunächst wird ein Glaskeramiksubstrat bereitgestellt. Sodann wird eine pigmentierte Sol-Gel-Schicht aufgebracht. Die Sol-Gel-Schicht wird getrocknet bzw. gehärtet und wahlweise (2b) bei einer Temperatur über 350 °C eingebrannt, dabei entsteht ein durch die Silikonfarbe infiltrierbares teilweise nanoskalig-poröses, teilweise anorganisch ausgebildetes Gerüst. First, a glass-ceramic substrate is provided. Then a pigmented sol-gel layer is applied. The sol-gel layer is dried or hardened and optionally ( 2 B ) baked at a temperature above 350 ° C, thereby forming a infiltratable by the silicone paint partially nanoscale-porous, partially inorganic scaffold.

Sodann wird eine pigmentierte Silikonfarbe aufgebracht und der so entstandene Schichtverbund, bei dem die Silikonfarbe die nanoskaligen Poren der Sol-Gel-Schicht auffüllt, wird bei einer Temperatur von über 300°C eingebrannt. Es versteht sich, dass dabei auch organische Bestandteile, insbesondere der Sol-Gel-Schicht entfernt werden können. Die verwendete Silikonfarbe sollte aber eine Temperaturstabilität zum Einbrennen des Schichtverbundes aufweisen. Then, a pigmented silicone paint is applied and the resulting composite layer in which the silicone ink fills the nanoscale pores of the sol-gel layer is baked at a temperature of about 300 ° C. It is understood that It also organic components, in particular the sol-gel layer can be removed. However, the silicone paint used should have a temperature stability for baking the layer composite.

3 zeigt eine Tabelle mit einer Zusammensetzung des verwendeten Sol-Gel-Beschichtungsmaterials in einer einfachen sowie in bevorzugten und besonders bevorzugten Ausführungsvarianten. 3 shows a table with a composition of the sol-gel coating material used in a simple as well as in preferred and particularly preferred embodiments.

Der Hybridpolymerlack weist zum Einen Binderkomponenten auf, welche ein Sol-Gel-Hydrolysat, Nanopartikel umfassen. The hybrid polymer lacquer has, on the one hand, binder components which comprise a sol-gel hydrolyzate, nanoparticles.

Als färbende Bestandteile werden anorganische Pigmente zugesetzt. As coloring ingredients inorganic pigments are added.

Weiter umfasst der Hybridpolymerlack ein hoch siedendes Lösungsmittel. Further, the hybrid polymer varnish comprises a high-boiling solvent.

Optional können Starter, organische Vernetzer und Additive in der genannten Menge zugesetzt werden. Optionally, starters, organic crosslinkers and additives in the stated amount can be added.

4 zeigt eine rasterelektronenmikroskopische Aufnahme eines Ausführungsbeispiels einer getrockneten Hybridpolymerschicht, welche als erste Schicht aufgetragen, aber noch nicht von einem Polymer infiltriert wurde. 4 shows a scanning electron micrograph of an embodiment of a dried hybrid polymer layer, which was applied as a first layer, but has not been infiltrated by a polymer.

Insbesondere aufgrund zugesetzter nanoskaliger Partikel ist eine infiltrierbare Schicht entstanden. In particular due to added nanoscale particles, an infiltratable layer has formed.

5 zeigt diese Schicht nach dem Aufbringen eines Polysiloxans. Die Struktur der ersten Schicht ist weiterhin gut zu erkennen. Die erste Schicht wurde vom Polysiloxan infiltriert, eine dichte Kompositschicht ist entstanden. 5 shows this layer after the application of a polysiloxane. The structure of the first layer is still easy to recognize. The first layer was infiltrated by the polysiloxane, creating a dense composite layer.

6 zeigt die in 5 gezeigte Kompositschicht nach einer Temperaturbelastung von über 500 °C. Die in 5 zu erkennen Struktur ist weitgehend erhalten geblieben. Die Schicht ist mithin temperaturstabil bis über 500 °C. 6 shows the in 5 shown composite layer after a temperature load of about 500 ° C. In the 5 to recognize structure has largely been preserved. The layer is therefore thermally stable up to over 500 ° C.

7 zeigt die in 4 dargestellte Schicht ohne Silikoninfiltrierung nach einer thermischen Behandlung nach 400 °C. Es ist eine poröse Schicht ohne infiltriertes Silikonharz entstanden. 7 shows the in 4 shown layer without Silikoninfiltrierung after a thermal treatment after 400 ° C. It is a porous layer without infiltrated silicone resin.

Im Konkreten kann ein erfindungsgemäßes Verbundmaterial wie folgt hergestellt werden: Concretely, a composite material according to the invention can be produced as follows:

Beispiel 1: Example 1:

Es werden zunächst 4 mol MPTES (Methacryloxypropyltriethoxysilan) mit 1 mol TEOS und 2,3g H2O, in welchem 0,344 g Paratoluolsulfonsäure gelöst sind, hydrolisiert. Von dem Gemisch wird anschließend am Rotationsverdampfer das Lösungsmittel entfernt und das sog. Hydrolysat erhalten. 4 mol of MPTES (methacryloxypropyltriethoxysilane) are first hydrolyzed with 1 mol of TEOS and 2.3 g of H 2 O in which 0.344 g of paratoluenesulphonic acid are dissolved. The solvent is then removed from the mixture on a rotary evaporator and the so-called hydrolyzate is obtained.

18 g des Hydrolysates werden anschließend mit 55 g einer 35 Mass-%igen Lösung von kettenförmigen SiO2-Nanopartikeln in Diethylenglycolmonoethylether versetzt. Zu dieser Lösung werden anschließend 30 g eines nanoskaligen (< 100 nm) Schwarzpigmentes (Manganferrit-Spinell) gegeben.. Then, 55 g of a 35% by mass solution of chain-shaped SiO 2 nanoparticles in diethylene glycol monoethyl ether are added to 18 g of the hydrolyzate. Then 30 g of a nanoscale (<100 nm) black pigment (manganese ferrite spinel) are added to this solution.

Die Farbe wird mittels einer Dissolverscheibe homogen verrührt. The color is stirred homogeneously by means of a dissolver disc.

Die Farbe wird dann mittels eines 140er Siebes auf eine transparente Glaskeramik aufgedruckt und anschließend bei 170°C für 1 Stunde getrocknet. Die später ein nanoskaliges Gerüst ausbildende Komponente ist damit nun aufgebracht. The color is then printed on a transparent glass ceramic by means of a 140 sieve and then dried at 170 ° C. for 1 hour. The later a nanoscale scaffolding forming component is now applied.

Dann wird auf die erste Schicht eine zweite Schicht mit der infiltrierenden Komponente ebenfalls über Siebdruck aufgebracht. Hierfür wird eine Silikonfarbe auf Basis eines Methyl/Phenylsilikonharzes gelöst in Xylol verwendet. (REN 80 von Wacker). Der Silikonfarbe sind dabei 22 Mass-% von glimmerförmigen Pigmenten mit einer mittleren Partikelgröße von 15 µm zugeben. Für den Siebdruck der infiltrierenden Komponente wird ein 77er Sieb verwendet. Then, a second layer with the infiltrating component is also applied to the first layer by screen printing. For this purpose, a silicone ink based on a methyl / phenyl silicone resin dissolved in xylene is used. (REN 80 from Wacker). The silicone paint is 22% by mass of mica pigments with an average particle size of 15 microns admit. For the screen printing of the infiltrating component, a sieve of 77 is used.

Anschließend wird das gesamte Schichtpaket bei 380°C für 1 Stunde eingebrannt. Subsequently, the entire layer package is baked at 380 ° C for 1 hour.

Es wird dabei ein Glaskeramiksubstrat mit einer dichten homogenen Kompositschicht, überdeckt von einer pigmentierten Silikonschicht, hergestellt. In this case, a glass-ceramic substrate with a dense homogeneous composite layer, covered by a pigmented silicone layer, is produced.

Beispiel 2: Example 2:

Es werden zunächst 4 mol GPTES (Glycidoxypropyltriethoxysilan) mit 1 mol TEOS und 2,3 g H2O, in welchem 0,344 g Paratoluolsulfonsäure gelöst sind, hydrolisiert. Von dem Gemisch wird anschließend am Rotationsverdampfer das Lösungsmittel entfernt und das sog. Hydrolysat erhalten. 4 mol of GPTES (glycidoxypropyltriethoxysilane) are first hydrolyzed with 1 mol of TEOS and 2.3 g of H 2 O in which 0.344 g of paratoluenesulphonic acid are dissolved. The solvent is then removed from the mixture on a rotary evaporator and the so-called hydrolyzate is obtained.

18 g des Hydrolysates werden anschließend mit 55 g einer 35 Mass-%igen Lösung von kettenförmigen SiO2-Nanopartikeln in Diethylenglycolmonoethylether versetzt. Zu dieser Lösung werden anschließend 30 g eines nanoskaligen (< 100 nm) Schwarzpigmentes (Manganferrit-Spinell) gegeben. Then, 55 g of a 35% by mass solution of chain-shaped SiO 2 nanoparticles in diethylene glycol monoethyl ether are added to 18 g of the hydrolyzate. Then 30 g of a nanoscale (<100 nm) black pigment (manganese ferrite spinel) are added to this solution.

Die Farbe wird mittels einer Dissolverscheibe homogen verrührt. The color is stirred homogeneously by means of a dissolver disc.

Die Farbe wird dann mittels eines 140er Siebes auf eine transparente Glaskeramik aufgedruckt und anschließend bei 170°C für 1 Stunde getrocknet und die Schicht bei 400 °C eingebrannt. Die später das nanoskalige Gerüst ausbildende Komponente ist damit aufgebracht. The color is then printed on a transparent glass ceramic by means of a 140 sieve and then dried at 170 ° C. for 1 hour and the layer is baked at 400 ° C. The later the nanoscale scaffolding-forming component is thus applied.

Dann wird auf die erste Schicht eine zweite Schicht mit der infiltrierenden Komponente ebenfalls über Siebdruck aufgebracht. Hierfür wird eine Silikonfarbe auf Basis eines Methyl/Phenylsilikonharzes, gelöst in Xylol, verwendet (DC 805 von Dow Corning). Der Silikonfarbe sind dabei 30 Mass-% von glimmerförmigen Pigmenten mit einer mittleren Partikelgröße von 15 µm zugeben. Für den Siebdruck der infiltrierenden Komponente wird ein 77er Sieb verwendet. Then, a second layer with the infiltrating component is also applied to the first layer by screen printing. For this purpose, a silicone ink based on a methyl / phenylsilicone resin, dissolved in xylene, is used (DC 805 from Dow Corning). The silicone paint is thereby 30% by mass of mica pigments with an average particle size of 15 microns admit. For the screen printing of the infiltrating component, a sieve of 77 is used.

Anschließend wird das gesamte Schichtpaket bei 420°C für 1 Stunde eingebrannt. Subsequently, the entire layer package is baked at 420 ° C for 1 hour.

Es wird dabei ein Glaskeramiksubstrat mit einer dichten homogenen Kompositschicht, überdeckt von einer pigmentierten Silikonschicht, erhalten. In this case, a glass-ceramic substrate having a dense homogeneous composite layer, covered by a pigmented silicone layer, is obtained.

Durch die Erfindung konnte ein Verfahren bereitgestellt werden, mit dem sich auf sehr einfache Weise hitzebeständige dekorative Beschichtungen mit nahezu beliebigen Farbort auf einem Glaskeramiksubstrat aufbringen lassen. By means of the invention, it was possible to provide a method with which heat-resistant decorative coatings with virtually any color location can be applied to a glass-ceramic substrate in a very simple manner.

ZITATE ENTHALTEN IN DER BESCHREIBUNG QUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Zitierte Nicht-PatentliteraturCited non-patent literature

  • EN ISO 2813 [0038] EN ISO 2813 [0038]

Claims (17)

Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung, umfassend die Schritte: – Bereitstellen eines Glas- oder Glaskeramiksubstrats, – Aufbringen einer Sol-Gel-Schicht, welcher zumindest Pigmentpartikel und Oxidpartikel- zugesetzt werden, – Aufbringen einer Polymerschicht auf die Sol-Gel-Schicht, wobei Sol-Gel-Schicht durch das Material der Polymerschicht infiltriert wird.  A method of producing a decorative coating composite comprising the steps of: Providing a glass or glass ceramic substrate, Applying a sol-gel layer to which at least pigment particles and oxide particles are added, - Applying a polymer layer on the sol-gel layer, wherein sol-gel layer is infiltrated by the material of the polymer layer. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach dem vorstehenden Anspruch, dadurch gekennzeichnet, dass als Oxidpartikel Nanopartikel verwendet werden, insbesondere SiO2-Nanopartikel. Method for producing a composite material with decorative coating according to the preceding claim, characterized in that nanoparticles are used as oxide particles, in particular SiO 2 nanoparticles. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass dem Sol-Gel Oxidpartikel mit faser- und/oder kettenförmiger Morphologie zugesetzt werden. A method of producing a decorative coating composite material according to any one of the preceding claims, characterized in that oxide particles of fiber and / or chain morphology are added to the sol gel. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass eine Sol-Gel-Schicht mit einer mittleren Porendurchmesser von weniger als 10 nm, bevorzugt weniger als 5 nm aufgebracht wird. A method for producing a decorative coating composite material according to any one of the preceding claims, characterized in that a sol-gel layer having an average pore diameter of less than 10 nm, preferably less than 5 nm, is applied. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Polymerschicht vor einem Einbrand der Sol-Gel-Schicht aufgebracht wird. A method for producing a composite material with a decorative coating according to any one of the preceding claims, characterized in that the polymer layer is applied before a penetration of the sol-gel layer. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass als Material für die Polymerschicht ein Polysiloxan oder Sol-Gel verwendet wird. Method for producing a composite material with decorative coating according to one of the preceding claims, characterized in that a polysiloxane or sol-gel is used as the material for the polymer layer. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach dem vorstehenden Anspruch, dadurch gekennzeichnet, dass für die Polymerschicht eine Silikonfarbe, insbesondere ein Methyl- oder Phenyl-Silikonharz verwendet wird. A method for producing a composite material with decorative coating according to the preceding claim, characterized in that a silicone ink, in particular a methyl or phenyl silicone resin is used for the polymer layer. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass dem Material der Polymerschicht Pigmente, insbesondere plättchenförmige Pigmente, zugesetzt werden. Method for producing a composite material with a decorative coating according to one of the preceding claims, characterized in that pigments, in particular flaky pigments, are added to the material of the polymer layer. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die poröse Schicht und/oder die Polymerschicht mittels Siebdruck aufgebracht werden. Method for producing a composite material with decorative coating according to one of the preceding claims, characterized in that the porous layer and / or the polymer layer are applied by means of screen printing. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass der aus Polymerschicht und die Sol-Gel-Schicht entstandene Verbund thermisch gehärtet wird, insbesondere bei einer Temperatur von über 200 °C. A method for producing a composite material with a decorative coating according to any one of the preceding claims, characterized in that the resulting polymer layer and the sol-gel layer composite is thermally cured, in particular at a temperature of above 200 ° C. Verfahren zum Herstellen eines Verbundmaterials mit dekorativer Beschichtung nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Sol-Gel-Schicht eine mittleren Porendurchmesser zwischen 0,5 und 500 nm, bevorzugt zwischen 1 und 200 nm, besonders bevorzugt zwischen 5 und 100 nm aufweist. Method for producing a composite material with decorative coating according to one of the preceding claims, characterized in that the sol-gel layer has an average pore diameter between 0.5 and 500 nm, preferably between 1 and 200 nm, particularly preferably between 5 and 100 nm , Verbundmaterial mit einer dekorativen Beschichtung, herstellbar, insbesondere hergestellt mit einem Verfahren nach einem der vorstehenden Ansprüche.  Composite material having a decorative coating, preparable, in particular produced by a method according to one of the preceding claims. Verbundmaterial, umfassend ein Glaskeramiksubstrat, wobei auf dem Glaskeramiksubstrat eine Kompositschicht angeordnet ist, die ein überwiegend anorganisches Gerüst mit Pigmentpartikeln umfasst, welches nanoskalige Poren umfasst, die mit einem Polymer aufgefüllt sind.  A composite material comprising a glass-ceramic substrate, wherein on the glass-ceramic substrate a composite layer is arranged, which comprises a predominantly inorganic framework with pigment particles, which comprises nanoscale pores, which are filled with a polymer. Verbundmaterial nach dem vorstehenden Anspruch, dadurch gekennzeichnet, dass es sich bei dem Polymer um ein Polysiloxan handelt. Composite material according to the preceding claim, characterized in that the polymer is a polysiloxane. Verbundmaterial nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Kompositschicht eine geschlossene Porosität von weniger als 20 %, vorzugsweise von weniger als 5 % aufweist. Composite material according to one of the preceding claims, characterized in that the composite layer has a closed porosity of less than 20%, preferably less than 5%. Verbundmaterial nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Beschichtung glänzt, insbesondere mit einem Glanzgrad von G1 nach EN ISO 2813. Composite material according to one of the preceding claims, characterized in that the coating shines, in particular with a gloss of G1 according to EN ISO 2813. Verwendung eines Verbundmaterials nach einem der vorstehenden Ansprüche als Teil eines Kochfeldes, als Kaminsichtscheibe oder Teil einer Backofentür.  Use of a composite material according to any one of the preceding claims as part of a hob, as chimney panel or part of a oven door.
DE201210109808 2012-04-20 2012-10-15 Preparing composite material used in e.g. door of oven, comprises applying of sol gel layer prepared by mixing pigment particle and oxide particle on glass or glass ceramic substrate, and applying polymer layer on sol gel layer Ceased DE102012109808A1 (en)