DE102007014496B3 - Laying good e.g. natural stone tiles, for use in e.g. sanitary room, has surface made of naturally grown crystalline structure that is held together by bonding agent, where crystalline structure has color of naturally grown layer - Google Patents

Laying good e.g. natural stone tiles, for use in e.g. sanitary room, has surface made of naturally grown crystalline structure that is held together by bonding agent, where crystalline structure has color of naturally grown layer Download PDF

Info

Publication number
DE102007014496B3
DE102007014496B3 DE102007014496A DE102007014496A DE102007014496B3 DE 102007014496 B3 DE102007014496 B3 DE 102007014496B3 DE 102007014496 A DE102007014496 A DE 102007014496A DE 102007014496 A DE102007014496 A DE 102007014496A DE 102007014496 B3 DE102007014496 B3 DE 102007014496B3
Authority
DE
Germany
Prior art keywords
color
naturally grown
binder
laying
crystal structure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE102007014496A
Other languages
German (de)
Other versions
DE102007014496B8 (en
Inventor
Damian Dronia
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE202007007508U priority Critical patent/DE202007007508U1/en
Priority to DE102007014496A priority patent/DE102007014496B8/en
Priority to US12/532,251 priority patent/US20100236170A1/en
Priority to EP08717676A priority patent/EP2139700A1/en
Priority to PCT/EP2008/052930 priority patent/WO2008113726A1/en
Publication of DE102007014496B3 publication Critical patent/DE102007014496B3/en
Application granted granted Critical
Publication of DE102007014496B8 publication Critical patent/DE102007014496B8/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The laying good has a surface made of a naturally grown crystalline structure (20) that is held together by a bonding agent. The structure has a color (61) of a naturally grown layer (60) made of minerals, citrine, amethyst, quartz and pyrite. The bonding agent is provided in a space (21) of the crystalline structure, where the bonding agent is a transparent adhesive made of synthetic resin, and the laying good is attached with a mounting plate that is made of a material e.g. glass, plexiglass(RTM: light, transparent, weather-resistant thermoplastic), and ceramics. An independent claim is also included for a method for manufacturing a laying good.

Description

Die Erfindung betrifft eine Verlegeware und ein Verfahren zur Herstellung einer solchen.The The invention relates to an adhesive and a method for the production such.

Gattungsgemäße Verlegeware ist hinreichend bekannt. Beispielsweise sind dies Fliesen, Kacheln, Paneelen etc., die mit einer optisch ansprechenden Schicht beschichtet sein können, die aber auch selbst aus einem optisch ansprechenden Material bestehen können (z. B. Steinzeug, Natursteinfliesen). Verlegeware kann unmittelbar auf die zu beschichtende Fläche aufgebracht werden, sie kann aber auch Trägerplatten oder ähnlichem befestigt werden. Dies ist z. B. dann notwendig, wenn die Unterseite der Verlegeware für eine Befestigung auf einen Untergrund ungeeignet ist.Generic laying materials is well known. For example, these are tiles, tiles, Panels, etc., which are coated with a visually appealing layer could be, but also consist of a visually appealing material can (eg stoneware, natural stone tiles). Laying can be immediate on the surface to be coated but they can also support plates or the like be attached. This is z. B. then necessary if the bottom the laying for An attachment to a substrate is unsuitable.

Die Möglichkeiten derartige Verlegeware in verschiedenen Ausführungsformen und unterschiedlichen farbigen Ausgestaltungen, von schlichten, einfachen Farbgebungen über verschiedene Muster, bis hin zu Malereien, herzustellen, sind in der Praxis bekannt. So offenbart beispielsweise die DE 697 01 983 T2 ein Verfahren, bei dem es möglich ist, Ziersteinmaterialien mit haltbaren bunten Malereien zu dekorieren.The possibilities of producing such types of installations in various embodiments and in different colored configurations, from simple, simple colors to various patterns, to paintings, are known in practice. For example, the DE 697 01 983 T2 a method of decorating ornamental stone materials with durable, colorful paintings.

Ferner sind Herstellungsverfahren von Platten, Fliesen und Panellen aus Agglomeratmaterialien bekannt, die aus verschiedenen Materialien, wie beispielsweise Sand, Quarz, Glas, Keramik, Holz, etc. bestehen und mit Bindemittel aus Harzen gebunden werden. Dabei werden die verschiedenen Materialien zerkleinert, gemischt und mit dem Klebemitteln vermengt. Anschließend wird das Agglomerat gepresst, gehärtet, geschliffen, poliert und zugeschnitten. Als Nachteil erweist sich hierbei, dass die natürlich gewachsenen Strukturen der Ausgangsmaterialien beim Zerkleinern zerstört werden. So ist es nicht möglich verschiedene Oberflächen so zu gestalten, dass diese eine wie in der Natur natürlich vorkommende, kristalline Struktur aufweisen.Further are made from sheets, tiles and panels Agglomerate materials known from various materials, such as sand, quartz, glass, ceramics, wood, etc. exist and bound with binder from resins. Here are the crushed various materials, mixed and with the adhesive mixed. Subsequently The agglomerate is pressed, hardened, ground, polished and tailored. The disadvantage here proves that the naturally grown Structures of the starting materials are destroyed during comminution. This is not possible different surfaces be designed so that they are naturally occurring, as in nature, have crystalline structure.

Ein Mineral ist ein natürlich vorkommender Feststoff mit einer einheitlichen chemischen Zusammensetzung und einem auch auf mikroskopischer Ebene gleichförmigen Aufbau. Die meisten Minerale sind kristallin. Natürlich gewachsene Kristallstrukturen kommen in der Natur häufig in Hohlräumen von Gesteinen vor. Diese können mit Kristallen verschiedener Arten gefüllt sein und werden als Druse oder Geode bezeichnet. Bei der Druse ist die Wand des Hohlraums von Kristallen bedeckt, bei der Geode hingegen ist der gesamte Innenraum von Kristallen ausgefüllt.One Mineral is a natural occurring solid with a uniform chemical composition and a uniform structure even at the microscopic level. Most Minerals are crystalline. Naturally Grown crystal structures often occur in nature cavities of rocks. these can be filled with crystals of different types and be called druse or Geode. In the case of the druse is the wall of the cavity covered by crystals, while the Geode is the entire interior filled with crystals.

In der vorliegenden Anmeldung werden natürlich gewachsenen Kristallstrukturen als Rohstücke, bzw. Stufe bezeichnet. Die Stufen teilen sich in zwei Bereiche auf, einen durchgefärbten Teil und einen nicht durchgefärbten Teil. Der durchgefärbte Teil zeichnet sich wiederum durch seine natürlich gewachsene Krone, mit frei kristallisierten Mineralen aus. Die zeigen äußerlich eine feste geometrische Form mit wohldefinierten natürlichen Flächen, die in festen Winkeln zueinander stehen. Dieser Teil der Stufe wird auch als Farbe bezeichnet, wohingegen der nicht eingefärbte Teil Wurzel genant wird.In of the present application are naturally grown crystal structures as blanks, or step called. The steps are divided into two sections, a through-colored Part and one not colored Part. The through-colored Part is again characterized by its naturally grown crown, with free crystallized minerals. Externally they show a solid geometric shape with well-defined natural surfaces, which are in fixed angles to each other. This part of the stage will also referred to as color, whereas the non-colored part Root is called.

Die oben beschriebenen Rohstücke sind in der Regel zwar sehr dekorativ, allerdings ist eine weitere Verwendung als Dekorationsmaterial, beispielsweise auf Fliesen, Platten und/oder Panellen so gut wie nicht möglich. Im Verhältnis sind die einzelnen Stücke zu groß, bzw. zu dick und weisen ein zu hohes Gewicht auf. Entsprechend besteht ein Interesse daran, den optisch überflüssigen, nicht eingefärbten Teil, also die Wurzel, von dem für Dekorationszwecke interessanten Teil, der Farbe, zu trennen, ohne dabei die natürlich gewachsenen Kristallstrukturen zu zerstören.The above-described blanks are usually very decorative, however, is another Use as decoration material, for example on tiles, Plates and / or panels as good as not possible. In proportion the individual pieces too large, or too thick and have too high a weight. Accordingly exists an interest in the optically superfluous, non-colored part, So the root from which for Decoration purposes interesting part, the color, separate, without the course, of course to destroy grown crystal structures.

Problematisch ist, dass das kristalline Gefüge zerfällt, sobald die Farbe von der Wurzel getrennt wird. Auch verlieren beispielsweise die Kristalle der Amethyststufen spätesten beim anschließenden Brennen den Halt untereinander, so dass auch hier das kristalline Gefüge beim Trennen der Farbe von den Kristallwurzeln zerfällt.Problematic is that the crystalline structure decays, as soon as the color is separated from the root. Also lose, for example the crystals of the amethyst stages latest in the subsequent firing the support among each other, so that here too the crystalline structure at Separating the color from the crystal roots crumbles.

Citrin beispielsweise ist die gelb gefärbte Varietät des Quarzes. Je nach Herkunft des Citrins und Ursache der Färbung variiert der Farbton von blass grünlich gelb über orange bis zu braun orange. Natürliche Citrine sind jedoch selten, so dass im Handel fast ausschließlich künstliche Citrine oder umgefärbte Quarze vertrieben werden. Eine Variante der Citrin Herstellung beruht darauf, dass violette Amethyste beim Erhitzen auf 300 bis ca. 700°C ihre violette Farbe verlieren und sich wie ein Citrin orange-gelb bis braun färben. Da aber die Kristalle der Amethyststufen, wie bereits beschrieben, beim Brennen den Halt untereinander verlieren, ist es nicht möglich künstliche Citrine herzustellen, die ein natürlich gewachsenes zusammenhängendes Gefüge aufweisen.citrine for example, the yellow colored variety of the quartz. Depending on the origin of citrine and cause of staining varies the hue of pale greenish yellow over orange to brown orange. natural However, citrines are rare, leaving almost exclusively artificial ones in trade Citrine or recolored Quartz crystals are distributed. A variant of citrine production is based that purple amethysts when heated to 300 to about 700 ° C their violet Lose color and turn orange-yellow to brown like a citrine. There but the crystals of the amethyst stages, as already described, when firing lose the grip between each other, it is not possible artificial Citrine, which is a naturally grown contiguous structure exhibit.

Im Stand der Technik ist derzeit kein Verfahren bekannt, Verlegeware herzustellen, die die Oberflächenstruktur von natürlich gewachsenen Kristallstrukturen aufweist und für Dekorationszwecke, wie beispielsweise der Weiterverarbeitung mit den oben genannten Platten, Panellen und/oder Fliesen geeignet ist.in the According to the state of the art, no process is currently known produce the surface texture of course has grown crystal structures and for decorative purposes, such as further processing with the above boards, panels and / or tiles is suitable.

Die Aufgabe der vorliegenden Erfindung besteht darin, eine Verlegeware bereitzustellen, die eine natürlich gewachsenen Kristallstruktur aufweist, aber dennoch für eine weiter Verwendung, wie beispielsweise eine Weiterverarbeitung mit den oben genannten Platten, Paneelen und/oder Fliesen geeignet ist.The object of the present invention is to provide a lay-up which has a naturally grown crystal structure but yet for further use, such as further processing with the above said plates, panels and / or tiles is suitable.

Weiterhin ist es Aufgabe der Erfindung, ein Verfahren zur Herstellung einer solchen Verlegeware zu finden.Farther It is an object of the invention to provide a method for producing a to find such materials.

Erfindungsgemäß wird die Aufgabe durch eine Verlegeware und ein Verfahren zur Herstellung einer Verlegeware gelöst, deren Oberfläche aus einer natürlich gewachsenen Kristallstruktur besteht, die durch ein Bindemittel zusammengehalten wird, wobei die Kristallstruktur aus einer Farbe eines natürlich gewachsenen Minerals besteht. Durch das Bindemittel ist es möglich, das Gewicht und die Größe der jeweiligen Kristallstufen zu reduzieren, ohne dass die natürlich gewachsenen Kristallstrukturen auseinanderfallen.According to the invention Task by a Verlegeware and a method for producing a Loosely solved, their surface from a course Grown crystal structure composed by a binder is held together, the crystal structure of a color one of course grown mineral. Due to the binder, it is possible that Weight and size of each To reduce crystal stages without the naturally grown crystal structures fall apart.

Erfindungsgemäß kann die Verlegeware aus verschiedenen Kristallstrukturen, wie beispielsweise der Kristallstrukturen von Citrin, Amethyst, Quarz, Pyrit, etc. bestehen, je nachdem welche Art Kristallstufe bzw. welche Rohrstücke verwendet werden.According to the invention, the Layers made of different crystal structures, such as the Crystal structures of citrine, amethyst, quartz, pyrite, etc. exist, depending on which type crystal stage or which pipe pieces used become.

Vorzugsweise kann das Bindemittel in Zwischenräume der natürlich gewachsenen Kristallstruktur eingebracht werden und ein transparentes Klebemittel aus Kunstharz, wie beispielsweise ein farbloser Zweikomponentenkleber auf Epoxidharzbasis sein.Preferably For example, the binder may be in interstices of the naturally grown crystal structure are introduced and a transparent adhesive made of synthetic resin, such as a colorless two-component adhesive based on epoxy resin be.

In einer weiterführenden Ausführungsform kann die Verlegeware durch ein Bindemittel mit einer Trägerplatte verbunden sein, die aus verschiedenen Materialien, wie beispielsweise Glas, Plexiglas, Keramik bestehen und die unterschiedlichsten Formen und Farben aufweisen kann.In a continuing Embodiment can the laid products by a binder with a carrier plate be connected, made of different materials, such as Glass, Plexiglas, ceramics and the most varied forms and Colors may have.

Vorzugsweise ist die Oberfläche der erfindungsgemäßen Verlegeware durch das Bindemittel versiegelt, so dass sich keine Verunreinigung, wie Keime oder Pilze in den Zwischen räumen bilden kann.Preferably is the surface the laying materials according to the invention sealed by the binder so that no contamination, how germs or fungi can form in the interstices.

Die Kristallgröße der Verlegeware beträgt vorzugsweise 0,2 mm bis 25 cm.The Crystal size of the laid goods is preferably 0.2 mm to 25 cm.

In der vorliegenden Beschreibung werden insgesamt drei vom Erfinder bevorzugte Herstellungsverfahren vorgestellt, die je nach Bedarf anwendbar sind. Mögliche andere Verfahren zur Herstellung erfindungsgemäßer Verlegeware sollen durch die hier beschriebenen Verfahren nicht ausgeschlossen werden.In In the present specification, a total of three are invented by the inventor preferred manufacturing methods are presented as needed are applicable. Possible Other methods for the production of inventive Verlegeware to the methods described here are not excluded.

Bei allen beschriebenen Verfahren steht im Vordergrund, dass durch eine starke Reduzierung des Flächengewichts der Rohware, die oben genannte Aufgabe, eine Verlegeware bereitzustellen, deren Oberfläche die natürlich gewachsenen Kristallstrukturen der Farbe aufweist, erfüllt werden soll.at All the described method is in the foreground, that by a strong reduction of the basis weight the raw material, the above-mentioned object, to provide a Verlegeware whose surface the course grown crystal structures of the color, are met should.

Bevor die einzelnen Kristallstufen verarbeitet werden, sollten sie von eventuellen Verunreinigungen befreit werden. Dies kann in mehreren Schritten erfolgen, in denen beispielsweise eine Nassreinigung und eine anschließende Trocknung vorgesehen ist, damit das zugeführte Restwasser wieder verdunsten kann.Before The individual crystal stages are processed, they should be from any impurities are freed. This can be done in several Steps are carried out in which, for example, a wet cleaning and a subsequent one Drying is provided so that the supplied residual water can evaporate again.

1. Verfahren1. Procedure

Bei diesem Verfahren wird das Bindemittel direkt, z. B. von Oben, in die Zwischenräume der natürlich gewachsenen Kristallstrukturen eingebracht, wobei das Bindemittel vorzugsweise ein transparentes Klebemittel aus Kunstharz, wie beispielsweise ein farbloser Zweikomponentenkleber auf Epoxidharzbasis ist. Das fertige Bindemittel wird vorteilhaft mit Hilfe von dünnen Kanülen in die Zwischenräume der Kristalle gespritzt. Die Kanülen weisen in der Regel eine Innenweite von 0,5 bis 0,8 Millimeter auf, können aber bei Bedarf auch jede andere Innenweite haben. Der für das Ausspritzen des Klebers in die Kristallzwischenräume benötigte Druck wird beispielsweise von einem Perfusor® erzeugt. Grundsätzlich besteht aber auch die Möglichkeit, den Druck manuell zu erzeugen oder andere zweckmäßige Geräte zu verwenden. Dabei dringt das Bindemittel aufgrund der Kappilarwirkung tiefer in die Kristallzwischenräume ein, als die Kanülen selber. Auf diese Weise werden die Kristallzwischenräume bis weit in die Wurzel hinein fest miteinander verbunden.In this method, the binder is directly, for. From the top, into the interstices of the naturally grown crystal structures, wherein the binder is preferably a transparent adhesive of synthetic resin, such as a colorless two-component adhesive based on epoxy resin. The finished binder is advantageously injected with the aid of thin cannulas in the interstices of the crystals. The cannulas generally have an inside width of 0.5 to 0.8 millimeters, but can also have any other internal width if required. The pressure required for the spraying of the adhesive in the crystal interstices is for example generated by a syringe ®. In principle, however, it is also possible to manually generate the pressure or to use other appropriate devices. Due to the capillary effect, the binder penetrates deeper into the interstices of the crystals than the cannulas themselves. In this way, the crystal interstices are firmly interconnected far into the root.

Vor der weiteren Verarbeitung sollten die einzelnen, bereits mit Bindemittel versehenen Rohstufen aushärten. Die mögliche Dauer der Aushärtung hängt dabei von äußeren Umständen, wie beispielsweise der Temperatur, der Luftfeuchte und dem verwendeten Bindemittel ab, liegt aber in der Regel bei circa 24 Stunden. Das Mischungsverhältnis möglicher Bindemittel hängt wiederum von den Herstellerangaben ab und sollte vorteilhafterweise von diesen nicht abweichen.In front Further processing should be the individual, already with binder cure provided raw stages. The possible Duration of curing depends from external circumstances, like for example, the temperature, the humidity and the used Binders, but is usually about 24 hours. The mixing ratio potential Binder hangs turn from the manufacturer's instructions and should be advantageous not deviate from these.

Anschließend können die verbundenen Kristallwurzeln zugeschnitten werden, wobei die natürlich gewachsene Kristallstruktur nicht mehr auseinander fällt. Der Zuschnitt selber erfolgt bevorzugt auf einer Edelsteinsäge. Nach der erfolgten Trennung der Farbe von der Wurzel ist es von Vorteil, wenn die Unterseite, also die von der natürlich gewachsenen Kristallstruktur abgewandten Seite, bzw. die Schnittseite glatt geschliffen und poliert wird, wodurch eine mögliche Weiterverarbeitung der Verlegeware erleichtert wird.Subsequently, the Cropped crystal roots are cut, the naturally grown Crystal structure no longer falls apart. The cutting itself is done preferably on a gemstone saw. After the separation of the color from the root it is from Advantage if the bottom, that is, that of the naturally grown Crystal structure averted side, or the cut side smooth is ground and polished, whereby a possible further processing of Laying is facilitated.

In einer bevorzugten Ausführungsform kann die erfindungsgemäße Verlegeware nicht nur direkt auf eine zu beschichtende Fläche beispielsweise eine Zimmerwand oder -decke aufgetragen werden, sondern auch durch das gleiche oder ein ähnliches Bindemittel mit Trägerplatten verbunden werden. Die Trägerplatten können aus verschiedenen Materialien, wie beispielsweise Glas, Plexiglas, Keramik bestehen und verschiedene Formen und Farben aufweisen.In a preferred embodiment, the laying material according to the invention can not only directly on a surface to be coated, for example a room wall or ceiling are applied, but also be connected by the same or a similar binder with support plates. The support plates can be made of various materials, such as glass, Plexiglas, ceramic and have different shapes and colors.

Besonders vorteilhaft ist es, wenn die Oberfläche der Verlegeware in einem weiteren Schritt dauerhaft versiegelt wird. Auf diese Weise kann einer Verunreinigung der Oberfläche durch beispielsweise im Wasser vorkommenden Kalk und anderen Elementen entgegengewirkt werden. Auch die Bildung von Keimen und Pilzen in den Kristallzwischenräumen kann verringert oder sogar vermieden werden. Dies ist besonders vorteilhaft bei einer Verwendung der Verlegeware in Sanitärräumen.Especially It is advantageous if the surface of the laying goods in a another step is permanently sealed. This way you can a contamination of the surface by, for example, occurring in the water lime and other elements be counteracted. Also the formation of germs and fungi in the crystal interstices can be reduced or even avoided. This is special advantageous when using the laying goods in sanitary facilities.

2. Verfahren2. Procedure

Dieses Verfahren erfolgt weitestgehend analog zum ersten Verfahren. Allerdings wird hierbei das Bindemittel nicht direkt in die Zwischenräume der natürlich gewachsenen Kristallstrukturen eingebracht, sondern es werden in die Stufe, zwischen Farbe und Wurzel, möglichst direkt unterhalb der Farbe, mit einem Bohrer, vorzugsweise einem Diamantbohrer, Löcher gebohrt. In diese Löcher wird das Bindemittel eingebracht, wobei die Löcher so nah aneinander gebohrt werden sollten, dass eine vollflächige Verklebung der Wurzeln gewährleistet werden kann. Die anschließende Weiterverarbeitung erfolgt wie im 1. Verfahren.This Method is largely analogous to the first method. Indeed In this case, the binder is not directly into the interstices of Naturally grown crystal structures are introduced, but it will be in the step, between color and root, as directly as possible below the Paint, drilled with a drill, preferably a diamond drill, holes. In these holes The binder is introduced with the holes drilled so close together that should be a full-surface Bonding of the roots ensured can be. The subsequent Further processing takes place as in the first method.

3. Verfahren3. Procedure

Bei diesem Verfahren wird als Bindemittel eine Art Schleifkitt verwendet. In einem ersten Schritt müssen die einzelnen Stufen erwärmt werden, damit der nötige Halt zwischen dem Schleifkitt und der natürlich gewachsenen Kristallstruktur gewährleistet ist. Die Art der Erwärmung sollte dabei so gewählt sein, dass eine Verunreinigung der natürlich gewachsenen Kristallstruktur vermieden wird. Als besonders vorteilhaft hat sich hierbei die Erwärmung auf einer Elektroplatte erwiesen.at This method uses a kind of abrasive cement as a binder. In a first step you have to the individual stages are heated so that the necessary Hold between the sanding block and the naturally grown crystal structure guaranteed is. The type of heating should be chosen be that an impurity of the naturally grown crystal structure is avoided. In this case, the heating has to be particularly advantageous an electrical panel proved.

Sind die Stufen erwärmt, können diese mit einem verflüssigten Schleifkitt überzogen werden. Auch bei diesem Verfahren sollten die mit Bindemittel versehenen Stufen anschließend vor der weiteren Verarbeitung aushärten. Nach dem Aushärten des Schleifkitts bleiben die Kristalle fixiert und lassen sich zuschneiden, ohne sie beim Trennen der Farbe von der Wurzel auseinander fallen.are the stages are heated, can these with a liquefied one Coated sanding putty become. Also in this process should be provided with the binder Then steps cure before further processing. After hardening of the abrasive cement the crystals remain fixed and can be cut without they fall apart when separating the color from the root.

Die abgeschnittene Verlegeware wird anschließend entweder direkt auf die endgültig zu beschichtende Fläche oder auf eine Trägerplatte aufgetragen. Anschließend wird die Verlegeware bzw. der Schleifkitt wieder erwärmt, so dass der Schleifkitt wieder von der natürlich gewachsenen Kristallstruktur abgezogen werden kann. Eine Reinigung der Kristallstruktur, beispielsweise mit einer alkoholhaltigen Lösung ist von Vorteil.The Cut stranded flooring is then either directly onto the finally to be coated surface or on a carrier plate applied. Subsequently If the laying material or sanding cement is reheated, then that the sanding putty back from the naturally grown crystal structure can be deducted. A purification of the crystal structure, for example with an alcoholic solution is advantageous.

Grundsätzlich können alle drei Verfahren auch miteinander kombiniert werden. Wesentlich ist auch, dass die Trennung der Farbe von der Wurzel in der Regel nicht exakt möglich ist, vielmehr ist der Übergang der Stufe von der Wurzel in die Farbe und damit auch die Position der Trennung, fließend. Um die Farbe möglichst sicher zu erhalten, erfolgt die Trennung meist im Bereich der Wurzel, möglichst nahe an der Farbe. Das Bindemittel kann also auch den an die Farbe angrenzenden Bereich der Wurzel verkleben, was automatisch dazu führt, dass auch die Farbe nicht auseinander fällt.In principle, everyone can three methods can also be combined. It is also essential that the separation of the color from the root is usually not exact possible is, rather, the transition is the step from the root to the color and thus the position the separation, fluent. To the color as possible to be sure, the separation takes place mostly in the area of the root, as close as possible on the color. The binder can therefore also the adjacent to the color Glue area of the root, which automatically causes that even the color does not fall apart.

Bei allen drei Verfahren kann die erfindungsgemäße Verlegeware auf einer Fläche, wie z. B. einer Trägerplatte, einem Tisch, einer Wand oder einer Arbeitsplatte aneinander gefügt werden. Dabei ist es möglich, dass einzelne Kristalle von der Verlegeware abgebrochen werden müssen, damit sich aneinandergrenzende Verlegewaren besser zusammenfügen können. Auch kann es notwendig werden, dass einzelne Zwischenräume aneinandergrenzender Verlegeware mit einzelnen Kristallen ausgefüllt werden müssen, damit eine einheitlichere Gesamtstruktur entsteht. Für derartige zusätzliche Arbeiten kann es vorteilhaft sein, das Bindemittel zu verwenden, das auch für die Herstellung der Verlegeware verwendet wurde.at all three methods can be laid on a surface, such as z. B. a support plate, a table, a wall or a worktop are joined together. It is possible that individual crystals must be broken off from the laying goods so that It is easier to join together adjacent laying products. Also It may become necessary for individual interspaces of adjoining installations filled with individual crystals Need to become, so that a more uniform overall structure is created. For such additional It may be advantageous to use the binder which works also for the production of the laying ware was used.

Es ist möglich, die Verlegeware an beliebige Formen oder Farben anzupassen.It is possible, to adapt the laying materials to any shapes or colors.

Eine mögliche Ausführungsform einer genannten Trägerplatte kann aus Glas bestehen. Glas ermöglicht eine sehr hohe Festigkeit des fertigen Produkts. Dabei kann die Verlegeware durch ein geeignetes Bindemittel mit dem Glas fest verbunden werden. Einscheibensicherheitsglas kann verwendet werden, wenn eine Sollbruchstelle notwendig ist. Diese kann mit geeigneten Zuschnittgeräten oder Maschinen erzeugt werden. Des Weiteren kann auch Verbundsicherheitsglas als Trägerplatte verwendet werden, wenn beim Einbau oder der späteren Verwendung hohe Drücke auftreten können und wenn keine vordefinierte Sollbruchstelle notwendig ist. Bei einer möglichen Verarbeitung mit Plexiglas wird dieses in einer bevorzugten Stärke ab 0,5 bis 1,0 Millimetern verwendet. Plexiglas hat den großen Vorteil, dass bei Bauten mit eingeschränktem oder vorgeschriebenem Gewicht eine deutliche Reduzierung der Gesamtlasten und eine sehr geringe Aufbauhöhe erreicht werden kann.A possible embodiment a said carrier plate can be made of glass. Glass allows a very high strength of the finished product. It can the Laying glued by a suitable binder firmly attached to the glass become. Single pane safety glass can be used if one Predetermined breaking point is necessary. This can be done with suitable cutting equipment or machines be generated. Furthermore, also laminated safety glass as support plate be used when high pressures occur during installation or later use can and if no predefined breaking point is necessary. At a potential Processing with Plexiglas this is in a preferred strength from 0.5 used up to 1.0 millimeters. Plexiglas has the great advantage that in buildings with limited or prescribed weight a significant reduction in overall loads and achieved a very low construction height can be.

In einer besonders vorteilhaften Ausführungsform können auch farbige Glasarten oder Plexiglas in den Farbtönen der einzusetzenden Steine verwendet werden. Dadurch kann die natürliche Farbgebung der einzusetzenden Mineralien, unterstützt werden. Die Intensität der Lichtdurchlässigkeit kann entsprechend variabel eingestellt werden. Vorteilhaft ist, wenn die Oberfläche der Trägermaterialien auf der Seite, auf der die Verlegeware angebracht wird glatt und auf der anderen Seite matt, rau, bzw. sandgestrahlt ist.In a particularly advantageous embodiment may also colored glass or Plexiglas used in the shades of the stones to be used become. This allows the natural coloring the minerals to be used. The intensity of light transmission can be adjusted accordingly variable. Is advantageous if the surface the carrier materials on the side on which the laying ware is mounted smoothly and on the other side is dull, rough, or sandblasted.

Erfindungsgemäße Verlegeware findet seine Verwendung in den unterschiedlichsten Anwendungsbereichen. In der Bauindustrie kann die Verlegeware beispielsweise als Wandverkleidungen, Deckengestaltungen und flächenartige Raumdekorationen eingesetzt werden. Aufgrund des geringen Gewichts und der geringen Aufbauhöhe eignet sich die Verlegeware auch für einen Einsatz in Bereichen, in denen eine geringe Masse maßgeblich ist, so z. B. im Kreuzfahrtschiff-, Motoryacht- und Yachtbau. In der Hotel- und Gastronomiebranche kann die Verlegeware beispielsweise als Dekoration in Wellnessbereichen und Restaurants eingesetzt werden.Laying products according to the invention finds its use in a wide variety of applications. In the construction industry, for example, the laid-up products can be used as wall coverings, Ceiling designs and area-like Room decorations are used. Due to the low weight and the low construction height the laying material is also suitable for use in areas in which a low mass is relevant is, so z. B. in cruise ship, motor yacht and yacht. In For example, in the hotel and restaurant industry, the laying ware can be to be used as a decoration in wellness areas and restaurants.

Auch in der Schmuckindustrie kann die Verlegeware beispielsweise bei der Gürtelschnallen-, Kettenanhänger-, Krawatten-, Broschen- oder Ringherstellung eingesetzt werden. So wird beispielsweise bei der Anhängerherstellung besonders viel Wert auf die Rückseite gelegt. Eine mögliche Anhängerherstellung mit Verle geware könnte wie folgt aussehen: Die Rückseite eines Verlegewarestückes wird geschliffen und poliert. Ferner kann ein weiteres, gleich großes Stück Verlegeware aus der gleichen Stufe hergestellt werden, bei dem alle Seiten, sowohl die Rückseite als auch die vordere Seite mit der natürlich gewachsenen Kristallstruktur geschliffen und poliert werden. Anschließend können die beiden Teile mittels Bindemittel zusammengeklebt und die Ränder ebenfalls geschliffen und poliert werden. Auf diese Weise würde ein Anhänger mit einer farblich stimmigen, aber dennoch glatt polierten Rückseite und einer Vorderseite mit natürlich gewachsener Kristallstruktur entstehen.Also in the jewelery industry, for example, the laying ware can the Belt Buckle, Chain Pendant, Tie, Brooch or ring production can be used. For example in trailer production a lot of emphasis on the back placed. A possible trailer manufacturing could be made with look like this: The back a laying piece of goods is sanded and polished. Furthermore, another, equal piece of laying materials made from the same stage, where all sides, both the back as well as the front side with the naturally grown crystal structure be sanded and polished. Subsequently, the two parts can by means of Binder glued together and the edges also ground and polished. In this way, a trailer with a color-matched, but still smooth polished back and a front with natural grown crystal structure arise.

Und auch wäre eine Verwendung der Verlegeware in Verbindung mit Massagematten in der Physiotherapie denkbar.And also would be a use of the laying ware in conjunction with massage mats conceivable in physiotherapy.

Im Bereich der Sanierung, in Altbauten, bei Modernisierungen, beim Schiffsbau oder Leichbau oder bei Dekorationen kann die Weiterverarbeitung der Verlegeware beispielsweise entweder auf Plexiglasträgern oder direkt auf die zu verkleidende Oberfläche erfolgen. Grundsätzlich gibt es keine festen Grundformen der Verlegeware. Diese ergeben sich immer aus den jeweiligen Anwendungsbereichen und den Wünschen der Abnehmer.in the Area of renovation, in old buildings, in modernization, in Schiffsbau or Leichbau or in decorations, the further processing of Lay, for example, either on Plexiglas carriers or directly on the surface to be clad. Basically there there are no fixed basic forms of the laid-up goods. These always arise from the respective fields of application and the wishes of the customers.

Nachfolgend werden die in der Beschreibung verwendeten Begriffe der vorliegenden Erfindung unter Bezugnahme auf die beiliegende Zeichnung näher beschrieben. Dabei zeigtfollowing become the terms used in the description of the present Invention with reference to the accompanying drawings described in more detail. It shows

1 eine Stufe, bzw. ein Rohstück, 1 a step, or a blank,

2 eine bereits getrennte Stufe, mit einer nicht eingefärbten Wurzel und einer eingefärbten Farbe, 2 an already separate step, with a non-colored root and a dyed color,

3 eine fertige Verlegeware 3 a ready to ship

Zunächst wird auf 1 Bezug genommen, in der beispielhaft eine Stufe 60, bzw. ein Rohstück veranschaulicht werden soll. Diese teilt sich in einen nicht eingefärbten Teil, die Wurzel 61 und einen eingefärbten Teil, die Farbe 61 auf. Die Farbe 61, weist eine Oberfläche 40 in Form einer natürlich gewachsenen Kristall struktur 20 auf. Die natürlich gewachsene Kristallstruktur 20 wird in der Wurzel 62 zusammengehalten. Bei einer Trennung der Farbe 61 von der Wurzel 62 würde die natürlich gewachsene Kristallstruktur 20 ihren Zusammenhalt verlieren und zerstört werden. Um dies zu verhindern wird in Zwischenräume 21 der natürlich gewachsenen Kristallstruktur 20 ein Bindemittel 30 eingebracht, bevor die Farbe 61 von der Wurzel 62 getrennt wird. Dadurch wird eine vollständige Verklebung der Kristallstruktur 20 erreicht. In einem alternativen Verfahren werden in die Stufe 60, zwischen Farbe 61 und Wurzel 62, möglichst direkt unterhalb der Farbe 61, mit einem Bohrer, vorzugsweise einem Diamantbohrer, Löcher 80 gebohrt. In die Löcher 80 wird anschließend das Bindemittel 30 eingebracht, so dass auch bei diesem Verfahren eine vollflächige Verklebung der Kristallstruktur 20 gewährleistet ist.First, it will open 1 Reference is made, in the example of a stage 60 , or a blank is to be illustrated. This splits into a non-colored part, the root 61 and a colored part, the color 61 on. The color 61 , has a surface 40 in the form of a naturally grown crystal structure 20 on. The naturally grown crystal structure 20 gets in the root 62 held together. At a separation of color 61 from the root 62 would the naturally grown crystal structure 20 lose their cohesion and be destroyed. To prevent this will be in intermediate spaces 21 the naturally grown crystal structure 20 a binder 30 introduced before the color 61 from the root 62 is disconnected. This will be a complete bond of the crystal structure 20 reached. In an alternative procedure will be in the stage 60 , between color 61 and root 62 , if possible directly below the color 61 , with a drill, preferably a diamond drill, holes 80 drilled. In the holes 80 then becomes the binder 30 introduced so that even in this method, a full-surface bonding of the crystal structure 20 is guaranteed.

Bei allen Verfahren ist eine zerstörungsfreie Trennung der Farbe 61 von der Wurzel 62, wie in 2 dargestellt, möglich, sobald das Bindemittel 30 ausgehärtet ist. Aufgrund der Tatsache, dass die in 2 abgebildete Farbe 61 bereits durch ein Bindemittel 30 verklebt ist, bildet diese bereits die erfindungsgemäße Verlegeware 10 aus. 3 stellt eine erfindungsgemäße Verlegeware 10 dar. Deutlich zu erkennen sind die mit Bindemittel gefüllten Zwischenräume 21.In all procedures is a nondestructive separation of the color 61 from the root 62 , as in 2 shown possible as soon as the binder 30 has hardened. Due to the fact that in 2 pictured color 61 already by a binder 30 is glued, this already forms the laying of the invention 10 out. 3 represents a Verlegeware invention 10 clearly visible are the spaces filled with binder 21 ,

Die Erfindung ist nicht auf die beschriebenen Ausführungsbeispiele beschränkt. Diese dienen lediglich der Verdeutlichung der Erfindung.The Invention is not limited to the described embodiments. These serve only to illustrate the invention.

1010
Verlegewareflooring product
2020
natürlich gewachsene Kristallstrukturnaturally grown crystal structure
2121
Zwischenräumeinterspaces
3030
Bindemittelbinder
4040
Oberfläche der VerlegewareSurface of the flooring product
5050
Trägerplattesupport plate
6060
Stufe, bzw. RohstückStep, or blank
6161
Farbecolour
6262
Wurzelroot
7070
SchleifkittSchleifkitt
8080
Löcherholes

Claims (12)

Verlegeware (10), gekennzeichnet durch eine Oberfläche (40) aus einer natürlich gewachsenen Kristallstruktur (20), die durch ein Bindemittel (30) zusammengehalten wird, wobei die Kristallstruktur (20) aus einer Farbe (61) eines natürlich gewachsenen Minerals besteht.Layers to be laid ( 10 ), characterized by a surface ( 40 ) from a naturally grown crystal structure ( 20 ) by a binder ( 30 ), the crystal structure ( 20 ) from one color ( 61 ) of a naturally grown mineral. Verlegeware (10) nach Anspruch 1, dadurch gekennzeichnet, dass die Kristallstruktur (20) aus der Farbe (61) einer natürlich gewachsenen Stufe (60) aus der Gruppe der Mineralien Citrin, Amethyst, Quarz, Pyrit, besteht.Layers to be laid ( 10 ) according to claim 1, characterized in that the crystal structure ( 20 ) from the color ( 61 ) of a naturally grown stage ( 60 ) from the group of minerals citrine, amethyst, quartz, pyrite. Verlegeware (10) nach einem der Ansprüche 1 oder 2, dadurch gekennzeichnet, dass das Bindemittel (30) in Zwischenräume (21) der natürlich gewachsenen Kristallstruktur (20) eingebracht ist.Layers to be laid ( 10 ) according to one of claims 1 or 2, characterized in that the binder ( 30 ) into spaces ( 21 ) of the naturally grown crystal structure ( 20 ) is introduced. Verlegeware (10) nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass das Bindemittel (30) ein transparentes Klebemittel aus Kunstharz ist.Layers to be laid ( 10 ) according to one of claims 1 to 3, characterized in that the binder ( 30 ) is a transparent adhesive made of synthetic resin. Verlegeware (10) nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Verlegeware (10) mit einer Trägerplatte (50) verbunden ist.Layers to be laid ( 10 ) according to one of claims 1 to 4, characterized in that the laying goods ( 10 ) with a carrier plate ( 50 ) connected is. Verlegeware (10) nach Anspruch 5, dadurch gekennzeichnet, dass die Trägerplatte (50) aus einem Material aus der Gruppe Glas, Plexiglas, Keramik besteht.Layers to be laid ( 10 ) according to claim 5, characterized in that the carrier plate ( 50 ) consists of a material from the group glass, plexiglass, ceramic. Verlegeware (10) nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass die Oberfläche (40) der Verlegeware (10) durch ein Bindemittel (30) versiegelt ist.Layers to be laid ( 10 ) according to one of claims 1 to 6, characterized in that the surface ( 40 ) of the laying ware ( 10 ) by a binder ( 30 ) is sealed. Verfahren zur Herstellung von Verlegeware (10) nach einem der Ansprüche 1 bis 7, gekennzeichnet durch die Verfahrensschritte: – Verbinden einer natürlich gewachsenen Kristallstruktur (20) der Farbe (61) einer Stufe (60) durch ein Bindemittel (30), wobei das Bindemittel (10) in die Zwischenräume (21) der natürlich gewachsenen Kristallstruktur (20) eingebracht wird und – Trennen der Farbe (61) von einer Wurzel (62) der Stufe (60).Process for the production of laying ware ( 10 ) according to one of claims 1 to 7, characterized by the method steps: - connecting a naturally grown crystal structure ( 20 ) the color ( 61 ) of a stage ( 60 ) by a binder ( 30 ), the binder ( 10 ) into the interstices ( 21 ) of the naturally grown crystal structure ( 20 ) and - separating the color ( 61 ) from a root ( 62 ) of the stage ( 60 ). Verfahren zur Herstellung von Verlegeware (10) nach Anspruch 8, dadurch gekennzeichnet, dass das Bindemittel (30) in Löcher (80) eingebracht wird, die mit einem Bohrer in die Stufe (60), zwischen die Wurzel (62) und die Farbe (61) gebohrt werden.Process for the production of laying ware ( 10 ) according to claim 8, characterized in that the binder ( 30 ) in holes ( 80 ) is brought into the stage with a drill ( 60 ), between the root ( 62 ) and the color ( 61 ) are drilled. Verfahren zur Herstellung von Verlegeware (10) nach Anspruch 8, dadurch gekennzeichnet, dass als Bindemittel (30) Schleifkitt (70) verwendet und über die natürlich gewachsene Kristallstruktur (20) der Farbe (61) gegossen wird.Process for the production of laying ware ( 10 ) according to claim 8, characterized in that as binder ( 30 Sanding putty ( 70 ) and via the naturally grown crystal structure ( 20 ) the color ( 61 ) is poured. Verfahren zur Herstellung von Verlegeware (10) nach Anspruch 10, dadurch gekennzeichnet, dass der Schleifkitt (70), nach dem Trennen der Farbe (61) von der Wurzel (62) und dem anschließenden Befestigen der Farbe (61) auf einer Fläche, wieder von der Farbe, (61) entfernt wird.Process for the production of laying ware ( 10 ) according to claim 10, characterized in that the abrasive cement ( 70 ), after separating the color ( 61 ) from the root ( 62 ) and the subsequent affixing of the paint ( 61 ) on a surface, again of the color, ( 61 ) Will get removed. Verfahren zur Herstellung von Verlegeware (10) nach einem der Ansprüche 8 oder 11, dadurch gekennzeichnet, dass in einem weiteren Schritt, die Verlegeware (10) mit einer Trägerplatte (50) verbunden wird.Process for the production of laying ware ( 10 ) according to any one of claims 8 or 11, characterized in that in a further step, the laying ware ( 10 ) with a carrier plate ( 50 ) is connected.
DE102007014496A 2007-03-22 2007-03-22 Laying fabric and a method for producing such Expired - Fee Related DE102007014496B8 (en)