DE1017898B - Process for the production of a storable starting material suitable for the production of artificial guts and other artificial skin structures from animal skin by molding using nozzles - Google Patents
Process for the production of a storable starting material suitable for the production of artificial guts and other artificial skin structures from animal skin by molding using nozzlesInfo
- Publication number
- DE1017898B DE1017898B DEB33696A DEB0033696A DE1017898B DE 1017898 B DE1017898 B DE 1017898B DE B33696 A DEB33696 A DE B33696A DE B0033696 A DEB0033696 A DE B0033696A DE 1017898 B DE1017898 B DE 1017898B
- Authority
- DE
- Germany
- Prior art keywords
- artificial
- production
- skin
- dry matter
- animal skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Bei der Herstellung von Kunstdärmen oder anderen künstlichen Hautgebilden, wie Membranen, Bändern und Fäden aus tierischer Haut ist es ein Hauptbedürfnis, daß die Faser des verwendeten Hautmaterials möglichst unverändert bleibt, damit das Kunstgebilde deren natürliche Eigenschaften behält.In the production of artificial casings or other artificial skin structures such as membranes, ligaments and threads from animal skin, it is a major requirement that the fiber of the skin material used remains unchanged as far as possible so that the artificial structure retains its natural properties.
In Hinsicht auf die Verformung des notwendigerweise zunächst zu zerkleinernden Hautmaterials haben verschiedene Überlegungen Veranlassung gegeben, das Hautmaterial durch eine Quellung mittels Säuren und Alkalien vorzubehandeln, vor allem, um dadurch die Wasseraufnahmefähigkeit zu steigern und bei der Formung ein Ausquetschen dieses aufgenommenen Wassers weitgehend zu vermeiden.With regard to the deformation of the skin material that must first be crushed various considerations give rise to the skin material by swelling by means of acids and To pretreat alkalis, especially in order to increase the water absorption capacity and with the Forming to largely avoid squeezing out this absorbed water.
Eine derartige Quellung greift jedoch die Faser in unerwünschter Weise an. Durch die erforderliche innige Vermischung des Hautmaterials mit dem Quellungsmittel, wobei es turbulenten Strömungen unterworfen wird und mechanisch angreifende Arbeitsteile, z. B. in Mischern, auf das Gut einwirken, ist es praktisch unvermeidbar, daß die durch das Quellungsmittel empfindlich gemachte Faser mehr oder weniger stark zertrümmert wird. Hierdurch werden die späteren Eigenschaften des Kunstgebildes, wie Knitterfestigkeit und Elastizität, nachteilig beeinflußt. Der Grad dieser Beeinträchtigung ist um so größer, je höher die bei der Mischung angewendeten Drücke sind; bei Anwendung von Hochdruckschnecken mit Drücken bis zu 200 atü kann diese Zertrümmerung gegebenenfalls so weit gehen, daß aus einer Masse räumlich definierter Fasern eine gelatinöse Masse entsteht.However, such swelling attacks the fiber in an undesirable manner. By the required intimate mixing of the skin material with the swelling agent, whereby it is subjected to turbulent currents and mechanically attacking working parts such. B. in mixers, act on the material, it is practical it is inevitable that the fiber made sensitive by the swelling agent will be more or less strong is smashed. This will improve the later properties of the artifact, such as crease resistance and elasticity, adversely affected. The degree of this impairment is greater, the greater the pressures used in mixing; when using high pressure screws with pressures up to At 200 atmospheres, this shattering can go so far that a mass is spatially more defined Fibers create a gelatinous mass.
Es gibt gewisse Anwendungszwecke, für welche eine derartige mehr oder weniger weitgehende Zerstörung der Faserstruktur keine Rolle spielt. In der Regel bedeutet diese Zerstörung jedoch den Verlust der Fähigkeit, durch Verfilzung oder Verflechtung eine genügende Festigkeit zu gewährleisten und die ursprüngliche Elastizität und Reißfestigkeit beizubehalten. Bei Kunstdärmen kann sich dadurch beispielsweise die natürliche Knitterfestigkeit im lufttrockenen Zustand so weit verringern, daß der flach gewickelte Kunstdarm beim Wiederauslegen und Einweichen zwecks Verwendung an den Knickstellen bricht.There are certain applications for which such a more or less extensive destruction the fiber structure does not matter. As a rule, however, this destruction means loss the ability to ensure sufficient strength through matting or interlacing and the maintain original elasticity and tear resistance. In the case of artificial casings, for example reduce the natural crease resistance in the air-dry state so much that the flat Wrapped artificial casings when re-laying and soaking for use at the kinks breaks.
Zu den vorgenannten Umständen der bisherigen Arbeitsweise kommt außerdem die mitunter sehr störende Tatsache, daß das angelieferte Hautmaterial im feuchten oder nassen Zustand einem unaufhaltbaren chemischen Abbau unterworfen ist, der auch durch Konservierungsmittel nur über beschränkte Zeit verzögert werden kann. In der Regel muß das Ausgangsmaterial, wenn es einmal in den Herstellungsvorgang, z. B. zur Erzeugung von Kunstdärmen, gelangt ist, infolge des Abbaues im feuchten Material, fortlaufend Verfahren zur HerstellungIn addition to the above-mentioned circumstances of the previous way of working, there is also the sometimes very annoying one The fact that the skin material delivered is unstoppable when it is damp or wet is subject to chemical degradation, which is only delayed over a limited time, even by preservatives can be. As a rule, the starting material, once it has entered the manufacturing process, z. B. for the production of artificial casings, has come, as a result of the degradation in the moist material, continuously Method of manufacture
eines lagerfähigen, für die Erzeugungone storable, for the production
von Kunstdärmen und anderen künstlichenof artificial casings and other artificial ones
Hautgebilden aus tierischer HautSkin formed from animal skin
durch Ausformung mittels Düsenby molding using nozzles
geeigneten Ausgangsmaterialssuitable starting material
Anmelder:
Walter Becker, Vöhrenbach (Schwarzw.)Applicant:
Walter Becker, Vöhrenbach (Black and White)
bis zum Endprodukt, z. B. Kunstdarm, verarbeitet werden. Infolge unvermeidbarer Schwankungen im angelieferten Rohmaterial — hinsichtlich Herkunft, Faserstruktur, Zusammensetzung, Vorbehandlung, z. B. Dauer einer Kälkung u. a. — sind die jeweils hergestellten Fasermassen und damit auch die Fertigerzeugnisse Schwankungen in ihren Eigenschaften unterworfen.to the end product, e.g. B. artificial casings are processed. As a result of unavoidable fluctuations in the delivered raw material - in terms of origin, fiber structure, composition, pretreatment, z. B. Duration of a liming, etc. - are the fiber masses produced in each case and thus also the finished products Subject to fluctuations in their properties.
Der vorliegenden Erfindung liegt danach die Aufgabe zugrunde, diese erwähnten Rückwirkungen der Vorbehandlung auf das Fasermaterial, insbesondere den Einfluß von Vorbehandlungsmitteln in der Gerberei und von Konservierungsmitteln, wie Kalk, auszuschalten, ferner ein Material herzustellen, das über längere Betriebszeiten und unabhängig von Schwankungen in der Herkunft, Zusammensetzung usw. unter praktisch stets gleichen Arbeitsbedingungen auf ein Fertigerzeugnis, wie Kunstdärme, verarbeitbar ist, fernerhin im trockenen Zustand praktisch unbegrenzt lagerfähig ist, ohne seine ursprünglichen Eigenschaften als Rohmaterial zur Herstellung von Kunstdärmen u. a. zu verändern, weiterhin ein Produkt herzustellen, mit welchem man Pasten mit höheren Trockensubstanzgehalten als 12 bis 13%, und zwar so hohen Gehalten an Trockensubstanz gewinnt, als man technisch verarbeiten kann, und schließlich ein Produkt herzustellen, mit dem man eine Paste für die Düsenverformung bereiten kann, wobei nach einfachen und genau festgelegten Mengenverhältnissen zwischen Trockenstoff, Ouellungsmittel und Wasser gearbeitet werden kann, sowie endlich damit ein besonders einfaches Verfahren für die fortlaufende Herstellung vonThe present invention is then based on the object of these mentioned repercussions Pretreatment on the fiber material, especially the influence of pretreatment agents in the tannery and to eliminate from preservatives such as lime, furthermore to produce a material that is over longer operating times and regardless of fluctuations in origin, composition, etc. under a finished product, such as artificial casings, can be processed with practically always the same working conditions, can furthermore be stored practically indefinitely in the dry state, without its original properties as a raw material for the production of artificial casings, among others. to change, continue to manufacture a product, with which pastes with higher dry matter contents than 12 to 13%, and so high The amount of dry matter that is retained is greater than what is technically possible to process, and ultimately a product produce, with which you can prepare a paste for the nozzle deformation, after simple and precisely defined proportions between dry matter, quenching agent and water worked can be, and finally a particularly simple process for the continuous production of
709 756/267709 756/267
Kunstgebilden, wie Kunstdärmen und Erzielung einer Art Standarderzeugnis möglich zu machen.Making artifacts such as artificial casings and achieving a kind of standard product possible.
Bei der bisherigen Aufbereitung des Ausgangsmaterials ist eine Kälkungszeit von mindestens zwei und üblicherweise von vier Wochen gebräuchlich, wodurch ein Abbau der Faser praktisch unvermeidbar ist. Durch diesen Abbau war es weiterhin bisher nicht möglich, Faserpasten mit höheren Trockensubstanzgehalten als 12 bis 13% zu erhalten. Diese bisher fürWith the previous preparation of the starting material, a liming time of at least two is required and usually used for four weeks, making degradation of the fiber practically inevitable is. Due to this degradation, it was still not possible to produce fiber pastes with higher dry matter contents than get 12 to 13%. This so far for
fernung von auswaschbaren Kalkanteilen durch ein- oder mehrmalige Zugabe von z. B. Salzsäurelösung zu den Waschwässern.removal of leachable limescale by adding one or more times z. B. hydrochloric acid solution to the washing waters.
Bei einem pH-Wert von etwa 5 bis 5,5 befindet sich das Material im isoelektrischen Punkt, was im übrigen mittels an sich bekannter Prüfvorrichtungen (pH-Meter) kontrolliert werden kann. Das auf seinen isoelektrischen Punkt eingestellte Material wird aus der Wasch- und Neutralisieranlage mit der esAt a pH value of about 5 to 5.5 the material is located in the isoelectric point, which can be controlled by means known per se in other testers (p H -meter). The material adjusted to its isoelectric point is taken from the washing and neutralizing system with which it
erforderlich gehaltene Reifung des Materials hat sich io fördernden Flotte ausgetragen und in eine Vorrich-The necessary maturation of the material was carried out in the conveying liquor and transferred to a device
als vermeidbar erwiesen. Es wurde nämlich gefunden, tung gebracht, die das Material in kleine, etwa pfen-proven avoidable. Namely, it was found that brought the material into small, e.g.
daß durch eine Wahrung bzw. Einstellung des Mate- " - - - - - -that by preserving or setting the mate- "- - - - - -
rials auf den isoelektrischen Punkt das Ausgangsmaterial in einen Zustand versetzt werden kann, wo-rials to the isoelectric point, the starting material can be put into a state in which
niggroße Läppchen stückt. Dieses kleinstückige Material wird durch das Ausquetschen in einer Druckschnecke, die in einem Siebzylinder arbeitet, so weit durch es in besonders schonender Weise den Wasser- 15 ausgepreßt, daß sein Trockensubstanzgehalt etwa gehalt abzugeben vermag und, einer Trocknung 30 bis 35% beträgt.nig-sized lobules. This small piece of material is squeezed out in a pressure screw, which works in a sieve cylinder, so far through it in a particularly gentle manner the water is pressed out that its dry matter content is about content is able to deliver and, a drying is 30 to 35%.
unterworfen, ein haltbares sowie besonders vorteilhaft Für die Trocknung dieses ausgepreßten Materialssubjected to a durable as well as particularly advantageous for drying this pressed material
zu beliebiger Zeit weiterzuverarbeitendes Zwischen- verwendet man vorteilhaft einen Umwälztrockner, der produkt ergibt. durch radiale Rippen am Innenumfang das Gut aufIntermediate to be further processed at any time, it is advantageous to use a circulating dryer which product results. the goods are opened by radial ribs on the inner circumference
Das Verfahren nach der vorliegenden Erfindung ist ao eine in dem zylindrischen Trockner zentrisch angedanach im wesentlichen dadurch gekennzeichnet, daß ordnete, schnell umlaufende Stachelwalze abwirft, das möglichst frische, tierische Hautmaterial, soweit Dadurch wird das krümelige, etwa erdfeuchte Mateerforderlich, zunächst zur Befreiung von Vorbehand- rial während des Trocknens durch eine Wärmequelle, lungsresten, insbesondere solchen einer Kälkung, sorg- z.B. Infrarottrockner, unter ständigem Zerzupfen fältig ausgewaschen und z. B. in einer schwingend be- 35 aufgelockert, nach außen geworfen und wieder zurück wegten, das Hautmaterial transportierenden Flotte auf die Stachelwalze, so daß nach einem verhältnisallmählich auf den isoelektrischen Punkt durch kon- mäßig kurzen Trockengang ein gekrülltes und bis zum tinuierliche Zugabe von Neutralitätsmitteln, wie Salz- gewünschten Trockengrad getrocknetes Gut entsteht, säurelösung, eingestellt wird. Nach Erreichung dieses d. h. bis zur Erreichung eines Trockensubstanzgehaltes Zustandes wird das Hautmaterial dann in kleine Läpp- 3° von etwa 75%.The method according to the present invention is ao angedanach centrally in the cylindrical dryer essentially characterized in that ordered, rapidly rotating spiked roller throws off, the freshest possible animal skin material, insofar as this makes the crumbly, roughly earth-moist material necessary, initially to free it from pretreatment during drying by means of a heat source, Lung residues, especially those from liming, carefully e.g. infrared dryer, with constant tearing washed out wrinkled and z. B. loosened up in a swinging motion, thrown outwards and back again wegten, the skin material transporting liquor on the spiked roller, so that after a relatively gradual on the isoelectric point due to a consistently short drying cycle, a crooked and up to Continuous addition of neutrality agents, such as salt - the desired degree of dryness is produced for dried goods, acid solution. After reaching this d. H. until a dry matter content is reached The skin material is then in small lapping 3 ° of about 75%.
chen zerteilt, durch Auspressen von anhaftender Flüssigkeit befreit und hierauf die etwa krümeligfeuchte Masse in einem Umwälztrockner schonend auf einen Trockensubstanzgehalt von etwa 75% getrocknet, bis ein granulatartiges, lockeres Produkt entsteht. Durch die Beachtung des isoelektrischen Punktes läßt sich anhaftende und aufgenommene Flüssigkeit aus dem Hautmaterial schon durch einfaches mechanisches Auspressen — beispielsweise mittels einer in einemchopped up, freed from adhering liquid by squeezing out and then gently spreading the crumbly moist mass in a tumble dryer a dry matter content of about 75% until a granular, loose product is formed. By observing the isoelectric point, adhering and absorbed liquid can be discharged the skin material simply by mechanical pressing - for example by means of one in one
Es hat sich gezeigt, daß hierdurch das Gut praktisch unbegrenzt lagerfähig bleibt, d. h. auch bei einer Lagerung in einfachen Lagerräumen kein Schimmeln oder sonstige Schädigungen durch Mikroorganismen auftreten. It has been shown that this means that the goods can be stored practically indefinitely, i. H. even with storage no mold or other damage from microorganisms occurs in simple storage rooms.
Will man das Quellmittel für die spätere Herstellung von Faserpasten bereits dem Trockenstoff zusetzen, so trocknet man zweckmäßig nach dem Ausquetschen in einer Trockeneinrichtung bis etwa 85 %,If you want to add the swelling agent for the later production of fiber pastes to the drying agent, it is advisable to dry it after squeezing in a drying device to about 85%,
Loch- oder Siebzylinder arbeitenden Schnecke — bis 4° um nach der Aufsaugung des Quellmittels wieder
auf einen Trockensubstanzgehalt von 30 bis 35 % ent- einen solchen Trockensubstanzgehalt von etwa 75 %
fernen. Dieses feucht-krümelige Material neigt weder
zum Klumpen noch zum Zusammenbacken und kannPerforated or sieve cylinder working screw - up to 4 ° after the absorption of the swelling agent again to a dry matter content of 30 to 35% away from such a dry matter content of about 75%. This moist, crumbly material does not tend
to clump or to cake and can
zu erhalten.to obtain.
Zur Herstellung künstlicher Hautgebilde, wieFor the production of artificial skin structures, such as
Kunstdärme, wird mit Flüssigkeit eingeweicht, wobei, trockner, mit radialen Rippen bei schonender Wärme- 45 w;e erwähnt, infolge der hohen Saugfähigkeit des einwirkung ohne die Gefahr üblicher Überhitzungen Trockenstoffes ein Aufsaugen, und zwar durch Über-Artificial intestines, soaked with liquid, whereby, drier, with radial ribs with gentle heat- 45 w ; e mentioned, due to the high absorbency of the dry matter without the risk of usual overheating, it can be sucked up by over-
durch einfaches Umwenden, z. B. in einem Umwälzoder ungenügender Durchtrocknung in verhältnismäßig kurzer Zeit getrocknet werden. Es entsteht ein granulatartiges, im Aussehen etwa Trockengemüse ähnelndes gekrülltes Material, das sich leicht ausfüllen und handhaben, z. B. in Säcke füllen läßt.by simply turning it over, e.g. B. in a circulation or insufficient drying in proportion be dried for a short time. The result is a granular vegetable, roughly dry in appearance similar crumpled material that is easy to fill in and handle, e.g. B. can be filled into bags.
Bei der Verwendung dieses Materials zur Herstellung verformbarer Faserpasten quillt dieser Trockenstoff schnell und gleichmäßig durch einfaches Aufsaugen der Flüssigkeit. Der Zustand des Trockenstoffes erlaubt es auch, Material, das aus verschiedenen Herstellungsgängen und aus verschiedenen Herkunftsquellen stammt, zu mischen, um damit einen möglichst allgemeingültigen Querschnitt und durchWhen this material is used to manufacture deformable fiber pastes, this dry matter swells quickly and evenly by simply sucking up the liquid. The condition of the dry matter It also allows material that comes from different manufacturing processes and from different Sources of origin comes to mix in order to achieve a cross-section that is as general as possible and through
schichten mit der Flüssigkeit genügt, um in verhältnismäßig kurzer Zeit eine gleichmäßig gequollene und unmittelbar verarbeitbare Paste zu erhalten.Layering with the liquid is sufficient to produce an evenly swollen and swollen in a relatively short time to obtain ready-to-use paste.
Durch einfache Diffusion und ohne mechanische Durcharbeitung, wie sie bisher nötig war und z. B. die Verwendung von Mischschnecken, Knetern, Anwendung turbulenter Strömungen usw. erforderte, erhält man nunmehr in wesentlich einfacherer und schonenderer Weise eine gleichmäßig gequollene Masse, die nach der üblichen Entfernung von Knötchen — z. B. durch Pressen durch Loch- oder Schlitzsiebe — sich fortlaufend in Ringdüsen od. dgl. verarbeiten läßt. Wenn man von einem TrockenstoffBy simple diffusion and without mechanical processing, as was previously necessary and z. B. required the use of mixing screws, kneaders, the use of turbulent flows, etc., you now get a uniformly swollen in a much simpler and gentler way Mass obtained after the usual removal of nodules - e.g. B. by pressing through perforated or slotted screens - Can be processed continuously in ring nozzles or the like. If you think of a dry matter
verschiedene Erscheinungsformen übliche Rohmate- 5° ausgeht, der bereits Quellmittel enthält, wird als Flüs-different manifestations common raw material- 5 °, which already contains swelling agent, is used as a liquid
rialien zu erhalten.to obtain supplies.
Bei der praktischen Durchführung geht man zweckmäßig so vor, daß das angelieferte Rohmaterial, wie Haut, zunächst durch möglichst intensive Waschung, z. B. im sprudelnden Wasser, von Verunreinigungen, vor allem von Resten einer Vorbehandlung, wie von Kalk, befreit wird und hierauf, in einer Flotte schwimmend, durch mehrere sich folgende Waschungen mit Zusatz von Chemikalien auf den isoelektrischen PunktIn practical implementation, it is expedient to proceed in such a way that the delivered raw material, such as Skin, first by washing it as intensively as possible, e.g. B. in the bubbling water, from impurities, above all from residues of a pretreatment, such as lime, is freed and then, floating in a liquor, by several subsequent washes with the addition of chemicals to the isoelectric point
sigkeit nur Wasser verwendet; für einen Trockenstoff ohne Quellmittelgehalt, der einen pH-Wert von etwa 5 aufweist, ist die erforderliche Menge an Quellmitteln außer Wasser zuzugeben, wodurch dem gewünschten pH-Wert und dem Trockensubstanzgehalt der zu verarbeitenden Paste entsprochen ist.sigkeit only uses water; for a dry matter content without swelling agent having a pH value of about 5, the amount of swelling agents is required to admit other than water, whereby the desired pH value and the dry matter content which is suited to be processed paste.
Beispiel
Will man z. B. 1 kg Hautfasergranulat von pH 5,5example
Do you want to z. For example, 1 kg Skin fiber granulate of p H 5.5
gebracht wird, d. h. bei gekalktem Material nach Ent- 70 und einem Trockensubstanzgehalt von 75% mit Hilfeis brought, d. H. with limed material after 70 and a dry matter content of 75% with help
von etwa 33 % H Cl in eine 15%ige gequollene Faserpaste mit einem pH-Wert von 3,0 überführen, so gilt folgende Gleichung:transfer of about 33% Cl H in a 15% swollen fiber paste having a pH value of 3.0, the following equation applies:
7575
- — 1 = Zugabe an Flüssigkeit- - 1 = addition of liquid
1515th
7575
Is"Is "
- 1 = 4,000 kg (H2 O + H Cl)- 1 = 4.000 kg (H 2 O + H Cl)
Die Zugabe an Gesamtflüssigkeit beträgt also in xo diesem Beispiel 41.The addition of total liquid is therefore in xo this example 41.
Bei einem pH-Wert des Granulats von 5,5 benötigt man 0,06 g H Cl auf 1 g 100%igen Trockenstoff, um eine verarbeitungsfertige Paste von pH3,0 zu erhalten. Für 1 kg 75%igen Trockenstoff braucht man alsoAt a pH value of the granules of 5.5, 0.06 g H Cl 1 g of 100% strength by weight dry matter, in order to obtain a ready-to-paste of p H 3.0 is required. So for 1 kg you need 75% dry matter
750-0,06 = 45,000 g H Cl,750-0.06 = 45,000 g H Cl,
somit sind alsothus are so
3,9551 H2O
+ 0,0451 HCl3.9551 H 2 O
+ 0.0451 HCl
= 4,000 (H2O+ HCl)= 4,000 (H 2 O + HCl)
nötig.necessary.
Man bringt nun das Granulat in ein Gefäß von etwa 10 1 Inhalt, übergießt es mit der obenerwähnten Menge der verdünnten Salzsäurelösung, deckt das Gefäß ab und läßt den Inhalt unter Vermeidung jeglichen Schütteins, Rührens, Bewegens oder Drehens etwa 1 Stunde stehen. Nach dieser Zeit ist ein praktisch vollkommenes Gleichgewicht eingetreten, d. h., an allen Stellen der nunmehr entstandenen gequollenen Fasermasse kann ein pH-Wert von 3,0 und ein Trokkensubstanzgehalt von 15 % festgestellt werden.The granulate is then placed in a container with a capacity of about 10 liters, the above-mentioned amount of the diluted hydrochloric acid solution is poured over it, the container is covered and the contents are left to stand for about 1 hour, avoiding any shaking, stirring, agitation or turning. After this time, a practically complete equilibrium has occurred, that is, at all points of the now resulting swollen fiber mass, a pH value of 3.0 and a Trokkensubstanzgehalt of 15% can be determined.
Auf die vorerwähnte Weise erhaltene Pasten lassen sich im gequollenen Zustand mit Trockensubstanzgehalten, auch über 12%, z. B. 15 oder 20%, soweit entsprechende Drücke Anwendung finden, mit Erfolg verarbeiten.Pastes obtained in the aforementioned manner can be swollen with dry matter contents, also over 12%, e.g. B. 15 or 20%, if appropriate pressures are used, with success to process.
Man ist durch die Anwendung höherer Trockensubstanzgehalte in der Lage, auch Massen mit pH-Werten oberhalb 3 pH zu verarbeiten, während es bisher nötig war, um das Quellwasser bei der Verarbeitung mittels Formdüsen zuhalten, jedenfalls pH-Werte unter 3 einzuhalten. Ein geringerer Quellwert liegt aber, wie bereits erwähnt, im Sinne einer Faserschonung, wodurch die Festigkeit der erhaltenen Gebilde größer ist als bei höher gequollenen, z. B. hoch gequollenen Massen.It is to be processed by the use of higher dry matter contents in a position to also materials having p H values above 3 p H, while it was previously needed to the source of water in the processing means of die nozzle noted observed in any case p H values below. 3 However, as already mentioned, a lower swelling value is in the sense of protecting the fibers, whereby the strength of the structures obtained is greater than in the case of more highly swollen, e.g. B. highly swollen masses.
Kunstdärme und künstliche Gebilde aus einem Hautmaterial, das durch Düsenverformung einer gemaß Erfindung zubereiteten Fasermasse hergestellt ist, haben alle erforderlichen Eigenschaften eines guten Kunstdarmes. Die Gewinnung einer Trockenmasse, die trocken praktisch unbegrenzt lagerfähig ist, ohne besondere Mittel versandfähig und praktisch von gleichbleibender Beschaffenheit, ist auch schließlich möglich, den Herstellungsprozeß von Kunstdärmen und anderen künstlichen Hautgebilden räumlich unabhängig zu machen von der Aufbereitung der Hautfasermasse und von den bisher dazu gehörenden Einrichtungen für die Zubereitung der verformbaren Masse mit zum Teil umständlichen Einrichtungen.Artificial intestines and artificial structures made of a skin material, which by nozzle deformation according to a Invention prepared pulp produced have all the required properties of a good artificial casing. Obtaining a dry matter that can be stored dry for practically unlimited periods is, can be shipped without special means and is practically of the same quality, is also finally possible, the manufacturing process of artificial casings and other artificial skin structures spatially to make it independent of the preparation of the skin fiber mass and of the previously associated Equipment for the preparation of the deformable mass with partly cumbersome equipment.
Claims (4)