DE10133813A1 - Surface treatment of cut foam plastic panels comprises pressing glued paper sheets on to their surfaces - Google Patents

Surface treatment of cut foam plastic panels comprises pressing glued paper sheets on to their surfaces Download PDF

Info

Publication number
DE10133813A1
DE10133813A1 DE10133813A DE10133813A DE10133813A1 DE 10133813 A1 DE10133813 A1 DE 10133813A1 DE 10133813 A DE10133813 A DE 10133813A DE 10133813 A DE10133813 A DE 10133813A DE 10133813 A1 DE10133813 A1 DE 10133813A1
Authority
DE
Germany
Prior art keywords
paper
plastic foam
plastic
foam
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE10133813A
Other languages
German (de)
Inventor
Jürgen BRUNING
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fagerdala Deutschland GmbH
Original Assignee
Fagerdala Deutschland GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fagerdala Deutschland GmbH filed Critical Fagerdala Deutschland GmbH
Priority to DE10133813A priority Critical patent/DE10133813A1/en
Publication of DE10133813A1 publication Critical patent/DE10133813A1/en
Withdrawn legal-status Critical Current

Abstract

Surface treatment of cut foam plastic panels (11) comprises pressing glued paper sheets (10) on to their surfaces.

Description

Die Erfindung betrifft ein Verfahren zur Herstellung von Teilen, teilweise bestehend aus Kunststoffschaum.The The invention relates to a method for producing parts, in part consisting of plastic foam.

Kunststoffschaum ist ein Produkt mit vielfältiger Anwendung.Plastic foam is a product with more variety Application.

Ein wesentliches Problem bei der Herstellung von Kunststoffschaum ist seit einigen Jahren das Treibmittel. Kunststoffschaum entsteht nämlich mit einem Treibmittel. Treibmittel werden gelegentlich auch als Blähmittel bezeichnet. Damit ist die Wirkung des Treibmittels beschrieben. Das Treibmittel bildet in dem schmelzflüssigen Kunststoff Blasen.One is a major problem in the production of plastic foam for some years the propellant. Plastic foam is created with a propellant. Propellants are sometimes also used as a blowing agent designated. This describes the effect of the propellant. The blowing agent forms bubbles in the molten plastic.

Vor einiger Zeit stand allen Herstellern ein zuverlässiges und einfach zu handhabendes Treibmittel in der Form von FCKW in verschiedenen Formen gleichermaßen zur Verfügung. Nachdem sich die Umweltschädlichkeit der herkömmlichen Treibmittel gezeigt hat, sind die Hersteller um andere Treibmittel bemüht. Das meistpräferierte Alternativtreibmittel ist Kohlendioxid. Dieses Treibmittel ist jedoch äußerst problematisch.In front For some time, all manufacturers have been reliable and easy to use Propellants in the form of CFCs in various forms equally to Available. After the environmental damage the conventional one Propellant has shown, the manufacturers are to other propellants endeavor. The most popular Alternative propellant is carbon dioxide. However, this propellant is extremely problematic.

Das zeigt sich unter anderem daran, daß nur bei bestimmten Dicken ein ausreichendes Schäumergebnis erreicht wird. Das hat zu der Überlegung geführt, größere Plattendicken durch Doppelung und kleinere Plattendicken durch Teilung zu erreichen. Die Teilung nennt sich auch Schälen.The shows, inter alia, that only at certain thicknesses a sufficient foaming result is reached. That has to the consideration guided, larger plate thicknesses to achieve by doubling and smaller plate thicknesses by division. The Division is also called peeling.

Das Schälen ist seit langem Stand der Technik für Partikelschaumteile. Dabei wird ein relativ großer Schaumblock aus Schaumstoffpartikeln in Bahnen geteilt. Die einzelnen Bahnen werden von dem Block abgeschält. Für das Schälen eignen sich z.B. Messer, Sägen und auch beheizte Schneiddrähte.The Peel has long been the state of the art for particle foam parts. there will be a relatively large one Foam block of foam particles divided into webs. The single ones Tracks are peeled off the block. For peeling, e.g. Knife, Sawing and also heated cutting wires.

Partikelschaumteile werden aus Schaumstoffpartikeln gewonnen, die aus unterschiedlichen Herstellungsvorgängen zur Verfügung stehen. In der Hauptsache werden Schaumstoffpartikel dadurch erzeugt, daß zunächst dünne Schmelzestränge granuliert werden. Die Schmelzestränge werden wahlweise ungeschäumt extrudiert und granuliert. Anschließend werden die Partikel in einen Autoklaven eingesetzt und unter Druck und Temperatur mit einem Treibmittel versetzt. Nach ausreichender Treibmittelbeladung und Erweichung werden die Partikel schlagartig aus dem Autoklaven entlassen. Das Treibmittel läßt die Partikel dabei aufschäumen.Particle foam parts are obtained from foam particles that come from different manufacturing processes disposal stand. In the main, foam particles are created by that initially granulated thin melt strands become. The melt strands are optionally unfoamed extruded and granulated. Subsequently, the particles in used an autoclave and under pressure and temperature with a propellant added. After sufficient propellant charge and softening The particles are suddenly released from the autoclave. The propellant leaves the particles lather up.

Ein anderer gebräuchlicher Weg zur Herstellung von Schaumstoffpartikel geht auch von einer Schmelzeextrusion aus. Im Unterschied zu der oben beschriebenen Extrusion ungeschäumter Schmelze wird bei dem anderen Weg eine treibmittelbeladene Schmelze extrudiert, so daß ein Schaumstrang entsteht und in der anschließenden Granulierung sofort Schaumstoffpartikel anfallen.One other common ones The way to produce foam particles is also melt extrusion out. In contrast to the extrusion of unfoamed melt described above extruding a blowing agent-laden melt in the other way, so that one Foam strand is formed and in the subsequent granulation immediately foam particles attack.

Die Schaumstoffpartikel werden in einem Formteilautomaten zu einem Formteil miteinander verbunden. Der Formteilautomat enthält einen Formhohlraum mit einer genauen Abbildung des gewünschten Formteiles. Der Formhohlraum wird mit den Schaumstoffpartikeln vollständig gefüllt, vorzugsweise geschieht das unter Druck Anschließend werden die Schaumstoffpartikel in der Form mit Heißdampf beaufschlagt. Der Heißdampf hat die Aufgabe, die Schaumstoffpartikel an der Außenfläche zu erweichen. Unter dem bestehenden Druck kommt es dann zu einer Verschweißung der Schaumstoffpartikel.The Foam particles become a molded part in a molding machine connected with each other. The molding machine contains a mold cavity with a exact picture of the desired Molding. The mold cavity is completely filled with the foam particles, preferably This happens under pressure Subsequently, the foam particles in the mold with superheated steam applied. The hot steam The task is to soften the foam particles on the outer surface. Under the existing pressure, it comes to a welding of Foam particles.

Die richtige Erweichung bedingt eine Heißdampftemperatur im Bereich des Schmelzpunktes des Kunststoffschaumes. Bei Polystyrol liegt der Schmelzpunkt geringfügig über 100 Grad Celsius. Die notwendige Heißdampftemperatur wird unter Erhöhung des Dampfdruckes erreicht. Bei anderen Kunststoffen ist eine größere Erhöhung erforderlich. Polypropylen hat einen Schmelzpunkt zwischen 150 und 170 Grad Celsius.The proper softening requires a superheated steam temperature in the range the melting point of the plastic foam. In polystyrene lies the melting point slightly above 100 Centigrade. The necessary hot steam temperature is under increase reached the vapor pressure. Other plastics require a larger increase. polypropylene has a melting point between 150 and 170 degrees Celsius.

Auf dem Wege können relativ dicke Blöcke erzeugt werden.On the ways produces relatively thick blocks become.

Mit den neuen Treibmittel lassen sich weniger dicke Platten durch reine Extrusion erzeugen.With The new propellant can be less thick plates by pure Create extrusion.

Sowohl die Platten/Blöcke aus Schaumstoffpartikeln wie auch die extrudierten Platten können geschält werden. Durch das Schälen entstehen Schnittflächen mit offenen Zellen.Either the plates / blocks made of foam particles as well as the extruded sheets can be peeled. By peeling arise cut surfaces with open cells.

In der Weiterverarbeitung geschälter Schaumprodukte sind die offenen Zellen ein Problem. Die offenen Zellen eignen sich nicht als Sichtfläche und sind einer Verschmutzung förderlich, weil der Schmutz sich in den Zellen sammelt. Entsprechendes gilt für Krankheitserreger.In the processing of skived foam products the open cells are a problem. The open cells are suitable not as a visible surface and are conducive to pollution, because the dirt collects in the cells. The same applies for pathogens.

Um solche Schnittflächen als Sichtflächen nutzen zu können oder als Berührungsflächen zuzulassen ist herkömmlich eine erhebliche Beschichtung erforderlich. Beim Aufkaschieren werden Folien relativ großer Dicke verwendet. Es ist bei geschälten EPS-Schaumplatten eine Melaminharzbeschichtung (Duroplast) der Schnittflächen bekannt. Bei der Kaschierung handelt es sich um eine Klebekaschierung.Around such cut surfaces as visible surfaces use to be able to or to allow as touch surfaces is conventional a significant coating required. When laminating be Slides relatively large Thickness used. It is a melamine resin coating (thermoset) for peeled EPS foam sheets the cut surfaces known. The lamination is a Klebekaschierung.

Die Schnittflächen lassen sich auch nicht unmittelbar lackieren. Zur Erzeugung einer ausreichenden Lackierqualität müssen die Schnittflächen gespachtelt werden, bis die offenen Zellen verschlossen/gefüllt sind.The cut surfaces can not be painted directly. To generate a adequate painting quality have to the cut surfaces be filled until the open cells are closed / filled.

Die Erfindung hat sich die Aufgabe gestellt, eine einfache und wirtschaftliche Bearbeitung von Kunststoffschaumschnittflächen, insbesondere von geschältem Kunststoffschaum, zu schaffen. Dabei hat die Erfindung erkannt, daß das herkömmliche Aufkaschieren von Kunststoff-Folien verschiedene Probleme hat:
Der Klebstoffverbrauch ist viel höher als der Verbrauch an vergleichbarer anderer Stelle. Die Einfärbung/Dekorgestaltung ist bei den üblichen Kunststoff-Folien aufwendig und schwierig.The object of the invention has been found to provide a simple and economical processing of plastic foam cut surfaces, in particular peeled plastic foam. The invention has recognized that the conventional lamination of plastic films has various problems:
The adhesive consumption is much higher than the consumption of comparable elsewhere. The coloring / decor design is complicated and difficult in the usual plastic films.

Nach der Erfindung wird das durch Aufbringen von Papier auf die Schnittflächen erreicht. Das Papier wird aufgeklebt oder aufkaschiert. Vorteilhafterweise kann mit der erfindungsgemäßen Papierschicht nicht nur das Problem der Schnittflächen gelöst werden. Die Anwendung der Papierschicht ist auch für ungeschnittene Formteilflächen von Partikelschaumformteilen von Vorteil. Normale Formteilflächen sind unbehandelte Flächen (als Oberflächenbehandlung wird auch eine Thermoverformung in der Form angesehen). Solche Flächen zeigen mehr oder weniger eine Apfelsinenhaut. Ursache sind die nach oben weisenden Flächen zwischen den Grenzen der Schaumstoffpartikel. Üblicherweise besteht bei ausreichender Temperatur des Formteiles an den nach oben weisenden Schaumstoffpartikelflächen eine Wölbung zwischen den seitlichen Grenzen der Schaumstoffpartikelflächen, die sich in der beschriebenen Form abzeichnet.To The invention is achieved by applying paper to the cut surfaces. The paper is glued or laminated. advantageously, can with the paper layer according to the invention not only the problem of cut surfaces can be solved. The application of Paper layer is also for uncut molding surfaces Of particle foam moldings advantage. Normal molding surfaces are untreated areas (as a surface treatment thermoforming in the mold is also considered). Such surfaces show more or less an orange peel. Cause are the up facing surfaces between the boundaries of the foam particles. Usually there is sufficient Temperature of the molded part at the upwardly facing foam particle surfaces a curvature between the lateral boundaries of the foam particle surfaces, which are described in the Shape is emerging.

Durch Aufkleben oder Aufkaschieren von Papier, wird die Oberfläche geglättet. Bei dem Kleben von Papier ist weniger Klebstoff als bei dem Aufkleben von Folien erforderlich.By Sticking or laminating paper, the surface is smoothed. at gluing paper is less adhesive than gluing required by slides.

Papier besitzt ideale Voraussetzungen für das Aufdrucken von Farben bzw. Dekor.paper has ideal conditions for this Imprinting of colors or decor.

Das für die erfindungsgemäße Oberflächenbehandlung vorgesehene Papier hat vorzugsweise eine Dicke, die durch das Gewicht in Gramm pro Quadratmeter gemessen wird und 5 bis 100 gr pro Quadratmeter beträgt.The for the Surface treatment according to the invention provided paper preferably has a thickness determined by the weight measured in grams per square meter and 5 to 100 gr per square meter is.

Das Papier besteht regelmäßig aus ungeordneten, miteinander verklebten Cellulosefasern. Solche Faserstrukturen lassen sich auch als Vlies bezeichnen. Es kann aber auch Gewirke aus geordneten Cellulosefasern Anwendung finden.The Paper is made regularly disordered, bonded together cellulose fibers. Such fiber structures can also be described as fleece. But it can also be knitted fabrics from ordered cellulose fibers find application.

Zum Aufkleben des Papiers eignen sich viele Kleber, z.B. Dispersionskleber, Acrylkleber Pulyurethankleber. Eine Klebermenge von 5 bis 80 Gramm pro Quadratmeter ist für eine Verklebung ausreichend. In der Regel wird die verwendete Klebermenge 20 bis 40 Gramm pro Quadratmeter betragen. Der Verbrauch an Klebemittel kann darüber hinaus dadurch reduziert werden, daß nur ein Kleberauftrag am geschnittenen/geschälten Kunststoffschaumschaum erfolgt. Dabei werden nur die Schnittflächen der Zellwände mit Kleber benetzt.To the Gluing the paper, many adhesives, e.g. Dispersion adhesive, Acrylic adhesive Pulyurethane adhesive. An amount of glue from 5 to 80 grams per Square meter is for a bond sufficient. As a rule, the amount of glue used 20 to 40 grams per square meter. The consumption of adhesive can over it be reduced by the fact that only a glue on the cut / peeled Plastic foam foam takes place. Only the cut surfaces of the cell walls wetted with glue.

Das Aufkaschieren von Papier kann im Wege des Bügelns erfolgen. Beim Bügeln wird das Papier an der dem Kunststoff abgewandten Seite erwärmt. Die Temperatur muß dabei so hoch gewählt werden, daß an der Berührungsfläche des Papiers mit dem Kunststoffschaum eine minimale Temperatur und eine maximale Temperatur nicht überschritten werden. Die minimale Temperatur liegt höchstens 20 Grad, vorzugsweise höchstens 10 Grad Celsius, unter dem Schmelzpunkt des betreffenden Kunststoffes. Die maximale Temperatur liegt höchstens 20 Grad, vorzugsweise höchstens 10 Grad Celsius, über dem Schmelzpunkt des betreffenden Kunststoffes. Das Papier ist bei den hier erforderlichen Temperaturen relativ unempfindlich.The Laminating paper can be done by ironing. When ironing is heats the paper on the side facing away from the plastic. The Temperature must be there be chosen so high that on the contact surface of the Paper with the plastic foam a minimum temperature and a maximum temperature should not be exceeded. The minimum temperature is at most 20 degrees, preferably at most 10 degrees Celsius, below the melting point of the plastic in question. The maximum temperature is at most 20 degrees, preferably at most 10 degrees Celsius, over the melting point of the plastic in question. The paper is at the temperatures required here are relatively insensitive.

Zum Bügeln eignen sich herkömmliche Bügeleisen. Solche Bügeleisen werden von Hand bedient. Ein Roboter könnte die manuelle Bedienung ersetzen.To the Iron are conventional Iron. Such irons are operated by hand. A robot could replace manual operation.

Im Sinne der Erfindung zählt zu dem Bügeln auch eine Erwärmung mit eine Heizwalze. Vorzugsweise erfolgt das Bügeln mit einer Heizpresse. Die Presse hat den Vorteil, daß sie bei entsprechender Auslegung gleichzeitig ihren Druck auf der gesamten Papieroberfläche aufbringen kann.in the Meaning of the invention counts to the ironing too a warming with a heating roller. Preferably, the ironing is done with a hot press. The press has the advantage of being with appropriate design at the same time apply their pressure on the entire paper surface can.

Wahlweise wird das Aufkaschieren mit einem Haftvermittler erleichtert. Als Haftvermittler kommen Anstriche/Grundierungen und/oder zusätzliche Oberflächenbehandlungen in Betracht. Es können auch Papiere Anwendung finden, die kunststoffschaumseitig mit einem Kunststoff beschichtet ist, der eine Verbindung mit dem Kunststoffschaum eingeht. Die Beschichtung kann z.B. dadurch hergestellt werden, daß feinkörnige Partikel aus gleichem Kunststoff wie der Kunststoffschaum auf dem Papier verteilt und anschließend aufgeschmolzen werden.Optional the lamination is facilitated with a bonding agent. When Adhesion promoters come with coatings / primers and / or additional surface treatments into consideration. It can too Papers find application, the plastic foam side with a plastic coated, which forms a connection with the plastic foam. The coating may e.g. be prepared by that fine-grained particles made of the same plastic as the plastic foam spread on the paper and subsequently be melted.

Ein Haftvermittler kann auch durch eine zwischen gelegte Kunststoff-Folie gebildet werden.One Adhesive can also by an interposed plastic film be formed.

Günstig ist es, wenn der mit Papier zu beschichtende Kunststoffschaum an zwei gegenüberliegenden Seiten zu beschichten. Damit wird eine gleichmäßige Ausdehnung/Kontraktion bei Temperaturänderungen gewährleistet.Cheap is it, when the plastic foam to be coated with paper on two opposite To coat pages. This will be a uniform expansion / contraction at temperature changes guaranteed.

Eine Presse ist besonders für eine Beschichtung an mehreren Seiten geeignet. Darüber hinaus können mit einer Presse gleichzeitig mehrere Beschichtungsvorgänge erledigt werden.A Press is especially for a coating on several sides suitable. In addition, with a press simultaneously several coating operations done become.

Die Beschichtungsvorgänge können auch mehrmals wiederholt werden. Vorteilhafterweise eignet sich Papier sehr gut zum Bedrucken. Es kann jegliches Dekor aufgedruckt werden.The coating operations can also be repeated several times. Advantageously eig Paper is very good for printing. Any decor can be printed.

Mit dem erfindungsgemäßen Verfahren lassen sich z.B. wirtschaftlich sehr günstige Dekorflächen erzeugen. Ein Anwendungsfeld bilden Wandverkleidungen wie z.B. die Imitation von Holzvertäfelung oder die Imitation von Steinflächen, z.B. Marmorflächen. Gegenüber echtem Holze sind die erfindungsgemäßen Imitationen nicht riß/feuchtigkeitsgefährdet. Desgleichen ist das Gewicht sehr günstig. Leichte Klebungen sichern erfindungsgemäße Verkleidungen in jeder gewünschten Position.With the method according to the invention can be e.g. economically produce very cheap decorative surfaces. One field of application is wall cladding, e.g. the imitation of wood paneling or the imitation of stone surfaces, e.g. Marble surfaces. Across from real wood imitations of the invention are not crack / moisture vulnerable. Similarly the weight is very cheap. light Bonding secure inventive panels in every desired Position.

Vorzugsweise wird das erfindungsgemäß aufgebrachte Papier bzw. Dekorpapier mit einer Schutzlackierung versehen, farbig oder farblos, je nach Bedarf.Preferably is applied according to the invention Paper or decorative paper provided with a protective coating, colored or colorless, as needed.

In der Zeichnung ist ein Ausführungsbeispiel einer Erfindung dargestellt.In The drawing is an embodiment of a Invention shown.

Die Zeichnung zeigt eine Mehrfachpresse, bestehend aus einer unteren Traverse 1, einer oberen Traverse 2, Führungs- und Zugstangen 3 und 4, darauf gleitenden Pressenteilen 6 und 7 und einem hydraulischen Kraftkolben 5.The drawing shows a multiple press, consisting of a lower crossbar 1 , an upper crossbar 2 , Guide and tie rods 3 and 4 , sliding on it press parts 6 and 7 and a hydraulic power piston 5 ,

Die Teile 1, 6 und 7 sind beheizt. Die Beheizung erfolgt elektrisch mit einer Vielzahl gleichmäßig verteilter Heizpatronen, die sich leicht steuern bzw. kontrollieren lassen, weil sie integrierte Temperaturfühler besitzen.The parts 1 . 6 and 7 are heated. The heating is done electrically with a variety of uniformly distributed heating cartridges that can be easily controlled or controlled, because they have integrated temperature sensor.

Im Ausführungsbeispiel werden geschälte Bahnen 11 aus Schwerschaum aus Polypropylen mit einem Raumgewicht von 150 kg pro Kubikmeter beiderseits mit Dekorpapier 10 beschichtet.In the embodiment, peeled webs 11 made of polypropylene foam with a density of 150 kg per cubic meter on both sides with decorative paper 10 coated.

Jeweils befindet sich eine Bahn 11 mit zwei Dekorpapieren 10 zwischen den Pressenteilen 6 und 7 bzw. 1 und 7.In each case there is a train 11 with two decor papers 10 between the press parts 6 and 7 respectively. 1 and 7 ,

Durch Betätigung des hydraulischen Kraftkolbens 5 werden alle Teile gegeneinander gepreßt. Zugleich erfährt der Kunststoffschaum an der Oberfläche eine Erwärmung bis auf Schmelztemperatur. Dabei ist die Heiztemperatur auf 200 Grad Celsius gestellt. Die Einwirkungsdauer ist durch einige Versuche so gewählt, daß genau die Schmelztemperatur an der Kunststoffschaumoberfläche erreicht wird und eine geringe Aufschmelzung stattfindet, so daß das Papier an dem Kunststoffschaum haftet.By actuating the hydraulic power piston 5 All parts are pressed against each other. At the same time the plastic foam on the surface undergoes heating up to melting temperature. The heating temperature is set to 200 degrees Celsius. The exposure time is selected by some experiments so that exactly the melting temperature is reached on the plastic foam surface and a small melting takes place, so that the paper adheres to the plastic foam.

Nach ausreichender Abkühlung können die beschichteten Platten der Presse wieder entnommen werden.To sufficient cooling can the coated plates are removed from the press again.

Danach erfolgt eine Schutzlackierung mit farblosem Lack.After that a protective coating with colorless varnish.

Claims (15)

Verfahren zur Oberflächenbehandlung von Kunststoffschaumteilen, insbesondere von Kunststoffschaumschnittflächen, dadurch gekennzeichnet, daß Papier aufgeklebt oder aufkaschiert wird, insbesondere aufgebügelt wird.Process for the surface treatment of plastic foam parts, in particular plastic foam cut surfaces, characterized in that paper is glued or laminated, in particular ironed. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für Kunststoffschaumschnittflächen mit offenen Zellen ein Kleber mit einer Menge von 5 bis 80 Gramm pro Quadratmeter, vorzugsweise 20 bis 40 Gramm pro Quadratmeter aufgetragen wird.Method according to claim 1, characterized in that that for plastic foam cut surfaces with open Cells an adhesive at a rate of 5 to 80 grams per square meter, preferably 20 to 40 grams per square meter is applied. Verfahren nach Anspruch 1 oder 2, gekennzeichnet durch Dispersionskleber, Acrylkleber oder Polyurethankleber.A method according to claim 1 or 2, characterized by dispersion adhesive, acrylic adhesive or polyurethane adhesive. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß beim Aufbügeln eine Temperatur an der Kunststoffschaumoberfläche erzeugt wird, die höchstens 20 vorzugsweise 10 Grad Celsius unter dem Schmelzpunkt des Kunststoffes liegt und/oder höchstens 20, vorzugsweise 10 Grad Celsius über dem Schmelzpunkt des Kunststoffes liegt.Method according to claim 1, characterized in that that at iron on a temperature is generated at the plastic foam surface, the maximum Preferably 10 degrees Celsius below the melting point of the plastic lies and / or at most 20, preferably 10 degrees Celsius above the melting point of the plastic lies. Verfahren nach Anspruch 4, gekennzeichnet durch Verwendung eines Papiers mit einem Flächengewicht von 5 bis 100 Gramm pro Quadratmeter.Method according to claim 4, characterized by use a paper with a basis weight from 5 to 100 grams per square meter. Verfahren nach einem der Ansprüche 1, 4, 5, dadurch gekennzeichnet, daß die Bügelwärme an der dem Kunststoffschaum abgewandten Seite auf dem Papier aufgebracht wird.Method according to one of Claims 1, 4, 5, characterized that the Ironing heat at the applied to the plastic foam side facing away from the paper becomes. Verfahren nach Anspruch 6, gekennzeichnet durch die Verwendung eines Bügeleisens und/oder einer Heizwalze und/oder einer beheizten Presse.Method according to claim 6, characterized by Use of an iron and / or a heating roller and / or a heated press. Verfahren nach Anspruch 7, gekennzeichnet durch die Verwendung einer Mehrfachpresse.Method according to claim 7, characterized by Using a multiple press. Verfahren nach Anspruch 7 oder 8, gekennzeichnet durch die Verwendung von elektrischen Heizpatronen, insbesondere mit integriertem Temperaturfühler.A method according to claim 7 or 8, characterized through the use of electric heating cartridges, in particular with integrated temperature sensor. Verfahren nach einem der Ansprüche 7 bis 9, gekennzeichnet durch eine Kühlung nach der Beschichtung.Method according to one of claims 7 to 9, characterized by cooling after the coating. Verfahren nach einem der Ansprüche 7 bis 10, gekennzeichnet durch eine gleichzeitige Beschichtung mehrerer Flächen in einer HeizpresseMethod according to one of claims 7 to 10, characterized by simultaneously coating several surfaces in a heating press Verfahren nach einem der Ansprüche 1 bis 11, gekennzeichnet durch eine Mehrfachbeschichtung.Method according to one of claims 1 to 11, characterized by a Mehrfachbeschich tung. Verfahren nach einem der Ansprüche 1 bis 12, gekennzeichnet durch die Verwendung eines Dekorpapiers.Method according to one of claims 1 to 12, characterized through the use of a decorative paper. Verfahren nach einem der Ansprüche 1 bis 13, gekennzeichnet durch eine Schutzlackierung nach dem Beschichten.Method according to one of claims 1 to 13, characterized by a protective coating after coating. Verfahren nach einem der Ansprüche 1 bis 14, gekennzeichnet durch die Anwendung auf extrudierte Schäume wie auch auf Partikelschaumformteile, auch auf geschälte Kunststoffschaumteile, insbesondere Bahnen und Platten.Method according to one of claims 1 to 14, characterized by application to extruded foams as well as to particle foam moldings, also peeled Plastic foam parts, in particular webs and plates.
DE10133813A 2001-05-20 2001-07-16 Surface treatment of cut foam plastic panels comprises pressing glued paper sheets on to their surfaces Withdrawn DE10133813A1 (en)