DE10017273A1 - Production of precipitated calcium carbonate comprises controlling the functional properties of the product by controlling the viscosity of the milk of lime - Google Patents
Production of precipitated calcium carbonate comprises controlling the functional properties of the product by controlling the viscosity of the milk of limeInfo
- Publication number
- DE10017273A1 DE10017273A1 DE2000117273 DE10017273A DE10017273A1 DE 10017273 A1 DE10017273 A1 DE 10017273A1 DE 2000117273 DE2000117273 DE 2000117273 DE 10017273 A DE10017273 A DE 10017273A DE 10017273 A1 DE10017273 A1 DE 10017273A1
- Authority
- DE
- Germany
- Prior art keywords
- lime
- milk
- precipitated calcium
- lime milk
- viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Die Erfindung betrifft ein Verfahren zur Herstellung von gefälltem Calciumcarbonat (CCP), das als funktioneller Füll stoff geeignet ist und sich durch definierte Eigenschaften auszeichnet. Ein typisches Anwendungsgebiet ist seine Verwen dung als Füllstoff in z. B. Plastisolen, Unterbodenschutzmas sen für Automobile, Dichtungsmassen und Druckfarben.The invention relates to a method for producing precipitated calcium carbonate (CCP), which is a functional filler is suitable and characterized by defined properties distinguished. A typical application is its use dung as a filler in z. B. plastisols, underbody protection mas for automobiles, sealants and printing inks.
Das gefällte Calciumcarbonat ist hier in der Lage, das Fließverhalten der Massen zu steuern. So können durch Einsatz der jeweilig geeigneten Calciumcarbonate Massen mit sehr unterschiedlichem Fließverhalten hergestellt werden. Als ein typisches Charakteristikum für die anwendungstechnische Eig nung von Calciumcarbonaten als Füllstoff wird üblicherweise die Fließgrenze nach Bingham im Weichmachergemisch (SEB) an gegeben. Je nach Anwendungszweck können hohe, mittlere oder niedrige Fließgrenzen gewünscht sein. Die Fähigkeit des ge fällten Calciumcarbonates, die Fließgrenzen zu steuern, wird unter anderem durch die Beschaffenheit des für die Herstel lung der Kalkmilch verwendeten Kalksteins, den Brennbedingun gen des Kalksteins und den Löschvorgang beeinflußt.The precipitated calcium carbonate is able to do this To control the flow behavior of the masses. So through use the respective suitable calcium carbonate masses with very different flow behavior can be produced. As a typical characteristic for the technical application Calcium carbonates as a filler is usually used the yield point to Bingham in the plasticizer mixture (SEB) given. Depending on the application, high, medium or low flow limits may be desired. The ability of the ge felled calcium carbonates to control the flow limits among other things by the nature of the for the manufacturer lime milk used, the burning conditions limestone and the deletion process.
Feindisperses Calciumcarbonat wird entweder aus natür lich vorkommenden Rohstoffen durch mechanische Aufbereitung oder auf chemischem Wege z. B. durch Fällung hergestellt.Finely dispersed calcium carbonate is either made from natural occurring raw materials through mechanical processing or by chemical means e.g. B. made by precipitation.
Üblicherweise wird gefälltes Calciumcarbonat durch Ein
leiten von CO2 in Kalkmilch hergestellt.
Precipitated calcium carbonate is usually produced by introducing CO 2 into milk of lime.
Ca(OH)2 + CO2 → CaCO3 + H2O Ca (OH) 2 + CO 2 → CaCO 3 + H 2 O
Die Eigenschaften des gefällten Calciumcarbonates sind z. B. abhängig von der chemischen Zusammensetzung des einge setzten Kalksteines, den Brennbedingungen und den Löschbedin gungen.The properties of the precipitated calcium carbonate are e.g. B. depending on the chemical composition of the set limestone, the firing conditions and the extinguishing conditions conditions.
Kalkstein unterschiedlicher Herkunft oder Zusammenset zung führt zu Calciumcarbonat mit sehr unterschiedlichen an wendungstechnischen Eigenschaften. Der Mechanismus dieser Be einflussung ist zur Zeit nicht genau bekannt. Es ist jedoch bekannt, daß z. B. Fe2+, Zn 2+, Cl-, Mn2+ und Be2+ Spuren die Kristallisation des CCP stören. In der Praxis vermeidet man z. B. hohe Magnesiumgehalt im Kalkstein, wenn hohe Fließgren zen angestrebt werden.Limestone of different origins or compositions leads to calcium carbonate with very different application properties. The mechanism of this influence is currently not exactly known. However, it is known that e.g. B. Fe2 + , Zn 2 + , Cl - , Mn2 + and Be2 + traces interfere with the crystallization of the CCP. In practice you avoid e.g. B. high magnesium content in limestone when high flow limits are aimed for.
Zur Herstellung von gefälltem Calciumcarbonat wird vor zugsweise sogenannter Weichbrannt eingesetzt. Hierzu wird Kalkstein bei einer Temperatur von 1.000 bis 1.250°C ge brannt.For the preparation of precipitated calcium carbonate is used preferably used so-called soft burn. To do this Limestone at a temperature of 1,000 to 1,250 ° C burns.
Der Brennvorgang wird üblicherweise in sogenannten Schachtöfen oder auch in Drehrohröfen durchgeführt. Als Brennstoff können z. B. Koks, Öl oder Erdgas verwendet wer den. Hierbei führen niedrige Brenntemperaturen zu hohen Kalk milchviskositäten. Die Verwendung dieser Kalkmilch für die CCP-Herstellung führt damit auch zu kleinen Teilchendurchmes sern des CCP und hohen Fließgrenzen im Weichmachergemisch. Entsprechend führen hohe Brenntemperaturen zu niedrigen Kalk milchviskositäten, groben CCP-Teilchen und niedrigen Fließ grenzen im Weichmachergemisch. Die Ausbeute an Branntkalk ist hierbei bei mittleren Temperaturen am höchsten, da bei nied rigen Temperaturen nicht alles CaCO3 zum CaO umgesetzt wird und bei hohen Temperaturen ein Teil den CaO überbrannt wird, d. h. er läßt sich mit den üblichen Methoden nicht mehr löschen.The burning process is usually carried out in so-called shaft furnaces or in rotary tube furnaces. As a fuel z. B. coke, oil or natural gas who used the. Low firing temperatures lead to high lime milk viscosities. The use of this lime milk for the CCP production therefore also leads to small particle diameters of the CCP and high flow limits in the plasticizer mixture. Accordingly, high firing temperatures lead to low lime milk viscosities, coarse CCP particles and low flow limits in the plasticizer mixture. The yield of quicklime is highest at medium temperatures, since not all CaCO 3 is converted to CaO at low temperatures and at high temperatures a portion of the CaO is overburned, ie it can no longer be extinguished using the usual methods.
Zur Charakteristik des Branntkalkes wird u. a. seine Fähigkeit, mit Wasser zu reagieren herangezogen. Gemessen wird der sogenannte VEC-Wert (Velocite d'Extinction de Chaux). Hierbei wird die Aufheizgeschwindigkeit einer defi nierten Wasser-Branntkalkmischung gemessen. Typische VEC- Werte für Branntkalk, der für die Herstellung von gefälltem Calciumcarbonat geeignet ist, liegen oberhalb 3°C/min.The characteristic of the quicklime is u. a. his Ability to react with water. Measured the so-called VEC value (Velocite d'Extinction de Chaux). The heating rate of a defi water and quicklime mixture measured. Typical VEC Values for quicklime, for the production of precipitated Calcium carbonate is suitable, are above 3 ° C / min.
Zur Herstellung der Kalkmilch wird der Branntkalk z. B. in einer Löschtrommel mit Wasser zur Reaktion gebracht, wobei sich eine Ca(OH)2-Suspension, die sogenannte Kalkmilch bil det. Die Kalkmilch hat üblicherweise einen Feststoffgehalt von 70 bis 220 g/l Ca(OH)2, eine Viskosität von 30 bis 2.500 m Pas und einen mittleren Teilchendurchmesser unter 50 µm.For the production of the milk of lime, the quicklime z. B. in an extinguishing drum with water to react, with a Ca (OH) 2 suspension, the so-called milk of lime bil det. The lime milk usually has a solids content of 70 to 220 g / l Ca (OH) 2 , a viscosity of 30 to 2,500 m Pas and an average particle diameter of less than 50 μm.
Kalkmilch wird z. B. zur Neutralisation von Abwasser, zur Herstellung von Soda oder gefälltem Calciumcarbonat ver wendet.Lime milk is e.g. B. for neutralizing waste water, for the production of soda or precipitated calcium carbonate turns.
Ein Nachteil der bisher bekannten Verfahren zur Herstel lung von gefälltem Calciumcarbonat ist, daß dessen anwen dungstechnische Eigenschaften, insbesondere als Rheologie steuerndes Additiv bisher nur ungenügend einstellbar sind.A disadvantage of the previously known manufacturing processes Precipitated calcium carbonate is used for this purpose manure properties, especially as rheology controlling additive have so far been insufficiently adjustable.
Aufgabe der Erfindung ist die Herstellung von gefälltem Calciumcarbonat (CCP) mit in breitem Bereich steuerbaren de finierten und reproduzierbaren Eigenschaften.The object of the invention is the production of precipitated Calcium carbonate (CCP) with de controllable in a wide range refined and reproducible properties.
Erfindungsgemäß wir die Aufgabe dadurch gelöst, daß für die Herstellung des Calciumcarbonates mit bestimmten rheolo gischen Eigenschaften eine Kalkmilch mit genau der Viskosität bei gegebener Konzentration eingesetzt wird, die zu den ge wünschten Eigenschaften des CCP führt. Durch die Viskosität der Kalkmilch werden also die Eigenschaften des Calciumcarbo nates als Rheologie steuerndes Additiv eingestellt.According to the invention we solved the problem in that for the production of calcium carbonate with certain rheolo lime milk with exactly the same viscosity is used at a given concentration that corresponds to the ge desired properties of the CCP. Because of the viscosity the milk of lime becomes the properties of calcium carbo nates set as a rheology control additive.
Je nach Verwendungszweck werden unterschiedliche Fließ grenzen des CCP gewünscht. In Plastisolen strebt man hohe Fließgrenzen an. Diese werden erreicht, indem Kalkmilch mit Viskositäten oberhalb 750 mPas eingesetzt wird. In Druckfarben werden mittlere Fließgrenzen angestrebt, so daß hierfür Kalkmilch mit Viskositäten zwischen 100 und 150 mPas einge setzt wird. Für hochgefüllte Silikonmassen werden CCP mit niedriger Fließgrenze eingesetzt, so daß hier Kalkmilch mit einer Viskosität unter 100 mPas Verwendung findet.Depending on the intended use, different flow limits of the CCP desired. One strives for high in plastisols Yield limits. These are achieved by using lime milk Viscosities above 750 mPas is used. In printing inks medium flow limits are aimed for, so that Lime milk with viscosities between 100 and 150 mPas is set. For highly filled silicone compounds, CCP are included low yield point used, so that here milk of lime with a viscosity below 100 mPas is used.
Die so hergestellte Kalkmilch mit eingestellter Viskosi tät wird anschließend einem Reaktor zugeführt, in den CO2 enthaltendes Gas zur Fällung des Calciumcarbonates eingelei tet und homogen in der Kalkmilch dispergiert wird.The milk of lime thus produced with the viscosity set is then fed to a reactor, into which gas containing CO 2 for precipitating the calcium carbonate is introduced and is homogeneously dispersed in the milk of lime.
Das gefällte Calciumcarbonat kann je nach Verwendungs zweck mit Fettsäuren nachbehandelt werden.The precipitated calcium carbonate can vary depending on the use after-treatment with fatty acids.
Es wurde überraschend gefunden, daß die Eigenschaften des gefällten Calciumcarbonates reproduzierbar sind und in breiten Bereichen variiert werden können, wenn die Viskosität der Kalkmilch eingestellt wird, und danach CO2 zur Fällung des Calciumcarbonates eingeleitet wird.It has surprisingly been found that the properties of the precipitated calcium carbonate are reproducible and can be varied over a wide range if the viscosity of the lime milk is adjusted and CO 2 is then introduced to precipitate the calcium carbonate.
Vergleicht man die Verfahren zur Herstellung von gefäll tem Calciumcarbonat aus unterschiedlich viskoser Kalkmilch, so fällt auf, daß die Viskosität einen Einfluß auf die Reak tionsgeschwindigkeit, auf den mittleren Teilchendurchmesser des gebildeten CaCO3 und auf die anwendungstechnischen Eigen schaften des CCP hat.Comparing the processes for the preparation of precipitated calcium carbonate from differently viscous lime milk, it is noticeable that the viscosity has an influence on the reaction rate, on the average particle diameter of the CaCO 3 formed and on the application properties of the CCP.
Es wurde gefunden, daß eine zunehmende Viskosität der Kalkmilch auch eine Abnahme des mittleren Teilchendurchmes sers der Primärteilchen des CCP nach sich zieht.It has been found that an increasing viscosity of the Lime milk also a decrease in the mean particle diameter of the primary particles of the CCP.
Es wurde weiterhin gefunden, daß durch die Steuerung der Viskosität der Kalkmilch die Fälldauer um ca. 20% ge senkt werden kann.It was also found that by the controller the viscosity of the lime milk the precipitation time by approx. 20% can be lowered.
Durch die erfindungsgemäße Einstellung der Viskosität der Kalkmilch ist es möglich, die Fließgrenze der CCP-ge füllten Plastisole signifikant zu beeinflussen, also gezielt einzustellen. Es wurde gefunden, daß die Fließgrenze eine Funktion der Viskosität der Kalkmilch bei gegebener Konzen tration ist. Es wurde also gefunden, daß die Eigenschaften des CCP durch die gezielt einstellbaren Viskositäten der Kalkmilch reproduzierbar beeinflußt werden können.By adjusting the viscosity according to the invention the lime milk it is possible to limit the yield point of the CCP filled plastisols significantly, so targeted adjust. The yield point was found to be one Function of the viscosity of the milk of lime at a given concentration tration is. So it was found that the properties of the CCP through the specifically adjustable viscosities of the Lime milk can be influenced reproducibly.
Die unerwünschte Beeinflussung der Eigenschaften des CCP durch undefinierte Schwankungen der Beschaffenheit des Kalk steins des Brennprozesses und des Löschvorganges kann z. B. durch das definierte Mischen verschiedener Kalke aufgehoben werden, wobei das Mischen der Kalke in dem Verhältnis er folgt, aus dem nach anschließendem Löschen die gewünschte Kalkmilchviskosität resultiert.The undesirable influence on the properties of the CCP due to undefined fluctuations in the quality of the lime Stone of the burning process and the extinguishing process can e.g. B. canceled by the defined mixing of different limes be, mixing the limes in the ratio he follows, from which the desired one is then deleted Lime milk viscosity results.
Erfindungsgemäß kann die Viskosität eingestellt werden, indem Branntkalke, die bei alleiniger Verwendung zu Kalk milchen mit sehr unterschiedlichen Viskositäten führen wür den, in einem solchen Verhältnis miteinander vermischt und gelöscht oder gemeinsam gelöscht werden, daß die gewünschte Viskosität der Kalkmilch eingestellt wird. Es ist ebenfalls möglich, jeden Kalk zunächst für sich zu löschen und an schließend die Kalkmilche miteinander zu vermischen. Weiter hin können die beiden Kalke im festgelegten Verhältnis sepa rat in die Löschapparatur gegeben werden, wo dann die ge wünschte Mischung gebildet wird, aus dem die gewünschte Kalk milchviskosität resultiert.According to the invention, the viscosity can be adjusted adding quicklime to lime when used alone lead milk with very different viscosities the, mixed in such a relationship and deleted or deleted together that the desired Lime milk viscosity is adjusted. It is also possible to first delete and turn on each lime finally mix the lime milk together. Next the two limes can be separated in a fixed ratio advice into the extinguishing apparatus, where the ge desired mixture is formed from which the desired lime milk viscosity results.
In einer Ausführungsform der Erfindung wird die Messung der Viskosität der Kalkmilch zur Steuerung des Mischungsver hältnisses der Kalkmilchsorten genutzt. Die Viskosität ist problemlos z. B. kontinuierlich zu messen, und über einen entsprechenden Regelkreis kann automatisch das Mischungsver hältnis der beiden Kalke und damit die resultierende Kalk milchqualität sehr genau gesteuert werden. In one embodiment of the invention, the measurement the viscosity of the milk of lime to control the mixing ratio ratio of the milk of lime. The viscosity is easily z. B. to measure continuously, and over a the corresponding control loop can automatically mix the Ver ratio of the two limes and thus the resulting lime milk quality can be controlled very precisely.
Branntkalk 1 und Branntkalk 2 werden in verschiedenen Ver
hältnissen miteinander vermischt und in einer Löschtrommel
gelöscht:
VEC Branntkalk 1: 4,8°C/min.
VEC Branntkalk 2: 9,8°C/min.
Stückelung jeweils: 2-5 cmQuicklime 1 and quicklime 2 are mixed together in different ratios and extinguished in an extinguishing drum:
VEC quicklime 1: 4.8 ° C / min.
VEC quicklime 2: 9.8 ° C / min.
Denomination each: 2-5 cm
Aus der so gemahlenen Kalkmilch wurde durch Einleiten von CO2-haltigem Gas Calciumcarbonat hergestellt:Calcium carbonate was produced from the lime milk thus ground by introducing CO 2 -containing gas:
Fälltemperatur: 18°C
CO2 Falling temperature: 18 ° C
CO 2
-Konzentration im Fällgas: 30 Vol.-%
Gasstrom: 1 m3 Concentration in the precipitation gas: 30 vol .-%
Gas flow: 1 m 3
/h pro 10 l Kalkmilch
Fälldauer: siehe Tabelle
Nachbehandlung: Fettsäurebehandlung mit
(0,85 mg Stearinsäure)/
(m2 / h per 10 l milk of lime
Felling time: see table
Post-treatment: fatty acid treatment with (0.85 mg stearic acid) / (m 2
CCP-Oberfläche)
CCP surface)
Es wird deutlich, daß durch das Mischen der Kalke die Visko sität der Kalkmilch gezielt gesteuert werden kann. Dadurch kann die Fälldauer von CCP bis zu 20% gesenkt werden. Die Teilchendurchmesser von CCP werden reproduzierbar einge stellt. Die Fließgrenze eines Gemisches aus Weichmacher und Calciumcarbonat kann reproduzierbar gesteuert werden. It becomes clear that by mixing the limes the visco quantity of lime milk can be controlled in a targeted manner. Thereby CCP's downtime can be reduced by up to 20%. The CCP particle diameters are reproducibly incorporated poses. The yield point of a mixture of plasticizer and Calcium carbonate can be controlled reproducibly.
Die Viskosität der Kalkmilch kann auch gesteuert werden, in dem die Kalkmilch gemahlen wird. Zur Mahlung der Kalkmilch können an sich bekannte Mühlen verwendet werden. Vorzugsweise werden Perlmühlen eingesetzt. Als Mahlperlen eignen sich ins besondere Zirkonoxid-Mahlperlen mit einem Durchmesser von 0,4 bis 2 mm. Das Mahlergebnis wird durch die Feinheit der Perlen stark beeinflußt.The viscosity of the lime milk can also be controlled in to which the lime milk is ground. For grinding lime milk mills known per se can be used. Preferably pearl mills are used. As grinding pearls are suitable special zirconium oxide grinding beads with a diameter of 0.4 up to 2 mm. The fineness is determined by the fineness of the pearls strongly influenced.
Der Mahleffekt wird außerdem durch die Drehzahl der Mühle, die Verweilzeit der Kalkmilch in der Mühle und den sich daraus ergebenden spezifischen Energieeintrag gesteuert.The grinding effect is also determined by the speed of the mill, the dwell time of the lime milk in the mill and the itself resulting specific energy input controlled.
Branntkalk wurde in einer Löschtrommel gelöscht:
Stückelung: 1-5 cm
VEC: 4,8°C/minSlaked lime was extinguished in an extinguishing drum:
Denomination: 1-5 cm
VEC: 4.8 ° C / min
Die resultierende Kalkmilch wurde gemahlen und charakteri
siert:
Feststoffgehalt: 150 g/l
Mahlbedingungen:
Horizontale Rührwerkskugelmühle
Mahlkammervolumen 5 l
Motorleistung 22 kW
Mahlkörper:
Kugeln aus Zirkonsilikat
Durchmesser 1,0-1,6 mm
Eingefülltes Volumen 4,8 lThe resulting lime milk was ground and characterized:
Solids content: 150 g / l
Grinding conditions:
Horizontal agitator ball mill
Grinding chamber volume 5 l
Motor power 22 kW
Grinding media:
Zirconia balls
Diameter 1.0-1.6 mm
Filled volume 4.8 l
Die Versuche werden bei konstanter Drehzahl von 1.990 U/min. durchgeführt. Die Verweilzeit der Kalkmilch in der Mühle wurde variiert. Daraus ergaben sich verschiedene spezifische Energieeinträge.The tests are carried out at a constant speed of 1,990 rpm. carried out. Lime milk in the mill was varied. This resulted in several specific ones Energy inputs.
Aus der so gemahlenen Kalkmilch wurde durch Einleiten von CO2-haltigem Gas Calciumcarbonat hergestellt:Calcium carbonate was produced from the lime milk thus ground by introducing CO 2 -containing gas:
Fälltemperatur: 18°C
CO2 Falling temperature: 18 ° C
CO 2
-Konzentration im Fällgas: 30 Vol.-%
Gasstrom: 1 m3 Concentration in the precipitation gas: 30 vol .-%
Gas flow: 1 m 3
/h pro 10 l Kalkmilch
Fälldauer: siehe Tabelle
Nachbehandlung: Fettsäurebehandlung mit
(0,85 mg Stearinsäure)/
(m2 / h per 10 l milk of lime
Felling time: see table
Post-treatment: fatty acid treatment with (0.85 mg stearic acid) / (m 2
CCP-Oberfläche)
CCP surface)
Es wird deutlich, daß durch die Naßmahlung die Viskosität der Kalkmilch und der mittlerer Teilchendurchmesser der Kalkmilch gezielt gesteuert werden können. Dadurch kann die Fälldauer von CCP bis zu 20% gesenkt werden. Die Teilchendurchmesser von CCP werden reproduzierbar eingestellt. Die Fließgrenzen werden erhöht.It is clear that the viscosity of the Lime milk and the average particle diameter of the lime milk can be controlled in a targeted manner. This can reduce the downtime can be reduced by CCP up to 20%. The particle diameter from CCP are reproducibly set. The flow limits are increased.
Es ist ebenfalls möglich, durch Variation der Brennbedingun gen Einfluß auf die Viskosität der resultierenden Kalkmilch zu nehmen. Es ist im Sinne der Erfindung, die Brenntemperatu ren im Bereich von 900 bis 1.200°C zu variieren. It is also possible to vary the firing conditions influence on the viscosity of the resulting lime milk to take. It is in the spirit of the invention, the firing temperature range from 900 to 1,200 ° C.
Kalkstein wird auf eine Körnung von < 10 mm gebrochen und an schließend 4 Stunden bei verschiedener Temperatur gebrannt. Nach dem Abkühlen wird der Kalk in einem gerührten Behälter gelöscht. Dazu wird dieser in Portionen zu Wasser gegeben. Die Portionen werden so gewählt, daß eine Temperatur im Löschbehälter 95°C nicht überschreitet. Insgesamt werden 200 g Branntkalk in 1 l Wasser gegeben. Nach vollständiger Reaktion wird der Rückstand über ein 100 µm-Sieb abgesiebt und ausgewogen. Die Kalkmilch wird auf 150 g/l verdünnt. Durch Einleiten von CO2 enthaltendem Gas in diese Kalkmilch wird CCP hergestellt.Limestone is broken down to a grain size of <10 mm and then burned for 4 hours at different temperatures. After cooling, the lime is extinguished in a stirred container. This is added to the water in portions. The portions are chosen so that a temperature in the extinguishing container does not exceed 95 ° C. A total of 200 g quicklime is added to 1 l water. After the reaction is complete, the residue is sieved through a 100 μm sieve and weighed out. The lime milk is diluted to 150 g / l. CCP is produced by introducing gas containing CO 2 into this milk of lime.
Fälltemperatur: 18°C
CO2 Falling temperature: 18 ° C
CO 2
-Konzentration im Fällgas: 30%
Gasstrom: 1 m3 -Concentration in the precipitation gas: 30%
Gas flow: 1 m 3
/h pro 10 l Kalkmilch
Nachbehandlung: Fettsäurebehandlung mit 0,85 g
Stearinsäure/m2 / h per 10 l milk of lime
Aftertreatment: fatty acid treatment with 0.85 g stearic acid / m 2
CCP-Oberfläche
CCP surface
Es ist im Sinne der Erfindung, eine Kalkmilch mit einer Vis kosität von 20 bis max. 2.500 mPas (gemessen bei 25°C) her zustellen. Eine höhere Viskosität sollte vermieden werden, da sonst die Eintragung des Fällgases nicht optimal möglich ist.It is within the meaning of the invention to make a lime milk with a vis viscosity from 20 to max. 2,500 mPas (measured at 25 ° C) to deliver. A higher viscosity should be avoided because otherwise the entry of the precipitation gas is not optimally possible.
Zur homogenen Dispergierung des Fällgases ist eine gute Fließfähigkeit der Kalkmilch erforderlich. A good one is for homogeneous dispersion of the precipitation gas Lime milk required to flow.
Je nach Anwendungszweck kann somit CaCO3, das als Mischungs bestandteil mit hoher Funktionalität für z. B. Polymere, Polymerzubereitungen, Kunststoffe, Überzugsmassen, Dichtungs massen, Papier oder Farben, insbesondere Druckfarben geeignet ist, in gleichbleibender Qualität bereitgestellt werden.Depending on the application, CaCO 3 can therefore be used as a component with high functionality for e.g. B. polymers, polymer preparations, plastics, coating compositions, sealing compounds, paper or paints, in particular printing inks is suitable, are provided in consistent quality.
Claims (7)