CN85109634A - The method of hydrocracking catalyst and application alumo-silicate molecular sieve - Google Patents
The method of hydrocracking catalyst and application alumo-silicate molecular sieve Download PDFInfo
- Publication number
- CN85109634A CN85109634A CN85109634.4A CN85109634A CN85109634A CN 85109634 A CN85109634 A CN 85109634A CN 85109634 A CN85109634 A CN 85109634A CN 85109634 A CN85109634 A CN 85109634A
- Authority
- CN
- China
- Prior art keywords
- sapo
- catalyzer
- weight
- zeolite
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclose the hydrogenolysis of using the catalyzer that contains alumo-silicate, this alumo-silicate is from No. 4440871, United States Patent (USP), and it is characterised in that its calcinated form is at ℃ following oxygen of absorption at least 4% (weight) of dividing potential drop 100 torrs and temperature-186.
Description
The method that the present invention relates to comprise the hydrocracking catalyst of special alumo-silicate molecular sieve and use these hydrocracking catalysts.
The document of relevant this class catalyzer and application method thereof is considerable.In a large amount of patents of some technical task, every clear and definite problem has easily all proposed its technical field, for example application of some zeolite in hydrocracking catalyst.The representative of this field patent be with hydrocracking in use the relevant patent of ZSM-type zeolite, it comprises: No. 3894934, United States Patent (USP) (ZSM-5), No. 3871993 (ZSM-5, ZSM-11, ZSM-12 and ZSM-21), No. 3702886 (ZSM-5), No. 3758403 (ZSM-5 combines with zeolite Y) and No. 3972983 (ZSM-20).
Though the above-mentioned patent in hydrocracking catalyst aspect the application ZSM type zeolite is important, uses these zeolites and does not still have commercial significance so far.Coml occasion major part concentrates on and further improves the alkali hydrocracking technology about zeolite Y that occurred No. 3130007, United States Patent (USP) (be disclosed in) in the hydrocracking field.
Developed hydrocracking catalyst in many aspects based on y-type zeolite.The method in the following patent of being disclosed in can be used as the explanation of the whole bag of tricks that has proposed:
United States Patent (USP) discloses " the overstable y-type zeolite silico-aluminate of synthetic " for No. 3293192 (referring to No. 3594331, United States Patent (USP), it discloses Z-14HS is zeolite Y), its preparation method be the low Y zeolite of calcining basic metal content, with the alkaline solution that contains ammonium or compound ammonia salt with calcinate carry out continuous alkali exchange until alkali content less than 1%(weight), calcine gained exchange product then.
Though, developed Y type hydrocracking catalyst widely, almost also do not develop fully new, based on the hydrocracking catalyst of the new molecular sieve component of development.This paradox, promptly lacking new catalytic material (although sizable economic benefit is arranged) is because the emphasis of coml hydrocracking work is a zeolite Y.Therefore, patent documentation is also recommended improved zeolite Y.
Now zeolite Y and as catalyzer the application in hydrogenolysis gains public acceptance., the state of the art that relates to zeolite Y and the application in hydrocracking catalyst thereof also is limited to ion exchange technique, aluminium abstraction technique, catalyst preparation technology and in general by the second-stage treatment method of removing aluminium in the zeolite Y.
The difference of hydrocracking catalyst of the present invention and prior art and preparation method thereof is to use one group of novel non-zeolite molecular sieve, and it can be used separately, also can combine use with the catalyzer commonly used in the hydrogenolysis.These new non-zeolite molecular sieves have particular performances, and it can obtain to be different from the resulting products distribution of catalyzer that is produced by zeolite aluminosilicate.
Fig. 1 is reference catalyst (catalyst A) and the petroleum naphtha fraction yield of catalyzer of the present invention (catalyst B) and the graph of a relation of conversion.
Fig. 2 is similar to Fig. 1, has just described catalyzer C of the present invention.
Fig. 3 is the RON(research octane value of the petroleum naphtha fraction of catalyst A and catalyst B) with the graph of a relation that transforms.
Fig. 4 is similar to Fig. 3, and that just describe is catalyzer C.
Fig. 5 is the heavy petrol fraction yield of catalyst A and catalyzer C and the graph of a relation of conversion.
Fig. 6 is the heavy petrol fraction yield of catalyst A and catalyst B and the graph of a relation of conversion.
Fig. 7 is the C of catalyst A and catalyzer C
5Different/the direct ratio of hydrocarbon and the graph of a relation of conversion.
Fig. 8 is the C of catalyst A and catalyzer C
6Different/the direct ratio of hydrocarbon is as the graph of a relation of the function that transforms.
Fig. 9 is the C of catalyst A and catalyst B
5Different/the direct ratio of hydrocarbon is as the graph of a relation of the function that transforms.
Figure 10 is the C of catalyst A and catalyst B
6Hydrocarbon different/just likening graph of a relation to into the function that transforms.
Figure 11 be catalyst A and catalyst B different/just likening graph of a relation to into carbonatoms purpose function.
Figure 12 is the C of catalyst A and catalyzer C
3Yield is as the graph of a relation of the function that transforms.
Figure 13 is the C of catalyst A and catalyst B
3Yield is as the graph of a relation of the function that transforms.
The present invention relates to hydrocracking catalyst and use the method for this catalyst. Catalyst comprises at least a following non-zeolite molecular sieve that will talk about, at least a hydrogenation component and random a kind of particle of making the hydrocracking hydrocarbon feed, having traditional hydrocracking catalyst of catalytic activity, for example contains traditional hydrocracking catalyst particle of the typical zeolite aluminosilicate of usually using in above-mentioned hydrocracking catalyst. This class alumo-silicate molecular sieve of using in the present invention is disclosed in No. 4440871, the United States Patent (USP) usually, they are members of such class alumo-silicate molecular sieve, be that its calcinated form is depressed at the branch of-186 ℃ of temperature and 100 torrs, have and adsorb at least 4%(weight) the supplementary features of oxygen. Traditional catalyst component (catalyst that for example contains zeolite aluminosilicate) can be called the hydrocracking catalyst component, such as so far tradition application in hydrogenolysis, contains various forms of y-type zeolite catalyst etc. The unique point of Catalyst And Method of the present invention is to use special alumo-silicate molecular sieve as catalyst in method, can form the product mixtures that can not obtain with traditional hydrocracking catalyst.
The present invention relates to use the hydroconversion process (seeing aftermentioned for details) of the catalyzer that contains at least a alumo-silicate molecular sieve.Method for hydrogen cracking is by cracking high boiling hydrocarbon raw material and the unsaturates hydrogenation that makes in the raw material, and high boiling hydrocarbon feed is converted into more lower boiling product.
The condition for validity of (seeing: zeolite chemistry and catalysis, Jule A.Rabo, American Chemical Society, the 13rd chapter, 171 special topics (1976)) hydrogenolysis and enforcement thereof in this technical field has belonged to altogether to be known, and knows that they have several frequently seen type.Two kinds of types that are very familiar to are a segment type and two segment types.In a segment type (Unicracking-JHC or damp western hydrocracking) method, raw material wants pre-treatment to remove nearly all sulphur and nitrogen, for example realizes desulfurization and denitrogenation with hydrotreater.Make the hydrocracking of hydrocarbon steam then in reactor in the presence of catalyzer, single-pass conversion is 40% to 70%.Unconverted hydrocarbon can be recycled to the removal process (to remove deammoniation) and the fractionating step that separates converted product behind the gas washing.Two-stage method (Unicracking-JHC) is developed, and second section application that it provides is from the input charging as fractionation plant of the effluent of a segment type hydrogenolysis (by behind the washer of ammonia) and second hydrocracking reactor.Unconverted raw material is recycled to the removal process of second hydrocracking reactor then.Because in fact the catalyzer in second hydrocracking reactor works in the environment of no ammonia, therefore the transformation efficiency in this reactor can maintain higher level, 60-80% for example, and usually can under the temperature lower than first section reactor, transform.
Have been found that the products distribution that obtains when using products distribution that special alumo-silicate molecular sieve forms and not using above-mentioned alumo-silicate molecular sieve is different.Catalyzer of the present invention can use separately, also can with under effective hydrocracking condition, have active general hydrocracking catalyst and be used in combination.So far, the hydrocracking catalyst of prior art need be stood some loss in order to reach optimizing at specific process variable or product property (as octane value).For example, when the application zeolite aluminosilicate is catalyst based, observe the improvement that improves the gasoline octane rating of indicated product by isoparaffin and n-paraffin ratio, be accompanied by the decline of gasoline yield and feedstock conversion.As the indication of higher octane product, therefore, increasing or descending of it is used as the indication of the octane of gasoline product to the ratio of isoparaffin and n-paraffin always.With respect to n-paraffin, the amount of isoparaffin increases, the loss that transforms of gasoline yield and crude oil simultaneously, even have, also not obvious increase, this commercial be crucial.The increase of (product contains at least 5 carbon atoms, and boiling point is lower than 185) isoparaffin and n-paraffin ratio is a particularly important in the petroleum naphtha fraction, because this fraction generally must be not treated again to improve its octane value.
The alumo-silicate molecular sieve of using among the present invention is selected from that class alumo-silicate molecular sieve that is disclosed in No. 4440871, the United States Patent (USP), and they be its calcinated form can also depress at-186 ℃ of temperature, 100 torr branches be adsorbed to few 4%(weight) the sort of alumo-silicate molecular sieve of oxygen.The essential characteristic of its calcinated form of alumo-silicate is to adsorb 2%(weight at least under 20 ℃ of temperature and dividing potential drop 500 torrs) Trimethylmethane.At the non-zeolite molecular sieve of this application, it is characterized in that preferably satisfying one of above-mentioned adsorption criteria, its feature is that also their calcinated form adsorbs triethylamine under 22 ℃ of temperature, dividing potential drop 2.6 torrs amount is zero to less than 5%, preferably less than 3%(weight).
Alumo-silicate molecular sieve with feature of above-mentioned adsorption criteria is selected from the alumo-silicate class that is disclosed in No. 4440871, the United States Patent (USP), is hereby incorporated by; To be described below simultaneously.The alumo-silicate molecular sieve that No. 4440871, United States Patent (USP) is the alumo-silicate of microporous crystalline, and its hole is uniformly, and has the specific diameter greater than about 3 dusts, and basic experience chemical constitution its synthesized form and anhydrous form is:
MR:(Si
XAl
YP
Z) O
2
Wherein " R " represents at least a organic formwork agent that is present in the intracrystalline hole system; " m " represents every mole of (Si
XAl
YP
Z) O
2The mole number that has " R ", " m " value from 0.02 to 0.3; " X " " Y " and " Z " represent the molar fraction of the silicon, aluminium and the phosphorus that exist with tetrahedral oxide respectively, and described molar fraction must drop in the area that the pentagon determined by ABCD and E point on the ternary diagram of the accompanying drawing 1 of No. 4440871, United States Patent (USP) forms.The SAPO molecular sieve that No. 4440871, United States Patent (USP) also is known as has PO
+ 2, AlO
+ 2And SiO
2The alumo-silicate of the three-dimensional microporous framework structure of tetrahedron element, its basic experience chemical constitution when anhydrous form is:
MR:(Si
xAl
yP
z) O
2,
Wherein " R " representative is present at least a organic formwork agent in the crystal inner pore system; " m " represents every mole of (Si
xAl
yP
z) O
2The mole number that has " R ", " m " are worth from zero to 0.3; " X " " Y " and " Z " represent the mole number of the silicon, aluminium and the phosphorus that exist with oxide compound part (oxide moiety) respectively, above-mentioned molar fraction drops in the area of being made up of A, B, C, D and the qualification of E point on the ternary diagram of Fig. 1, above-mentioned alumo-silicate has the X-ray powder diffraction figure of feature, and this figure contains the d spacing of the expression in any one table of table I, III, V, VII, IX, XII, X VII, X XI, XX III or XX V of No. 4440871, United States Patent (USP) below at least.In addition, such crystalline aluminium silicophosphate can be at sufficiently high temperature lower calcination, to remove some organic formwork agent at least that is present in the crystal inner pore system.
The alumo-silicate that No. 4440871, United States Patent (USP), usually be called " SAPO-n " there, as one type, promptly as " SAPO-n ", wherein n is the integer of a kind of specific SAPO of expression, has reported the preparation of specific SAPO in No. 4440871, the United States Patent (USP).Therefore catalyzer of the present invention will be called the catalyzer that contains " SAPO ", contain one or more SAPO of No. 4440871, United States Patent (USP) with the expression catalyzer, catalyzer of the present invention has above-mentioned adsorb oxygen, adsorb isobutane and the characteristic of absorption triethylamine under conditions suitable simultaneously.Applicable SAPO class includes, but is not limited among the present invention: SAPO-11, SAPO-17, SAPO-31, SAPO-33, SAPO-34, SAPO-35, SAPO-40, SAPO-41, SAPO-44 and its mixture.
The SAPO that uses among the present invention
SAbove-mentioned feature relevant with the characterization of adsorption of SAPO, this SAPO through synthetic aftertreatment (for example calcining or chemical treatment) to remove as synthesizing quite most of template " R " that the result exists.Although the adsorpting characteristic of specific herein SAPO oxygen, Trimethylmethane or triethylamine is relevant with the characterization of adsorption of its calcinated form, the present invention also comprises the SAPO that uses non-incinerating or improvement certainly
S, these SAPO
SHave above-mentioned adsorpting characteristic at its calcinated form or improved form since the non-incinerating SAPO that uses under effective hydrocracking condition in the inventive method will be calcined on the spot or hydrothermal treatment consists to make it to have one or more characterization of adsorptions in oxygen, Trimethylmethane and the triethylamine.So SAPO can become the form with above-mentioned characterization of adsorption at on-the-spot disposal, this also is a scope of the present invention.For example, though the calcinated form of SAPO-11 has the characteristic of adsorb isobutane, the SAPO-11 of synthesized form, owing to exist in template " R " in the synthetic product, so there is not the characteristic of above-mentioned adsorb isobutane.Therefore, when talking about its calcinated form and have the SAPO of specific characterization of adsorption, be not the synthesized form that does not use SAPO, the latter can have above-mentioned characterization of adsorption in former ground warp calcining, hydrothermal treatment consists and/or other processing (as: with the ion-exchange of suitable atoms).
Can see this class SAPO as top discussion
SCan obtain to use traditional products distribution that hydrocracking catalyst did not have.So far, the hydrocracking catalyst of prior art (containing zeolite) in order to reach the optimizing of special process variable or product property (for example octane value of gasoline product), always is accompanied by the decline of gasoline yield and/or conversion usually.Use catalyzer of the present invention and can reduce these losses.People wish that the ratio of isoparaffin and n-paraffin in the gasoline product increases, because this reflects higher octane product.
Except the octane value that has improved above-mentioned gasoline product, the improvement of octane value also might be used base metal catalysts in method, and in the past, need obtain the higher octane product with noble metal catalyst.Because base metal catalysts is more stable to charging pollutent, organic compounds containing sulfur usually, therefore, the invention provides do not have loss of octane than stable catalyst (in the past, will follow loss of octane) with base metal catalysts.As noble metal catalyst and SAPO of the present invention
SWhen using together, the present invention can further improve the isoparaffin amount of gasoline product.
Catalyzer of the present invention can with traditional use of hydrocracking catalyst, also can be optionally and application of zeolite aluminosilicate component.The zeolite aluminosilicate component of this class catalyzer can be any silico-aluminate that was used as the hydrocracking catalyst component in the past, for example zeolite Y of various ways.As the hydrocracking catalyst component, the representative of disclosed zeolite aluminosilicate so far is the zeolite Y (zeolite Y that comprises steam stable, as overstable zeolite Y), X zeolite, zeolite beta (No. 3308069, United States Patent (USP)), zeolite KZ-20(United States Patent (USP) 3445727), No. 3415736, zeolite ZSM-3(United States Patent (USP)), faujusite (faujasite), LZ-10(English Patent 2014970, June 9 nineteen eighty-two), ZSM type zeolite, erionite, mordenite, offretite, chabazite, FU-1-type zeolite, NU-type zeolite and composition thereof.Usually with the Na in traditional cracking catalyst
2O content is less than about 1%(weight) for well.
Think that herein applicable y-type zeolite includes, but is not limited to those disclosed zeolite Y component in following United States Patent (USP), the patent No. is: 3130007,3835032,3830725,3293192,3449070,3839539,3867310,3929620,3929621,3933983,4058484,4085069,4175059,4192778,3676368,3595611,3594331,3536521,3293192,3966643,3966882 and 3957623.
The another kind of zeolite catalyst of Ying Yonging is " LZ-210 " herein, and it has done to introduce in E, P, C can be for reference.The publication that publish June 29 nineteen eighty-three is also introduced at this for No. 82211.In our embodiment, the mol ratio of silicon oxide and aluminum oxide is between about 7 to about 11, is preferably in about 8 to about 10.The hydrocracking catalyst that contains LZ-210 is disclosed in serial No. 490951 of common unsettled U.S. of submitting to May 2 nineteen eighty-three, is incorporated herein by reference in the lump at this, and this LZ-210 can be used as optional, traditional hydrocracking component at this.
Term " ZSM-type " zeolite at those zeolites that are used to refer to use buzz word " ZSM-n " name in the art, is an integer at this " n " usually.ZSM type silico-aluminate includes, but is not limited to: ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48 and other similar material.
ZSM-5 has detailed introduction in No. 3702886, United States Patent (USP) and Re29948 number.The complete explanation of these patents, the X-ray diffractogram of especially disclosed ZSM-5 is hereby incorporated by.
United States Patent (USP) has been introduced ZSM-11 No. 3709979.This explanation, especially the X-ray diffractogram of ZSM-11 is hereby incorporated by.
United States Patent (USP) has been described ZSM-12 No. 3832449.This explanation and wherein disclosed X-ray diffractogram are hereby incorporated by.
United States Patent (USP) has been described ZSM-23 No. 4076842.The detailed description of the X-ray diffractogram of its whole contents and disclosed zeolite is hereby incorporated by.
United States Patent (USP) has been introduced ZSM-35 No. 4016245.The explanation and the X-ray diffractogram thereof of this zeolite are hereby incorporated by.
United States Patent (USP) has been mentioned ZSM-38 No. 4046859 especially.The explanation of this zeolite and characteristic X-ray diffractogram thereof are incorporated herein by reference.
United States Patent (USP) has described ZSM-48 in greater detail No. 4423021.The explanation of this zeolite and characteristic X-ray diffractogram thereof also are hereby incorporated by.In addition, No. 4061724, crystalline silicate such as Silicalite(United States Patent (USP)) can with use of SAPOs of the present invention.
Catalyzer of the present invention comprises the SAPO of at least a above-mentioned sign, a kind of hydrogenation catalyst (component) and one or more traditional hydrocracking catalyst components random, that comprise zeolite aluminosilicate component and hydrogenation/cracking component (as nickelous sulfide, tungsten sulfide or the like).The products distribution that the relative quantity of SAPO component and traditional hydrocracking component (if any) will depend on the hydrocarbon feed of selection at least in part and therefrom want to obtain, but in all instances, use the SAPO of at least a significant quantity.When using traditional hydrocracking catalyst (THC) component, THC is generally about 1: 10 to about 500: 1 with the relative weight ratio of SAPO, wishes at about 1: 10 to about 200: 1, and is better between about 1: 2 and about 50: 1, is preferably about 1: 1 to about 20: 1.
SAPO and THC(are if any) can carry out ion-exchange, infiltration and/or occlusion with positively charged ion and/or the heat treating method selected, these processing are carried out after can or joining them in one or more inorganic oxide matrix components individually or simultaneously before or after mixing mutually.When SAPO used ion-exchange, it preferably and hydrogen generation cationoid (NH for example
+ 4, H
+, quaternary ammonium cation or the like) exchange.It partly is the positively charged ion (hydrogen-forming cation) of giving birth to hydrogen that the positively charged ion of SAPO preferably has at least.
If SAPO and THC(are the words that have) ion-exchange, infiltration and/or occlusion can be undertaken by its cationic solution with a selection is contacted, THC or SAPO can be through Overheating Treatment, positively charged ion is selected from ammonium, II A family, III A family, the III B positively charged ion to VII B family and rare earth, and rare-earth cation is selected from Ce, La, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and its mixture.The definite character of rare-earth cation and SAPO mutual relationship and they are to containing the SAPO activity of such catalysts and/or optionally influencing also not fully aware of at present.Because ion-exchange and/or infiltration, positively charged ion (for example rare-earth cation) perhaps can replace at least a portion and be present in positively charged ion among SAPO and/or the THC at first.The significant quantity that positively charged ion can exist is by the weight of initial SAPO and/or THC, for about 0.1% to about 20%(weight), be generally about 0.5% to about 10%(weight).
Hydrocracking catalyst of the present invention contains the hydrogenation catalyst (component) that is generally used in hydrocracking catalyst significant quantity, at least a.The hydrogenation component generally is selected from the hydrogenation catalyst group of being made up of the metal of one or more VI families and VIII family, comprises the salt, complex compound and the solution that contain above-mentioned metal.Hydrogenation catalyst preferably is selected from by at least a that form or by at least a metal of forming, salt and its complex compound in Ni, Mo, Co, W, Ti, Cr and its mixture in Pt, Pd, Rh, Ir and its mixture.
As what recognized in the art, precious metal and base metal generally shall not be applied in the same catalyst system of hydrocracking catalyst, though this situation and being not precluded within outside the scope of the present invention.Be meant the metal of elementary state or oxide compound, sulfide, halogenide, carboxylate salt or the like other form about the active metal in catalysis aspect.
The existence of the hydrogenation catalyst of significant quantity makes hydrocracking catalyst have hydrogenating function.When hydrogenation catalyst is precious metal, its amount is generally about 0.05% to about 1.5%, this is that (below will discuss) is though also may use the significant quantity that exceeds this scope by the total weight of the catalyzer that comprises the matrix weight that THC, tackiness agent maybe may exist.Although can use weight above 1.5%() significant quantity,, the recommended significant quantity of hydrogenation component is about 0.3% to about 1.2%(weight).(represent) that when hydrogenation catalyst is base metal the significant quantity of base metal oxide usually will be for about 1.0% to about 30%(weight with oxide compound) or more (based on the gross weights of catalyzer), also can use though exceed the significant quantity of this scope.
The last form of the hydrogenation component of hydrocracking catalyst is a metal oxide still in this not strict restriction mostly, and metallic sulfide or other have the form of catalytic activity.Because sulphur generally is present in the pending hydrocarbon feed, therefore since the actual form of some hydrogenation component of situ reaction probably to small part be sulfide.
When being used as the hydrogenation component by precious metal, catalyzer activates in air usually, reduces in nitrogen atmosphere then.When using base metal, base metal is also handled with sulphur compound usually.
There are many methods to join the hydrogenation component in total catalyst composition.They can be added in SAPO component, the THC component (if any), can add take office with other metal oxide component in, also can be added in its mixture.In adoptable method, a plurality of hydrogenation components (two or more) can join in the composition of catalyzer with powder type.They can add by grinding altogether, dipping, ion-exchange or occlusion, thereby one or more hydrogenation components can join among SAPO and/or the THC.For example, before composition is at last by calcining, by with common grinding, dipping or the precipitation of the binding substances of catalyzer each component or its each component, metallic sulfide, metal oxide or its water-soluble salt can be added wherein.In the method that selection can be provided, the method by the aqueous solution, spirituous solution, hydrocarbon solution or other non-aqueous solution with soluble compounds or its parent flood can join these components in the particle of having processed.When the hydrogenation component is base metal, dipping or to grind altogether be the method for recommending, and when making the hydrogenation component with precious metal, ion-exchange techniques is better.
Though the hydrogenation component can be with oxide form and SAPO and/or THC(if having) component mixes, and it is not common situation.They generally add with metal-salt, and this metal-salt can thermal conversion become corresponding oxide compound in oxidizing atmosphere, perhaps be reduced into metal with hydrogen or other reductive agent.As mentioned above, body (as dithiocarbonic anhydride, hydrogen sulfide, hydrocarbon mercaptan, elementary sulfur or the like) reaction of giving of composition and sulphur can reach sulfuration.Above-mentioned oxidation or sulfidation are generally carried out on catalyst composition; this catalyst composition partly dry (on demand), compressing tablet, granulation, push with tackiness agent or matrix; or be shaped with other method; and at last more than 600 °F, general at the temperature lower calcination more than 800.
In the art, as you know, hydrocracking catalyst generally uses with a kind of binder substance, perhaps resembles common theory, uses with inorganic oxide matrix, and this inorganic oxide matrix can be an inert, also can be catalytic activity.For example adaptable inorganic matrix has silicon oxide, aluminum oxide, silica-alumina, silicon oxide-zirconium white, silicon oxide-magnesium oxide, zirconium white-boron oxide, aluminium oxide-titanium oxide or the like and composition thereof.Inorganic oxide not necessarily often uses, if use, its amount is for about 5% to about 95%(weight), be preferably about 10% to about 80%(weight), the total weight of pressing hydrocracking catalyst.
Use term " crude oil material " relevant with hydrogenolysis, be meant an any crude oil material or a part wherein at this, it comprises the various raw materials that obtain by common oil field or submarine oil field and from the there crude oil by the entire area of elementary, secondary or three grades of recovery." crude oil material " also can obtain " synthetic crude " from coal, shale oil, Tar sands and pitch earth.Crude oil material can be direct-distilled (straight run), also can be the synthetics through fusion.Because in many hydrocracking operations, sodium oxide is a kind of poisonous substance as everybody knows, therefore above-mentioned crude oil material is wanted desalination before use usually.In addition, term " crude oil material " also comprises the various components (up to the present, the crude oil component is generally as raw material or possible charging) of crude oil and comprises fraction (the gasoline boiling range generally comprises the compound that contains greater than about 11 carbon atoms) and their all kinds of chargings such as mixture that distillates gas oil, heavy vacuum gas oil, vacuum gas oil, atmosphere and vacuum resid, synthetic crude, fine coal, surpasses the gasoline boiling range.
In method for hydrogen cracking, the general boiling point of the hydrocarbon feed of the hydroeracking unit of packing into surpasses 300 °F, and is better between about 400 °F to 1200 °F, is preferably between about 400 °F to about 900 °F.The hydrocarbon charging can be obtained by above-mentioned many sources, comprises catalytic cracking method, pyrogenic process, the fractionator from crude oil, hydrocracking, pyrolysis method or the like.So that gasoline products when reaching maximum value, the full boiling point of industrial general raw material is not more than about 800 °F usually when implementing hydrogenolysis.In general, boiling range from about 300 to 800 light catalytic cycle oil or light straight run just diesel oil or its mixture as raw material.Material can be in hydrotreater pre-treatment to reach hydrodenitrification and/or hydrogenating desulfurization.The sulfur-bearing scope that exists with hydrogen sulfide in the charging can be up to 0.1 to 3%(weight); Can be with the nitrogen content that the ammonia form exists up to 4000ppm or more.Temperature, space velocity and other process variable can control to and can compensate nitrogen to the active influence of hydrocracking catalyst.In the hydrocracking reaction district, raw material contacts with hydrocracking catalyst in the presence of the compound of hydrogenous gas and/or generation hydrogen.In hydrocracking process, hydrogen is consumed, and excessive hydrogen generally is retained in reaction zone.It is comparatively favourable that the ratio of hydrogen that uses and oil (charging) is at least 1000 standard cubic foot hydrogen/every barrel of charging (SCFB), also can preferably use about 4000 to 12000SCFB up to 20000 SCFB.Generally operate under high temperature and high pressure in the hydrocracking reaction district.Total hydrocracking pressure be generally about 400 to about 4000 pounds/square inch (gauge pressures) (Psig), be preferably about 500 to 2000psig.Hydrocracking reaction is thermopositive reaction, and temperature rises and occurs in the direction of passing catalyst bed.Therefore the temperature in hydrocracking reaction district can be than low 10 to 40 of temperature out.Average hydrocracking catalyst bed tempertaure is about 450 °F to 800 °F, depends on whether there is NH
3Aging conditions with catalyzer.Liquid in hour space velocity (LHSV) be generally 0.2 to 5 feed volume/catalyst volume hour, be preferably 0.25 to 4LHSV.
Following example can be used for illustrating the application of hydrocracking catalyst of the present invention and method, but is not limited to these examples.
Experimental procedure
Prepare hydrocracking catalyst by the method for introducing in the following example, and test its effectiveness as hydrocracking catalyst.These catalyzer are used as hydrocracking catalyst in first section hydrogenolysis.
With the hydrocarbon charging (the gas-oil feed boiling point about 332 °F to about 853 °F (ASTM methods of test D-2887), and contain the sulphur of the 5000ppm that has an appointment and the nitrogen of 2000ppm) contact with the catalyzer of selecting for use and estimate the catalyzer of selecting for use in the hydrocracking.The density of raw material is 0.8341 gram per centimeter at 60 °F
3The nitrogen (with the TERTIARY BUTYL AMINE form) of the sulphur of 0.5 weight % (with the thiophene form) and 0.2 weight % is joined in the raw material, make raw material contain sulphur and nitrogen, wherein, weight % is based on the gross weight of raw material.The about 1450psig of pressure, temperature about 685 °F to about 709 and LHSV(liquid hourly space velocity) carry out method for hydrogen cracking about 1.7 times.It is about 8000 standard cubic foots/every barrel of hydrocarbon feed that hydrogen is introduced speed.
The raw material selected for use introduced carry out the hydrocracking experiment in the stainless steel reactor that axial temperature meter jack is arranged.The thermocouple monitoring of temperature in the reactor in the jack.Catalyzer is the extrudate form and is arranged in reactor, and mixes so that the local superheating position of reactor reaches minimum with quartzy small pieces.
The hydrocarbon feed that uses in the following example is a kind of gas oil, its IBP(initial boiling point) be 332 °F, the FBP(full boiling point) be 853 °F, api gravity (American Petroleum Institute's api gravity index) is 37.9.Total nitrogen content is less than 0.1%(weight in the raw material).The chemical analysis results of raw material is:
Percent by volume
Total aromatic substance 24.7
One aromatic substance 19.0
Two aromatic substance 3.1
Three aromatic substance 1.2
Percent by volume
Four aromatic substance 0.6
Five aromatic substance 0.8
Total saturates 75.4
Reference catalyst (catalyst A) and as follows by the preparation method of two kinds of catalyzer of the present invention (catalyst B and catalyzer C).Except as otherwise noted, all weight is by anhydrous calculating.
With LZ-210(zeolite aluminosilicate) the preparation catalyst A.LZ-210 prepares for No. 82211 by disclosed E.P.C. publication, its SiO
2With Al
2O
3Than being 9.0, this LZ-210 is 600 ℃ of steam treatment 1 hour in 100% steam down, and with every pound of NH
4NO
3(with 10%(weight) aqueous solution provides) ratio of 1 pound of LZ-210 refluxed 1 hour, to carry out the ammonium exchange.Mix 140 gram LZ-210 and 60 gram Pseudobeohmite aluminum oxide (with 4.2 milliliters of concentrated nitric acid peptizations in 60 ml waters), pulverized this mixture then 10 minutes, catalyst A is shaped.Mixture is configured as 1/16 inch extrudate, and drying is 10 hours under 100 ℃, calcines 2 hours in 500 ℃ of air again.Calcining under 500 ℃ is a proceed step by step, earlier with more than one hour catalyzer is heated to 220 ℃, then 220 ℃ of following heatable catalysts 1.5 hours, with more than one hour catalyzer is warmed up to 500 ℃ from 220 ℃ again, at last 500 ℃ times heating 2 hours.With incinerating extrudate and Ni(NO
3)
2, 6H
2O and ammonium metatungstate solution mix, and make the hole of incinerating extrudate obtain filling, the dry again mixture that obtains.The catalyst A that makes at last contains the various oxide compounds of following weight percentage: 5%NiO, 20%WO
3, 52.5% LZ-210 and 22.5% aluminum oxide.NiO and WO in the catalyst A
3Chemical analysis results be NiO 4.7 weight % and WO
320.8 weight %.
In the preparation of hydrocracking catalyst, catalyst B is with SAPO-11 and LZ-210 preparation.According to the routine 17(of No. 4440871, United States Patent (USP) be dissolution time be 24 hours) preparation SAPO-11, and use with synthesized form.The LZ-210 that uses in LZ-210 zeolite and the catalyst A is identical.Grind the LZ-210 zeolite aluminosilicate that 15.0 gram SAPO-11 and 105 grams are used in catalyst A, prepare catalyst B.Will be at 100 centimetres
3(c.c) contain 42.4 ammonium metawolframates that restrain and 33.93 gram Ni(NO in the water
3)
26H
2The solution of O adds in SAPO-11 and the LZ-210 mixture.Pseudobeohmite aluminum oxide (30.0 grams are dissolved in 60 ml waters with 4.2 milliliters of concentrated nitric acid epoxy glues) is added in the said mixture again, and push the mixture that obtains, the extrudate size is 1/16 inch.Extrudate is dry and resemble under 500 ℃ to the catalyst A narration and calcine.The catalyst B that makes contains the various oxide compounds of following weight percentage: 5.0%NiO, 20%WO
3, 52.5%LZ-210,7.5%SAPO-11 and 15%Al
2O
3Catalyst B is to NiO and WO
3The chemical analysis value be: NiO 4%(weight) and WO
316%(weight).
The LZ-210 that uses SAPO-34 and preparation catalyzer prepares catalyzer C.Method by 32 to 38 narrations of the example in No. 4440871, the United States Patent (USP) prepares SAPO-34.LZ-210 uses steaming identical with preparing catalyst A and ammonium exchange LZ-210 method to make.Catalyzer C can make by mixing 25.08 gram SAPO-34 and 175 gram LZ-210.This mixture was ground 15 minutes, and add that 53.8 grams use in catalyst B, through the aluminum oxide of above-mentioned peptization.The mixture that obtains was mixed 15 minutes.In mixture, add entry again, the formation mixture of can extruding, the extrudate size is 1/16 inch.Be blended in 53 centimetres
3Contain 19.39 gram Ni(NO in the water
3)
26H
2The solution of O and 24.2 gram ammonium tungstates is full of the hole of incinerating extrudate.Dry then extrudate and resembling under 500 ℃ is above-mentionedly calcined described catalyst A.The weight percentage that the catalyzer C that makes contains various oxide compounds is as follows: 5%NiO, 20%WO
3, 52.5% LZ-210,7.5% SAPO-34 and 15% aluminum oxide.Among the catalyzer C to NiO and WO
3The chemical analysis value be: NiO 4.99%(weight) and WO
320.32%(weight).
Example 4 to 6
Example 1 to 3(catalyst A, B and C) the middle catalyzer for preparing, estimate at a series of conversion aspect (Table A of face, B and C as follows) by above-mentioned step as hydrocracking catalyst.Analyze various products, and adopt ASTM report " antidetonation characteristic of pure hydro carbons ", technology discloses the octane value of listing in No. 225 (1958), utilizes C
5And C
6The volume averaging value of product is calculated the MON(motor-method octane number of petroleum naphtha) and the RON(research octane number (RON)).The compound that utilization records in the petroleum naphtha fraction calculates MON and RON, and it comprises following component: the 2-methylbutane, just-and pentane, 2, the 3-dimethylbutane, the 2-methylpentane, the 3-methylpentane, just-hexane, methylcyclopentane, 2,4-dimethylbutane, hexanaphthene and benzene." conversion " is that material changes into boiling point and is lower than 420 weight percentage that product is shared.In Table A, B and C, reported following product (being expressed as the weight percentage of raw material): " %C
1To C
4"=contain 1 to 4 carbon atom product; " %C
3"=contain three carbon atoms product; " %C
5185 of to "=containing the product of at least 5 carbon atoms, boiling point is lower than 185 °F; " C185-420 "=product boiling point is from 185 °F to 420 °F; " C
5420 of to "=at least 5 carbon atoms of product, boiling point is lower than 420 °F.C
5, C
6, C
7, C
8And C
9Product be reported in below.Every kind of situation is measured following product: " C
5"=Skellysolve A and 2-methylbutane; " C
6"=normal hexane, 2,3-dimethylbutane, 2-methylpentane and 3-methylpentane; " C
7"=normal heptane, 2-methyl hexane, 3-methyl hexane and 2, the 4-dimethylpentane; " C
8"=octane, 2,2,4-dimethylhexane, 2,3-dimethylhexane, 2-methylheptane, 3,4-dimethylhexane and 3-methylheptane; " C
9"=positive nonane, 2,4-dimethyl heptane, 2,6-dimethyl heptane, 2,5-dimethyl heptane, 4-methyloctane, 2-methyloctane and 3-methyloctane.Report various products with weight.Measure various products with the simulation distil of describing in the ASTM test method(s) 2887.
To compare with catalyst A products distribution that obtains and the products distribution of utilizing catalyst B and C to obtain, illustrate,, obtain petroleum naphtha fraction (C by catalyzer of the present invention when when similarly transforming
5185 of to) octane value has improvement.In addition, for catalyst B and C, C
5And C
6Different/positive the ratio of hydrocarbon has raising.Because isoparaffin has higher octane value, the product that obtains with catalyst B and C has improved the octane value that calculates.
The data of Table A, B and C are plotted on Fig. 1 to 13, these data declarations in hydrogenolysis, use the benefit that catalyzer of the present invention obtained.Fig. 1 and 2 is at petroleum naphtha yield (C
5-185 °F) as the function aspect that transforms, the comparison diagram of catalyst A, B and catalyzer C.With with the resulting product of reference catalyst A relatively, catalyst B and catalyzer C generate similar or than the petroleum naphtha product of high yield.Fig. 3 and Fig. 4 have compared the calculating RON(research octane number (RON) of the petroleum naphtha fraction that obtains with catalyst A, B and C).Compare with the petroleum naphtha fraction that produces with catalyst A, catalyst B and C produce the petroleum naphtha fraction of higher RON value.Fig. 5 is at heavy petrol fraction (C
5420 of to) yield is as transforming the function aspect, the comparison diagram of catalyst A and catalyzer C, and shown that reference catalyst generates more heavy petrol product.Fig. 6 be in heavy petrol fraction yield as aspect the function that transforms, the comparison diagram of catalyst A and catalyst B.Surprised is, applications catalyst B, and heavy petrol fraction yield and reference catalyst A are similar, and the RON of petroleum naphtha fraction is improved.Fig. 7,8,9 and 10 has compared the C that produces with catalyst A, B and C
5And C
6Different/the direct ratio of hydro carbons.In each case, compare with the product that is produced by catalyst A, the product that catalyst B and C produce all has higher different/direct ratio.Figure 11 is at C
5, C
6, C
7, C
8And C
9Different/the direct ratio of hydrocarbon is as the function aspect of carbonatoms, the comparison diagram of catalyst A and catalyst B.The product that applications catalyst B obtains demonstrates C
5, C
6, C
7, C
8And C
9Therefore the higher different/direct ratio of hydrocarbon has shown higher octane product.Figure 12 and 13 is for catalyst A, B and C, its C
3The product yield is as the functional arrangement that transforms.With comparison shows that of catalyst A, the C of catalyzer C
3Product slightly increases, and the C of catalyst B
3The yield of product is similar to catalyst A.
The above results explanation applications catalyst B and catalyzer C have improved the RON of petroleum naphtha fraction, have increased C
5To C
9Different/the direct ratio of product and the yield of petroleum naphtha and heavy petrol fraction are constant substantially or increase arranged.Therefore, application contains the of the same race catalyzer of the catalyzer of SAPO than no SAPO component, and the octane value of the petroleum naphtha fraction that it obtains increases.These results also show, catalyst B (containing SAPO-11) contains SAPO-34 being better than catalyzer C(aspect the octane value that improves the petroleum naphtha product), and do not have the loss of gasoline yield.The characteristics of SAPO-11 are adsorb isobutane and SAPO-34 does not have this characteristic, and therefore, SAPO-11 belongs to recommend the SAPO that uses in catalyzer of the present invention
S
Example 7
Use SAPO-11 and prepare catalyzer, with the hydrocracking that catalyzer of the present invention is described and the functionality of dewaxing.The method of describing by the example 18 of No. 4440871, United States Patent (USP) prepares SAPO-11, is last di-n-propylamine and Al
2O
3Mol ratio be 1.0 to 1.The concrete preparation process of catalyzer is: 150 gram SAPO-11 are mixed to form extrusioning mixture (slurry) with the water of 100 gram Kelvin (Kaiser) intermediate density aluminum oxide and q.s.This mixture is squeezed into 1/16 inch extrudate and 100 ℃ of air dryings 16 hours.Then extrudate was calcined 2 hours in 480 ℃ of air.Again with extrudate (153 gram) with contain 40.0 gram Ni(NO
3)
2, 6H
2150 milliliters of aqueous solution (filling up hole) of O and 48.8 gram ammonium metawolframates.Then mixture was calcined 2 hours down 100 ℃ of following dryings 16 hours and at 480 ℃.The catalyzer that makes contains (being expressed as oxide weight percentage ratio): 5%NiO, 23%WO
3, 36%SAPO-11 and 36% Al
2O
3NiO and WO
3The chemical analysis value be: NiO 5.4% and WO
323.0%.
Be in total pressure that 2000psig, liquid hourly space velocity (LASV) are 1, hydrogen flow rate is the 10000SCFB(standard cubic feet per barrel) be to contact with hydrogen by the raw material of selecting for use under about 700 to 840 condition to estimate this catalyzer with temperature.Collect and estimate boiling point and be lower than 600 product, and provide conversion values according to these products.The raw material of using in the present embodiment is a kind of vacuum gas oil, its IBP(initial boiling point) be 560 °F, the FBP(full boiling point) be 1148 °F (both determine with ASTM methods of test D-2887), api gravity is 22.3, pour point is greater than 95 °F.The physics and the chemical property of raw material are as follows:
Weight percentage
Alkane 24.1
Weight percentage
Mononaphthene 9.5
Poly-cycloalkanes 8.7
One aromatic substance 13.3
Two aromatic substance 9.3
Three aromatic substance 4.3
Four aromatic substance 2.7
Five aromatic substance 0.7
Collect reactor effluent, and change into the umber of the charging (by weight) that boiling point is lower than 600 products with determination of simulated distillation.Translation table is shown feedstock conversion and becomes boiling point to be lower than the weight percentage of 600 products.During collecting, keep the effluent liquid temperature at about 130 °F, by the pour point of ASTM methods of test D-97-66 assaying reaction device effluent liquid.
Conversion and pour point are as follows:
Temperature (°F) the conversion pour point (°F)
700 7.52 85
724 9.84 80
749 17.95 70
769 30.06 55
788 41.60 25
797 36.64 35
788 29.89 40
788 33.74 45
807 43.64 30
Temperature (°F) the conversion pour point (°F)
821 45.12 30
822 45.50 30
840 56.88 20
The feedstock conversion of above-mentioned data declaration higher in the presence of hydrogen becomes more lower boiling product, illustrates that also above-mentioned product compares with starting raw material and have lower pour point.
Claims (59)
1, the method for processing crude oil material in the presence of hydrogen, the conversion catalyst that is included in the alumo-silicate (SAPO) of No. 4440871, at least a United States Patent (USP) that makes crude oil material and hydrogen and at least a hydrogenation catalyst that comprises significant quantity and significant quantity under the effective process conditions contacts, and this alumo-silicate is characterised in that its calcinated form is at ℃ following oxygen of absorption at least 4% (weight) of dividing potential drop 100 torrs and temperature-186.
2, the method for processing crude oil material in the presence of hydrogen, the conversion catalyst that is included in the alumo-silicate (SAPO) of No. 4440871, hydrogen that makes crude oil material and significant quantity under the effective process conditions and at least a United States Patent (USP) that comprises significant quantity contacts, and this alumo-silicate is characterised in that its calcinated form adsorbs 2%(weight at least under 20 ℃ of dividing potential drop 500 torrs and temperature) Trimethylmethane.
3, in the presence of hydrogen and a kind of conversion catalyst, the processing boiling point is higher than the crude oil material of petroleum naphtha fraction with in the method that produces the petroleum naphtha fraction, the conversion catalyst that improvement is included in the alumo-silicate (SAPO) that makes No. 4440871, crude oil material and at least a hydrogenation catalyst that comprises significant quantity and at least a United States Patent (USP) under the effective process operation condition contacts, this alumo-silicate is characterised in that its calcinated form adsorbs 4%(weight at least under dividing potential drop 100 torrs and temperature-186 ℃) oxygen, thereby improved the isoparaffin of gasoline fraction and the ratio of n-paraffin.
4, the method for claim 3, wherein another feature of SAPO is that its calcinated form adsorbs 2%(weight at least under 20 ℃ of dividing potential drop 500 torrs and temperature) Trimethylmethane.
5, claim 1 or 2 or 3 or 4 method, wherein SAPO is characterised in that its calcinated form under the condition of 22 ℃ of dividing potential drop 2.6 torrs and temperature, absorption zero is to less than 5%(weight) triethylamine.
6, the method for claim 5, wherein the absorption of triethylamine is less than 3%(weight).
7, claim 1 or 2 or 3 or 4 method, wherein said catalyzer contains at least a activated traditional hydrocracking catalyst (THC) of significant quantity, the weight ratio of THC and SAPO be about 1: 10 to about 500: 1 and zero to about 99%(weight) at least a inorganic oxide matrix component (based on the gross weight of above-mentioned catalyzer).
8, the method for claim 7, wherein the weight ratio of THC and SAPO is about 1: 2 to about 50: 1.
9, the method for claim 8, wherein the weight ratio of THC and SAPO is about 1: 1 to about 20: 1.
10, the method for claim 7, wherein the inorganic oxide components amount be based on the gross weight of above-mentioned catalyzer about 5% to about 95%(weight).
11, according to the method for claim 7, wherein the above-mentioned THC component in the conversion catalyst is a zeolite aluminosilicate, and contain significant quantity, be selected from ammonium, II A family, III A family, the III B positively charged ion to VII B family, Ce, La, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and its mixture group.
12, claim 1,2 or 3 method, wherein the positively charged ion of SAPO to small part is to exist with the form of giving birth to hydrogen.
13, the method for claim 12, the form of wherein giving birth to hydrogen cation is NH
+ 4Or H
+
14, claim 1,2,3 or 7 method, wherein this method be temperature be about 400 to about 1600, pressure for about 14.7Psig to the condition of about 100psig, be that 400 extremely about 1200 crude oil materials contact with above-mentioned conversion catalyst in the presence of the hydrogen of significant quantity and implement with boiling point.
15, the method for claim 11, wherein zeolite aluminosilicate contain have an appointment 0.1% to about 20%(weight) polyvalent cation.
16, the method for claim 10, wherein the inorganic oxide matrix component is selected from clay, silicon oxide, aluminum oxide, silica-alumina, silicon oxide-zirconium white, silicon oxide-magnesium oxide, aluminum oxide-boron oxide, aluminium oxide-titanium oxide and its mixture.
17, claim 1,2 or 3 method, wherein SAPO is selected from SAPO-5, SAPO-11, SAPO-17, SAPO-31, SAPO-34, SAPO-35, SAPO-40, SAPO-41, SAPO-44 and its mixture.
18, the method for claim 17, wherein SAPO is SAPO-11.
19, the method for claim 17, wherein SAPO is SAPO-17.
20, the method for claim 17, wherein SAPO is SAPO-31.
21, the method for claim 17, wherein SAPO is SAPO-34.
22, the method for claim 17, wherein SAPO is SAPO-40.
23, the method for claim 17, wherein SAPO is SAPO-41.
24, claim 1,2 or 3 method, wherein crude oil material is selected from and distillates gas oil, heavy vacuum gas oil, vacuum gas oil, atmosphere Residual oil, vacuum resid, synthetic crude, fine coal and its mixture.
25, the method for claim 7, wherein THC contains at least a zeolite aluminosilicate, and the latter is selected from zeolite Y, overstable zeolite Y, X zeolite, zeolite beta, zeolite KZ-20, faujusite, LZ-210, LZ-10, ZSM type zeolite and its mixture.
26, the method for claim 25, wherein zeolite aluminosilicate is selected from zeolite Y, overstable zeolite Y, zeolite beta, zeolite KZ-20, faujusite, LZ-210, LZ-10, ZSM-5 and its mixture.
27, the method for claim 3, wherein the octane value of petroleum naphtha fraction has raising than the similar conversion catalyst that does not contain SAPO.
28, according to claim 1,2 or 3 method, wherein the hydrogenation component of significant quantity is selected from least a in Pt, Pd, Rh, Ru, Ni, W, Mo, Co, Ti, Cr and its mixture.
29, the method for claim 28, metal wherein are selected from Pt, Pd, Rh, Ru and its mixture, and its amount is about 0.05%(weight) to about 1.5%(weight).
30, the method for claim 28, wherein metal is selected from Ni, W, Mo, Co, Ti, Cr and its mixture, its amount is about 1.0%(weight) to about 30%(weight).
31, the method for claim 14, wherein this method is to be about 400 °F and to carry out to about 900 effective hydrocracking condition of hydrocarbon charging containing boiling point, hydrogen is at least 1000SCFB with the ratio of charging, the operation total pressure is about 400 to about 4000psig, temperature is about 450 °F to 800 °F, and LHSV is 0.2 to 5.
32, the method for claim 31, wherein charging has been subjected to hydrogenation.
33, the method for claim 31, wherein charging has been subjected to the hydrogenating desulfurization effect.
34, the method for claim 31, wherein the boiling point of hydrocarbon charging is between about 400 °F to 800 °F.
35, the method for claim 14, wherein the boiling point of hydrocarbon charging is between about 400 °F to 900 °F.
36, a kind of catalyzer, it contains the SAPO of No. 4440871, at least a United States Patent (USP), with significant quantity, be selected from least a hydrogenation catalyst of Co, Ni, Mo, W, Pt, Pd, Cr, Rh, Ru and Ti group, this SAPO is characterised in that its calcinated form adsorbs 4%(weight at least under dividing potential drop 100 torrs and temperature-186 ℃) oxygen.
37, the catalyzer of claim 36, wherein another feature of SAPO is that its calcinated form adsorbs 2%(weight at least under 20 ℃ of dividing potential drop 500 torrs and temperature) Trimethylmethane.
38, the catalyzer of claim 36 or claim 37, wherein another feature of SAPO be its calcinated form 22 ℃ of pressure 2.6 torrs and temperature down absorption zero to less than 5%(weight) triethylamine.
39, the catalyzer of claim 30, wherein Xi Fu triethylamine is less than 3%(weight).
40, claim 36,37 or 38 catalyzer, wherein said catalyzer contains at least a activated traditional hydrocracking catalyst (THC) of significant quantity, the weight ratio of THC and SAPO is about 1: 10 to about 500: 1 and zero extremely about 99%(weight) at least a inorganic oxide matrix component (based on the gross weight of catalyzer).
41, the method for claim 40, wherein the weight ratio of THC and described SAPO is about 1: 2 to about 50: 1.
42, the method for claim 41, wherein the weight ratio of THC and described SAPO is about 1: 1 to about 20: 1.
43, the method for claim 40, wherein the content of inorganic oxide components be based on the gross weight of above-mentioned catalyzer about 1% to about 99%(weight).
44, by the method for claim 40, wherein the THC component in the conversion catalyst contain significant quantity, be selected from ammonium, II A family, III A family, III B positively charged ion to VII B family, Ce, La, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and its mixture.
45, the method for claim 36, wherein the positively charged ion of above-mentioned SAPO to small part is to exist with the form of giving birth to hydrogen.
46, the method for claim 45, wherein giving birth to hydrionic form is NH
+ 4Or H
+
47, the catalyzer of claim 40, wherein catalyzer contains at least a traditional hydrocracking catalyst that is selected from zeolite Y, overstable zeolite Y, X zeolite, zeolite beta, zeolite KZ-20, faujusite, LZ-210, LZ-10, ZSM type zeolite and its mixture.
48, the catalyzer of claim 44, wherein the inorganic oxide matrix component is selected from clay, silicon oxide, aluminum oxide, silica-alumina, silicon oxide-zirconium white, silicon oxide-magnesium oxide, aluminum oxide-boron oxide, aluminium oxide-titanium oxide and its mixture.
49, claim 36,37 or 38 catalyzer, wherein SAPO is selected from SAPO-11, SAPO-17, SAPO-31, SAPO-34, SAPO-35, SAPO-40, SAPO-41, SAPO-44 and its mixture.
50, the catalyzer of claim 49, wherein SAPO is SAPO-11.
51, the catalyzer of claim 49, wherein SAPO is SAPO-17.
52, the catalyzer of claim 49, wherein SAPO is SAPO-31.
53, the catalyzer of claim 49, wherein SAPO is SAPO-34.
54, the catalyzer of claim 49, wherein SAPO is SAPO-40.
55, the catalyzer of claim 49, wherein SAPO is SAPO-41.
56, the catalyzer of claim 47, wherein said catalyzer contains LZ-210, at least a SAPO-11 of being selected from, SAPO-17, SAPO-31, SAPO-34, SAPO-35, the SAPO-40 of significant quantity, SAPO SAPO-41) and at least a Co, Ni, W and the Mo of being selected from) hydrogenation catalyst.
57, the catalyzer of claim 56, wherein the mol ratio of silicon oxide among the LZ-210 and aluminum oxide is about 7 to about 11.
58, the catalyzer of claim 56, wherein the mol ratio of silicon oxide and aluminum oxide is greater than 8.0.
59, the catalyzer of claim 58, wherein the mol ratio of silicon oxide and aluminum oxide is about 8 to about 10.