CN85108710B - 沸腾炉轻烧菱镁矿石的方法和装置 - Google Patents
沸腾炉轻烧菱镁矿石的方法和装置 Download PDFInfo
- Publication number
- CN85108710B CN85108710B CN85108710A CN85108710A CN85108710B CN 85108710 B CN85108710 B CN 85108710B CN 85108710 A CN85108710 A CN 85108710A CN 85108710 A CN85108710 A CN 85108710A CN 85108710 B CN85108710 B CN 85108710B
- Authority
- CN
- China
- Prior art keywords
- fluidizing furnace
- flue gas
- furnace
- light
- ore
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
本发明涉及一种生产轻烧氧化镁的方法和装置，特别是一种用沸腾炉轻烧菱镁矿石生产轻烧氧化镁的方法和装置。将粒度为０～２５ｍｍ的菱镁矿石置于沸腾炉内，经干燥、加热、分解、爆裂、气流磨细、分选后，得到烧减低、活性高、粒度细而均匀的优质轻烧氧化镁，从而简化了工艺，提高了产品的氧化镁品位。其生产装置包括沸腾炉、排料螺旋、烟气－空气换热器、旋风收尘器、多管旋风收尘器、布袋或电收尘器、料斗、负压输送冷却***和排烟机等。
Description
本发明涉及一种生产轻烧氧化镁的方法和装置，特别是一种用沸腾炉轻烧菱镁矿石生产轻烧氧化镁的方法和装置。将粒度为0～25mm的菱镁矿石置于沸腾炉内，经干燥、加热、分解、爆裂、气流磨细、分选后，得到烧减低、活性高、粒度细而均匀的优质轻烧氧化镁，简化了工艺，提高了产品的品位。
本发明所生产的产品为轻烧氧化镁（又称苦土粉），该产品可进一步加工成镁砂，作为碱性耐火材料。也可以制成多种建筑材料，以及作造纸填充材料。
目前对天然菱镁矿石的热加工一般有两种方法。其一是一步煅烧，即
天然菱镁矿MgCO3 
重烧镁砂MgO+CO2↑其二是二步煅烧，即
天然菱镁矿MgCO3 
轻烧氧化镁MgO+CO2↑
重烧镁砂MgO
长期以来，我国生产轻烧氧化镁用反射炉。但是反射炉只能使用粒度为25～100mm的大块原矿，而采矿时产出粒度小于25mm的矿石占40～45%，这部分粉矿基本不能利用而堆积起来。既浪费资源、占用土地，又污染环境。为处理粉矿曾用迴转窑、环形窑来生产轻烧氧化镁，但产品合格率较低，能源消耗高。
西德、美国、日本等国生产轻烧氧化镁的方法为多层炉，该炉结构复杂，需用较多的高温钢，作业率低，检修条件差，单位面积生产能力低。
上述反射炉、迴转窑、环形窑、多层炉等在轻烧天然菱镁矿石时，都是以块状矿石入炉，产出块状轻烧氧化镁，而耐火、建材、轻工等部门需用的轻烧氧化镁均要求粒度小于120μm，因此需用雷蒙磨等设备进一步粉碎，增加了作业环节，消耗了能源。块状菱镁矿石入炉，产出块状轻烧氧化镁，产品质量往往不均，一般来说容易形成表面过烧，中心欠烧，因此残余烧减高达3～8%，给下一步工序带来不良后果。
奥地利采用悬浮炉来处理细粒菱镁矿石，类似水泥行业的炉外分解工艺，其细粒菱镁矿石为粒度在150μm以下的浮选精矿或事先磨细的原矿，经悬浮炉处理后产出质量均匀、残余烧减小于1%的轻烧氧化镁。但是事先磨矿、磨烧仍需两次作业。
上述反射炉、迴转窑、多层炉、悬浮炉等方法轻烧菱镁矿石所得产品中的MgO、CaO、AL2O3、SiO2、Fe2O3等成份，只能随原矿的成份而定，炉内对有用成份氧化镁MgO没有富集作用，对无用成份AL2O2、SiO2、Fe2O3等亦无废弃功能。
本发明的目的是提供一种菱镁矿石的轻烧方法和装置，以获得产品质量均匀、残余烧减低的优质轻烧氧化镁。并且能将轻烧前、轻烧后的细磨作业取消或简化。使轻烧产品中有用成份MgO的品位提高，杂质成份AL2O3、SiO2、Fe2O3等品位降低。根据产品对CaO/SiO2的要求，将其调整到适当的比例。
本发明的工艺流程和装置见图1。粒度为0～25mm的菱镁矿石由螺旋加料机〔1〕连续加入沸腾炉〔2〕内，矿石被沸腾炉内的热风（由罗茨风机供给并通过烟气-空气换热器加热）与燃料燃烧产生的烟气所沸腾，矿石在炉内被干燥、加热、分解、爆裂、气流磨细、分选，生成烧减低、活性高、粒度细的轻烧氧化镁，随上升烟气带出炉顶，经烟气-空气换热器〔3〕，旋风收尘器〔4〕，多管旋风收尘器〔5〕，布袋或电收尘器〔6〕，将细粉与烟气分离开，细粉集于料斗〔7〕，由负压输送***〔8〕送至成品仓，烟气净化后由排烟机〔9〕及烟囱〔10〕排入大气。
通过沸腾炉底部的排料螺旋〔11〕放出部份炉内物料，可排除矿石中不能分解的杂质成分，提高炉顶产品中氧化镁MgO的含量，起到热态分选矿物的效果。
在原矿中配加一定粒度适量的高钙矿石，可以调整产品中CaO/SiO2的比值，满足重烧镁砂的成分要求。
沸腾炉为上大下小的直立空炉，下部设有分布板，分布板上有若干个雾化效果良好的重油烧嘴。
整个工艺的温度、压力、风量、油量、加料量等参数，均集中于中心控制室，用仪表显示、记录和调节。
本发明的主要工艺参数及产品质量指标为：
（1）轻烧温度800～900℃
（2）沸腾床操作风速2～3米/秒
（3）产品质量
MgO含量80～97.5%（根据入炉矿石的品位而定）;
烧 减 1%左右;
粒 度 -74μm＞99%-40μm＞90%;
（4）每吨产品油耗 164公斤/吨（发热值为9500千卡/公斤左右）。
Claims (4)
1、一种生产轻烧氧化镁的方法，特别是一种用沸腾炉轻烧菱镁矿石生产轻烧氧化镁的方法，其特征是菱镁矿石由螺旋加料器连续加入沸腾炉内，矿石被沸腾炉内的热风与燃料燃烧产生的烟气所沸腾，矿石在炉内被干燥、加热、分解、爆裂、气流磨细，细粒度的轻烧氧化镁随上升烟气带出炉顶，经烟气-空气换热器、旋风收尘器、多管旋风收尘器、布袋或电收尘器，将细粉与烟气分开，细粉集于料斗，由负压输送***送至成品仓，而不能分解的杂质成分再行分选。
2、根据权利要求1所述的方法，其特征是所述的分选是在沸腾炉内的热态分选，在沸腾炉底部由排料螺旋排除矿石中不能分解的、颗粒较大的杂质成分，从而提高产品中的氧化镁含量。
3、根据权利要求1所述的方法，其特征是所述的菱镁矿石中还要配入适量高钙矿物，以调整产品的CaO/Sio2比值。
4、一种用沸腾炉轻烧菱镁矿石生产轻烧氧化镁的装置，其特征是该装置包括沸腾炉、排料螺旋、烟气-空气换热器、旋风收尘器、多管旋风收尘器、布袋或电收尘器、料斗、负压输送冷却***、排烟机。