CN85107725A - 制造玻璃瓶模具的蠕墨铸铁 - Google Patents
制造玻璃瓶模具的蠕墨铸铁 Download PDFInfo
- Publication number
- CN85107725A CN85107725A CN 85107725 CN85107725A CN85107725A CN 85107725 A CN85107725 A CN 85107725A CN 85107725 CN85107725 CN 85107725 CN 85107725 A CN85107725 A CN 85107725A CN 85107725 A CN85107725 A CN 85107725A
- Authority
- CN
- China
- Prior art keywords
- graphite
- cast iron
- rare earth
- vermicular cast
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明的制造玻璃瓶模具的蠕墨铸铁，可采用钒钛生铁或一般普通生铁为原料，以稀土硅铁为主，辅以少量的稀土镁硅铁合金为变质处理剂熔制而成。用该材料熔制成高速制瓶机上的玻璃模具其抗氧化和抗生长性能好，耐磨性高，使玻璃制品光洁度改善，模具使用寿命延长，经济效益显著。
Description
制造玻璃瓶模具的蠕墨铸铁。
瓶罐的质量与玻璃瓶模具的质量有密切的关系，实践证明只有好的制瓶机器而没有好的模具是生产不出好的瓶罐的，只有不断改善模具的质量，才能提高玻璃制品的质量和生产率。现在国内使用的玻璃瓶模具的材质多属于低合金灰铸铁，这种材料的模具普遍存在着耐磨性差，易氧化起皮，使用寿命短等缺点。目前，日本采用低硅铝系蠕墨铸铁作为玻璃模具材料，参阅日本《特许公报》昭和52-46321“ガラス成形全型用的铸铁”。但是，这种材料易形成夹渣，工艺操作不便，易形成铸造缺陷。
本发明的任务是：利用富有的稀土资源和镁资源作为合金添加剂，熔制成高速制瓶机用的蠕墨铸铁玻璃模具，以提高模具的使用寿命，改善玻璃制品的表面质量。
本发明可采用钒钛生铁为原料，以稀土硅铁为主，辅以少量的稀土镁硅铁合金为变质处理剂，熔制成蠕墨铸铁。其化学成分控制在C3.5%～3.8%，Si2.8%～3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%，Cu0.4%～0.6%，V0.2%～0.3%，Ti0.1%～0.2%。金相组织为在珠光体和铁素体混合的基体组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量应占石墨总量的50%～80%;或者采用一般普通生铁为原料，以稀土硅铁为主，辅以少量的稀土镁硅铁合金为变质处理剂，熔制成蠕墨铸铁。其化学成分控制在C3.5%～3.8%，Si2.8～3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%，Sb0.05%～0.07%。金相组织为在珠光体量大于85%的基体组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量应占石墨总量的50%～80%。
按本发明熔制的蠕墨铸铁玻璃模具材料，由于其抗氧化性能，抗生长性能及耐磨性能皆优于低合金灰铸铁玻璃模具材料，所以，其模具的使用寿命将提高1倍以上，制成的瓶罐表面光洁，不凹陷。
本发明的实施方案：
实施例1.以钒钛生铁为原料，以稀土硅铁（含Re21.5%）为主，辅以少量的稀土镁硅铁合金（占变质处理剂总量的1/8～1/10）作为变质处理剂，熔制蠕墨铸铁玻璃模具：C3.5%～3.8%，Si2.8%3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%（炉后添加），Cu0.4%～0.6%（炉前包中冲入），V0.2%～0.3%（生铁带入），Ti0.1%～0.2%（生铁带入）。金相组织为在珠光体-铁素体混合的基本组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量占石墨总量的50%～80%。生产试验证明，在QD6型四分部行列机上生产1市斤装的酒瓶，原来采用Cr-Mo-Cu低合金灰铸铁模具的产瓶数是：雏型模20万只，成型模30万只。用本发明的蠕墨铸铁成型玻璃模具，产瓶数为50万只，模具寿命大幅度提高。
实施例2，采用一般普通生铁为原料，以稀土硅铁（含Re21.5%）为主，辅以少量的稀土镁硅铁合金（占变质处理剂总量的1/8～1/10）为变质处理剂，熔制蠕墨铸铁玻璃模具：C3.5%，Si2.8%～3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%（炉后添加），Sb0.05%～0.07%（金属纯锑在包中冲入）。金相组织为在珠光体量大于85%的基体组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量占石墨总量的50%～80%。生产试验证明，用QD6型四分部行列机生产500克罐头瓶，原来采用加锡灰铸铁模具，产瓶数为21.8万只。用本发明的蠕墨铸铁玻璃模具，产瓶数可达33.2万只;又如，用QD6型四分部行列机生产输液瓶，原来采用Cr-Mo-Cu合金灰铸铁模具，产瓶数为6.5～7.0万只，而采用本发明的蠕墨铸铁模具，产瓶数可达16万只。
补正 85107725
文件名称 页 行 补正前 补正后
说明书 1 24 Si2.8～3.2%， Si2.8%～3.2%，
2 7 2.8%3.2%， 2.8%～3.2%，
2 16 实施例2， 实施例2。
Claims (2)
1、制造玻璃瓶模具的蠕墨铸铁，以稀土硅铁为主，辅以少量的稀土镁硅铁合金为变质处理剂，本发明的特征在于，以钒钛生铁为原料熔制蠕墨铸铁，化学成分控制在C3.5%～3.8%，Si2.8%～3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%，Cu0.4%～0.6%，V0.2%～0.3%，Ti0.1%～0.2%，金相组织为在珠光体和铁素体混合的基体组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量占石墨总量的50%～80%。
2、制造玻璃瓶模具的蠕墨铸铁，以稀土硅铁为主，辅以少量的稀土镁硅铁合金为变质处理剂，本发明的特征在于，以一般普通生铁为原料熔制蠕墨铸铁，化学成分控制在C3.5%～3.8%，Si2.8%～3.2%，Mn0.5%～0.8%，P＜0.1%，S＜0.04%，Cr0.2%～0.4%，Sb0.05%～0.07%，金相组织为在珠光体量大于85%的基体组织上分布着蠕虫状石墨和球状石墨，不得出现片状石墨，其中蠕虫状石墨的量占石墨总量的50%～80%。