CN219762612U - 一种未固化或部分固化的围条和鞋类物品 - Google Patents
一种未固化或部分固化的围条和鞋类物品 Download PDFInfo
- Publication number
- CN219762612U CN219762612U CN201990000931.8U CN201990000931U CN219762612U CN 219762612 U CN219762612 U CN 219762612U CN 201990000931 U CN201990000931 U CN 201990000931U CN 219762612 U CN219762612 U CN 219762612U
- Authority
- CN
- China
- Prior art keywords
- uncured
- cured
- article
- partially cured
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本实用新型涉及一种未固化或部分固化的围条,所述未固化或部分固化的围条包括:未固化或部分固化的橡胶制成的基础围条和未交联或部分交联的粘合剂的两层结构,其中所述基础围条具有第一侧面和与所述第一侧面相对的第二侧面,其中所述未交联或部分交联的粘合剂与所述基础围条的所述第二侧面上的所述未固化或部分固化的橡胶接触。本实用新型还涉及一种鞋类物品。
Description
相关申请的交叉引用
本申请要求于2018年6月4日提交并且指定为申请号CN201810562947.X的标题为"A vulcanized shoe foxing strip,its production method and application"的共同未决的中国专利申请的优先权,该中国专利申请通过引用以其整体并入本文。
背景技术
在传统的鞋类固化橡胶物品的制造工艺中,需要两个人来完成围条(foxingtape)与鞋面构件和鞋底结构的附接。特别地,围条必须使用处理剂清洁和/或涂底漆,并且然后干燥。随后,将粘合剂施加至围条和鞋底和/或鞋面两者,并且在将围条与鞋类物品的鞋面构件和鞋底结构结合之前将粘合剂干燥。另一个问题是处理剂和/或粘合剂是基于溶剂的组合物,并且在加工(例如,干燥工艺)期间向空气中排放一种或更多种挥发性有机化合物(VOC)。排放的VOC导致工作环境中的VOC,这可能是不健康的。
实用新型内容
本实用新型涉及以下内容:
1).一种未固化或部分固化的围条,其特征在于,所述未固化或部分固化的围条包括:未固化或部分固化的橡胶制成的基础围条和未交联或部分交联的粘合剂的两层结构,其中所述基础围条具有第一侧面和与所述第一侧面相对的第二侧面,其中所述未交联或部分交联的粘合剂与所述基础围条的所述第二侧面上的所述未固化或部分固化的橡胶接触。
2).根据1)所述的未固化或部分固化的围条,其特征在于所述未固化或部分固化的橡胶是天然橡胶或合成橡胶。
3).根据1)所述的未固化或部分固化的围条,其特征在于所述未交联或部分交联的粘合剂包含:(i)未固化或部分固化的橡胶;(ii)增粘树脂;以及(iii)填料。
4).根据3)所述的未固化或部分固化的围条,其特征在于所述增粘树脂选自烃类树脂或萜烯树脂。
5).根据4)所述的未固化或部分固化的围条,其特征在于所述烃类树脂是芳香族烃类树脂。
6).根据3)所述的未固化或部分固化的围条,其特征在于所述填料是二氧化硅。
7).根据3)所述的未固化或部分固化的围条,其特征在于所述粘合剂还包括橡胶固化剂,所述橡胶固化剂包括硫组分,其中所述硫组分选自元素硫或含硫有机化合物。
8).根据1)至7)中任一项所述的未固化或部分固化的围条,其特征在于所述未固化或部分固化的围条还包括布置在所述未固化或部分固化的围条的第一侧面上的释放材料。
9).根据8)所述的未固化或部分固化的围条,其特征在于所述释放材料包含聚合物膜或纺织品。
10).根据1)-7)和9)中任一项所述的未固化或部分固化的围条,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
11).根据8)所述的未固化或部分固化的围条,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
12).根据1)-7)和9)中任一项所述的未固化或部分固化的围条,其特征在于交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
13).根据8)所述的未固化或部分固化的围条,其特征在于交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
14).根据1)-7)、9)、11)和13)中任一项所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
15).根据8)所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
16).根据10)所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
17).根据12)所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
18).一种鞋类物品,包括:鞋面,其特征在于,在所述鞋面和所述鞋类物品的外边缘周界上的固化的橡胶鞋结构之间的接触点处是接合部,其中固化的橡胶围条沿着所述接合部被布置在所述鞋面和所述固化的橡胶鞋结构的至少第一部分上,其中所述固化的橡胶围条具有基础围条和交联的粘合剂的两层结构,其中所述基础围条具有第一侧面和与所述第一侧面相对的第二侧面,其中第一所述侧面是面向外的,其中所述交联的粘合剂在所述基础围条的第二侧面上,其中所述交联的粘合剂邻近所述鞋面、所述固化的橡胶鞋结构和所述接合部,并且其中所述固化的橡胶围条通过所述交联的粘合剂被结合至所述固化的橡胶鞋结构、所述鞋面或两者。
19).根据18)所述的鞋类物品,其特征在于所述基础围条由天然橡胶、或合成橡胶制成。
20).根据18)所述的鞋类物品,其特征在于所述交联的粘合剂是包含以下的组合物的固化反应产物:(i)未固化或部分固化的橡胶;(ii)增粘树脂;以及(iii)填料。
21).根据20)所述的鞋类物品,其特征在于所述增粘树脂选自烃类树脂或萜烯树脂。
22).根据21)所述的鞋类物品,其特征在于所述烃类树脂是芳香族烃类树脂。
23).根据20)所述的鞋类物品,其特征在于所述填料是二氧化硅。
24).根据20)所述的鞋类物品,其特征在于所述粘合剂还包括橡胶固化剂,所述橡胶固化剂包括硫组分,其中所述硫组分选自元素硫或含硫有机化合物。
25).根据18)至24)中任一项所述的鞋类物品,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
26).根据18)至24)中任一项所述的鞋类物品,其特征在于所述交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
27).根据18)-24)中任一项所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
28).根据25)所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
29).根据26)所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
30).根据18)-24)和28)-29)中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
31).根据25)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
32).根据26)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
33).根据27)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
34).根据30)所述的鞋类物品,其特征在于所述第一部分是鞋头、缓冲器或两者。
35).根据31)-33)中任一项所述的鞋类物品,其特征在于所述第一部分是鞋头、缓冲器或两者。
36).根据18)-24)和28)-29)中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
37).根据25)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
38).根据26)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
39).根据27)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
40).根据36)所述的鞋类物品,其特征在于所述第二部分包含鞋跟标志。
41).根据37)-39)中任一项所述的鞋类物品,其特征在于所述第二部分包含鞋跟标志。
42).根据18)-24)和28)-29)中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
43).根据25)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
44).根据26)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
45).根据27)所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
附图说明
图1是本公开内容的围条在加工(例如,固化)之前的示意图。
图2图示出围条的生产方法的流程图。
图3A和图3B图示出围条的应用的流程图。
图4图示出包括固化的围条的鞋类物品的透视图。
具体实施方式
一般来说,本公开内容提供了可以被用作鞋类物品中的粘合剂,例如用于在固化期间将未固化的橡胶部件彼此固定的组合物。例如,通过在还固化围条的橡胶、鞋结构的橡胶或两者的工艺期间将该组合物交联至橡胶围条、橡胶鞋结构或两者,围条可以被固定至鞋类物品的鞋面构件和鞋结构(例如,鞋头(toe cap)、缓冲器(bumper)、鞋跟标志、鞋底夹层、杯形鞋底(cup sole)、鞋外底或鞋中的其他橡胶部件)。在交联之前,该组合物可以包含未固化或部分固化的橡胶、填料和增粘树脂以及任选地一种或更多种其他组分(例如,聚醚、橡胶固化剂、其他填料、脂肪酸、抗氧化剂和防雾剂)。该组合物是一种未交联或部分交联的粘合剂,该未交联或部分交联的粘合剂被配置用于在橡胶固化工艺(例如,硫化)中结合至未固化或部分固化的橡胶或结合在未固化或部分固化的橡胶之间。在将未固化或部分固化的部件(例如,围条)固定至鞋类时使用该组合物可以通过除去对于该工艺中清洁/涂底漆和干燥步骤的需求,通过除去对于将粘合剂施加至未固化或部分固化的部件(例如,围条)和鞋的其他部件(例如,施加至鞋面构件、鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件)两者的需求来简化用于制造鞋类的工艺,例如,允许单个人将围条施加至鞋面构件和/或其他橡胶部件。另外,通过除去对于使用基于溶剂的处理剂的需求并且通过使用本文描述的不排放令人担忧的水平的潜在有毒挥发性有机化合物(VOC)的粘合剂组合物,使用本文描述的组合物避免了令人担忧的水平的潜在有毒VOC的排放。除了这些之外,鞋类物品与目前的技术相比具有增强的耐用性,并且虽然不受理论限制,但鞋类物品呈现出增强的耐用性可能是由于组合物中存在的橡胶的量的相对增加。
VOC是在普通室温具有高蒸气压的有机化学品。它们的高蒸气压是由低沸腾温度引起的,该低沸腾温度导致大量分子蒸发或升华并且进入周围的空气。一些VOC对人体健康有危险或对环境造成危害。虽然各个政府机构对什么构成VOC具有不同的定义,但欧洲联盟将VOC定义为“在101.3kPa的标准大气压测量的具有小于或等于250摄氏度(℃)的初始沸点的任何有机化合物”。导致VOC的排放的化合物的实例包括醇(乙醇、甲醇、异丙醇等)、氯氟烃、乙烷、二醇醚、酮(丙酮、甲基乙基酮等)、硅氧烷、二甲苯、苯、丁醛、二硫化碳、乙酸乙酯、甲醛、乙酸甲酯、二氯甲烷、全氯乙烯、苯乙烯、四氢呋喃、甲苯及类似物。特别要避免的VOC的实例包括丙酮、苯、乙醇、乙酸乙酯、甲醛、异丙醇、甲醇、乙酸甲酯、二氯甲烷、甲基乙基酮、四氢呋喃和甲苯。
关于鞋类制造,常用的VOC的实例包括丙酮、甲基乙基酮、乙酸甲酯、乙酸乙酯、二氯甲烷、甲基环己烷、乙酸正丁酯、甲基丙烯酸甲酯及其组合。关于如本领域已知的和当前实践的传统清洁和/或粘合剂活化,消耗约7克/双鞋的溶剂。使用本公开内容的实施方案减少或消除了大部分先前消耗的溶剂(例如,消除了清洁和/或活化以及本公开内容的粘合剂中不存在的VOC)。
在这方面,在一些实例中,未交联或部分交联的粘合剂组合物大体上不含排放VOC的化合物。在另一个实例中,未交联或部分交联的粘合剂组合物可以被布置在鞋类物品的未固化或部分固化的橡胶部件(例如,围条、鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件)上,以将未固化或部分固化的橡胶部件固定至其他部件,使得可以产生大体上不含排放VOC的化合物的鞋类物品。在其他实例中,未固化或部分固化的围条(包括未固化或部分固化的橡胶基础围条和未交联或部分交联的粘合剂组合物)大体上不含排放VOC的化合物。在又其他实例中,制造未固化或部分固化的围条的工艺大体上没有VOC的排放。在又其他实例中,使用未固化或部分固化的围条以将围条固定至鞋面构件或鞋结构或两者的工艺大体上没有VOC的排放。在一个实例中,本公开内容的未固化或部分固化的围条在用于制造如本文描述的鞋类物品期间大体上不含并且不排放具有在101.3kPa的标准大气压测量的小于或等于250℃的初始沸点的任何有机化合物。在另一个实例中,本公开内容的未固化或部分固化的围条在用于制造如本文描述的鞋类物品期间大体上不含并且不排放丙酮、甲基乙基酮、乙酸甲酯、乙酸乙酯、二氯甲烷、甲基环己烷、乙酸正丁酯、甲基丙烯酸甲酯及其组合。
虽然在一些实例中,组合物在低于约55摄氏度的温度是固体,但是组合物在高于约55℃至60℃的温度可以相变成液体或半固体,或者当被加热至高于约55℃至60℃的温度时可以变得越来越发粘,这允许组合物被储存,并且然后在将未固化或部分固化的橡胶部件粘附至其他部件(例如,将围条粘附至鞋面构件和其他部件)之前,通过升高温度来活化,而不是被涂底漆(例如,使用溶剂来活化)或“湿法”施加并且立即干燥。因此,与用于类似目的的传统的基于溶剂的处理剂和/或粘合剂体系相比,使用本文描述的组合物可以导致在组合物的使用期间很少(如果有的话)的VOC被排放(例如,少至少50重量百分比、少至少75重量百分比、少至少90重量百分比、或少至少99重量百分比)。另外,使用本文描述的组合物还在鞋类物品中提供所需的结合性能。
粘合剂(例如,组合物)可以被布置在用于形成鞋类物品的未固化或部分固化的橡胶部件(例如,围条、鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件)的一个或更多个表面上。使用围条来举例说明可以如何实现这一点的实例,但是粘合剂可以被施加至用于形成鞋的所有其他未固化或部分固化的橡胶部件且围条实例仅仅是例证,并且可以被施加至鞋类物品的其他未固化或部分固化的橡胶部件。
未固化或部分固化的围条可以通过首先使组分混合以形成粘合剂(例如,组合物)来形成。随后,未交联或部分交联的粘合剂材料可以被施加至基础围条材料,形成具有两层结构(例如,粘合剂和基础围条)的围条。例如,未交联或部分交联的粘合剂可以与形成基础围条的橡胶组合物共挤出,以形成具有两层结构的未固化或部分固化的围条,其中第一层是基础围条并且第二层是未交联或部分交联的粘合剂,并且第一层和第二层被布置为彼此相邻。
如上文所提到的,组合物可以用于围条。对于未固化或部分固化的围条,条具有基础围条和未交联或部分交联的粘合剂(例如,组合物)的两层结构。基础围条包含未固化或部分固化的橡胶,并且具有第一侧面和与第一侧面相对的第二侧面。未交联或部分交联的粘合剂与基础围条的第二侧面上的未固化或部分固化的橡胶接触。在形成之后且在使用之前,未固化或部分固化的围条可以在未固化或部分固化的围条的第一侧面和/或第二侧面上包含隔离材料(release material)(膜或纺织品),使得条可以被堆叠和储存。
对于其他未固化或部分固化的橡胶部件(例如,鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件),粘合剂组合物可以通过用诸如刷子的装置施加、喷涂、浇注或以其他方式放置到未固化或部分固化的橡胶部件的表面上而被布置在部件上。具有布置在其上的粘合剂组合物的未固化或部分固化的橡胶部件可以具有与围条类似的两层结构。
由于未固化或部分固化的围条包括包含增粘树脂的粘合剂组合物,所以在加工期间,增粘树脂可以用于将围条保持在鞋面构件和/或鞋结构(例如,鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件)上的适当位置,直到实现结合。由于粘合剂组合物中存在未固化或部分固化的橡胶和橡胶固化包装,所以将未固化或部分固化的围条暴露于足以固化围条和/或鞋结构的橡胶的加工条件导致粘合剂的橡胶自身交联、与围条的橡胶交联、与鞋结构的橡胶交联或其任何组合,形成具有足以承受鞋类物品通常暴露于的磨损和撕裂的强度的结合部。
在加工(例如,活化和固化)之后,由未固化或部分固化的围条形成固化的橡胶围条。固化的橡胶围条具有基础围条和交联的粘合剂层的两层结构,其中基础围条和交联的粘合剂层彼此结合。在固化之后,基础围条包含固化的橡胶,其中交联的粘合剂与基础围条的第二侧面上的固化的橡胶接触(例如,结合)。
关于使用未交联或部分交联的围条来制造鞋类物品,未固化或部分固化的围条可以被布置在鞋类物品的鞋面构件和未固化或部分固化的鞋结构之间的外边缘周边上的接合部(junction)上。未交联或部分交联的围条可以大体上围绕鞋类物品的整个周边延伸。在可选择方案中,一件或更多件未交联或部分交联的围条可以围绕鞋类物品的一部分(例如,鞋跟区域、鞋头区域)延伸。在将未固化或部分固化的围条布置到接合部之前或在将未固化或部分固化的围条布置到接合部的同时,未固化或部分固化的围条通过加热至约55摄氏度至60摄氏度或更高而被活化。在一些实例中,加热导致粘合剂层软化或变成液体或半固体层或变得越来越发粘。未交联或部分交联的围条可以被附接至鞋面构件,并且通过粘合剂保持在适当的位置,直到固化。例如,在固化工艺(例如,硫化工艺)期间,未交联或部分交联的围条可以沿着接合点(joint)附接至鞋面构件和/或未固化或部分固化的鞋结构。在固化工艺完成后,鞋面构件和固化的鞋结构至少部分地通过固化的围条彼此固定。类似地,其他未固化或部分固化的橡胶部件(例如,鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件)可以被附接至鞋类物品的一个或更多个部件,以在固化工艺期间固定它们。
本公开内容提供了一种未固化或部分固化的围条,包括:基础围条和未交联或部分交联的粘合剂的两层结构,其中基础围条包含未固化或部分固化的橡胶,其中未固化或部分固化的围条具有第一侧面和与第一侧面相对的第二侧面,其中未交联或部分交联的粘合剂与未固化或部分固化的围条的第二侧面上的未固化或部分固化的橡胶接触,其中未交联或部分交联的粘合剂包含:未固化或部分固化的橡胶;增粘树脂;以及填料。
与鞋类制造中使用的常规的粘合剂组合物相比,本公开内容的粘合剂组合物的实例可以具有更高浓度的未固化或部分固化的橡胶。当未固化或部分固化的围条用于鞋类制造时,这种高浓度的未固化或部分固化的橡胶允许粘合剂组合物与基础围条、鞋结构或两者的未固化或部分固化的橡胶交联,并且与这些部件中的一个或两个形成固定、柔性的结合部。高浓度的未固化或部分固化的橡胶还增加了在粘合剂组合物交联后粘合剂组合物本身的柔性。在一个实例中,粘合剂组合物可以包含至少40重量百分比的未固化或部分固化的橡胶。粘合剂组合物可以包含从约40重量百分比至约80重量百分比的未固化或部分固化的橡胶。粘合剂组合物可以包含从约40重量百分比至约70重量百分比的未固化或部分固化的橡胶。粘合剂组合物可以包含从约40重量百分比至约64重量百分比的未固化或部分固化的橡胶。
与鞋类制造中使用的常规的粘合剂组合物相比,本公开内容的粘合剂组合物的实例可以具有更高浓度的增粘树脂。高浓度的增粘树脂允许粘合剂组合物在制造工艺期间很好地粘附至基础围条或鞋结构或两者,并且在粘合剂组合物和橡胶部件被完全固化之前将部件保持在一起。粘合剂组合物可以包含至少5重量百分比的增粘树脂。粘合剂可以包含从约5重量百分比至约15重量百分比的增粘树脂。粘合剂可以包含约8重量百分比至约12重量百分比的增粘树脂。在一个方面中,增粘树脂可以包含C3-C9石油树脂或萜烯酚醛树脂或两者。在另一个方面中,增粘树脂可以包含C5石油树脂或基本上由C5石油树脂组成。增粘树脂可以包含C9石油树脂或基本上由C9石油树脂组成。增粘树脂可以包含萜烯酚醛树脂或基本上由萜烯酚醛树脂组成。
本公开内容的粘合剂组合物的实例可以包括高浓度的未固化或部分固化的橡胶和增粘树脂两者。例如,粘合剂组合物中存在的未固化或部分固化的橡胶的重量百分比与增粘剂的重量百分比的比可以是至少3:1。在一个方面中,该比可以是约3:1至5:1。在另一个方面中,该比可以是至少4:1。
除了未固化或部分固化的橡胶和增粘树脂之外,粘合剂组合物任选地可以包含填料。当填料存在时,粘合剂组合物可以包含至少10重量百分比的填料。粘合剂组合物可以包含至少20重量百分比的填料。粘合剂组合物可以包含从约10重量百分比至约50重量百分比的填料。粘合剂组合物可以包含从约20重量百分比至约44重量百分比的填料。
未固化或部分固化的橡胶的重量百分比与填料的重量百分比的比可以是至少1.5:1,或者可以是约1.5:1至2.5:1,或者可以是约1.5:1至约2:1。粘合剂组合物中填料的重量百分比与增粘剂的重量百分比的比可以是至少1.5:1,或者可以是约1.5:1至2.5:1,或者可以是约1.5:1至约2:1。
未交联或部分交联的粘合剂的组分的重量百分比可以如下:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约8重量百分比至12重量百分比的增粘树脂、约20重量百分比至44重量百分比的填料以及0重量百分比至15重量百分比的一种或更多种另外的组分。组合物大体上不含当在约1个大气压被加热至60摄氏度或更高的温度时变得挥发的有机化合物,其中有机化合物包括丙酮、甲基乙基酮、乙酸乙酯或其组合。
本公开内容提供了一种制造鞋类物品的方法,包括:活化未固化或部分固化的围条,其中未固化或部分固化的围条是基础围条和未交联或部分交联的粘合剂的两层结构,其中基础围条包含未固化或部分固化的橡胶,其中未固化或部分固化的围条具有第一侧面和与第一侧面相对的第二侧面,其中未交联或部分交联的粘合剂与未固化或部分固化的围条的第二侧面上的未固化或部分固化的橡胶接触,其中未交联或部分交联的粘合剂包含:未固化或部分固化的橡胶、增粘树脂、以及填料;在鞋面构件和未固化或部分固化的鞋结构之间的接触点处的接合部处,将未固化或部分固化的围条布置在接合部上鞋类的周边的第一部分上,使得未固化或部分固化的围条沿着接合部被布置在鞋面构件的第一部分上和未固化或部分固化的鞋结构的第一部分上,其中包含粘合剂的未固化或部分固化的围条的一部分邻近鞋面构件的第一部分、未固化或部分固化的鞋结构的第一部分、和接合部;以及固化物品以形成包括固化的橡胶围条和固化的橡胶鞋结构的固化的橡胶鞋,其中固化的橡胶鞋结构和鞋面构件至少部分地通过在围条的固化的橡胶和鞋结构的固化的橡胶之间形成的交联部结合在一起。
当提供值的范围时,在该范围的上限和下限之间的每一个中间值(以下限单位的十分之一为单位,除非上下文另外明确指示)以及该陈述的范围中的任何其他陈述的值或中间值被涵盖在本公开内容中。这些较小范围的上限和下限可以独立地被包括在较小范围中,并且也被涵盖在本公开内容中,受制于所陈述的范围中任何特定排除的限值。当所陈述的范围包括限值中的一个或两个时,排除那些被包括的限值中的任一个或两个的范围也被包括在本公开内容中。
在阅读本公开内容后对于本领域技术人员将明显的是,本文描述和示出的各个方面中的每一个具有离散的部件和特征,这些部件和特征可以在不脱离本公开内容的范围或精神的情况下与其他若干个方面中的任何方面的特征容易地分离或组合。任何叙述的方法可以以所叙述的事件的顺序来进行或以逻辑上可能的任何其他顺序来进行。
除非另外指示,否则本公开内容可以采用本领域的技术范围内的材料科学、化学、纺织、聚合物化学、纺织化学及类似技术的技术。这样的技术在文献中被充分解释。
除非另外定义,否则本文使用的所有技术术语和科学术语具有与材料科学、化学、纺织、聚合物化学、纺织化学及类似领域的普通技术人员通常理解的相同的含义。尽管与本文描述的方法和材料类似或等同的方法和材料可以用于本公开内容的实践或测试,但本文描述了合适的方法和材料。
如说明书和所附权利要求中使用的,单数形式“一(a)”、“一(an)”和“该(the)”可以包括复数指示物,除非上下文另外明确指示。因此,例如,提及“一个支撑物”包括多于一个支撑物。在本说明书和所附的权利要求中,将提及许多术语,这些术语应被定义为具有以下含义,除非相反的意图是明显的。
如本文使用的,术语“重量”指的是质量值,诸如具有克、千克的单位及类似单位的质量值。此外,通过端点对数值范围的叙述包括端点和该数值范围内的所有数。例如,在从按重量计40%至按重量计60%的范围内的浓度包括按重量计40%、按重量计60%的浓度,以及在按重量计40%和按重量计60%之间的所有浓度(例如,40.1%、41%、45%、50%、52.5%、55%、59%等)。
如本文使用的,术语“提供”,诸如“提供分层的材料”,当在权利要求中叙述时,不意图要求所提供的制品(item)的任何特定的递送或接收。而是,为了清楚和易于阅读的目的,术语“提供”仅用于叙述将在权利要求的后续要素中提及的制品。
如本文使用的,术语“至少一个/种”要素和“一个/种或更多个/种”要素可互换地使用,并且具有包括单个要素和多于一个要素的相同的含义,并且还可以由要素末尾的后缀“(s)”表示。例如,“至少一种聚氨酯”、“一种或更多种聚氨酯”和“聚氨酯(polyurethane(s))”可以可互换地使用,并且具有相同的含义。
现在已经大体上描述了本公开内容,提供另外的细节。本公开内容的组合物可以被用作鞋类物品中的粘合剂。特别地,粘合剂可以用于将未固化或部分固化的橡胶部件彼此固定,所述未固化或部分固化的橡胶部件诸如围条、鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层、鞋外底及类似部件。在一个实例中,粘合剂可以用于围条,其中围条可以具有基础围条和粘合剂的两层结构。其他橡胶部件也可以具有带有粘合剂的两层结构。尽管实施方案不限于围条,但是围条的实例为了说明的目的被提供。
图1图示出本公开内容的围条10的横截面视图;围条包括基础围条11和粘合剂12。如在本文中详细提供的,围条可以被形成、活化、布置在鞋类物品上并固化。
图2是图示出未固化或部分固化的围条的形成的框图。在步骤1中,形成粘合剂的材料被混合。在步骤2中,基础围条的材料(例如,未固化或部分固化的橡胶材料)和未交联或部分交联的粘合剂彼此接触,以形成如步骤3中示出的未固化或部分固化的围条。在实例中,基础围条材料和未交联或部分交联的粘合剂可以被共挤出以形成未固化或部分固化的围条。在另一个实例中,可以制造基础围条,并且未交联或部分交联的粘合剂可以被形成为膜,并且然后该膜可以被施加(例如,层压)至基础围条,以形成未固化或部分固化的围条。在又一个实例中,可以制造基础围条,并且然后未交联或部分交联的粘合剂可以被喷涂、印刷或浇注至基础围条,以形成未固化或部分固化的围条。
图3A是图示出未固化或部分固化的围条在鞋类物品上的活化和放置的框图。在步骤A中,未固化或部分固化的围条被活化(例如,被加热至高于60摄氏度),使得粘合剂变得更软或越来越发粘(例如,使得它变得足够粘,以致于它当放置成与材料的表面接触时粘附)。在步骤B中,未固化或部分固化的围条被布置在鞋面构件和未固化或部分固化的鞋结构之间的接合部上。在步骤C中,未固化或部分固化的围条和未固化或部分固化的鞋结构被固化,以形成具有粘附至鞋面构件和固化的鞋结构的固化的围条的鞋类物品。
图3B是图示出未固化或部分固化的围条在鞋类物品上的活化和放置的框图。在步骤A中,未固化或部分固化的围条被活化(例如,被加热至高于60摄氏度),使得粘合剂变得更软或越来越发粘(例如,使得它变得足够粘,以致于它当放置成接触时粘附)。在步骤B中,未固化或部分固化的围条被布置在鞋面构件和未固化或部分固化的鞋结构之间的接合部上。未固化或部分固化的围条可以被布置到鞋类上的粘合剂以及处理剂上。当在施加围条之前将另外的粘合剂施加至鞋面材料或橡胶鞋或两者时,施加至鞋面材料或橡胶鞋或两者的粘合剂可以是如本文描述的粘合剂组合物。可选择地,在施加围条之前施加至鞋面材料或橡胶鞋或两者的粘合剂组合物可以是鞋类制造中使用的常规粘合剂,诸如包含一种或更多种有机溶剂的水性粘合剂。在步骤C中,未固化或部分固化的围条和未固化或部分固化的鞋结构被固化,以形成具有粘附至鞋面构件和固化的鞋结构的固化的围条的鞋类物品。
粘合剂的组合物可以包含未固化或部分固化的橡胶、增粘树脂和任选地填料(例如,二氧化硅)以及一种或更多种其他组分(例如,填料、聚醚、脂肪酸、橡胶固化剂、抗氧化剂和防雾剂)。该组合物是一种未交联或部分交联的粘合剂,该未交联或部分交联的粘合剂可以被施加至基础围条,使得未固化或部分固化的围条可以在橡胶固化工艺中与未固化或部分固化的鞋结构和鞋面构件结合。典型地,将常规的围条布置到鞋类包括多个个体和多个步骤,而本公开内容减少了所需的个体和/或步骤的数目,因此简化了用于制造鞋类的工艺。另外,本文描述的粘合剂的组合物包含很少(如果有的话)的VOC,和/或活化围条的步骤不需要用溶剂涂底漆,因此与传统工艺相比,本公开内容的粘附围条的工艺可以在排放更少且有害程度更低的VOC的情况下进行。这些优点可以在保持或改进耐用性的同时实现。
尽管在围条的粘合剂中使用该组合物,但是该组合物(例如,作为粘合剂)可以被并入到物品诸如并入橡胶部件的纺织品中。例如,纺织品可以包括鞋类或其部件、服装(例如,衬衫、毛衫、裤子、短裤、手套、眼镜、袜子、带沿帽、便帽、夹克、内衣)或其部件、容装物(例如,背包、包)和用于家具(例如,椅子、长沙发、车辆座椅)的装饰用品、床上用品(例如,床单、毛毯)、桌布、毛巾、旗帜、帐篷、帆和降落伞。此外,该组合物可以用于生产物品或被布置在物品上的其他制品,其中物品可以是击打装置(例如,球棒、球拍、棍棒、球棍、高尔夫球杆、桨等)、运动装备(例如,高尔夫球袋、棒球手套和足球手套、英式足球限制结构)、保护性装备(例如,垫、头盔、防护件、帽舌、面罩、护目镜等)、机车装备(例如,自行车、摩托车、滑板、汽车、卡车、船、冲浪板、雪橇、滑雪板等)、用于多种运动的球或冰球、钓鱼或狩猎装备、家具、电子装备、建筑材料、眼睛防护物(eyewear)、钟表、珠宝以及类似物。
本公开内容的鞋类物品可以被设计用于多种用途,诸如休闲用途、体育用途、运动用途、军事用途、工作相关用途或娱乐用途。鞋类物品可以被设计用于户外体育活动,诸如国际足球(global football)/英式足球(soccer)、高尔夫、美式橄榄球、英式橄榄球、棒球、跑步、田径、自行车(例如,公路自行车和山地自行车)以及类似户外体育活动。鞋类物品可以任选地包括附着摩擦力元件(例如,凸耳、防滑件、鞋钉(stud)和钉子(spike)以及胎面图案),以在柔软和光滑的表面上提供附着摩擦力。防滑件、鞋钉和钉子通常被包括在被设计用于运动诸如国际足球/英式足球、高尔夫、美式橄榄球、英式橄榄球、棒球及类似运动的鞋类中,这些运动经常在未铺砌的表面上进行。凸耳和/或增强的胎面图案通常被包括在鞋类中,包括设计用于在诸如越野跑、徒步旅行和军事用途的恶劣户外条件下使用的靴子。
图4图示出鞋类物品100的透视图。鞋类包括鞋面构件102和固化的鞋底结构104(例如,一种或更多种橡胶部件,诸如鞋底夹层、杯形鞋底、鞋外底和类似部件),其中固化的围条114至少部分地粘附鞋面构件102和固化的鞋底结构104。特别地,在制造期间,未固化或部分固化的围条被布置在鞋类物品100的鞋面构件102和未固化或部分固化的鞋底结构之间的外边缘周边上的接合部上。未固化或部分固化的围条可以大体上围绕鞋类物品100的整个周边延伸。在可选择方案中,一件或更多件未固化或部分固化的围条可以围绕鞋类物品的一部分(例如,鞋跟区域、鞋头区域)延伸。在固化工艺(例如,硫化工艺)期间,未固化或部分固化的围条可以沿着接合点附接至鞋面构件102和未固化或部分固化的鞋底结构。在固化工艺完成后,鞋面构件102和固化的鞋底结构104至少部分地通过固化的围条114彼此固定。尽管未示出,但是其他橡胶部件诸如鞋头、缓冲器、鞋底夹层、杯形鞋底、鞋跟标志及类似部件可以使用本公开内容的粘合剂被固定至鞋类物品。
制造鞋类物品的方法可以包括活化未固化或部分固化的围条。未固化或部分固化的围条可以通过将未固化或部分固化的围条加热至约55摄氏度至60摄氏度持续约2分钟至60分钟来活化。在活化后,未固化或部分固化的围条被布置在鞋面构件和未固化或部分固化的鞋结构之间的接触点处的接合部处。特别地,未固化或部分固化的围条被布置在接合部上鞋类的周边的第一部分上,使得未固化或部分固化的围条沿着接合部被布置在鞋面构件的第一部分上和未固化或部分固化的鞋结构的第一部分上。接下来,物品被固化(例如,硫化)以形成鞋类物品,该鞋类物品包括至少部分地通过固化的围条固定在一起的固化的鞋结构和鞋面构件。固化工艺可以包括将物品加热至约100摄氏度至140摄氏度,或任选地约120摄氏度持续约50分钟至120分钟。活化和固化工艺可以在约1个大气压进行。类似地,使用粘合剂的其他橡胶部件可以以这种方式被固定至鞋。
现在已经大体上描述了本公开内容的方面,提供关于用于粘合剂中的组合物的另外的细节。该组合物是一种未交联或部分交联的粘合剂,该未交联或部分交联的粘合剂被配置用于在橡胶固化工艺中结合至未固化或部分固化的橡胶或结合在未固化或部分固化的橡胶之间。在一个实例中,该组合物大体上不含排放VOC的化合物(例如,大体上不含丙酮、甲基乙基酮、乙酸乙酯及类似物)。例如,与使用传统处理剂或传统粘合剂或两者的方法相比,在活化和固化期间释放(例如,少至少50重量百分比、少至少75重量百分比、少至少90重量百分比、少至少99重量百分比)的VOC。在一些实例中,该组合物在低于55摄氏度的温度是固体,并且在高于约55摄氏度至60摄氏度的温度是液体或半固体。在其他实例中,粘合剂在高于约55摄氏度至60摄氏度的温度变得越来越发粘。
在两个实例中,由于粘合剂的温度敏感性,当围条包括在基础围条上的未交联或部分交联的粘合剂的层时,复合材料(例如,未固化或部分固化的围条)可以被形成,并且然后通过任选地在复合材料的一个或两个侧面上或单独在复合材料围条的层之间包括隔离层来储存用于将来使用。然后在使用之前,未固化或部分固化的围条可以被加热(例如,高于60摄氏度)以活化未交联或部分交联的粘合剂,这与使用溶剂并在使用之前需要干燥的其他粘合剂相反。随后,在具有更少的步骤还与使用传统的基于溶剂的处理剂和/或粘合剂的工艺相比产生更少的VOC的更方便的工艺中,具有未交联或部分交联的粘合剂的未固化或部分固化的围条被布置在鞋类物品上,并且然后被固化以附接鞋面构件和鞋结构。
组合物可以包括未固化或部分固化的橡胶、添加剂、增粘树脂和橡胶固化剂。任选的另外的组分可以包括其他填料、聚醚、橡胶固化剂、脂肪酸、抗氧化剂、防雾剂、着色剂及类似物中的一种或更多种。
组合物的橡胶(例如,未固化的橡胶、部分固化的橡胶或固化的橡胶)、基础围条、鞋结构或这些的全部可以包含一种或更多种天然橡胶和/或合成橡胶。橡胶是弹性材料,诸如热固性材料或热塑性橡胶。
“热固性材料”被理解为指的是不能被加热并熔化的材料,因为其熔化温度处于或高于其分解温度。“热固性材料”指的是包含至少一种热固性聚合物(例如,任选地可以包含热塑性聚合物)的组合物。热固性聚合物和/或热固性材料可以使用光化辐射(例如,热能、紫外线辐射、可见光辐射、高能辐射、红外线辐射)由前体(例如,未固化或部分固化的聚合物或材料)来制备,以形成不再保持完全热塑性的部分固化或完全固化的聚合物或材料。在一些情况下,固化或部分固化的弹性材料可以保持一些热塑性性质,因为可能在高温和/或高压部分地软化和模制弹性材料,但是不可能熔化和重整弹性材料。例如,可以使用高压和/或催化剂来促进固化。固化过程是不可逆的,因为其导致前体的交联反应和/或聚合反应。未固化或部分固化的弹性材料在固化之前可以是可延展的或液态的。在一些情况下,未固化的组合物或部分固化的弹性材料可以被模制成它们的最终形状。在硬化后,热固性材料不能被再熔化以便再成形,但是可能使其软化。相反地,热塑性橡胶包括弹性性质和热塑性性质两者,并且可以被反复熔化和冷却。
橡胶可以是天然橡胶、聚丁二烯橡胶、聚异戊二烯橡胶或其任何组合。橡胶可以包括热塑性聚氨酯弹性体、热塑性聚脲弹性体、热塑性聚酰胺弹性体(PEBA或聚醚嵌段聚酰胺)、热塑性聚酯弹性体、乙烯和α-烯烃的茂金属催化的嵌段共聚物以及苯乙烯嵌段共聚物弹性体。天然橡胶或合成橡胶可以包括:丁二烯橡胶、苯乙烯-丁二烯(SBR)橡胶、丁基橡胶、异戊二烯橡胶、氨基甲酸酯橡胶(例如,可碾磨的)、丁腈橡胶、氯丁橡胶、乙烯丙烯二烯单体(EPDM)橡胶、表氯醇橡胶、聚丙烯酸酯橡胶、聚醚嵌段酰胺、乙烯-乙酸乙烯酯、乙烯-丙烯橡胶、氨基甲酸酯橡胶或其任何组合。橡胶化合物的其他实例包括但不限于聚降冰片烯橡胶、甲基丙烯酸甲酯丁二烯苯乙烯橡胶(MBS)、苯乙烯乙烯丁烯(SEBS)橡胶、有机硅橡胶及其混合物。橡胶化合物的还其他实例可以包括热塑性聚酯-聚氨酯、聚醚-聚氨酯、聚碳酸酯-聚氨酯、尼龙6、尼龙66、尼龙610、尼龙11、尼龙12、共聚的尼龙、尼龙MXD6、尼龙46、HYTREL(从DuPont可获得)、EXACT(从ExxonMobil可获得)、ENGAGE(从Dow Chemical Company可获得)、聚(苯乙烯-丁二烯-苯乙烯)、聚(苯乙烯-乙烯-共-丁烯-苯乙烯)和聚(苯乙烯-异戊二烯-苯乙烯)。
在方面中,橡胶是天然橡胶。未固化或部分固化的橡胶部件(例如,未固化或部分固化的围条)和粘合剂中的每一种包含约7重量百分比或更多的天然橡胶或约8重量百分比或更多的天然橡胶。尽管不意图受理论束缚,但是包含天然橡胶的每种部件和粘合剂具有改进的结合和耐用性。
在方面中,天然橡胶与增粘剂的比可以是约3:1至5:1或约4:1。天然橡胶与填料的比可以是约1.5:1至2.5:1或约2:1。填料与增粘剂的比可以是约1.5:1至2.5:1或约2:1。
橡胶可以包含添加剂。例如,添加剂可以包含多于一个聚合物链,这些聚合物链单独地具有接枝到聚合物链的马来酸酐部分。添加剂可以是已经通过将马来酸酐基团接枝到聚合物主链、端基或侧基中而被改性的官能化聚合物,包括具有马来酸酐接枝的基于乙烯的聚合物。添加剂可以是马来酸酐改性的聚合物,诸如“FUSABOND”(由E.I.du Pont deNemours and Company,Wilmington,DE,USA出售)。官能化聚合物可以包括改性的乙烯丙烯酸酯一氧化碳三元共聚物、乙烯乙酸乙烯酯(EVA)、聚乙烯、茂金属聚乙烯、乙烯丙烯橡胶和聚丙烯,其中对官能聚合物的改性可以包括接枝到官能聚合物的马来酸酐。未固化的橡胶制剂中存在的添加剂的量可以是多达10份每百份树脂(phr)、或从约1phr至约8phr或从约3phr至约6phr。
增粘树脂可以是烃类树脂、萜烯树脂或其组合。烃类树脂可以是脂肪族烃类树脂(例如,C1至C9或C3至C9),或芳香族烃类树脂(例如,C1至C9或C3至C9)。烃类树脂可以是芳香族烃类树脂(例如,C9石油树脂、C8石油树脂、C5石油树脂)。萜烯树脂选自萜烯酚醛树脂、聚萜烯树脂、苯乙烯化萜烯树脂或其组合。
填料可以包括二氧化硅、炭黑、滑石、钙组分(例如,钙组分包括纳米钙、碳酸钙或其组合)及其组合。在方面中,填料是二氧化硅(例如,具有纳米至微米尺度的尺寸)。
未固化或部分固化的橡胶可以至少部分地(例如,约5%或更多、约10%或更多、约25%或更多、约50%或更多)溶于聚醚中。聚醚可以是聚亚烷基二醇(例如,C2至C6),诸如聚乙二醇或聚丙二醇(例如,约3000道尔顿至6000道尔顿或约4000道尔顿)。
组合物可以包含脂肪酸。脂肪酸可以包括饱和脂肪酸,诸如硬脂酸。
组合物还可以包含过程油(process oil),抗氧化剂(例如,苯乙烯酚),防雾剂(例如,脱水山梨糖醇酯)和/或包含交联剂、促进剂和交联阻滞剂中的至少一种的固化包装。过程油的实例包括但不限于石蜡油和/或芳香油。
固化包装可以包含交联剂,诸如硫组分(例如,元素硫或含硫有机化合物(例如,单硫化物化合物、二硫化物化合物或多硫化物化合物))、或过氧化物剂(例如,二叔戊基过氧化物、二叔丁基过氧化物、叔丁基枯基过氧化物、二枯基过氧化物(DCP)、二(2-甲基-1-苯基-2-丙基)过氧化物、叔丁基2-甲基-1-苯基-2-丙基过氧化物、二(叔丁基过氧基)-二异丙基苯、2,5-二甲基-2,5-二(叔丁基过氧基)己烷、2,5-二甲基-2,5-二(叔丁基过氧基)己炔-3,1,1-二(叔丁基过氧基)-3,3,5-三甲基环己烷、4,4-二(叔丁基过氧基)-正丁基戊酸酯及其混合物)、或硫组分和过氧化物剂的组合。在方面中,固化包装包含硫组分。
固化包装可以包含:促进剂,诸如N-环己基-2-苯并噻唑亚磺酰胺(CBZ)、N-氧基二亚乙基-2-苯并噻唑亚磺酰胺、N,N-二异丙基-2-苯并噻唑亚磺酰胺、2-巯基苯并噻唑、2-(2,4-二硝基苯基)巯基苯并噻唑、2-(2,6-二乙基-4-吗啉基硫代)苯并噻唑和二苯并噻唑二硫化物;胍化合物,诸如二苯基胍(DPG)、三苯基胍、二邻腈胍(diorthonitrileguanidine)、邻腈双胍和邻苯二甲酸二苯基胍;醛胺化合物或醛氨化合物,诸如乙醛-苯胺反应产物、丁醛-苯胺缩合物、六亚甲基四胺和乙醛合氨;咪唑啉化合物,诸如2-巯基咪唑啉;硫脲化合物,诸如对称二苯硫脲(thiocarbanilide)、二乙基硫脲、二丁基硫脲、三甲基硫脲和二邻甲苯基硫脲;秋兰姆(thiuram)化合物,诸如单硫化四甲基秋兰姆、二硫化四甲基秋兰姆、二硫化四乙基秋兰姆、二硫化四丁基秋兰姆和四硫化五亚甲基秋兰姆;二硫醇盐化合物(dithioate compound),诸如二甲基二硫代氨基甲酸锌、二乙基二硫代氨基甲酸锌、二正丁基二硫代氨基甲酸锌、乙基苯基二硫代氨基甲酸锌、丁基苯基二硫代氨基甲酸锌、二甲基二硫代氨基甲酸钠、二甲基二硫代氨基甲酸硒和二甲基二硫代氨基甲酸碲;黄原酸盐化合物,诸如二丁基黄原酸锌;以及锌组分诸如氧化锌、碳酸锌和本文提到的其他锌化合物。特别地,促进剂可以包括:N-乙基-N-苯基二硫代氨基甲酸锌盐、2-巯基苯并噻唑、2,2'-二苯并噻唑二硫化物、单硫化四甲基秋兰姆、二硫化四苄基秋兰姆及其组合。
交联阻滞剂可以包括但不限于烷氧基酚、儿茶酚和苯醌,以及烷氧基酚诸如3,5-二叔丁基-4-羟基茴香醚。
组合物(例如,粘合剂)的组分的重量百分比可以是:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约8重量百分比至12重量百分比的增粘树脂、约20重量百分比至44重量百分比的填料以及0重量百分比至15重量百分比的一种或更多种另外的组分。
组合物(例如,粘合剂)的组分的重量百分比可以是:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约1重量百分比至1.4重量百分比的聚醚、约8重量百分比至12重量百分比的增粘树脂、约1.4重量百分比至2重量百分比的橡胶固化剂和任选地以下中的一种或更多种:约20重量百分比至44重量百分比的填料、约2重量百分比至2.6重量百分比的锌组分、约0.6重量百分比至1重量百分比的饱和脂肪酸、约0.1重量百分比至1.4重量百分比的促进剂、约0.1重量百分比至1.4重量百分比的防雾剂和约0.1重量百分比至1重量百分比的抗老化剂。
组合物可以通过在约50摄氏度至80摄氏度的烘箱中使上文描述的组分混合来制备。在混合后,组合物(粘合剂)可以被用于形成未固化或部分固化的围条(或被施加至其他未固化或部分固化的橡胶部件)。未固化或部分固化的围条可以通过将基础围条材料(例如,橡胶)和粘合剂施加(例如挤出、层压、印刷、浇注)至彼此而形成,其中未固化或部分固化的围条具有两层结构。例如,基础围条材料(例如,橡胶)和粘合剂可以被共挤出。在另一个实例中,基础围条可以被形成,并且粘合剂被印刷、浇注或喷涂到基础围条上。第一层是基础围条(例如,未固化或部分固化的),并且第二层是未交联或部分交联的粘合剂,其中第一层和第二层被布置为彼此相邻。在这方面,未交联或部分交联的粘合剂与基础围条的第二侧面上的未固化或部分固化的橡胶接触。
固化的橡胶围条可以通过固化(例如,在硫化工艺中)由未固化或部分固化的围条形成。在固化之后,基础围条包含固化的橡胶,其中交联的粘合剂与基础围条的第二侧面上的固化的橡胶结合。此外,在固化之后,固化的围条沿着鞋面构件和固化的鞋结构之间的接合部被固定(例如,结合)至鞋面构件和固化的鞋结构。
基础围条可以由如本文中参考组合物中的橡胶描述的橡胶材料制备。交联的粘合剂层可以具有约0.1毫米至5毫米或约0.1毫米-1.4毫米的厚度。基础围条可以具有约0.1毫米至10毫米或更大或约0.5毫米至5毫米的厚度。基础围条可以具有约1毫米至150毫米或约5毫米至75毫米的宽度。固化的橡胶围条可以具有约0.2毫米至15毫米或更大或约0.6毫米至6毫米的厚度。
如本文使用的,术语“部分固化的”通常指的是具有小于或等于10-3摩尔每立方厘米、或小于或等于10-5摩尔每立方厘米的相对低的交联密度的化合物(例如,橡胶)。例如,部分固化的第一组合物或第二组合物可以具有在交联部之间存在的从约15个至约1500个单体单元。动态力学分析(DMA)可以用于确定化合物的模量平台(modulus plateau)。在高于化合物的玻璃化转变温度且低于化合物的熔点的模量平台的区域中,交联密度与化合物的模量成正比。如本文使用的,术语“固化的”通常指的是具有相对高的交联密度的化合物(例如,橡胶)。例如,固化的化合物的交联密度可以比未固化或部分固化的组合物的交联密度大至少20%、或大至少30%或大至少50%。
术语“部分固化的”可以表示实现大体上完全固化所需的总聚合的至少约1%、可选择地至少约5%的发生率。术语“完全固化的”意图意指大体上完全固化,其中固化的程度是使得固化的材料的物理性质在进一步暴露于诱导固化的条件(例如,温度、压力、固化剂的存在等)后不显著改变。
术语“部分交联的”可以表示实现大体上完全交联所需的总交联的至少约1%、可选择地至少约5%的发生率。术语“完全交联的”意图意指大体上完全交联,其中交联的程度是使得交联的材料的物理性质在进一步暴露于诱导交联的条件(例如,温度、压力、交联剂的存在等)后不显著改变。
除了橡胶之外,粘合剂组合物、基础围条、橡胶鞋结构、鞋面构件的材料或其任何组合可以包含一种或更多种另外的聚合物。本文描述的聚合物可以是热固性聚合物或热塑性聚合物(例如,其在粘合剂、基础围条及类似物中提及)。聚合物可以是弹性聚合物,包括弹性热固性聚合物或弹性热塑性聚合物。聚合物可以选自:聚氨酯(包括弹性聚氨酯、热塑性聚氨酯(TPU)和弹性TPU)、聚酯、聚醚、聚酰胺、乙烯基聚合物(例如,乙烯醇、乙烯酯、乙烯、丙烯酸酯、甲基丙烯酸酯、苯乙烯等的共聚物)、聚丙烯腈、聚苯醚、聚碳酸酯、聚脲、聚苯乙烯、其共聚物(包括聚酯-聚氨酯、聚醚-聚氨酯、聚碳酸酯-聚氨酯、聚醚嵌段聚酰胺(PEBA)和苯乙烯嵌段共聚物)及其任何组合,如本文描述的。聚合物可以包括选自由以下组成的组的一种或更多种聚合物:聚酯、聚醚、聚酰胺、聚氨酯、每种的聚烯烃共聚物及其组合。
术语“聚合物”指的是由多于一个被称为单体的重复结构单元形成的化合物。聚合物通常通过聚合反应形成,在聚合反应中,多于一个结构单元变得共价地键合在一起。当形成聚合物的单体单元全部具有相同的化学结构时,聚合物是均聚物。当聚合物包括两种或更多种具有不同化学结构的单体单元时,聚合物是共聚物。共聚物类型中的一个实例是三元共聚物,其包括三种不同类型的单体单元。共聚物可以包括两种或更多种无规地分布在聚合物中的不同单体(例如,无规共聚物)。可选择地,包含多于一种第一类型的单体的一个或更多个嵌段可以被结合到包含多于一种第二类型的单体的一个或更多个嵌段,形成嵌段共聚物。单个单体单元可以包括一个或更多个不同的化学官能团。
组合物还可以包含以下、由以下组成或基本上由以下组成:一种或更多种先前未描述的加工助剂。这些加工助剂可以独立地选自包括但不限于以下的组:引发剂、增塑剂、脱模剂(mold release agent)、润滑剂、抗氧化剂、阻燃剂、染料、颜料、增强填料和非增强填料、纤维增强剂和光稳定剂。
实施例:
实施例1
未固化或部分固化的围条的实例包括具有约0.1mm-1.2mm的厚度的粘合剂。粘合剂具有以下重量份:天然橡胶42份、二氧化硅16份、纳米钙和活性碳酸钙30份、聚乙二醇1.2份、碳酸锌2份、抗老化剂SP 0.9份、增粘树脂(C5石油树脂)8.4份、活性剂RX-87 0.5份、硬脂酸0.45份、硫1.05份和促进剂(PX粉末)1.05份。
未固化或部分固化的围条通过以下方法生产:
(1)粘合剂通过使上文列出的所有成分根据前文提及的比混合和共混来制备;
(2)基础围条的材料被混合、水冷却并切割;
(3)粘合剂和基础围条从挤出机中被共挤出;以及
(4)任选地,可以在未固化或部分固化的围条的层之中使用隔离衬垫(releaseliner)诸如隔离织物,使得未固化或部分固化的围条可以被堆叠用于储存。
实施例2
未固化或部分固化的围条的实例包括具有约0.1mm-1.2mm的厚度的粘合剂。粘合剂具有以下重量份:天然橡胶和合成橡胶的混合物50份、二氧化硅30份、纳米钙35份、聚乙二醇2份、氧化锌4份、抗老化剂SP 1.5份、增粘树脂(C9石油树脂)15份、活性剂RX-87 1份、硬脂酸1份、硫2份和促进剂(促进剂M)2份。
未固化或部分固化的围条通过以下方法生产:
(1)粘合剂通过使上文列出的所有成分根据前文提及的比混合和共混来制备;
(2)基础围条的材料被混合、水冷却并切割;
(3)粘合剂和基础围条从挤出机中被共挤出;以及
(4)任选地,可以在未固化或部分固化的围条的层之中使用隔离衬垫诸如隔离织物,使得未固化或部分固化的围条可以被堆叠用于储存。
实施例3
未固化或部分固化的围条的实例包括具有约0.1mm-1.2mm的厚度的粘合剂。粘合剂具有以下重量份:天然橡胶30份、二氧化硅5份、活性碳酸钙5份、聚乙二醇0.5份、碳酸锌1份、抗老化剂SP 0.1份、增粘树脂(萜烯酚醛树脂)5份、活性剂RX-87 0.1份、硬脂酸0.1份、硫0.5份和促进剂(促进剂TBZTD)0.5份。
未固化或部分固化的围条通过以下方法生产:
(1)粘合剂通过使上文列出的所有成分根据前文提及的比混合和共混来制备;
(2)基础围条的材料被混合、水冷却并切割;
(3)粘合剂和基础围条从挤出机中被共挤出;以及
(4)任选地,可以在未固化或部分固化的围条的层之中使用隔离衬垫诸如隔离织物,使得未固化或部分固化的围条可以被堆叠用于储存。
在将未固化或部分固化的围条施加至鞋面构件或鞋底结构(例如,橡胶部件诸如本文描述的那些)之前,粘合剂可以通过将未固化或部分固化的围条的至少粘合剂层加热至60摄氏度-70摄氏度的温度来活化。在活化围条的粘合剂后,使粘合剂与鞋面构件或鞋底结构或两者接触。任选地,在使鞋面构件或鞋底结构与活化的围条接触之前,处理剂或粘合剂或两者可以被施加至鞋面构件或鞋底结构或两者。在使围条的粘合剂与鞋面构件或鞋底结构或两者接触之后,向围条和鞋面构件或鞋底结构或两者施加压力。在施加压力之后或施加压力期间,光化辐射被施加至围条和鞋面构件或鞋底结构或两者的组合,固化围条的橡胶、橡胶鞋底结构、粘合剂或其任何组合,将部件(围条、鞋面构件、鞋底结构、粘合剂及其组合)彼此结合。
用实施例1-实施例3的固化的围条生产的固化橡胶鞋类物品的结合性能的测试方法是:在固化(例如,硫化)之后24小时,拉伸测试,以3.0kg/cm的标准;在固化之后24小时,60度的弯曲测试,以超过70000次的标准。使用常规的围条以及常规的粘合剂和处理剂制造的固化橡胶鞋类物品被用作对照。该工艺包括用处理剂处理未固化的围条,干燥处理剂,施加包含溶剂的水性粘合剂,并且然后干燥粘合剂。还用处理剂处理鞋面构件和鞋底结构,干燥处理剂,施加包含溶剂的水性粘合剂,并且然后干燥粘合剂。然后将常规制备的围条、鞋面构件和鞋底结构放在一起,施加压力,并且然后暴露于光化辐射以固化围条和鞋底结构的橡胶,将鞋面构件和鞋底结构结合在一起并形成固化橡胶鞋类物品。具体测试结果在下表1中示出。
表1用实施例1-实施例3的围条以及常规的围条和粘合剂生产的固化橡胶鞋类物品的结合性能
/>
如表1中示出的,用本公开内容的围条和方法生产的固化橡胶鞋类物品的结合性能与用传统材料和方法生产的固化橡胶鞋类物品的结合性能相当或优于用传统材料和方法生产的固化橡胶鞋类物品的结合性能。
实施例4
未固化或部分固化的围条的实例包括具有约0.1mm-1.2mm的厚度的粘合剂。粘合剂具有以下重量份:天然橡胶100份、二氧化硅45份、碳酸钙30份、聚乙二醇4.5份、碳酸锌4.76份、抗老化剂SP 2.4份、增粘树脂(C5石油树脂)20份、活性剂RX-87 1.2份、硬脂酸1份、硫1.7份和促进剂(PX粉末)1.6份。
固化的围条通过以下方法生产:
(1)粘合剂通过使上文列出的所有成分根据前文提及的比混合和共混来制备;
(2)基础围条的材料被混合、水冷却并切割;
(3)粘合剂和基础围条从挤出机中被共挤出;以及
(4)任选地,可以在未固化或部分固化的围条的层之中使用隔离衬垫诸如隔离织物,使得未固化或部分固化的围条可以被堆叠用于储存。
本公开内容还在以下项目中被描述。
项目1.一种组合物,包含:
未固化或部分固化的橡胶;
增粘树脂;以及任选地,
填料。
项目2.根据项目1所述的组合物,其中组合物的组分的重量百分比如下:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约8重量百分比至12重量百分比的增粘树脂、约20重量百分比至44重量百分比的填料以及0重量百分比至15重量百分比的一种或更多种另外的组分。
项目3.根据任一前述项目所述的组合物,其中组合物大体上不含当在约1个大气压被加热至60摄氏度或更高的温度时变得挥发的有机化合物。
项目4.根据项目3所述的组合物,其中有机化合物包括丙酮、甲基乙基酮、乙酸乙酯或其组合。
项目5.根据任一前述项目所述的组合物,其中组合物是一种未交联或部分交联的粘合剂,所述未交联或部分交联的粘合剂被配置用于在橡胶固化工艺中结合至未固化或部分固化的橡胶或结合在未固化或部分固化的橡胶之间。
项目6.根据任一前述项目所述的组合物,其中未固化或部分固化的橡胶是天然橡胶、合成橡胶、或天然橡胶和合成橡胶的混合物,任选地其中未固化或部分固化的橡胶是天然橡胶。
项目7.根据任一前述项目所述的组合物,其中增粘树脂选自烃类树脂、萜烯树脂或其组合。
项目8.根据项目7所述的组合物,其中烃类树脂是脂肪族烃类树脂或芳香族烃类树脂,任选地其中烃类树脂是芳香族烃类树脂。
项目9.根据项目7所述的组合物,其中萜烯树脂选自萜烯酚醛树脂、聚萜烯树脂、苯乙烯化萜烯树脂或其组合。
项目10.根据任一前述项目所述的组合物,其中填料包括二氧化硅、钙组分或其组合,任选地其中填料是二氧化硅,并且任选地其中钙组分包括纳米钙、碳酸钙或其组合。
项目11.根据任一前述项目所述的组合物,其中组合物在低于55摄氏度的温度是固体,并且在高于60摄氏度的温度是液体或半固体。
项目12.根据任一前述项目所述的组合物,其中组合物还包含聚醚、橡胶固化剂或两者。
项目13.根据任一前述项目所述的组合物,其中未固化或部分固化的橡胶至少部分地溶于聚醚中。
项目14.根据任一前述项目所述的组合物,其中聚醚选自聚乙二醇或聚丙二醇。
项目15.根据任一前述项目所述的组合物,其中橡胶固化剂包括硫组分或过氧化物或两者。
项目16.根据项目15所述的组合物,其中硫组分选自元素硫或含硫有机化合物。
项目17.根据任一前述项目所述的组合物,其中含硫有机化合物是单硫化物化合物、二硫化物化合物或多硫化物化合物。
项目18.根据任一前述项目所述的组合物,其中橡胶固化剂还包括氧化锌、促进剂或两者。
项目19.根据项目18所述的组合物,其中锌组分包括碳酸锌、氧化锌或其组合。
项目20.根据项目18所述的组合物,其中促进剂选自:N-乙基-N-苯基二硫代氨基甲酸锌盐、2-巯基苯并噻唑、2,2'-二苯并噻唑二硫化物、单硫化四甲基秋兰姆或二硫化四苄基秋兰姆。
项目21.根据任一前述项目所述的组合物,其中组合物的组分的重量百分比如下:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约8重量百分比至12重量百分比的增粘树脂、约20重量百分比至44重量百分比的填料、约1重量百分比至1.4重量百分比的聚醚、约1.4重量百分比至2重量百分比的橡胶固化剂以及0重量百分比至10重量百分比的一种或更多种另外的组分。
项目22.根据任一前述项目所述的组合物,其中组合物还包含脂肪酸,任选地其中脂肪酸是饱和脂肪酸,并且任选地其中饱和脂肪酸是硬脂酸。
项目23.根据任一前述项目所述的组合物,其中组合物还包含抗氧化剂、防雾剂或两者。
项目24.根据项目23所述的组合物,其中抗氧化剂包括苯乙烯酚。
项目25.根据项目24所述的组合物,其中防雾剂是脱水山梨糖醇酯。
项目26.根据任一前述项目所述的组合物,其中组合物的组分的重量百分比如下:约40重量百分比至64重量百分比的未固化或部分固化的橡胶、约1重量百分比至1.4重量百分比的聚醚、约8重量百分比至12重量百分比的增粘树脂、约1.4重量百分比至2重量百分比的橡胶固化剂和任选地以下中的一种或更多种:约20重量百分比至44重量百分比的填料、约2重量百分比至2.6重量百分比的锌组分、约0.6重量百分比至1重量百分比的饱和脂肪酸、约0.1重量百分比至1.4重量百分比的促进剂、约0.1重量百分比至1.4重量百分比的防雾剂和约0.1重量百分比至1重量百分比的抗老化剂。
项目27.一种未固化或部分固化的围条,包括:基础围条和未交联或部分交联的粘合剂的两层结构,其中基础围条包含未固化或部分固化的橡胶,其中未固化或部分固化的围条具有第一侧面和与第一侧面相对的第二侧面,其中未交联或部分交联的粘合剂与未固化或部分固化的围条的第二侧面上的未固化或部分固化的橡胶接触,其中未交联或部分交联的粘合剂包含:根据项目1至26中任一项所述的组合物。
项目27.根据项目26所述的未固化或部分固化的围条,其中未固化或部分固化的围条还包含布置在未固化或部分固化的围条的第一侧面上的隔离材料。
项目28.根据项目27所述的未固化或部分固化的围条,其中隔离材料包含聚合物膜、纺织品或两者。
项目29.根据任一前述项目所述的未固化或部分固化的围条,其中交联的粘合剂层具有约0.1毫米-1.5毫米的厚度。
项目30.根据任一前述项目所述的未固化或部分固化的围条,其中基础围条具有约0.5毫米至5毫米的厚度,任选地其中基础围条具有约5毫米至75毫米的宽度,或任选地其中固化的橡胶围条具有约0.6毫米至6毫米的厚度。
项目31.根据任一前述项目所述的未固化或部分固化的围条,其中基础围条和未交联或部分交联的粘合剂包含至少约7重量百分比的天然橡胶。
项目32.根据任一前述项目所述的未固化或部分固化的围条,其中未交联或部分交联的粘合剂为未固化或部分固化的围条的约5重量百分比至10重量百分比。
项目33.一种鞋类物品,包括:鞋面,其中在鞋面与鞋类的外边缘周边上的固化的橡胶鞋结构之间的接触点处是接合部,其中固化的橡胶围条沿着接合部被布置在鞋面和固化的橡胶鞋结构的至少第一部分上,其中固化的橡胶围条具有基础围条和交联的粘合剂的两层结构,其中基础围条具有第一侧面和与第一侧面相对的第二侧面,其中第一侧是面向外的,其中交联的粘合剂在基础围条的第二侧面上,其中交联的粘合剂邻近鞋面、固化的橡胶鞋结构和接合部,并且其中固化的橡胶围条通过交联的粘合剂被结合至固化的橡胶鞋结构、鞋面或两者,其中交联的粘合剂是根据项目1至26中任一项所述的组合物的固化反应产物。
项目34.根据项目33所述的物品,其中固化的橡胶围条沿着接合部被结合至鞋面和固化的橡胶鞋结构的第一部分,其中第一部分在鞋头区域中,任选地其中第一部分是鞋头、缓冲器或两者。
项目35.根据项目33所述的物品,其中固化的橡胶围条沿着接合部被结合至鞋面和固化的橡胶鞋结构的第一部分和第二部分,其中第一部分在鞋头区域中,并且第二部分在鞋跟区域中,任选地其中第二部分包含鞋跟标志。
项目36.根据项目33所述的物品,其中固化的橡胶围条沿着接合部围绕鞋面和固化的橡胶鞋结构的整个周边结合。
项目37.根据任一前述项目所述的物品,其中基础围条是固化的围条,并且其中固化的围条包含固化的橡胶,任选地其中固化的橡胶是固化的天然橡胶。
项目38.根据任一前述项目所述的物品,还包括以下中的一种或更多种:其中交联的粘合剂层具有约0.1毫米-1.2毫米的厚度,其中基础围条具有约0.5毫米至5毫米的厚度,其中基础围条具有约5毫米至75毫米的宽度,或其中固化的橡胶围条具有约0.6毫米至6毫米的厚度。
项目39.一种制造鞋类物品的方法,包括:
活化根据项目27至32所述的未固化或部分固化的围条;
在鞋面构件和未固化或部分固化的鞋结构之间的接触点处的接合部处,将未固化或部分固化的围条布置在接合部上鞋类的周边的第一部分上,使得未固化或部分固化的围条沿着接合部被布置在鞋面构件的第一部分上和未固化或部分固化的鞋结构的第一部分上,其中包含粘合剂的未固化或部分固化的围条的一部分邻近鞋面构件的第一部分、未固化或部分固化的鞋结构的第一部分、和接合部;以及
固化物品以形成包括固化的橡胶围条和固化的橡胶鞋结构的固化的橡胶鞋,其中固化的橡胶鞋结构和鞋面构件至少部分地通过在围条的固化的橡胶和鞋结构的固化的橡胶之间形成的交联部结合在一起。
项目40.根据项目39所述的方法,其中活化、布置或两者大体上不含变得挥发的有机化合物。
项目41.根据项目40所述的方法,其中有机化合物包括丙酮、甲基乙基酮、乙酸乙酯或其组合。
项目42.根据项目39所述的方法,其中固化包括将物品加热至约100摄氏度至140摄氏度,或任选地约120摄氏度,并且任选地持续约50分钟至120分钟。
项目43.根据任一前述项目所述的方法,其中活化包括将未固化或部分固化的围条加热至约55摄氏度至60摄氏度。
项目44.根据任一前述项目所述的方法,其中鞋面构件的第一部分在未固化或部分固化的围条被布置到的表面上不包括粘合剂或胶合剂,并且其中未固化或部分固化的鞋结构的第一部分在未固化或部分固化的围条被布置到的表面上不包括粘合剂或胶合剂。
项目45.根据任一前述项目所述的方法,其中在将未固化或部分固化的围条布置在鞋面构件的第一部分和未固化或部分固化的鞋结构的第一部分上之前,鞋面构件的第一部分、未固化或部分固化的鞋结构的第一部分、和未固化或部分固化的围条不被涂底漆,任选地其中不对未固化或部分固化的围条涂底漆包括在活化未固化或部分固化的围条期间不使用丙酮、甲基乙基酮、乙酸乙酯或其组合。
项目46.一种鞋类物品,使用根据项目39至45中任一项所述的方法制造。
项目47.一种制造未固化或部分固化的围条的方法,包括:
将未固化或部分固化的粘合剂的层施加至基础围条材料,以形成具有两层结构的未固化或部分固化的围条,其中未固化或部分固化的围条的第一层是包含未固化或部分固化的橡胶的基础围条,并且第二层是根据项目1至26中任一项所述的未交联或部分交联的粘合剂组合物,其中第一层和第二层被布置为彼此相邻。
项目48.根据项目47所述的方法,其中施加包括将未固化或部分固化的粘合剂共挤出到基础围条材料,以形成未固化或部分固化的围条。
项目49.根据项目47所述的方法,其中施加包括将未固化或部分固化的粘合剂层压到基础围条材料,以形成未固化或部分固化的围条。
项目50.根据项目47所述的方法,还包括由基础围条材料形成基础围条,并且其中施加包括将未固化或部分固化的粘合剂喷涂、印刷或浇注到基础围条上。
项目51.根据任一前述项目所述的方法,还包括将组分混合以形成未固化或部分固化的粘合剂,其中组分是根据项目1至26中任一项所述的组合物。
项目52.根据任一前述项目所述的方法,还包括将隔离材料施加至第一层、第二层或两者。
项目53.根据项目52所述的方法,其中隔离材料包含聚合物膜或纺织品或两者。
项目54.根据任一前述项目所述的方法,还包括以下中的一种或更多种:其中第二层具有约0.1毫米-1.2毫米的厚度,其中第一层具有约0.5毫米至5毫米的厚度,其中未固化或部分固化的围条具有约5毫米至75毫米的宽度,或其中未固化或部分固化的围条具有约0.6毫米至6毫米的厚度。
项目55.一种未固化或部分固化的橡胶部件,包括:在未固化或部分固化的橡胶部件的表面上的未交联或部分交联的粘合剂,其中未固化或部分固化的橡胶部件包含未固化或部分固化的橡胶,其中未交联或部分交联的粘合剂与未固化或部分固化的橡胶部件的未固化或部分固化的橡胶接触,其中未交联或部分交联的粘合剂包含:根据项目1至26中任一项所述的组合物。
项目56.根据项目55所述的未固化或部分固化的橡胶部件,其中未固化或部分固化的橡胶部件包括围条、鞋头、缓冲器、鞋跟标志、杯形鞋底、鞋底夹层或鞋外底。
应注意,比、浓度、量和其他数值数据可以在本文中以范围格式表示。应当理解,这样的范围格式为了方便和简洁被使用,并且因此,应当以灵活的方式被解释为不仅包括明确叙述为范围限值的数值,而且包括该范围内涵盖的所有单独的数值或子范围,如同每一个数值和子范围被明确地叙述。为了说明,“约0.1%至约5%”的浓度范围应当被解释为不仅包括明确叙述的约0.1wt%至约5wt%的浓度,而且还包括指示的范围内的单独的浓度(例如,1%、2%、3%和4%)和子范围(例如,0.5%、1.1%、2.2%、3.3%和4.4%)。在方面中,术语“约”可以包括根据数值的有效数字的传统舍入。此外,措辞“约‘x’至‘y’”包括“约‘x’至约‘y’”。
可以对上文描述的方面进行许多变型和修改。所有这样的修改和变型在本文中意图被包括在本公开内容的范围内,并且由所附权利要求保护。
Claims (45)
1.一种未固化或部分固化的围条,其特征在于,所述未固化或部分固化的围条包括:未固化或部分固化的橡胶制成的基础围条和未交联或部分交联的粘合剂的两层结构,其中所述基础围条具有第一侧面和与所述第一侧面相对的第二侧面,其中所述未交联或部分交联的粘合剂与所述基础围条的所述第二侧面上的所述未固化或部分固化的橡胶接触。
2.根据权利要求1所述的未固化或部分固化的围条,其特征在于所述未固化或部分固化的橡胶是天然橡胶或合成橡胶。
3.根据权利要求1所述的未固化或部分固化的围条,其特征在于所述未交联或部分交联的粘合剂包含:(i)未固化或部分固化的橡胶;(ii)增粘树脂;以及(iii)填料。
4.根据权利要求3所述的未固化或部分固化的围条,其特征在于所述增粘树脂选自烃类树脂或萜烯树脂。
5.根据权利要求4所述的未固化或部分固化的围条,其特征在于所述烃类树脂是芳香族烃类树脂。
6.根据权利要求3所述的未固化或部分固化的围条,其特征在于所述填料是二氧化硅。
7.根据权利要求3所述的未固化或部分固化的围条,其特征在于所述粘合剂还包括橡胶固化剂,所述橡胶固化剂包括硫组分,其中所述硫组分选自元素硫或含硫有机化合物。
8.根据权利要求1至7中任一项所述的未固化或部分固化的围条,其特征在于所述未固化或部分固化的围条还包括布置在所述未固化或部分固化的围条的第一侧面上的释放材料。
9.根据权利要求8所述的未固化或部分固化的围条,其特征在于所述释放材料包含聚合物膜或纺织品。
10.根据权利要求1-7和9中任一项所述的未固化或部分固化的围条,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
11.根据权利要求8所述的未固化或部分固化的围条,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
12.根据权利要求1-7和9中任一项所述的未固化或部分固化的围条,其特征在于交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
13.根据权利要求8所述的未固化或部分固化的围条,其特征在于交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
14.根据权利要求1-7、9、11和13中任一项所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
15.根据权利要求8所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
16.根据权利要求10所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
17.根据权利要求12所述的未固化或部分固化的围条,其特征在于所述基础围条具有5毫米至75毫米的宽度。
18.一种鞋类物品,包括:鞋面,其特征在于,在所述鞋面和所述鞋类物品的外边缘周界上的固化的橡胶鞋结构之间的接触点处是接合部,其中固化的橡胶围条沿着所述接合部被布置在所述鞋面和所述固化的橡胶鞋结构的至少第一部分上,其中所述固化的橡胶围条具有基础围条和交联的粘合剂的两层结构,其中所述基础围条具有第一侧面和与所述第一侧面相对的第二侧面,其中第一所述侧面是面向外的,其中所述交联的粘合剂在所述基础围条的第二侧面上,其中所述交联的粘合剂邻近所述鞋面、所述固化的橡胶鞋结构和所述接合部,并且其中所述固化的橡胶围条通过所述交联的粘合剂被结合至所述固化的橡胶鞋结构、所述鞋面或两者。
19.根据权利要求18所述的鞋类物品,其特征在于所述基础围条由天然橡胶、或合成橡胶制成。
20.根据权利要求18所述的鞋类物品,其特征在于所述交联的粘合剂是包含以下的组合物的固化反应产物:(i)未固化或部分固化的橡胶;(ii)增粘树脂;以及(iii)填料。
21.根据权利要求20所述的鞋类物品,其特征在于所述增粘树脂选自烃类树脂或萜烯树脂。
22.根据权利要求21所述的鞋类物品,其特征在于所述烃类树脂是芳香族烃类树脂。
23.根据权利要求20所述的鞋类物品,其特征在于所述填料是二氧化硅。
24.根据权利要求20所述的鞋类物品,其特征在于所述粘合剂还包括橡胶固化剂,所述橡胶固化剂包括硫组分,其中所述硫组分选自元素硫或含硫有机化合物。
25.根据权利要求18至24中任一项所述的鞋类物品,其特征在于所述基础围条具有0.5毫米至5毫米的厚度。
26.根据权利要求18至24中任一项所述的鞋类物品,其特征在于所述交联的粘合剂的层具有0.1毫米至1.5毫米的厚度。
27.根据权利要求18-24中任一项所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
28.根据权利要求25所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
29.根据权利要求26所述的鞋类物品,其特征在于所述基础围条具有5毫米至75毫米的宽度。
30.根据权利要求18-24和28-29中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
31.根据权利要求25所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
32.根据权利要求26所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
33.根据权利要求27所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分,其中所述第一部分在鞋头区域中。
34.根据权利要求30所述的鞋类物品,其特征在于所述第一部分是鞋头、缓冲器或两者。
35.根据权利要求31-33中任一项所述的鞋类物品,其特征在于所述第一部分是鞋头、缓冲器或两者。
36.根据权利要求18-24和28-29中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
37.根据权利要求25所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
38.根据权利要求26所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
39.根据权利要求27所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部被结合至所述鞋面和所述固化的橡胶鞋结构的第一部分和第二部分,其中所述第一部分在鞋头区域中,并且所述第二部分在鞋跟区域中。
40.根据权利要求36所述的鞋类物品,其特征在于所述第二部分包含鞋跟标志。
41.根据权利要求37-39中任一项所述的鞋类物品,其特征在于所述第二部分包含鞋跟标志。
42.根据权利要求18-24和28-29中任一项所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
43.根据权利要求25所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
44.根据权利要求26所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。
45.根据权利要求27所述的鞋类物品,其特征在于所述固化的橡胶围条沿着所述接合部围绕所述鞋面和所述的固化的橡胶鞋结构的整个周界结合。