CN211647121U - Multifunctional floor tile using mineral wool as blank plate - Google Patents
Multifunctional floor tile using mineral wool as blank plate Download PDFInfo
- Publication number
- CN211647121U CN211647121U CN201922107719.6U CN201922107719U CN211647121U CN 211647121 U CN211647121 U CN 211647121U CN 201922107719 U CN201922107719 U CN 201922107719U CN 211647121 U CN211647121 U CN 211647121U
- Authority
- CN
- China
- Prior art keywords
- layer
- glass fiber
- mineral wool
- fiber mat
- floor tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a multifunctional floor tile taking mineral wool as a blank plate, which relates to a floor tile. A multifunctional floor tile using mineral wool as a blank plate is formed by tightly hot-pressing a porcelain surface layer, a polyurethane gluing layer, a first glass felt layer, a mineral wool blank plate layer and a second glass felt layer from top to bottom in sequence. The porcelain surface layer is ceramic tile, marble, granite or white marble; equivalent substitutions can also be made by acrylic sheets, wood sheets, bamboo sheets or decorative papers. The first glass fiber mat layer is provided with a first glass fiber mat layer, and the upper surface and the lower surface of the first glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin. The second glass fiber mat layer is provided with a second glass fiber mat layer, and the upper surface and the lower surface of the second glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin. The thickness of the mineral wool embryo board layer is 20mm plus or minus 10mm, further 20mm plus or minus 5mm, and further 20 mm.
Description
Technical Field
The utility model relates to a multifunctional floor tile taking mineral wool as a blank plate, which relates to a floor tile.
Background
In modern home decoration, the floor tiles are widely applied as a decoration material, the existing floor tiles are solid floor tiles, and the floor tiles have single function, are only simply paved on the ground and have no functions of heat preservation and sound insulation; modern buildings are developed towards the direction of energy conservation and environmental protection, the floor tiles used indoors are inevitably required to have the functions, and meanwhile, materials, labor, construction period and construction procedures are required to be saved as far as possible, so that a new floor tile is required to be designed to meet the actual use requirement.
SUMMERY OF THE UTILITY MODEL
The utility model provides a use mineral wool as multi-functional ceramic tile of base board in view of this, it has good heat preservation and sound insulation performance, is the good ornamental material of modern house, has very high use and spreading value.
A multifunctional floor tile using mineral wool as a blank plate is formed by tightly hot-pressing a porcelain surface layer, a polyurethane gluing layer, a first glass felt layer, a mineral wool blank plate layer and a second glass felt layer from top to bottom in sequence.
The porcelain surface layer is ceramic tile, marble, granite or white marble; equivalent substitutions can also be made by acrylic sheets, wood sheets, bamboo sheets or decorative papers.
The first glass fiber mat layer is provided with a first glass fiber mat layer, and the upper surface and the lower surface of the first glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
The second glass fiber mat layer is provided with a second glass fiber mat layer, and the upper surface and the lower surface of the second glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
The thickness of the mineral wool embryo board layer is 20mm plus or minus 10mm, further 20mm plus or minus 5mm, and further 20 mm.
The utility model relates to a method for manufacturing multifunctional floor tiles by using mineral wool as blank boards, which comprises the following steps:
(1) uniformly coating glass fiber reinforced plastic resin or melamine resin on the lower surface of the first glass felt layer and the upper surface of the second glass felt layer by taking the mineral wool embryonic ply as a basic layer, and simultaneously attaching the first glass felt layer and the second glass felt layer along the upper surface and the lower surface of the mineral wool embryonic ply;
(2) feeding the plate formed by the first glass felt layer, the mineral wool blank plate layer and the second glass felt layer in a hot press for hot pressing;
the hot pressing time is 5-8min, the hot pressing temperature is 130-;
(3) shearing and trimming the hot-pressed plate;
(4) uniformly coating a polyurethane cementing layer on the upper surface of the first glass felt layer;
(5) tightly attaching the lower surface of the porcelain surface layer to the polyurethane cementing layer, and performing static pressure at normal temperature by using a hydraulic machine;
(6) further edging the plate with the static pressure to remove the overflowing polyurethane glue in the static pressure removing process;
(7) and packaging and stacking the ground tile finished product after edge grinding.
The time for static pressing in the step (5) is not less than 18 hours, preferably 24 hours; the pressure intensity of the static pressure is 10-12kg/c square meter, namely 1.0-1.2 MPa.
And (4) grinding the edges in the step (6) by using a grinding machine which is a belt sander.
The utility model discloses think about ingenious, simple structure, and have good heat preservation and sound insulation performance, it has effectively solved the current difficult problem of pouring formula floor heat preservation, sound insulation and this the scaling up of floor ground fracture has been of a specified duration. The utility model discloses a mineral wool utilizes metallurgical blast furnace hot slag to make for the essential material, the heat energy of make full use of hot slag realizes that the low carbon makes and solid useless material resource cyclic utilization can also practice thrift a large amount of mineral resources, if can realize that extensive application volume production will support the low carbon that the country advocated and make, energy saving and emission reduction, cyclic utilization, green development, it is exactly the theory of gold mountain silver mountain to stick up and go on green water mountain completely, form the space pattern of resources saving and environmental protection with actual action, optimize the industrial structure, adjust the production mode, still naturally with new life style is quiet, harmonious, beautiful. Creates a good living environment for people for building beautiful China and makes a contribution to global ecological safety. The product has outstanding social and economic benefits and great and profound influence.
The present invention will be further explained with reference to the accompanying drawings.
Drawings
Fig. 1 is a schematic sectional view of a multifunctional floor tile using mineral wool as a blank according to the present invention.
Detailed Description
Referring to the attached figure 1, the multifunctional floor tile taking mineral wool as a blank plate is formed by tightly hot-pressing a porcelain surface layer 1, a polyurethane cementing layer 2, a glass felt layer I3, a mineral wool blank plate layer 4 and a glass felt layer II 5 from top to bottom in sequence.
The porcelain surface layer 1 is ceramic tile, marble, granite or white marble; equivalent substitutions can also be made by acrylic sheets, wood sheets, bamboo sheets or decorative papers.
The first glass fiber mat layer 3 is provided with a first glass fiber mat layer, and the upper surface and the lower surface of the first glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
The second glass fiber mat layer 5 is provided with a second glass fiber mat layer, and the upper surface and the lower surface of the second glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
The thickness of the mineral wool embryo board layer 4 is 20mm plus or minus 10mm, further 20mm plus or minus 5mm, and further 20 mm.
The utility model relates to a method for manufacturing multifunctional floor tiles by using mineral wool as blank boards, which comprises the following steps:
(1) uniformly coating glass fiber reinforced plastic resin or melamine resin on the lower surface of the first glass felt layer 3 and the upper surface of the second glass felt layer 5 by taking the mineral wool embryo board layer 4 as a basic layer, and simultaneously attaching the first glass felt layer 3 and the second glass felt layer 5 along the upper surface and the lower surface of the mineral wool embryo board layer 4;
(2) feeding the plate formed by laminating the first glass felt layer 3, the mineral wool blank plate layer 4 and the second glass felt layer 5 into a hot press for hot pressing;
the hot pressing time is 5-8min, the hot pressing temperature is 130-;
(3) shearing and trimming the hot-pressed plate;
(4) uniformly coating a polyurethane cementing layer on the upper surface of the first glass felt layer 3;
(5) tightly attaching the lower surface of the porcelain surface layer 1 to the polyurethane cementing layer, and performing static pressure at normal temperature by using a hydraulic machine;
(6) further edging the plate with the static pressure to remove the overflowing polyurethane glue in the static pressure removing process;
(7) and packaging and stacking the ground tile finished product after edge grinding.
The time for static pressing in the step (5) is not less than 18 hours, preferably 24 hours; the pressure intensity of the static pressure is 10-12kg/c square meter, namely 1.0-1.2 MPa.
And (4) grinding the edges in the step (6) by using a grinding machine which is a belt sander.
Claims (6)
1. The utility model provides an use multi-functional ceramic tile of mineral wool as base board which characterized in that: the ceramic tile is formed by tightly hot-pressing a ceramic surface layer, a polyurethane cementing layer, a first glass felt layer, a mineral wool blank plate layer and a second glass felt layer from top to bottom in sequence.
2. The multifunctional floor tile using mineral wool as blank according to claim 1, wherein: the porcelain surface layer is ceramic tile, marble, granite or white marble.
3. The multifunctional floor tile using mineral wool as blank according to claim 1, wherein: the first glass fiber mat layer is provided with a first glass fiber mat layer, and the upper surface and the lower surface of the first glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
4. The multifunctional floor tile using mineral wool as blank according to claim 1, wherein: the second glass fiber mat layer is provided with a second glass fiber mat layer, and the upper surface and the lower surface of the second glass fiber mat layer are coated with glass fiber reinforced plastic resin or melamine resin.
5. The multifunctional floor tile using mineral wool as blank according to claim 1, wherein: the thickness of the mineral wool embryonic plate layer is 20 +/-10 mm.
6. The multifunctional floor tile using mineral wool as blank according to claim 1, wherein: the thickness of the mineral wool embryonic plate layer is 20 mm.