CN209194921U - A kind of high intensity solid wooden compound floor - Google Patents
A kind of high intensity solid wooden compound floor Download PDFInfo
- Publication number
- CN209194921U CN209194921U CN201821222293.8U CN201821222293U CN209194921U CN 209194921 U CN209194921 U CN 209194921U CN 201821222293 U CN201821222293 U CN 201821222293U CN 209194921 U CN209194921 U CN 209194921U
- Authority
- CN
- China
- Prior art keywords
- substrate
- solid wooden
- panel
- wooden compound
- veneer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of high-intensitive solid wooden compound floors, including panel, substrate and bottom plate, panel is pasted onto the surface of substrate, and base plate sticking is made in the bottom surface of substrate, substrate of rubber veneer according to the number of plies of odd-level, every layer of criss-cross mode gluing hot pressing.Rubber veneer is the veneer handled by boiling ungrease treatment and preservative, and panel and bottom plate pass through high-pressure impregnation respectively and have modified adhesive, and hot-forming with substrate respectively.The utility model floor have anti-corrosive properties are good, toughness is strong, tongue and groove appearance preferably, mat formation after without characteristics such as sound, surface layer intensity height, lower production costs, can meet the needs of consumer is to high-intensitive solid wooden compound floor well.
Description
Technical field
The utility model relates to arrive technical field of floor, specifically a kind of high-intensitive solid wooden compound floor.
Background technique
Solid wooden compound floor has become a kind of main material of current home decoration.Existing solid wooden compound floor is used
Substrate generally be mostly Eucalyptus multi-layer substrate.Since the material of Eucalyptus is relatively rough, influence whether that finished product floor is especially its tenon
The appearance of groove face.Meanwhile the prices of raw materials of Eucalyptus are higher (currently about 1800~2000 yuan/cubic metre or so), lead
Causing floor, the cost is relatively high.In addition, the mechanical property effect of the surface layer fabric of existing most of solid wooden compound floors is poor, hold
Easily cause cracking, rot, decoration quality is caused to decline.
Summary of the invention
The technical problem to be solved by the utility model is to propose that a kind of anti-corrosive properties are good, toughness is strong, tongue and groove appearance effect
Fruit preferably, the high-intensitive solid wooden compound floors of lower production costs.
In order to solve the above technical problems, a kind of high-intensitive solid wooden compound floor of the utility model includes panel, substrate and bottom
Plate, the panel are pasted onto the surface of the substrate, and the base plate sticking is in the bottom surface of the substrate, and the substrate is by rubber wood timber
Veneer composition, the rubber veneer are the veneers handled by boiling ungrease treatment and preservative.
A kind of above-mentioned high-intensitive solid wooden compound floor, the panel and bottom plate pass through high-pressure impregnation respectively and have modified gluing
Agent, and it is hot-forming with the substrate respectively.
A kind of above-mentioned high-intensitive solid wooden compound floor, the rubber veneer with a thickness of 0.9~2.2mm.
A kind of above-mentioned high-intensitive solid wooden compound floor, the substrate with a thickness of 5.0~15.0mm, by the rubber wood timber list
Plate is made according to the number of plies of odd-level, every layer of criss-cross mode gluing hot pressing.
A kind of above-mentioned high-intensitive solid wooden compound floor, the panel with a thickness of 0.6~3.0mm, the thickness of the bottom plate
For 0.9~2.2mm.
China is rubber production big country, and rubber wood timber is widely cultivated in provinces such as Hainan, Guangdong, Yunnan, Guangxi, is local
A kind of Important Economic crop, thus, as the by-produced material of natural rubber, every annual meeting generates a large amount of rubber wood timber timber, rubber
The wooden raw material are very more.The utility model by adopting the above-described technical solution, it with rubber wood timber sheet making substrate, it is not only former
Material is easy to get, and price also 300~500 yuan/cubic metre lower than Eucalyptus, significantly reduces the production cost on floor.Meanwhile
Due to rubber wood timber material much than Eucalyptus exquisiteness, manufactured floor be especially after tongue and groove mortise its tongue and groove appearance effect
Fruit is more preferable, and greatly improves because of sound problem after mating formation brought by coarse tongue-and-groove.Panel and bottom plate pass through high-pressure impregnation
Modified adhesive, is then affixed on that reheating on rubber wood timber substrate is molded, and not only intensity is high, but also toughness and antiseptic property are good, energy
Meets the needs of consumer is to high-intensitive solid wooden compound floor well.
Detailed description of the invention
Fig. 1 is the layer structure schematic diagram on the utility model floor.
Specific embodiment
As shown in Figure 1, the utility model high intensity solid wooden compound floor includes panel 1, substrate 2 and bottom plate 3, panel 1 is viscous
It is attached to the surface of substrate 2, bottom plate 3 is pasted onto the bottom surface of substrate 2.Panel 1 can use the common panels such as oak, birch, maple,
Bottom plate 3 can use Eucalyptus veneer.Panel 1 and bottom plate 3 have a modified adhesive by high-pressure impregnation respectively, hardness reach 8H and
More than, it is hot-forming with substrate 2 respectively.Panel 1 with a thickness of 0.6~3.0mm, bottom plate 3 with a thickness of 0.9~2.2mm.Substrate
2 are made of rubber veneer according to the number of plies of odd-level, every layer of criss-cross mode gluing hot pressing, and preferably 5 layers, 7 layers of the number of plies
Structure, be made rear substrate 2 with a thickness of 5.0~15.0mm.Rubber veneer is handled by boiling ungrease treatment and preservative
Veneer, with a thickness of 0.9~2.2mm.When boiling, rubber veneer can be placed in boiling case, mass content, which is added, is
0.8~1.5% NaOH solution makes it have efficient anti-boiling 24 hours under conditions of pressure 2MPa, 120 DEG C of temperature
Worm, Anticorrosive Character.The molten alkylamine copper solution (ACQ) of the ammonia that rubber veneer available quality content is 0.3~0.8% carries out anti-corrosion
Agent processing, impregnates 24 hours.Panel 1, bottom plate 3 carry out six using modified adhesive impregnation under 1.5~3.0Mpa high pressure
A impregnation cycles, each impregnation cycles include: to be evacuated to negative pressure 0.5Mpa, inject maceration extract, are forced into 1.5~3.0Mpa,
It is kept for 2 hours, maceration extract is discharged.
Claims (4)
1. a kind of high intensity solid wooden compound floor, including panel, substrate and bottom plate, the panel are pasted onto the table of the substrate
Face, the base plate sticking is in the bottom surface of the substrate, which is characterized in that the substrate is made of rubber veneer, the rubber
Veneer is the veneer handled by boiling ungrease treatment and preservative；The panel and bottom plate, which pass through high-pressure impregnation respectively and have, to be changed
Property adhesive, and it is hot-forming with the substrate respectively.
2. a kind of high-intensitive solid wooden compound floor as described in claim 1, which is characterized in that the thickness of the rubber veneer
For 0.9~2.2mm.
3. a kind of high-intensitive solid wooden compound floor as claimed in claim 1 or 2, which is characterized in that the substrate with a thickness of
5.0~15.0mm is made of the rubber veneer according to the number of plies of odd-level, every layer of criss-cross mode gluing hot pressing.
4. a kind of high-intensitive solid wooden compound floor as claimed in claim 1 or 2, which is characterized in that the panel with a thickness of
0.6~3.0mm, the bottom plate with a thickness of 0.9~2.2mm.