CN208392814U - A kind of high barrier low transparency moisture proof PET composite membrane - Google Patents
A kind of high barrier low transparency moisture proof PET composite membrane Download PDFInfo
- Publication number
- CN208392814U CN208392814U CN201820487750.XU CN201820487750U CN208392814U CN 208392814 U CN208392814 U CN 208392814U CN 201820487750 U CN201820487750 U CN 201820487750U CN 208392814 U CN208392814 U CN 208392814U
- Authority
- CN
- China
- Prior art keywords
- layer
- polyacrylamide amine
- thickness
- pet
- moisture proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of high barrier low transparency moisture proof PET composite membranes, including the upper layer PET base copolyester, the compound barrier layer of water oxygen and lower layer's PET base copolyester set gradually;The upper surface of the upper layer PET base copolyester is provided with the first polyacrylamide amine layer, and the upper surface of the first polyacrylamide amine layer is provided with polyvinyl chloride layer, and nano fluoropolymer particle layer is arranged in the upper surface of the polyvinyl chloride layer;The lower surface of the lower layer PET base copolyester is provided with the second polyacrylamide amine layer;And the lower surface of the second polyacrylamide amine layer is provided with nano fluoropolymer particle layer.In the compound barrier layer of the water oxygen of the application, provided with evoh layer, since above-mentioned polymer is to combine the barrier action of polyvinyl processability and vinyl alcohol polymer, so that ethylene-vinyl alcohol copolymer not only shows fabulous processing performance, but also excellent blocking effect is showed to gas, smell, fragrance, solvent etc..
Description
Technical field
The utility model relates to a kind of high barrier low transparency moisture proof PET composite membranes.
Background technique
PET film also known as high temperature resistance polyester film.It has excellent physical property, chemical property and dimensional stability, thoroughly
Bright property, recuperability, can be widely used in magnetic recording, photosensitive material, electronics, electric insulation, industrial film, package decoration,
The fields such as screen protection, the protection of optical grade specular surface.
Currently, the curtain or shower curtain of usually household can be all made of opaque or low light transmission material, in order to reach
To the effect for avoiding privacy from leaking, general way is exactly to coat a coating on a plastic film, but this coating is in high temperature
Under be easy to fall off, and smell is larger, causes screening effect bad, poor user experience.In addition, due to the use of curtain or shower curtain
It can be often subject to the corrosion of rainwater etc., so after long-time use, be easy mouldy, reduce its service life.
In addition, PET film used in also requiring has the moisture-proof equal barrier properties of higher choke, with extend PET film with
And its service life and shelf-life of the electronic product of protection.
Utility model content
The utility model aim is to provide a kind of high barrier low transparency moisture proof in view of the defects existing in the prior art
PET composite membrane.
The utility model to achieve the above object, adopts the following technical scheme that a kind of high barrier low transparency moisture proof
PET composite membrane, including the upper layer PET base copolyester, the compound barrier layer of water oxygen and lower layer's PET base copolyester set gradually;It is described
The upper surface of upper layer PET base copolyester is provided with the first polyacrylamide amine layer, and the upper surface of the first polyacrylamide amine layer
It is provided with polyvinyl chloride layer, nano fluoropolymer particle layer is arranged in the upper surface of the polyvinyl chloride layer;The lower layer PET polyester
The lower surface of base is provided with the second polyacrylamide amine layer;And the lower surface of the second polyacrylamide amine layer is provided with a nanometer fluorine
Polymer beads sublayer;Wherein, the compound barrier layer of the water oxygen includes the boron nitride nanometer layer that top upper layer is arranged in, and is arranged in
Between upper layer evoh layer, the water-soluble polymer layer in intermediate middle layer is set, the poly- of immediate underlying layer is set
Vinylamine-polyvinyl alcohol copolymer layer, and the graphene nano layer of lower part lower layer is set;Wherein, the boron nitride nanometer
Layer with a thickness of 100-180nm, the evoh layer with a thickness of 50-70nm, the water-soluble polymer layer
With a thickness of 50-80nm, the polyvinylamine-polyvinyl alcohol copolymer layer is with a thickness of 40-60nm, the graphene nano layer
With a thickness of 150-180nm.
Wherein, the first polyacrylamide amine layer with a thickness of 2-4um, the second polyacrylamide amine layer with a thickness of 1-
3um。
Wherein, in the nano fluoropolymer particle layer partial size of particle between 20-30nm.
The utility model has the beneficial effects that being provided with ethylene-vinyl alcohol copolymer in the compound barrier layer of the water oxygen of the application
Layer and polyvinylamine-polyvinyl alcohol copolymer layer, since above-mentioned polymer is to gather polyvinyl processability and vinyl alcohol
The barrier action for closing object combines, so that ethylene-vinyl alcohol copolymer not only shows fabulous processing performance, but also to gas
Body, smell, fragrance, solvent etc. show excellent blocking effect;Due to being equipped with polychlorostyrene in the upper surface of upper layer PET base copolyester
Pvdf layer so that PET film upper surface has the characteristics that higher heat resistance, flexibility and anti-aging, and can reach very low
Light transmittance so that light will not penetrate PET film substantially, the curtain or shower curtain of PET film production can with this configuration in this way
To accomplish the effect of masking very well.
In addition, due to being provided with the first polyacrylamide amine layer and the second polyacrylamide amine layer in the utility model, so that PET
Film integrally effectively blocking oxygen, vapor can penetrate PET film, and in the upper surface of polyvinyl chloride layer and the second polyacrylamide
The lower surface of layer is respectively arranged with nano fluoropolymer particle layer, can further prevent PET film by humid air, moisture etc.
Corrosion, the service life of PET film can be greatly prolonged.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the utility model;
Fig. 2 is the compound barrier schematic diagram of a layer structure of water oxygen of the utility model.
Specific embodiment
Shown in Fig. 1, it is related to a kind of high barrier low transparency moisture proof PET composite membrane, including the upper layer PET set gradually
The compound barrier layer 2 of base copolyester 1, water oxygen and lower layer's PET base copolyester 3;Above-mentioned trilaminate material is using co-extrusion technology through two-way drawing
It stretches obtained.
PET film length is damp and mouldy in order to prevent, when design, can be provided in the upper surface of the upper layer PET base copolyester 1
First polyacrylamide amine layer 11, and the upper surface of the first polyacrylamide amine layer 11 is provided with polyvinyl chloride layer 110, it is described poly-
Nano fluoropolymer particle layer 111 is arranged in the upper surface of pvdc layer 110;The lower surface of the lower layer PET base copolyester 3 is arranged
There is the second polyacrylamide amine layer 31, and the lower surface of the second polyacrylamide amine layer 31 is provided with nano fluoropolymer particle layer
111。
Due to being provided with the first polyacrylamide amine layer and the second polyacrylamide amine layer, so that PET film integrally can be obstructed effectively
Oxygen, vapor penetrate PET film, and set respectively in the lower surface of the upper surface of polyvinyl chloride layer and the second polyacrylamide amine layer
It is equipped with nano fluoropolymer particle layer, can further prevent PET film by the corrosion of humid air, moisture etc., it can be significantly
Extend the service life of PET film.
In Fig. 2, the compound barrier layer 2 of water oxygen includes the boron nitride nanometer layer 21 that top upper layer is arranged in, and is arranged in
Between upper layer evoh layer 22, the water-soluble polymer layer 23 in intermediate middle layer is set, is arranged in immediate underlying layer
Polyvinylamine-polyvinyl alcohol copolymer layer 24, and the graphene nano layer 25 of lower part lower layer is set;Wherein, the nitrogen
Change boron nanometer layer with a thickness of 100-180nm, the evoh layer with a thickness of 50-70nm, the water solubility
Polymeric layer with a thickness of 50-80nm, the polyvinylamine-polyvinyl alcohol copolymer layer is with a thickness of 40-60nm, the graphite
Alkene nanometer layer with a thickness of 150-180nm.
In the barrier layer of the application, advised using the impermeability and its conjunction of graphene nano layer and boron nitride nanometer layer
Nanoscale has the barrier property high to gas and excellent mechanical performance, can dramatically ground to PET laminated film obtained
The barrier property for improving composite membrane, substantially increases the shelf-life of electronic product.
Another key technology is, in the compound barrier layer 2 of the water oxygen of the application, is provided with ethylene-vinyl alcohol copolymer
Layer and polyvinylamine-polyvinyl alcohol copolymer layer, since above-mentioned polymer is to gather polyvinyl processability and vinyl alcohol
The barrier action for closing object combines, so that ethylene-vinyl alcohol copolymer not only shows fabulous processing performance, but also to gas
Body, smell, fragrance, solvent etc. show excellent blocking effect.Also, in known available polymer, polyvinyl alcohol
(PVOH) gas permeability is minimum.Currently, ethylene-vinyl alcohol copolymer (EVOH) copolymer is in current prior art is
It produces in this way: being ethylene and vinyl acetate copolymerization first, followed by hydrolyze the copolymer and obtain ethylene-vinyl alcohol.Therefore, still
The barrier action of height is so remained, and is had clear improvement in terms of moisture-proof and processing performance.
For in nature, EVOH copolymer is highly crystalline body, its property depends primarily on the phase of its comonomer
To concentration.In general, when ethylene contents increase, gas barrier property decline, humidity resistance is improved, and resin is easier to add
Work.
Wherein, in order to reach optimal effect, the first polyacrylamide amine layer 11 with a thickness of 2-4um, described second
Polyacrylamide amine layer 31 with a thickness of 1-3um.
Wherein, in order to reach optimal effect, the partial size of particle is in 20- in the nano fluoropolymer particle layer 111
Between 30nm.
The above is only the preferred embodiment of the present invention, is not intended to limit the utility model, all practical at this
Within novel spirit and principle, any modification, equivalent replacement, improvement and so on should be included in the guarantor of the utility model
Within the scope of shield.
Claims (3)
1. a kind of high barrier low transparency moisture proof PET composite membrane, including upper layer PET base copolyester (1), the water set gradually
The compound barrier layer of oxygen (2) and lower layer's PET base copolyester (3);It is characterized by: the upper surface of the upper layer PET base copolyester (1)
It is provided with the first polyacrylamide amine layer (11), and the upper surface of the first polyacrylamide amine layer (11) is provided with polyvinyl chloride layer
(110), nano fluoropolymer particle layer (111) are arranged in the upper surface of the polyvinyl chloride layer (110);The lower layer PET polyester
The lower surface of base (3) is provided with the second polyacrylamide amine layer (31);And the lower surface of the second polyacrylamide amine layer (31)
It is provided with nano fluoropolymer particle layer (111);
Wherein, the compound barrier layer of the water oxygen (2) includes the boron nitride nanometer layer that top upper layer is arranged in, and is arranged on intermediate upper layer
Evoh layer, the water-soluble polymer layer in intermediate middle layer is set, the polyethylene of immediate underlying layer is set
Amine-polyvinyl alcohol copolymer layer, and the graphene nano layer of lower part lower layer is set;Wherein, the boron nitride nanometer layer
With a thickness of 100-180nm, the evoh layer with a thickness of 50-70nm, the thickness of the water-soluble polymer layer
Degree is 50-80nm, and the polyvinylamine-polyvinyl alcohol copolymer layer is with a thickness of 40-60nm, the thickness of the graphene nano layer
Degree is 150-180nm.
2. a kind of high barrier low transparency moisture proof PET composite membrane as described in claim 1, it is characterised in that: described the
One polyacrylamide amine layer (11) with a thickness of 2-4um, the second polyacrylamide amine layer (31) with a thickness of 1-3um.
3. a kind of high barrier low transparency moisture proof PET composite membrane as described in claim 1, it is characterised in that: described to receive
The partial size of particle is between 20-30nm in rice fluoropolymer particles layer.