CN208148863U - Radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional - Google Patents
Radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional Download PDFInfo
- Publication number
- CN208148863U CN208148863U CN201820531958.7U CN201820531958U CN208148863U CN 208148863 U CN208148863 U CN 208148863U CN 201820531958 U CN201820531958 U CN 201820531958U CN 208148863 U CN208148863 U CN 208148863U
- Authority
- CN
- China
- Prior art keywords
- layer
- radium
- protective layer
- mucigel
- shine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses press radium-shine heat transfer film after a kind of novel high-performance solid; including the PET film layer as thermal transfer carrier; and it is successively overlying on release layer on PET film layer, preceding protective layer, rear protective layer, printing layer, three-dimensional laser protective layer, aluminium coated, presses radium-shine flower-pattern layer, mucigel afterwards; protective layer is metal oxide, metal halide or nonmetal oxide after described, and the mucigel is the structure of the double-deck viscose.The utility model transfer film combines bright gold, silver lustre or single golden effect and radium-shine effect of decorative patterns, it is bright-colored, three-dimensional sense is strong, level is abundant, surface is smooth, adhesive force is strong, wear-resisting property is good, easy to operate, high-efficient pollution-free, be worth with high promotion and application.
Description
Technical field
The utility model presses radium-shine thermal transfer after belonging to packages printing field more particularly to a kind of novel high-performance solid
Film.
Background technique
Transprint material is the medium of caloric transfer printing technology, and caloric transfer printing technology is incited somebody to action by transprint material one-time heating
Decorative pattern in thermal transfer is needed on and on Dicoration base material surface, is formed high-quality facing film.It is compared to common printed pattern
Method, advantage are to be suitable for substrate surface shape as complex changeable curved surface.Thermal transfer technology due to it efficiently, it is convenient and
Printing quality is good, is widely used in the fields such as stationery, toy, bamboo and wood, hardware, glass, metal, daily necessities, cosmetics.Thermal transfer
Material includes heat transfer colour ribbon and heat transfer film, wherein heat transfer film is needed in view of post-production, and technical requirements compare thermal transfer
Colour band is higher.During the manufacturing of heat transfer film, organic solvent is inevitably used, the quality of current country's heat transfer film is not
One and foot, the pollution and damage in production are inevitable.Radium-shine thermal transfer technology is that laser effect is added on the basis of thermal transfer
Thermal transfer technology, due to conspicuous appearance, preferable commercial propaganda effect and be used widely.
Currently, radium-shine heat transfer film and its technique face following problem：
It is existing there are silver lustre, bright gold thermal transfer film, i.e. aluminium coated embodies a kind of structure；And single compact heat
Turn printed film, the i.e. monochromatic decorative pattern of foreign capitals import, both this cannot be combined into a kind of new assembly.
The utility model combines above the two, embodies a variety of above different patterns, different shape with a kind of combination
Novel laser thermal transfer film.
Utility model content
Purpose of utility model：The utility model proposes a kind of novel high-performance it is three-dimensional after press radium-shine heat transfer film, silver lustre,
Bright gold thermal transfer film and single radium-shine thermal transfer film combine, to solve problems of the prior art.
Utility model content：Radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, including as thermal transfer carrier
PET film layer, and successively it is overlying on release layer, preceding protective layer, rear protective layer, printing layer, three-dimensional laser on PET film layer
Protective layer, aluminium coated press radium-shine flower-pattern layer, mucigel afterwards, and the rear protective layer is metal oxide, metal halide or non-
Metal oxide, the mucigel are the structure of the double-deck viscose.
Preferably, the thickness of the release layer, preceding protective layer, rear protective layer, three-dimensional laser protective layer, aluminium coated is distinguished
For 20 ~ 200 μm, 5-50 μm, 5-50 μm, 10-100 μm.The thickness of each layer makes economy and performance reach unified.
Preferably, the release layer includes one of silicon mould release, fluorine element mould release.Silicon mould release, fluorine element are release
Agent keeps release peeling force suitable, and low temperature is easily bonded, and high temperature is easily peelable.
Preferably, the mucigel includes the first mucigel, the second viscose successively covered from the rear radium-shine flower-pattern layer of pressure
Layer, and the adhesion of first mucigel is greater than the adhesion of the second mucigel.The adhesion of first mucigel is greater than second
The adhesion of mucigel can make transfer film integral adhesive secured, and can obtain very high stability after being overlying on material.
Further, second mucigel is one of epoxide-resin glue, PP glue, ABS glue.It is general to glue, it is used for
It is directly bonded material, and the first mucigel is stronger.
Compared to the prior art, the beneficial effects of the utility model are：The utility model layer of structure is distinct, and product is suitable
Strong with property, laser effect extremely dazzles fineness, durable.Release layer has peeling force appropriate, adapts under being bonded and heating under low temperature
The excellent results of removing；Preceding protective layer, rear protective layer have carried out reinforcement and weather-proof guarantor to the machinery and optics of entire transfer film layer
Shield；Three-dimensional laser protective layer shows silver lustre, bright gold or single golden effect early period, embodies radium-shine effect by post-production
Fruit, it is consistent in the effect that different angle is presented；Two layers of mucigel forms the viscose peeling force having levels to material and membrane structure,
Product and material is firmly combined；The succinct high efficient and reliable of the operation of radium-shine embossing machine and silica gel wheel.The utility model transfer film knot
Closed bright gold, silver lustre or single golden effect and radium-shine effect of decorative patterns, it is bright-colored, three-dimensional sense is strong, level is abundant, surface is smooth,
Adhesive force is strong, wear-resisting property is good, easy to operate, high-efficient pollution-free, is worth with high promotion and application.
Detailed description of the invention
Fig. 1 is the general structure schematic diagram of the utility model.
In figure：1-PET film layer 1,2- release layer, protective layer before 3-, protective layer after 4-, 5- printing layer, 6- three-dimensional laser
Protective layer, 7- aluminium coated press radium-shine flower-pattern layer, 9- mucigel, the first mucigel of 91-, the second mucigel of 92- after 8-.
Specific embodiment
In order to illustrate the technical solutions in the embodiments of the present application or in the prior art more clearly, letter will be made to embodiment below
Single introduction.
Embodiment 1
Such as Fig. 1, radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, including the PET film as thermal transfer carrier
Layer 1, and successively it is overlying on release layer 2, preceding protective layer 3, rear protective layer 4, printing layer 5, three-dimensional laser on PET film layer 1
Protective layer 6, aluminium coated 7 press radium-shine flower-pattern layer 8, mucigel 9 afterwards, and the rear protective layer 4 is metal oxide, metal halide
Or nonmetal oxide, the mucigel 9 are the structure of the double-deck viscose；
Wherein, the thickness point of the release layer 2, preceding protective layer 3, rear protective layer 4, three-dimensional laser protective layer 6, aluminium coated 7
It Wei not 20 ~ 200 μm, 5-50 μm, 5-50 μm, 10-100 μm；
The release layer 2 includes one of silicon mould release, fluorine element mould release, and the release effect that release layer 2 is formed
The following conditions should be met, at 100 DEG C or less, release layer 2 and PET film layer adhesive force are splendid, reach 100 in ambient temperature
DEG C or more when can be significantly reduced with PET original film adhere to, to be easily peeled off；The material of protective layer 4 is respectively selected from after described
SiO、SiO2、Si2O3、MgF2、CaF2、Y2O3、GeO2、Ta2O5、Al2O3、Nd2O3、ZnO、TiO2、PbO、ThO2、Sc2O3、ZrO、
ZrO2One of；
The mucigel 9 includes the first mucigel 91, the second mucigel 92 successively covered from the rear radium-shine flower-pattern layer 8 of pressure,
And the adhesion of first mucigel 91 is greater than the adhesion of the second mucigel 92；First mucigel 91 is polyurethanes
Compound viscose, it includes the components of following parts by weight：
35 parts of polyurethane resin
Acrylic resin modified 10 parts
5 parts of epoxy resin
3 parts of ethylene-vinyl acetate resin
2 parts of cellulose acetate resin
0.5 part of curing agent
100 parts of organic solvent；
Second mucigel 92 is one of epoxide-resin glue, PP glue, ABS glue；
The production technology that radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, includes the following steps：
（1）, choose clean PET film layer, sprawl；With ceramic wafer be coated with release layer, the release layer be self-crosslinking,
In the composition containing 3 kinds or more acrylic resin monomers of semifluid shape, it is coated with 70 line of line number；Halftone cable is 150-220 line,
Wherein " line " is unit-line number/inch, indicates the per inch line number of halftone, 1 line=2.5 mesh；The wet coating amount of release layer is
6.0g/m2, dry-coated amount is 1.2g/m2；
（2）, in release layer surface form the fine and close structure sheaf of crosslinking using host agent and curing agent, as preceding protective layer；
（3）, using be evaporated in vacuo or sputter deposition craft, preceding protective layer coating after protective layer；
（4）, printed using the ink of organic solvent-resistant in rear protective layer, it is 80 that four primaries ink, which prints line number,
Line, it is 60 lines that chalk, which prints line number, forms printing layer；Again toward coating three-dimensional laser protective layer in printing layer, it is extra then to clean
Ink air-dries and stands 2h or more, and silver lustre, bright gold or single golden effect is presented in three-dimensional laser protective layer at this time；
（5）, will（4）In semi-finished product be put into baking oven and continuously solidify, 55 DEG C of solidification temperature, time 16h；
（6）, aluminized on three-dimensional laser protective layer using vacuum aluminium plating process, aluminium is washed after aluminizing, is stood；
（7）, on radium-shine embossing machine by radium-shine pressure roller decorative pattern all overstock be transferred on product, ultimately form radium-shine
Decorative pattern, namely after press radium-shine flower-pattern layer to be formed；The temperature of radium-shine embossing machine is 1150 DEG C, pressure 11kg, speed 59m/
min；
（8）, successively coat in the radium-shine decorative pattern layer surface of rear pressure or with the first mucigel of type, the second mucigel, every layer is applied
Tree lace number is 70 lines；
（9）, using rubber with the pressure of 200-500g to heat transfer film carry out wear-resisting test；The production of wear-resisting test qualification
Product heat silica gel wheel into transfer, are shifted the decorative pattern on radium-shine product in material by the thermal energy of silica gel wheel, extruding force
On；The silica gel wheel hardness is 75 degree, and temperature is 270 DEG C.
Embodiment 2
Such as Fig. 1, radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, including the PET film as thermal transfer carrier
Layer 1, and successively it is overlying on release layer 2, preceding protective layer 3, rear protective layer 4, printing layer 5, three-dimensional laser on PET film layer 1
Protective layer 6, aluminium coated 7 press radium-shine flower-pattern layer 8, mucigel 9 afterwards, and the rear protective layer 4 is metal oxide, metal halide
Or nonmetal oxide, the mucigel 9 are the structure of the double-deck viscose；
Wherein, the thickness point of the release layer 2, preceding protective layer 3, rear protective layer 4, three-dimensional laser protective layer 6, aluminium coated 7
It Wei not 20 ~ 200 μm, 5-50 μm, 5-50 μm, 10-100 μm；
The release layer 2 includes one of silicon mould release, fluorine element mould release, and the release effect that release layer 2 is formed
The following conditions should be met, at 100 DEG C or less, release layer 2 and PET film layer adhesive force are splendid, reach 100 in ambient temperature
DEG C or more when can be significantly reduced with PET original film adhere to, to be easily peeled off；The material of protective layer 4 is respectively selected from after described
SiO、SiO2、Si2O3、MgF2、CaF2、Y2O3、GeO2、Ta2O5、Al2O3、Nd2O3、ZnO、TiO2、PbO、ThO2、Sc2O3、ZrO、
ZrO2One of；
The mucigel 9 includes the first mucigel 91, the second mucigel 92 successively covered from the rear radium-shine flower-pattern layer of pressure, and
The adhesion of first mucigel 91 is greater than the adhesion of the second mucigel 92；First mucigel 91 is multiple for polyurethanes
Viscose is closed, it includes the components of following parts by weight：
33 parts of polyurethane resin
Acrylic resin modified 12 parts
7 parts of epoxy resin
1 part of ethylene-vinyl acetate resin
3 parts of cellulose acetate resin
1 part of curing agent
120 parts of organic solvent；
Second mucigel 92 is one of epoxide-resin glue, PP glue, ABS glue；
The production technology that radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, includes the following steps：
（1）, choose clean PET film layer, sprawl；With ceramic wafer be coated with release layer, the release layer be self-crosslinking,
In the composition containing 3 kinds or more acrylic resin monomers of semifluid shape, it is coated with 70 line of line number；Halftone cable is 150-220 line,
Wherein " line " is unit-line number/inch, indicates the per inch line number of halftone, 1 line=2.5 mesh；The wet coating amount of release layer is
6.5g/m2 dry-coated amount is 1.25g/m2；
（2）, in release layer surface form the fine and close structure sheaf of crosslinking using host agent and curing agent, as preceding protective layer；
（3）, using be evaporated in vacuo or sputter deposition craft, preceding protective layer coating after protective layer；
（4）, printed using the ink of organic solvent-resistant in rear protective layer, it is 80 that four primaries ink, which prints line number,
Line, it is 60 lines that chalk, which prints line number, forms printing layer；Again toward coating three-dimensional laser protective layer in printing layer, it is extra then to clean
Ink air-dries and stands 2h or more, and silver lustre, bright gold or single golden effect is presented in three-dimensional laser protective layer at this time；
（5）, will（4）In semi-finished product be put into baking oven and continuously solidify, 51 DEG C of solidification temperature, time 20h；
（6）, aluminized on three-dimensional laser protective layer using vacuum aluminium plating process, aluminium is washed after aluminizing, is stood；
（7）, on radium-shine embossing machine by radium-shine pressure roller decorative pattern all overstock be transferred on product, ultimately form radium-shine
Decorative pattern, namely after press radium-shine flower-pattern layer to be formed；The temperature of radium-shine embossing machine is 1100 DEG C, pressure 8kg, speed 62m/min；
（8）, successively coat in the radium-shine decorative pattern layer surface of rear pressure or with the first mucigel of type, the second mucigel, every layer is applied
Tree lace number is 70 lines；
（9）, using rubber with the pressure of 200-500g to heat transfer film carry out wear-resisting test；The production of wear-resisting test qualification
Product heat silica gel wheel into transfer, are shifted the decorative pattern on radium-shine product in material by the thermal energy of silica gel wheel, extruding force
On；The silica gel wheel hardness is 65 degree, and temperature is 255 DEG C.
Embodiment 3
Such as Fig. 1, radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, including the PET film as thermal transfer carrier
Layer 1, and successively it is overlying on release layer 2, preceding protective layer 3, rear protective layer 4, printing layer 5, three-dimensional laser on PET film layer 1
Protective layer 6, aluminium coated 7 press radium-shine flower-pattern layer 8, mucigel 9 afterwards, and the rear protective layer 4 is metal oxide, metal halide
Or nonmetal oxide, the mucigel 9 are the structure of the double-deck viscose；
Wherein, the thickness point of the release layer 2, preceding protective layer 3, rear protective layer 4, three-dimensional laser protective layer 6, aluminium coated 7
It Wei not 20 ~ 200 μm, 5-50 μm, 5-50 μm, 10-100 μm；
The release layer 2 includes one of silicon mould release, fluorine element mould release, and the release effect that release layer 2 is formed
The following conditions should be met, at 100 DEG C or less, release layer 2 and PET film layer adhesive force are splendid, reach 100 in ambient temperature
DEG C or more when can be significantly reduced with PET original film adhere to, to be easily peeled off；The material of protective layer 4 is respectively selected from after described
SiO、SiO2、Si2O3、MgF2、CaF2、Y2O3、GeO2、Ta2O5、Al2O3、Nd2O3、ZnO、TiO2、PbO、ThO2、Sc2O3、ZrO、
ZrO2One of；
The mucigel 9 includes the first mucigel 91, the second mucigel 92 successively covered from the rear radium-shine flower-pattern layer of pressure, and
The adhesion of first mucigel 91 is greater than the adhesion of the second mucigel 92；First mucigel 91 is multiple for polyurethanes
Viscose is closed, it includes the components of following parts by weight：
45 parts of polyurethane resin
Acrylic resin modified 14 parts
10 parts of epoxy resin
2 parts of ethylene-vinyl acetate resin
2.5 parts of cellulose acetate resin
0.2 part of curing agent
150 parts of organic solvent；
Second mucigel 92 is one of epoxide-resin glue, PP glue, ABS glue；
The production technology that radium-shine heat transfer film is pressed after a kind of novel high-performance is three-dimensional, includes the following steps：
（1）, choose clean PET film layer, sprawl；With ceramic wafer be coated with release layer, the release layer be self-crosslinking,
In the composition containing 3 kinds or more acrylic resin monomers of semifluid shape, it is coated with 70 line of line number；Halftone cable is 150-220 line,
Wherein " line " is unit-line number/inch, indicates the per inch line number of halftone, 1 line=2.5 mesh；The wet coating amount of release layer is
7.0g/m2, dry-coated amount is 1.4g/m2；
（2）, in release layer surface form the fine and close structure sheaf of crosslinking using host agent and curing agent, as preceding protective layer；
（3）, using be evaporated in vacuo or sputter deposition craft, preceding protective layer coating after protective layer；
（4）, printed using the ink of organic solvent-resistant in rear protective layer, it is 80 that four primaries ink, which prints line number,
Line, it is 60 lines that chalk, which prints line number, forms printing layer；Again toward coating three-dimensional laser protective layer in printing layer, it is extra then to clean
Ink air-dries and stands 2h or more, and silver lustre, bright gold or single golden effect is presented in three-dimensional laser protective layer at this time；
（5）, will（4）In semi-finished product be put into baking oven and continuously solidify, 48 DEG C of solidification temperature, the time is for 24 hours；
（6）, aluminized on three-dimensional laser protective layer using vacuum aluminium plating process, aluminium is washed after aluminizing, is stood；
（7）, on radium-shine embossing machine by radium-shine pressure roller decorative pattern all overstock be transferred on product, ultimately form radium-shine
Decorative pattern, namely after press radium-shine flower-pattern layer to be formed；The temperature of radium-shine embossing machine is 1200 DEG C, pressure 12kg, speed 65m/
min；
（8）, successively coat in the radium-shine decorative pattern layer surface of rear pressure or with the first mucigel of type, the second mucigel, every layer is applied
Tree lace number is 70 lines；
（9）, using rubber with the pressure of 200-500g to heat transfer film carry out wear-resisting test；The production of wear-resisting test qualification
Product heat silica gel wheel into transfer, are shifted the decorative pattern on radium-shine product in material by the thermal energy of silica gel wheel, extruding force
On；The silica gel wheel hardness is 70 degree, and temperature is 265 DEG C.
Above embodiments are only to illustrate the optimal technical scheme of the utility model, it is noted that for the art
Those of ordinary skill for, without departing from the principle of this utility model, several improvement made or equivalent replacement,
It is accordingly to be regarded as the protection scope of the utility model, should be covered in the scope of the claims of the utility model.
Claims (5)
1. pressing radium-shine heat transfer film after a kind of novel high-performance is three-dimensional, which is characterized in that thin including the PET as thermal transfer carrier
Film layer, and successively it is overlying on release layer, preceding protective layer, rear protective layer, printing layer, three-dimensional laser protection on PET film layer
Layer, aluminium coated press radium-shine flower-pattern layer, mucigel afterwards, and the rear protective layer is metal oxide, metal halide or nonmetallic
Oxide, the mucigel are the structure of the double-deck viscose.
2. pressing radium-shine heat transfer film after a kind of novel high-performance according to claim 1 is three-dimensional, which is characterized in that it is described from
Type layer, preceding protective layer, rear protective layer, three-dimensional laser protective layer, aluminium coated thickness be respectively 20 ~ 200 μm, 5-50 μm, 5-50 μ
m、10-100μm。
3. pressing radium-shine heat transfer film after a kind of novel high-performance according to claim 1 is three-dimensional, which is characterized in that it is described from
Type layer includes one of silicon mould release, fluorine element mould release.
4. pressing radium-shine heat transfer film after a kind of novel high-performance according to claim 1 is three-dimensional, which is characterized in that described glutinous
Glue-line includes the first mucigel, the second mucigel successively covered from the rear radium-shine flower-pattern layer of pressure, and first mucigel is glutinous
Put forth effort the adhesion greater than the second mucigel.
5. pressing radium-shine heat transfer film after a kind of novel high-performance according to claim 4 is three-dimensional, which is characterized in that described the
Two mucigels are one of epoxide-resin glue, PP glue, ABS glue.