CN207537382U - A kind of self-lubricating anticorrosive composite coating structure - Google Patents
A kind of self-lubricating anticorrosive composite coating structure Download PDFInfo
- Publication number
- CN207537382U CN207537382U CN201721118576.3U CN201721118576U CN207537382U CN 207537382 U CN207537382 U CN 207537382U CN 201721118576 U CN201721118576 U CN 201721118576U CN 207537382 U CN207537382 U CN 207537382U
- Authority
- CN
- China
- Prior art keywords
- self
- lubricating
- coating
- composite coating
- anticorrosive composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of self-lubricating anticorrosive composite coating structures, are combined by materials at two layers, are followed successively by erosion resistant coating and self-lubricating layer from the inside to the outside.The material has the performances such as anti-corrosion, wear-resisting, super hydrophilic and self-lubricating, both economically and environmentally beneficial, can be widely used for the fields such as spacecraft, aircraft, satellite, rocket, atomic power device, instrument and meter, vehicle, ship, lathe punching press.
Description
Technical field
The utility model belongs to self-lubricating anti-corrosion material field, more particularly to a kind of anti-corrosion applied to industrial materials surface
Wear-resistant self-lubricating composite coating structure.
Background technology
People's living standards continue to improve, the usage amount of air-conditioning are increasing year by year.The air conditioner of China's production in 2005
Up to 53,000,000,200,000 tons of aluminium foil is consumed.The use of air-conditioning is more universal, but air-conditioning is during long-term use, it may appear that
Power consumption increases, many problems such as dust pollution, peculiar smell, bacteria breed.With national energy-saving method and the phase of Law on Environmental Protection
After appearance, air-conditioning constantly develops to miniaturization, lightweight and high performance direction, the function and performance of idle call aluminum fin-stock is carried
Higher requirement is gone out.Heat exchanger of air condition cooling fin is made of the aluminium foil of 1mm or so thickness, in order to obtain good performance,
The aluminium foil cooling fin of the small pitch of fins of generally use, complicated piece shape.
During air conditioner refrigeration, Water vapor condensation in air is simultaneously attached to fin surface, forms " water bridge " between fin, makes
Increase into ventilation resistance, noise increases, the work efficiency drop of heat exchanger, and energy consumption increases;If aluminium foil is directly used in radiator
Fin in the air conditioner of cooling-heating room dual-purpose, is in the environment of alternation of wetting and drying, forms oxygen concentration cell, be easily corroded in use, raw
Into Al2O3.3H2The white powder object of O, is commonly called as " white powder ", in wet condition, makes mould growth in heat exchanger, is sent into the wind
It is indoor and pollute environment.The problems such as in order to solve " water bridge ", " white powder " well, it is necessary to surface coated treatment is carried out to aluminium foil,
Make it have good corrosion resistance and high-hydrophilic energy.
Meanwhile wear-resisting oil can be used when processing air-conditioner fin, later stage fin can be generated during secondary baking a large amount of
Flue gas pollutes environment, causes shopwork bad environments, health is damaged very big, while wastes many wear-resisting
Oil.
Self-lubricating anticorrosive composite coating structure has the function of anti-corrosion, wear-resisting, super hydrophilic and self-lubricating, not only economic but also ring
It protects, can be widely used for the necks such as spacecraft, aircraft, satellite, rocket, atomic power device, instrument and meter, vehicle, ship, lathe punching press
Domain.
Invention content
Technical problem to be solved in the utility model is:For the deficiency of currently available technology, provide a kind of with anti-
Rotten, wear-resisting, super hydrophilic and self-lubricating coating structure;The coating can be such that frictional interface is lubricated well, while give
The anti-corrosion protection of effect reduces abrasion;Suitable for spacecraft, aircraft, satellite, rocket, atomic power device, instrument and meter, vehicle, ship
The fields such as oceangoing ship, lathe punching press.
Technical solution is used by the utility model solves its technical problem:A kind of self-lubricating anticorrosive composite coating knot
Structure, it is characterised in that:It is combined by materials at two layers, is followed successively by erosion resistant coating 2, self-lubricating layer 1 from the inside to the outside.
The erosion resistant coating 2 is waterborne epoxy modified acrylic resin coating, aqueous polyurethane acrylate coating or aqueous
Organosilicon-modified acrylate coating, thickness are 0.5~10.0um;More preferable 0.6~2.0um.
The self-lubricating layer 1 is polyimides-water-based acrylic resin coating, and thickness is 0.15~0.5um.
The beneficial effects of the utility model are:With excellent anti-corrosion capability, surface friction factor can be effectively reduced, is carried
High surface lubrication and wearability;In the case where lubricating grease cannot play a role, it can substitute lubricating grease, in high temperature, strong spoke
It penetrates, in deep-etching, high vacuum and other special medias, frictional interface is made to be lubricated well, while give effective anti-corrosion
Erosion protection, reduces abrasion.Hydrophile function is cleverly introduced in lubricant layer, surface layer has super hydrophilicity, water droplet contact angle
It goes to zero, surface blot is taken away by the gravity of uniform water film, there is splendid self-cleaning ability, while can also allow self-lubricating
It is better.
Description of the drawings
Fig. 1 is the longitudinal profile structure schematic of the self-lubricating anticorrosive composite coating structure of the utility model.
In Fig. 1,1- self-lubricating layers, 2- erosion resistant coatings, 3- base materials.
Specific embodiment
The utility model is described in further detail with reference to the accompanying drawings and examples.
The utility model self-lubricating anticorrosive composite coating structure, is combined by materials at two layers, is followed successively by from the inside to the outside anti-
Rotten layer 2 and self-lubricating layer 1.
Erosion resistant coating 2 is waterborne epoxy modified acrylic resin coating, aqueous polyurethane acrylate coating or aqueous organic
Fluorine-silicon modified acrylic ester coating, certain temperature and under the time carry out baking-curing form, thickness be 0.5~10.0um, it is more excellent
Select 0.6~2.0um.Waterborne epoxy modified acrylic resin coating is by waterborne epoxy modified acrylic resin, curing agent, attachment
Power accelerating agent, substrate wetting agents, catalyst, pigment and solvent is heated cures;Aqueous polyurethane acrylate coating is
By aqueous polyurethane acrylate resin, curing agent, adhesion promoter, substrate wetting agents, catalyst, pigment and solvent through adding
Heat cure forms;Waterborne organic silicon modification acrylate coating is by waterborne organic silicon modified urethane acrylate resin, dredges
Waterborne acrylic paint, double bond containing methyl carboxylic acids/epoxy group/amide groups monomer, diluent, curing agent and auxiliary agent are heated
Cure.Selected matrix resin has good anti-corrosion capability, and adhesion promoter can be crosslinked with each raw material well
Curing forms tridimensional network, makes interlayer structure finer and close.
Self-lubricating layer 1 is polyimides-water-based acrylic resin coating, and thickness is 0.15~0.5um.Polyimides-
Water-based acrylic resin coating is by soluble polyimide, water-based acrylic resin, glycoluril resin, wetting agent, graphite, poly- four
Vinyl fluoride, molybdenum disulfide, carbon fiber, dispersant, levelling agent and solvent are passed through certainly dry or are heating and curing.Soluble polyimide
The replacements such as aramid fiber, polyphenylene sulfide, polyethersulfone ketone, poly (aryl ether sulfone ketone), polypyromelliticimide, polyamide-imides can be used.Water
Property acrylic resin is by 2- acrylamide-2-methyl propane sulfonics sodium, 3- allyloxy -2- hydroxyl -1- propanesulfonates, propylene
Acid, hydroxy-ethyl acrylate, hydroxypropyl acrylate, initiator etc. are obtained by synthetic reaction.Self-lubricating layer can effectively reduce surface
Friction factor improves surface lubrication and wearability;In the case where lubricating grease cannot play a role, it can substitute lubricating grease,
In high temperature, intense radiation, deep-etching, high vacuum and other special medias, frictional interface is made to be lubricated well, is given simultaneously
Effective anti-corrosion protection reduces abrasion.The utility model has cleverly introduced hydrophile function in lubricant layer, and surface layer has super
Hydrophilicity, water droplet contact angle go to zero, and surface blot is taken away by the gravity of uniform water film, can play well from clear
Clean effect, while can also allow self-lubricating effect more preferably.
Roller coating, brushing or spraying method can be used in the utility model, and preparation process flow is:It is coated successively on base material 3
Corrosion-resistant coating 2 and self-lubricating layer 1, baking-curing must be carried out under certain temperature and time by being often painted with one layer;Baking temperature exists
Between 215~265 DEG C, baking time is between 5~20 seconds.The utility model product is obtained after it is fully cured.Base material 3 is
Metal component.
It the above is only the concrete application example of the utility model, protection domain be not limited in any way, it is all using equivalent
Transformation or equivalence replacement and the technical solution that is formed, all fall within the utility model rights protection scope.
Claims (2)
1. a kind of self-lubricating anticorrosive composite coating structure, it is characterised in that:It is combined by materials at two layers, is followed successively by from the inside to the outside
Erosion resistant coating(2)And self-lubricating layer(1);Self-lubricating layer (1) be polyimides-water-based acrylic resin coating, thickness 0.15
~0.5um.
2. self-lubricating anticorrosive composite coating structure according to claim 1, it is characterised in that:The erosion resistant coating(2)For water
Property epoxy modified acrylic resin coating, aqueous polyurethane acrylate coating or waterborne organic silicon modification acrylate coating,
Its thickness is 0.5~10.0um.