CN207484896U - Non-planar transfer printing wood composite floor - Google Patents
Non-planar transfer printing wood composite floor Download PDFInfo
- Publication number
- CN207484896U CN207484896U CN201721619405.9U CN201721619405U CN207484896U CN 207484896 U CN207484896 U CN 207484896U CN 201721619405 U CN201721619405 U CN 201721619405U CN 207484896 U CN207484896 U CN 207484896U
- Authority
- CN
- China
- Prior art keywords
- substrate
- transfer printing
- panel
- floor
- composite floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a wooden laminate flooring of non-planar rendition, including plain board and rendition in the transfer printing layer on plain board surface, transfer printing layer surface still has the wearing layer, and wherein, plain board includes: the base plate is formed by alternately overlapping, forging and pressing two solid wood base plates; a bottom plate attached to the lower surface of the substrate; the panel is attached to the upper surface of the substrate, and the panel is processed manually or mechanically to form a groove on the upper surface of the panel, so that the non-planar effect of imitating the European and American style is obtained; the transfer printing layer completely covers all the upper surfaces of the panels including the bottom surfaces of the grooves. The non-planar transfer printing wood composite floor adopting the technical scheme can not only have the antique effect of a solid wood floor, but also have the effect of decorating high-grade patterns on low-grade fast-growing wood by the transfer printing floor. Therefore, the fast-growing and high-yield forest can be fully utilized, valuable wood resources are saved, and the requirements of individuation, diversification, layering and the like of home decoration can be met.
Description
Technical field
The utility model is related to timber floor, more particularly to a kind of on-plane surface transfer wooden composite floor.
Background technology
International market rare tree is more and more rare at present, some seeds have reached the situation in imminent danger that faces, and the whole world is more next
More people starts to pay attention to the ecological balance, some countries start to formulate a series of laws and regulations.In order to strengthen to country and generation
The protection of boundary's forest reserves rare tree species, while meet pursuit of the high-end consumer group to domestic environment again, this just gives us
Bring new thinking.
At this stage, the transfer floor generally sold on the market, the overwhelming majority are produced in a manner that roller directly prints, color
Pool is not abundant, texture is unintelligible, and solid layer feeling is poor, while dicoration present in printed decoration technology is distorted, is fast light
The common problems such as poor color fastness, adhesive force is low.
Utility model content
One purpose of the utility model is to provide a kind of on-plane surface transfer wooden composite floor.
One side according to the present utility model provides a kind of on-plane surface transfer wooden composite floor, including plain plate and
The transfer printing layer being needed in plain plate surface, transfer layer surface also have wearing layer, wherein, plain plate includes:
Substrate is overlapping forging forming by two kinds of solid wood baseplates, and solid wood baseplate includes first substrate and second substrate, the
Width direction of the grain direction of one substrate along substrate, the length direction of the grain direction of second substrate along substrate;
Bottom plate fits in base lower surface;
Panel fits in upper surface of base plate, and panel is handled surface on it by craft or machinery and forms groove,
So as to obtain the effect of nonplanar American-European style modelled after an antique;
Transfer printing layer is completely covered by all panel upper surfaces including groove floor.
Further, substrate is symmetrical lamination structure, and moisture content≤10%;
Bottom plate is poplar bottom plate, and thickness is 1.2~2mm, and moisture content is 14%~20%;
Panel is for A grades without splicing beech or birch panel, thickness >=1.2mm, moisture content≤8%.
Further, groove floor is arc, and its depth is 0.1mm~0.3mm, and the area of groove distribution is on panel
The 30%~70% of surface area.
Further, the pattern of transfer printing layer is wooden native texture, stone texture, the wood mutually arranged in pairs or groups with American-European style modelled after an antique
The image of material parquets texture or aesthetic.
Further, wearing layer is made of the coating that one layer or multilayer ultraviolet-curing paint are formed.
Further, hardness >=2H of wearing layer, wear-resisting revolution is >=500 turns, and wearing valve≤0.12g/100r.
Wooden composite floor is transferred using the on-plane surface of above technical scheme, using elastic transfer film and cold-press process,
Nonplanar surface of wood floors by process one layer of transfer pattern extremely true to nature of coating completely, can both have
The antique effect of solid wooden floor board, it may have the effect of high-grade pattern is decorated on transfer floor on inferior grade fast growing wood.Thus
It can reach and make full use of fast-growing, high-yield woods, save rare timber resources, and it is personalized, various to meet home decoration
The needs such as change, stratification.Meanwhile substrate takes two kinds of solid wood baseplates to be overlapping the mode of forging forming, can effectively eliminate
The internal stress on floor prevents timber floor from deforming due to moisture absorption expansion or xeothermic contraction, is especially suitable for south humidity and north
Xeothermic environment in Fang Dongji rooms.
Description of the drawings
Fig. 1 is that a kind of on-plane surface of embodiment of the utility model transfers the structure diagram of wooden composite floor.
Fig. 2 is the structure diagram of plain plate shown in Fig. 1.
Fig. 3 is the vertical section structure schematic diagram of plain plate shown in Fig. 2.
Specific embodiment
The utility model is described in further detail below in conjunction with the accompanying drawings.
Fig. 1 to Fig. 3 schematically shows a kind of a kind of on-plane surface transfer wood of embodiment according to the present utility model
Matter composite floor board.As shown in the figure, on-plane surface transfer wooden composite floor includes plain plate 1 and is needed on plain 1 surface of plate to turn
Print layer 2.2 surface of transfer printing layer also has wearing layer 3.
Wherein, plain plate 1 includes:Substrate 11, bottom plate 12 and panel 13.
Substrate 11 is overlapping forging forming by two kinds of solid wood baseplates, and the number of plies of overlapping is 2~14 layers.
Solid wood baseplate includes first substrate 11a and second substrate 11b.
Width direction of the grain direction of first substrate 11a along substrate 11, the grain direction of second substrate 11b is along substrate 11
Length direction.
Bottom plate 12 fits in 11 lower surface of substrate.
Panel 13 fits in 11 upper surface of substrate.
Panel 13 is handled surface formation groove 13a on it by craft or machinery, nonplanar so as to obtain
The effect of America and Europe's style modelled after an antique.
Transfer printing layer 2 is completely covered by the upper surface of all panels 13 including groove 13a bottom surfaces.
In the present embodiment, substrate 11 is symmetrical lamination structure, and moisture content≤10%.
Bottom plate 12 is poplar bottom plate, and thickness is 1.2~2mm, and moisture content is 14%~20%.
Panel 13 is for A grades without splicing beech or birch panel, thickness >=1.2mm, moisture content≤8%.
Groove 13a bottom surfaces are arc, and its depth is 0.1mm~0.3mm.
The area of groove 13a distributions is the 30%~70% of 13 upper surface area of panel.
The pattern of transfer printing layer 2 is wooden native texture, stone texture, the timber parquets line mutually arranged in pairs or groups with American-European style modelled after an antique
The image of reason or aesthetic.
Wearing layer 3 is made of the coating that one layer or multilayer ultraviolet-curing paint are formed.
Hardness >=2H of wearing layer 3, wear-resisting revolution is >=500 turns, and wearing valve≤0.12g/100r.
Wooden composite floor is transferred using the on-plane surface of above technical scheme, using elastic transfer film and cold-press process,
Nonplanar surface of wood floors by process one layer of transfer pattern extremely true to nature of coating completely, can both have
The antique effect of solid wooden floor board, it may have the effect of high-grade pattern is decorated on transfer floor on inferior grade fast growing wood.Thus
It can reach and make full use of fast-growing, high-yield woods, save rare timber resources, and it is personalized, various to meet home decoration
The needs such as change, stratification.
The on-plane surface transfers wooden composite floor, by various wooden native textures, stone texture, timber parquets texture, skill
Image of art aesthetic feeling etc. is transferred to the surface of timber floor, is realized and decorated on inferior grade fast growing wood by way of film transfer
The ornament materials of high-grade effect.Fast-growing, high-yield woods is made full use of to reach, saves rare timber resources, meets home decoration
The needs such as property, diversification, stratification.
Since on-plane surface transfer wooden composite floor can approach the true embodiment various traditional decorations such as timber, marble
The texture of material, while there are many merits such as production efficiency height, at low cost, low-carbon, environmental protection, it is possible to predict film transfer wood
Floor will significantly replace these traditional floor materials later, not only with huge market economy benefit, will also play
Rare wood kind is protected, the forest reserves of preserving our planet build the social benefit of the living environment of low-carbon environment-friendly.
The production method that wooden composite floor is transferred by above-mentioned on-plane surface, can be in any solid wood composite base material or low
Grade is by printing any desired seeds texture (such as ebony, red santal, teak, Brazilian rosewood on the solid wood material after repairing
Deng), efficent use of resources, and its clarity, stereoscopic effect, sense of reality etc. can with solid wooden compound floor currently on the market and
Solid wooden floor board is the same.
For floor is directly printed, the decorative pattern synchronous error of on-plane surface transfer wooden composite floor is small, color
Level is more rich (being usually that 4-6 colors are finely tuned), can more really restore the texture of embodiment timber, marble etc..Simultaneously
Using fast-growing, high-yield woods wood materials as base material, resource is stable, not welding, and content of formaldehyde is low.So as to meet higher
The demand of the consumer group of level has further expanded the market space of printing floor.
For consolidated floor, on-plane surface transfers wooden composite floor and simplifies with technique, and production efficiency is high, prints
Film without melamine glue water process, without techniques such as hot pressing balances, plain plate can be directly transferred on oil paint coating line
Above, anti-tarnishing ability is strong, and 60 DEG C are toasted the advantages of non-discolouring in 48 hours;Decorative pattern obtained is than consolidated floor facing paper simultaneously
Decorative pattern more have three-dimensional sense, it is more true to nature.
Above-described is only some embodiments of the utility model.For those of ordinary skill in the art,
Under the premise of not departing from the utility model and creating design, various modifications and improvements can be made, these belong to this practicality
Novel protection domain.
Claims (6)
1. a kind of on-plane surface transfers wooden composite floor, described including plain plate and the transfer printing layer being needed in the plain plate surface
Transferring layer surface also has wearing layer, wherein, the element plate includes:
Substrate is overlapping forging forming by two kinds of solid wood baseplates, and the solid wood baseplate includes first substrate and second substrate, institute
State width direction of the grain direction of first substrate along the substrate, the length of the grain direction of the second substrate along the substrate
Spend direction;
Bottom plate fits in the base lower surface;
Panel, fits in the upper surface of base plate, and the panel is handled surface on it by craft or machinery and formed
Groove, so as to obtain the effect of nonplanar American-European style modelled after an antique;
The transfer printing layer is completely covered by all panel upper surfaces including the groove floor.
2. on-plane surface according to claim 1 transfers wooden composite floor, which is characterized in that the substrate is symmetrical lamination
Structure, and moisture content≤10%;
The bottom plate is poplar bottom plate, and thickness is 1.2~2mm, and moisture content is 14%~20%;
The panel is for A grades without splicing beech or birch panel, thickness >=1.2mm, moisture content≤8%.
3. on-plane surface according to claim 1 transfers wooden composite floor, which is characterized in that the groove floor is arc
Shape, and its depth is 0.1mm~0.3mm, the area of the groove distribution is the 30%~70% of the panel upper surface area.
4. on-plane surface according to claim 1 transfers wooden composite floor, which is characterized in that the pattern of the transfer printing layer is
The image of wooden native texture, stone texture, timber parquets texture or aesthetic mutually arranged in pairs or groups with American-European style modelled after an antique.
5. on-plane surface according to claim 1 transfers wooden composite floor, which is characterized in that the wearing layer by one layer or
The coating that person's multilayer ultraviolet-curing paint is formed is formed.
6. on-plane surface according to claim 1 transfers wooden composite floor, which is characterized in that the hardness of the wearing layer >=
2H, wear-resisting revolution is >=500 turns, and wearing valve≤0.12g/100r.