CN206800193U - A kind of durable cement concrete bridge floor composite pavement structure - Google Patents
A kind of durable cement concrete bridge floor composite pavement structure Download PDFInfo
- Publication number
- CN206800193U CN206800193U CN201720452229.8U CN201720452229U CN206800193U CN 206800193 U CN206800193 U CN 206800193U CN 201720452229 U CN201720452229 U CN 201720452229U CN 206800193 U CN206800193 U CN 206800193U
- Authority
- CN
- China
- Prior art keywords
- cement concrete
- concrete bridge
- strength polymer
- concrete
- pavement structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of durable cement concrete bridge floor composite pavement structure,Including cement concrete bridge deck plate,The cement concrete bridge deck plate is sequentially arranged above high-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata and high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer,The cement concrete bridge deck plate and high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer pass through the Thief zone epoxy coating that is sequentially overlapped,Modified resin confining bed,Water-proof tack coat,Rubber asphalt crushed stone sealing bonds,The utility model uses the durability paving structure of " water-proof tack coat+double-layer high-strength Polymer-Modified Mortar asphalt reperfusion concrete ",Water-proof tack coat can effectively prevent water from entering the early disease that concrete slab causes bridge structure using four layers,Double-layer high-strength Polymer-Modified Mortar asphalt reperfusion concrete has good high temperature anti-rut behavior,Rut can be reduced,Gather around the diseases such as bag.
Description
Technical field
Making be the utility model is related in the paving structure technical field on cement concrete bridge deck, be specially a kind of resistance to
Long cement concrete bridge floor composite pavement structure.
Background technology
In recent years, with the development of communication, the volume of traffic and heavy vehicle are more and more, in heavy duty, overload, canalization etc.
Bridge and its deck installation structure durability directly carried are faced with acid test under traffic environment.
It with cement concrete or bituminous concrete is a kind of layer of the main material-paving on floorings that deck paving, which is,
Shape structure, it, which should be played, provides vehicle safety, the smooth, function comfortably run, plays protection floorings again, maintains or prolong
The effect of long bridge service life.Therefore, for resisting the erosion damage of outer bound pair bridge main body structure, it may be said that design
Together with will being cement concrete bridge or floorings with good deck paving of constructing " artificial barrier ".
For asphalt concrete pavement, due to deck paving in current Chinese code of practice and waterproofing design or blank, in work
It is generally consistent with normal section for ease of construction, deck installation structure type in journey practice.Dripped more using close-graded or SMA
The form of mating formation of blue or green concrete, 4~8cm of pavement thickness are soft only with one layer of weak pitch class between pave-load layer and floorings
Property binder course(Such as emulsified asphalt, polyurethane solvent-borne type pitch bonding agent etc.).This kind of pavement structure system, even if pave-load layer uses
The modified asphalt binders or SMA mixture of function admirable, but due to can not be formed between asphalt pavement main body and floorings
Effect connection, under carload effect, pave-load layer easily occurs delamination and causes pave-load layer cracking destruction with floorings.Meanwhile by
In the waterproof effect for not taking into full account pavement structure system.Water is by between layer surface infiltration pave-load layer floorings of mating formation, will add
The peeling of fast pave-load layer and floorings;On the other hand, the water penetrated between pave-load layer and floorings, will penetrate further into floorings
And in bridge structure, cause the steel bar corrosion of structure, it can also produce freeze-thaw damage, the mechanical property of bridge structure in extremely frigid zones
Decline, bridge durability will be affected.
And for Bridge Surface Paving by Cement, then certain thickness individual layer coagulating cement is directly laid on floorings
Soil, or laid respectively by leveling layer and concrete pavement surface layer, 3~10cm of thickness.Typically floorings and pave-load layer it
Between waterproof layer is not set specially, but the water-proof function of deck paving is realized as pave-load layer by using water-proof concrete.But
Due to some concrete pavement layer thickness deficiency, pave-load layer easily produces damaged in the presence of vehicular load and temperature;And by
Bad and concrete is handled in the water shutoff of contracting seam and construction joint and produces warm plastic forming, and rain, snow-broth will immerse concrete pavement layer
With the concrete component of bridge structure, steel member corrosion is set to bring harm to corrode to bridge structure.
Utility model content
The purpose of this utility model is to provide a kind of durable cement concrete bridge floor composite pavement structure, with solution
State the problem of being proposed in background technology.
To achieve the above object, the utility model provides following technical scheme:A kind of durable cement concrete bridge deck is answered
Paving structure is closed, including cement concrete bridge deck plate, the cement concrete bridge deck plate are sequentially arranged above high strength polymer and changed
Property mortar injection bituminous concrete upper strata and high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer, the cement concrete
Floorings and high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer pass through the Thief zone epoxy coating that is sequentially overlapped, modification
Resin-blocked layer, water-proof tack coat, the bonding of rubber asphalt crushed stone sealing.
Preferably, the thickness of the high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer is 5~6cm, wherein female
The nominal maximum particle diameter of body compound is not more than 13.2mm.
Preferably, the thickness on the high-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata is 5~6cm, wherein female
The nominal maximum particle diameter of body compound is not more than 13.2mm.
Preferably, the upper surface of the cement concrete bridge deck plate is dew stone interface.
Preferably, the Thief zone epoxy coating dosage is 500~1200g/m2。
Preferably, the modified resin confining bed dosage is 1.8~3.0kg/m2。
Preferably, the water-proof tack coat is that the coating of second-order reaction type high-strength quick-acting water-proof adhesive forms, and dosage is
200~400g/m2。
Preferably, the rubber asphalt spreading amount of the rubber asphalt crushed stone sealing is 1.5~2.5kg/m2。
Compared with prior art, the beneficial effects of the utility model are:A kind of compound paving of durable cement concrete bridge deck
Assembling structure, the utility model Bridge Surface Paving by Cement structure, using " water-proof tack coat+double-layer high-strength polymer modification sand
Starch asphalt reperfusion concrete " the substantially zeroed durability paving structure of voidage, water-proof tack coat can be effective using four layers
Prevent water from entering the early disease that concrete slab causes bridge structure, and improve the bonding with floorings;Double-layer high-strength polymer
Modified mortar asphalt reperfusion concrete modulus is higher, has good high temperature anti-rut behavior, can reduce rut, gather around bag, pit
It is very fine and close etc. disease, while also, so as to effectively prevent surface layer to be seeped into floorings under water and cause damage, strengthen water stability;
High-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata is again surface abrasion functional layer, has asphalt surface course flexibility and cement concurrently
The advantages of concrete topping rigidity, it can better meet to form comfortableness and security.Overall paving structure combination property is good,
Bridge service life can effectively be extended, reduce maintenance cost, meet heavy duty, canalized traffic demand, there is preferable society
Can benefit and economic benefit.
Brief description of the drawings
Fig. 1 is structural representation of the present utility model.
In figure:1- cement concrete bridge deck plates, 2- Thief zone epoxy coatings, 3- modified resin confining beds, 4- water-proof bindings
Layer, 5- rubber asphalt crushed stone sealings, the high-strength Polymer-Modified Mortar asphalt reperfusion concrete pavement lower floors of 6-, the high strength polymers of 7-
Modified mortar asphalt reperfusion concrete upper strata.
Embodiment
Below in conjunction with the accompanying drawing in the utility model embodiment, the technical scheme in the embodiment of the utility model is carried out
Clearly and completely describing, it is clear that described embodiment is only the utility model part of the embodiment, rather than whole
Embodiment.Based on the embodiment in the utility model, those of ordinary skill in the art are not under the premise of creative work is made
The every other embodiment obtained, belong to the scope of the utility model protection.
Referring to Fig. 1, the utility model provides a kind of technical scheme:A kind of durable cement concrete bridge floor composite pavement
Structure, including cement concrete bridge deck plate 1, cement concrete bridge deck plate 1 are sequentially arranged above high-strength Polymer-Modified Mortar and filled
Note bituminous concrete upper strata 7 and high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer 6, double-layer high-strength polymer modification sand
It is higher to starch asphalt reperfusion concrete modulus, there is good high temperature anti-rut behavior, rut can be reduced, gather around the diseases such as bag, pit,
Cement concrete bridge deck plate 1 and 6 Thief zone by being sequentially overlapped of high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer
Epoxy coating 2, modified resin confining bed 3, water-proof tack coat 4, rubber asphalt crushed stone sealing 5 bond, and water-proof tack coat 4 can have
Effect prevents water from entering the early disease that concrete slab causes bridge structure, and improves the bonding with concrete slab 1.
Specifically, the thickness of high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer 6 is 5~6cm, wherein parent
The nominal maximum particle diameter of compound is not more than 13.2mm, can reduce rut, gather around the diseases such as bag, pit, while also very fine and close, has
Effect prevents surface layer to be seeped into floorings under water and cause damage, and strengthens water stability.
Specifically, the thickness on high-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata 7 is 5~6cm, wherein parent
The nominal maximum particle diameter of compound is not more than 13.2mm, has the advantages of asphalt surface course flexibility is with Portland Cement Concrete Surface Course rigidity concurrently,
Can better meet to form comfortableness and security, so as to having good high temperature anti-rut behavior, can reduce rut, gather around bag,
The diseases such as pit, at the same it is also very fine and close, effectively prevent surface layer to be seeped into floorings under water and cause damage, strengthen water stability.
Specifically, the upper surface of cement concrete bridge deck plate 1 is dew stone interface, strong so as to improve the shearing resistance of deck paving
Degree and layer stability energy.
Specifically, the dosage of Thief zone epoxy coating 2 is 500~1200g/m2, so as to preferably infiltrate floorings.
Specifically, the dosage of modified resin confining bed 3 is 1.8~3.0kg/m2, so as to preferably consolidate rubble.
Specifically, water-proof tack coat 4 is that the coating of second-order reaction type high-strength quick-acting water-proof adhesive forms, and dosage is
200~400g/m2, prevent water from entering the early disease that concrete slab causes bridge structure, and improve the bonding with floorings.
Specifically, the rubber asphalt spreading amount of rubber asphalt crushed stone sealing 5 is 1.5~2.5kg/m2, it is had drip concurrently
The flexibility of blue or green surface layer.
Operation principle:Cut after blasted rough degree reaches 0.3~0.6mm, brush hypertonic on cement concrete bridge deck plate 1
Saturating epoxy coating 2, dosage is 500~1200g/m2, can infiltrate floorings with live Thief zone epoxy coating 2 is advisable, then sprays
Modified-reaction resin forms modified resin confining bed 3, and dosage is 1.8~3.0kg/m2, and 0.6~1.18mm is being dispensed thereon
Rubble, recommendation spreading amount is 500~800g/m2, can consolidate rubble with modified resin confining bed 3 is advisable, resin envelope to be modified
Close after layer 3 solidifies, coating second-order reaction type high-strength quick-acting water-proof adhesive forms water-proof tack coat 4, dosage be 200~400g/
m2,Then construction rubber asphalt crushed stone sealing 5, rubber asphalt spreading amount is 1.5~2.5kg/m2, crushed stone spreading amount be 10.0~
13.0kg/m2, finally point two layers of construction high-strength Polymer-Modified Mortar asphalt reperfusion of 10cm mixes on rubber asphalt crushed stone sealing 5
Solidifying soil, the globality that makes to mat formation is more preferable, improves paving structure water stability under heavy duty, canalized traffic, high temperature anti-rut behavior, durable
Property, effectively extend bridge service life.
While there has been shown and described that embodiment of the present utility model, for the ordinary skill in the art,
It is appreciated that these embodiments can be carried out with a variety of changes in the case where not departing from principle of the present utility model and spirit, repaiied
Change, replace and modification, the scope of the utility model are defined by the appended claims and the equivalents thereof.
Claims (8)
- A kind of 1. durable cement concrete bridge floor composite pavement structure, it is characterised in that:Including cement concrete bridge deck plate (1), the cement concrete bridge deck plate(1)It is sequentially arranged above high-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata (7)With high-strength Polymer-Modified Mortar asphalt reperfusion concrete layer(6), the cement concrete bridge deck plate(1)Gather with high-strength Polymer modified mortar injection bituminous concrete lower floor(6)Pass through the Thief zone epoxy coating being sequentially overlapped(2), modified resin closing Layer(3), water-proof tack coat(4), rubber asphalt crushed stone sealing(5)Bonding.
- A kind of 2. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described High-strength Polymer-Modified Mortar asphalt reperfusion concrete layer(6)Thickness be 5~6cm, the wherein nominal of precursor mix most Big particle diameter is not more than 13.2mm.
- A kind of 3. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described High-strength Polymer-Modified Mortar asphalt reperfusion concrete upper strata(7)Thickness be 5~6cm, the wherein nominal of precursor mix most Big particle diameter is not more than 13.2mm.
- A kind of 4. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described Cement concrete bridge deck plate(1)Upper surface be dew stone interface.
- A kind of 5. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described Thief zone epoxy coating(2)Dosage is 500~1200g/m2。
- A kind of 6. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described Modified resin confining bed(3)Dosage is 1.8~3.0kg/m2。
- A kind of 7. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described Water-proof tack coat(4)Formed for the coating of second-order reaction type high-strength quick-acting water-proof adhesive, and dosage is 200~400g/m2。
- A kind of 8. durable cement concrete bridge floor composite pavement structure according to claim 1, it is characterised in that:It is described Rubber asphalt crushed stone sealing(5)Rubber asphalt spreading amount be 1.5~2.5kg/ m2。