CN205877554U - Reinforce type elbow - Google Patents
Reinforce type elbow Download PDFInfo
- Publication number
- CN205877554U CN205877554U CN201620122332.1U CN201620122332U CN205877554U CN 205877554 U CN205877554 U CN 205877554U CN 201620122332 U CN201620122332 U CN 201620122332U CN 205877554 U CN205877554 U CN 205877554U
- Authority
- CN
- China
- Prior art keywords
- elbow
- welding
- welding bead
- elbow body
- bead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a reinforce type elbow, including the elbow body, the build -up welding has the coating on the inner wall of elbow body. The coating comprises the welding bead, and the welding bead is the heliciform build -up welding on the inner wall of elbow body. The utility model discloses just make this internal welding bead that is covered with of elbow, and only the head and the tail position there is welded joint to practiced thrift the material, very big this internal intensity and the resistant corrosion degree of elbow that has strengthened has lengthened life, has guaranteed the quality of product.
Description
Technical field:
This utility model relates to pipe fitting processing technique field, particularly to a kind of enhanced type elbow.
Background technology:
The oil gas of current exploitation contains the medium of high corrosion, use pressure height, needs to use the product of high-strength corrosion-resisting;
In the pipelines such as mining machinery and granule conveying, need to use the product of high-strength abrasion-proof due to erosion, it is therefore desirable to pipeline turns
Crook uses complex intensifying type elbow.Existing solution is to carry out built-up welding at the inwall of elbow body as shown in Figure 1, but hands
Work built-up welding mode time-consumingly long, wlding is wasted greatly, layer is uneven, of poor quality;Linear type built-up welding welding point is many, welding point position
The place of putting is then the position starting at first to be corroded and wear and tear, and causes elbow inherent quality to reduce, simultaneously because the welding bead in elbow
Flow to parallel with medium, product can shorten service life.
Utility model content:
The purpose of this utility model is aiming at the deficiency of prior art, and provides a kind of enhanced type elbow, solves existing
Having workload in technology big, expend material, linear type welding procedure has substantial amounts of welding point, causes elbow corrosion resistance resistance to
The problem that mill property is substantially reduced.
Technology solution of the present utility model is as follows:
A kind of enhanced type elbow, including elbow body, on the inwall of elbow body, heap is welded with coating.
As preferably, coating is made up of welding bead, and welding bead heap in the shape of a spiral is welded on the inwall of elbow body.Thus make
This internal welding bead that is covered with of elbow, and there is welding point position only from beginning to end, thus saved material, enhance elbow body greatly
Interior intensity and corrosion-resistant degree, extend service life, it is ensured that the quality of product.
As preferably, the width of the welding bead of heap postwelding is 5mm~10mm, and the thickness of the welding bead of heap postwelding is 2mm~4mm,
The welding bead of heap postwelding is levels helical form against one another.Welding bead thus can be made to be distributed in elbow inner body wall, and
And owing to the internal surface area of the part in the inner part of elbow body is less than the internal surface area of part in the outer part, so arranges and just can make
The state that inside welding bead realization, narrow outside is wide, in practical operation, the width of the welding bead of part in the outer part of elbow body is elbow
1.2 times~2.3 times of the width of the welding bead of part in the inner part of body, so that what welding bead can be the most complete is compounded in
On the whole inwall of elbow body, it is further ensured that quality and the service life of product, enhances the intrinsic intensity of elbow and resistance to
Degree of corrosion.
As preferably, the spiral angle of the welding bead of heap postwelding is 1 °~5 °.Thus can ensure that welding bead is at elbow body
Interior windings, so that this internal densely covered welding bead of elbow, less spiral angle also makes welding bead protect in weld deposit process
Keep steady fixed, further ensure that the welding bead of the part in the inner part of elbow body is narrower than the weldering of the part in the outer part of elbow body
Road.
As preferably, the material that bead welding uses is wlding, and the material of wlding is corrosion-resistant or abrasion-resistant welding wire.
As preferably, the material of wlding is rustless steel or nickel-bass alloy material.
As preferably, the material of elbow body is carbon steel.
The overlaying method of a kind of corrosion-resistant elbow, including spiral built-up welder, comprises the steps:
A, previous step: clean elbow inner body wall, and carry out polishing, polishing;
B, built-up welding: the elbow body after polishing, polishing is carried out spiral overlaid with spiral butt welding machine.
As preferably, the smoothness of the inwall of the elbow body after sanding and polishing is less than Ra 6.2.Control elbow body
The smoothness of inwall just can preferably make welding bead attached thereto, and make weld deposit process more smoothly, thus further
Enhance corrosion-resistant and strengthening effect.
The beneficial effects of the utility model are:
This utility model can make welding bead be distributed in elbow inner body wall, and due to the part in the inner part of elbow body
Internal surface area less than the internal surface area of part in the outer part, so arrange and just can make the wide shape in narrow outside inside welding bead realization
State, so that what welding bead can be the most complete is compounded on the whole inwall of elbow body, is further ensured that the quality of product
And service life, enhance the intrinsic intensity of elbow and corrosion-resistant degree.
Accompanying drawing illustrates:
Fig. 1: original bend pipe built-up welding sectional view;
Fig. 2: this utility model bend pipe built-up welding sectional view;
In figure, 1 is elbow body, and 2 is welding bead.
Detailed description of the invention:
Embodiment 1: a kind of enhanced type elbow as shown in Figure 2, including elbow body 1, on the inwall of elbow body 1, heap is welded with
Coating.
Coating is made up of welding bead 2, and welding bead 2 heap in the shape of a spiral is welded on the inwall of elbow body 1.
The width of the welding bead 2 of part in the inner part of elbow body 1 is 5mm, the welding bead 2 of the part in the outer part of elbow body 1
Width be 8.2mm, the thickness of the welding bead 2 of elbow body 1 is 2mm, and the welding bead 2 of heap postwelding is spiral against one another in levels
Shape.
The spiral angle of the welding bead 2 of heap postwelding is 1 °.
The material that bead welding 2 uses is wlding, and the material of wlding is corrosion-resistant or abrasion-resistant welding wire.
The material of wlding is rustless steel or nickel-bass alloy material.
The material of elbow body 1 is carbon steel.
The overlaying method of a kind of corrosion-resistant elbow, including spiral built-up welder, comprises the steps:
A, previous step: clean elbow body 1 inwall, and carry out polishing, polishing;
B, built-up welding: the elbow body 1 after polishing, polishing is carried out spiral overlaid with spiral butt welding machine.
The smoothness of the inwall of the elbow body 1 after sanding and polishing is Ra 3.8.
Embodiment 2: a kind of enhanced type elbow as shown in Figure 2, including elbow body 1, on the inwall of elbow body 1, heap is welded with
Coating.
Coating is made up of welding bead 2, and welding bead 2 heap in the shape of a spiral is welded on the inwall of elbow body 1.
The width of the welding bead 2 of part in the inner part of elbow body 1 is 5mm, the welding bead 2 of the part in the outer part of elbow body 1
Width be 10mm, the thickness of the welding bead 2 of elbow body 1 is 3.8mm, and the welding bead 2 of heap postwelding is spiral shell against one another in levels
Rotation shape.
The spiral angle of the welding bead 2 of heap postwelding is 1 °.
The material that bead welding 2 uses is wlding, and the material of wlding is corrosion-resistant or abrasion-resistant welding wire.
The material of wlding is rustless steel or nickel-bass alloy material.
The material of elbow body 1 is carbon steel.
The overlaying method of a kind of corrosion-resistant elbow, including spiral built-up welder, comprises the steps:
A, previous step: clean elbow body 1 inwall, and carry out polishing, polishing;
B, built-up welding: the elbow body 1 after polishing, polishing is carried out spiral overlaid with spiral butt welding machine.
The smoothness of the inwall of the elbow body 1 after sanding and polishing is Ra 4.2.
Embodiment 3: a kind of enhanced type elbow as shown in Figure 2, including elbow body 1, on the inwall of elbow body 1, heap is welded with
Coating.
Coating is made up of welding bead 2, and welding bead 2 heap in the shape of a spiral is welded on the inwall of elbow body 1.
The width of the welding bead 2 of part in the inner part of elbow body 1 is 6mm, the welding bead 2 of the part in the outer part of elbow body 1
Width be 8.75mm, the thickness of the welding bead 2 of elbow body 1 is 3.6mm, and the welding bead of heap postwelding 2 is in levels against one another
Helical form.
The spiral angle of the welding bead 2 of heap postwelding is 5 °.
The material that bead welding 2 uses is wlding, and the material of described wlding is corrosion-resistant or abrasion-resistant welding wire.
The material of wlding is rustless steel or nickel-bass alloy material.
The material of elbow body 1 is carbon steel.
The overlaying method of a kind of corrosion-resistant elbow, including spiral built-up welder, comprises the steps:
A, previous step: clean elbow body 1 inwall, and carry out polishing, polishing;
B, built-up welding: the elbow body 1 after polishing, polishing is carried out spiral overlaid with spiral butt welding machine.
The smoothness of the inwall of the elbow body 1 after sanding and polishing is Ra 5.4.
Embodiment 4: a kind of enhanced type elbow as shown in Figure 2, including elbow body 1, on the inwall of elbow body 1, heap is welded with
Coating.
Coating is made up of welding bead 2, and welding bead 2 heap in the shape of a spiral is welded on the inwall of elbow body 1.
The width of the welding bead 2 of part in the inner part of elbow body 1 is 8mm, the welding bead 2 of the part in the outer part of elbow body 1
Width be 10mm, the thickness of the welding bead 2 of elbow body 1 is 3mm, and the welding bead 2 of heap postwelding is spiral against one another in levels
Shape.
The spiral angle of the welding bead 2 of heap postwelding is 3 °.
The material that bead welding 2 uses is wlding, and the material of described wlding is corrosion-resistant or abrasion-resistant welding wire.
The material of wlding is rustless steel or nickel-bass alloy material.
The material of elbow body 1 is carbon steel.
The overlaying method of a kind of corrosion-resistant elbow, including spiral built-up welder, comprises the steps:
A, previous step: clean elbow body 1 inwall, and carry out polishing, polishing;
B, built-up welding: the elbow body 1 after polishing, polishing is carried out spiral overlaid with spiral butt welding machine.
The smoothness of the inwall of the elbow body 1 after sanding and polishing is Ra 2.4.
The foregoing is only preferred embodiment of the present utility model, those of ordinary skill in the art are not making creativeness
The every other embodiment obtained under work premise, all should belong to the scope of this utility model protection.
Claims (5)
1. an enhanced type elbow, including elbow body, it is characterised in that: on the inwall of described elbow body, heap is welded with coating,
Described coating is made up of welding bead, and described welding bead heap in the shape of a spiral is welded on the inwall of elbow body, the width of the welding bead of heap postwelding
For 5mm~10mm, the thickness of the welding bead of described heap postwelding is 2mm~4mm, the welding bead of described heap postwelding be levels against one another
Helical form.
A kind of enhanced type elbow the most according to claim 1, it is characterised in that: the spiral angle of the welding bead of described heap postwelding
It it is 1 °~5 °.
A kind of enhanced type elbow the most according to claim 1, it is characterised in that: the material that described bead welding uses is weldering
Material, the material of described wlding is corrosion-resistant or abrasion-resistant welding wire.
A kind of enhanced type elbow the most according to claim 2, it is characterised in that: the material of described wlding is rustless steel or nickel
Base alloy material.
A kind of enhanced type elbow the most according to claim 4, it is characterised in that: the material of described elbow body is carbon steel.