CN205836040U - Novel carbon fiber fabric shaping equipment - Google Patents
Novel carbon fiber fabric shaping equipment Download PDFInfo
- Publication number
- CN205836040U CN205836040U CN201620797347.8U CN201620797347U CN205836040U CN 205836040 U CN205836040 U CN 205836040U CN 201620797347 U CN201620797347 U CN 201620797347U CN 205836040 U CN205836040 U CN 205836040U
- Authority
- CN
- China
- Prior art keywords
- roller
- fabric
- resin layer
- carbon fiber
- shaping equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
This utility model provides a kind of novel carbon fiber fabric shaping equipment, upper surface at carbon fibre fabric adds more than one layer thin resin layer with more than one in lower surface, by the adhesion after resin melting, mutually will bond between carbon fibre fabric fiber and fiber, realize the sizing of carbon fibre fabric, and by thin resin layer or make during paving self-adhesion between carbon fibre fabric by hot blast simultaneously.This kind of novel carbon fiber fabric shaping equipment, it is possible to increase the mould paving performance of fabric and efficiency, simultaneously, owing to being extraneous interpolation thin resin layer rather than directly fiber processed or use sizing fiber, it is ensured that produce simplification, reduce production cost, can beneficially produce in enormous quantities.
Description
Technical field
This utility model relates to a kind of novel carbon fiber fabric shaping equipment.
Background technology
Along with the development in epoch, what carbon fibre composite was the widest is applied to various field, including space flight and aviation, ferrum
The fields such as road traffic, automobile, Leisure Sports.At present, in order to reduce manufacturing cost, carbon fibre composite industry is advocated and is used liquid
Body formed technique (including RTM, VARI etc.) produces product, this would is that after the main flow molding work of carbon fibre composite industry
One of skill.
In general, liquid molding process is directly to use carbon fibre fabric as matrix, then irrigates resin, makes resin
Infiltration carbon fibre fabric post-heating solidification.But carbon fibre fabric is due to the flexibility of carbon fiber itself and fabric structure
Reason, be frequently present of certain problem when directly using, that causes that paving operates is highly difficult, have impact on the life of subsequent product
Produce efficiency, the fiber glacing flatness of the fabric that is the most relatively hard to keep and cannot directly paving at die surface (need to be by spray) etc..
Because carbon fibre composite has strict anisotropic characteristic, so above-mentioned operational issue results in material and cannot send out
Wave optimal performance, have impact on product quality.
It addition, traditional fabric method for shaping is all carbon fiber to carry out pretreatment make fabric or shuffling sizing fibre again
Dimension, these sizing modes the most all exist loses time or the problem of subsequent operation difficulty, have impact on product from another point of view
Production efficiency.
Therefore to keep the fiber glacing flatness of fabric in process of production and meet the requirement producing product in enormous quantities,
It is necessary to study a kind of novel carbon fibre fabric shaping equipment.
Utility model content
The purpose of this utility model is to provide a kind of novel carbon fiber fabric shaping equipment and solves present in prior art
In production process fabric lines distortion, follow-up paving operating difficulties and cannot high efficiency produce in enormous quantities product problem.
Technical solution of the present utility model is:
A kind of novel carbon fiber fabric shaping equipment, adds assembly, heating roller, cooling group including setting gradually thin resin layer
Part and for receiving the wind-up roll of pattern bonded fabrics, thin resin layer is added assembly and is used for adding under room temperature resin for powdery
Dusting roller or for adding under room temperature the sprinkler of resin for liquid, the left roller of dusting that dusting roller includes being arranged in order setting and
The powder groove being jointly arranged over for accommodating under room temperature the resin being powdery of the right roller of dusting, the left roller of dusting and the right roller of dusting,
Heating roller includes being arranged above and below roller and heating lower roll in the heating arranged, and cooling assembly uses coldplate or chill roll.
Further, it is provided with for the carbon fiber after adding thin resin layer is knitted between thin resin layer interpolation assembly and heating roller
Thing carries out baking oven or the heating plate heated, and is additionally provided with protection material unwinding roller between heating roller and chill roll.
Further, novel carbon fiber fabric shaping equipment is located at the discharging opening of loom, or the sizing of novel carbon fiber fabric
The feed end of device is provided with emptying roller.
A kind of novel carbon fiber fabric setting process, the upper surface at carbon fibre fabric adds with more than one in lower surface
Add more than one layer thin resin layer, by the adhesion after resin melting, mutually will bond between carbon fibre fabric fiber and fiber,
Realize the sizing of carbon fibre fabric, and by thin resin layer or simultaneously by hot blast make during paving carbon fibre fabric it
Between self-adhesion;Particularly as follows:
The composition of the molding resin thin layer of S1, the structure of design typification fabric and pattern bonded fabrics;
S2, carbon fibre fabric is imported the novel carbon fiber fabric shaping equipment described in any of the above-described item;
S3, by shaping equipment the surface of carbon fibre fabric add one layer or the thin resin layer of two-layer;
S4, the carbon fibre fabric that with the addition of thin resin layer is heated and pressurized treatments;And gluing according to thin resin layer
Property size, select add or without protection material;
S5, cool down and shape add thin resin layer carbon fibre fabric, obtain pattern bonded fabrics;Correction rolling gained sizing is knitted
Thing.
Further, carbon fibre fabric uses carbon fiber one-way fabric, plain cloth, twills, satin fabric, warp knit
Fabric, carbon fiber and the one in other fiber blended fabric, the fiber areal densities of carbon fibre fabric is 75 ~ 1500gsm.
Further, in novel carbon fiber fabric shaping equipment, thin resin layer adds assembly on the surface of carbon fibre fabric
Adding thin resin layer, then the carbon fibre fabric after adding thin resin layer is heated by heating roller, then by cooling assembly to adding
Add the carbon fibre fabric of thin resin layer to carry out cooling and shaping and obtain pattern bonded fabrics, then by wind-up roll, gained pattern bonded fabrics has been carried out
Rolling.
Further, the mode that thin resin layer is added to carbon fibre fabric surface determines to adopt according to resin form under room temperature
Carrying out dusting with dusting roller or sprinkler sprays, the surface density of thin resin layer accounts for the 2% of whole pattern bonded fabrics total areal density
~10%。
Further, the surface density of thin resin layer accounts for the 2.5% ~ 4% of whole pattern bonded fabrics total areal density.
Further, during the resin in thin resin layer uses epoxy resin, bimaleimide resin, phenolic resin
Kind.
Further, in step S4, selecting the protection material added is one or both combinations in kraft paper and PE film.
This kind of novel carbon fiber fabric shaping equipment, adds one layer or two layers of resin thin layer on carbon fibre fabric surface, logical
Cross resin melting after adhesion, will mutually bond between fiber and fiber, thus play styling.Meanwhile, resin is passed through
The character of thin layer, makes with self-adhesion, or just mutually to bond by hot blast between fabric during paving.This technique, if
Meter fabric face thin resin layer, including the number of plies and composition, determines in the way of fabric face adds thin resin layer by this, according to knitting
The fiber areal densities of thing and resinous type select to use single-layer resin thin layer or two-sided thin resin layer;And according to thin resin layer
Viscosity size, the optional protection material that adds, the protection material of optional interpolation is one or both in kraft paper and PE film
Combination.
This kind of novel carbon fiber fabric shaping equipment, carbon fibre fabric lead-in mode can be to take off-line or online two kinds of sides
Formula: the first is directly to be imported carbon fibre fabric finished product by emptying roller;The second, for being connected on outside shaping equipment on loom, will be knitted
Thing carries out heat treatment before rolling.In this kind of novel carbon fiber fabric shaping equipment, deviation correcting device during fabric rolling, is used to protect
Card pattern bonded fabrics rolling is neat, can use actively rolling or passive rolling.
In this kind of novel carbon fiber fabric shaping equipment, the resinous type of the thin resin layer of interpolation is epoxy resin, span
One in bismaleimide resin, phenolic resin.Resin state at room temperature can be powder particle or resin solution, by setting
Fat type decided.The mode adding thin resin layer on carbon fibre fabric surface uses sprinkling or dusting, and concrete mode is according to resin
Form determines.The surface density of thin resin layer accounts for the 2% ~ 10% of whole pattern bonded fabrics total areal density, and preferably 2.5% ~ 4%.
In this kind of novel carbon fiber fabric shaping equipment, the temperature that the fabric that with the addition of thin resin layer is heated up to
60~200℃.Actual temp determines according to solvent species in the fusing point of toner or resin solution and speed of production.Should
In kind of novel carbon fiber fabric shaping equipment, the form of fabric heating pressurization can be used after first heated plate or baking oven baking again
Pressurize with running roller, or directly use heating roller heating pressurization.
The beneficial effects of the utility model are, this kind of carbon fibre fabric shaping equipment, have the advantage that
One, processing through this device, the fixed effect of fabric is excellent, and the fabric that heat treatment is crossed will not go out during using
The phenomenon of existing torsion of fibers deformation, it is ensured that the optimal performance of material.
Two, with self-adhesion, or just can mutually can bond by hot blast between fabric during paving.Reduce use process
In operating difficulties, improve production efficiency.
Three, in pattern bonded fabrics, thin resin layer content is low, and resinous type is fitted with follow-up use resin-phase, does not interferes with material
Performance.
Four, whole heat treatment process operation is simple and efficient, conveniently carries out the mass disposal of fabric, improves follow-up
Production efficiency, greatly reduce production cost.
Accompanying drawing explanation
Fig. 1 is the structural representation of double-side shaping fabric in this utility model embodiment one.
Fig. 2 is process units and the process schematic of double-side shaping fabric in embodiment one.
Fig. 3 is the structural representation of one side pattern bonded fabrics in embodiment two.
Fig. 4 is process units and the process schematic of one side pattern bonded fabrics in embodiment two.
Wherein: 11, ground floor thin resin layer;12, carbon fiber warp-knitting fabric;13, second layer thin resin layer.
21, emptying roller;22, powder groove;23, dusting roller;24, heating roller;25, coldplate;26, wind-up roll.
31, kraft paper;32, epoxy resin thin layer;33, carbon fiber one-way fabric.
41, loom;42, equipped with the sprinkler of epoxy resin solution;43, baking oven;44, heating roller;45, kraft paper unreels
Roller;46, chill roll;47, wind-up roll.
Detailed description of the invention
Describe preferred embodiment of the present utility model below in conjunction with the accompanying drawings in detail.
A kind of novel carbon fiber fabric shaping equipment, such as Fig. 2, Fig. 4, adds assembly including setting gradually thin resin layer, adds
Hot-rolling 24,44, cooling assembly and for receiving the wind-up roll 26,47 of pattern bonded fabrics, thin resin layer is added assembly and is used for adding
Add under room temperature the dusting roller 23 of the resin being powdery or for adding under room temperature the sprinkler 42 of the resin being liquid, dusting roller 42
Including being jointly arranged over for accommodating of the left roller of the dusting being arranged in order setting and the right roller of dusting, the left roller of dusting and the right roller of dusting
Being the powder groove 22 of the resin of powdery under room temperature, heating roller 24,44 includes being arranged above and below roller and heating lower roll in the heating arranged,
Cooling assembly uses coldplate 25 or chill roll 46.
It is provided with for the carbon fibre fabric after adding thin resin layer is carried out between thin resin layer interpolation assembly and heating roller 44
The baking oven 43 of heating, is additionally provided with protection material unwinding roller between heating roller 44 and chill roll 46.Novel carbon fiber fabric shaping equipment
It is located at the discharging opening of loom, or the feed end of novel carbon fiber fabric shaping equipment is provided with emptying roller.
This kind of novel carbon fiber fabric shaping equipment, by using thin resin layer to add assembly, it is possible to realize at carbon fiber
Add thin resin layer outside fabric, and by heating roller 24,44 or baking oven 43, the carbon fibre fabric after adding thin resin layer is carried out
Heating, so that the adhesion that the resin after Tian Jiaing is the most each other, mutually will bond between fiber and fiber, thus
Play styling.This device can make with self-adhesion, or can to borrow between fabric during paving by the character of thin resin layer
Help hot blast just can play the effect of mutually bonding, improve mould paving performance and the efficiency of fabric.This kind of novel carbon fiber is knitted
Thing shaping equipment, reasonable in design, low cost, it is possible to solve the problem that in existing shaping equipment, structure is complicated, cost is high,
The efficiency that simultaneously solves to shape present in existing shaping equipment is low, the unconspicuous problem of fixed effect.
The carbon fibre fabric shaping equipment of embodiment, the fabric processed has at least double-layer structure, on the surface of fabric
Cover one layer or two layers of resin thin layer, by this resin adhesion the most each other, by phase between fiber with fiber
Bonding mutually, thus play styling.The method by the character of thin resin layer, make to can between fabric during paving from
Viscous, or the effect mutually bondd just can be played by hot blast, improve mould paving performance and the efficiency of fabric.Meanwhile, by
Then the external world adds thin resin layer rather than directly processes fiber or use sizing fiber, it is ensured that produce simplification,
Reduce production cost, can beneficially produce in enormous quantities.
Embodiment 1
According to pattern bonded fabrics structural representation, such as Fig. 1, describe embodiment 1 in detail.
According to design, in order to ensure fixed effect, carbon fiber warp-knitting fabric 12 of shaping, need according to three as shown in Figure 1
Rotating fields carries out heat treatment, including ground floor thin resin layer 11, carbon fiber warp-knitting fabric 12 and second layer thin resin layer 13.
Wherein, carbon fibre fabric 12 is the carbon fiber warp-knitting fabric of fiber areal densities 900 gsm.
Wherein, ground floor thin resin layer 11 and second layer thin resin layer 13 are bimaleimide resins.Set at 110 DEG C
The viscosity of fat is 5000 Pa.s.The surface density of every layer of thin layer is 12gsm.
Implement process as follows:
The carbon fiber warp-knitting fabric 12 wound by emptying roller 21 can be through the powder equipped with span imide resin powder
The bottom of groove 22, through the turning effort of dusting roller 23, is sprinkling upon the surface of carbon fiber warp-knitting fabric 12 uniformly by powder.Pass through
The temperature 60 ~ 200 DEG C that heating roller 24 provides, is fixed on carbon fiber firmly by thin resin layer by preferably 130 DEG C and pressure such as 200N
The surface of WARP-KNITTING 12.Then unreeled by release paper, with one group of press bonding roller, release paper is added on fabric face.Warp after
After being rectified a deviation by deviation correcting device after supercooling plate 25, by the pattern bonded fabrics of wind-up roll 26 rolling double-layer structure.Speed of production is 4m/
min。
In order to ensure double-side shaping, the double-layer structure pattern bonded fabrics wound is unreeled again, add resin at reverse side thin
Layer, parameter is consistent with the above.
After testing, embodiment one gained pattern bonded fabrics surface viscosity is less, and in pattern bonded fabrics, the collimation deviation of fiber is
1%.Paving pattern bonded fabrics, during flat plate mold, after pattern bonded fabrics laying well rear electricity consumption blowing 30s, presses with hands
After, fabric can be pasted at die surface.Through checking without obvious hole after using the solidification of RTM technique, mechanical property reaches requirement.
Embodiment 2
According to pattern bonded fabrics structural representation, such as Fig. 3, describe embodiment 2 in detail.
According to design, in order to ensure fixed effect, carbon fiber one-way fabric of shaping, need according to three layers as shown in Figure 3
Structure carries out heat treatment, including kraft paper 31, thin resin layer 32 and carbon fiber one-way fabric 33.
Wherein, carbon fiber one-way fabric 33 is the carbon fiber one-way fabric of fiber areal densities 160 gsm.
Wherein, thin resin layer 32 is epoxy resin, and at 90 DEG C, the viscosity of resin is 50 Pa.s.The face of thin resin layer is close
Degree is 5gsm.
Implement process as follows:
By external for shaping equipment loom 41, the most woven carbon fiber one-way fabric 33 runs past equipped with asphalt mixtures modified by epoxy resin liposoluble
The bottom of the sprinkler 42 of liquid, is sprinkled upon carbon fiber one-way fabric 33 surface uniformly by sprinkler by resin solution.By drying
The temperature such as 80 DEG C that case 43 provides, vapors away the solvent in solution, makes thin resin layer 32 paste at fabric face.Through heating
Thin resin layer is the most uniformly fixed on carbon fiber one-way fabric 33 surface by temperature such as 40 DEG C and pressure 250N that roller 44 provides.
Then kraft paper let off roll 45 releases kraft paper 31, and kraft paper 31 on carbon fiber one-way fabric 33 covers, through chill roll 46
Cooling and shaping, finally by wind-up roll 47 rolling.Speed of production is 3m/min.
After testing, embodiment two gained pattern bonded fabrics surface viscosity is big, by the isolation of kraft paper 31, and will not between fabric
Mutually bonding, convenient use.In fabric, the collimation deviation of fiber is 1%.Paving pattern bonded fabrics during flat plate mold,
Directly fabric can be coated with at die surface.Through checking without obvious hole after using the solidification of RTM technique, mechanical property reaches to want
Ask.
The novel pattern bonded fabrics production technology of embodiment one, two, key point is to have abandoned traditional setting process to fiber
Carry out pretreatment or shuffling sizing fiber way, novelty be cladded with thin resin layer 33, tried hard to keep by the bonding between resin
The glacing flatness of card fabric fibre.During production, first according to the pattern bonded fabrics structure of design select to add thin resin layer 33 quantity and
Mode, then adds thin resin layer 33 by fabric face, reheats pressurized treatments, finally obtains the pattern bonded fabrics of needs.Simultaneously
In order to ensure the cleanliness factor on pattern bonded fabrics surface, eliminate the phenomenon of bonding between fabric, and ensure paving performance when using,
Covered plus protection material for pattern bonded fabrics before fabric rolling.
The technique of embodiment one, two is applicable to the heat treatment of carbon fibre fabric, solves existing direct use carbon fiber
Fibre deformation, paving complex operation and the problem of complicated die paving difficulty occurred in fabric, also solve cannot be big simultaneously
The problem that batch carries out carbon fibre fabric heat treatment.
Above-described instantiation is intended merely to describe this utility model in detail, but of the present utility model not damaging
In the case of objective and scope, various change, amendment can be carried out.It is new that these changes and improvement both fall within this practicality claimed
In the range of type, this utility model claims scope appended claims and equivalent defines.
Claims (3)
1. a novel carbon fiber fabric shaping equipment, it is characterised in that: include that setting gradually thin resin layer adds assembly, heating
Roller, cooling assembly and the wind-up roll for rolling pattern bonded fabrics, thin resin layer is added assembly and is used for adding under room temperature as powder
The dusting roller of the resin of shape or for adding under room temperature the sprinkler of the resin for liquid, dusting roller includes being arranged in order setting
Jointly being arranged over for accommodating under room temperature for the resin of powdery of the left roller of dusting and the right roller of dusting, the left roller of dusting and the right roller of dusting
Powder groove, heating roller includes being arranged above and below roller and heating lower roll in the heating arranged, and cooling assembly uses coldplate or cooling
Roller.
2. novel carbon fiber fabric shaping equipment as claimed in claim 1, it is characterised in that: thin resin layer is added assembly and is added
The baking oven for the carbon fibre fabric after adding thin resin layer is heated or heating plate, heating roller and cooling it is provided with between hot-rolling
Protection material unwinding roller it is additionally provided with between roller.
3. novel carbon fiber fabric shaping equipment as claimed in claim 1 or 2, it is characterised in that: described novel carbon fiber is knitted
The discharging opening of loom is located at by thing shaping equipment, or the feed end of novel carbon fiber fabric shaping equipment is provided with emptying roller.