CN205687853U - Graphene modified waterborne epoxy heavy-duty antiseptic paint - Google Patents
Graphene modified waterborne epoxy heavy-duty antiseptic paint Download PDFInfo
- Publication number
- CN205687853U CN205687853U CN201620478566.XU CN201620478566U CN205687853U CN 205687853 U CN205687853 U CN 205687853U CN 201620478566 U CN201620478566 U CN 201620478566U CN 205687853 U CN205687853 U CN 205687853U
- Authority
- CN
- China
- Prior art keywords
- paint
- primer
- epoxy
- thickness
- modified waterborne
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of Graphene modified waterborne epoxy heavy-duty antiseptic paint, aim to provide a kind of antiseptic property excellent, base material adhesive force is strong, pliability and resistance to impact are good, hardness is high, crocking resistance is excellent, the coating structure that salt fog resistance is excellent, its drip irrigation device is, including the priming paint set gradually, intermediate coat and finish paint, priming paint includes epoxy iron red shop primer, zinc oxide anti-corrosive primer, phosphomolybdic acid yellow zinc chromate primer paint, intermediate coat includes graphene sheet layer floating coating, micaceous iron oxide floating coating, finish paint is water-base epoxy antisepsis finishing paint, this coating does not contains Pb, Sb, Hg, the poisonous heavy iron and steel such as Cr, environmental friendliness, meet European Union's ROSE environmental protection standard.
Description
Technical field
This utility model relates to the laminar product field with special nature or special surface characteristic, particularly to a kind of graphite
Alkene modified waterborne epoxy heavy-duty antiseptic paint.
Background technology
From carried of crude oil, store transfer, pipeline transportation, oil refining produce the storage of product oil, be required for building a large amount of storage
Tank, the coating of reservoir walls needs to tackle various types of oil product, such as crude oil, semi-finished product oil, product oil and solvent
Deng, and storage tank outer wall needs to keep out ultraviolet and various industry and the erosion of marine corrosion environment.
At present, corrosion-inhibiting coating structure on the market is a lot, but the most all can have the poisonous heavy steel such as Pb, Sb, Hg, Cr
Ferrum, does not meets European Union's ROSE environmental protection standard, to environment.
Utility model content
The purpose of this utility model is to provide a kind of Graphene modified waterborne epoxy heavy-duty antiseptic paint, and it is excellent that it has antiseptic property
Different, base material adhesive force is strong, and pliability and resistance to impact are good, and hardness is high, and crocking resistance is excellent, excellent salt fog resistance, construction
The advantages such as strong adaptability.
Above-mentioned technical purpose of the present utility model has the technical scheme that
A kind of Graphene modified waterborne epoxy heavy-duty antiseptic paint, including the priming paint set gradually, intermediate coat and finish paint, the described end
Enamel-cover includes epoxy iron red shop primer, zinc oxide anti-corrosive primer, phosphomolybdic acid yellow zinc chromate primer paint, and described intermediate coat includes being coated with in graphene sheet layer
Paint, micaceous iron oxide floating coating, described finish paint is water-base epoxy antisepsis finishing paint.
Arrange further: the thickness of described epoxy iron red shop primer is 70 μm, and the thickness of zinc oxide anti-corrosive primer is 100 μm,
The thickness of phosphomolybdic acid yellow zinc chromate primer paint is 125 μm, thickness 125 μm of epoxy iron red shop primer.
Arrange further: the thickness of described graphene sheet layer floating coating is 120 μm, and the thickness of micaceous iron oxide floating coating is
80μm。
Arrange further: described water-base epoxy antisepsis finishing paint dry thickness 80 μm.
In sum, this utility model has the advantages that graphene sheet layer improves anticorrosion with coat: have physics to prevent
Corruption and some chemical preservation multiple action.
The conjugated structure of graphene sheet layer, is layering in the coating and forms fine and close thermal insulation layer, intercepts moisture to film
Infiltration and infiltration, play physical preservation effect, graphenic surface hydrophobic property strengthens moisture penetration.
Anticorrosion mechanism: iron and steel ground anode reaction makes Fe lose electronics to be progressively corroded, and the electric conductivity of Graphene makes it
Promptly the electronics that Fe in anode reaction loses can be transmitted to coating surface, stop Fe → Fe3+ reaction, prevent rust from generating
Corrode；
Phosphomolybdic acid yellow zinc chromate primer paint plays the effect of stable rust.
Anticorrosion mechanism: phosphomolybdic acid zinc occurs chemical complexing with coated article top layer, forms insoluble passivating film, suppresses environment pair
The corrosion of metal substrate；
Zinc oxide anti-corrosive primer has the incomparable new capability of general zinc oxide and new application, and coating can be made to have shielding
Ultraviolet, absorption infrared ray and fungus and mildew resistance effect；
It is essential that this coating is without the poisonous heavy iron and steel such as Pb, Sb, Hg, Cr, environmental friendliness, meet European Union's ROSE environmental protection
Standard.
Accompanying drawing explanation
Fig. 1 is embodiment 1 structural representation；
In figure, 1, base material；2, epoxy iron red shop primer；3, zinc oxide anti-corrosive primer；4, phosphomolybdic acid yellow zinc chromate primer paint；5, graphene film
Layer floating coating；6, micaceous iron oxide floating coating；7, water-base epoxy antisepsis finishing paint.
Detailed description of the invention
Below in conjunction with accompanying drawing, this utility model is described in further detail.
Embodiment 1: a kind of Graphene modified waterborne epoxy heavy-duty antiseptic paint, as it is shown in figure 1, what base material 1 surface set gradually
Priming paint, intermediate coat and finish paint, priming paint includes epoxy iron red shop primer 2, zinc oxide anti-corrosive primer 3, phosphomolybdic acid yellow zinc chromate primer paint 4, intermediate coat
Including graphene sheet layer floating coating 5, micaceous iron oxide floating coating 6, finish paint is water-base epoxy antisepsis finishing paint 7.
The manufacture method of coating structure, base material 1 surface elder generation spray-applied primer, each priming paint sprays successively, and the thickness of priming paint is respectively
For: the thickness of epoxy iron red shop primer 2 is 70 μm, and the thickness of zinc oxide anti-corrosive primer 3 is 100 μm, the thickness of phosphomolybdic acid yellow zinc chromate primer paint 4
It is 125 μm.
In above-mentioned priming paint, epoxy iron red shop primer 2 has excellent antirust, water resistance and resistance to chemical corrosion, film
Fast drying, adhesive force is good；Zinc oxide anti-corrosive primer 3 is mainly used in the antirust bottoming of petrochemical plant outer wall, has metallic luster,
Chemical property torpescence, is difficult to work with medicines such as acid, alkali, resistance to chemical attack；Phosphomolybdic acid yellow zinc chromate primer paint 4 has stable rust
Effect.
After spray-applied primer, spraying intermediate coat further, in intermediate coat, the thickness of graphene sheet layer floating coating 5 is 120
μm, the thickness of micaceous iron oxide floating coating 6 is 80 μm.
In above-mentioned intermediate coat, graphene sheet layer improves anticorrosion with coat: have physical preservation and the point many recasts of chemical preservation
With；Micaceous iron oxide floating coating 6 has the shielding properties of uniqueness, pigment part oriented parallel overlapping arrangement of energy, forms " fish scale "
As bridging arrangement, therefore, film has excellent impermeabilisation, protection against the tide, antirust, resistance to chemical corrosion.
Last spray paint, water-base epoxy antisepsis finishing paint 7 dry thickness 80 μm.
Above-mentioned water-base epoxy antisepsis finishing paint 7 has ceramic tile glossy surface, and the paint film of formation is hard, wear-resisting, and color and luster is plentiful
Advantage, the corrosion of the chemical substances such as water-fast, oil resistant, acidproof alkali salt.
Above-mentioned Graphene modified waterborne epoxy heavy-duty antiseptic paint has excellent physical property and excellent chemical-resistant,
Particularly salt fog resistance, paint film tough and hard wear resistant, adhesive force is strong, and construction adaptability is strong, has the good feature of environmental protection.
Above-mentioned Graphene modified waterborne epoxy heavy-duty antiseptic paint can be used for C4 environment, even C5 environment.Especially rail vehicle,
The application such as engineering machine ring, LHG vehicle and storage tank, truck and bus.
The above embodiments are only that it is not to restriction of the present utility model, ability to explanation of the present utility model
The present embodiment can be made after reading this specification by field technique personnel as required does not has the amendment of creative contribution, but
As long as all being protected by Patent Law in right of the present utility model.
Claims (4)
1. a Graphene modified waterborne epoxy heavy-duty antiseptic paint, it is characterised in that: include priming paint, the intermediate coat dough-making powder set gradually
Paint, described priming paint includes epoxy iron red shop primer (2), zinc oxide anti-corrosive primer (3) and phosphomolybdic acid yellow zinc chromate primer paint (4), described intermediate coat
Including graphene sheet layer floating coating (5), micaceous iron oxide floating coating (6), described finish paint is water-base epoxy antisepsis finishing paint (7).
Graphene modified waterborne epoxy heavy-duty antiseptic paint the most according to claim 1, it is characterised in that: at the bottom of described epoxy iron red shop
The thickness of paint (2) is 70 μm, and the thickness of zinc oxide anti-corrosive primer (3) is 100 μm, and the thickness of phosphomolybdic acid yellow zinc chromate primer paint (4) is 125 μ
m。
Graphene modified waterborne epoxy heavy-duty antiseptic paint the most according to claim 2, it is characterised in that: described graphene sheet layer
The thickness of floating coating (5) is 120 μm, and the thickness of micaceous iron oxide floating coating (6) is 80 μm.
Graphene modified waterborne epoxy heavy-duty antiseptic paint the most according to claim 3, it is characterised in that: described water-base epoxy is prevented
Rotten finish paint (7) dry thickness 80 μm.