CN205443159U - Yoga mat - Google Patents
Yoga mat Download PDFInfo
- Publication number
- CN205443159U CN205443159U CN201620177167.XU CN201620177167U CN205443159U CN 205443159 U CN205443159 U CN 205443159U CN 201620177167 U CN201620177167 U CN 201620177167U CN 205443159 U CN205443159 U CN 205443159U
- Authority
- CN
- China
- Prior art keywords
- silica gel
- gel layer
- glue film
- face
- yoga mat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a yoga mat, include by the last face glue film (1) that sets gradually under to, foaming silica gel layer one (2), substrate (3), foaming silica gel layer two (4) and limited slip glue film (5), during preparation, to join in marriage good face glue film sizing material coats in forming face glue film (1) from type paper or from the epimembranal vulcanization of type, join in marriage a good foaming silica gel layer sizing material laminate substrate (3) that coat on face glue film (1), to join in marriage good limited slip glue film sizing material coats in obtaining the substrate face from type paper or from the epimembranal and vulcanization of type, to join in marriage good two sizing material on the foaming silica gel layer coats on limited slip glue film (5) silica gel face, laminating substrate face, the utility model discloses a yoga mat material compressing deformation is little, the resilience good, environmental protection, nontoxic, free from extraneous odour, resistant dirtyly, hydrophobic, water -fast separate, ageing -resistant, gentle and agreeable, the anti book, can regard as the use of baby crawling pad material. Preparation method is simple, safety, environmental protection, easily realize industrialization continuous production.
Description
Technical field
This utility model relates to a kind of Novel yoga cushion material and preparation method thereof, belongs to technical field of synthetic leather.
Background technology
The mat underlayed when Yoga mat is as exercise Yoga is widely used by people.On market, the main material of Yoga mat has PVC, EVA, TPE tri-kinds.Wherein, PVC material: have abnormal flavour, skid resistance, heat stability and actinic difference, the harmful substances such as two English and hydrogen chloride can be produced during waste products burn processing；EVA material: belong to rigid foam, belongs to low side Yoga mat raw material, and majority is used in manufacture sole, and abnormal smells from the patient is heavier, and elasticity is the best, and skidproof effect is poor；TPE material: the at present the most high-grade articles for use of Yoga mat product, but its compression, elastic recovery, durability, thermostability and actinic poor.
Utility model content
This utility model for the deficiency of the problems referred to above, proposes a kind of Yoga mat, Yoga mat compression is little, resilience good for this, environmental protection, nontoxic, free from extraneous odour, resistant, hydrophobic, hydrolysis, folding ageing-resistant, submissive, anti-, it is possible to as baby crawling pad materials'use.And preparation method is simple, safe and environment-friendly, easily realize industrialization produces continuously.
This utility model is that the technical scheme solving the proposition of above-mentioned technical problem is:
A kind of Yoga mat, including the face glue-line (1) set gradually from top to bottom, foamed silica gel layer one (2), base material (3), foamed silica gel layer two (4) and on-slip glue-line (5).
Preferred: described glue-line (1), foamed silica gel layer one (2), base material (3), foamed silica gel layer two (4) and on-slip glue-line (5) composite joint successively are together.
Preferred: the thickness of described base material (3) is 0.01-3mm.
Preferred: the raw materials used each Composition Weight Parts proportioning of described glue-line one (1) is as follows:
First vinyldimethicone 40～70 parts
First filler 20～50 parts
First platinum catalyst 0.01～0.5 part
First inhibitor 0.001～0.1 part
First containing hydrogen silicone oil 1～10 parts
First color 1～10 parts.
Wherein, described first vinyldimethicone is at least to contain the polydimethylsiloxane that two vinyls are joined directly together with silicon atom at the end of the chain or chain side.
Described first filler can be one or more the mixture in white carbon, organic siliconresin, silicon powder, calcium carbonate, aluminium oxide, magnesium oxide, Graphene.
Described first platinum catalyst is isopropyl alcohol solution of chloroplatinic acid or chloroplatinic acid tetrahydrofuran solution or chloroplatinic acid-1,3,5,7-tetravinyl-1,3,5,7-tetramethyl-cyclotetrasiloxane or chloroplatinic acid-divinyl tetramethyl disiloxane.
Described first inhibitor is methyl butynol or ethynylcyclohexanol or the maleic acid containing alkynyl and derivant thereof or many vinyl polysiloxane.
Described first containing hydrogen silicone oil is the polydimethylsiloxane that at least three hydrogen atom is directly connected with silicon, and hydrogen atom content accounts for the 0.1～1.6% of raw material.
Described first color is the pigment with vinyldimethicone as disperse medium.
Preferred: described foamed silica gel layer one (2) and the raw materials used each Composition Weight Parts proportioning of foamed silica gel layer two (4) are as follows:
Second vinyldimethicone 40～70 parts
Second filler 20～50 parts
Second platinum catalyst 0.01～0.5 part
Second inhibitor 0.001～0.1 part
Second containing hydrogen silicone oil 1～10 parts
Second color 0～10 parts
Foaming agent 2～10 parts.
Wherein, described second vinyldimethicone is at least to contain the polydimethylsiloxane that two vinyls are joined directly together with silicon atom at the end of the chain or chain side.
Described second filler can be one or more the mixture in white carbon, organic siliconresin, silicon powder, calcium carbonate, aluminium oxide, magnesium oxide, Graphene.
Described second platinum catalyst is isopropyl alcohol solution of chloroplatinic acid or chloroplatinic acid tetrahydrofuran solution or chloroplatinic acid-1,3,5,7-tetravinyl-1,3,5,7-tetramethyl-cyclotetrasiloxane or chloroplatinic acid-divinyl tetramethyl disiloxane.
Described second inhibitor is methyl butynol or ethynylcyclohexanol or the maleic acid containing alkynyl and derivant thereof or many vinyl polysiloxane.
Described second containing hydrogen silicone oil is the polydimethylsiloxane that at least three hydrogen atom is directly connected with silicon, and hydrogen atom content accounts for the 0.1～1.6% of raw material.
Described second color is the pigment with vinyldimethicone as disperse medium.
Preferred: described foaming agent is foam powder or cenosphere.
Preferred: each Composition Weight Parts proportioning that described on-slip glue-line (5) is raw materials used is as follows:
Trivinyl polydimethylsiloxane 40～70 parts
3rd filler 20～50 parts
3rd platinum catalyst 0.01～0.5 part
3rd inhibitor 0.001～0.1 part
3rd containing hydrogen silicone oil 1～10 parts
Tertiary color cream 1～10 parts.
Wherein, described trivinyl polydimethylsiloxane is at least to contain the polydimethylsiloxane that two vinyls are joined directly together with silicon atom at the end of the chain or chain side.
Described 3rd filler can be one or more the mixture in white carbon, organic siliconresin, silicon powder, calcium carbonate, aluminium oxide, magnesium oxide, Graphene.
Described 3rd platinum catalyst is isopropyl alcohol solution of chloroplatinic acid or chloroplatinic acid tetrahydrofuran solution or chloroplatinic acid-1,3,5,7-tetravinyl-1,3,5,7-tetramethyl-cyclotetrasiloxane or chloroplatinic acid-divinyl tetramethyl disiloxane.
Described 3rd inhibitor is methyl butynol or ethynylcyclohexanol or the maleic acid containing alkynyl and derivant thereof or many vinyl polysiloxane.
Described 3rd containing hydrogen silicone oil is the polydimethylsiloxane that at least three hydrogen atom is directly connected with silicon, and hydrogen atom content accounts for the 0.1～1.6% of raw material.
Described tertiary color cream is the pigment with vinyldimethicone as disperse medium.
Preferred: described base material (3) is any in super fine, the glass of chemistry super fine, cotton, numb, paper, metal or two or more mixture.
The preparation method of a kind of Yoga mat, it is characterised in that comprise the following steps:
A. the face glue-line sizing material prepared is coated on release paper or mould release membrance, vulcanizes 3～10 minutes at a temperature of 80～180 DEG C, form face glue-line (1).
B. bubble layer of silica gel one sizing material is allotted by each Composition Weight Parts proportioning of the raw material of foamed silica gel layer one (2), foamed silica gel layer one sizing material prepared is coated on the face glue-line (1) that step a is cured, laminating base material (3), vulcanize 3～20 minutes at a temperature of 80～180 DEG C, peel off release paper or mould release membrance, obtain leather substrate face.
C. join on-slip glue-line sizing material by each Composition Weight Parts proportioning of the raw material of on-slip glue-line (5), the on-slip glue-line sizing material prepared is coated on release paper or mould release membrance, vulcanize 3～10 minutes at a temperature of 80～180 DEG C.
D. bubble layer of silica gel two sizing material is allotted by each Composition Weight Parts proportioning of the raw material of foamed silica gel layer two (4), foamed silica gel layer two sizing material prepared is coated on on-slip glue-line (5) the silica gel face that step c is cured, the substrate surface of laminating leather obtained by step b, vulcanize 3～20 minutes at a temperature of 80～180 DEG C, peel off release paper or mould release membrance, can be prepared by Yoga mat.
A kind of Yoga mat of the present utility model, compared to existing technology, has the advantages that
Yoga mat includes face glue-line (1), foamed silica gel layer one (2), base material (3), foamed silica gel layer two (4) and the on-slip glue-line (5) set gradually from top to bottom, therefore its compression is little, resilience good, environmental protection, nontoxic, free from extraneous odour, resistant, hydrophobic, hydrolysis, folding ageing-resistant, submissive, anti-, can be as baby crawling pad materials'use.And preparation method is simple, safe and environment-friendly, easily realize industrialization produces continuously.
Accompanying drawing explanation
Fig. 1 is the structural representation of this utility model embodiment.
Detailed description of the invention
Accompanying drawing discloses the structural representation of one preferred embodiment of this utility model without limitation, explains the technical solution of the utility model below with reference to accompanying drawing.
Embodiment 1
A kind of Yoga mat, as it is shown in figure 1, include composite joint face glue-line 1, foamed silica gel layer 1, base material 3, foamed silica gel layer 24 and on-slip glue-line 5 together the most successively.The thickness of described base material 3 is 0.01-3mm.
Composition and the weight proportion of described glue-line 1 employing are as follows:
Vinyldimethicone uses 10000mpa.s pendant vinyl base silicone oil 68g, wherein, Vi=1.0%；
Vinyldimethicone uses and at least contains the polydimethylsiloxane that two vinyls are joined directly together with silicon atom at the end of the chain or chain side, and its effect obtained is consistent with the effect of this law embodiment 10000mpa.s pendant vinyl base silicone oil.
Filler 1 is spherical shaped silicone, 5g；
Filler 2 is white carbon (A200), 22g；
Containing hydrogen silicone oil uses hydrogen content to be 0.75% containing hydrogen silicone oil, 5g；
Platinum catalyst, wherein, Pt content in the catalyst is 3000ppm, 0.3g；
Inhibitor uses methyl butynol, 0.05g；
Black cream, 5g.
The raw material that described foamed silica gel layer 1 uses with foamed silica gel layer 24 is consistent, and the weight proportion of its raw material is as follows:
Vinyldimethicone uses 10000mpa.s vinyl-terminated silicone fluid, 70g；
Filler uses white carbon (A200), 28g；
Platinum catalyst uses Pt content to be the platinum catalyst of 3000ppm, and this platinum catalyst is chloroplatinic acid tetrahydrofuran solution, 0.3g；
Inhibitor uses methyl butynol, 0.05g
Containing hydrogen silicone oil uses hydrogen content to be 0.75% containing hydrogen silicone oil, 2g；
Color is black cream 5g；
Foaming agent uses foam powder 2g.
The weight proportion of the described raw materials used raw material of on-slip glue-line 5 is as follows:
Vinyldimethicone employing 10000mpa.s pendant vinyl base silicone oil, 70；
Filler uses white carbon (A200), 28g；
Platinum catalyst uses Pt content to be the platinum catalyst of 3000ppm, and this platinum catalyst is chloroplatinic acid tetrahydrofuran solution, 0.3g；
3rd inhibitor uses methyl butynol, 0.05g；
Containing hydrogen silicone oil hydrogen content is 0.75% containing hydrogen silicone oil, 2g；
Color uses black cream, 5g.
Described base material 3 is made for any in super fine, the glass of chemistry super fine, cotton, numb, paper, metal or two or more mixture materials.
Containing hydrogen silicone oil is the polydimethylsiloxane that at least three hydrogen atom is directly connected with silicon, and hydrogen atom content accounts for the 0.1～1.6% of raw material.
Platinum catalyst can be isopropyl alcohol solution of chloroplatinic acid or chloroplatinic acid-1,3,5,7-tetravinyl-1,3,5,7-tetramethyls-cyclotetrasiloxane or chloroplatinic acid-divinyl tetramethyl disiloxane, and its effect obtained is as chloroplatinic acid tetrahydrofuran solution.
Color is the pigment with vinyldimethicone as disperse medium.
Vinyldimethicone can use and at least contain the polydimethylsiloxane that two vinyls are joined directly together with silicon atom at the end of the chain or chain side, and its effect reached is as the effect of vinyl-terminated silicone fluid.
The preparation method of a kind of Yoga mat, comprises the following steps:
A. the face glue-line sizing material prepared is coated on release paper or mould release membrance, vulcanizes 3～10 minutes at a temperature of 80～180 DEG C, form face glue-line 1.
B. bubble layer of silica gel one sizing material is allotted by each Composition Weight Parts proportioning of the raw material of foamed silica gel layer 1, foamed silica gel layer one sizing material prepared is coated on the face glue-line 1 that step a is cured, laminating base material 3, vulcanize 3～20 minutes at a temperature of 80～180 DEG C, peel off release paper or mould release membrance, obtaining leather substrate face, rolling is standby.
C. join on-slip glue-line sizing material by each Composition Weight Parts proportioning of the raw material of on-slip glue-line 5, the on-slip glue-line sizing material prepared is coated on release paper or mould release membrance, vulcanize 3～10 minutes at a temperature of 80～180 DEG C.
D. bubble layer of silica gel two sizing material is allotted by each Composition Weight Parts proportioning of the raw material of foamed silica gel layer two (4), foamed silica gel layer two sizing material prepared is coated on the on-slip glue-line 5 silica gel face that step c is cured, the substrate surface of laminating leather obtained by step b, vulcanize 3～20 minutes at a temperature of 80～180 DEG C, peel off release paper or mould release membrance, can be prepared by yoga mat material.
With in place of the difference of embodiment 1, embodiment 2-embodiment 7 is that the raw material weight proportioning of foamed silica gel layer 1 and foamed silica gel layer 24 is different respectively, and the raw material weight proportioning of on-slip glue-line is different, and details are shown in Table 1.
Comparative example 1: in addition to being not added with the foaming agent such as foam powder in foamed silica gel layer raw material, other raw materials are with embodiment 3.
Comparative example 2: be coated with Yoga mat TPE material best on market on 1.0 super fine two sides, yoga mat material controls the thickness identical with the yoga mat material of embodiment 3 and lines.
Yoga mat material prepared by embodiment 1-7 and comparative example 1,2 is carried out following test:
1, folding fastness
Folding fastness is tested by the regulation of QB/T2714-2005.Cut two groups of samples in the width direction, every 2 groups, specimen surface layer folded inward, respectively two groups of samples are folded 200,000 times in (23 ± 2) DEG C and fold 2.5 ten thousand times with (-10 ± 1) DEG C, then observe by position, folding part table, inner two-part situation of change, observe and have flawless.
2, wearability
Test by the regulation of QB/T2726-2005, use CS-10 emery wheel, experimental condition loading 1000g, test revolution 1000 turns.
Evaluation criteria:
1 grade clearly
2 grades obvious
Can tell for 3 grades
4 grades are difficult to tell
Cannot tell for 5 grades.
3, smooth feeling
A is dry and comfortable smooth
B is smooth
C on-slip.
4, pliability
With reference to CN100400678 " leather coating composition, coating process and application leather ", grade is as follows:
A is the most soft
B is soft
C is medium
D is hard
E is very rigid
5, resilience
Test with reference to GB/T1681-1991 " the elastic mensuration of vulcanite "
6, soil resistance.
Ball pen ink is sprinkled upon on material, contrasts after clearing up with ethanol after 24 hours:
5 grades: inviolateness remains
4 grades: slightly stain residual
3 grades: some stains remain
2 grades: many stain residuals
1 grade: dirty.
The raw materials used proportioning of embodiment 1 to 7 and test result are as shown in table 1:
Table 1
Can be seen that from upper table 1, the addition of foam powder has considerable influence to wearability, resilience and the pliability of yoga mat material, and when foam powder adds 6%, the combination property of material is optimal, i.e. embodiment 3 is combination property preferred plan.
Embodiment 3 is as shown in table 2 with the comparison of comparative example 1,2:
Table 2
Can be seen that foam powder provides good flexibility for yoga mat material of the present utility model from upper table 2；Compared with traditional TPE yoga mat material, the Novel yoga cushion material that this utility model is mentioned is significantly improved at aspects such as resilience, on-slip and soil resistances.
It is merely to illustrate embodiment of the present utility model above in conjunction with this utility model preferred embodiment described by accompanying drawing; not as to aforementioned utility model purpose and claims content and the restriction of scope; every according to technical spirit of the present utility model to any simple modification made for any of the above embodiments, equivalent variations and modification, the most still belong to this utility model technology and rights protection category.
Claims (3)
1. a Yoga mat, it is characterised in that: include face glue-line (1), foamed silica gel layer one (2), base material (3), foamed silica gel layer two (4) and the on-slip glue-line (5) set gradually from top to bottom.
Yoga mat the most according to claim 1, it is characterised in that: described glue-line (1), foamed silica gel layer one (2), base material (3), foamed silica gel layer two (4) and on-slip glue-line (5) composite joint successively are together.
Yoga mat the most according to claim 1, it is characterised in that: the thickness of described base material (3) is 0.01-3mm.