CN205133410U - Novel production of dull polish borosilicate glass microwave stone or metal plate for standing a stove on as a precaution against fire device - Google Patents
Novel production of dull polish borosilicate glass microwave stone or metal plate for standing a stove on as a precaution against fire device Download PDFInfo
- Publication number
- CN205133410U CN205133410U CN201520872537.7U CN201520872537U CN205133410U CN 205133410 U CN205133410 U CN 205133410U CN 201520872537 U CN201520872537 U CN 201520872537U CN 205133410 U CN205133410 U CN 205133410U
- Authority
- CN
- China
- Prior art keywords
- machine
- stove
- stone
- standing
- metal plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a novel production of dull polish borosilicate glass microwave stone or metal plate for standing a stove on as a precaution against fire device, the device belong to the glassware production field, include: mixer, plane smelting pot, stone or metal plate for standing a stove on as a precaution against fire mould, flame polishing machine, high -temperature annealing furnace, flat grinder, sand blasting machine, rinsing machine, drying -machine, be equipped with raw materials import on the mixer, be equipped with first conveyer between mixer and plane smelting pot, be equipped with the gas import on the smelting pot of plane, be equipped with first pipeline between plane smelting pot and stone or metal plate for standing a stove on as a precaution against fire mould, be equipped with first manipulator between stone or metal plate for standing a stove on as a precaution against fire mould and flame polishing machine, be equipped with the second manipulator between flame polishing machine and high -temperature annealing furnace, be equipped with the second conveyer between high -temperature annealing furnace and flat grinder, be equipped with the third conveyer between flat grinder and sand blasting machine, be equipped with husky import on the sand blasting machine, useless husky export, be equipped with the fourth conveyer between sand blasting machine and rinsing machine, be equipped with high -pressure water inlet on the rinsing machine, the outlet of sewer, be equipped with the 5th conveyer between rinsing machine and drying -machine, be equipped with the product outlet on the drying -machine.
Description
Technical field
The utility model belongs to glasswork production field, particularly relates to a kind of mechanism producing frosted high-boron-silicon glass microwave plate.
Background technology
High-boron-silicon glass is the characteristic utilizing glass to conduct electricity at high operating temperatures, by realizing glass melting in inside glass heating, through a kind of glass that vanguard technology processes, it is a kind of low thermal expansion, high temperature resistant, high strength, high rigidity, the specific glass material of high transmission rate and high chemical stability, excellent performance, high-boron-silicon glass and general glassy phase ratio, its advantage has no side effect, mechanical property, thermal stability, water resistant, alkali resistant, the performance such as antiacid improves greatly, especially high-boron-silicon glass has low-down thermal expansivity, about 1/3rd of simple glass, what minimizing caused because of thermograde stress by this expands with heat and contract with cold, be applicable to very much making light fixture, tableware, tea set, bidding quotation, to look in the distance eyeglass, washing machine vision slit, microwave plate, the multiple products such as solar water heater.Because circumstance of temperature difference residing when microwave plate uses is comparatively large, initial temperature is low to moderate 0 DEG C sometimes, and Heating temperature reaches 100 DEG C sometimes, and the limit can reach 120 DEG C, and the stone or metal plate for standing a stove on as a precaution against fire that high-boron-silicon glass is made uses under being highly suitable for this temperature; Carry out frosted to product, namely the stone or metal plate for standing a stove on as a precaution against fire produced is made through frosting technology again, after frosted, stone or metal plate for standing a stove on as a precaution against fire presents oyster white sensation, and its distinguishing feature is that surface is fine and smooth, and printing opacity is opaque.The utility model device be a kind of method of mechanical frosted that adopts to process high-boron-silicon glass microwave plate, its great advantage is without soda acid, very environmental protection, and the finished product can meet the required terms and conditions that to work in microwave oven, elegant in appearance again.
Summary of the invention:
The problem that the utility model mainly solves is to provide a kind of novel frosted high-boron-silicon glass microwave plate production equipment, this device for equipment, carrys out production frosted high-boron-silicon glass microwave plate with quartz sand, borax, SODIUMNITRATE, feldspar, salt of wormwood for raw material with stirrer, plane smelting furnace, stone or metal plate for standing a stove on as a precaution against fire mould, fire polishing machine, high-temperature annealing furnace, surface grinding machine, sandblast machine, rinsing machine, dryer.
The technical solution adopted in the utility model is:
A kind of novel frosted high-boron-silicon glass microwave plate production equipment, comprising: stirrer 1, plane smelting furnace 2, stone or metal plate for standing a stove on as a precaution against fire mould 3, fire polishing machine 4, high-temperature annealing furnace 5, surface grinding machine 6, sandblast machine 7, rinsing machine 8, dryer 9, stirrer 1 is provided with material inlet 10, the first transfer roller 11 is provided with between stirrer 1 and plane smelting furnace 2, plane smelting furnace 2 is provided with fuel gas inlet 12, the first pipeline 13 is provided with between plane smelting furnace 2 and stone or metal plate for standing a stove on as a precaution against fire mould 3, the first mechanical manipulator 14 is provided with between stone or metal plate for standing a stove on as a precaution against fire mould 3 and fire polishing machine 4, the second mechanical manipulator 15 is provided with between fire polishing machine 4 and high-temperature annealing furnace 5, second conveyor 16 is provided with between high-temperature annealing furnace 5 and surface grinding machine 6, the 3rd transfer roller 17 is provided with between surface grinding machine 6 and sandblast machine 7, sandblast machine 7 is provided with husky import 18, useless husky outlet 19, the 4th transfer roller 20 is provided with between sandblast machine 7 and rinsing machine 8, rinsing machine 8 is provided with high pressure water import 21, sewage outlet 22, the 5th transfer roller 23 is provided with between rinsing machine 8 and dryer 9, dryer 9 is provided with product outlet 24.
Further technical scheme of the present utility model is:
Described plane smelting furnace is 15 square metres of combustion gas smelting furnaces.
The first described transfer roller is scraper conveyor.
Described second conveyor is silicon carbide material rotary conveyor.
Described the 3rd, the 4th, the 5th transfer roller is polyurethane skin belt conveyor.
The first described pipeline is aluminum oxide material.
The beneficial effects of the utility model are: provide a kind of novel frosted high-boron-silicon glass microwave plate production equipment, and this device uses general-purpose equipment combination, structure is simple, easy to operate, production process is pollution-free waste discharge; The product frosted high-boron-silicon glass microwave plate produced is elegant in appearance, and its advantage has low thermal expansion, high temperature resistant, high strength, high rigidity and high chemical stability, and product is used for microwave oven, particularly adapts to the temperature of frequent variations in microwave oven.
Accompanying drawing illustrates:
If Fig. 1 is Structure and energy FB(flow block) of the present utility model.
Embodiment
Embodiment:
The particular content using this mechanism production frosted high-boron-silicon glass microwave plate most preferred embodiment is further illustrated below in conjunction with accompanying drawing:
1. the quartz sand of formula ratio, borax, SODIUMNITRATE, feldspar, salt of wormwood are sent into stirrer 1 by the material inlet 10 be arranged on stirrer 1, compound is obtained after even blend, compound sends into plane smelting furnace 2 by the first transfer roller 11 be arranged between stirrer 1 and plane smelting furnace 2, send into fuel gas buring by the fuel gas inlet 12 be arranged on plane smelting furnace 2 to heat compound, when temperature reaches 1500 DEG C, keep this temperature 20-22 hour, make compound become high-boron-silicon glass molten mass completely.
2. high-boron-silicon glass molten mass is sent into stone or metal plate for standing a stove on as a precaution against fire mould 3 by the first pipeline 13 be arranged between plane smelting furnace 2 and stone or metal plate for standing a stove on as a precaution against fire mould 3 shaping, mold temperature is 1500 DEG C, shaping relief temperature reduces naturally, when being reduced to 1050 DEG C, melts becomes solid, now slough mould, the product of first one-step forming sends into fire polishing machine 4 polishing by the first mechanical manipulator 14 be arranged between stone or metal plate for standing a stove on as a precaution against fire mould 3 and fire polishing machine 4, by the second mechanical manipulator 15 be arranged between fire polishing machine 4 and high-temperature annealing furnace 5, product is sent into high-temperature annealing furnace 5 immediately after polishing, progressively the temperature of product is down to after below 150 DEG C and enters air cooling-down to normal temperature.
3. the outside surface that the product of normal temperature sends into surface grinding machine 6 pairs of products by the second conveyor 16 be arranged between high-temperature annealing furnace 5 and surface grinding machine 6 is carried out ground, except irregularities such as deburrings, then it is sent into sandblast machine 7 by the 3rd transfer roller 17 be arranged between surface grinding machine 6 and sandblast machine 7, sand is sent into by the husky import 18 be arranged on sandblast machine 7, sand sprays to stone or metal plate for standing a stove on as a precaution against fire at a high speed under the effect of sandblast machine 7, useless husky useless sand outlet 19 discharge by being arranged on sandblast machine 7 after stone or metal plate for standing a stove on as a precaution against fire completion of processing, the stone or metal plate for standing a stove on as a precaution against fire of completion of processing sends into rinsing machine 8 by the 4th transfer roller 20 be arranged between sandblast machine 7 and rinsing machine 8, send into high pressure water by the high pressure water import 21 be arranged on rinsing machine 8 to clean stone or metal plate for standing a stove on as a precaution against fire, the waste water produced is discharged by the wastewater outlet 22 be arranged on rinsing machine 8, the stone or metal plate for standing a stove on as a precaution against fire cleaned sends into dryer 9 by the 5th transfer roller 23 be arranged between rinsing machine 8 and dryer 9 dries, stone or metal plate for standing a stove on as a precaution against fire after oven dry is by being arranged at product outlet 24 discharging on dryer 9.
Certainly, the utility model also has other embodiment, not leaving the improvement of any technology, principle and the technique done under spiritual background of the present utility model, all drops within protection domain of the present utility model.
Claims (6)
1. a novel frosted high-boron-silicon glass microwave plate production equipment, comprising: stirrer (1), plane smelting furnace (2), stone or metal plate for standing a stove on as a precaution against fire mould (3), fire polishing machine (4), high-temperature annealing furnace (5), surface grinding machine (6), sandblast machine (7), rinsing machine (8), dryer (9), it is characterized in that: stirrer (1) is provided with material inlet (10), the first transfer roller (11) is provided with between stirrer (1) and plane smelting furnace (2), plane smelting furnace (2) is provided with fuel gas inlet (12), the first pipeline (13) is provided with between plane smelting furnace (2) and stone or metal plate for standing a stove on as a precaution against fire mould (3), the first mechanical manipulator (14) is provided with between stone or metal plate for standing a stove on as a precaution against fire mould (3) and fire polishing machine (4), the second mechanical manipulator (15) is provided with between fire polishing machine (4) and high-temperature annealing furnace (5), second conveyor (16) is provided with between high-temperature annealing furnace (5) and surface grinding machine (6), the 3rd transfer roller (17) is provided with between surface grinding machine (6) and sandblast machine (7), sandblast machine (7) is provided with husky import (18), useless husky outlet (19), the 4th transfer roller (20) is provided with between sandblast machine (7) and rinsing machine (8), rinsing machine (8) is provided with high pressure water import (21), sewage outlet (22), the 5th transfer roller (23) is provided with between rinsing machine (8) and dryer (9), dryer (9) is provided with product outlet (24).
2. a kind of novel frosted high-boron-silicon glass microwave plate production equipment as claimed in claim 1, is characterized in that: described plane smelting furnace is 15 square metres of combustion gas smelting furnaces.
3. a kind of novel frosted high-boron-silicon glass microwave plate production equipment as claimed in claim 1, is characterized in that: the first described transfer roller is scraper conveyor.
4. a kind of novel frosted high-boron-silicon glass microwave plate production equipment as claimed in claim 1, is characterized in that: described second conveyor is silicon carbide material rotary conveyor.
5. a kind of novel frosted high-boron-silicon glass microwave plate production equipment as claimed in claim 1, is characterized in that: the described the 3rd, the 4th, the 5th transfer roller is polyurethane skin belt conveyor.
6. a kind of novel frosted high-boron-silicon glass microwave plate production equipment as claimed in claim 1, is characterized in that: the first described pipeline is aluminum oxide material.