CN205043106U - Continuous casting of metal crystallizer narrow face copper plate - Google Patents
Continuous casting of metal crystallizer narrow face copper plate Download PDFInfo
- Publication number
- CN205043106U CN205043106U CN201520712165.1U CN201520712165U CN205043106U CN 205043106 U CN205043106 U CN 205043106U CN 201520712165 U CN201520712165 U CN 201520712165U CN 205043106 U CN205043106 U CN 205043106U
- Authority
- CN
- China
- Prior art keywords
- continuous casting
- filling member
- copper plate
- bolt
- copper coin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a continuous casting of metal crystallizer narrow face copper plate, including the work copper that the back is connected with the backplate through the connecting piece, the connecting piece sets up on the filling member at the back of work copper, the connecting piece through its go up to set up protruding and constitute the cooling agent clearance between the backplate, the utility model discloses a copper back sets up the recess working to wherein setting up the structural style that upper portion has the bolt filling member, the structural strength of reinforcing work copper and backplate, the quantity of reducing coupling spare, thus reduce the cooling agent at wherein resistance, autofrettage through to the work copper has prolonged life, the utility model discloses simple structure, it is easy and simple to handle, be worth popularization and application.
Description
Technical field
The utility model relates to metal freezing and continuous casting technical field, particularly a kind of metal continuous casting crystallizer narrow copper plate.
Background technology
Along with the development of world's metallurgical technology, the constantly progress of modern continuous casting technology, steel grade of can casting constantly expands, and some high alloys, high-quality, high crack sensitivity steel grade are continuous is produced in the production procedure of large iron and steel enterprise continuous casting; One of this wherein main technological progress is the development of big cross section strand continuous casting technology; The development of big cross section strand continuous casting technology, the compression ratio of steel increases, and the product quality of steel improves; But the adverse effect that the increase of casting blank section brings is exactly: because strand volume is larger in casting process, when in the process of solidifying, it becomes solid phase from liquid phase, need to discharge the effect that a large amount of heat ensures solidification, if copper coin heat-conducting effect is not good, very easily cause heat radiation obstructed, the phenomenon that solidification effect is not good, if solidifying crust when carry-over pinch rolls draw crosses thin, very easily cause compressive deformation, gently then affect billet quality weight then may due to the pressurized serious production accident causing molten steel to leak that causes steel billet sheetmetal to break.
Chinese utility model patent ZL02214026.3(notification number CN2547438Y, title " slab continuous-casting crystallizer narrow-strop copper plate ") provide a kind of narrow face copper plate of crystallizer with side chamfering, its chamfer dimesion is 6 ~ 10mm, and angle is 45 degree.This patent does not have the type of cooling pointing out side chamfering, is unfavorable for the uniformity of product cooling on a horizontal plane.The patent of CN201744629Y, discloses a kind of narrow copper plate of continuous casting combination mould, although it arranges comparatively comprehensively cooling bath, the less effect that will certainly affect cooling of cooling surface, the phenomenon causing heat conduction bad occurs.
Utility model content
The purpose of this utility model is to overcome above-mentioned deficiency, discloses the chamfering narrow boards that a kind of middle part arranges liquid cooling face.
Technical scheme adopted to achieve these goals:
A kind of metal continuous casting crystallizer narrow copper plate, comprise the work copper coin that a back side is connected with backboard by connector, described connector is arranged on the filling member at the back side of described work copper coin, described connector by it arrange projection and described backboard between form cooling agent gap.
Further, the back side of described work copper coin arranges connector place and arranges groove, arranges the filling member with its mating shapes in described groove.
Further, described groove is dovetail groove or T-slot.
Further, described connector is bolt, and described bolt bottom and described filling member are designed to one.
Further, described projection is for being set in the sleeve on described connector.
Further, described projection and bolt design are integrated.
Further, described filling member is hard member.
Further, described bolt outer wall arranges chromium coating.
Further, described hard member is steelwork.
Further, described filling member top is concordant with the back side of work copper coin.
The utility model arranges groove at the work copper coin back side, and the form of filling member is set in groove, increase the contact area of copper coin and filling member and improve support force, be dovetail groove or T-slot by groove design, strengthen stability with this, reduce the risk that filling member comes off from the work copper coin back side; Filling member arranges bolt, and bolt and filling member is designed to one, the intensity of connection can be increased, reduce the magnitude setting of bolt.
In the middle part of bolt, arrange projection can supporting back board, backboard is made to produce cooling agent gap with the work copper coin back side, and the fixed form that projection can be integrated with bolt design, ensure support force, only projection is set at the contact surface place of bolt and backboard simultaneously, decrease the shape of the resistant block in cooling agent, and then reduce the resistance of cooling agent in cooling gap; In order to ensure that the quality cooled arranges sealed wall at backboard and the avris of work copper coin, thus ensure that it can not cause revealing from both sides the phenomenon of cooling agent because hydraulic pressure is excessive after work copper coin and backboard assemble.
The projection adopted also can be designed to the cylinder that aperture is greater than the diameter of bolt, the cylinder of middle part or bottom or top or overall hollow out is adopted according to the needs of design, make cylinder to be taken off recycling after copper coin use is discarded, also the form of nut can be designed to, because the lower end of screw thread is identical to the distance of filling member, the form of nut is achieved.
The work copper coin adopted and filling member are all through autofrettage, can reduce because work copper coin is heated the phenomenon that the work copper coin internal stress that causes assembles, extend the service life of work copper coin, avoid because internal stress assembles the phenomenon causing filling member and work copper coin to produce gap or seesaw, the filling member adopted is mutually concordant with the work copper coin back side, decreases the flow resistance of cooling agent.
The utility model adopts and arranges groove at the work copper coin back side, and arranges the version of top with bolt filling member wherein, strengthens the structural strength of work copper coin and backboard, reduces the quantity of connector, thus reduce cooling agent resistance wherein; By the autofrettage to work copper coin, extend service life; The utility model structure is simple, easy and simple to handle, is worthy to be popularized and application.
Accompanying drawing explanation
Fig. 1 is side structure schematic diagram of the present utility model;
Fig. 2 is the first structural representation at connector place of the present utility model;
Fig. 3 is the second structural representation at connector place of the present utility model;
Fig. 4 is the third structural representation at connector place of the present utility model;
Fig. 5 is the groove structure schematic diagram of dove-tail form of the present utility model;
Fig. 6 is the structural representation of T-slot of the present utility model;
Fig. 7 is the partial structurtes schematic diagram at the utility model pilot hole place;
Fig. 8 is the partial structurtes schematic diagram of the utility model cylinder.
Detailed description of the invention
In order to further instruction superiority of the present utility model, performance of the present utility model is carried out to the test of different pieces of information:
First group: adopt identical copper plate of crystallizer to adopt conventional bolt to connect and version of the present utility model respectively, test cracks and the service life of steel billet respectively, the experimental data of acquisition is as shown in the table:
| Title | Cracking breakout % | Service life (ten thousand tons) |
| Conventional stud connects | 7～8 | 6～8 |
| The utility model | 0.5～1.3 | 13～15 |
Note: this group experiment test is the data of producing 200*240 millimeter corrosion resistant plate, the acquisition of 900*20 steel plate, carries out testing the average range value obtained continuously to 200 complete equipments.
Produce in the corrosion resistant plate of 200*240 and the continuous cast mold of 900*20 steel plate although adopt identical copper plate of crystallizer to be all applied in as can be seen from the above table, continuously produce acquisition mean values through 200 complete equipments can find out, the utility model not only reduces cracking breakout and service life promotes greatly, this shows that the utility model possesses good heat conductivility.
Second group: adopt connected mode of the present utility model, the routine work copper coin back side arrange boss bolt connect be connected with plane bolt, measuring unit area (1 square metre) work copper coin obtains same intensity bolt quantity used and service life respectively, and the data of acquisition are as follows:
| Title | Bolt quantity | Service life (ten thousand tons) |
| The utility model connected mode | 50～70 | 13～15 |
| Boss bolt connects | 110～130 | 9～11 |
| Plane bolt connects | 180～200 | 6～8 |
Note: this group experiment test 200 times, the copper coin boss area of testing employing 1.8 meters long is 4 ~ 8 square centimeters, and the bolt of employing is the average data of the closely-pitched Steel Bolt acquisition of M16/M12.
Although all adopt the bolt of identical performance as can be seen from the above table, but want to obtain identical bonding strength, the utility model only needs 50 ~ 70 bolts to realize, and the connection of boss bolt is connected with plane bolt, it causes the thermal conductive surface at the work copper coin back side to reduce owing to needing to arrange bolt quantity at most, but the bolt of One's name is legion does not increase the service life, and the utility model not only Stability Analysis of Structures but also thermal conductive surface increase, service life is increased greatly.
3rd group: the utility model adopts Shi Hanzhang respectively then to assemble again the rear prestressed mode of the mode of Shi Hanzhang, conventional copper coin prestressing force and assembling, tests its structural strength relatively improved with conventional copper coin and service life respectively.
| Title | The structural strength improved | Service life |
| The utility model | 150～160MPa | 13 ~ 150,000 tons |
| Conventional copper coin prestressing force | 50～60MPa | 8 ~ 100,000 tons |
| Prestressing force after assembling | 80～100MPa | 10 ~ 120,000 tons |
Note: this group experiment test 200 times, the copper coin of testing employing 2.8 meters long carries out optimum prestress process to it, tests its flexural tensile strength and service life.
As can be seen from the above table, be adopt prestressed mode equally, its structural strength improved of ordinary copper board prestress only has 50 ~ 60MPa, and service life, more conventional copper coin improve about 20,000 tons, same material and structure, when but the prestressing force mode adopted is different, and the structure produced differs widely, if carry out autofrettage after filling member and work copper coin being assembled, then structural strength improves 80 ~ 100 MPas, service life is 10 ~ 120,000 tons, increase rate is not very large, then to filling member with work copper coin respectively Shi Hanzhang after then assembling again the mode of Shi Hanzhang but make structural strength and service life be greatly improved, flexural tensile strength is made to improve 150 ~ 160MPa, reach 13 ~ 150,000 tons service life, to trace it to its cause the mode of the Shi Hanzhang more after mounting of Shi Hanzhang both finding, it can the internal stress that produced by both prestressing force of the mode of Shi Hanzhang after mounting be offset, not only increase structural strength and too increase service life under mutually collaborative effect.
Superiority of the present utility model is further illustrated below in conjunction with accompanying drawing 1 ~ 8 specific embodiment:
Embodiment one:
A kind of metal continuous casting crystallizer narrow copper plate, comprise the work copper coin 1 that a back side is connected with backboard 2 by connector 3, described connector 3 is arranged on the filling member 4 at the back side of described work copper coin 1, described connector 3 by it arrange projection 6 and described backboard 2 between form cooling agent gap 5.
Further, the back side of described work copper coin 1 arranges connector 3 place and arranges groove, arranges the filling member 4 with its mating shapes in described groove.
Further, described groove 7 is dovetail groove.
Further, described connector 3 is bolt 32, and described bolt 32 bottom and described filling member 4 are designed to one.
Further, described protruding 33a and bolt design are integrated.
Further, described filling member 4 is hard member, and described hard member is steelwork.
Further, described bolt 32 outer wall arranges chromium coating.
Further, described filling member 4 top is concordant with the back side of work copper coin 1.
Embodiment two:
A kind of metal continuous casting crystallizer narrow copper plate, comprise the work copper coin 1 that a back side is connected with backboard 2 by connector 3, described connector 3 is arranged on the filling member 4 at the back side of described work copper coin 1, described connector 3 by it arrange projection 6 and described backboard 2 between form cooling agent gap 5.
Further, the back side of described work copper coin 1 arranges connector 3 place and arranges groove, arranges the filling member 4 with its mating shapes in described groove.
Further, described groove 7 is dovetail groove.
Further, described connector 3 is bolt 32, and described bolt 32 bottom and described filling member 4 are designed to one.
Further, described projection is for being set in the cylinder 33b on bolt 32.
Further, described filling member 4 is hard member, and described hard member is steelwork.
Further, described bolt 32 outer wall arranges chromium coating.
Further, described filling member 4 top is concordant with the back side of work copper coin 1.
Embodiment three:
A kind of metal continuous casting crystallizer narrow copper plate, comprise the work copper coin 1 that a back side is connected with backboard 2 by connector 3, described connector 3 is arranged on the filling member 4 at the back side of described work copper coin 1, described connector 3 by it arrange projection 6 and described backboard 2 between form cooling agent gap 5.
Further, the back side of described work copper coin 1 arranges connector 3 place and arranges groove, arranges the filling member 4 with its mating shapes in described groove.
Further, described groove 7 is dovetail groove.
Further, described connector 3 is bolt 32, and described bolt 32 bottom and described filling member 4 are designed to one.
Further, described protruding 6 for being set in the cylinder 33b on bolt 32.
Further, described filling member 4 is hard member, and described hard member is steelwork.
Further, described bolt 32 outer wall arranges chromium coating.
Further, described filling member 4 top is concordant with the back side of work copper coin 1.
Further, screw thread place, described bolt top is disposed radially circular hole 34.
Further, the hole inwall of described backboard 2 avris arranges the pilot hole 35 be communicated with backboard side.
Further, in described circular hole 34 and pilot hole 35, rigidity tension rope 36 is set.
Further, the back side of described backboard 2 is higher than the plane residing for circular hole 34.
Embodiment four:
A kind of metal continuous casting crystallizer narrow copper plate, comprise the work copper coin 1 that a back side is connected with backboard 2 by connector 3, described connector 3 is arranged on the filling member 4 at the back side of described work copper coin 1, described connector 3 by it arrange projection 6 and described backboard 2 between form cooling agent gap 5.
Further, the back side of described work copper coin 1 arranges connector 3 place and arranges groove, arranges the filling member 4 with its mating shapes in described groove.
Further, described groove 7 is T-slot.
Further, described connector 3 is bolt 32, and described bolt 32 bottom and described filling member 4 are designed to one.
Further, described protruding 6 for being set in the cylinder 33b on bolt 32.
Further, described filling member 4 is hard member, and described hard member is steelwork.
Further, described bolt 32 outer wall arranges chromium coating, described backboard is arranged bolt hole 31.
Further, described filling member 4 top is concordant with the back side of work copper coin 1.
Further, screw thread place, described bolt top is disposed radially circular hole 34.
Further, the hole inwall of described backboard 2 avris arranges the pilot hole 35 be communicated with backboard side.
Further, in described circular hole 34 and pilot hole 35, rigidity tension rope 36 is set.
Further, the back side of described backboard 2 is higher than the plane residing for circular hole 34.
Further, described work copper coin and filling member are joined through the laggard luggage of autofrettage, after assembling completes, are carrying out autofrettage.
A kind of prestressed construction method, comprises the following steps:
1) work copper coin and filling member are applied respectively to the lateral surface compressing power of 0.8 ~ 0.9 times of flexural tensile strength;
2) stablize lateral surface compressing power 2 ~ 5 hours, filling member is assemblied in the work copper coin back side, then entirety is applied to the lateral surface compressing power of the flexural tensile strength of 0.8 ~ 0.9 times of minimum flexural tensile strength;
3) steady pressure 3 ~ 5 hours, removes thrust, applies 1.05 times of pressure of its flexural tensile strength, observe whether occur deformation, if having, remove pressure in work copper coin face, if without, continue to exert pressure, until 1.5 times of pressure, then product is qualified.
The present embodiment, work copper coin and filling member assemble through autofrettage by it, after assembling completes, are carrying out autofrettage; Improve the flexural tensile strength of work copper coin and then extend service life, rigidity tension rope is set in circular hole and pilot hole, it can ensure to provide a kind of outside tightening force by rigidity tension rope to cylinder boss after nut is fixed, what backboard and work copper coin were fixed is more firm, the pulling force of rigidity tension rope can be adjusted simultaneously according to the actual needs, obtain best practical function with this.
Production practices, certain steel mill 5 platen base height pulling rate casting machine crystallizer, ladleful 150t, size of plate blank is 900mm × 20mm, conticaster radius is 6.5m, metallurgical length 26.5m, and design pulling rate is 1.8 ~ 3.2m/min, obtain the cracking breakout 10 ~ 11% of steel plate, this high pulling rate casting machine crystallizer average life span is 435 stoves.
After this crystallizer uses design of the present utility model, the steel plate cracking breakout obtained is 0.5 ~ 0.9%, decrease the generation of steel plate crackle, substantially increase the quality of product, this high pulling rate casting machine crystallizer average life span is simultaneously extended for 979 stoves, has increased substantially the life-span of continuous casting of middle-thin slabs crystallizer.
Claims (10)
1. metal continuous casting crystallizer narrow copper plate, comprise the work copper coin that a back side is connected with backboard by connector, it is characterized in that: described connector is arranged on the filling member at the back side of described work copper coin, described connector by it arrange projection and described backboard between form cooling agent gap.
2. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: the back side of described work copper coin arranges connector place and arranges groove, arranges the filling member with its mating shapes in described groove.
3. metal continuous casting crystallizer narrow copper plate as claimed in claim 2, is characterized in that: described groove is dovetail groove or T-slot.
4. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: described connector is bolt, and described bolt bottom and described filling member are designed to one.
5. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: described projection is for being set in the sleeve on described connector.
6. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: described projection and bolt design are integrated.
7. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: described filling member is hard member.
8. metal continuous casting crystallizer narrow copper plate as claimed in claim 4, is characterized in that: described bolt outer wall arranges chromium coating.
9. metal continuous casting crystallizer narrow copper plate as claimed in claim 7, is characterized in that: described hard member is steelwork.
10. metal continuous casting crystallizer narrow copper plate as claimed in claim 1, is characterized in that: described filling member top is concordant with the back side of work copper coin.