CN204266539U - A kind of heavy bamboo floor of improvement - Google Patents
A kind of heavy bamboo floor of improvement Download PDFInfo
- Publication number
- CN204266539U CN204266539U CN201420484022.5U CN201420484022U CN204266539U CN 204266539 U CN204266539 U CN 204266539U CN 201420484022 U CN201420484022 U CN 201420484022U CN 204266539 U CN204266539 U CN 204266539U
- Authority
- CN
- China
- Prior art keywords
- plate body
- bamboo
- floor
- bamboo silk
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of heavy bamboo floor of improvement, comprise plate body, the ground rete that described plate body comprises bamboo silk layer, adhesive layer and is located at bottom plate body, described bamboo silk layer and adhesive layer are irregular cross-distribution, the bamboo filament diameter of described bamboo silk layer is less than or equal to 4mm, the quality of described adhesive layer and bamboo silk layer is 13%-15% than scope, and described plate body thickness is less than or equal to 9mm.Control the size of bamboo silk and its water content and realize the gluing effect higher to floor, and then realize entirely better intensity after sheet metal forming, sheet material is thinner simultaneously, good spread make shaping after floor there is preferably toughness and humidity resistance, add the ground rete bottom upper plate body, further promote plate body antivibration and humidity resistance, use procedure feel better and not easily make a noise; And the integral thickness on floor is thinning, reduces the consumption of former material, effectively reduce processing cost.
Description
Technical field
The utility model relates to a kind of heavy bamboo floor of improvement.
Background technology
Although vast territory and abundant resources in China, but poor forest resources per capita, how the efficiency utilization forest reserves are significant problems, and what existing various heavy bamboo floor did due to the problem of technical elements thicklyer can not overcome the every technical requirements doing 9 below ㎜ latch floors, causes the waste of resource.The heavy bamboo floor of the improvement of 9 below ㎜ can be accomplished, by market today active demand.
Utility model content
The technical problems to be solved in the utility model is to provide a kind of heavy bamboo floor of improvement, and can effectively realize within bamboo clappers is worked into 9 ㎜, floor performance is given prominence to simultaneously, comfortable foot feeling.
For solving the problems of the technologies described above, the technical solution adopted in the utility model is: a kind of heavy bamboo floor of improvement, comprise plate body, the ground rete that described plate body comprises bamboo silk layer, adhesive layer and is located at bottom plate body, described bamboo silk layer and adhesive layer are irregular cross-distribution, the bamboo filament diameter of described bamboo silk layer is less than or equal to 4mm, and the quality of described adhesive layer and bamboo silk layer is 13%-15% than scope, and described plate body thickness is less than or equal to 9mm.Control the size of bamboo silk and its water content and realize the gluing effect higher to floor, and then realize entirely better intensity after sheet metal forming, sheet material is thinner simultaneously, good spread make shaping after floor there is preferably toughness and humidity resistance, add the ground rete bottom upper plate body, further promote plate body antivibration and humidity resistance, use procedure feel better and not easily make a noise; And the integral thickness on floor is thinning, reduces the consumption of former material, effectively reduce processing cost.
Improve as one, the cementing agent of described adhesive layer is modified phenolic glue, and cementing agent operating temperature remains on 25 DEG C, and the solid content of cementing agent is more than or equal to 50%.At the operate at ambient temperature of its performance the best, like this, the phenolic aldehyde glue as cementing agent can reach the bond effect of its best, and glue concentration is large, and number of seconds is lower, and molecule is less, and spread increases thereupon, and shaping strength is better.
Improve as one, described cementing agent immerses 1.5mm in bamboo silk surface.To improve the bond effect of cementing agent, whole floor fastness is better.
Improve as one, before the gluing of described bamboo silk layer in it mass fraction of moisture lower than 8%.Effectively can improve it and inhale glue amount, and then intensity after raising ground sheet metal forming.
The technical solution adopted in the utility model, its beneficial effect is: the heavy bamboo floor of improvement, we make heavy bamboo wood floor thick-ness can be accomplished within 9 ㎜ by research of technique now, with regard to 9 ㎜ material-saving 9 compared with 14 ㎜, and nearly 1/3 is reduced on the outlet cost of transportation on floor, carrying labor reduction is installed, does not lose the attractive in appearance and service property (quality) of the style on similar floor simultaneously, effectively can realize protection against the tide, quiet, comfortable foot feeling, the teaching effect such as easy for installation.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the utility model is described further:
Fig. 1 is the structural representation of a kind of embodiment of the utility model.
Detailed description of the invention
The structural representation of a kind of embodiment of the utility model as shown in Figure 1, a kind of heavy bamboo floor of improvement, comprise plate body 1, the ground rete 4 that described plate body comprises bamboo silk layer 3, adhesive layer 2 and is located at bottom plate body, described bamboo silk layer and adhesive layer are irregular cross-distribution, the bamboo filament diameter of described bamboo silk layer is less than or equal to 4mm, and the quality of described adhesive layer and bamboo silk layer is 13%-15% than scope, and described plate body thickness is less than or equal to 9mm.
Control the size of bamboo silk and its water content and realize the gluing effect higher to floor, and then reach entirely better intensity after sheet metal forming, sheet material is thinner simultaneously, good spread make shaping after floor there is preferably toughness and humidity resistance, use procedure feel is better and not easily make a noise; And the integral thickness on floor is thinning, reduces the consumption of former material, effectively reduce processing cost.
In the present embodiment, the cementing agent of described adhesive layer is modified phenolic glue, and cementing agent operating temperature remains on 25 DEG C, and the solid content of cementing agent is more than or equal to 50%.
At the operate at ambient temperature of its performance the best, like this, the phenolic aldehyde glue as cementing agent can reach the bond effect of its best, and glue concentration is large, and number of seconds is lower, and molecule is less, and spread increases thereupon, and shaping strength is better.
Described cementing agent immerses 1.5mm in bamboo silk surface.To improve the bond effect of cementing agent, whole floor fastness is better.
Before the gluing of described bamboo silk layer in it mass fraction of moisture lower than 8%.Effectively can improve it and inhale glue amount, and then intensity after raising ground sheet metal forming.
The heavy bamboo floor of a kind of improvement that this programme provides and processing technology thereof, comprise the steps:
1), choose the Bamboo silk of thin slice strip, and scale operation is carried out to it;
2), successively by step 1) in the Bamboo silk of scale carry out pressing, the treatment process such as roller, stone roller, the sheet of cracking is processed into Bamboo silk, and Bamboo silk that is blue or green or yellow patch will be there is in crack, select rejecting, with the strike-through technique avoiding the wax component in makings patch to affect the later stage;
3), by step 2) the sheet shape Bamboo silk that processes carries out carbonization or rinsing process process, to remove the material such as lipid, carbohydrate in Bamboo silk;
4), to step 3) in obtained Bamboo silk carry out drying process, drying plant can be adopted to carry out drying or tedding under natural environment, and causing its extexine is that dry lack of water whitens the state of look;
5), by step 4) in the dry Bamboo silk processed carry out strike-through technique, Bamboo silk is placed in glue, oozes 2mm to Bamboo silk surface to glue;
6), by step 5) the Bamboo silk that completes of strike-through is placed in mold pressing in pressing plate die cavity, and mold pressing keeps 90 minutes, to its curing molding;
7), by step 6) in sheet material after curing molding deposit health, the environment temperature of storage environment remains on 25 DEG C-35 DEG C, and ambient humidity remains on 14%-18%, deposits health and continues 30 days;
8), the whole plate after health process is processed as 8-10mm, and carried out equilibrium water release, this equilibrium water release flow process is carried out in balance cylinder, described balance indoor environment temperature controls at 25-35 DEG C, keep balance interior temperature to be realized by the electrical heating of hot-water heating sheet and blower fan acting in conjunction, reach 6-8 to stress moisture standards value;
9), by step 8) in obtained whole plate health one week, ambient humidity remains on 6%-9%;
10), by step 9) in whole plate after health, carry out sanding, plane Milling Machining, fluting, then back of the body paint on whole plate front, the length and width size of whole plate is left 230cm*95cm;
11), by step 10) obtained whole back sticks mulch film, and described ground film thickness is 1-4mm, and now whole plate adds ground film thickness is 9mm, namely obtains required product.
Described step 2) in the water content of Bamboo silk be between 12%-18%.
Described step 5) in glue strike-through technique in its temperature remain on 25 degrees Celsius, the solid content of described glue is more than or equal to 50%.
Described step 5) in glue strike-through technique in its number of seconds control at 13 seconds-15 seconds.
Program product can reach about 8mm, can possess the technique effects such as protection against the tide, quiet, comfortable foot feeling, installation be convenient simultaneously.
Except above preferred embodiment, the utility model also has other embodiment, those skilled in the art can make various change and distortion according to the utility model, only otherwise depart from spirit of the present utility model, all should belong to the scope that the utility model claims define.
Claims (3)
1. the heavy bamboo floor improved, it is characterized in that: comprise plate body (1), the ground rete (4) that described plate body comprises bamboo silk layer (3) and adhesive layer (2) and is located at bottom plate body, described bamboo silk layer and adhesive layer are irregular cross-distribution, the bamboo filament diameter of described bamboo silk layer is less than or equal to 4mm, the quality of described adhesive layer and bamboo silk layer is 13%-15% than scope, and described plate body thickness is less than or equal to 9mm.
2. the heavy bamboo floor of a kind of improvement according to claim 1, is characterized in that: the cementing agent of described adhesive layer is the modified phenolic glue that solid content is more than or equal to 50%, and the operating temperature of cementing agent remains on 25 DEG C.
3. the heavy bamboo floor of a kind of improvement according to claim 1 and 2, is characterized in that: described cementing agent immerses 2.0mm in bamboo silk surface.