CN203748140U - Mobile terminal shell - Google Patents
Mobile terminal shell Download PDFInfo
- Publication number
- CN203748140U CN203748140U CN201320881993.9U CN201320881993U CN203748140U CN 203748140 U CN203748140 U CN 203748140U CN 201320881993 U CN201320881993 U CN 201320881993U CN 203748140 U CN203748140 U CN 203748140U
- Authority
- CN
- China
- Prior art keywords
- layer
- mobile terminal
- terminal shell
- sheet material
- patterned layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model discloses a mobile terminal shell which comprises a sheet material, a pattern layer and a background layer. The pattern layer is arranged on part of the lower surface of the sheet material. The pattern layer is an ink layer and is internally provided with a plurality of metal films. The background layer is arranged on the remaining lower surface of the sheet material and the lower surface of the pattern layer. According to the mobile terminal shell of the utility model, the pattern layer is printed with ink containing metal films, and the layered metal films have strong reflection on incident light after printing so that the pattern layer of the mobile terminal shell has a super-bright appearance effect. As the pattern layer is disposed between the sheet material and the background layer, the pattern layer is ensured not to be scratched or worn in the using process and is durable. Meanwhile, the mobile terminal shell is simple in structure and can be easily processed and molded.
Description
Technical field
The utility model relates to electronic product field, especially relates to a kind of mobile terminal shell.
Background technology
In correlation technique, the electronic product casing such as mobile phone mostly adopts the techniques such as injection moulding, spraying, printing to realize; its surperficial coating plays the effect of protection; but by injection moulding, be difficult to realize the manufacture of the following thickness product of 0.8mm; its product surface has injection moulding clamp, heterochromatic point etc. bad; need to cover by spraying; spraying coating process is larger to the damage ratio of environment; and spray paint surface easily occurs that orange peel, long-pending wet goods are bad; affect outward appearance; spray paint case hardness is generally no more than 2H in addition, is in use more easily worn and scratches.
Another manufactures the mode IML of phone housing, printed patterns on film, and then through in-mould injection with plastic parts combination, need to pass through printing, moulding, die-cut, injection moulding, CNC(computer-aided is processed) etc. multiple technique, processing procedure is complicated, and cost is high, yield is low.
Utility model content
The utility model is intended at least solve one of technical problem existing in prior art.For this reason, an object of the present utility model is to propose a kind of mobile terminal shell, has the appearance effect of superbright, and patterned layer can not be scratched or wear and tear.
According to mobile terminal shell of the present utility model, comprising: sheet material; Patterned layer, described patterned layer is located on the part lower surface of described sheet material, and described patterned layer is to be provided with a plurality of metal films in ink layer and described patterned layer; Background layer, described background layer is located on all the other lower surfaces of described sheet material and the lower surface of described patterned layer.
According to mobile terminal shell of the present utility model, patterned layer adopts the ink printing contain metal film, and after printing, the metal film of stratiform has stronger reflection to incident light, thereby makes the patterned layer of mobile terminal shell have the appearance effect of superbright.And because patterned layer is between sheet material and background layer, guarantee that patterned layer in use can not be scratched or wear and tear, durable in use, this mobile terminal shell is simple in structure simultaneously, is convenient to machine-shaping.
Additional aspect of the present utility model and advantage in the following description part provide, and part will become obviously from the following description, or recognize by practice of the present utility model.
Accompanying drawing explanation
Above-mentioned and/or additional aspect of the present utility model and advantage accompanying drawing below combination obviously and is easily understood becoming the description of embodiment, wherein:
Fig. 1 is according to the schematic diagram of the mobile terminal shell of the utility model embodiment;
Fig. 2 is the reflective schematic diagram according to the patterned layer in the mobile terminal shell of the utility model embodiment.
Reference numeral:
Mobile terminal shell 100, plate body 1, layer of polycarbonate 10, add hard formation 11, transition resin bed 12, patterned layer 2, metal film 20, background layer 3
Embodiment
Describe embodiment of the present utility model below in detail, the example of described embodiment is shown in the drawings, and wherein same or similar label represents same or similar element or has the element of identical or similar functions from start to finish.Below by the embodiment being described with reference to the drawings, be exemplary, only for explaining the utility model, and can not be interpreted as restriction of the present utility model.
In description of the present utility model, it will be appreciated that, orientation or the position relationship of the indications such as term " " center ", " on ", D score, 'fornt', 'back', " left side ", " right side " be based on orientation shown in the drawings or position relationship; be only the utility model and simplified characterization for convenience of description; rather than the device of indication or hint indication or element must have specific orientation, with specific orientation structure and operation, so can not be interpreted as restriction of the present utility model.
In description of the present utility model, it should be noted that, unless otherwise clearly defined and limited, term " installation ", " being connected ", " connection " should be interpreted broadly, and for example, can be to be fixedly connected with, and can be also to removably connect, or connect integratedly; It can be mechanical connection; Can be to be directly connected, also can indirectly be connected by intermediary, can be the connection of two element internals.For the ordinary skill in the art, can concrete condition understand the concrete meaning of above-mentioned term in the utility model.
In addition,, in description of the present utility model, except as otherwise noted, the implication of " a plurality of " is two or more.
Below with reference to Fig. 1 and Fig. 2, describe according to the mobile terminal shell 100 of the utility model embodiment, wherein this mobile terminal shell 100 can be the housing of phone housing or other electronic products.
As depicted in figs. 1 and 2, mobile terminal shell 100 according to the utility model embodiment, comprising: sheet material 1, patterned layer 2 and background layer 3, wherein, patterned layer 2 is located on the part lower surface of sheet material 1, and patterned layer 2 is for being provided with a plurality of metal films 20 in ink layer and patterned layer 2.That is to say, the part lower surface of sheet material 1 is provided with patterned layer 2, and all the other lower surfaces of sheet material 1 are not provided with patterned layer 2.In concrete example of the present utility model, metal film 20 is aluminium film, and the thickness of sheet material 1 is 0.3-1.0mm, and the thickness of patterned layer 2 is 15-20 μ m, and the thickness of background layer 3 is 15-30 micron.
Particularly, this patterned layer 2 is to form with the ink printing of the metal film 20 that contains ultra-fine layer structure.Wherein metal film 20 is, under vacuum condition, evaporation of metal is deposited as to membrane structure, then be crushed to certain particle diameter, in concrete example of the present utility model, thicknesses of layers is 20-100 nanometer, be of a size of 4-8 micron, metal film 20 after pulverizing be uniformly distributed and the parallel resin that spreads over ink in, a plurality of metal films 20 are uniformly distributed and parallel spreading in patterned layer 2.The weight of metal film 20 accounts for the 20-60% of the total weight of patterned layer 2.It should be noted that, the total weight of patterned layer 2 refers to the weight sum of ink layer and metal film 20.Wherein require the metal film 20 in the ink layer after printing parallelly to sprawl, as shown in the arrow in Fig. 2, incident optical energy reflects away to greatest extent, obtains the appearance effect of superbright.
Background layer 3 is located on all the other lower surfaces of sheet material 1 and the lower surface of patterned layer 2.Wherein background layer 3 provides background color for whole product, and protects patterned layer 2 not to be damaged.
According to the mobile terminal shell 100 of the utility model embodiment, patterned layer 2 adopts the ink printing that contains metal film 20, after printing, 20 pairs of incident lights of the metal film of stratiform have stronger reflection, thereby make the patterned layer 2 of mobile terminal shell 100 have the appearance effect of superbright.And because patterned layer 2 is between sheet material 1 and background layer 3, guarantee that patterned layer 2 in use can not be scratched or wear and tear, durable in use, this mobile terminal shell 100 is simple in structure simultaneously, is convenient to machine-shaping.
In examples more of the present utility model, background layer 3 is ink layer, and now require has stable color performance in printing process, can not corrode dried patterned layer 2.
As shown in Figure 1, in specific embodiment of the utility model, sheet material 1 comprises: Merlon (PC) layer and add hard formation 11, add on the upper surface that hard formation 11 is positioned at layer of polycarbonate 10, the hardness that adds hard formation 11 is greater than the hardness of layer of polycarbonate 10, and patterned layer 2 is located on the lower surface of layer of polycarbonate 10.Thereby make sheet material 1 there is good physical and chemical performance, can improve the hardness of sheet material 1.Particularly, add hard formation 11 for polyorganosiloxane resin layer.Wherein, between patterned layer 2 and layer of polycarbonate 10, to there is good adhesion.
Further, mobile terminal shell 100 also comprises transition resin bed 12, and transition resin bed 12 is at layer of polycarbonate 10 and add between hard formation 11, and particularly, transition resin bed 12 is acrylic (PMMA) layer.That is to say, on the upper surface of layer of polycarbonate 10, be compounded with one deck acrylic layer 12, then on the surface of acrylic layer 12, carry out stiffened, for example, adopt spraying technology will add hard formation 11 and be sprayed on transition resin bed 12 surfaces.Now because the degree of crystallinity of acrylic layer 12 is higher, its surperficial stiffened can obtain than higher hardness add hard formation 11, more than hardness can reach 5H, and the overall flexibility of sheet material 1 is better, can carry out the operations such as bending of large radian.If what separately can only obtain maximum hardness 2H hardness at the surperficial stiffened of layer of polycarbonate 10 adds hard formation 11.
Particularly, add hard formation 11 and require have good planarization and light transmittance, light transmittance is greater than 90%, guarantee fully curing, to obtain high hardness; In addition, adding hard formation 11 need to have certain ductility, guarantees when moulding stretches not by drawing crack.
Acrylic layer 12, for to be compounded in the resin bed on layer of polycarbonate 10, requires light transmittance higher than 92%, and good forming ability has good adhesive force with layer of polycarbonate 10, and both thermal contraction deflections are close.
Layer of polycarbonate 10 is the matrix resin of sheet material 1, requires light transmittance higher than 90%, and good forming ability.
As shown in Figure 1, according to the mobile terminal shell 100 of the utility model preferred embodiment, comprise: sheet material 1, patterned layer 2 and background layer 3, sheet material 1 is by layer of polycarbonate 10, transition resin bed 12 and add hard formation 11 and form, background layer 3 is ink layer, now mobile terminal shell 100 machine-shaping in the following way: by the sheet material of selecting 1 in oven for baking, to remove internal stress wherein, prevent that in printing or forming process Stress Release causes cracking or other is bad.Toasted and cooling after; at the lower surface of layer of polycarbonate 10, use the required LOGO of ink printing and other pattern to form patterned layer 2; after dry; printing background color or protection ink are to form background layer 3; to product, give different colors and protect patterned layer 2 not to be damaged in operating process; guaranteeing has release agent or similar additive in last one deck background ink of background layer 3, and while preventing subsequent forming, ink adheres on mould.
After being completed for printing, ink setting is complete, be then placed in high-pressure molding mould and carry out high-pressure molding, mold required shape, take out cooling after, by CNC(computer-aided, process) all leftover bits and pieces of material are cut away, obtain required product.
Wherein, it should be noted that, high-pressure molding refers to the pressure by gases at high pressure, softening sheet material 1 is formed into the process of required form.CNC refers to milling cutter, according to predefined Program path, cuts and obtains product.
To adopt two specific embodiments to being described according to the processing method of the mobile terminal shell 100 of the utility model embodiment below.
Embodiment 1:
(1) prebake conditions: sheet material 1 is cut into required size, and sheet metal thickness is 0.3mm, tears its surperficial diaphragm off, is laid on grill, then grill is placed in to baking box, toasts 2 hours at 80 ℃, then takes out cooling.
(2) printed patterns and LOGO are to form patterned layer 2, and ink paint model is beautiful magnificent JM-80004DY, and the aluminium film content in ink is 40%, and average grain diameter is 6 microns of left and right, and printing thickness 16 μ m toast 1 hour at 80 ℃.
(3) printing background ink is to form background layer 3, and ink paint model is beautiful magnificent IPL-1021C, and ink is white, printing thickness 16 μ m; And then printing beautiful magnificent QIPL-534856, ink is grey, has wherein added 0.5% levelling agent XC3-210, printing thickness 16 μ m; At 80 ℃, toast and be dried completely for 4 hours.
(4) set 350 ℃ of bakings of gases at high pressure former baking temperature 30 seconds, high-pressure 50KG, 30 seconds dwell times, 5 seconds pressure release time.The dried sheet material 1 of printing is placed in to gases at high pressure mould, at 350 ℃, toast 30 seconds softening after, after matched moulds, pour pressure-air, it is pasted on bed die face, obtain predefined shape, after pressure release, die sinking is taken out, cooling.
(5) the cooled sheet material 1 of moulding is fixed on CNC cutting tool, according to the 2D/3D figure of final products, sets CNC cutter cutting path, the speed of mainshaft is set: 5000r/min, feed speed: 1000mm/min cuts, obtains product.
Embodiment 2:
(1) prebake conditions: sheet material 1 is cut into required size, and sheet metal thickness is 0.3mm, tears its surperficial diaphragm off, is laid on grill, then grill is placed in to baking box, toasts 2 hours at 80 ℃, then takes out cooling.
(2) printed patterns and LOGO are to form patterned layer 2, and ink paint model is beautiful magnificent JM-80004DY, and the aluminium film content in ink is 50%, and average grain diameter is 8 microns of left and right, and printing thickness 15 μ m toast 1 hour at 80 ℃.
(3) printing background ink is to form background layer 3, and ink paint model is beautiful magnificent IPL-1021C, and ink is white, printing thickness 15 μ m; And then printing beautiful magnificent QIPL-534856, ink is grey, has wherein added 0.5% levelling agent XC3-210, printing thickness 15 μ m; At 80 ℃, toast and be dried completely for 4 hours.
(4) set 350 ℃ of bakings of gases at high pressure former baking temperature 28 seconds, high-pressure 60KG, 30 seconds dwell times, 8 seconds pressure release time.The dried sheet material 1 of printing is placed in to gases at high pressure mould, at 350 ℃, toast 30 seconds softening after, after matched moulds, pour pressure-air, it is pasted on bed die face, obtain predefined shape, after pressure release, die sinking is taken out, cooling.
(5) the cooled sheet material 1 of moulding is fixed on CNC cutting tool, according to the 2D/3D figure of final products, sets CNC cutter cutting path, the speed of mainshaft is set: 5000r/min, feed speed: 1000mm/min cuts, obtains product.
According to the mobile terminal shell 100 of the utility model embodiment, thickness can be low to moderate 0.33mm, has complied with the lightening trend of the electronic products such as present mobile phone; Its case hardness is high, more than can arriving 5H, far surpasses common spraying and IML product; Patterned layer 2 adopts the ink printing of the aluminium film 20 that contains ultra-fine layer structure, and after printing, parallel the sprawling of aluminium film 20 of stratiform, has stronger reflection to incident light, and outward appearance has the effect of superbright; The patterned layer 2 of product is between sheet material 1 and background layer 3, and 1 layer of sheet material has fabulous physical and chemical performance, guarantees that inner patterned layer 2 in use can not be scratched or wear and tear, durable in use; This product can be assembled on the miscellaneous part of electronic product by marine glue, plays the effect of complete machine waterproof.Its technique is simple, with low cost.
In the description of this specification, the description of reference term " embodiment ", " some embodiment ", " illustrative examples ", " example ", " concrete example " or " some examples " etc. means to be contained at least one embodiment of the present utility model or example in conjunction with specific features, structure, material or the feature of this embodiment or example description.In this manual, the schematic statement of above-mentioned term is not necessarily referred to identical embodiment or example.And the specific features of description, structure, material or feature can be with suitable mode combinations in any one or more embodiment or example.
Although illustrated and described embodiment of the present utility model, those having ordinary skill in the art will appreciate that: in the situation that not departing from principle of the present utility model and aim, can carry out multiple variation, modification, replacement and modification to these embodiment, scope of the present utility model is limited by claim and equivalent thereof.
Claims (10)
1. a mobile terminal shell, is characterized in that, comprising:
Sheet material;
Patterned layer, described patterned layer is located on the part lower surface of described sheet material, and described patterned layer is to be provided with a plurality of metal films in ink layer and described patterned layer;
Background layer, described background layer is located on all the other lower surfaces of described sheet material and the lower surface of described patterned layer.
2. mobile terminal shell according to claim 1, is characterized in that, described in each, metal film is of a size of 4-8 micron, and described in each, the thickness of metal film is 20-100 nanometer.
3. mobile terminal shell according to claim 1, is characterized in that, the weight of described metal film accounts for the 20-60% of the total weight of described patterned layer.
4. mobile terminal shell according to claim 1, is characterized in that, described a plurality of metal films are uniformly distributed and parallel spreading in described patterned layer.
5. mobile terminal shell according to claim 1, it is characterized in that, described sheet material comprises: layer of polycarbonate and add hard formation, described adding on the upper surface that hard formation is positioned at described layer of polycarbonate, the described hardness that adds hard formation is greater than the hardness of described layer of polycarbonate, and described patterned layer is located on the lower surface of described layer of polycarbonate.
6. mobile terminal shell according to claim 5, is characterized in that, also comprises transition resin bed, described transition resin bed described layer of polycarbonate and described in add between hard formation.
7. mobile terminal shell according to claim 6, is characterized in that, described transition resin bed is acrylic layer.
8. mobile terminal shell according to claim 5, is characterized in that, described in to add hard formation be polyorganosiloxane resin layer.
9. according to the mobile terminal shell described in any one in claim 1-8, it is characterized in that, the thickness of described sheet material is 0.3-1.0mm; The thickness of described patterned layer is 15-20 μ m, and the thickness of described background layer is 15-30 micron.
10. mobile terminal shell according to claim 1, is characterized in that, described background layer is ink layer.