CN203159521U - Surface protection sheet - Google Patents
Surface protection sheet Download PDFInfo
- Publication number
- CN203159521U CN203159521U CN 201220622650 CN201220622650U CN203159521U CN 203159521 U CN203159521 U CN 203159521U CN 201220622650 CN201220622650 CN 201220622650 CN 201220622650 U CN201220622650 U CN 201220622650U CN 203159521 U CN203159521 U CN 203159521U
- Authority
- CN
- China
- Prior art keywords
- substrate layer
- black
- color system
- white color
- protective plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a surface protection sheet. The outermost surface of a base material layer is subjected to surface roughening to an extent that foreign substances are not obvious even though existing between the surface protection sheet and adhered objects, no matter the adhered objects have smooth surfaces or rough surfaces, the surface protection sheet can show full and appropriate adhesion force. The surface protection sheet provided by the utility model sequentially comprises a white base material layer, a black base material layer and a bonding layer; the surface roughness Ra at the outermost surface of the white base material layer is above 0.30 micron; the surface undulation degree Wa of the outermost surface of the white base material layer is 0.40 micron-0.60 micron; and the gloss of the 60-degree glossy outermost surface of the white base material layer is below 65.
Description
Technical field
The utility model relates to a kind of surface protective plate.Specifically, the utility model relates to and comprises the white color system substrate layer successively, black is the surface protective plate of substrate layer and bonding coat, and this white color system substrate layer is outermost surface protective plate.Surface protective plate of the present utility model is for example being carried, when opticses such as parts, polarizing coating, liquid crystal panel, electronic unit etc. such as processing or maintenance metal sheet, coated plate, aluminum alloy frame, resin board, decorative steel plate, vinylchlorid laminate steel, sheet glass, can be used for sticking on these the surface purposes to protect etc.
Background technology
Surface protective plate is provided with bonding coat in a side of substrate layer usually.As the method for making such surface protective plate that comprises substrate layer and bonding coat, the method (for example, with reference to patent documentation 1) that substrate layer and bonding coat are formed as one by coextrusion has been proposed.
From rakish viewpoint, the outmost surface of the substrate layer in the surface protective plate is preferably smoothly sometimes.Yet; if the outmost surface of the substrate layer in the surface protective plate is too level and smooth; then can cause the problem that the foreign matter that is present between this surface protective plate and the adherend is apparent in view, the sense of touch variation is such, also can cause the such problem of precise decreasing of visual inspection, also can have influence on productivity.
In addition, with regard to existing surface protective plate, to the insufficient and immoderation of bonding force under the attaching state of adherend.Therefore, when the adherend that has attached existing surface protective plate is processed etc., exist the part of this surface protective plate can peel off such problem.The situation of the insufficient and immoderation of the bonding force that the low speed when for example, having 23 ℃ is peeled off, paste the situation of the insufficient and immoderation of same bonding force after 1 week.
And then there is the low such problem of cementability to uneven surface in existing surface protective plate.For example, under the situation that pastes the SUS hairline plate that the surface has been carried out hairline processing, have to add to peel off in man-hour etc. or break etc. and can't show the such problem of abundant and appropriate cementability.
The prior art document
Patent documentation
Patent documentation 1: Japanese kokai publication sho 61-103975 communique
Summary of the invention
Problem of the present utility model is, even if the outmost surface that substrate layer is provided by asperities change into foreign matter be present between surface protective plate and the adherend also unconspicuous degree, no matter be the adherend of surface smoothing or the surface protective plate that the adherend of uneven surface can show abundant and appropriate bonding force to it.
Surface protective plate of the present utility model, its for comprise the white color system substrate layer successively, black is the surface protective plate of substrate layer and bonding coat, wherein,
This white color system substrate layer is outermost layer,
The surface roughness Ra of the outmost surface of this white color system substrate layer is more than the 0.30 μ m,
The surface undulation degree Wa of the outmost surface of this white color system substrate layer is 0.40 μ m~0.60 μ m,
The surface gloss of 60 ° of gloss of the outmost surface of this white color system substrate layer is below 65.
In preferred embodiment, above-mentioned white color system substrate layer and described black are that the substrate layer both sides comprise inorganic particulate.
In preferred embodiment, the inorganic particulate in the above-mentioned white color system substrate layer to contain proportional be 0.1 weight %~3.0 weight %.
In preferred embodiment, above-mentioned black be inorganic particulate in the substrate layer to contain proportional be 1.0 weight %~5.0 weight %.
In preferred embodiment, the median size of above-mentioned inorganic particulate is 5 μ m~10 μ m.
In preferred embodiment, above-mentioned inorganic particulate is from SiO
2And CaCO
3Middle at least a kind of selecting.
In preferred embodiment, be that substrate layer and above-mentioned bonding coat form as one by coextrusion and form by above-mentioned white color system substrate layer, above-mentioned black.
In preferred embodiment, above-mentioned white color system substrate layer comprises polyethylene-based resin as main component.
In preferred embodiment, above-mentioned polyethylene-based resin comprises Low Density Polyethylene.
In preferred embodiment, above-mentioned black is that substrate layer comprises polyethylene-based resin as main component.
In preferred embodiment, above-mentioned polyethylene-based resin comprises Low Density Polyethylene.
In preferred embodiment, above-mentioned polyethylene-based resin comprises straight chain shape Low Density Polyethylene.
In preferred embodiment, for surface protective plate of the present utility model, the initial stage bonding force with respect to the SUS430BA plate in the time of 23 ℃ is for more than the 1.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed.
In preferred embodiment, for surface protective plate of the present utility model, in the time of 23 ℃ with respect to the bonding force after 1 week of stickup of SUS430BA plate, be for more than the 2.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed.
In preferred embodiment, for surface protective plate of the present utility model, the initial stage bonding force with respect to SUS304 hairline plate in the time of 23 ℃ is for more than the 1.5N/20mm during 180 ° of 0.3m/min are peeled off at draw speed.
In preferred embodiment, for surface protective plate of the present utility model, in the time of 23 ℃ with respect to the bonding force after 1 week of stickup of SUS304 hairline plate, be for more than the 2.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed.
In preferred embodiment, for surface protective plate of the present utility model, breaking tenacity is more than the 20N/20mm.
In preferred embodiment, for surface protective plate of the present utility model, elongation is more than 200% during fracture.
The effect of utility model
According to the utility model, even if the outmost surface that substrate layer can be provided by asperities change into foreign matter be present between surface protective plate and the adherend also unconspicuous degree, no matter be the adherend of surface smoothing or the surface protective plate that the adherend of uneven surface can both show abundant and appropriate bonding force to it.
Description of drawings
Fig. 1 is the sectional view that schematically shows a configuration example of surface protective plate of the present utility model.
Embodiment
Surface protective plate of the present utility model for comprise the white color system substrate layer successively, black is the surface protective plate of substrate layer and bonding coat.An outermost side of surface protective plate of the present utility model is the white color system substrate layer.Surface protective plate of the present utility model can also contain other suitable arbitrarily layers in the scope of not damaging effect of the present utility model.
The integral thickness of surface protective plate of the present utility model is preferably 30 μ m~150 μ m, 35 μ m~140 μ m more preferably, and more preferably 40 μ m~130 μ m are preferably 45 μ m~120 μ m especially, most preferably are 50 μ m~110 μ m.Be adjusted in the above-mentioned scope by the integral thickness with surface protective plate of the present utility model, can become the surface protective plate that operability is excellent and have sufficient mechanical.
The white color system substrate layer is the layer of the tone of display white system, and for example, the whiteness of stipulating among the JIS-L-1015 is preferably more than 60%, more preferably more than 70%, more preferably more than 80%, is preferably more than 85% especially.The white color system substrate layer preferably comprises white pigment.As white pigment, can adopt suitable white pigment arbitrarily.As such white pigment, for example can enumerate titanium oxide.Contain at the white color system substrate layer under the situation of white pigment, with respect to the resinous principle that forms the white color system substrate layer, it contains the proportional 0.1 weight %~50 weight % that are preferably, more preferably 1 weight %~40 weight %, more preferably 2 weight %~30 weight %.By with contain proportional be adjusted into above-mentioned scope in of white pigment with respect to the resinous principle that forms the white color system substrate layer, can make the surface protective plate of weathering resistance excellence, plasticity such as extrudability is also excellent.
The resinous principle that forms the white color system substrate layer is preferably polyolefin-based resins.As polyolefin-based resins, particularly, for example can enumerate high density polyethylene(HDPE) (HDPE), medium-density polyethylene, Low Density Polyethylene (LDPE), straight chain shape Low Density Polyethylene (LLDPE), polypropylene, the propylene resin that is formed by propylene composition and ethene composition, poly-1-butylene, poly--4-methyl-1-pentene, ethylene-propylene copolymer, ethene-butene-1 copolymer, ethene-1-hexene copolymer, ethene-4 methyl 1 pentene copolymer, ethene-1-octene copolymer, ethylene-methyl acrylate copolymer, the ethylene-methyl methacrylate methyl terpolymer, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, ethylene-vinyl alcohol copolymer etc.Form the resinous principle of white color system substrate layer, more preferably acrylic polymer, ethylene-based polymer.As the resinous principle that forms the white color system substrate layer, particularly, preferably can enumerate homo-polypropylene, block polypropylene, Atactic Polypropelene, high density polyethylene(HDPE) (HDPE), medium-density polyethylene, Low Density Polyethylene (LDPE), straight chain shape Low Density Polyethylene (LLDPE).The white color system substrate layer preferably comprises vinylite as main component.Density as this polyethylene-based resin is preferably 0.880g/cm
3~0.940g/cm
3, 0.880g/cm more preferably
3~0.923g/cm
3, 0.880g/cm more preferably
3~0.915g/cm
3By comprising polyethylene-based resin as main component in the white color system substrate layer, the white color system substrate layer can have thermotolerance, solvent resistance, flexible thus, and can be with surface protective plate of the present utility model coiling tubular easily.Comprise in the white color system substrate layer under the situation of polyethylene-based resin as main component, this polyethylene-based resin preferably comprises Low Density Polyethylene.By in above-mentioned polyethylene-based resin, comprising Low Density Polyethylene, can make the white color system substrate layer have sufficient thermotolerance, solvent resistance, flexible thus, can be with surface protective plate of the present utility model coiling tubular more easily.
At this, " main component " refers to be preferably more than the 50 weight % in the utility model, more preferably more than the 60 weight %, more preferably more than the 70 weight %, is preferably especially more than the 80 weight %, most preferably is more than the 90 weight %.
Polyolefin-based resins in the white color system substrate layer contain proportional being preferably more than the 60 weight %, more preferably more than the 70 weight %, more preferably more than the 80 weight %, be preferably especially more than the 85 weight %, most preferably be more than the 90 weight %.Such polyolefin-based resins can only use a kind, also can use more than 2 kinds.
The thickness of white color system substrate layer can adopt suitable thickness arbitrarily according to purpose.Such thickness is preferably 2 μ m~100 μ m, 3 μ m~80 μ m more preferably, and more preferably 4 μ m~60 μ m are preferably 5 μ m~50 μ m especially.
Black is that substrate layer is the layer that shows the tone of black system.Black is that substrate layer preferably comprises black pigment.As black pigment, can adopt suitable black pigment arbitrarily.As such black pigment, for example can enumerate carbon black.Be to contain in the substrate layer under the situation of black pigment at black, with respect to the resinous principle that forms black system layer, it contains the proportional 0.01 weight %~10 weight % that are preferably, more preferably 0.1 weight %~5 weight %, more preferably 0.5 weight %~3 weight %.By with black pigment with respect to form black be substrate layer resinous principle contain proportional being adjusted in the above-mentioned scope, then can make the surface protective plate of weathering resistance excellence, plasticity such as extrudability is also excellent.
Formation black is that the resinous principle of substrate layer is preferably polyolefin-based resins.As polyolefin-based resins, particularly, for example can enumerate high density polyethylene(HDPE) (HDPE), medium-density polyethylene, Low Density Polyethylene (LDPE), straight chain shape Low Density Polyethylene (LLDPE), polypropylene, the propylene resin that is formed by propylene composition and ethene composition, poly-1-butylene, poly--4-methyl-1-pentene, ethylene-propylene copolymer, ethene-butene-1 copolymer, ethene-1-hexene copolymer, ethene-4 methyl 1 pentene copolymer, ethene-1-octene copolymer, ethylene-methyl acrylate copolymer, the ethylene-methyl methacrylate methyl terpolymer, ethylene-vinyl acetate copolymer, ethylene-ethyl acrylate copolymer, ethylene-vinyl alcohol copolymer etc.The resinous principle that forms black and be substrate layer is acrylic polymer, ethylene-based polymer more preferably.Be the resinous principle of substrate layer as forming black, particularly, preferably can enumerate homo-polypropylene, block polypropylene, Atactic Polypropelene, high density polyethylene(HDPE) (HDPE), medium-density polyethylene, Low Density Polyethylene (LDPE), straight chain shape Low Density Polyethylene (LLDPE).Black is that substrate layer preferably comprises polyethylene-based resin as main component.Density as this polyethylene-based resin is preferably 0.880g/cm
3~0.940g/cm
3, 0.880g/cm more preferably
3~0.923g/cm
3, 0.880g/cm more preferably
3~0.915g/cm
3By being to comprise polyethylene-based resin in the substrate layer as main component at black, substrate layer can have thermotolerance, solvent resistance, flexible, and can be with surface protective plate of the present utility model coiling tubular easily.Be to comprise in the substrate layer under the situation of polyethylene-based resin as main component at black, this polyethylene-based resin preferably comprises at least a kind that selects from Low Density Polyethylene and straight chain shape Low Density Polyethylene.By in above-mentioned polyethylene-based resin, comprising at least a kind that from Low Density Polyethylene and straight chain shape Low Density Polyethylene, selects; black is that substrate layer can have sufficient thermotolerance, solvent resistance, flexible thus, and can be with surface protective plate of the present utility model coiling tubular more easily.
Black is proportional being preferably more than the 60 weight % that contain of polyolefin-based resins in the substrate layer, more preferably more than the 70 weight %, more preferably more than the 80 weight %, is preferably especially more than the 85 weight %, most preferably is more than the 90 weight %.Such polyolefin-based resins can only use a kind, also can use more than 2 kinds.
Black is the thickness of substrate layer, can adopt suitable thickness arbitrarily according to purpose.Such thickness is preferably 2 μ m~100 μ m, 3 μ m~80 μ m more preferably, and more preferably 4 μ m~60 μ m are preferably 5 μ m~50 μ m especially.
White color system substrate layer and black are preferably to comprise inorganic particulate among the substrate layer both sides.As such inorganic particulate, so long as just can use as the known material of inorganic particulate usually, but in order fully to show effect of the present utility model, be preferably from SiO
2And CaCO
3Middle at least a kind of selecting.The inorganic particulate that comprises in the white color system substrate layer and black are that the inorganic particulate that comprises in the substrate layer can be that inorganic particulate of the same race also can be inorganic particulate not of the same race, and the viewpoint from cost etc. is preferably inorganic particulate of the same race.
Fig. 1 is that to schematically show white color system substrate layer and black be the sectional view that comprises a configuration example of the surface protective plate of the present utility model under the situation of inorganic particulate among the substrate layer both sides.In Fig. 1, schematically illustrated surface protective plate 100 of the present utility model has a configuration example under the situation of stacked formation of " white color system substrate layer 21/ black is substrate layer 22/ bonding coat 10 ".Reaching black in white color system substrate layer 21 is to comprise inorganic particulate 30 in the substrate layer 22.
In the white color system substrate layer, comprise under the situation of inorganic particulate, inorganic particulate in the white color system substrate layer contain the proportional 0.1 weight %~3.0 weight % that are preferably, more preferably 0.5 weight %~2.5 weight %, more preferably 1.0 weight %~2.0 weight %.By with containing of the inorganic particulate in the white color system substrate layer of proportional being adjusted in this scope, be present between surface protective plate and the adherend also unconspicuous degree even if can make the abundant asperities of the outmost surface of substrate layer change into foreign matter thus.Containing under the proportional situation less than 0.1 weight % of inorganic particulate in the white color system substrate layer, if having foreign matter between surface protective plate and adherend, then when observing the outmost surface of substrate layer, foreign matter might be obvious.Containing of inorganic particulate in the white color system substrate layer is proportional when surpassing 3.0 weight %, the dispersion that not only causes white pigment easily is bad, the coming off of inorganic particulate, and the intensity rerum natura of film is descended and adds the damage to adherend that the film fracture takes place man-hour or follow with it at adherend.
Comprise in the white color system substrate layer under the situation of inorganic particulate, the median size of inorganic particulate is preferably 5 μ m~10 μ m, more preferably 5 μ m~9 μ m, more preferably 6 μ m~9 μ m.Be adjusted in this scope by the median size that makes inorganic particulate, be present between surface protective plate and the adherend also unconspicuous degree even if can make the abundant asperities of the outmost surface of substrate layer change into foreign matter thus.Under the situation of median size less than 5 μ m of inorganic particulate, if foreign matter is present between surface protective plate and the adherend, might the foreign matter apparition during outmost surface of then observing substrate layer.Median size at inorganic particulate surpasses under the situation of 10 μ m, the dispersion that not only causes white pigment easily is bad, the coming off of inorganic particulate, and the intensity rerum natura of film is descended and adds the damage to adherend that the film fracture takes place man-hour or follow with it at adherend.
Be to comprise in the substrate layer under the situation of inorganic particulate at black, black is the proportional 1.0 weight %~5.0 weight % that are preferably that contain of inorganic particulate in the substrate layer, more preferably 1.5 weight %~4.5 weight %, more preferably 2.0 weight %~4.0 weight %.Be proportional being adjusted in this scope that contain of inorganic particulate in the substrate layer by making black, be present between surface protective plate and the adherend also unconspicuous degree even if can make the abundant asperities of the outmost surface of substrate layer change into foreign matter.Be containing under the proportional situation less than 1.0 weight % of inorganic particulate in the substrate layer at black, if foreign matter is present between surface protective plate and the adherend, when then observing the outmost surface of substrate layer, foreign matter might be obvious.Be under containing of inorganic particulate in the substrate layer of the proportional situation that surpasses 5.0 weight % at black, the Wa that rises and falls from the inside of film might become excessive, and bonding force extremely reduces.
White color system substrate layer, black are that substrate layer can contain any suitable additive.As such additive, can enumerate for example antioxidant, UV light absorber, antiaging agent, photostabilizer, antistatic agent, surface lubricant, flow agent, softening agent, low-molecular(weight)polymer, sanitas, stopper, silane coupling agent, inorganic and organic weighting agent (for example calcium oxide, magnesium oxide, silicon-dioxide, zinc oxide, titanium oxide etc.), metal powder, tinting material, pigment, heat-resisting stabilizing agent, preventing materials accumulation agent Japanese: order ヤ ニ prevents from cuing open), lubrication prescription, antiblocking agent etc.
White color system substrate layer, black are that substrate layer preferably comprises Photostabilised dose.Be that substrate layer comprises Photostabilised dose by white color system substrate layer, black, can give sufficient weathering resistance to surface protective plate of the present utility model.
As Photostabilised dose, in the scope of not damaging effect of the present utility model, can adopt any suitable Photostabilised dose.As such Photostabilised dose, for example preferably can enumerate hindered amine is Photostabilised dose (HALS).
Be that substrate layer comprises under Photostabilised dose the situation at white color system substrate layer, black; weight with respect to surface protective plate integral body of the present utility model; this Photostabilised dose contain proportional being preferably more than the 0.10 weight %; 0.20 weight %~0.64 weight % more preferably; more preferably 0.30 weight %~0.60 weight % is preferably 0.34 weight %~0.55 weight % especially.Be that substrate layer comprises under Photostabilised dose the situation at white color system substrate layer, black; as long as will this Photostabilised dose to contain the proportional weight that is adjusted to respect to surface protective plate integral body of the present utility model be in the above-mentioned scope, then can give weathering resistance more fully to surface protective plate of the present utility model.
Can implement the back side to the outmost surface of white color system substrate layer handles.Method as handle at the back side can adopt any appropriate means in the scope of not damaging effect of the present utility model.As the method that handle at such back side, for example can enumerate surface working such as embossing processing or concavo-convex processing, make it to contain the method for derivative of fatty acid etc.Such derivative of fatty acid can only be a kind of, also can be for two or more.
Comprise at the white color system substrate layer under the situation of derivative of fatty acid, with respect to the resinous principle in the white color system substrate layer, derivative of fatty acid in the white color system substrate layer contain the proportional 0.05 weight %~1.00 weight % that are preferably, more preferably 0.10 weight %~0.90 weight %, more preferably 0.30 weight %~0.80 weight %.As long as with containing of the derivative of fatty acid in the white color system substrate layer, proportional to be adjusted to respect to the resinous principle in the white color system substrate layer be in the above-mentioned scope; then can easily make the surface protective plate uncoiling of the present utility model of making drum; embody stripping result fully, can suppress fully simultaneously because of the pollution due to the oozing out of this derivative of fatty acid.
As derivative of fatty acid, refer to comprise in the molecular structure compound of derivative of fatty acid structure.
As derivative of fatty acid, for example can enumerate saturated fatty acid bisamide, unsaturated fatty acids bisamide, fragrant family bisamide, substituted ureas, fatty acid metal salt etc.As derivative of fatty acid, particularly, for example can enumerate methylene-bis stearic amide, ethylenebis stearic amide, ethylenebisoleaamide, ethylenebis mountain Yu acid acid amides, N, N-two oleyl hexanodioic acid acid amides, N-stearyl-N '-N-stearyl-N '-stearic amide, Zinic stearass etc. such as stearyl urea.
As derivative of fatty acid, be preferably fatty acid amide, more preferably from methylene-bis stearic amide, ethylenebis stearic amide, ethylenebis mountain Yu acid acid amides, N-stearyl-N '-stearic amide, select at least a kind.
The preferred fusing point of derivative of fatty acid is more than 100 ℃.Fusing point is less than 100 ℃ derivative of fatty acid, becomes significantly to the transfer printing on bonding coat surface, and the decline of bounding force might take place easily.
The thickness of bonding coat is preferably 1 μ m~50 μ m, 2 μ m~40 μ m more preferably, and more preferably 3 μ m~30 μ m are preferably 4 μ m~20 μ m especially, most preferably are 5 μ m~10 μ m.Be adjusted in the above-mentioned scope by the thickness with bonding coat, when utilizing coextrusion to be shaped manufacturing surface protective plate of the present utility model, the control transfiguration that layer constitutes is easy, in addition, can obtain having the surface protective plate of sufficient mechanical thus.
Bonding coat preferably comprises thermoplastic resin as main component.The contained thermoplastic resin of bonding coat can only be a kind, also can be for more than 2 kinds.
As thermoplastic resin, can adopt suitable thermoplastic resin arbitrarily.As such thermoplastic resin, for example can enumerate ethylene series resin, the olefin/diene copolymers that contains aromatic group, phenylethylene resin series, ester is resin etc.In these thermoplastic resins, optimization styrene is resin, more preferably styrene series thermoplastic elastomer.
As styrene series thermoplastic elastomer, preferably can enumerate hydrogenated styrene-divinyl rubber (HSBR), styrene block copolymer or its hydride.
As styrene block copolymer, for example can enumerate styrene-butadiene-styrene multipolymer (SBS), styrene-isoprene-styrene copolymer-polystyrene ABA block polymer (triblock copolymer) such as (SIS); Styrene-butadiene-styrene-butadienecopolymer (SBSB), styrene-isoprene-phenylethene-isoprene copolymer polystyrene ABAB type segmented copolymers (Tetrablock copolymer) such as (SISI); Styrene-butadiene-styrene-butadiene-styrene copolymer (SBSBS), styrene-isoprene-phenylethene-isoprene-styrol copolymer polystyrene ABABA type segmented copolymers (five segmented copolymers) such as (SISIS); Styrene block copolymer with its above AB repeating unit; Deng.
As the hydride of styrene block copolymer, for example can enumerate the multipolymer (SEBSEB) of styrene-ethylene-butylene copolymer-styrol copolymer (SEBS), styrene-ethylene-propylene copolymer-styrol copolymer (SEPS), styrene-ethylene-butylene copolymer-styrene-ethylene-butylene copolymer; Deng.
Styrene series thermoplastic elastomer can only use a kind, also can use more than 2 kinds.
Styrene content in the styrene series thermoplastic elastomer (being styrene block content under the situation of styrene block copolymer) is preferably 5 weight %~13 weight %, 1 weight %~20 weight % more preferably, more preferably 2 weight %~18 weight % are preferably 3 weight %~15 weight % especially.By above-mentioned styrene content is adjusted in the above-mentioned scope, for surface protective plate of the present utility model, can show abundant and appropriate bonding force to it regardless of the adherend or the adherend of uneven surface that are surface smoothing thus.If above-mentioned styrene content tails off, the not enough caused cull of cohesive force because of bonding coat then might take place easily.If it is many that above-mentioned styrene content becomes, then bonding coat hardening might can't obtain the binding property good with respect to uneven surface.
As styrene series thermoplastic elastomer, preferably has the hydride (SEBS, SEBSEB, SEBSEBS etc.) of the styrene block copolymer of the repeating structure (ABA type, ABAB type, ABABA type etc.) more than the triblock copolymer that is formed by vinylbenzene (A) and divinyl (B).By adopting such styrene series thermoplastic elastomer, more fully and moderately show thus the bonding force under the attaching state of adherend, on the other hand, the bonding force that attaches to when peeling off behind the adherend is more abundant and appropriate size, therefore just can easily peel off from adherend with the slight power of appropriateness, and then, can be fully and moderately show the bonding force that exposes to the sun in the carrying capacity of the environment of prolonged preservation.
Under the situation of hydride (SEBS, SEBSEB, SEBSEBS etc.) of styrene series thermoplastic elastomer for styrene block copolymer with the repeating structure (ABA type, ABAB type, ABABA type etc.) more than the triblock copolymer that is formed by vinylbenzene (A) and divinyl (B), butylene structure shared ratio in the ethylene-butene copolymer block is preferably more than the 60 weight %, more preferably more than the 70 weight %, more preferably more than the 75 weight %.By butylene structure shared ratio in above-mentioned ethylene-butene copolymer block is adjusted in the above-mentioned scope, bonding force when more fully and moderately showing the attaching state to adherend thus, on the other hand, the bonding force that attaches to when peeling off behind the adherend is more abundant and appropriate size, therefore, just can more easily peel off from adherend with the power that appropriateness is slight, and then, can be fully and moderately show the bonding force that exposes to the sun in the carrying capacity of the environment of prolonged preservation.Need to prove that above-mentioned butylene structure shared ratio in the ethylene-butene copolymer block is preferably below the 90 weight %.
In order to carry out fusible adjusting etc., bonding coat can contain other styrene series thermoplastic elastomers in the scope of not damaging the purpose of this utility model.
As other styrene series thermoplastic elastomer, can enumerate above-mentioned styrene block copolymer in addition; The multipolymer (SEB) of styrene-butadiene copolymer (SB), styrene-isoprene multipolymer (SI), styrene-ethylene-butylene copolymer, the multipolymer AB type block polymers such as (SEP) of styrene-ethylene-propylene copolymer; Styrene butadiene rubbers polystyrene random copolymerss such as (SBR); Vinylbenzene-alkene crystal system the block polymer of the multipolymer A-B-C types such as (SEBC) of styrene-ethylene-butylene copolymer-alkene crystallization; The hydride of these materials; Deng.
When forming bonding coat, for control of carrying out adhesion characteristic etc., can suitably add for example tenderizer as required, tackifier, the such polyolefin-based resins that uses in the substrate layer, the silicone-based polymkeric substance, aqueous acrylic copolymer, the phosphoric acid ester based compound, antiaging agent, Photostabilised dose, UV light absorber, surface lubricant, flow agent, softening agent, low-molecular(weight)polymer, antioxidant, sanitas, stopper, silane coupling agent, inorganic and organic weighting agent (for example, calcium oxide, magnesium oxide, silicon-dioxide, zinc oxide, titanium oxide etc.), metal powder, tinting material, pigment, additives such as heat-resisting stabilizing agent.
Can also to the bonding coat surface as required embodiment such as Corona discharge Treatment, uviolizing processing, flame treating, Cement Composite Treated by Plasma, sputter etching processing etc. with the control binding property or to attach operation etc. be the surface treatment of purpose.
It is effective that being engaged in of tackifier improved the bounding force aspect.Wherein, about the use level of tackifier, for fear of taking place because of the caused cull problem of the decline of cohesive force, and can suitably determine according to the adherend of application surface screening glass.With respect to the base polymer of bonding coat, the use level of tackifier is preferably below the 80 weight %, more preferably below the 40 weight %, more preferably below the 20 weight %.
The softening temperature of tackifier is preferably 90 ℃~120 ℃, more preferably 70 ℃~135 ℃, more preferably 80 ℃~130 ℃, is preferably 85 ℃~125 ℃ especially.Be adjusted in the above-mentioned scope by the softening temperature with above-mentioned tackifier, no matter be the adherend of surface smoothing or the adherend of uneven surface, surface protective plate of the present utility model can further show abundant and appropriate bonding force to it thus.
As tackifier, can use petroleum line resin, coumarone-indenes such as aliphatics based copolymer for example, aromatic series based copolymer, aliphatic-aromatic based copolymer system or ester ring type based copolymer ad lib is that resin, terpenic series resin, terpenes phenolic aldehyde are that rosin series resins such as resin, polymerized rosin, (alkyl) phenolic aldehyde are that resin, diformazan benzene series resin, these hydride etc. are generally used for the material of tackiness agent.Tackifier can only use a kind, also can use more than 2 kinds.In these tackifier, from the viewpoint of separability, weathering resistance etc., the tackifier that preferred hydrogenation is, especially preferred C5 is the hydrogenated aromatic petroleum resin.Need to prove that tackifier also can use with the form of the mixture of olefin resin and commercially available product.
The cooperation of tenderizer is effective to improving bounding force.As tenderizer, for example can enumerate low-molecular-weight diene polymer, polyisobutene, hydrogenated polyisoprene, hydrogenated butadiene polymer, their derivative etc.As such derivative, for example can be illustrated in the material that single end or two ends have OH base or COOH base, particularly, can enumerate hydrogenated butadiene polymer glycol, hydrogenated butadiene polymer single methanol, hydrogenated polyisoprene glycol, hydrogenated polyisoprene single methanol etc.Especially the purpose from the fusible raising with respect to adherend is suppressed, the hydride of diene polymers such as preferred hydrogenated butadiene polymer, hydrogenated polyisoprene or ethylene series tenderizer etc.As such tenderizer, particularly, can obtain the trade(brand)name " KurapreneLIR-200 " of (strain) Kuraray system etc.These tenderizers can only use a kind, also can use more than 2 kinds.
The molecular weight of tenderizer can suitably be set at the amount of any suitable, if molecular weight diminishes, might become then that material from the bonding coat to the adherend is divided a word with a hyphen at the end of a line or the heavy reason of peeling off etc., on the other hand, if the molecule quantitative change is big, then having becomes lacks the tendency of the raising effect of bounding force, so the number-average molecular weight of tenderizer is preferably 5000~100,000, and more preferably 10,000~50,000.
Under the situation of using tenderizer, its addition can suitably be set at the amount of any suitable, but if it is many to add quantitative change, the tendency that cull increases when exposing outside high temperature or room is then arranged, therefore, with respect to the base polymer of bonding coat, be preferably below the 100 weight %, more preferably below the 60 weight %, more preferably below the 40 weight %.
Be purpose with the rising that suppresses bonding force etc., in bonding coat, can also add polyolefin-based resins.Polyolefin-based resins can example illustrate the same resin of resin that uses in the formation with substrate layer.This polyolefin-based resins can only be a kind, also can be for more than 2 kinds.The use level of this polyolefin-based resins is below the 50 weight % with respect to the base polymer of bonding coat preferably, more preferably below the 30 weight %, more preferably below the 20 weight %.
In bonding coat, as required, until for during practicality, also can the temporary adhesion dividing plate etc. protect.
For surface protective plate of the present utility model, the surface roughness Ra of the outmost surface of white color system substrate layer is more than the 0.30 μ m, is preferably 0.30 μ m~1.0 μ m, and more preferably 0.30 μ m~0.8 μ m is preferably 0.30 μ m~0.60 μ m especially.Be adjusted in the above-mentioned scope by the surface roughness Ra with the outmost surface of the white color system substrate layer in the surface protective plate of the present utility model; for surface protective plate of the present utility model, be present between surface protective plate and the adherend also unconspicuous degree even if can make the outmost surface asperities of substrate layer change into foreign matter.Need to prove, about the measuring method of surface roughness Ra, as described later.
For surface protective plate of the present utility model, the surface undulation degree Wa of the outmost surface of white color system substrate layer is 0.40 μ m~0.60 μ m, is preferably 0.42 μ m~0.58 μ m, more preferably 0.45 μ m~0.55 μ m.Be adjusted in the above-mentioned scope by the surface undulation degree Wa with the outmost surface of the white color system substrate layer in the surface protective plate of the present utility model; for surface protective plate of the present utility model, be present between surface protective plate and the adherend also unconspicuous degree even if can make the outmost surface asperities of substrate layer change into foreign matter.Need to prove, about the measuring method of surface undulation degree Wa, as described later.
For surface protective plate of the present utility model, the surface gloss of 60 ° of gloss of the outmost surface of white color system substrate layer is below 65, is preferably 20~65, more preferably 25~60, be preferably 25~55 especially.Be adjusted in the above-mentioned scope by the surface gloss with 60 ° of gloss of the outmost surface of the white color system substrate layer in the surface protective plate of the present utility model; for surface protective plate of the present utility model, also can become very not obvious between surface protective plate and the adherend even if there is foreign matter to be present in.Need to prove, about the measuring method of surface gloss, as described later.
For surface protective plate of the present utility model; the initial stage bonding force with respect to the SUS430BA plate in the time of 23 ℃; be to be preferably more than the 1.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed; 1.0N/20mm~3.0N/20mm more preferably; more preferably 1.2N/20mm~2.8N/20mm is preferably 1.4N/20mm~2.5N/20mm especially.By the above-mentioned initial stage bonding force in the surface protective plate of the present utility model is adjusted in the above-mentioned scope, during surface protective plate of the present utility model low speed is at room temperature peeled off, can show fully and the high bonding force of appropriateness.Need to prove, about the measuring method with respect to the various bonding forces of SUS430BA plate, as described later.
For surface protective plate of the present utility model; in the time of 23 ℃ with respect to the bonding force after 1 week of stickup of SUS430BA plate; be to be preferably more than the 2.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed; 2.0N/20mm~4.0N/20mm more preferably; more preferably 2.0N/20mm~3.8N/20mm is preferably 2.0N/20mm~3.5N/20mm especially.By the above-mentioned bonding force in the surface protective plate of the present utility model is adjusted in the above-mentioned scope; with regard to surface protective plate of the present utility model; in the low speed under the situation of the carrying capacity of environment of prolonged preservation of exposing to the sun was peeled off, surface protective plate of the present utility model can show fully and the high bonding force of appropriateness.Need to prove, about the measuring method with respect to the various bonding forces of SUS430BA plate, as described later.
For surface protective plate of the present utility model; the initial stage bonding force with respect to SUS304 hairline plate in the time of 23 ℃; be to be preferably more than the 1.5N/20mm during 180 ° of 0.3m/min are peeled off at draw speed; 1.5N/20mm~3.0N/20mm more preferably; more preferably 1.5N/20mm~2.8N/20mm is preferably 1.5N/20mm~2.5N/20mm especially.By the above-mentioned initial stage bonding force in the surface protective plate of the present utility model is adjusted in the above-mentioned scope; during surface protective plate of the present utility model low speed is at room temperature peeled off, even if be that the adherend of uneven surface also can show fully and the high bonding force of appropriateness with respect to the surface.Need to prove, about the measuring method with respect to the various bonding forces of SUS304 hairline plate, as described later.
For surface protective plate of the present utility model; in the time of 23 ℃ with respect to the bonding force after 1 week of stickup of SUS304 hairline plate; be to be preferably more than the 2.0N/20mm during 180 ° of 0.3m/min are peeled off at draw speed; 2.0N/20mm~4.0N/20mm more preferably; more preferably 2.0N/20mm~3.8N/20mm is preferably 2.0N/20mm~3.5N/20mm especially.Be adjusted in the above-mentioned scope by the above-mentioned bonding force with surface protective plate of the present utility model; with regard to surface protective plate of the present utility model; in the low speed under the situation of the carrying capacity of environment of prolonged preservation of exposing to the sun is peeled off, even if surface protective plate of the present utility model is that the adherend of uneven surface also can show fully and the high bonding force of appropriateness with respect to the surface.Need to prove, about the measuring method with respect to the various bonding forces of SUS304 hairline plate, as described later.
Need to prove that the material that in this specification sheets, is called " SUS hairline plate " is surperficial by the finished SUS plate of hairline, is to have the SUS plate that surface roughness Ra is the uneven surface of 0.210 μ m~0.310 μ m.This surface roughness Ra is to use contact surfaceness meter, and (SJ400: Mitutoyo Corp (MITUTOYO) system), it is that benchmark is measured that the ridge orientation SUS plate, hairline and the right angle orientation of having carried out hairline processing are measured (condition determination: with JIS-B-0601:(2001).Specifically, at contact pilotage radius 2 μ m, measure under the condition of (cut off) value 0.8mm, measured length 4mm) time value.
For surface protective plate of the present utility model, breaking tenacity is preferably more than the 20N/20mm, 20N/20mm~50N/20mm more preferably, and more preferably 20N/20mm~45N/20mm is preferably 20N/20mm~40N/20mm especially.By the breaking tenacity in the surface protective plate of the present utility model is adjusted in the above-mentioned scope, surface protective plate of the present utility model can show sufficient mechanical.Need to prove, about the measuring method of breaking tenacity, as described later.
For surface protective plate of the present utility model, elongation is preferably more than 200% during fracture, and more preferably 200%~600%, more preferably 200%~500%, be preferably 200%~400% especially.Elongation is adjusted in the above-mentioned scope by with the fracture in the surface protective plate of the present utility model the time, for surface protective plate of the present utility model, can show sufficient mechanical.Need to prove, the measuring method of elongation during about fracture, as described later.
For surface protective plate of the present utility model, be that substrate layer and bonding coat form as one by coextrusion and form by white color system substrate layer, black preferably.Be shaped as coextrusion, can adopt that normally used suitable coextrusion arbitrarily is shaped in the manufacturing of film, sheet material etc.Be shaped as coextrusion, can adopt for example blow moulding, coextrusion T-modulus method etc.From the cost aspect or the productivity aspect consider that preferably these coextrusion are shaped.
The manufacture method of surface protective plate of the present utility model, preferably making white color system substrate layer, black is that substrate layer and bonding coat form as one by coextrusion and made.Thus, can high-level efficiency and make the surface protective plate of the stepped construction with specific thickness at an easy rate.Be shaped as coextrusion, can adopt that normally used suitable coextrusion arbitrarily is shaped in the manufacturing of film, sheet material etc.Be shaped as coextrusion, can adopt for example blow moulding, coextrusion T-modulus method etc.
Be shaped according to coextrusion, because white color system substrate layer and bonding coat do not join under the fusion heated condition, therefore do not generate the by product that the thermal degradation when because of the white color system substrate layer produces, and there be not its by product dividing a word with a hyphen at the end of a line to bonding coat, demonstrate excellent uncoiling, can suppress the pollution on bonding coat surface.
[embodiment]
Below, be specifically described by the utility model of embodiment, but the utility model is not subjected to any restriction of these embodiment.
(mensuration of density)
Density (the g/cm of resin
3) measure the value that obtains for foundation ISO1183.
(mensuration of surface roughness Ra)
Surface protective plate is carried out round attaching on the SUS430BA plate with the 2kg roller.Based on JIS B0601 (2001), with contact pilotage front end footpath 2 μ m, measured length 4mm, cutoff 0.8mm the surface roughness Ra (μ m) of the outmost surface of the white color system substrate layer of the surface protective plate after attaching is measured.
(mensuration of surface undulation degree Wa)
Surface protective plate is carried out round being attached on the SUS430BA plate with the 2kg roller.Use contact pilotage front end footpath 2 μ m, mensuration long 4mm, cutoff 0.8mm, ripple to filter (Waveness filter) 0.8mm (KLA TENCOR corporate system; P-15), the outmost surface side of the white color system substrate layer of the surface protective plate after attach is measured surperficial waviness Wa.
(mensuration of surface gloss)
Use GUARDNER corporate system Micro TRIgloss, carried out the mensuration of 60 ° of corner reflection rates.
(with respect to the mensuration of the initial stage bonding force of SUS430BA plate)
Draw speed is the initial stage bonding forces with respect to the SUS430BA plate during 180 ° of 0.3m/min are peeled off, 23 ℃ the time, measures according to following.
That is, bonding force of above-mentioned initial stage is measured according to JIS-Z-0237 (2000).Particularly, use the SUS430BA plate as adherend, behind the surface with this SUS430BA plate of toluene wash, make 2kg roller round trip crimping evaluation sample, after 30 minutes, use INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph (オ one ト グ ラ Off)), draw speed is set at above-mentioned speed, peels off with 180 ° and measured the initial stage bonding force.At this moment, mensuration environment and preservation environment carry out with 23 ℃/humidity of temperature 50%.
(with respect to the mensuration SUS430BA plate, that paste the bonding force after 1 week)
Draw speed be during 180 ° of 0.3m/min are peeled off, 23 ℃ the time with respect to the bonding force after 1 week of stickup of SUS430BA plate, measure according to following.
That is, above-mentioned bonding force is measured according to JIS-Z-0237 (2000).Particularly, use the SUS430BA plate as adherend, behind the surface with this SUS430BA plate of toluene wash, make 2kg roller round trip crimping evaluation sample, use INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph) through back between above-mentioned preservation period, draw speed is set at above-mentioned speed, peels off with 180 ° and measured bonding force.At this moment, measuring environment carries out with 23 ℃/humidity of temperature 50%.
(with respect to the mensuration of the initial stage bonding force of SUS304 hairline plate)
Draw speed is the initial stage bonding forces with respect to SUS304 hairline plate during 180 ° of 0.3m/min are peeled off, 23 ℃ the time, measures according to following.
That is, bonding force of above-mentioned initial stage is measured according to JIS-Z-0237 (2000).Particularly, use SUS304 hairline plate as adherend, behind the surface with this SUS304 hairline plate of toluene wash, make 2kg roller round trip crimping evaluation sample, after 30 minutes, use INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph), draw speed is set at above-mentioned speed, peels off with 180 ° and measured the initial stage bonding force.At this moment, mensuration environment and preservation environment carry out with 23 ℃/humidity of temperature 50%.
(with respect to mensuration SUS304 hairline plate, that paste the bonding force after 1 week)
Draw speed be during 180 ° of 0.3m/min are peeled off, 23 ℃ the time with respect to the bonding force after 1 week of stickup of SUS304 hairline plate, measure according to following.
That is, above-mentioned bonding force is measured according to JIS-Z-0237 (2000).Particularly, use SUS304 hairline plate as adherend, behind the surface with this SUS304 hairline plate of toluene wash, make 2kg roller round trip crimping evaluation sample, use INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph) through back between above-mentioned preservation period, draw speed is set at above-mentioned speed, peels off with 180 ° and measured bonding force.At this moment, measuring environment carries out with 23 ℃/humidity of temperature 50%.
(mensuration of breaking tenacity)
Breaking tenacity is measured according to following.
Carry out tension test based on JIS-K-7127.Measure the surface protective plate that sample uses the shape of the test film type 2 that is cut into the JIS-K-7127 record, carry out with grip separation 50mm, test film width 10mm, trial speed 300mm/min.In addition, the trier that uses in the mensuration is INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph).Intensity when with N/20mm being the sample fracture of unit when calculating tension test.
(mensuration of elongation during fracture)
Elongation is measured according to following during fracture.
Carry out tension test based on JIS-K-7127.Measure the surface protective plate that sample uses the shape of the test film type 2 that is cut into the JIS-K-7127 record, carry out with grip separation 50mm, test film width 10mm, trial speed 300mm/min.In addition, the trier that uses in the mensuration is INSTRON type tensile testing machine (Shimadzu Seisakusho Ltd.'s corporate system, Autograph).Elongation when being the sample fracture of benchmark when calculating tension test with % in spacing jig from 50mm.
(pliability test)
Pliability test is measured according to following.
Carrying out crimping with the 2kg roller surface protective plate is attached on the stainless steel plate (304HL) of thickness 2.0mm, is after the mode of the opposition side of drift is arranged according to surface protective plate, has carried out metal V bending machining test (V-block method) (JIS-Z-2248).At this moment; with die orifice V angle: 88 degree, die orifice V width (L width): 16 or 12mm, die orifice R:2.0 or 1.0mm, drift angle: the condition of 88 degree, drift R:0.6 is carried out, the cracked situation of surface protective plate takes place after the bending machining to be designated as *, situation about not taking place is designated as zero.In addition, the surface protective plate after the processing is peeled off, confirmed that the stainless steel plate surface has or not scar.The situation that scar takes place is designated as *, situation about not taking place is designated as zero.
(foreign matter identification)
(median size=10 μ m, clear and electrician's system, CB-A10S) sticks on the cotton rod with aluminium oxide particles, makes it be attached to the surface of SUS430BA plate.Wall-attached surface screening glass on the SUS430BA plate of this aluminium oxide particles is arranged in surface attachment, carry out lamination with 0.4MPa after, have or not the particle of nipping by visual observation.The situation of observing the particle of nipping is designated as *, unobserved situation is designated as zero.
(coextrusion shaping condition)
In embodiment and the comparative example, utilize blow moulding to form according to following melt temperature condition.
White color system substrate layer: 165 ℃
Black is substrate layer: 165 ℃
Bonding coat: 165 ℃
Coextrusion temperature: 165 ℃
(embodiment 1)
As shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 2 weight parts in 80 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: Ti-PureR103) 18 weight parts have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 87 weight parts
3) 10 weight parts, and cooperation silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 2 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 1, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (1) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 1.
(embodiment 2)
As shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 2 weight parts in 80 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: Ti-PureR103) 18 weight parts have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 86 weight parts
3) 10 weight parts, and cooperation silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 3 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 1, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (2) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 1.
(embodiment 3)
As shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 2 weight parts in 80 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: Ti-PureR103) 18 weight parts have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 1, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, and cooperation silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 1, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (3) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 1.
(comparative example 1)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=3.5 μ m, Unimin system, MINEX7) 2 weight parts in 80 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: Ti-PureR103) 18 weight parts have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 89 weight parts
3) 10 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C1) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 2)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=3.5 μ m, Unimin system, MINEX7) 7 weight parts in 75 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: Ti-PureR103) 18 weight parts have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 89 weight parts
3) 10 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C2) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 3)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate calcium carbonate (median size=3.2 μ m, Bai Shi Calcium (strain) system, PO-150-B-10) 7 weight parts in 75 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 89 weight parts
3) 10 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C3) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 4)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate calcium carbonate (median size=1.5 μ m, be equipped with northern efflorescence industry (strain) system, Softone 1500) 7 weight parts in 75 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 89 weight parts
3) 10 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARVP140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C4) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 5)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and formed material to cooperate white pigment in 82 weight parts.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, cooperate silicon-dioxide (median size=6.8 μ m, Unimin system, MINEX4) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C5) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 6)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and formed material to cooperate white pigment in 82 weight parts.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, cooperate silicon-dioxide (median size=8.7 μ m, Unimin system, MINEX4F) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C6) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 7)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and formed material to cooperate white pigment in 82 weight parts.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, cooperate silicon-dioxide (median size=3.5 μ m, Unimin system, MINEX7) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C7) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 8)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=8.7 μ m, Unimin system, MINEX4F) 4 weight parts in 78 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, cooperate silicon-dioxide (median size=8.7 μ m, Unimin system, MINEX4F) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C8) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
(comparative example 9)
As shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate silicon-dioxide (median size=8.7 μ m, Unimin system, MINEX4F) 7 weight parts in 75 weight parts, and then (titanium oxide, Dupont system, trade(brand)name: 18 weight parts Ti-Pure R103) have obtained the white color system substrate layer and have formed material to cooperate white pigment.
Then, as shown in table 2, to Low Density Polyethylene (eastern Cao's system, trade(brand)name: Petrothene 186R, density=0.924g/cm
3) cooperate straight chain shape Low Density Polyethylene (Sumitomo Chemical system, trade(brand)name: Excellen FX FX307, density=0.890g/cm in 85 weight parts
3) 10 weight parts, and cooperation silicon-dioxide (median size=8.7 μ m, Unimin system, MINEX4F) 4 weight parts, and then cooperate carbon black MB (firmly change Color system, trade(brand)name: Black SPEMB-865, carbon content 20%) 5 weight parts, having obtained black is that substrate layer forms material.
And then, as shown in table 2, (styrene content=10 weight %, JSR system, trade(brand)name: 82 weight parts and tackifier (C5 is that hydrogenated aromatic petroleum resin, bright dipping emergingly produce, trade(brand)name: I-MARV P140, softening temperature=140 ℃) 18 weight parts DYNARON 1321P) have obtained bonding coat and have formed material to cooperate HSBR.
Using above-mentioned white color system substrate layer formation material, the black that obtains is that substrate layer forms material, bonding coat forms material; be shaped by the coextrusion that utilizes blow moulding, obtain the surface protective plate (C9) (thickness: white color system substrate layer/black is substrate layer/bonding coat=20 μ m/35 μ m/5 μ m) of 3-tier architecture (white color system substrate layer/black is substrate layer/bonding coat).
The results are shown in table 2.
[table 1]
By table 1; table 2 as can be known; for surface protective plate of the present utility model; the surface roughness Ra of the outmost surface of white color system substrate layer is more than the 0.30 μ m; the surface undulation degree Wa of the outmost surface of white color system substrate layer is 0.40 μ m~0.60 μ m; the surface gloss of 60 ° of gloss of the outmost surface of white color system substrate layer is below 65; even if being changed into foreign matter by asperities, the outmost surface of substrate layer is present between surface protective plate and the adherend also unconspicuous degree; no matter the adherend or the adherend of asperities that are surface smoothing can both show abundant and appropriate bonding force to it; breaking tenacity; mechanical characteristics excellence such as elongation during fracture, bendability are also excellent.
Utilize possibility on the industry
Surface protective plate of the present utility model is for example being carried, when opticses such as parts, polarizing coating, liquid crystal panel, electronic unit etc. such as processing or maintenance metal sheet, coated plate, aluminum alloy frame, resin board, decorative steel plate, vinylchlorid laminate steel, sheet glass, can be used for sticking on these the surface purposes to protect etc.
Nomenclature
100 surface protective plates
10 bonding coats
21 white color system substrate layers
22 black are substrate layer
30 inorganic particulates
Claims (2)
1. surface protective plate, its for comprise the white color system substrate layer successively, black is the surface protective plate of substrate layer and bonding coat, wherein,
This white color system substrate layer is outermost layer,
The surface roughness Ra of the outmost surface of this white color system substrate layer is more than the 0.30 μ m,
The surface undulation degree Wa of the outmost surface of this white color system substrate layer is 0.40 μ m~0.60 μ m,
The surface gloss of 60 ° of gloss of the outmost surface of this white color system substrate layer is below 65.
2. surface protective plate as claimed in claim 1, wherein,
Be that substrate layer and described bonding coat form as one by coextrusion and form by described white color system substrate layer, described black.