CN202923051U - BOPET (Biaxially-Oriented Polyethylene Terephthalate) high-imitation metal drawing VCM (Vinyl Chloride Monomer) thin film - Google Patents
BOPET (Biaxially-Oriented Polyethylene Terephthalate) high-imitation metal drawing VCM (Vinyl Chloride Monomer) thin film Download PDFInfo
- Publication number
- CN202923051U CN202923051U CN 201220510493 CN201220510493U CN202923051U CN 202923051 U CN202923051 U CN 202923051U CN 201220510493 CN201220510493 CN 201220510493 CN 201220510493 U CN201220510493 U CN 201220510493U CN 202923051 U CN202923051 U CN 202923051U
- Authority
- CN
- China
- Prior art keywords
- coating
- bopet
- film
- thin film
- vcm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model provides a BOPET (Biaxially-Oriented Polyethylene Terephthalate) high-imitation metal drawing VCM (Vinyl Chloride Monomer) thin film comprising a surface hardened coating, a transparent BOPET thin film, an enhanced fastness coating, a vacuum aluminum-plated layer and an anti-oxidization protection coating in sequence, wherein one single face of the transparent BOPET thin film is subjected to surface drawing treatment; one face of the transparent BOPET thin film, which is subjected to the surface drawing treatment, is connected with the enhanced fastness coating; one face of the transparent BOPET thin film, which is not subjected to the surface drawing treatment, is connected with the surface hardened coating; the surface hardened coating is a polyurethane ultraviolet light cured coating layer; the enhanced fastness coating is a polyurethane coating layer; and the anti-oxidization protection coating is the polyurethane coating layer. Single layer of the BOPET is used as a thin film main body material so that the use amount of a raw material film is greatly reduced and the production and manufacturing cost is saved; and meanwhile, the service lives of products are prolonged and the performance of bearing various bad conditions is improved. The thin film has the best vision effect of a high-imitation metal drawing plate and really realizes the high-imitation aim of the drawing metal plates with different materials.
Description
Technical field
The utility model relates to the high imitative metal wire-drawing VCM film of a kind of BOPET.
Background technology
Non-ferrous metal, nonmetal plate and non-ferrous metal and composite non-metal sheet material, owing to economizing on resources, being easy to processing, with low cost, the application in industry and life is more and more general.Particularly the application of thin plate is more extensive, and the furniture of automobile, refrigerator, washing machine, elevator wallboard and top grade and room division board etc. all will use.Be all print again after the shape that sheet material is processed into requirement or spray to obtain appearance attractive in appearance the earliest, but the appearance that this nonplanar printing and spray process obtain is limited, technology is complicated and not environmental protection of technical process.In recent years in the household electrical appliance industry, rise gradually at the surface of steel plate composite plastic film and substitute the sheet metal with special decoration appearance characteristics, can not only play protective action, also has decoration function, has good appearance, regrettably plastic foil when producing multicolour and pattern, has also hidden the gloss of metal, has lost the peculiar texture of metal material.
At present, be used for the stainless steel wire drawing plate, fine aluminium bushing, titanizing wire drawing steel plate of family expenses panel etc., its material price is higher, has therefore restricted it and has applied.
Patent 201110365769.X discloses a kind of imitative aluminium wiredrawing composition membrane, comprises PET rete, adhesive phase, PVC rete and wire drawing aluminium foil layer.Another kind of technical scheme replaces the PVC rete with the PET rete.This imitative aluminium wiredrawing composition membrane has metallic luster and the wire drawing texture of wire drawing aluminum, simultaneously due to wire drawing paper tinsel layer between PET rete and PVC rete, therefore, can starvation, anti-oxidation, realize permanent keep the wire drawing aluminium foil metallic luster and wire-drawing effect; Should can further be compound in flat cold-rolled sheet, aluminium sheet, galvanized sheet, building material surface by imitative aluminium wiredrawing composition membrane, and play a part to decorate protection and attractive in appearance, technique is simple, easy and simple to handle, cost is low.
Patent 201110357527.6 discloses a kind of artificial stainless steel composite membrane with wire-drawing effect, comprises metal aluminum foil layer, PET rete, PVC rete, printing color layer and the protective layer that process through wire drawing on the surface.This artificial stainless steel composite membrane has very strong stainless steel wire drawing gloss, and the artificial stainless steel degree is high, and metallic luster is lasting, is applied on household electrical appliances, cooking apparatus to make it more attractive in appearance, improves product specification.
But above-mentioned two patents all adopt the trilaminate material complex technique, and technology is complicated, and is still very large to the energy and raw-material consumption demand, and are limited in the progress of the aspect such as energy-conservation, as to economize on resources; And owing to having used aluminium foil, because aluminium foil belongs to non-feature of environmental protection composite, so product does not possess environment-friendly function.
Number of patent application 201020640194.9 discloses a kind of stainless steel wire drawing plate.This is a kind of PCM precoating plate, and base material adopts corrosion resistant plate, carries out wire drawing with wire-drawing equipment, the surface roller coating finishing oil.Pencil hardness is greater than HB, and the cupping performance can be rushed dark 8mm, and combination property reaches conventional precoating product requirement comprehensively.But; this patent is large to corrosion resistant plate consumption demand; not only cost of material is high; compare simultaneously and carry out the wire drawing processing on plastic sheeting; carry out on corrosion resistant plate the wire drawing intractability larger, protect more difficult realization; therefore cost is very high, its production technology neither energy-conservation, economize on resources, also not environmental protection.
The utility model content
Technical problem to be solved in the utility model be to have overcome existing imitative metal wire-drawing composite film material consumption large, not energy-conservation, economize on resources, the also defective such as not environmental protection and production cost height provides the high imitative metal wire-drawing VCM film of a kind of BOPET.
The utility model is to solve above-mentioned technical problem by following technical proposals: the high imitative metal wire-drawing VCM film of a kind of BOPET, it comprises a hard surface coating successively, one single face carried out the transparent BOPET film that surperficial wire drawing is processed, and one strengthens fastness coating, a vacuum aluminium coated layer and an anti-oxidation protection coating; The one side of wherein processing through surperficial wire drawing in this BOPET film is connected with this enhancing fastness coating, and the one side of not processing through surperficial wire drawing is connected with this hard surface coating; This hard surface coating is the polyurethane ultraviolet curing dope layer; This enhancing fastness coating is the polyurethane coating layer, and this anti-oxidation protection coating is the polyurethane coating layer.
In the utility model, described " BOPET film " is the art technology term, refers to biaxially oriented polyester film.
In the utility model, described " VCM " is the art technology term, refers to the colorful laminated film-covered colored steel, and the covering material of this colorful laminated film-covered colored steel is called " VCM film ".
In the utility model, the thickness of the former film of this transparent BOPET film is preferably 23~188 microns.The light transmittance of the former film of this transparent BOPET film is preferably that 80~92%, 45 ° of glossiness are preferably 80~160Gs, and mist degree is preferably 0.8~3.0%.Described former film refers to not carry out surperficial wire drawing and processes front BOPET film.
Wherein, described surperficial wire drawing is processed and is adopted the surperficial Wire Drawing technique of this area routine to carry out, and in the utility model, preferred publication number is that the preparation method of the wire drawing decorative film put down in writing in the patent application of CN101746203A carries out described surperficial wire drawing and processes.Should be considered as quoting in full it for quoting of this patent application in the utility model.Processing by described wire drawing the wire drawing lines that obtains can obtain by this area conventional method, as the speed of changing the wire drawing roller of different lines and regulating the wire drawing roller is controlled.
Wherein, the thickness of this hard surface coating is preferably 0.8~1.2 micron.This hard surface coating is polyurethane ultraviolet curing coating (polyurethane UV coating) layer, and it is the light UV coating of UV6763-50 or the dumb light UV coating that model is UV6763M-BASE that the model that fine horse packaging material Co., Ltds produces is full of in preferred Shanghai.
Wherein, the thickness of this enhancing fastness coating is preferably 0.8~1.2 micron.Polyurethane coating in this enhancing fastness coating is preferably for to release the model that international trade (Shanghai) Co., Ltd. buys be the front primary coat of aluminizing of SC-400 from white.This primary coat is the commercial goods.The fastness that this transparent BOPET film surface is directly aluminized is generally 1~2.5N/15mm, and after being coated with this enhancing fastness coating, the attachment fastness of this vacuum aluminium coated layer and BOPET can be brought up to 6~10N/mm.
Wherein, the thickness of this vacuum aluminium coated layer can be selected arbitrarily between 0.1%~50% at the light transmittance that makes the BOPET film with this vacuum aluminium coated layer, preferably to have the light transmittance of the BOPET film of this vacuum aluminium coated layer be 5~7% or 26~28% two kinds.When light transmittance is 5~7%, can realize the effect of high imitative wire drawing aluminium sheet, when light transmittance is 26~28%, can realize the effect of high imitative titanizing steel plate, high artificial stainless steel bushing.This vacuum aluminium coated layer adopts the vacuum aluminum-coated processing technology of this area routine to obtain, and preferably adopting publication number is that the aluminum plating method for plastic film of putting down in writing in the patent application of CN101503790A carries out.Should be considered as quoting in full it for quoting of this patent application in the utility model.
Wherein, the thickness of this anti-oxidation protection coating is preferably 0.8~1.2 micron.Polyurethane coating in this anti-oxidation protection coating is preferably for to release model that international trade (Shanghai) Co., Ltd. buys be that the face of SC-500 is coated with from white.
Positive progressive effect of the present utility model is:
1, the utility model adopts individual layer BOPET as the main film body material, compares to have now by imitative metal wire-drawing film production technology two-layer or that plural layers are compound, has reduced the consumption of raw material film, production and the manufacturing cost of greatly having saved film.
2, in the enhancing fastness coating of BOPET film wire-drawing surface, strengthened the attachment fastness of vacuum aluminium coated layer and BOPET film, extended the performance of life of product and all kinds of bad conditions of tolerance.More than the pencil hardness of hard surface coating reached 2H, not only rub resistance, weather-resistant property were strong, also had simultaneously excellent anti-ultraviolet function, and protective film and metal level are avoided ultraviolet long-time irradiation and aging, the oxidation that cause fully.Accurately the vacuum aluminium coated layer of processing, obtained best imitative metal wire-drawing plate visual effect, really realized the high emulation purpose to unlike material wire drawing metallic plate.The protective finish of face of aluminizing has been realized the anti-oxidant, corrosion-resistant of aluminium coated, effectively guarantees and extended the life-span of integral product.
3, the high imitative metal wire-drawing VCM film of BOPET of the present utility model, undertaken compound by adhesive and sheet metal (as corrosion resistant plate, galvanized sheet etc.), real core plank, plastic plate, glass etc., the effect that had both had high imitative metal wire-drawing plate, lightweight, attractive in appearance, durable in, having again cheaper manufacturing cost, is existing by low cost two-layer or the imitative metal wire-drawing film production technology that plural layers the are compound production method that upgrades.
4, the high imitative metal wire-drawing VCM film of BOPET of the present utility model, drip respectively the sodium hydroxide solution 72 hours of 10% hydrochloric acid and 10% without significant change at film surface, hard surface coating face pencil hardness 〉=2H, can rush dark 8mm with the compound rear detection cupping performance of sheet metal, all reach or surpass the technical requirement of conventional precoating color steel product, therefore, have high industrial value and application prospect.
Description of drawings
Fig. 1 is the structural representation of the high imitative metal wire-drawing VCM film of BOPET of the utility model embodiment 1 and 2.
The specific embodiment
The below enumerates the embodiment of the high artificial stainless steel metal wire-drawing of BOPET VCM film, and comes by reference to the accompanying drawings the clearer the utility model that intactly illustrates.
Embodiment 1
One, the high imitative metal wire-drawing VCM membrane structure of BOPET:
As shown in Figure 1, the high imitative metal wire-drawing VCM film of the BOPET that produces of the present embodiment comprises successively: a hard surface coating 12, a single face carried out transparent BOPET film 13, that surperficial wire drawing processes to strengthen fastness coating 14, a light transmittance were 26~28% vacuum aluminium coated layer 15 and an anti-oxidation protection coating 16; The one side that BOPET processes through surperficial wire drawing is connected with this enhancing fastness coating 14.
Wherein, the BOPET film is 188 microns at the thickness that carries out before wire drawing is processed, and 90.2%, 45 ° of glossiness of former film light transmittance is 138Gs, mist degree 1.96%, other physical performance indexs meet State Standard of the People's Republic of China GB/T16958-2008[packing biaxially oriented polyester film].
It is the light UV coating of UV6763-50 that the surface cured coating selects buying to be full of the model that fine horse packaging material Co., Ltds produces from Shanghai, it is stirred rear standby.
Strengthen aluminium coated fastness coating and select buying from the white product of releasing international trade (Shanghai) Co., Ltd., name of product: the front primary coat of aluminizing, model: SC-400 stirs it rear standby.
The anti-oxidation protection coating selects buying from the white product of releasing international trade (Shanghai) Co., Ltd., and name of product: face is coated with, model: SC-500 stirs it rear standby.
Two, the high imitative metal wire-drawing VCM thin film technology method of BOPET:
(1) transparent BOPET film is carried out surperficial wire drawing and process, this processings entrusts Guangdong forever to contain packaging material Co., Ltds to carry out, and processing line number is No. 1 line.
(2) coating of surperficial cured coating layer: adopt the Zhongshan City Songde Coating Machine Co., Ltd, model: the coating apparatus of ST1650-21 type, utilize the applicator roll of roller H2, it is the coating (coating complete after the thickness of coating be 1 ± 0.2 micron) of 2 ± 0.2 g/ms that the non-wire-drawing surface of transparent BOPET film is coated with dry measure, the drying proposal that adopts heat cure and UV lamp drying both to combine, 65~100 ℃ of physical dryness Temperature Settings, UV is dry adopts four groups of power to be all the 250 burnt UV lamps of milli, naturally cooling standby after coating.
(3) strengthen the coating of fastness coating: adopt the Zhongshan City Songde Coating Machine Co., Ltd, model: the coating apparatus of ST1650-21 type, utilize the applicator roll of roller H2, it is the coating (coating complete after 1 ± 0.2 micron of the thickness of coating) of 4 g/ms that the wire-drawing surface of transparent BOPET film is coated with wet amount, naturally cooling standby after coating.
(4) processing of vacuum aluminium coated layer: vacuum aluminum-plating equipment adopts the photoelectricity technology corporation, Ltd. available from German Lai Bao, and PRO-M2100 type packaging material web coating system vacuumizes and reaches high vacuum levels (10
-4~10
-5Between mba), evaporation boat is preheated to 65%~80%(equipment and sets) between, the aluminium wire transfer rate is controlled at 160~250mm/min, during device start winding speed 〉=3.5m/s, the equipment baffle plate of opening begins evaporation, and the aluminium steam-condensation does not stop to cooling main hub surface on the enhancing fastness coating surface of the transparent BOPET film of reeling; The measured aluminum layer thickness of the on-line measurement instrument of the on-line determination metallized film aluminum layer thickness measure of the change of providing for oneself according to aluminum-spraying machine in process is adjusted winding speed (speed is controlled between 5.0~10.0m/s).Finally can obtain light transmittance by this processing technology is 26~28% the BOPET film with vacuum aluminium coated layer, has the corrosion resistant plate surface wire-drawing effect of high emulation.The transparent BOPET aluminium coated film of entire volume produce complete after, shutdowns, cooling evaporation boat, vacuum pumping, open a position and unload film, detect aluminum layer thickness, the end of product evaporation, the concrete operations condition can be referring to CN101503790A.
(5) coating of anti-oxidation protection coating: adopt the Zhongshan City Songde Coating Machine Co., Ltd; model: the coating apparatus of ST1650-21 type; utilize the applicator roll of roller H2; it is the coating (coating complete after 1 ± 0.2 micron of the thickness of coating) of 4 g/ms that vacuum aluminium coated layer is coated with wet amount, naturally coolingly after coating can make the high metal wire-drawing VCM film of imitating of BOPET.
Three, the performance test of the high imitative metal wire-drawing VCM film of BOPET:
The high imitative metal wire-drawing VCM film of the BOPET of the present embodiment is cut test piece, after the sodium hydroxide solution 72h that drips 10% hydrochloric acid and 10% on its hard surface coating, rinses well respectively, check dropping liquid film surface place, and with the not test piece surface contrast of dropping liquid.Result shows: the surface is without significant change, and product is qualified;
Test recording its hard surface coating and reach pencil hardness 2H by GB/T6739-1996 " hardness of film pencil determination method " (eqv JIS K5400-90-8.4), without obviously scratch or breakage, product is qualified;
With the high imitative metal wire-drawing VCM film of BOPET and the thick galvanized steel plain sheet of 0.8mm pass through the EAA PUR compound after, test by GB4156-84 " cupping test of metal method ", record the cupping performance and can rush dark 8.3mm, product is qualified;
Above emphasis detects the technical requirement that index all meets or exceeds conventional precoating color steel product.
Embodiment 2
One, the high imitative metal wire-drawing VCM membrane structure of BOPET:
As shown in Figure 1, the high imitative metal wire-drawing VCM film of the BOPET that produces of the present embodiment comprises successively: a hard surface coating 12, a single face carried out transparent BOPET film 13, that surperficial wire drawing processes to strengthen fastness coating 14, a light transmittance were 5~7% vacuum aluminium coated layer 15 and an anti-oxidation protection coating 16; The one side that BOPET processes through surperficial wire drawing is connected with this enhancing fastness coating 14.
Wherein, the BOPET film is 23 microns at the thickness that carries out before wire drawing is processed, and 91%, 45 ° of glossiness of former film light transmittance is 139Gs, mist degree 1.92%, other physical performance indexs meet State Standard of the People's Republic of China GB/T16958-2008[packing biaxially oriented polyester film].
It is the dumb light UV coating of UV6763M-BASE that the surface cured coating selects buying to be full of the model that fine horse packaging material Co., Ltds produces from Shanghai, it is stirred rear standby.
Strengthen aluminium coated fastness coating and select buying from the white product of releasing international trade (Shanghai) Co., Ltd., name of product: the front primary coat of aluminizing, model: SC-400 stirs it rear standby.
The anti-oxidation protection coating selects buying from the white product of releasing international trade (Shanghai) Co., Ltd., and name of product: face is coated with, model: SC-500 stirs it rear standby.
Two, the high imitative metal wire-drawing VCM thin film technology method of BOPET:
(1) transparent BOPET film is carried out surperficial wire drawing and process, concrete operations are with embodiment 1.
(2) coating of surperficial cured coating layer: concrete operations are with embodiment 1.
(3) strengthen the coating of fastness coating: concrete operations are with embodiment 1.
(4) processing of vacuum aluminium coated layer: vacuum aluminum-plating equipment adopts the photoelectricity technology corporation, Ltd. available from German Lai Bao, and PRO-M2100 type packaging material web coating system vacuumizes and reaches high vacuum levels (10
-4~10
-5Between mba), evaporation boat is preheated to 65%~80%(equipment and sets) between, the aluminium wire transfer rate is controlled at 250~350mm/min, during device start winding speed 〉=3.5m/s, the equipment baffle plate of opening begins evaporation, and the aluminium steam-condensation does not stop to cooling main hub surface on the enhancing fastness coating surface of the transparent BOPET film of reeling; The measured aluminum layer thickness of the on-line measurement instrument of the on-line determination metallized film aluminum layer thickness measure of the change of providing for oneself according to aluminum-spraying machine in process is adjusted winding speed, and (speed is controlled at 5.0~8.5m/s).Finally can obtain light transmittance by this processing technology is 5~7% the BOPET film with vacuum aluminium coated layer, has the surface of aluminum plate wire-drawing effect of high emulation.The transparent BOPET aluminium coated film of entire volume produce complete after, shutdowns, cooling evaporation boat, vacuum pumping, open a position and unload film, detect aluminum layer thickness, the end of product evaporation, the concrete operations condition can be referring to CN101503790A.
(5) coating of anti-oxidation protection coating: concrete operations are with embodiment 1.
Three, the performance test of the high imitative metal wire-drawing VCM film of BOPET:
The high imitative metal wire-drawing VCM film of the BOPET of the present embodiment is cut test piece, after the sodium hydroxide solution 72h that drips 10% hydrochloric acid and 10% on its hard surface coating, rinses well respectively, check dropping liquid film surface place, and with the not test piece surface contrast of dropping liquid.Result shows: the surface is without significant change, and product is qualified;
Test recording its hard surface coating and reach pencil hardness 2H by GB/T6739-1996 " hardness of film pencil determination method " (eqv JIS K5400-90-8.4), without obviously scratch or breakage, product is qualified;
With the high imitative metal wire-drawing VCM film of BOPET and the thick galvanized steel plain sheet of 0.8mm pass through the EAA PUR compound after, test by GB4156-84 " cupping test of metal method ", record the cupping performance and can rush dark 8.5mm, product is qualified;
Above emphasis detects the technical requirement that index all meets or exceeds conventional precoating color steel product.
Although more than described the specific embodiment of the present utility model, but those skilled in the art is to be understood that, these only illustrate, and under the prerequisite that does not deviate from principle of the present utility model and essence, can make various changes or modifications to these embodiments.Therefore, protection domain of the present utility model is limited by appended claims.
Claims (5)
1. a BOPET height is imitated metal wire-drawing VCM film, and it is characterized in that: it comprises a hard surface coating successively, and a single face carried out the transparent BOPET film that surperficial wire drawing is processed, and one strengthens fastness coating, a vacuum aluminium coated layer and an anti-oxidation protection coating; The one side of wherein processing through surperficial wire drawing in this BOPET film is connected with this enhancing fastness coating, and the one side of not processing through surperficial wire drawing is connected with this hard surface coating; This hard surface coating is the polyurethane ultraviolet curing dope layer; This enhancing fastness coating is the polyurethane coating layer, and this anti-oxidation protection coating is the polyurethane coating layer.
2. BOPET height as claimed in claim 1 is imitated metal wire-drawing VCM film, and it is characterized in that: the thickness of the former film of this transparent BOPET film is 23~188 microns.
3. BOPET height as claimed in claim 1 is imitated metal wire-drawing VCM film, and it is characterized in that: the thickness of this hard surface coating is 0.8~1.2 micron.
4. BOPET height as claimed in claim 1 is imitated metal wire-drawing VCM film, and it is characterized in that: the thickness of this enhancing fastness coating is 0.8~1.2 micron.
5. BOPET height as claimed in claim 1 is imitated metal wire-drawing VCM film, and it is characterized in that: the thickness of this anti-oxidation protection coating is 0.8~1.2 micron.