CN202911236U - 一种保温材料用高阻隔薄膜 - Google Patents

一种保温材料用高阻隔薄膜 Download PDF

Info

Publication number
CN202911236U
CN202911236U CN 201220336253 CN201220336253U CN202911236U CN 202911236 U CN202911236 U CN 202911236U CN 201220336253 CN201220336253 CN 201220336253 CN 201220336253 U CN201220336253 U CN 201220336253U CN 202911236 U CN202911236 U CN 202911236U
Authority
CN
China
Prior art keywords
thickness
film
insulation material
isolation film
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201220336253
Other languages
English (en)
Inventor
孙宏
徐莘
汤志敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Zijiang Colour Printing & Packaging Co Ltd
Original Assignee
Shanghai Zijiang Colour Printing & Packaging Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Zijiang Colour Printing & Packaging Co Ltd filed Critical Shanghai Zijiang Colour Printing & Packaging Co Ltd
Priority to CN 201220336253 priority Critical patent/CN202911236U/zh
Application granted granted Critical
Publication of CN202911236U publication Critical patent/CN202911236U/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本实用新型提供了一种保温材料用高阻隔薄膜，其特征在于：由尼龙薄膜层、高阻隔镀铝膜层、铝箔层和热封层从外到内通过粘合剂依次连接组成。本实用新型提供的一种保温材料用高阻隔薄膜通过采用铝箔叠加高阻隔镀铝薄膜方式，避免铝箔存在的微量针孔引起阻隔性能降低，具有很好的阻湿阻气性能，能维持真空绝热板长效保温。

Description

一种保温材料用高阻隔薄膜
技术领域
本实用新型涉及一种保温材料用高阻隔薄膜，属于真空绝热板保温技术领域。
背景技术
真空绝热板(简称VIP)是近年来全世界迅速发展的一种新型高效节能隔热保温材料，主要由无机纤维隔热芯材与高阻隔薄膜组合而成。除芯材本身具有一定的热阻外，还须用高阻隔薄膜将无机纤维隔热芯材和少量吸气剂密闭其中，并最大限度地抽去内部空气，以减少空气对流产生的热传导。高阻隔薄膜用于保证和维持内部真空度，使整个绝热板处于低导热状态，高阻隔薄膜的阻湿阻气性能直接影响到保温材料的节能效果和使用寿命。
在目前已有的VIP中，采用多层镀铝薄膜层压一起形成的高阻隔膜，初期导热系数较低，符合技术指标，但加速老化试验显示导热系数上升趋势较快，表明阻隔性能不够理想。
发明内容
本实用新型要解决的技术问题是提供一种有很好的阻湿阻气性能、能维持真空绝热板长效保温的高阻隔薄膜。
为了解决上述第一个技术问题，本实用新型的技术方案是提供一种保温材料用高阻隔薄膜，其特征在于：由尼龙薄膜层、高阻隔镀铝膜层、铝箔层和热封层从外到内通过粘合剂依次连接组成。
优选地，所述尼龙薄膜层为厚度为15μm的双向拉伸尼龙薄膜。
优选地，所述高阻隔镀铝膜层为镀有厚度
Figure BDA00001876979800011
的铝层的厚度为15～35μm的聚烯烃或聚酯基材。
优选地，所述高阻隔镀铝膜层为镀有厚度
Figure BDA00001876979800012
的铝层的厚度为12μm的双向拉伸聚酯基材。
优选地，所述铝箔层为厚度为6～9μm的软质铝箔。
优选地，所述热封层为厚度为30～100μm的共挤聚烯烃薄膜。
优选地，所述热封层为厚度为50μm的三层共挤吹塑聚乙烯薄膜，三层共挤吹塑聚乙烯薄膜由两个含10％低密度聚乙烯的线性低密度聚乙烯树脂层和一个茂金属线性低密度聚乙烯层从外到内依次连接组成。
优选地，所述粘合剂为厚度为2.5～3.0μm的双组分聚氨酯胶黏剂。
本实用新型提供的一种保温材料用高阻隔薄膜通过采用铝箔叠加高阻隔镀铝薄膜方式，避免铝箔存在的微量针孔引起阻隔性能降低，具有很好的阻湿阻气性能，能维持真空绝热板长效保温。
附图说明
图1为本实用新型提供的一种保温材料用高阻隔薄膜示意图；
图2为用本实用新型提供的保温材料用高阻隔薄膜和无机纤维隔热芯材制成的真空绝热板保温材料横截面示意图；
附图标记说明
1-尼龙薄膜层；2-高阻隔镀铝膜层；3-铝箔层；4-热封层；5-粘合剂；6-一种保温材料用高阻隔薄膜；7-无机纤维隔热芯材。
具体实施方式
为使本实用新型更明显易懂，兹以一优选实施例，并配合附图作详细说明如下。
图1为本实用新型提供的一种保温材料用高阻隔薄膜示意图，所述的一种保温材料用高阻隔薄膜由尼龙薄膜层1、高阻隔镀铝膜层2、铝箔层3和热封层4从外到内通过粘合剂5依次连接组成。
尼龙薄膜层1为厚度为15μm的双向拉伸尼龙薄膜。
高阻隔镀铝膜层2通过在厚度为15～35μm的聚烯烃或聚酯基材上蒸镀厚度
Figure BDA00001876979800021
的铝层而得到，优选地，在厚度为12μm的双向拉伸聚酯基材蒸镀厚度
Figure BDA00001876979800022
的铝层而得到。
铝箔层3为厚度为6～9μm的软质铝箔，优选厚度为7μm。
热封层4为厚度为30～100μm的共挤聚烯烃薄膜。优选厚度为50μm的三层共挤吹塑聚乙烯薄膜，三层共挤吹塑聚乙烯薄膜由两个含10％低密度聚乙烯的线性低密度聚乙烯树脂层和一个茂金属线性低密度聚乙烯层从外到内外到内依次连接。
粘合剂5为厚度为2.5～3.0μm的双组分聚氨酯胶黏剂。
本实用新型提供的一种保温材料用高阻隔薄膜制作方法分为以下3个步骤：
步骤1：在厚度为12μm的双向拉伸聚酯基材上真空蒸镀厚度为
Figure BDA00001876979800031
的铝层，制成高阻隔镀铝膜；
步骤2：采用多层共挤吹塑法生产厚度为50μm的三层共挤聚乙烯薄膜，将两个含10％低密度聚乙烯的线性低密度聚乙烯树脂层和一个茂金属线性低密度聚乙烯层从外到内依次连接；其中含茂金属线性低密度聚乙烯树脂的一面作为热封面，含线性低密度聚乙烯树脂的一面作复合面；茂金属线性低密度聚乙烯层厚度为20μm，线性低密度聚乙烯树脂层选用C8辛烯基共聚线性聚乙烯树脂。
步骤3：采用干法复合工艺，用双组份聚氨酯粘合剂依次将厚度为15μm的双向拉伸尼龙薄膜、步骤1制作的高阻隔镀铝膜、厚度为7μm的软质铝箔和厚度为50μm的三层共挤吹塑聚乙烯薄膜层压在一起，其中高阻隔镀铝膜的镀铝面与铝箔层压在一起。
采用ASTM D3985-05《Standard Test Method for Oxygen Gas TransmissionRate Through Plastic Film and Sheeting Using a Coulometric Sensorl》测试得高阻隔镀铝膜的氧气透过率小于0.5cm3/m2.24hr.0.1MPa，采用ASTM F1249-06《Standard Test Method for Water Vapor Transmission Rate Through Plastic Film andSheeting Using a Modulated Infrared Sensorl》测试得高阻隔镀铝膜的水蒸气透过率小于0.2g/m2·4hr，证明本实用新型提供的保温材料用高阻隔薄膜具有很好的阻湿阻气性能。
图2为用本实用新型提供的保温材料用高阻隔薄膜6和无机纤维隔热芯材7制成的真空绝热板保温材料横截面示意图，测量得该真空绝热板保温材料的导热系数不大于0.003w/m·k，证明本实用新型提供的一种保温材料用高阻隔薄膜能维持真空绝热板长效保温。

Claims (7)

1.一种保温材料用高阻隔薄膜，其特征在于：由尼龙薄膜层（1）、高阻隔镀铝膜层（2）、铝箔层（3）和热封层（4）从外到内通过粘合剂（5）依次连接组成。
2.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述尼龙薄膜层（1）为厚度为15μm的双向拉伸尼龙薄膜。
3.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述高阻隔镀铝膜层（2）为镀有厚度200~900Å的铝层的厚度为15~35μm的聚烯烃或聚酯基材。
4.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述高阻隔镀铝膜层（2）为镀有厚度600~750Å的铝层的厚度为12μm的双向拉伸聚酯基材。
5.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述铝箔层（3）为厚度为6~9μm的软质铝箔。
6.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述热封层（4）为厚度为30~100μm的共挤聚烯烃薄膜。
7.如权利要求1所述的一种保温材料用高阻隔薄膜，其特征在于：所述粘合剂（5）为厚度为2.5~3.0μm的双组分聚氨酯胶黏剂。
CN 201220336253 2012-07-03 2012-07-11 一种保温材料用高阻隔薄膜 Expired - Fee Related CN202911236U (zh)