CN202546910U - Impregnated paper laminated wooden floor-heating board - Google Patents
Impregnated paper laminated wooden floor-heating board Download PDFInfo
- Publication number
- CN202546910U CN202546910U CN2012200125643U CN201220012564U CN202546910U CN 202546910 U CN202546910 U CN 202546910U CN 2012200125643 U CN2012200125643 U CN 2012200125643U CN 201220012564 U CN201220012564 U CN 201220012564U CN 202546910 U CN202546910 U CN 202546910U
- Authority
- CN
- China
- Prior art keywords
- layer
- heating
- impregnated
- substrate layer
- paper laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an impregnated paper laminated wooden floor-heating board, which comprises a wear-resisting layer, a decorating layer, a heating substrate layer and a balance layer which are formed by stacking, adhering and hot-pressing treatments in sequence, wherein the heating substrate layer is composed of an upper substrate layer, a heating layer and a lower substrate layer which are adhered and hot-pressed by using glue in sequence; and the heating layer is a piece of far-infrared carbon fiber low-temperature heating paper. The impregnated paper laminated wooden floor-heating board is simple to install, low in continuing maintenance lost, low in heat consumption, and rapid to heat, is environmental-friendly and energy-saving, and is applicable for heat supply of places such as modern families and offices.
Description
Technical field
The utility model relates to a kind of floor, is specifically related to a kind of impregnated-paper laminated wooden ground heating floor.
Background technology
Widely used in the market impregnated-paper laminated wood floor is mated formation on artificial board substrates such as particieboard, high density fiberboard surface with one deck dedicated paper dipping thermoset amino resin, and the back side adds balance layer, and the front adds wearing layer, through the floor of hot pressing, moulding.The main timber floor of mating formation as ground now is popular in world architecture, home decoration industry, be the main development trend of modern timber floor, but impregnated-paper laminated wood floor does not possess the spontaneous heating function; Ground heating material on the market all is to separate with timber floor to mat formation or combine with construction material; Aspects such as the service life of geothermal heating material, energy-conservation, safety, environmental protection, health, physiotherapy all are not very desirable.
Carbon current fiber electric heating plane composite material low temperature radiation heating technology; Be to be different from radiator, air-conditioning, radiator to be the point type heating system of representative and to be the line formula heating system of representative, adopt the low-carbon (LC) heating high-tech product of modern science and technology art research and development in plane formula heating field with the heating cable.
In view of the above problems, the utility model discloses a kind of impregnated-paper laminated wooden ground heating floor.It has technical characterictic as mentioned below, to solve existing problem.
The utility model content
The purpose of the utility model provides a kind of impregnated-paper laminated wooden ground heating floor; Ingenious, the safety of its design, environmental protection, energy-conservation, regulate temperature automatically; Broken through the function of use of impregnated-paper laminated wood floor, carbon fiber electric heating composite and impregnated-paper laminated wood floor have been organically combined.
The purpose of the impregnated-paper laminated wooden ground heating floor of the utility model realizes through following technical scheme: a kind of impregnated-paper laminated wooden ground heating floor; Comprise that stacking wearing layer, decorative layer, heating base material layer and the balance layer pasting hot pressing and form successively forms; Wherein, Described heating base material layer is pasted hot pressing through glue successively by last substrate layer, heating layer and following substrate layer and is constituted, and described heating layer is a far infrared carbon fiber low temperature heating paper.
Above-mentioned impregnated-paper laminated wooden ground heating floor, wherein, described balance layer is the melamine-impregnated balance paper; Described decorative layer is the melamine-impregnated facing paper; Described wearing layer is the alundum (Al abrasion-proof paper.
Above-mentioned impregnated-paper laminated wooden ground heating floor, wherein, the resistance value scope of described heating layer is 350～2200 Ω, is evenly distributed with the glue nail hole of some pore diameter ranges at 6～15mm on the described heating layer; The limit of one group of described heating layer symmetry is provided with pair of electrodes, and the broadside of described electrode and heating layer is isometric, and described electrode is that width range is that the Copper Foil of 10～15mm presses bundle to form, and thickness range is 0.1～0.3mm.
Above-mentioned impregnated-paper laminated wooden ground heating floor, wherein, the limit of one group of symmetry of described substrate layer down is provided with the pair of conductive hole, and the diameter range of described conductive hole is 8～12mm, and the position of conductive hole is corresponding with the electrode position of heating layer.
Above-mentioned impregnated-paper laminated wooden ground heating floor; Wherein, The described glue of pasting substrate layer, heating layer and following substrate layer is urea-formaldehyde-modified resin glue or phenolic resin glue or cyanurotriamide modified resin glue, and said glue is evenly smeared front and the whole reverse side of going up substrate layer that is distributed in described whole substrate layer down.
Above-mentioned impregnated-paper laminated wooden ground heating floor wherein, also comprises connector, and described connector is made up of connector female terminal positioning set and connector male terminal assembly, and described connector male terminal assembly inserts connector female terminal positioning set; Described connector female terminal positioning set is arranged on down in the conductive hole of substrate layer, contacts with the electrode of heating layer.
Above-mentioned impregnated-paper laminated wooden ground heating floor, wherein, four sides of described impregnated-paper laminated wooden ground heating floor are provided with corresponding public tenon and female tenon, and described public tenon and female tenon mesh through public female mode to plug tenon or bayonet type tenon.
Above-mentioned impregnated-paper laminated wooden ground heating floor, wherein, described impregnated-paper laminated wooden ground heating floor length range is 300～1200mm, and width range is 300～1200mm, and thickness range is 8～16mm.
Above-mentioned impregnated-paper laminated wooden ground heating floor; Wherein, The described substrate layer of going up is that high-density plate is processed with following substrate layer; Described upward substrate layer thickness is 3～7mm, and described substrate layer thickness down is 5～8mm, and the described air-dry density that goes up substrate layer and following substrate layer is 0.80～1.00g/cm3.
Above-mentioned impregnated-paper laminated wooden ground heating floor wherein, also comprises temperature control system, and described temperature control system is made up of power switch, temperature controller, time controller and measurement and control of temperature probe.
The impregnated-paper laminated wooden ground heating floor of the utility model makes it compared with prior art owing to adopted such scheme, has following advantage and good effect:
1, the impregnated-paper laminated wooden ground heating floor of the utility model has combined carbon fiber electric heating plane composite material low temperature radiation heating technology and impregnated-paper laminated wood floor technology, and the two is united two into one, and has following characteristics:
(1) the low-carbon (LC) energy: the cleaning of the heating energy, renewable.With respect to heating energy such as coal, natural gas, stalk, timber, electric energy is as a kind of heating energy that development potentiality is arranged most, just along with being the rise of the new forms of energy of representative with solar energy, wind energy, water ability, nuclear energy etc., and flourish.And new forms of energy to offer human electric energy be cleaning, reproducible, be real low-carbon (LC) even " zero " carbon energy.
(2) low-carbon (LC) conversion: the thermal conversion efficiency of carbon fiber electric heating composite is high.With respect to the traditional heating mode, the thermal conversion rate of carbon fiber electric heating composite heating system can significantly reduce the energy loss in conversion and the transmittance process up to 99%.
(3) low-carbon emission: the zero-emission that waste gas etc. pollute.Relative traditional heating mode, thus use electric energy to reduce carbon emission on the whole as the heating energy, strengthen the low-carbon (LC) property that the energy uses thus.
(4) low-carbon (LC) life: meet the design of human body merit, comfortable and intelligent.Reaching with the heating cable with respect to the point type heating system that with radiator, air-conditioning, radiator is representative is the line formula heating system of representative; With the carbon fiber electric heating composite is the plane of new generation electric power heating system of representative, very agrees with the people at the cool livable needs of the warm head of activity space foot.Specifically: this exclusive heating mode, let the people feel that indoor temperature is even, pure and fresh, comfortable quiet, and do not have drying that tradition heating produces and sultry, can not cause indoor floating ash because of air-flow yet.It has not only heated room air, the far infrared outside line ripple that distributes in the simultaneity factor to human body the immunity regulated is arranged, function such as delay senility, the human health-preserving that temperature-rise period from bottom to top meets warm foot temperature head learns principle.In addition, the intelligent temperature control function can let people's heating of following one's inclinations, and promotes behavior energy saving, opens brand-new generation hommization low-carbon (LC) life.
(5) low-carbon economy: utilization and extra earning that force urges building energy conservation and valley power are arranged.See from electricity usage balance angle, the peak power consumption and night power consumption differ greatly, cause the waste of night electricity.Make full use of the low ebb electric weight, not only can take in, and can reduce cost of electricity-generating, stabilize electricity price for country increases valley power, energy savings, the low carbonization that promotes electric power energy is used.
2, the impregnated-paper laminated wooden ground heating floor simple installation of the utility model, follow-up maintenance cost is low, thermal losses is low, quick heating, and environmental protection and energy saving are economical and practical, are applicable to the heating on ground such as modern house life, office space.
Below; To do further explanation through concrete embodiment; Yet embodiment only is giving an example of the optional embodiment of the utility model, and its disclosed characteristic only is used to explain and set forth the technical scheme of the utility model, and is not used in the protection domain that limits the utility model.
Description of drawings
In order better to understand the utility model, the accompanying drawing for your guidance that can quote with reference to this specification, in the accompanying drawing:
Fig. 1 is the structural representation of the impregnated-paper laminated wooden ground heating floor of the utility model.
Fig. 2 is the structural representation of the heating base material layer of the impregnated-paper laminated wooden ground heating floor of the utility model.
Fig. 3 is the structural representation of the connector female terminal positioning set of the impregnated-paper laminated wooden ground heating floor of the utility model.
Fig. 4 is the structural representation of the connector male terminal assembly of the impregnated-paper laminated wooden ground heating floor of the utility model.
Fig. 5 is the structural representation that the connector of the impregnated-paper laminated wooden ground heating floor of the utility model is fit into the heating base material layer.
The specific embodiment
According to the claim and the disclosed content of utility model content of the utility model, the technical scheme of the utility model is specific as follows said.
See also shown in the accompanying drawing 1; The impregnated-paper laminated wooden ground heating floor of the utility model comprises that stacking wearing layer 1, decorative layer 2, heating base material layer 3 and the balance layer 4 pasting hot pressing and form successively forms; Wherein, Described heating base material layer 3 is pasted hot pressing through glue successively by last substrate layer 31, heating layer 32 and following substrate layer 33 and is constituted, and described heating layer 32 can adopt far infrared carbon fiber low temperature heating paper.
Described impregnated-paper laminated wooden ground heating floor length range is about 300～1200mm, and width range is about 300～1200mm, and thickness range is about 8～16mm, and the moisture content of said impregnated-paper laminated wooden ground heating floor is 3～8%; Four sides of described impregnated-paper laminated wooden ground heating floor are provided with corresponding public tenon and female tenon; Described public tenon and female tenon can adopt general public mother to plug tenon or bayonet type tenon; Only need during installation to fix connection, can accomplish the installation of module through the tongue and groove between two impregnated-paper laminated wooden ground heating floors.
Described balance layer 4 can adopt the melamine-impregnated balance paper; Described decorative layer 2 can adopt the melamine-impregnated facing paper, and described melamine-impregnated facing paper heavily is about 70～80g/m surely
2Described wearing layer 1 can adopt the alundum (Al abrasion-proof paper, and the fixed of described alundum (Al abrasion-proof paper heavily is 45g/g
2Stack hot pressing to wearing layer 1, decorative layer 2, heating base material layer 3 and balance layer 4 successively, hot pressing pressure is about 2000～3000 tons, and hot pressing time is about 1～8min.
See also shown in the accompanying drawing 2; The described substrate layer 31 of going up can adopt high-density plate to process with following substrate layer 33; Described substrate layer 31 thickness ranges of going up are about 3～7mm; Described substrate layer 33 thickness ranges down are about 5～8mm, and the described air-dry density scope that goes up substrate layer 31 and following substrate layer 33 is about 0.80～1.00g/cm3.
The resistance value scope of described heating layer 32 is about 350～2200 Ω, is evenly distributed with the glue nail hole 322 of some pore diameter ranges at 6～15mm on the described heating layer 32, is used to permeate glue; The limit of one group of symmetry of described heating layer 32 is provided with pair of electrodes 321; And described electrode 321 is isometric with the length on the bundle electrode limit of heating layer 32; Described electrode 321 presses bundle to form for the Copper Foil that width range is about 10～15mm, and thickness range is about 0.1～0.3mm.
The limit of one group of symmetry of described substrate layer 33 down is provided with pair of conductive hole 331, and the diameter range of described conductive hole 331 is about 8～12mm, and the position of conductive hole 331 is corresponding with electrode 321 positions of heating layer 32, is easy to conduction.
The glue that substrate layer 31, heating layer 32 and following substrate layer 33 are pasted in hot pressing can adopt urea-formaldehyde-modified resin glue or phenolic resin glue or cyanurotriamide modified resin glue, and said glue is evenly smeared front and the whole reverse side of going up substrate layer 31 that is distributed in whole substrate layer 33 down.Last substrate layer 31, heating layer 32 and following substrate layer 33 have been coated with glue and have pasted and do colding pressing typing after accomplishing and handle, and the shaping time of colding pressing is about 60～120min, and pressure is about 8～15kg/cm
2After the typing of colding pressing is accomplished, do hot-pressing processing, hot pressing time is about 45min～120min, and pressure is about 80 kg/cm
2～120kg/cm
2, hot pressing temperature is about 95 ℃～120 ℃; After accomplishing, hot pressing must handle the indoor again health of doing 5～7 days of heating base material.
See also shown in accompanying drawing 3, accompanying drawing 4 and the accompanying drawing 5; The impregnated-paper laminated wooden ground heating floor of the utility model also comprises connector; Described connector is made up of connector female terminal positioning set 5 and connector male terminal assembly 6, and described connector male terminal assembly 6 is promptly realized connecting after inserting connector female terminal positioning set 5; Described connector female terminal positioning set 5 is arranged on down in the conductive hole 331 of substrate layer 33, contacts with the electrode 321 of heating layer 32.
The impregnated-paper laminated wooden ground heating floor of the utility model also comprises the temperature control system (not shown), and described temperature control system is made up of power switch, temperature controller, time controller and measurement and control of temperature probe, and described power switch connects lead.
Embodiment 1:
The heating base material layer 3 of the impregnated-paper laminated wooden ground heating floor of the utility model is 0.80～1.00g/cm by air-dry density
3The hot pressing compacting formed after high-density plate was colded pressing and finalized the design.Two long limits of heating layer 32 are provided with pair of electrodes 321, electrode 321 and heating layer 32 the length on bundle electrode limit isometric, and adopt Copper Foil to press to prick and form; It is 10mm that electrode 321 adopts width; Thickness is the Copper Foil of 0.2mm, and the aperture that distribution rule is arranged on the heating layer 32 is the glue nail hole 322 of 10mm; Be respectively equipped with a conductive hole 331 on the broadside of following substrate layer 33, the pore diameter range of conductive hole 331 is about 8mm～12mm; The position of conductive hole 331 is corresponding with the position of heating layer 32 top electrodes 321.
In sum, the impregnated-paper laminated wooden ground heating floor simple installation of the utility model, follow-up maintenance cost is low, thermal losses is low, quick heating, and environmental protection and energy saving are economical and practical, are applicable to the heating on ground such as modern house life, office space.
Foregoing is the enumerating of specific embodiment of the impregnated-paper laminated wooden ground heating floor of the utility model, for the wherein not equipment of detailed description and structure, is to be understood that to taking existing common apparatus in this area and universal method to implement.
Claims (10)
1. impregnated-paper laminated wooden ground heating floor; It is characterized in that: comprise that stacking wearing layer, decorative layer, heating base material layer and the balance layer pasting hot pressing and form successively forms; Wherein, Described heating base material layer is pasted hot pressing through glue successively by last substrate layer, heating layer and following substrate layer and is constituted, and described heating layer is a far infrared carbon fiber low temperature heating paper.
2. impregnated-paper laminated wooden ground heating floor according to claim 1 is characterized in that: described balance layer is the melamine-impregnated balance paper; Described decorative layer is the melamine-impregnated facing paper; Described wearing layer is the alundum (Al abrasion-proof paper.
3. impregnated-paper laminated wooden ground heating floor according to claim 1 is characterized in that: the resistance value scope of described heating layer is 350～2200 Ω, is evenly distributed with the glue nail hole of some pore diameter ranges at 6～15mm on the described heating layer; The limit of one group of described heating layer symmetry is provided with pair of electrodes, and the broadside of described electrode and heating layer is isometric, and described electrode is that width range is that the Copper Foil of 10～15mm presses bundle to form, and thickness range is 0.1～0.3mm.
4. impregnated-paper laminated wooden ground heating floor according to claim 3; It is characterized in that: the limit of one group of symmetry of described substrate layer down is provided with the pair of conductive hole; The diameter range of described conductive hole is 8～12mm, and the position of conductive hole is corresponding with the electrode position of heating layer.
5. impregnated-paper laminated wooden ground heating floor according to claim 1; It is characterized in that: the described glue of pasting substrate layer, heating layer and following substrate layer is urea-formaldehyde-modified resin glue or phenolic resin glue or cyanurotriamide modified resin glue, and described glue is evenly smeared front and the whole reverse side of going up substrate layer that is distributed in described whole substrate layer down.
6. impregnated-paper laminated wooden ground heating floor according to claim 4; It is characterized in that: also comprise connector; Described connector is made up of connector female terminal positioning set and connector male terminal assembly, and described connector male terminal assembly inserts connector female terminal positioning set; Described connector female terminal positioning set is arranged on down in the conductive hole of substrate layer, contacts with the electrode of heating layer.
7. impregnated-paper laminated wooden ground heating floor according to claim 1; It is characterized in that: four sides of described impregnated-paper laminated wooden ground heating floor are provided with corresponding public tenon and female tenon, and described public tenon and female tenon mesh through public female mode to plug tenon or bayonet type tenon.
8. impregnated-paper laminated wooden ground heating floor according to claim 1 is characterized in that: described impregnated-paper laminated wooden ground heating floor length range is 300～1200mm, and width range is 300～1200mm, and thickness range is 8～16mm.
9. impregnated-paper laminated wooden ground heating floor according to claim 1; It is characterized in that: the described substrate layer of going up is that high-density plate is processed with following substrate layer; Described upward substrate layer thickness is 3～7mm; Described substrate layer thickness down is 5～8mm, and the described air-dry density that goes up substrate layer and following substrate layer is 0.80～1.00g/cm3.
10. impregnated-paper laminated wooden ground heating floor according to claim 1 is characterized in that: also comprise temperature control system, described temperature control system is made up of power switch, temperature controller, time controller and measurement and control of temperature probe.